WO2016072358A1 - Procédé de fabrication de film optique comprenant un film protecteur - Google Patents

Procédé de fabrication de film optique comprenant un film protecteur Download PDF

Info

Publication number
WO2016072358A1
WO2016072358A1 PCT/JP2015/080676 JP2015080676W WO2016072358A1 WO 2016072358 A1 WO2016072358 A1 WO 2016072358A1 JP 2015080676 W JP2015080676 W JP 2015080676W WO 2016072358 A1 WO2016072358 A1 WO 2016072358A1
Authority
WO
WIPO (PCT)
Prior art keywords
protective film
film
polarizing plate
width direction
adhesive layer
Prior art date
Application number
PCT/JP2015/080676
Other languages
English (en)
Japanese (ja)
Inventor
宙孝 石川
泰礼 加藤
規光 坂田
Original Assignee
住友化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 住友化学株式会社 filed Critical 住友化学株式会社
Priority to KR1020177013989A priority Critical patent/KR20170078716A/ko
Priority to CN201580059768.9A priority patent/CN107073921A/zh
Publication of WO2016072358A1 publication Critical patent/WO2016072358A1/fr

Abstract

L'invention concerne un procédé pour fabriquer un film optique comprenant un film protecteur, le procédé comprenant une étape consistant à fixer un film protecteur à la surface d'un film optique, la force d'arrachage du film protecteur à partir du film optique dans les deux sections d'extrémité dans la direction de largeur du film optique comprenant un film protecteur, obtenu par l'étape consistant à fixer le film protecteur, étant augmentée par rapport à la force d'arrachage dans l'autre partie du film optique comprenant un film protecteur. Ce procédé de fabrication comprend en outre de préférence une étape consistant à retirer les deux sections d'extrémité dans la direction de largeur après l'étape consistant à fixer le film protecteur.
PCT/JP2015/080676 2014-11-04 2015-10-30 Procédé de fabrication de film optique comprenant un film protecteur WO2016072358A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
KR1020177013989A KR20170078716A (ko) 2014-11-04 2015-10-30 프로텍트 필름을 갖는 광학 필름의 제조 방법
CN201580059768.9A CN107073921A (zh) 2014-11-04 2015-10-30 带防护膜的光学膜的制造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2014224382 2014-11-04
JP2014-224382 2014-11-04

Publications (1)

Publication Number Publication Date
WO2016072358A1 true WO2016072358A1 (fr) 2016-05-12

Family

ID=55909083

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2015/080676 WO2016072358A1 (fr) 2014-11-04 2015-10-30 Procédé de fabrication de film optique comprenant un film protecteur

Country Status (4)

Country Link
KR (1) KR20170078716A (fr)
CN (1) CN107073921A (fr)
TW (1) TWI666474B (fr)
WO (1) WO2016072358A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2019215470A (ja) * 2018-06-14 2019-12-19 住友化学株式会社 液晶フィルムの製造方法及び光学積層体の製造方法

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110506307B (zh) * 2017-06-23 2022-09-20 日东电工株式会社 图像显示装置的制造方法及通过该制造方法所得的图像显示装置
TW201947778A (zh) * 2018-05-10 2019-12-16 日商住友化學股份有限公司 積層體
TWI702426B (zh) * 2018-11-20 2020-08-21 住華科技股份有限公司 偏光板及包含其之顯示裝置的製造方法

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0716962A (ja) * 1993-06-30 1995-01-20 Sumitomo Chem Co Ltd 物品の表面一時保護フィルム
JP2001281454A (ja) * 2000-04-03 2001-10-10 Nitto Denko Corp 保護フィルム付き光学フィルム
JP2010100038A (ja) * 2008-09-26 2010-05-06 Japan Polyethylene Corp 表面保護用積層フィルム
JP2014069465A (ja) * 2012-09-28 2014-04-21 Tsuchiya Yac Corp 保護フィルム貼着部材
JP2014113687A (ja) * 2012-12-06 2014-06-26 Nitto Denko Corp 薄ガラス積層体

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2005119631A2 (fr) * 2004-06-04 2005-12-15 Fujifilm Corporation Etiquette adhesive, rouleau d'etiquettes adhesives, bande photosensible et appareil et procede de fabrication d'un corps stratifie photosensible
JP5134299B2 (ja) * 2007-07-25 2013-01-30 ユニ・チャーム株式会社 吸収性物品
WO2013059600A1 (fr) * 2011-10-20 2013-04-25 Eaves Felmont Revêtement amovible et emballage interactif

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0716962A (ja) * 1993-06-30 1995-01-20 Sumitomo Chem Co Ltd 物品の表面一時保護フィルム
JP2001281454A (ja) * 2000-04-03 2001-10-10 Nitto Denko Corp 保護フィルム付き光学フィルム
JP2010100038A (ja) * 2008-09-26 2010-05-06 Japan Polyethylene Corp 表面保護用積層フィルム
JP2014069465A (ja) * 2012-09-28 2014-04-21 Tsuchiya Yac Corp 保護フィルム貼着部材
JP2014113687A (ja) * 2012-12-06 2014-06-26 Nitto Denko Corp 薄ガラス積層体

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2019215470A (ja) * 2018-06-14 2019-12-19 住友化学株式会社 液晶フィルムの製造方法及び光学積層体の製造方法
JP7085414B2 (ja) 2018-06-14 2022-06-16 住友化学株式会社 液晶フィルムの製造方法及び光学積層体の製造方法

Also Published As

Publication number Publication date
KR20170078716A (ko) 2017-07-07
CN107073921A (zh) 2017-08-18
TWI666474B (zh) 2019-07-21
TW201632921A (zh) 2016-09-16

Similar Documents

Publication Publication Date Title
KR102662175B1 (ko) 광학 적층체 및 그 제조 방법
JP6154099B2 (ja) 偏光性積層フィルムの製造方法及び偏光板の製造方法
JP6120779B2 (ja) 偏光性積層フィルムの製造方法及び偏光板の製造方法
CN105717572B (zh) 带有保护膜的偏振板及包含它的层叠体
JP6741477B2 (ja) 偏光フィルム、粘着剤層付き偏光フィルム、及び画像表示装置
KR102436860B1 (ko) 광학 필름 세트 및 그의 제조 방법
KR20100117591A (ko) 편광판
JP7542967B2 (ja) 積層体
JP5976969B1 (ja) プロテクトフィルム付偏光板の製造方法
WO2016072358A1 (fr) Procédé de fabrication de film optique comprenant un film protecteur
JP6968531B2 (ja) プロテクトフィルム付偏光板の製造方法
KR102266085B1 (ko) 편광 필름 롤의 제조 방법
KR102587187B1 (ko) 편광판의 제조 방법
KR20160131027A (ko) 편광판의 제조 방법
JP7564170B2 (ja) 光学シート
KR102356930B1 (ko) 매엽상의 광학 필름
KR102502463B1 (ko) 프로텍트 필름을 갖는 편광판의 제조 방법
TWI698667B (zh) 附保護膜之偏光板之製造方法
JP6359048B2 (ja) 偏光フィルムの製造方法
KR102256908B1 (ko) 편광판 매엽체의 제조 방법
KR102425954B1 (ko) 광학 표시 패널의 제조 방법과 광학 표시 패널의 제조 시스템
JP6333168B2 (ja) 偏光板の製造方法
KR102691166B1 (ko) 프로텍트 필름 구비 편광판 매엽체의 제조 방법
JP6761144B2 (ja) 積層フィルムの製造方法
KR20160028874A (ko) 표면보호필름을 구비하는 편광판

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15856869

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 20177013989

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: JP

122 Ep: pct application non-entry in european phase

Ref document number: 15856869

Country of ref document: EP

Kind code of ref document: A1