WO2016067406A1 - Ruban adhésif - Google Patents

Ruban adhésif Download PDF

Info

Publication number
WO2016067406A1
WO2016067406A1 PCT/JP2014/078879 JP2014078879W WO2016067406A1 WO 2016067406 A1 WO2016067406 A1 WO 2016067406A1 JP 2014078879 W JP2014078879 W JP 2014078879W WO 2016067406 A1 WO2016067406 A1 WO 2016067406A1
Authority
WO
WIPO (PCT)
Prior art keywords
sensitive adhesive
pressure
radical polymerization
adhesive tape
weight
Prior art date
Application number
PCT/JP2014/078879
Other languages
English (en)
Japanese (ja)
Inventor
由貴 石川
泰志 石堂
戸田　智基
Original Assignee
積水化学工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=53277906&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=WO2016067406(A1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by 積水化学工業株式会社 filed Critical 積水化学工業株式会社
Priority to KR1020167024811A priority Critical patent/KR102263797B1/ko
Priority to CN201480075883.0A priority patent/CN106029805B/zh
Priority to JP2014555436A priority patent/JP5721917B1/ja
Priority to PCT/JP2014/078879 priority patent/WO2016067406A1/fr
Publication of WO2016067406A1 publication Critical patent/WO2016067406A1/fr

Abstract

La présente invention a pour objet un ruban adhésif qui est résistant au décollement bien qu'il soit un ruban adhésif mince et qui présente une haute performance de décollement sous une charge constante et une haute énergie de cohésion d'agent adhésif par rapport à un objet à coller. À cet effet la présente invention porte sur un ruban adhésif comprenant une couche adhésive comprenant un agent de réticulation et un constituant polymère qui contient 60 % en poids ou plus d'un polymère acrylique qui est obtenu par polymérisation radicalaire vivante et qui a les groupes fonctionnels de réticulation, une masse moléculaire moyenne en poids de 300 000 à 2 000 000 et une distribution de masse moléculaire (Mw/Mn) de 1,05 à 2,5. Le pourcentage de gel de la couche adhésive est inférieur ou égal à 15 % en poids.
PCT/JP2014/078879 2014-10-30 2014-10-30 Ruban adhésif WO2016067406A1 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
KR1020167024811A KR102263797B1 (ko) 2014-10-30 2014-10-30 점착 테이프
CN201480075883.0A CN106029805B (zh) 2014-10-30 2014-10-30 粘合带
JP2014555436A JP5721917B1 (ja) 2014-10-30 2014-10-30 粘着テープ
PCT/JP2014/078879 WO2016067406A1 (fr) 2014-10-30 2014-10-30 Ruban adhésif

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/JP2014/078879 WO2016067406A1 (fr) 2014-10-30 2014-10-30 Ruban adhésif

Publications (1)

Publication Number Publication Date
WO2016067406A1 true WO2016067406A1 (fr) 2016-05-06

Family

ID=53277906

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2014/078879 WO2016067406A1 (fr) 2014-10-30 2014-10-30 Ruban adhésif

Country Status (4)

Country Link
JP (1) JP5721917B1 (fr)
KR (1) KR102263797B1 (fr)
CN (1) CN106029805B (fr)
WO (1) WO2016067406A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2018188630A (ja) * 2017-05-01 2018-11-29 積水化学工業株式会社 粘着テープ
KR20220111300A (ko) 2019-12-13 2022-08-09 토요잉크Sc홀딩스주식회사 블록 공중합체, 수지 조성물, 신축성 도체, 전자 디바이스 및 점착 필름

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN107709494A (zh) * 2015-10-30 2018-02-16 积水化学工业株式会社 双面粘合带
CN109355024A (zh) * 2018-10-14 2019-02-19 佛山市顺德区永创翔亿电子材料有限公司 锂电芯抗静电压敏胶及制备方法及锂电芯抗静电保护膜
CN109385236A (zh) * 2018-10-14 2019-02-26 佛山市顺德区永创翔亿电子材料有限公司 锂电池抗静电耐电解液胶黏剂及其制备方法及终止胶带
JP7137434B2 (ja) * 2018-10-15 2022-09-14 大塚化学株式会社 粘着剤組成物および粘着フィルム
JP6888181B1 (ja) * 2019-12-06 2021-06-16 大塚化学株式会社 粘着材、粘着シートおよび屈曲性積層部材

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000290625A (ja) * 1999-04-07 2000-10-17 Nitto Denko Corp 粘着剤組成物とその製造方法
JP2011074380A (ja) * 2009-09-07 2011-04-14 Lintec Corp 保護フィルム及び保護フィルムの製造方法
JP5256515B2 (ja) * 2006-04-14 2013-08-07 大塚化学株式会社 樹脂組成物および耐熱性粘着剤
JP2014031442A (ja) * 2012-08-03 2014-02-20 Lintec Corp 保護フィルム

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5256515Y2 (fr) 1973-06-15 1977-12-21
KR101374511B1 (ko) * 2007-03-09 2014-03-13 세키스이가가쿠 고교가부시키가이샤 점착제, 양면 점착 시트 및 표시 장치

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000290625A (ja) * 1999-04-07 2000-10-17 Nitto Denko Corp 粘着剤組成物とその製造方法
JP5256515B2 (ja) * 2006-04-14 2013-08-07 大塚化学株式会社 樹脂組成物および耐熱性粘着剤
JP2011074380A (ja) * 2009-09-07 2011-04-14 Lintec Corp 保護フィルム及び保護フィルムの製造方法
JP2014031442A (ja) * 2012-08-03 2014-02-20 Lintec Corp 保護フィルム

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2018188630A (ja) * 2017-05-01 2018-11-29 積水化学工業株式会社 粘着テープ
JP7271089B2 (ja) 2017-05-01 2023-05-11 積水化学工業株式会社 粘着テープ
KR20220111300A (ko) 2019-12-13 2022-08-09 토요잉크Sc홀딩스주식회사 블록 공중합체, 수지 조성물, 신축성 도체, 전자 디바이스 및 점착 필름

Also Published As

Publication number Publication date
CN106029805A (zh) 2016-10-12
KR102263797B1 (ko) 2021-06-10
JPWO2016067406A1 (ja) 2017-04-27
JP5721917B1 (ja) 2015-05-20
CN106029805B (zh) 2020-07-14
KR20170076618A (ko) 2017-07-04

Similar Documents

Publication Publication Date Title
JP5779696B2 (ja) 粘着テープ
JP5721917B1 (ja) 粘着テープ
JP6364224B2 (ja) 光学フィルム固定用両面粘着テープ
WO2017073722A1 (fr) Bande adhésive double face sensible à la pression
JP6424034B2 (ja) 電子機器用粘着シート
JP7065655B2 (ja) 粘着テープ
WO2017110839A1 (fr) Composition adhésive et ruban adhésif
JP5820512B1 (ja) 構造制御されたブロック共重合ポリマー、粘着剤及び粘着テープ
JP6352219B2 (ja) 粘着テープ
WO2016181691A1 (fr) Ruban adhésif double face pour la fixation d'un film optique
JP2019007027A (ja) 電子機器用粘着シート
JP6352159B2 (ja) 熱伝導性粘着テープ及び熱伝導性粘着剤組成物
JP2019196492A (ja) 粘着テープ
JP6564499B2 (ja) 熱伝導性粘着テープ
JP6560022B2 (ja) 粘着テープ
JP2018003012A (ja) 難燃性粘着剤組成物及び難燃性粘着テープ
JP7271089B2 (ja) 粘着テープ
JP6557510B2 (ja) 導電性粘着テープ及び導電性粘着剤組成物
JP6174993B2 (ja) グラファイトシート用両面粘着テープ
JP7348811B2 (ja) 粘着テープ
JP2016023238A (ja) 粘着テープ

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2014555436

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14905055

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 20167024811

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14905055

Country of ref document: EP

Kind code of ref document: A1