WO2016013492A1 - Poudre d'alliage utilisée en dépôt de fil en fusion - Google Patents

Poudre d'alliage utilisée en dépôt de fil en fusion Download PDF

Info

Publication number
WO2016013492A1
WO2016013492A1 PCT/JP2015/070465 JP2015070465W WO2016013492A1 WO 2016013492 A1 WO2016013492 A1 WO 2016013492A1 JP 2015070465 W JP2015070465 W JP 2015070465W WO 2016013492 A1 WO2016013492 A1 WO 2016013492A1
Authority
WO
WIPO (PCT)
Prior art keywords
concentration
less
alloy
alloy powder
atomic
Prior art date
Application number
PCT/JP2015/070465
Other languages
English (en)
Japanese (ja)
Inventor
隆彦 加藤
孝介 桑原
正 藤枝
青田　欣也
高橋　勇
佐竹　弘之
山賀　賢史
元 村上
Original Assignee
株式会社日立製作所
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2014150027A external-priority patent/JP6388381B2/ja
Priority claimed from JP2014151336A external-priority patent/JP6388278B2/ja
Application filed by 株式会社日立製作所 filed Critical 株式会社日立製作所
Publication of WO2016013492A1 publication Critical patent/WO2016013492A1/fr

Abstract

L'invention a pour objet une structure en alliage de forme et de taille quelconques qui a une grande uniformité de composition élémentaire et de distribution de la résistance mécanique et qui a d'excellentes résistance à haute température et résistance à la corrosion, cette poudre d'alliage utilisée en dépôt de fil en fusion étant caractérisée en ce qu'elle contient de l'Al, du Co, du Cr, du Fe et du Ni en une concentration atomique de 5 à 30 % at. chacun, en ce que la différence entre les concentrations atomiques d'au moins quatre des éléments susmentionnés est inférieure à 3 % at. et en ce qu'elle contient, en tant qu'impuretés inévitables, une concentration atomique inférieure ou égale à 0,005 % en poids de P, inférieure ou égale à 0,040 % en poids de Si, inférieure ou égale à 0,002 % en poids de S, inférieure ou égale à 0,005 % en poids de Sn, inférieure ou égale à 0,002 % en poids de Sb, inférieure ou égale à 0,005 % en poids d'As, inférieure ou égale à 0,050 % en poids de Mn, inférieure ou égale à 0,001 % en poids d'O et inférieure ou égale à 0,002 % en poids de N.
PCT/JP2015/070465 2014-07-23 2015-07-17 Poudre d'alliage utilisée en dépôt de fil en fusion WO2016013492A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2014150027A JP6388381B2 (ja) 2014-07-23 2014-07-23 合金構造体
JP2014-150027 2014-07-23
JP2014151336A JP6388278B2 (ja) 2014-07-25 2014-07-25 溶融積層造形に用いる合金粉末
JP2014-151336 2014-07-25

Publications (1)

Publication Number Publication Date
WO2016013492A1 true WO2016013492A1 (fr) 2016-01-28

Family

ID=55163018

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2015/070465 WO2016013492A1 (fr) 2014-07-23 2015-07-17 Poudre d'alliage utilisée en dépôt de fil en fusion

Country Status (1)

Country Link
WO (1) WO2016013492A1 (fr)

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN108642363A (zh) * 2018-05-28 2018-10-12 西北工业大学 一种高强高塑共晶高熵合金及其制备方法
CN109402484A (zh) * 2019-01-02 2019-03-01 中国科学院兰州化学物理研究所 一种等轴晶和纳米析出耦合AlxCoCrFeNi高熵合金的制备方法
CN110684917A (zh) * 2019-11-06 2020-01-14 四川大学 相变诱导塑性的高强度铁锰铝镍基多主元合金
CN110791693A (zh) * 2019-11-20 2020-02-14 安徽工业大学 低Al含量、高强韧性、耐酸腐蚀的高熵合金及其制备方法
CN111394636A (zh) * 2020-03-24 2020-07-10 太原理工大学 具有马氏体相变的高强度大塑性高熵合金及其制备方法
CN113215468A (zh) * 2021-05-06 2021-08-06 西北工业大学 一种双相高熵高温合金及其增材制造方法
CN113355625A (zh) * 2021-06-04 2021-09-07 福建工程学院 一种NbC增强的高熵合金基复合涂层及其制备方法
CN114939654A (zh) * 2022-05-27 2022-08-26 中机新材料研究院(郑州)有限公司 一种用于激光增材制造的高熵合金粉末及其制备方法、应用

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2002173732A (ja) * 2000-11-29 2002-06-21 Univ Qinghua ハイエントロピー多元合金
JP2004124201A (ja) * 2002-10-04 2004-04-22 Japan Science & Technology Corp 金属粉末光造形方法
CN102220026A (zh) * 2011-04-11 2011-10-19 黄元盛 高熵合金粉末导电高分子复合材料及其制作方法
CN103056352A (zh) * 2012-12-04 2013-04-24 中国人民解放军装甲兵工程学院 用于超音速喷涂的高熵合金粉末材料及其制备方法
US20130323116A1 (en) * 2012-05-31 2013-12-05 Swe-Kai Chen Alloy material with constant electrical resistivity, applications and method for producing the same
JP2014105373A (ja) * 2012-11-29 2014-06-09 Canon Inc 金属光造形用金属粉末、射出成形用金型の製造方法、射出成形用金型および成形品

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2002173732A (ja) * 2000-11-29 2002-06-21 Univ Qinghua ハイエントロピー多元合金
JP2004124201A (ja) * 2002-10-04 2004-04-22 Japan Science & Technology Corp 金属粉末光造形方法
CN102220026A (zh) * 2011-04-11 2011-10-19 黄元盛 高熵合金粉末导电高分子复合材料及其制作方法
US20130323116A1 (en) * 2012-05-31 2013-12-05 Swe-Kai Chen Alloy material with constant electrical resistivity, applications and method for producing the same
JP2014105373A (ja) * 2012-11-29 2014-06-09 Canon Inc 金属光造形用金属粉末、射出成形用金型の製造方法、射出成形用金型および成形品
CN103056352A (zh) * 2012-12-04 2013-04-24 中国人民解放军装甲兵工程学院 用于超音速喷涂的高熵合金粉末材料及其制备方法

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
F. J. WANG ET AL.: "Cooling Rate and Size Effect on the Microstructure and Mechanical Properties of AlCoCrFeNi High Entropy Alloy", JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY, vol. 131, no. 3, July 2009 (2009-07-01), pages 034501.1 - 034501.3 *
YEVGENI BRIF ET AL.: "The use of high-entropy alloys in additive manufacturing", SCRIPTA MATERIALIA, vol. 99, pages 93 - 96 *

Cited By (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN108642363A (zh) * 2018-05-28 2018-10-12 西北工业大学 一种高强高塑共晶高熵合金及其制备方法
CN109402484A (zh) * 2019-01-02 2019-03-01 中国科学院兰州化学物理研究所 一种等轴晶和纳米析出耦合AlxCoCrFeNi高熵合金的制备方法
CN109402484B (zh) * 2019-01-02 2021-03-26 中国科学院兰州化学物理研究所 一种等轴晶和纳米析出耦合AlxCoCrFeNi高熵合金的制备方法
CN110684917B (zh) * 2019-11-06 2021-03-23 四川大学 相变诱导塑性的高强度铁锰铝镍基多主元合金
CN110684917A (zh) * 2019-11-06 2020-01-14 四川大学 相变诱导塑性的高强度铁锰铝镍基多主元合金
CN110791693A (zh) * 2019-11-20 2020-02-14 安徽工业大学 低Al含量、高强韧性、耐酸腐蚀的高熵合金及其制备方法
CN110791693B (zh) * 2019-11-20 2021-05-07 安徽工业大学 低Al含量、高强韧性、耐酸腐蚀的高熵合金及其制备方法
CN111394636A (zh) * 2020-03-24 2020-07-10 太原理工大学 具有马氏体相变的高强度大塑性高熵合金及其制备方法
CN111394636B (zh) * 2020-03-24 2021-06-15 太原理工大学 具有马氏体相变的高强度大塑性高熵合金及其制备方法
CN113215468A (zh) * 2021-05-06 2021-08-06 西北工业大学 一种双相高熵高温合金及其增材制造方法
CN113355625A (zh) * 2021-06-04 2021-09-07 福建工程学院 一种NbC增强的高熵合金基复合涂层及其制备方法
CN114939654A (zh) * 2022-05-27 2022-08-26 中机新材料研究院(郑州)有限公司 一种用于激光增材制造的高熵合金粉末及其制备方法、应用
CN114939654B (zh) * 2022-05-27 2023-04-07 中机新材料研究院(郑州)有限公司 一种用于激光增材制造的高熵合金粉末及其制备方法、应用

Similar Documents

Publication Publication Date Title
JP6388381B2 (ja) 合金構造体
JP6393885B2 (ja) 合金粉末の製造方法
JP6459272B2 (ja) 合金構造体
US10576538B2 (en) Alloy structure and method for producing alloy structure
US10702944B2 (en) Alloy structure and method for producing alloy structure
JP6455701B2 (ja) 合金構造体
JP6455699B2 (ja) 合金構造体の製造方法
JP6388277B2 (ja) 合金構造体の製造方法
JP6455700B2 (ja) 合金構造体の製造方法
WO2016013492A1 (fr) Poudre d'alliage utilisée en dépôt de fil en fusion
WO2016013495A1 (fr) Structure en alliage et procédé de fabrication de structure en alliage
WO2016013494A1 (fr) Poudre d'alliage utilisée dans la modélisation par dépôt fondu, et procédé de production de ladite poudre d'alliage
WO2016013496A1 (fr) Structure d'alliage et procédé de production de structure d'alliage.
JP7116495B2 (ja) 高炭素コバルト系合金
JP6536927B2 (ja) 合金構造体
EP2361704A1 (fr) Matériau métallique multiphase et son procédé de fabrication
JP2009293108A (ja) Ａｌ基合金スパッタリングターゲット材の製造方法
JP6432822B2 (ja) 溶融積層造形に用いる合金粉末
JP6388278B2 (ja) 溶融積層造形に用いる合金粉末
CN113795603B (zh) Ni基合金、Ni基合金粉末、Ni基合金构件和具备Ni基合金构件的制造物
WO2016013493A1 (fr) Procédé de production d'un alliage de coulée
JP6393884B2 (ja) 合金粉末の製造方法
JP6443721B2 (ja) 合金構造体の製造方法
JP7103548B2 (ja) Ｎｉ－Ｃｒ－Ｍｏ系合金部材、Ｎｉ－Ｃｒ－Ｍｏ系合金粉末、および、複合部材

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15824560

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 15824560

Country of ref document: EP

Kind code of ref document: A1