WO2015186474A1 - 消耗電極式アーク溶接のアークスタート制御方法、溶接装置 - Google Patents

消耗電極式アーク溶接のアークスタート制御方法、溶接装置 Download PDF

Info

Publication number
WO2015186474A1
WO2015186474A1 PCT/JP2015/063496 JP2015063496W WO2015186474A1 WO 2015186474 A1 WO2015186474 A1 WO 2015186474A1 JP 2015063496 W JP2015063496 W JP 2015063496W WO 2015186474 A1 WO2015186474 A1 WO 2015186474A1
Authority
WO
WIPO (PCT)
Prior art keywords
welding
welding current
wire
current
initial
Prior art date
Application number
PCT/JP2015/063496
Other languages
English (en)
French (fr)
Japanese (ja)
Inventor
昇吾 中司
英市 佐藤
敦史 福永
Original Assignee
株式会社神戸製鋼所
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社神戸製鋼所 filed Critical 株式会社神戸製鋼所
Priority to CN201580029891.6A priority Critical patent/CN106413966B/zh
Priority to KR1020167034071A priority patent/KR101960151B1/ko
Publication of WO2015186474A1 publication Critical patent/WO2015186474A1/ja

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K9/00—Arc welding or cutting
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K9/00—Arc welding or cutting
    • B23K9/06—Arrangements or circuits for starting the arc, e.g. by generating ignition voltage, or for stabilising the arc
    • B23K9/067—Starting the arc
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K9/00—Arc welding or cutting
    • B23K9/06—Arrangements or circuits for starting the arc, e.g. by generating ignition voltage, or for stabilising the arc
    • B23K9/073—Stabilising the arc
    • B23K9/0732—Stabilising of the arc current
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K9/00—Arc welding or cutting
    • B23K9/10—Other electric circuits therefor; Protective circuits; Remote controls
    • B23K9/1006—Power supply
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K9/00—Arc welding or cutting
    • B23K9/12—Automatic feeding or moving of electrodes or work for spot or seam welding or cutting
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K9/00—Arc welding or cutting
    • B23K9/16—Arc welding or cutting making use of shielding gas
    • B23K9/173—Arc welding or cutting making use of shielding gas and of a consumable electrode

Definitions

  • the present invention relates to an arc start control method and welding apparatus for consumable electrode arc welding.
  • a short-circuit current is caused to flow by bringing both electrodes into contact with each other while a voltage is applied between the welding wire and the workpiece.
  • the arc is started by fusing the welding wire with an electric current and generating an arc between them.
  • the welding voltage is continuously controlled so as to synchronize the change between the wire feeding speed and the welding voltage, and further the welding voltage associated with the wire feeding speed. Is applied for a predetermined length of time (see Patent Document 4).
  • An object of the present invention is to suppress wire fusing during the arc start period and the occurrence of spatter accompanying the wire fusing.
  • the present invention feeds the welding wire toward the workpiece, and when the fed welding wire comes into contact with the workpiece, a welding current is passed through the welding wire and the workpiece,
  • a welding current is passed through the welding wire and the workpiece
  • an arc start control method for consumable electrode arc welding in which welding is started by generating an arc with a welding current, an initial welding current is supplied as the welding current when the welding wire comes into contact with the workpiece. And a step of supplying a steady welding current larger than the initial welding current as the welding current after a predetermined set period has elapsed after the supply of the initial welding current is started. It is said.
  • the initial welding current is selected from a range of 100 (A) to 300 (A), and the steady welding current is 350 (A).
  • the welding apparatus includes a power supply unit that supplies a welding current to a workpiece via a welding wire, and the welding wire that is fed toward the workpiece.
  • an initial welding current is supplied from the power supply unit as the welding current, and after a predetermined set period has elapsed since the start of the supply of the initial welding current, A current control unit that supplies a steady welding current larger than the initial welding current from the power supply unit.
  • a control device that controls welding work on the workpiece, a determination unit that detects that the initial welding current has flowed through the welding wire and the workpiece, and a power source that drives the power source unit A drive unit, wherein the control unit determines that the initial welding current has flowed through the welding wire and the workpiece by the determination unit, and further, after the predetermined set time has elapsed, A current setting signal for supplying the steady welding current from the power supply unit to the drive unit may be output.
  • FIG. 1 is a diagram showing a schematic configuration of a welding system 1 according to an embodiment of the present invention.
  • the welding system 1 performs welding of the workpiece 200 by a carbon dioxide arc welding method using carbon dioxide gas as a shielding gas among consumable electrode type (melting electrode type) gas shielded arc welding methods.
  • a welding system 1 as an example of a welding apparatus includes a welding torch 10 that welds a workpiece 200 using a welding wire 100, and a robot arm 20 that holds the welding torch 10 and sets the position and orientation of the welding torch 10.
  • the wire feeding device 30 that feeds the welding wire 100 to the welding torch 10, the shield gas supply device 40 that feeds the shielding gas (here, carbon dioxide gas) to the welding torch 10, and the welding wire 100 via the welding torch 10.
  • a power supply device 50 for controlling the welding current, the feeding speed, the welding speed, and the like.
  • the welding system 1 includes a robot control device 60 for controlling the robot arm 20 as an example of a control device for controlling a welding operation to the workpiece 200 by the welding torch 10 and the robot arm 20.
  • the robot controller 60 controls the movement and the speed (welding speed) of the welding torch 10 (welding wire 100) provided in the robot arm 20.
  • the robot control device 60 and the power supply device 50 can be configured to transmit and receive data and control signals.
  • the welding wire 100 used in the welding system 1 may be either a solid wire not containing flux or a flux-cored wire containing flux. Further, the welding current used in the welding system 1 may be either direct current or alternating current.
  • FIG. 2 is a diagram for explaining the configuration of the power supply control means provided in the welding system 1 shown in FIG.
  • a power supply device 50 as a power supply control unit includes a switch 51 that receives an instruction to start welding by an operator, a welding current setting unit 52 that sets a welding current to be supplied to the welding wire 100, and welding using the wire feeding device 30.
  • a feed rate setting unit 53 that sets the feed rate of the wire 100 and a welding current that converts a set value of the welding current set by the welding current setting unit 52 into a set value of the feed rate in the feed rate setting unit 53 / Feed speed conversion unit 54.
  • the power supply device 50 drives the power supply unit 55 based on the setting by the power supply unit 55 that supplies a welding current between the welding torch 10 (welding wire 100) and the workpiece 200 and the welding current setting unit 52.
  • a power supply drive unit 56 and a welding current detection unit 57 that detects a welding current flowing from the welding torch 10 to the workpiece 200 via the welding wire 100 are provided.
  • the power supply device 50 determines that the welding current has flowed based on the detection result of the welding current by the welding current detection unit 57, and outputs a determination result (current detection result).
  • An energization determination unit 59 that determines that the welding current has flowed for a predetermined time based on the determination result by the unit 58 and outputs the determination result (energization determination result) is provided.
  • the welding current setting unit 52 has a function as a current control unit.
  • FIG. 3 is a flowchart for explaining an arc start procedure in welding system 1 of the present embodiment.
  • FIG. 4 is a timing chart for explaining an example of an arc start procedure in the welding system 1 of the present embodiment.
  • the welding start signal S input from the switch 51 to the welding current setting unit 52, the feeding speed setting unit 53, and the power source driving unit 56, and the feeding speed setting unit 53 is connected to the wire feeding device 30.
  • the energization determination unit 59 is welded. Current It shows the relationship between the current judgment signal J to be output to the tough 52.
  • the welding start signal S
  • the welding start signal S, the current detection signal D, and the energization determination signal J are set to “L”, the feeding speed setting signal F and the welding current setting signal C are set to “0”, respectively. It is assumed that it is set. As a result, the feeding speed V and the welding current I are also assumed to be “0”. Furthermore, in the initial state before the arc start, the tip of the welding wire 100 held by the welding torch 10 is arranged at a position away from the workpiece 200 by a predetermined distance.
  • step 10 it is identified whether the welding start signal S input from the switch 51 is “L” or “H” (step 10). If the welding start signal S is “L” in step 10 (NO), the process returns to step 10 and the process is continued.
  • the welding current setting unit 52 changes the welding current setting signal C from “0” to “initial welding current setting value Ca” (Ste 20). Further, the feeding speed setting unit 53 changes the feeding speed setting signal F from “0” to “starting feeding speed setting value Fi” (step 30).
  • step 40 it is determined whether the current detection signal D input from the current determination unit 58 is “L” or “H” (step 40). If the current detection signal D is “L” in step 40 (NO), the process returns to step 40 and the process is continued.
  • the feed speed setting unit 53 changes the feed speed setting signal F from “start feed speed setting value Fi” to “initial feed”. Change to “feed speed set value Fa” (step 50).
  • step 60 it is identified whether the energization determination signal J input from the energization determination unit 59 is “L” or “H” (step 60).
  • the energization determination signal J is “L” in step 60 (NO)
  • the process returns to step 60 and the process is continued.
  • the welding current setting unit 52 changes the welding current setting signal C from “initial welding current setting value Ca” to “steady welding current setting value Cr”.
  • the feeding speed setting unit 53 changes the feeding speed setting signal F from “initial feeding speed setting value Fa” to “steady feeding speed setting value Fr” (step 80). Thereby, the arc start is completed.
  • the welding start signal S is changed from “L” to “H” (YES in step 10).
  • the welding current setting unit 52 changes the welding current setting signal C from “0” to “initial welding current setting value Ca”. 20: 0 ⁇ Ca)
  • the feeding speed setting unit 53 changes the feeding speed setting signal F from “0” to “starting feeding speed setting value Fi” (step 30: 0 ⁇ Fi).
  • the welding current setting signal C is set to the initial welding current setting value Ca. Accordingly, the power supply unit 55 applies a welding voltage corresponding to the initial welding current set value Ca between the welding wire 100 and the workpiece 200. However, at this time, feeding of the welding wire 100 has just started, and the tip of the welding wire 100 has not reached the workpiece 200. Therefore, at this time, the welding current I is maintained at “0”, and the current detection signal D and the energization determination signal J also remain “L”.
  • the feeding speed setting signal F is set to the starting feeding speed setting value Fi, whereby the wire feeding device 30 starts feeding the welding wire 100.
  • the feed speed V does not immediately reach the start feed speed Vi according to the start feed speed set value Fi from 0, it takes time to accelerate, so there is a slight delay (lag). Along with this, the starting feed speed Vi is reached.
  • the initial welding current Ia begins to flow as the welding current I through the welding wire 100 and the workpiece 200 by the set welding voltage. Further, as the initial welding current Ia flows through the welding wire 100, the tip side of the welding wire 100 is melted, and an arc (not shown) is generated between the welding wire 100 and the workpiece 200.
  • the welding current I (initial welding current Ia) has started to flow in this way is detected by the welding current detection unit 57 and the detection result is output to the current determination unit 58.
  • the current determination unit 58 changes the output current detection signal D from “L” to “H” (YES in Step 40).
  • the feeding speed setting unit 53 changes the feeding speed setting signal F from “starting feeding speed setting value Fi” to “initial feeding”. Change to “speed set value Fa” (step 50: Fi ⁇ Fa).
  • the feeding speed setting signal F is set to the initial feeding speed setting value Fa, whereby the wire feeding device 30 starts changing the feeding speed V of the welding wire 100.
  • the feed speed V does not immediately reach the initial feed speed Va corresponding to the initial feed speed set value Fa from the start feed speed Vi, but takes some time for acceleration.
  • the initial feeding speed Va is reached with a lag).
  • the energization determination unit 59 starts measuring time.
  • the energization determination unit 59 changes the energization determination signal J to be output from “L” to “H”. Change (YES in step 60).
  • the welding current setting unit 52 changes the welding current setting signal C from “initial welding current setting value Ca” to “steady welding current setting value Cr”.
  • the feeding speed setting unit 53 changes the feeding speed setting signal F from “initial feeding speed setting value Fa” to “steady feeding speed setting value Fr”.
  • Fa ⁇ Fr Fa ⁇ Fr
  • the welding current setting signal C is set to the steady welding current set value Cr, so that the welding current I flowing through the welding wire 100 shifts from the initial welding current Ia to the steady welding current Ir (Ia ⁇ Ir).
  • the wire feeding device 30 starts changing the feeding speed V of the welding wire 100 by setting the feeding speed setting signal F to the steady feeding speed setting value Fr.
  • the feed speed V does not immediately reach the steady feed speed Vr corresponding to the steady feed speed set value Fr from the initial feed speed Va, but takes some time for acceleration. ) To reach the steady feeding speed Vr. Thereby, the arc start is completed.
  • the welding current setting signal C is instantaneously switched from the initial welding current setting value Ca to the steady welding current setting value Cr, whereby the welding current I is changed to the initial welding current Ia.
  • the method for switching the welding current I from the initial welding current Ia to the steady welding current Ir is not limited to this.
  • FIG. 5 is a timing chart for explaining a modification of the arc start procedure in the welding system 1 of the present embodiment.
  • a slope setting value Cs is provided in the welding current setting signal C when the welding current setting signal C is switched from the initial welding current setting value Ca to the steady welding current setting value Cr.
  • the steady welding current set value Cr may be reached at a fourth time t4 when a predetermined time has elapsed from the third time t3.
  • the welding current I that is the initial welding current Ia at the third time t3 gradually increases at the rising slope Is from the third time t3 to the fourth time t4, and is steady at the fourth time t4.
  • the welding current Ir is reached.
  • the inclination setting value Cs is set in the feeding speed setting signal F along with the setting of the inclination setting value Cs in the welding current setting signal C.
  • the rising slope Vs is also set for the speed V.
  • an initial welding current Ia smaller than the steady welding current Ir is supplied as the welding current I, and the initial welding current Ia is set in advance. After flowing for a predetermined set period T, the initial welding current Ia is switched to the target steady welding current Ir. As a result, it is possible to suppress the fusing (wire fusing) of the welding wire 100 caused by the welding current I immediately after the arc start and the increase in spatter accompanying the wire fusing.
  • the rising slope Is is provided when switching from the initial welding current Ia to the steady welding current Ir.
  • the amount of current supplied to the welding wire 100 temporarily increases. Accordingly, at the time of switching, the red heat of the welding wire 100 increases, so that the welding wire 100 is easily softened and wire fusing is likely to occur. For this reason, the steep red heat of the welding wire 100 can be suppressed by providing the rising slope Is.
  • the steady welding current Ir is set to be high, it is possible to suppress wire fusing and burnback associated therewith, and to suppress an increase in spatter.
  • ⁇ Initial welding current Ia> The period during which the initial welding current Ia flows is provided to stabilize the arc before reaching the steady welding current Ir.
  • the welding current I exceeds 350 (A) the Joule heat generated in the welding wire 100 is increased, wire breakage is likely to occur, and the droplet transfer is also a globule transfer welding in which the droplet immediately below the wire becomes large. As a result, wire fusing is likely to occur and sputtering is likely to increase. Therefore, the initial welding current Ia is preferably 300 (A) or less.
  • the more preferable range of the initial welding current Ia is 100 (A) to 250 ( A).
  • the initial welding current Ia does not include 0 (A).
  • ⁇ Steady welding current Ir> The frequency of wire fusing changes depending on the value of the steady welding current Ir transferred from the initial welding current Ia, and the higher the steady welding current Ir, the more likely the wire fusing due to the red heat effect occurs.
  • the steady welding current Ir is less than 350 (A)
  • the steady welding current Ir exceeds 600 (A)
  • the range of the steady welding current Ir is defined as 350 (A) to 600 (A).
  • the current is 350 (A) to 550 (A).
  • the set period T is set to 20 (msec) or longer, the arc is stabilized while the initial welding current Ia is flowing, and therefore wire fusing at the time of transition from the initial welding current Ia to the steady welding current Ir is further suppressed. It becomes possible. Therefore, the set period T is preferably 20 (msec) or more, and more preferably 50 msec or more, since the arc is more stable. However, even if the setting period T through which the initial welding current Ia flows is excessively long, the efficiency is reduced. Therefore, the setting period T is preferably less than 700 (msec).
  • ⁇ Rising slope Is> When there is a difference between the steady welding current Ir and the initial welding current Ia, the welding wire 100 is easily red-hot, and the larger the current difference between the two is, the easier the welding wire 100 is softened by red heat. Along with this, wire fusing is likely to occur when the initial welding current Ia is shifted to the steady welding current Ir. It is preferable to provide the slope Is. By giving such a rising inclination Is, steep red heat of the wire can be suppressed, and therefore, it is more preferable to provide an inclination of 50 (A / 100 msec) or more. Note that the rising slope Is does not have to be a linear and continuous value (linear function of time) as shown in FIG. 5, and may be a curve or a step.
  • control may be performed to change the welding speed between the period in which the initial welding current Ia is supplied and the period in which the steady welding current Ir is supplied.
  • the welding speed during the period when the initial welding current Ia is supplied is set to be equal to or lower than the welding speed (the welding speed under this condition) during the period when the steady welding current Ir is supplied. This makes it possible to match the welding amount between the period in which the initial welding current Ia is supplied and the period in which the steady welding current Ir is supplied, and the bead shape of the start portion is stabilized.
  • the welding speed during the period in which the steady welding current Ir is supplied (the welding speed under this condition) is 0.
  • the welding speed during the period in which the initial welding current Ia is supplied is controlled to 0.3 (mpm).
  • the steady welding current Ir is controlled to a constant value.
  • the present invention is not limited to this, and it may be a pulse current that repeatedly applies a peak current to the base current at a certain frequency. Absent.
  • the arc start control according to the present embodiment is realized by the function provided in the power supply device 50.
  • the robot control device 60 may be configured to bear a part of the function for realizing the arc start control according to the present embodiment.
  • FIG. 6 is a diagram for explaining another configuration example of the power supply control means provided in the welding system 1 according to the embodiment of the present invention.
  • the switch 51, the welding current setting unit 52, and the energization determination unit 59 provided in the power supply device 50 in the configuration example illustrated in FIG. 2 are provided in the robot control device 60.
  • the power supply device 50 includes a power supply device interface unit 501 for sending and receiving various signals to and from the robot control device 60.
  • the robot control device 60 sends and receives various signals to and from the power supply device 50.
  • a control device interface unit 601 is provided.
  • the functions of the switch 51, the welding current setting unit 52, and the energization determining unit 59 provided in the robot control device 60 shown in FIG. 6 are the same as those provided in the power supply device 50 shown in FIG. Therefore, detailed description thereof is omitted here.
  • the welding start signal S, the welding current setting signal C, and the current detection signal D are exchanged between the power supply device 50 and the robot control device 60.
  • the functions of the welding current setting unit 52 and the feeding speed setting unit 53 in the present embodiment can be realized by an analog circuit or a digital circuit.
  • the welding current setting unit 52 and the feed rate setting unit 53 are realized by a digital circuit, for example, a program describing the output procedure of each control signal at each timing described with reference to FIGS. Is stored in a memory provided in the welding current setting unit 52 or the feeding speed setting unit 53, the function of the present embodiment can be implemented. And each function is implement
  • the inventor uses the welding system 1 shown in FIG. 1 and sets the welding wire 100 type, the diameter of the welding wire 100, the initial welding current Ia and the steady welding current Ir supplied to the welding wire 100, and the set period as welding conditions. Experiments for welding the workpiece 200 with different T and rising slope Is were performed, and the occurrence of arc breakage at the time of arc start was evaluated.
  • the type (wire type) of the welding wire 100 a solid wire not containing flux and a flux-cored wire containing flux were used.
  • the welding wire 100 having a diameter of ⁇ 1.2 (mm) and ⁇ 1.4 (mm) was used.
  • carbon dioxide gas (100% CO 2 ) was used as the shielding gas.
  • a steel plate defined by JIS G3106 SM490A was used as the workpiece 200 to be welded.
  • the initial welding current Ia was selected from the range of 100 (A) to 550 (A).
  • the steady welding current Ir was selected from the range of 250 (A) or more and 550 (A) or less.
  • the set period T was selected from the range of 0 (mesc) to 800 (msec).
  • the rising slope Is was selected from the range of no slope to 1500 (A / 100 msec) or less.
  • Tables 1 to 17 shown below show the relationship between the 336 welding conditions (No. 1 to No. 336) used in this experiment and the obtained evaluation results.
  • the solid wire is represented as “Solid”, and the flux-cored wire is represented as “Cored”.
  • No. 1-No. Reference numeral 50 (Tables 1 to 5) shows comparative examples of the present invention, and the rest show examples of the present invention.
  • the magnitudes of the initial welding current Ia and the steady welding current Ir at this time were 250 (A) to 500 (A).
  • the magnitudes of the initial welding current Ia and the steady welding current Ir at this time were 250 (A) to 500 (A).
  • the initial welding current Ia and the steady welding current Ir at this time were 250 (A) to 550 (A).
  • the initial welding current Ia and the steady welding current Ir at this time were 250 (A) to 550 (A).
  • Table 1 and Table 2 the wire type of the same wire diameter is different, but in Table 1 and Table 3, the wire diameter of the same wire type is different. Further, Table 2 and Table 4 have different wire diameters with the same wire type, and Tables 3 and 4 have different wire types with the same wire diameter.
  • Tables 1 to 4 in the conventional arc start method, since the initial welding current Ia and the steady welding current Ir have the same magnitude, the set period T is inevitably set to “0” and the rising slope Is. Becomes “none”.
  • Table 5 shows a case where a solid wire of ⁇ 1.2 is used as the welding wire 100 and the initial welding current Ia is smaller than the steady welding current Ir (Ia ⁇ Ir). At this time, the magnitude of the steady welding current Ir was 500 (A), and the magnitude of the initial welding current Ia was 100 (A).
  • the wire type and the wire diameter are the same in Table 1 and Table 5, the magnitude relationship between the initial welding current Ia and the steady welding current Ir is different.
  • the set period T was set to 700 (msec) to 800 (msec), and the rising slope Is was set to 1500 (A / 100 msec).
  • Table 6 shows that a ⁇ 1.2 solid wire is used as the welding wire 100, the initial welding current Ia is smaller than the steady welding current Ir (Ia ⁇ Ir), and the initial welding current Ia is fixed to 100 (A). Shows the case.
  • the magnitude of the steady welding current Ir at this time was 350 (A) to 500 (A).
  • Table 7 also shows that a ⁇ 1.2 solid wire is used as the welding wire 100, the initial welding current Ia is smaller than the steady welding current Ir (Ia ⁇ Ir), and the initial welding current Ia is 200 (A). The case of fixing is shown. The magnitude of the steady welding current Ir at this time was 350 (A) to 500 (A).
  • Table 8 uses a ⁇ 1.2 solid wire as the welding wire 100, reduces the initial welding current Ia compared to the steady welding current Ir (Ia ⁇ Ir), and sets the initial welding current Ia to 300 (A). The case of fixing is shown. The magnitude of the steady welding current Ir at this time was 350 (A) to 500 (A).
  • the wire type and the wire diameter are the same, but the magnitude relationship between the initial welding current Ia and the steady welding current Ir is different.
  • the wire type and the wire diameter are the same, but the magnitude of the initial welding current Ia is different.
  • the set period T was set to 0 (msec) to 650 (msec), and the rising slope Is was set to 150 (A / 100 msec) to 1500 (A / 100 msec).
  • the set period T is set to 0 (msec) to 350 (msec), and the rising slope Is is set to 100 (A / 100 msec) to 1000 (A / 100 msec).
  • the setting period T is set to 0 (msec) to 250 (msec), and the rising slope Is is set to 50 (A / 100 msec) to 1000 (A / 100 msec).
  • Table 9 uses a flux-cored wire of ⁇ 1.2 as the welding wire 100, reduces the initial welding current Ia compared to the steady welding current Ir (Ia ⁇ Ir), and fixes the initial welding current Ia to 100 (A). Shows the case.
  • the magnitude of the steady welding current Ir at this time was 350 (A) to 500 (A).
  • Table 10 shows that a flux-cored wire having a diameter of ⁇ 1.2 is used as the welding wire 100, the initial welding current Ia is made smaller than the steady welding current Ir (Ia ⁇ Ir), and the initial welding current Ia is 200 (A). The case where it fixes to is shown. The magnitude of the steady welding current Ir at this time was 350 (A) to 500 (A).
  • Table 11 shows that a flux-cored wire of ⁇ 1.2 is used as the welding wire 100, the initial welding current Ia is made smaller than the steady welding current Ir (Ia ⁇ Ir), and the initial welding current Ia is 300 (A). The case where it fixes to is shown. The magnitude of the steady welding current Ir at this time was 350 (A) to 500 (A).
  • the wire type and the wire diameter are the same in Table 2 and Tables 9 to 11, the magnitude relationship between the initial welding current Ia and the steady welding current Ir is different.
  • Tables 6 to 8 and Tables 9 to 11 have the same wire diameter but different wire types.
  • the magnitude of the initial welding current Ia is different.
  • the set period T was set to 0 (msec) to 250 (msec)
  • the rising slope Is was set to 50 (A / 100 msec) to 1500 (A / 100 msec).
  • the set period T is set to 0 (msec) to 325 (msec), and the rising slope Is is set to 100 (A / 100 msec) to 1500 (A / 100 msec). Further, in Table 11, the set period T is set to 0 (msec) to 175 (msec), and the rising slope Is is set to 50 (A / 100 msec) to 1500 (A / 100 msec).
  • Table 12 uses a ⁇ 1.4 solid wire as the welding wire 100, reduces the initial welding current Ia compared to the steady welding current Ir (Ia ⁇ Ir), and fixes the initial welding current Ia to 100 (A). Shows the case.
  • the magnitude of the steady welding current Ir at this time was 400 (A) to 550 (A).
  • Table 13 shows that a solid wire of ⁇ 1.4 is used as the welding wire 100, the initial welding current Ia is made smaller than the steady welding current Ir (Ia ⁇ Ir), and the initial welding current Ia is 200 (A). The case of fixing is shown. The magnitude of the steady welding current Ir at this time was 400 (A) to 550 (A).
  • Table 14 shows that a solid wire of ⁇ 1.4 is used as the welding wire 100, the initial welding current Ia is made smaller than the steady welding current Ir (Ia ⁇ Ir), and the initial welding current Ia is set to 300 (A). The case of fixing is shown. The magnitude of the steady welding current Ir at this time was 400 (A) to 550 (A).
  • the wire type and the wire diameter are the same, but the magnitude relationship between the initial welding current Ia and the steady welding current Ir is different.
  • the wire diameters of the same wire types are different.
  • the wire type and the wire diameter are the same, but the magnitude of the initial welding current Ia is different.
  • the set period T is set to 0 (msec) to 275 (msec)
  • the rising slope Is is set to 250 (A / 100 msec) to 1500 (A / 100 msec).
  • the set period T is set to 0 (msec) to 225 (msec), and the rising slope Is is set to 200 (A / 100 msec) to 1500 (A / 100 msec). Further, in Table 14, the set period T is set to 0 (msec) to 225 (msec), and the rising slope Is is set to 200 (A / 100 msec) to 1500 (A / 100 msec).
  • Table 15 uses a ⁇ 1.4 flux-cored wire as the welding wire 100, reduces the initial welding current Ia compared to the steady welding current Ir (Ia ⁇ Ir), and fixes the initial welding current Ia to 100 (A). Shows the case.
  • the magnitude of the steady welding current Ir at this time was 400 (A) to 550 (A).
  • Table 16 also shows that a ⁇ 1.4 flux cored wire is used as the welding wire 100, the initial welding current Ia is made smaller than the steady welding current Ir (Ia ⁇ Ir), and the initial welding current Ia is 200 (A). The case where it fixes to is shown. The magnitude of the steady welding current Ir at this time was 400 (A) to 550 (A).
  • Table 17 shows that a ⁇ 1.4 flux cored wire is used as the welding wire 100, the initial welding current Ia is made smaller than the steady welding current Ir (Ia ⁇ Ir), and the initial welding current Ia is 300 (A). The case where it fixes to is shown. The magnitude of the steady welding current Ir at this time was 400 (A) to 550 (A).
  • the wire type and the wire diameter are the same in Table 4 and Tables 15 to 17, the magnitude relationship between the initial welding current Ia and the steady welding current Ir is different.
  • Tables 9 to 11 and Tables 15 to 17 have the same wire type but different wire diameters.
  • the magnitude of the initial welding current Ia is different.
  • the setting period T is set to 0 (msec) to 175 (msec)
  • the rising slope Is is set to 250 (A / 100 msec) to 1500 (A / 100 msec).
  • the set period T is set to 0 (msec) to 125 (msec), and the rising slope Is is set to 250 (A / 100 msec) to 1500 (A / 100 msec). Further, in Table 17, the set period T is set to 0 (msec) to 200 (msec), and the rising slope Is is set to 150 (A / 100 msec) to 1500 (A / 100 msec).
  • the inventor uses the welding system 1 shown in FIG. 1 and sets the welding wire 100 type, the diameter of the welding wire 100, the initial welding current Ia and the steady welding current Ir supplied to the welding wire 100, and the set period as welding conditions.
  • the scattered matter refers to a spatter generated from the start to the end of welding, a wire piece of the welding wire 100 scattered at the time of wire fusing, or the like.
  • a solid wire containing no flux was used as the type (wire type) of the welding wire 100.
  • the diameter of the welding wire 100 was ⁇ 1.2 mm.
  • carbon dioxide gas (100% CO 2 ) was used as the shielding gas.
  • a steel plate defined by JIS G3106 SM490A was used as the workpiece 200 to be welded.
  • the initial welding current Ia was selected from the range of 250 (A) to 500 (A). Further, in this experiment, the steady welding current Ir was selected from the range of 350 (A) to 500 (A). Furthermore, in this experiment, the set period T was selected from the range of 0 (mesc) to 50 (msec). In this experiment, the rising slope Is was selected from the range of no slope to 200 (A / 100 msec) or less.
  • Table 18 and Table 19 below show the relationship between the eight welding conditions (No. 337 to No. 344) used in this experiment and the obtained evaluation results.
  • No. shown in Table 18 The welding conditions of 337 to N0.340 are No. 1 shown in Table 1. 5, no. 7, no. 9, no. 11 corresponds to each.
  • No. The reduction rate of 341 is No. 337 based on the result of No. 337 and shown in Table 19.
  • the reduction rate of 342 is No. shown in Table 18.
  • the reduction rate of 343 is No. shown in Table 18. 339 based on the result of No. 339.
  • the reduction rate of 344 is No. shown in Table 18. Based on 340 results.

Landscapes

  • Engineering & Computer Science (AREA)
  • Physics & Mathematics (AREA)
  • Plasma & Fusion (AREA)
  • Mechanical Engineering (AREA)
  • Arc Welding Control (AREA)
  • Arc Welding In General (AREA)
PCT/JP2015/063496 2014-06-06 2015-05-11 消耗電極式アーク溶接のアークスタート制御方法、溶接装置 WO2015186474A1 (ja)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN201580029891.6A CN106413966B (zh) 2014-06-06 2015-05-11 自耗电极式电弧焊接的起弧控制方法、焊接装置
KR1020167034071A KR101960151B1 (ko) 2014-06-06 2015-05-11 소모 전극식 아크 용접의 아크 스타트 제어 방법, 용접 장치

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2014-117822 2014-06-06
JP2014117822A JP6320851B2 (ja) 2014-06-06 2014-06-06 消耗電極式アーク溶接のアークスタート制御方法、溶接装置

Publications (1)

Publication Number Publication Date
WO2015186474A1 true WO2015186474A1 (ja) 2015-12-10

Family

ID=54766552

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2015/063496 WO2015186474A1 (ja) 2014-06-06 2015-05-11 消耗電極式アーク溶接のアークスタート制御方法、溶接装置

Country Status (4)

Country Link
JP (1) JP6320851B2 (ko)
KR (1) KR101960151B1 (ko)
CN (1) CN106413966B (ko)
WO (1) WO2015186474A1 (ko)

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN107350606B (zh) * 2017-08-23 2019-08-16 唐山松下产业机器有限公司 脉冲控制的方法及电焊机
KR101987967B1 (ko) * 2017-11-23 2019-06-11 한국생산기술연구원 아크용접 제어방법
CN108098117B (zh) * 2018-01-02 2020-04-10 清华大学 Tig电弧辅助的mig焊非接触引弧方法及装置
CN115283785B (zh) * 2022-07-07 2023-11-24 西部超导材料科技股份有限公司 一种var用辅助电极的对焊方法

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008149361A (ja) * 2006-12-20 2008-07-03 Daihen Corp 消耗電極アーク溶接のアークスタート制御方法
WO2009051107A1 (ja) * 2007-10-16 2009-04-23 Daihen Corporation アークスタート制御方法
JP2011025307A (ja) * 2009-06-29 2011-02-10 Daihen Corp アークスタート制御方法
JP2012245547A (ja) * 2011-05-27 2012-12-13 Daihen Corp 溶接装置
WO2013128262A1 (en) * 2012-03-02 2013-09-06 Lincoln Global, Inc. Apparatus for and method of starting arc welding process with pulsing wire before initiation of arcing

Family Cites Families (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5890376A (ja) * 1981-11-24 1983-05-30 Hitachi Seiko Ltd ア−ク溶接装置
JPS5939471A (ja) * 1982-08-30 1984-03-03 Ishikawajima Harima Heavy Ind Co Ltd Ｔｉｇ溶接方法
JPS60108175A (ja) * 1983-11-18 1985-06-13 Osaka Denki Kk 消耗電極式ア−ク溶接方法におけるア−ク起動方法
JPS613667A (ja) * 1984-06-18 1986-01-09 Kobe Steel Ltd ア−ク溶接スタ−ト方法
JP3312713B2 (ja) * 1995-04-28 2002-08-12 オリジン電気株式会社 交流プラズマアーク溶接機
JP2002160059A (ja) * 2000-11-29 2002-06-04 Babcock Hitachi Kk 消耗電極アーク溶接におけるアークスタート方法と溶接装置
JP4490011B2 (ja) * 2001-11-13 2010-06-23 株式会社ダイヘン アークスタート制御方法
JP4312999B2 (ja) 2002-06-27 2009-08-12 株式会社ダイヘン アークスタート制御方法。
JP2005262264A (ja) * 2004-03-18 2005-09-29 Daihen Corp 消耗電極ガスシールドアーク溶接のアークスタート方法
JP4934363B2 (ja) 2006-07-07 2012-05-16 株式会社小松製作所 アーク溶接機の制御方法およびアーク溶接機
CN101356038B (zh) * 2006-10-27 2012-03-28 松下电器产业株式会社 自动焊接装置
JP4946785B2 (ja) 2007-10-22 2012-06-06 パナソニック株式会社 アーク溶接制御方法およびアーク溶接装置
JP2010172953A (ja) 2009-02-02 2010-08-12 Panasonic Corp アークスタート制御方法および溶接ロボットシステム
JP2012206167A (ja) * 2011-03-14 2012-10-25 Daihen Corp 消耗電極アーク溶接のアークスタート制御方法
CN102672307B (zh) * 2011-03-14 2016-03-16 株式会社大亨 消耗电极电弧焊接的起弧控制方法
CN103846528B (zh) * 2014-03-21 2015-12-09 佛山晓世科技服务有限公司 一种环形焊接方法

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008149361A (ja) * 2006-12-20 2008-07-03 Daihen Corp 消耗電極アーク溶接のアークスタート制御方法
WO2009051107A1 (ja) * 2007-10-16 2009-04-23 Daihen Corporation アークスタート制御方法
EP2206574A1 (en) * 2007-10-16 2010-07-14 Daihen Corporation Arc start control method
JP2011025307A (ja) * 2009-06-29 2011-02-10 Daihen Corp アークスタート制御方法
JP2012245547A (ja) * 2011-05-27 2012-12-13 Daihen Corp 溶接装置
WO2013128262A1 (en) * 2012-03-02 2013-09-06 Lincoln Global, Inc. Apparatus for and method of starting arc welding process with pulsing wire before initiation of arcing

Also Published As

Publication number Publication date
KR101960151B1 (ko) 2019-03-19
JP2015229187A (ja) 2015-12-21
KR20160147056A (ko) 2016-12-21
JP6320851B2 (ja) 2018-05-09
CN106413966A (zh) 2017-02-15
CN106413966B (zh) 2022-07-08

Similar Documents

Publication Publication Date Title
JP5400696B2 (ja) 消耗電極式ガスシールドアーク溶接方法および消耗電極式ガスシールドアーク溶接システム
US8373093B2 (en) Method and system to increase heat input to a weld during a short-circuit arc welding process
MX2015003481A (es) Sistema y metodo de soldadura por pulsos de toque leves.
US20170334011A1 (en) Method and system to use combination filler wire feed and high intensity energy source for welding and arc suppression of a variable polarity hot-wire
JP2015522426A (ja) ホットワイヤ処理を開始及び停止させるための方法及びシステム
JP6577879B2 (ja) 短絡アーク溶接工程中に溶接部への入熱を増加させる方法およびシステム
WO2015186474A1 (ja) 消耗電極式アーク溶接のアークスタート制御方法、溶接装置
JP5840921B2 (ja) 消耗電極アーク溶接のくびれ検出制御方法
CN108883486B (zh) 电弧焊接控制方法
JP6524412B2 (ja) アーク溶接制御方法
JP4952315B2 (ja) 複合溶接方法と複合溶接装置
KR20160105319A (ko) 아크 용접 방법, 아크 용접 장치 및 아크 용접용 제어 장치
JP5545996B2 (ja) 消耗電極アーク溶接のくびれ検出制御方法
JP2010214399A (ja) アーク溶接方法
JP6754935B2 (ja) アーク溶接制御方法
JP6994623B2 (ja) アークスタート方法
JP2010194566A (ja) Ｇｍａ溶接方法
WO2020218288A1 (ja) アーク溶接制御方法及びアーク溶接装置
JP5871360B2 (ja) 消耗電極アーク溶接のくびれ検出制御方法
US20220055136A1 (en) Arc welding method and arc welding device
JP4461874B2 (ja) 溶接装置
CN113825580B (zh) 电弧焊接方法以及电弧焊接装置
EP4180163A1 (en) Welding or additive manufacturing system with discontinuous electrode feeding
JP2012071331A (ja) ２電極アーク溶接方法および２電極アーク溶接システム
CN113677471A (zh) 多重焊接工艺

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15803560

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 20167034071

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 15803560

Country of ref document: EP

Kind code of ref document: A1