WO2015141941A1 - Composition de béton modifié par polymère et procédé de réparation de chaussée à l'aide de celle-ci - Google Patents

Composition de béton modifié par polymère et procédé de réparation de chaussée à l'aide de celle-ci Download PDF

Info

Publication number
WO2015141941A1
WO2015141941A1 PCT/KR2015/000729 KR2015000729W WO2015141941A1 WO 2015141941 A1 WO2015141941 A1 WO 2015141941A1 KR 2015000729 W KR2015000729 W KR 2015000729W WO 2015141941 A1 WO2015141941 A1 WO 2015141941A1
Authority
WO
WIPO (PCT)
Prior art keywords
polymer
concrete
concrete composition
weight
strength
Prior art date
Application number
PCT/KR2015/000729
Other languages
English (en)
Korean (ko)
Inventor
허형석
노재호
이태경
정혁진
Original Assignee
(주)제이엔티아이엔씨
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)제이엔티아이엔씨 filed Critical (주)제이엔티아이엔씨
Publication of WO2015141941A1 publication Critical patent/WO2015141941A1/fr

Abstract

La présente invention concerne une composition de béton modifié par polymère pour la réparation d'une chaussée et un procédé de réparation de la chaussée à l'aide de celle-ci. Le procédé de réparation de la chaussée selon la présente invention comprend les étapes consistant à : broyer une surface de chaussée, nécessitant une réparation ; mélanger une émulsion de polymère avec du béton prêt à l'emploi, transférer le mélange vers l'emplacement de la réparation, et mélanger un additif de prise rapide au mélange au niveau de l'emplacement de la réparation pour préparer une composition de béton modifié par polymère ; et étaler la composition de béton modifié par polymère sur la surface de chaussée broyée, ce qui est suivi d'un durcissement. En outre, la composition de béton modifié par polymère utilisée pour réparer et enrober une route comprend un béton prêt à l'emploi, une émulsion de polymère et un additif à prise rapide de résistance élevée. En particulier, l'émulsion de polymère contient un accélérateur de résistance à base d'amine et un tensioactif de type polymère, et l'additif à prise rapide de résistance élevée contient de la silice précipitée.
PCT/KR2015/000729 2014-03-20 2015-01-27 Composition de béton modifié par polymère et procédé de réparation de chaussée à l'aide de celle-ci WO2015141941A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
KR10-2014-0032427 2014-03-20
KR20140032427A KR101507934B1 (ko) 2014-03-20 2014-03-20 폴리머 개질 콘크리트 조성물 및 이를 이용한 도로 포장 보수방법

Publications (1)

Publication Number Publication Date
WO2015141941A1 true WO2015141941A1 (fr) 2015-09-24

Family

ID=53033661

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2015/000729 WO2015141941A1 (fr) 2014-03-20 2015-01-27 Composition de béton modifié par polymère et procédé de réparation de chaussée à l'aide de celle-ci

Country Status (2)

Country Link
KR (1) KR101507934B1 (fr)
WO (1) WO2015141941A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3819273A1 (fr) * 2019-11-07 2021-05-12 Martellus GmbH Additif pulvérulent modifié par polymère pour béton et procédé de fabrication d'un béton

Families Citing this family (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101658573B1 (ko) * 2016-04-01 2016-09-21 한국건설기술연구원 자가다짐형 속경성 경량기포 모르타르 조성물을 이용한 되메움 시공방법
KR101694807B1 (ko) * 2016-08-09 2017-01-11 콘스타주식회사 친환경 그린시멘트를 이용한 내염화물, 내산 콘크리트 단면 보수보강용 모르타르 및 콘크리트 표면 보호 마감재 그리고 이를 이용한 콘크리트를 보수보강하는 방법
KR102042161B1 (ko) * 2017-08-17 2019-12-18 (주)제이엔티아이엔씨 폴리머 개질 콘크리트 조성물 및 이를 이용한 도로 포장 보수 방법
KR102045157B1 (ko) 2018-12-05 2019-11-20 주식회사 빌트존 도로 보수재 및 이를 이용한 도로 보수 시공방법
KR102058674B1 (ko) 2019-08-01 2019-12-23 주식회사 성안이엔씨 개질 아스팔트 콘크리트 조성물 및 이의 시공방법
KR102292413B1 (ko) * 2020-06-17 2021-08-23 건양대학교산학협력단 향상된 마찰 부착강도를 가지는 실리카 나노 입자 코팅 탄소섬유를 포함하는 시멘트 페이스트 조성물
CN115650658A (zh) * 2022-09-19 2023-01-31 福建省地恒建材有限责任公司 一种混凝土路面快速修复材料

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH06234558A (ja) * 1993-01-13 1994-08-23 Rhone Poulenc Chim セメント用組成物及びこれらの組成物から得られたセメント
JP2501591B2 (ja) * 1987-08-13 1996-05-29 電気化学工業株式会社 モルタル・コンクリ−トの養生用封緘剤
JP2004300008A (ja) * 2003-04-01 2004-10-28 Denki Kagaku Kogyo Kk 吹付け用急硬剤、急硬性セメントコンクリート、及びそれを用いた吹付け工法
JP2006044960A (ja) * 2004-07-30 2006-02-16 Ube Ind Ltd 湿潤接着性が向上した水硬性組成物
KR20110090050A (ko) * 2010-02-02 2011-08-10 이풍희 초속경 아크릴 폴리머 콘크리트를 이용한 콘크리트 포장의 재포장 공법

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2501591B2 (ja) * 1987-08-13 1996-05-29 電気化学工業株式会社 モルタル・コンクリ−トの養生用封緘剤
JPH06234558A (ja) * 1993-01-13 1994-08-23 Rhone Poulenc Chim セメント用組成物及びこれらの組成物から得られたセメント
JP2004300008A (ja) * 2003-04-01 2004-10-28 Denki Kagaku Kogyo Kk 吹付け用急硬剤、急硬性セメントコンクリート、及びそれを用いた吹付け工法
JP2006044960A (ja) * 2004-07-30 2006-02-16 Ube Ind Ltd 湿潤接着性が向上した水硬性組成物
KR20110090050A (ko) * 2010-02-02 2011-08-10 이풍희 초속경 아크릴 폴리머 콘크리트를 이용한 콘크리트 포장의 재포장 공법

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3819273A1 (fr) * 2019-11-07 2021-05-12 Martellus GmbH Additif pulvérulent modifié par polymère pour béton et procédé de fabrication d'un béton
WO2021089401A1 (fr) * 2019-11-07 2021-05-14 Martellus Gmbh Additif pour béton pulvérulent modifié par polymère et procédé pour la production d'un béton

Also Published As

Publication number Publication date
KR101507934B1 (ko) 2015-04-08

Similar Documents

Publication Publication Date Title
WO2015141941A1 (fr) Composition de béton modifié par polymère et procédé de réparation de chaussée à l'aide de celle-ci
CN111533517B (zh) 一种高速铁路混凝土轨道板用快速修补砂浆及其制备方法
CN104030644B (zh) 一种用于高速铁路板式无砟轨道充填层的聚合物水泥砂浆
KR101465446B1 (ko) 내염성 초속경 콘크리트 조성물 및 이를 이용한 교면 또는 포장면 보수방법
CN103073253B (zh) 板式无砟轨道充填层快速抢修砂浆及其制备方法和使用方法
US11981602B2 (en) High-toughness geopolymer grouting material modified by ultra-high weight fibers and emulsified asphalt, preparation and application
WO2016111438A1 (fr) Composition de béton bitumineux semi-rigide à froid recyclé et son procédé de préparation
CN105271890A (zh) 一种预应力孔道压浆剂及其制备和使用方法
KR100755039B1 (ko) 초속경형 고강도 콘크리트 조성물
KR101377475B1 (ko) 마사토와 마사토로부터 모래 분리에 따라 발생되는 슬러지를 이용한 황토 블록의 제조방법
CN101585688A (zh) 一种高速公路及城市道路的混凝土路面快速维修材料
Ruan et al. Effects of red mud on properties of magnesium phosphate cement-based grouting material and its bonding mechanism with coal rock
Chen et al. Effect of early strength agent on the hydration of geopolymer mortar at low temperatures
Zhang et al. Experimental research on mechanical properties and microstructure of magnesium phosphate cement-based high-strength concrete
Han et al. Experimental study on the properties of a polymer-modified superfine cementitious composite material for waterproofing and plugging
WO2015060666A1 (fr) Composition de mortier à haute résistance pour la réparation de routes, et son procédé de préparation
WO2024066530A1 (fr) Matériau de réparation de chaussée préparé à partir de déchets solides industriels et utilisé pour la construction d'hiver
JP2004210557A (ja) グラウト組成物
Wang et al. Mechanical Properties Improvement Mechanism of Silica Fume‐Modified Ultrafine Cement Used to Repair Pavement Microcracks
Li et al. Formulation and properties of a new cleaner double liquid alkali-activated grouting material
JP2013139348A (ja) 速硬性組成物、モルタルおよびコンクリート
KR102549198B1 (ko) 폐유리 또는 파유리를 이용한 고강도 시멘트 콘크리트 모르타르 조성물 및 이를 이용한 콘크리트제품 및 그 제조방법
WO2015060667A1 (fr) Composition de mortier à durcissement rapide pour la réparation de routes, et son procédé de préparation
JP2015127286A (ja) 速硬性膨張セメント混練物の製造方法
CN111620655B (zh) 一种聚合物砂浆及其制备方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15764935

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 15764935

Country of ref document: EP

Kind code of ref document: A1