WO2015032662A1 - Procédé de production de particules de dioxyde d'étain - Google Patents

Procédé de production de particules de dioxyde d'étain Download PDF

Info

Publication number
WO2015032662A1
WO2015032662A1 PCT/EP2014/068133 EP2014068133W WO2015032662A1 WO 2015032662 A1 WO2015032662 A1 WO 2015032662A1 EP 2014068133 W EP2014068133 W EP 2014068133W WO 2015032662 A1 WO2015032662 A1 WO 2015032662A1
Authority
WO
WIPO (PCT)
Prior art keywords
tin
dioxide particles
tin dioxide
range
carbon
Prior art date
Application number
PCT/EP2014/068133
Other languages
English (en)
Inventor
Heino Sommer
Christoph Weidmann
Torsten Brezesinski
Jürgen Janek
Original Assignee
Basf Se
Karlsruher Institut Für Technologie (Kit)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Basf Se, Karlsruher Institut Für Technologie (Kit) filed Critical Basf Se
Publication of WO2015032662A1 publication Critical patent/WO2015032662A1/fr

Abstract

L'invention concerne un procédé pour produire des particules de dioxyde d'étain comprenant l'élément carbone, des particules de dioxyde d'étain comprenant l'élément carbone qui peuvent être obtenues ou sont obtenues au moyen du procédé selon l'invention, des électrodes conçues pour une cellule électrochimique comprenant lesdites particules de dioxyde d'étain qui comportent l'élément carbone, ainsi que des cellules électrochimiques comportant lesdites électrodes.
PCT/EP2014/068133 2013-09-06 2014-08-27 Procédé de production de particules de dioxyde d'étain WO2015032662A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP13183365 2013-09-06
EP13183365.9 2013-09-06

Publications (1)

Publication Number Publication Date
WO2015032662A1 true WO2015032662A1 (fr) 2015-03-12

Family

ID=49117735

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2014/068133 WO2015032662A1 (fr) 2013-09-06 2014-08-27 Procédé de production de particules de dioxyde d'étain

Country Status (1)

Country Link
WO (1) WO2015032662A1 (fr)

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20110104553A1 (en) * 2009-10-29 2011-05-05 Uchicago Argonne, Llc Autogenic pressure reactions for battery materials manufacture
WO2013042034A1 (fr) * 2011-09-19 2013-03-28 Basf Se Matériaux composites polymères contenant de l'oxyde d'étain

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20110104553A1 (en) * 2009-10-29 2011-05-05 Uchicago Argonne, Llc Autogenic pressure reactions for battery materials manufacture
WO2013042034A1 (fr) * 2011-09-19 2013-03-28 Basf Se Matériaux composites polymères contenant de l'oxyde d'étain

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
J. BA ET AL: "Non-aqueous Synthesis of Tin Oxide Nanocrystals and Their Assembly into Ordered Porous Mesostructures", ADVANCED MATERIALS, vol. 17, no. 20, 17 October 2005 (2005-10-17), pages 2509 - 2512, XP055161835, ISSN: 0935-9648, DOI: 10.1002/adma.200501018 *

Similar Documents

Publication Publication Date Title
JP5225615B2 (ja) 負極活物質としてＴｉＯ２−Ｂを含むリチウムイオン蓄電池
US9577246B2 (en) Negative electrode active material, negative electrode for nonaqueous electrolyte secondary battery, and nonaqueous electrolyte secondary battery
US8932758B2 (en) Electrode active material, nonaqueous secondary battery electrode, and nonaqueous secondary battery
JP2008282819A (ja) 非水電解質二次電池用負極活物質の製造方法およびこれによって得られる非水電解質電池用負極活物質
JP6176510B2 (ja) シリコン材料及び二次電池の負極
JPWO2015182116A1 (ja) ナノシリコン材料とその製造方法及び二次電池の負極
JP5992198B2 (ja) 非水電解質二次電池用負極活物質の製造方法およびこれによって得られる非水電解質電池用負極活物質
US6291100B1 (en) Electrode composition comprising doped tungsten oxides and electrochemical cell comprising same
US20150171426A1 (en) POROUS AMORPHOUS GeOx AND ITS APPLICATION AS AN ANODE MATERIAL IN LI-ION BATTERIES
TW201308733A (zh) 用於鋰二次電池之正極活性物質其製造方法
JP5235444B2 (ja) 複合体負極活物質、その製造方法及びそれを採用した負極とリチウム電池
JP5858297B2 (ja) 負極活物質及び蓄電装置
US20200403224A1 (en) Lithium molybdate anode material
US9831494B2 (en) Negative-electrode active material and electric storage apparatus
EP3244472A1 (fr) Composites comprenant des microsphères creuses d'oxyde de vanadium pour des cellules lithium-soufre
JP6065678B2 (ja) 負極活物質とその製造方法及び蓄電装置
EP3312909A1 (fr) Composites électroactives comprenant des particules de silicium, des nanoparticles metalliques et des nanostructures de carbone.
JP2023526984A (ja) 新規の固体硫化物電解質
KR20120100740A (ko) 리튬 이차 전지용 양극 활물질, 이의 제조 방법 및 이를 포함하는 리튬 이차 전지
JP2000113877A (ja) リチウム二次電池
JP6176511B2 (ja) シリコン材料及び二次電池の負極
JP6299154B2 (ja) 負極活物質及び蓄電装置
WO2015032662A1 (fr) Procédé de production de particules de dioxyde d'étain
KR102228749B1 (ko) 리튬 이차 전지용 양극 활물질, 이의 제조 방법 및 이를 포함하는 리튬 이차 전지
JP7480096B2 (ja) 活物質、電極、二次電池、電池パック、及び車両

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14761969

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14761969

Country of ref document: EP

Kind code of ref document: A1