WO2014208758A1 - Matériau protecteur pour cellule solaire - Google Patents
Matériau protecteur pour cellule solaire Download PDFInfo
- Publication number
- WO2014208758A1 WO2014208758A1 PCT/JP2014/067284 JP2014067284W WO2014208758A1 WO 2014208758 A1 WO2014208758 A1 WO 2014208758A1 JP 2014067284 W JP2014067284 W JP 2014067284W WO 2014208758 A1 WO2014208758 A1 WO 2014208758A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- protective material
- film
- solar cell
- layer
- weather
- Prior art date
Abstract
L'invention concerne un matériau pour une cellule solaire, ledit matériau protecteur étant obtenu en superposant en tant que couches constitutives de matériau protecteur (P) au moins un film résistant aux intempéries, une couche de résine, et un film résistant à l'humidité ayant une couche inorganique sur au moins une face d'un substrat et ayant un taux de transmission de vapeur d'eau inférieur ou égal à 0,1 g/m2, la couche de résine étant formée d'une composition de résine thermoplastique contenant une résine à base d'éthylène, et le rapport (WP/WA) entre la largeur maximale WP des couches constitutives de matériau protecteur (P) autres que le film résistant aux intempéries et la largeur (WA) du film résistant aux intempéries est inférieur à 1.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2015524149A JPWO2014208758A1 (ja) | 2013-06-28 | 2014-06-27 | 太陽電池用保護材 |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2013-137581 | 2013-06-28 | ||
JP2013137581 | 2013-06-28 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2014208758A1 true WO2014208758A1 (fr) | 2014-12-31 |
Family
ID=52142080
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2014/067284 WO2014208758A1 (fr) | 2013-06-28 | 2014-06-27 | Matériau protecteur pour cellule solaire |
Country Status (2)
Country | Link |
---|---|
JP (1) | JPWO2014208758A1 (fr) |
WO (1) | WO2014208758A1 (fr) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2021050515A (ja) * | 2019-09-25 | 2021-04-01 | 株式会社エフコンサルタント | 被膜積層体 |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20080289682A1 (en) * | 2007-02-27 | 2008-11-27 | Adriani Paul M | Structures for Low Cost, Reliable Solar Modules |
JP2011254073A (ja) * | 2010-05-06 | 2011-12-15 | Mitsubishi Chemicals Corp | ロールスクリーンシステム |
JP2012204458A (ja) * | 2011-03-24 | 2012-10-22 | Fujifilm Corp | 太陽電池モジュールの製造方法 |
-
2014
- 2014-06-27 WO PCT/JP2014/067284 patent/WO2014208758A1/fr active Application Filing
- 2014-06-27 JP JP2015524149A patent/JPWO2014208758A1/ja active Pending
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20080289682A1 (en) * | 2007-02-27 | 2008-11-27 | Adriani Paul M | Structures for Low Cost, Reliable Solar Modules |
JP2011254073A (ja) * | 2010-05-06 | 2011-12-15 | Mitsubishi Chemicals Corp | ロールスクリーンシステム |
JP2012204458A (ja) * | 2011-03-24 | 2012-10-22 | Fujifilm Corp | 太陽電池モジュールの製造方法 |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2021050515A (ja) * | 2019-09-25 | 2021-04-01 | 株式会社エフコンサルタント | 被膜積層体 |
JP7388858B2 (ja) | 2019-09-25 | 2023-11-29 | 株式会社エフコンサルタント | 被膜積層体 |
Also Published As
Publication number | Publication date |
---|---|
JPWO2014208758A1 (ja) | 2017-02-23 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP2800148B1 (fr) | Feuille protectrice | |
JP5623325B2 (ja) | 太陽電池用保護シートおよびその製造方法、ならびに太陽電池モジュール | |
WO2012053475A1 (fr) | Feuille de protection pour pile solaire, son procédé de fabrication et module de pile solaire | |
WO2013118570A1 (fr) | Feuille protectrice pour photopile et module solaire | |
WO2012105512A1 (fr) | Matière de protection de surface pour cellule solaire, et module de cellule solaire produit utilisant cette matière | |
WO2013100108A1 (fr) | Matériau protecteur pour cellules solaires | |
WO2013121838A1 (fr) | Feuille protectrice pour cellule solaire, son procédé de fabrication et module de cellule solaire | |
JP2014041900A (ja) | 太陽電池用保護材及び太陽電池 | |
WO2014208758A1 (fr) | Matériau protecteur pour cellule solaire | |
WO2014208759A1 (fr) | Matériau protecteur de cellule solaire | |
JP5474171B1 (ja) | 太陽電池用保護材 | |
JP2011204880A (ja) | 太陽電池モジュール用保護シート及び太陽電池モジュール | |
JP6442879B2 (ja) | 積層防湿フィルム | |
JP2012209375A (ja) | 太陽電池用封止材・表面保護材積層体 | |
JP2013077818A (ja) | 太陽電池用保護材 | |
JP5449312B2 (ja) | 太陽電池用保護材 | |
JP2012158154A (ja) | 透明積層防湿フィルム | |
JP2012176608A (ja) | 太陽電池用表面保護材及びそれを用いて作製された太陽電池モジュール | |
JP5696172B2 (ja) | 太陽電池用保護シートおよびその製造方法、ならびに太陽電池モジュール | |
JP2013084929A (ja) | 太陽電池用保護材 | |
JP2012209371A (ja) | 太陽電池用表面保護シート | |
JP2012160550A (ja) | 太陽電池用表面保護材及びそれを用いて作製された太陽電池モジュール | |
JP2012176609A (ja) | 太陽電池用表面保護材及びそれを用いて作製された太陽電池モジュール | |
JP2012209372A (ja) | 太陽電池用表面保護シート・封止材積層体 | |
JP2013214555A (ja) | 太陽電池用保護材 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 14818086 Country of ref document: EP Kind code of ref document: A1 |
|
ENP | Entry into the national phase |
Ref document number: 2015524149 Country of ref document: JP Kind code of ref document: A |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 14818086 Country of ref document: EP Kind code of ref document: A1 |