Classifications

• • G—PHYSICS
  • G02—OPTICS
  • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
  • G02B3/00—Simple or compound lenses
  • G02B3/12—Fluid-filled or evacuated lenses
  • G02B3/14—Fluid-filled or evacuated lenses of variable focal length
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29D—PRODUCING PARTICULAR ARTICLES FROM PLASTICS OR FROM SUBSTANCES IN A PLASTIC STATE
  • B29D11/00—Producing optical elements, e.g. lenses or prisms
  • B29D11/00009—Production of simple or compound lenses
• • G—PHYSICS
  • G02—OPTICS
  • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
  • G02B1/00—Optical elements characterised by the material of which they are made; Optical coatings for optical elements
  • G02B1/04—Optical elements characterised by the material of which they are made; Optical coatings for optical elements made of organic materials, e.g. plastics
  • G02B1/041—Lenses
• • G—PHYSICS
  • G02—OPTICS
  • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
  • G02B1/00—Optical elements characterised by the material of which they are made; Optical coatings for optical elements
  • G02B1/06—Optical elements characterised by the material of which they are made; Optical coatings for optical elements made of fluids in transparent cells
• • G—PHYSICS
  • G02—OPTICS
  • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
  • G02B1/00—Optical elements characterised by the material of which they are made; Optical coatings for optical elements
  • G02B1/10—Optical coatings produced by application to, or surface treatment of, optical elements
• • G—PHYSICS
  • G02—OPTICS
  • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
  • G02B26/00—Optical devices or arrangements for the control of light using movable or deformable optical elements
  • G02B26/004—Optical devices or arrangements for the control of light using movable or deformable optical elements based on a displacement or a deformation of a fluid
• • G—PHYSICS
  • G02—OPTICS
  • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
  • G02B27/00—Optical systems or apparatus not provided for by any of the groups G02B1/00 - G02B26/00, G02B30/00
  • G02B27/28—Optical systems or apparatus not provided for by any of the groups G02B1/00 - G02B26/00, G02B30/00 for polarising
• • G—PHYSICS
  • G02—OPTICS
  • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
  • G02B26/00—Optical devices or arrangements for the control of light using movable or deformable optical elements
  • G02B26/004—Optical devices or arrangements for the control of light using movable or deformable optical elements based on a displacement or a deformation of a fluid
  • G02B26/005—Optical devices or arrangements for the control of light using movable or deformable optical elements based on a displacement or a deformation of a fluid based on electrowetting
• • G—PHYSICS
  • G02—OPTICS
  • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
  • G02B3/00—Simple or compound lenses
  • G02B3/12—Fluid-filled or evacuated lenses

Definitions

• the present invention relates to transparent optical device elements comprising a deformable lens body.
• the present invention relates to polymers or pre-polymer mixtures for preparing such a deformable lens body.
• the present invention does also relate to the use of polymer or pre-polymer mixture for preparing transparent optical device elements, such as adjustable optical lenses.
• the present invention does also relate to a method of changing the refractive index (RI) of a deformable lens body and to a method of manufacturing of transparent optical device elements.
• US 20110038625 discloses a rather complex adaptive lens comprising at least an actuator and a lens, the lens being mechanically coupled to the actuator so that energization of the actuator adjusts a focal point of the lens.
• the actuator may comprise a multilayer stack of electromechanical polymer (EMP) layers, having electrodes configured to apply an electric field across each EMP layer.
• EMP electromechanical polymer
• the actuator may be operable to move and/or deform a lens, so as to adjust the focus properties of the lens.
• the actuator has an annular shape, supporting a lens within the inner radius of the annulus.
• the actuator may be mechanically coupled to a surface of a deformable lens, either directly or through another element of a lens structure.
• This adjustable lens assembly seems to be rather complex in that it comprises several moving parts consisting of different materials.
• the lens body or lens structure itself is said to be prepared by molding using a mold, where it can be cured. When cured, the lens structure is removed from the mold and an actuator is mounted on one or both sides of the lens structure.
• the fixing agent must have a refractive index matching the refracting index of the lens to avoid optical disturbances.
• the fixing agent must be compatible with the other parts and materials of the lens assembly, both chemically, optically and mechanically. It is also necessary to retain the elasticity and flexibility of the lens body and other parts of the adjustable lens assembly, and accordingly the fixing agent must be just as soft and flexible as the other flexible parts of the assembly. If such requirements are not met, tensions will rise between the different parts of a lens assembly, e.g. between a fixing agent, a glass surface, an actuator and/or a lens body, i.e. between all parts having an undesired stiffness.
• WO 2010/005315 discloses a method and arrangement for reducing thermal effects in compact adjustable optical lenses.
• the compact adjustable lens according to WO 2010/005315 is considered to be an especially interesting lens.
• This adjustable optical lens comprises a deformable lens body confined in a cavity bounded by a flexible glass surface supported by rigid sidewalls and an attached transparent bottom plate. Furthermore, there is an opening between the sidewalls and the edges of the transparent bottom plate and a corresponding opening around the lens body and the sidewalls. Additionally actuators are arranged on the flexible glass surface to deform the lens body, thereby enabling adjustments of focal length.
• the above mentioned lens design requires a flexible polymer that is partially surrounded by air (no physical contact with the sidewalls of the cavity).
• a further problem faced when manufacturing such a lens is how to shape the deformable polymer in such a (flat) cylindrical shape.
• adjustable optical lenses There are many issues to be solved associated with adjustable optical lenses and their manufacturing wherein a soft polymer is deformed by an actuator layer structure that is located adjacent to a surface of the soft polymer constituting the lens body. Especially, the manufactured lens must satisfy certain strict
• an isotropic lens body will have homogeneous optical properties, such as refraction and
• the optical and mechanical properties remain relatively stable at the temperatures the device, e.g. a camera, will be exposed to during operation. If changes occur over a temperature range, it is important that there are no abrupt, irreversible or unpredictable changes. Thus, not only must the lens including the polymer body withstand high temperatures during manufacturing but it must also function at much lower temperatures as the lens may be operated at temperatures ranging from -25 to 80°C, or wider.
• a transparent optical device element comprising a deformable lens body having an improved mechanical stability would be advantageous, and in particular a deformable lens body having a high refractive index, an optimal degree of stiffness and sheer modulus would be advantageous.
• a further object of the present invention is to avoid the use of undesired components such as fixing agents by providing a lens body which in itself has adhesive properties making the use of any kind of fixing agents unnecessary.
• Still another object of the invention is to provide a process for manufacturing adjustable optical lens assemblies.
• a transparent optical device element comprising : at least one deformable lens body; a bendable transparent cover member attached to a surface of the at least one deformable lens body thereby providing mechanical stability to the at least one deformable lens body; - actuators for shaping the bendable transparent cover member into a desired shape, the actuators located on a top surface of the bendable transparent cover member, the desired shape defined by a disposition pattern of the actuators and by a magnitude of respective applied voltages onto the disposition pattern of actuators, wherein the at least one deformable lens body has
• the absorbance in the visible range is less than 10% per millimeter thickness of the deformable lens body
• the deformable lens body comprises a polymer network of cross-linked or partly cross-linked polymers; and further comprises a miscible oil or combination of oils, thereby increasing the refractive index of the polymer network of cross- linked or partly cross-linked polymers.
• the invention is particularly, but not exclusively, advantageous for obtaining a transparent optical device element having the desired mechanical stability.
• the polymer network of cross-linked or partly cross- linked polymers has to have a certain degree of mechanical stability.
• mechanical stability is provided within the chemical structure of the polymer network by introducing polymers or pre-polymers having a desired chemical composition and thus the chemical structure, once cured, provides a desired degree of mechanical stability.
• the polymer structure in itself provides the desired mechanical stability to the lens body.
• the solution of the invention stems from the use of a polymer network of cross- linked or partly cross-linked polymers that do not have a specific mechanical stability but where the desired mechanical stability of the transparent optical element is provided through the presence of a bendable transparent cover member.
• the solution of the invention is to combine a deformable lens body and a bendable transparent cover member, the combination of which provides the desired mechanical stability.
• the actuators have the function of shaping the bendable transparent cover member into a desired shape.
• the bendable transparent cover member is bent into the desired shape due to the pattern and disposition of the actuators located on a top surface of said bendable transparent cover member and by the magnitude of respective applied voltages.
• the invention relates to a transparent optical device element where the response to the actuator is optimized so as to provide a fast response upon minimum stimulus, such as a minimum applied voltage and power consumption .
• the autofocus system When taking photos with a modern digital camera, the autofocus system will normally operate by a repetitive loop of changing the focus point and analysing the image sharpness, until the desired area of a picture is in focus. It is also a growing trend to provide image manipulation functions based on a series of images being for example interpolated into one picture.
• the relevant time scale in this process is the so called frame rate of the camera, i.e. the number of pictures acquired per second .
• frame rate of the camera i.e. the number of pictures acquired per second .
• response time for the actuator of less than 10 milliseconds is preferred, even a response time lower than 1 millisecond is beneficial .
• low power consumption may be required in order to not wear out the battery too fast.
• An actuator that dissipates less than 1 mW is considered to be a low power actuator having a minimum power consumption.
• the bendable transparent cover member may be made out of a transparent material providing a mechanical and structural reinforcement of the deformable lens body attached to the bendable transparent cover member.
• the bendable transparent cover member may be made from a transparent material selected from the group of glasses, inorganic oxides and rigid polymeric materials such as carbonates, acrylates, and epoxies.
• the bendable transparent cover member is made of glass and has a thickness in the range of 10 to 50 ⁇ " ⁇ .
• the lens body With respect to mechanical properties such as the mechanical stability, the lens body must have a desired stiffness/softness for the lens to easily shift its focus. Stiffness is the rigidity of an object the extent to which it resists deformation in response to an applied force. In elastic or viscoelastic material hardness in the elastic range is known as stiffness. Hardness is a measure of how resistant solid matter is to various kinds of permanent shape change when a force is applied . Hardness is associated with parameters such as ductility, elastic stiffness, plasticity, strain, strength, toughness, viscoelasticity, and viscosity. If the lens body is too stiff, the degree of bending of the transparent cover member that is provided by the actuator will be reduced. A certain reduction can be acceptable.
• the solution of the invention is the use of a deformable lens body that is of solid matter.
• a solid matter means in this context that it has a non-zero plastic or elastic modulus, meaning that it will resist deformation when exposed to a given stress. Having a low or even zero plastic deformation, and for the relevant degrees of deformation an elastic behaviour is desirable.
• Polymeric materials are commonly viscoelastic, that is, they inhibit both elastic and viscous behaviour when exposed to stress. Viscous materials resist shear flow and strain linearly with time when a stress is applied. Elastic materials strain instantaneously when stretched and just as quickly return to their original state once the stress is removed. Viscoelastic materials have elements of both of these properties and, as such, exhibit time-dependent strain.
• the invention uses elastomeric materials, made up of a physically or chemically cross linked three dimensional network of polymer molecules that are exhibiting high degree of mobility under deformation. Elastomers typically have a glass transition
• Viscoelasticity may be studied by using dynamic mechanical analysis, for example applying a small oscillatory stress and measuring the resulting strain .
• Purely elastic materials have stress and strain in phase, so that the response of one caused by the other is immediate.
• strain lags stress by a 90 degree phase lag .
• Viscoelastic materials exhibit behaviour somewhere in the middle of these two types of material, exhibiting some lag in strain.
• Complex Dynamic modulus is the ratio of stress to strain under vibratory conditions e.g . calculated from data obtained from either free or forced vibration tests, in shear, i.e. shear modulus G and can be used to represent the relations between the oscillating stress and strain :
• G' is the storage modulus that is dependent on the elastic modulus, such as the Young's modulus, while G" is the loss modulus that is more heavily dependent on the viscosity variable ⁇ .
• Viscosity ⁇ is a measure of the resistance of a fluid which is being deformed by either shear stress or tensile stress.
• Young's modulus also known as the tensile modulus or called the elastic modulus, being the most common elastic modulus, is a measure of the stiffness of an elastic material . It is defined as the ratio of the uniaxial stress over the uniaxial strain in the range of stress. In solid mechanics, the slope of the stress-strain curve at any point is called the tangent modulus. The tangent modulus of the initial, linear portion of a stress-strain curve is called Young's modulus (E) . It can be
• the deformable lens body must be adjustable for changing focus of the lens, it must have the ability to return from a deformed state (temporary shape) induced by an external stimulus (trigger) to its original (permanent) shape. Thus, the deformable lens body must not be permanently deformed when under stress or strain.
• the shear modulus G is often used as a relevant measure.
• the shear modulus is the mathematical description of an object or substance's tendency to be deformed when a shear force is applied to it and is defined as the ratio of shear stress to the shear strain.
• the stiffness/softness of the lens body may be defined by G.
• shear modulus which is lower than 100 kPa. It is even more desirable to have a shear modulus lower than 50 kPa, or even as low as 10 kPa.
• the deformable lens body in an adjustable autofocus camera lens, there will be a minimum required stiffness or modulus.
• the device must withstand significant deformation due to gravity and gravitational forces that might occur during the working life of the autofocus camera.
• the inventors have observed that a shear modulus of larger than 100 Pa is required.
• the elastic modulus should be above a desired minimum value of 300 Pa, thereby avoiding deformation due to gravitational forces in normal operation of the transparent optical device element.
• the preferred range of shear modulus between 100 Pa and 100 KPa gives a preferred range of the elastic modulus between 300 Pa and 300 KPa.
• the at least one deformable lens body has a shear modulus of less than 100 KPa.
• a shear modulus (measured at 1-lOOHz in an oscillating parallel plate rheometer) of below 100 kPa can be achieved in several ways:
• the former of these solutions has the disadvantage of making elastomeric materials that exhibit low storage modulus, but a relatively high loss modulus, thus giving a viscoelastic material with a rather slow behavior when exposed to rapidly changing stress.
• the solution of the invention decreases the shear modulus by adding oils to the polymer network. Such oils are often also called plasticizers.
• the solution of the invention differs from others as a shear modulus lower than 100 Kpa is achieved by introducing a low molecular weight oil or swelling agent (Mw ⁇ 10 000) that is miscible with and not covalently bound in the network (0 to 90 weight% is in principle feasible). In this way the storage modulus is reduced while the loss modulus is not substantially increased thus leading to polymer network including oil or combination of oils having the desired degree of softness to be used as lens body, while at the same time retaining a quick response to rapidly changing stresses.
• the desired value of shear modulus allows for use of the invention as a lens body, such as a lens body for a camera, having a quick reaction time upon application of rapidly imposed small forces.
• this effect is achieved by introducing oil or a combination of oils into a polymer network, so as to achieve the desired value of shear modulus, thus providing a lens body with very fast response to application of very small force.
• the solution of the invention thus leads to a polymer network including oils having both a low shear modulus in general, or a low dynamic storage modulus, but at the same time having an even lower loss modulus so as to have a fast response to a rapidly changing external stimuli or stress.
• the low modulus may create a problem in using the polymer network as a lens body as such.
• a lens body needs to have degree of hardness or stiffness so as to be able to mechanically withstand the use as a lens.
• the lens must withstand forces applied both during the production or assembly process, when integrating the lens in a camera, and during normal operation of the device.
• the solution of the invention is thus to provide an optical device element that further comprises a bendable transparent cover member attached to a surface of at least one deformable lens body.
• the bendable transparent cover member will give mechanical rigidity and stability towards damage both due to deformations, impact, handling, scratching and dust particles.
• the solution of the invention solves also the problem of how to use a polymer network lacking of mechanical properties needed to be used as a lens body, by providing the necessary mechanical stability of the polymer through the use of a bendable transparent cover member, such as a plate, such as a glass or a polymer plate, which is attached to a surface of the deformable lens body.
• a bendable transparent cover member such as a plate, such as a glass or a polymer plate
• the invention thus provides a lens body having an optimal response to the application of forces changing its shape due to its composition.
• This composition would not be able to be used as a lens body due to its low modulus as it does not fulfill the requirements of mechanical stability for a lens.
• this problem has been solved by providing a support for the lens body through a bendable transparent cover member that provide the mechanical stability to the lens body that is located on its surface.
• the invention thus provides, according to one embodiment a lens body that should be clear and highly transparent, be isotropic, be very soft with a shear modulus (G) of less than 100 kPa, be thermally stable and have satisfactory long term stability and ageing resistance. These are the characteristics of the final polymer of the lens body.
• the present invention relates to the use of a pre-polymer mixture of the invention for preparing adjustable optical components which comprise a transparent, thermally stable, soft and deformable polymer having a shear modulus of less than 100 kPa.
• a third aspect of the present invention relates to the use of the pre-polymer mixture of the present invention for preparing adjustable optical lenses of sandwich structure which comprise a transparent, thermally stable, soft and deformable lens body having a shear modulus of less than 100 kPa.
• an adjustable optical lens of sandwich structure prepared in accordance with the present invention, comprising a soft and deformable lens body confined on a transparent bendable cover comprising actuators on a thin glass surface supported by sidewalls
• polymers having a high refractive index may not have the mechanical properties required for being employed in a lens.
• the refractive index ratio between the transparent polymer network of cross-linked or partly cross-linked polymers and the oil or combination of oils is between 0.8 and 1. In some further embodiments the difference in refractive index ratio between the transparent polymer network of cross-linked or partly cross-linked polymers and the oil or combination of oils is between 0.01 and 0.30.
• the oil or combination of oils has a refractive index which is at least 0.02 units higher than the refractive index of the transparent polymer network of cross-linked or partly cross-linked polymers.
• Transparent is herein defined as having a high transmittance, or consequently a low absorbance, such as lower than 10% per mm in the visible range of the electromagnetic spectrum.
• the visible range may include near infrared (N.I.R.) and at least part of the UV spectrum.
• the invention is particularly, but not exclusively, advantageous for obtaining a transparent optical device element having a high refractive index, RI.
• the refractive index is the measure for the speed of light in a material, relative to the speed of light in vacuum - a refractive index of 1.5 is for example equivalent to saying that the speed of light in that material is 50% less than in vacuum.
• the refractive index is an important physical parameter with practical use, especially in optics, where effects such as refraction and reflection both depend on the refractive index of materials and the interfaces of such materials.
• the refractive index is theoretically linked to the dielectric properties of the material. The dielectric properties are also very much correlated with the polarity of a chemical compound and also the miscibility of materials.
• the refractive index of a lens body is limited by the RI of the polymer used to produce the lens body, thus polymer with high RI are desired.
• these polymers generally do not have the desired properties so as to comply with the requirement for lens body to be used as adjustable optical lens.
• the lens body should have a refractive index being as high as possible, e.g. in the range of 1.35-1.90. Accordingly, the refractive index of the lens body should be at least 1.35, e.g . in the range between 1.35-1.75, such as in the range between 1.35 and 1.55.
• oils that differ quite much in refractive index. It is not trivial to create homogeneous, transparent blends of two components that differ in refractive index, especially when one or both of the components are polymeric materials.
• plasticizer or oil for incorporation in a swollen polymeric network a non-functional polymer or oil that is as similar as possible to the functional components that will make up the three dimensional network was selected.
• the refractive index of a swollen cross-linked polymer was increased by as much as 0.05 units, which for the application of the material in a prism or lens, is equivalent to an increase in refraction by as much as 15%.
• the oil or combination of oils has a molecular weight lower than 1000 g/mol.
• the use of specific polymers having a molecular weight lower than 1000 g/mol has the advantage of allowing addition of miscible oil or combination of oils having a difference in refractive index in comparison to the one of the specific polymer that is higher than the polymer having a molecular weight higher than 1000 g/mol.
• the solution of the invention allows for a higher increase in the refractive index of the lens body following a linear addition rule.
• the polymer network of cross-linked or partly cross-linked polymers and the oil or combination of oils may be in the same liquid phase.
• the oil or the combination of oils has a very high degree of miscibility with the polymer.
• the invention thus provides a combination of miscible oils and polymers so as to achieve the desired RI.
• Miscibility is the property of liquids to mix in different proportions, forming a homogeneous solution.
• a miscible oil is defined as an oil that can be mixed with a polymer leading to a system of an oil and a polymer that is homogeneous and stable at a given mixing ratio over a wide temperature range. Full miscibility might occur at mix ratios from 0 to 100%, or there can be a miscibility window for binary or ternary systems, outside of which phase separation occurs.
• a miscible oil, or mixture of oils is defined as an oil that creates a homogeneous solution with the polymer and cross-linked polymer within a given miscibility window that ranges from 0.1 - 10% to 0.1 - 90%.
• the mix ration is from 20 to 80% vol/vol.
• oils/solvents/plasticizers into a polymeric three dimensional network is not trivial. Even when several theoretical aspects of thermodynamics of polymer blends are considered prediction on miscibility may be done with poor success based on compounds dipole moments, surface tensions, solubility parameters and other parameters.
• transparent polymer network of cross-linked or partly cross-linked polymers Contained is herein defined as included in the polymer network, for example the polymer and the oil or combination of oils may be in the form of a gel.
• the amount of the oil or combination of oils is in a range between 0.1 and 90 % vol/vol, such as in the range between 10 and 80 % vol/vol , e.g. in the range between 20 and 70 % vol/vol , of said transparent polymer network of cross-linked or partly cross-linked polymers.
• the amount of the oil or combination of oils constitutes about 80% by volume of the deformable lens body.
• the oil or combination of oils has a boiling point above 200 °C at atmospheric pressure at sea level.
• Operating temperatures for camera devices containing an adjustable lens with the deformable lens body can be as wide as -40°C to 100°C. In order to withstand especially the higher temperature ranges for prolonged times, the stability of the deformable lens body must be excellent at these temperatures. Neither the transparency nor the stiffness, nor the total weight of the lens body should change by more than 5% after exposure to 100°C for a period of 1000 hours. When low molecular weight oils, such as lower than 1000 gr/mol constitute a significant part of such lens bodies, such oils must have a high boiling point and a low vapour pressure at the relevant temperatures.
• the polymer network of cross-linked or partly cross-linked polymers is a polymer network of cross-linked or partly cross-linked polysiloxanes.
• polysiloxanes From the enormous number of polymers certain polysiloxanes have shown to be useful for soft deformable lens bodies and their manufacturing.
• Polysiloxanes frequently referred to as silicones, are partially organic compounds, but, unlike most polymers, they have a backbone containing no carbon, instead they are composed of alternating silicon and oxygen atoms. In most polysiloxanes, two organic groups, often methyl or phenyl, are attached to each silicon atom.
• Polysiloxanes in general are exceptionally stable and inert. Due to availability and also the rather well-defined structure, vinyl-terminated siloxanes are commonly used when preparing elastomeric silicone networks.
• vinyl terminated it is generally meant that there is one vinyl group on each of the ends of a linear polymeric molecule. These are available from different producers, with molecular weights ranging from 200 to more than 200 000.
• the DMS-V00 to DMS-V52 series from Gelest Inc. indicates the span of easily available vinyl-terminated
• polydimethylsiloxanes Phenyl containing analogues are also available from Gelest Inc. (the PDV and PMV series), and also copolymers of dimethyl and diethyl siloxanes exist (EDV-2025).
• PDV and PMV series the PDV and PMV series
• EDV-2025 copolymers of dimethyl and diethyl siloxanes exist
• vinyl-terminated polysiloxanes there exists poly co-(vinylmethyl dimethyl) siloxanes, polyvinylmethylsiloxanes, long chain branched vinyl-functional polysiloxanes and silsesquioxanes with multiple vinyl-terminal groups.
• vinyl-containing polysiloxanes containing two or more vinyl groups per molecule are preferred. More preferably vinyl-containing polysiloxanes containing between 2 and 5 vinyl groups per molecule can be used.
• Such vinyl-containing polysiloxanes can preferably be chosen from the group of polydimethyl siloxanes, poly(methyl phenyl) siloxanes, poly co-(dimethyl diphenyl) siloxanes, poly ter-(dimethyl diphenyl methylphenyl) siloxanes, containing between 2-5 vinyl groups per molecule.
• PDMS polydimenthylsiloxane
• PDMS is optically clear, and, is considered to be inert, non-toxic and non-flammable.
• any compound containing two or more Si-H groups per molecule can act as a cross-linker of the present invention for the formation of a three dimensional silicone network, since this group readily reacts with vinyl groups catalyzed by transition metals such as the Karstedt catalysts. It is often desirable to use polymeric cross-linkers - for example in order to reduce volatility.
• polymethylhydrosiloxanes are applicable, such as HMS-991 from Gelest Inc.
• Equivalent cross-linkers with other side groups such as ethyl, phenyl also exist as hydrosilyl functional co- and homopolymers. Examples are HES-992, HDP-111, HPM-502 from Gelest Inc. It is also possible to use non-polymeric cross-linkers, such as certain well-defined molecules with 3 and 4 hydrosilyl groups, which act as cross linkers.
• Some examples of tetrafunctional SiH cross-linkers are tetrakis- dimethylsiloxy silane, tetrakisdiphenylsiloxy silane and tetrakisdiethylsiloxy silane.
• three-functional cross-linkers are, e.g. metyltrisdimethylsiloxysilane and phenyltrisdimethylsiloxysilane.
• a useful cross-linker with hydride functionality for use in the present invention is a hydrosilyl-containing short chained polymer such as a polysiloxane having in average 2 or more hydrosilyl groups per molecule. More preferably such hydrosilyl-containing polysiloxanes can be selected from the group of
• Even more preferred hydrosilyl-containing polysiloxanes can be selected from the group of polymethylsiloxanes, polymethylphenyl siloxanes and poly co-(dimethyl diphenyl) siloxanes containing in average between 3-15 hydrosilyl groups per molecule.
• Such hydrosilyl-containing polysiloxanes should have a number average molecular weight from 300 to 100 000, preferably from 300 to 40 000, more preferred from 300 to 20 000 and most preferred from 320 to 10 000.
• (Mw/Mn) of the polymers should be in the range from 1 to 5, preferably from 1 to 3.
• Another important factor for obtaining a qualitatively good lens polymer is the ratio of vinyl-containing polysiloxane and the hydrosilyl-containing cross-linker as this ratio is decisive for the cross-linking of the polymer and will thus influence the softness and elasticity of the lens.
• the stoichiometric ratio between hyd rosilyl and vinyl g roups is from 0.3 to 0.9, more preferably from 0.3 to 0.7 in the pre-polymer mixture. Reaction rates are in general more or less proportional to the concentration of the species that undertake the reaction .
• Karstedt catalysts are normally employed in the area 5- 100 ppm Pt, typically an optimization between desired cross-linking rate and discoloration of the final polymer, as hig her catalyst concentration could both give inherent absorption by itself and cause thermal deg radation at elevated temperatures. Uncontrolled discoloration is of course a problem when one wants to control the formation of a deformable polymer with specific properties in a fast and reproducible process
• a ready mixed pre-polymer mixture for making the cross-linked silicone polymer through hyd rosilylation consists in principle of at least a vinyl-containing polysiloxane (preferably having 2 or more vinyl groups per molecule), a hydrosilyl-containing cross-linker such as, e.g ., a hydrosilyl-containing polysiloxane (preferably having 2 or more H-Si groups per molecule) and a suitable transition metal catalyst for the hyd rosilylation reaction to occur.
• the pre-polymer mixture may contain additives such as nonfunctional siloxanes (0-90%), stabilizing aids (UV stabilizers, thermal stabilizers, antimicrobial compounds), fillers (inorganic or organic particles), dyes/colorants etc.
• additives such as nonfunctional siloxanes (0-90%), stabilizing aids (UV stabilizers, thermal stabilizers, antimicrobial compounds), fillers (inorganic or organic particles), dyes/colorants etc.
• additives such as nonfunctional siloxanes (0-90%), stabilizing aids (UV stabilizers, thermal stabilizers, antimicrobial compounds), fillers (inorganic or organic particles), dyes/colorants etc.
• additives such as nonfunctional siloxanes (0-90%), stabilizing aids (UV stabilizers, thermal stabilizers, antimicrobial compounds), fillers (inorganic or organic particles), dyes/colorants etc.
• the pre-polymer mixture When the three required components (vinyl, hydrosilyl and catalyst) are mixed, a cross-linking reaction will start and it is a matter of time before the continuous polymer network is formed. Thus, the pre-polymer mixture is considered to be in a pseudo or quasi-stable state. In the practical application of soft polymers for tunable lenses, it is required that the pre-polymer mixture is prepared in such a way that the cross-linking is controlled.
• the pre-polymer mixture will ideally have a reasonable long pot-life, i.e. a fairly long time window for which the pre-polymer mixture can be used after mixing of the relevant components, while at the same time cure to an elastomeric solid within short time at elevated temperatures. In fact the present pre-polymer mixture will normally have a storage stability of more than 6 hours. When mixing the components of the pre-polymer mixture it is important that all components are well mixed.
• the pre-polymer mixture must have a stable and low viscosity after mixing.
• the pre-polymer mixture should have a viscosity of less than 5000cst for easy and fast handling, which is achievable with low molecular weight starting materials. Such low viscosity is favourable for fast position/deposition and spreading of the droplet on the bottom plate.
• pre-polymer mixture must have a high concentration of reactive groups for a fast reaction to take place when the polymerization is initiated.
• Reaction rate (r) is dependent on concentration of the reactants, for example proportional to the concentration of the hydrosilyl containing cross-linker
• one aspect of the present invention relates to a pre-polymer mixture useful for preparing adjustable optical components such as adjustable optical lenses, wherein the pre-polymer mixture comprises a hydrosilyl-containing cross-linker having 2 or more hydrosilyl groups per molecule, a vinyl-containing polysiloxane having 2 or more vinyl groups per molecule, and a transition metal catalyst.
• the present invention relates to a pre-polymer mixture comprising a hydrosilyl-containing polysiloxane having in average 2 or more hydrosilyl groups per molecule, a vinyl-containing polysiloxane having between 2 and 5 vinyl groups per molecule, and a platinum catalyst.
• the pre-polymer mixture comprises a hydrosilyl- containing cross-linker selected from the group of polymethylsiloxanes,
• polysiloxane selected from the group of polydimethylsiloxane, poly(methyl phenyl) siloxanes, poly co-(dimethyl diphenyl) siloxanes, poly ter-(dimethyl diphenyl methylphenyl) siloxanes, containing between 2-5 vinyl groups per molecule, and platinum catalyst.
• the pre-polymer mixture comprises a hydrosilyl- containing cross-linker selected from the group of polymethylsiloxanes,
• polymethylphenyl siloxanes and poly co(dimethyl diphenyl) siloxanes containing in average between 3 to 15 hydrosilyl groups per molecule, a vinyl-containing polysiloxane selected from the group of polydimethylsiloxane, poly(methyl phenyl) siloxanes, poly co-(dimethyl diphenyl) siloxanes, poly ter-(dimethyl diphenyl methylphenyl) siloxanes, containing between 2-5 vinyl groups per molecule, and platinum catalyst.
• vinyl-containing polysiloxanes chosen from the group of polydimethyl siloxanes, poly(methyl phenyl) siloxanes, poly co-(dimethyl diphenyl) siloxanes, poly ter-(dimethyl diphenyl methylphenyl) siloxanes, containing between 2-5 vinyl groups per molecule, are vinyl-terminated
• the hydrosilyl-containing polysiloxane having 3 to 15 hydrosilyl groups per molecule is also a hydrosilyl-terminated polysiloxane.
• a non-stoichiometric amount of vinyl groups and hydrosilyl groups are used in the pre-polymer mixture, and preferably an excess of vinyl groups is used.
• the stoichiometric ratio between hydrosilyl and vinyl groups is from 0.3 to 0.9, more preferably from 0.3 to 0.7 in the pre-polymer mixture.
• the pot life of the pre- polymer mixture is about 6 hours at ambient temperature.
• Curing the pre-polymer may be obtained by placing the adjustable lens assembly in an oven at any temperature from for example 50°C to 180°C or higher during 1 - 20 hours (depending on the polymer formulation).
• the present invention relates to including a oil in the cross-linked polymers.
• the oils of the invention are miscible with the cross-linking polymer at all
• Relevant oils might be selected from the groups of aliphatic and aromatic esters of various organic and inorganic acids, such as phthalates, phosphates, maleates, fumarates, stearates; aromatic or aliphatic hydrocarbons; polymeric or oligomeric esters or polyesters; aromatic ethers; oligomeric or polymeric siloxanes with various ligands, such as methyl, phenyl, naphthyl, and even substituted aromatic ligands, with particularly heavy atomic substituents such as Bromine or Iodine; metalorganic oils containing heavy metal atoms, such as Ti, Zr, Zn, Ge, As.
• the oil or combination of oils is selected from the group of oligomeric or polymeric siloxanes.
• Nanoparticles In some embodiments the deformable lens body further comprises inorganic or metalorganic nanoparticles, useful for increasing the refractive index of the deformable lens body, contained in the transparent oil or in the polymeric network, either as dispersed particles, or as hybrid materials where the
• metalorganic or inorganic phase is created in situ.
• the nanoparticles may have average particle size in the range of less than 10 nm.
• the nanoparticles may be selected from the group of titanium oxides, zirconium oxides, tin oxides, zinc oxides etc.
• the nanoparticles may constitute 0-50 % by volume of the deformable lens body.
• the polymer network of cross-linked or partly cross-linked polysiloxanes constituting the deformable lens body is prepared from a liquid pre- polymer mixture having a viscosity of less than 5000 cSt comprising a hydrosilyl- containing cross-linker selected from the group of polymethylsiloxanes,
• polymethylphenylsiloxanes and poly co(dimethyl diphenyl) siloxanes containing in average between 3 to 15 hydrosilyl groups per molecule and having from 10 to 25 monomer units; a vinyl-containing polysiloxane selected from the group of polydimethylsiloxane, poly(methyl phenyl) siloxanes, poly co-(dimethyl diphenyl) siloxanes, poly ter-(dimethyl diphenyl methylphenyl) siloxanes, containing between 2-5 vinyl groups per molecule and having from 10 to 40 repeating monomer units, the stoichiometric ration of hydrosilyl groups to vinyl groups being from 0.3 to 0.9; and a transition metal catalyst.
• the transition metal catalyst is platinum (II) bis(acetylacetonate). In some further embodiments the transition metal catalyst is a Karstedt Catalyst, e.g . Pt 1,3 divinyl-l,l,3,3,-tetramethyldisiloxane.
• a cross linking rate moderator such as an inhibitor or retardant is included in the formulation.
• moderators may be selected from a range of electron donating compounds, containing one or more groups such as vinyl, allyl, carbonyls etc.,
• the transparent optical device element may be used as lens in a camera module, such as a mobile phone camera, endoscopes, automotive cameras, laptops, industrial applications and numerous more.
• a camera module such as a mobile phone camera, endoscopes, automotive cameras, laptops, industrial applications and numerous more.
• the invention has the advantage of being an imagine a simple autofocus technology, produced in automated or semi-automated mass production facilities, employing both wafer scale MEMS or semi-conductor facilities and advanced assembly and packaging technology, capable of producing very large volumes at extremely low prices.
• the invention enables the production of large volumes of adjustable lenses for example for use in autofocus cameras that can change focus within very short time frames, even down to within 1 ms, and doing so with a low use of electrical power that prolongs the battery life time for such hand-held, mobile devices as cameras and laptop PCs.
• a method for changing the refractive index of a deformable lens body comprising:
• Changing the refractive index of a deformable lens body may be read as changing the refractive index of the transparent optical device element.
• the changing may be a reduction or an increase of the RI.
• the method according to the fifth aspect of the invention may further comprise: - curing the transparent polymer network and the oil or combination of oils, thereby providing a transparent polymer network of crossed linked or partly crossed linked polymers including the oil or combination of oils.
• the method according to the fifth aspect of the invention employs the oil or combination of oils according to the first aspect of the invention.
• the present invention relates to an adjustable optical lens of sandwich structure prepared according to the present invention comprising a soft and deformable lens body (3) confined in a cavity bounded by a first side comprising actuators (1) on a thin glass surface (2) supported by sidewalls (4), wherein second surface constituting a bottom side of the cavity is arranged as an attached transparent plate (5) onto the lens body such that there is an opening between the side walls and the edges of the transparent plate, wherein the deformable lens body (3) have an shear modulus of less than 100 kPa.
• first, second and third and other aspects or embodiments of the present invention may each be combined with any of the other aspects and embodiments.
• FIG 1 shows the transparent optical device element and the different steps of production of the transparent optical device element according to one aspect of the invention.
• Figure 2 shows the increase of the refractive index of a crosslinked
• Figure 3 shows the increase of the refractive index of a crosslinked poly co- (diphenyl dimethyl)siloxane by incorporating oils with higher refractive index.
• Figure 4 shows the increase of the refractive index of a crosslinked poly co- (diphenyl dimethyl)siloxane by incorporating oils with higher refractive index.
• Figure 5 shows the increase the refractive index of a commercial optical silicone by incorporating high index oils.
• Figure 6 shows another commercially available silicone - OE-6450 from Dow Corning, with refractive index of 1,546 was mixed according to instructions and added various amounts of 1,1,3,5,5-Pentaphenyl, 1,3,5-Trimethyl-Trisiloxane, with refractive index of 1,58
• Figure 7 shows the loss tangent (tan ⁇ ) as a function of the shear modulus, measured using a dynamic rheometer.
• Figure 1 shows the transparent optical device element and the different steps (a- e) of production of the transparent optical device element according to one aspect of the invention.
• the transparent optical device element illustrated in Figure 1 comprises a deformable lens body 3, actuators 1 arranged on a thin, flexible glass surface 2 supported by continuous or semi-continuous rigid sidewalls 4.
• Example 1 Polydimethylsiloxane networks
• Figure 2 shows the increase of the refractive index of a crosslinked polydimethylsiloxane by incorporating oils with higher refractive index.
• the three d imensional network consists of vinyl terminated polyd imethylsiloxane (PDMS), crosslinked with tetrakis(dimethylsiloxy)silane giving a refractive index of 1.404.
• the oils are (g rey), 1, 1,5,5-Tetraphenyl, 1,3,3,5-Tetramethyl- Trisiloxanewith refractive index 1.55, (checkered) 2-bromonaphthalene with refractive index 1.66, (open circles) a low molecular weight
• poly(phenylmethyl)siloxane with refractive index 1.48 (PMM-0011 from Gelest, molecular weig ht of 350-450, according to the producer) .
• PMM-0011 from Gelest, molecular weig ht of 350-450, according to the producer
• poly(phenylmethyl)siloxane with higher molecular weight than the 1.48 index one was incorporated (PMM-0021 from Gelest Inc.) .
• This polymer has a refractive index of 1.52, and a molecular weig ht according to the producer of 700-900. With only as little as 1% of the oil in the PDMS network, the resulting polymer was opaque, and useless in optical applications.
• poly(phenylmethyl)siloxane (PMM-0011) to a ratio 1 : 9, it was possible to implement more than 50% into a polydimethylsiloxane network.
• the refractive index of the polymer was 1.448, with 50% of only PMM-0011, a refractive index of 1.440 was achieved . This shows that, by carefully choosing optimal oils or blends of oils, it is possible to tweak and obtain miscible polymers with higher index of refraction than the pure polymer network would give.
• Example 2 Poly-cofdiphenyl dimethyl ' ) siloxane networks
• Figure 3 shows the increase of the refractive index of a crosslinked poly co- (diphenyl dimethyl)siloxane by incorporating oils with higher refractive index.
• the three d imensional network consists of vinyl terminated poly co-(dimethyl, diphenyl)siloxane (approx. 16 mole % diphenyl), crosslinked with
• oils are (open circles), 1, 1,3,5,5-Pentaphenyl, 1,3,5-Trimethyl-Trisiloxanewith refractive index 1.58, (checkered) 1, 1,5,5-Tetraphenyl, 1,3,3,5-Tetramethyl-Trisiloxanewith refractive index 1.55.
• About 20% of the higher molecular weig ht oil was compatible with the three dimensional PDMS network. Above this level, the resulting polymer yielded an opaque solid, d ue to phase separation of the oil and the polymer network.
• the 1.55 index oil was miscible with the network silicone throughout the whole range from 0- 100% . At >80% oil, the polymer became too loosely cross-linked, giving a semi-solid or even liquid matter.
• FIG. 4 shows the increase of the refractive index of a crosslinked poly co- (diphenyl dimethyl)siloxane by incorporating oils with higher refractive index.
• the three dimensional network consists of vinyl terminated poly co-(dimethyl, diphenyl)siloxane (approx. 20 mole % diphenyl), crosslinked with
• Example 4 Blending hig h refractive index oils into commercially available silicones
• Figure 5 shows the increase the refractive index of a commercial optical silicone by incorporating high index oils.
• a commercially available silicone - LS-6257 from Nusil was mixed according to the recommendations, and added various amounts of 1,1,3,5,5-Pentaphenyl, 1,3,5-Trimethyl-Trisiloxane with refractive index 1.58.
• concentrations up to 55% oil the resulting polymer was transparent, soft and stable after curing. With 60% oil, the cured polymer turned slightly opaque, rendering it not suitable for use in optical applications.
• the refractive index increased from 1.55 to 1.567 with a level of 55% oil of index 1.58. This was in line with the linear addition rule.
• Figure 6 shows another commercially available silicone - OE-6450 from Dow Corning, with refractive index of 1,546 was mixed according to instructions and added various amounts of 1,1,3,5,5-Pentaphenyl, 1,3,5-Trimethyl-Trisiloxane, with refractive index of 1,58. At concentrations up to 50%, the resulting polymer was gradually softer and softer, while stable and transparent after curing. With 60% oil, the polymer did not cure, and remained a liquid. The refractive index increased from 1.546 to 1.563 with 50% oil, in line with the linear addition rule. By adding to the mixture of the OE-6450 1% of tetrakis(dimethylsiloxy)silane, solid, stable and transparent polymers could be prepared with as much as 80% oil, resulting in a refractive index of 1.573.
• Example 5 Dynamic viscoelastic behavior of elastomers with different modulus
• Figure 7 shows the loss tangent (tan ⁇ ) as a function of the shear modulus, measured using a dynamic rheometer. All polymers were prepared by mixing vinyl terminated polydimethylsiloxane with a poly co(-dimethyl methyl) siloxane (DMS- V22 and HMS-151 from Gelest) and a small amount of a Pt catalyst. The polymers with "non-stoichiometric" ratio between vinyl and hydride were all prepared with surplus vinyl groups, with from 3-10 percent by weight of HMS-151. The resulting shear modulus varied from 0.2 to 210 kPa.
• the polymers with added oil were prepared with a 1 :9 ratio of HMS-151 to DMS-V22, and adding from 0 to 89% by weight of a linear polydimethylsiloxane oil.
• the resulting shear modulus varied from 3 to 200 kPa.

Landscapes

• Physics & Mathematics (AREA)
• Optics & Photonics (AREA)
• General Physics & Mathematics (AREA)
• Engineering & Computer Science (AREA)
• Health & Medical Sciences (AREA)
• Ophthalmology & Optometry (AREA)
• Mechanical Engineering (AREA)
• Manufacturing & Machinery (AREA)
• Compositions Of Macromolecular Compounds (AREA)
• Chemical & Material Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Organic Chemistry (AREA)
• Lens Barrels (AREA)

Priority Applications (3)

Applications Claiming Priority (2)

Related Child Applications (2)

Publications (1)

Family

ID=47997038

Family Applications (1)

Country Status (8)

Cited By (5)

Families Citing this family (16)

Citations (6)

Family Cites Families (15)

• 2013
  • 2013-03-18 EP EP13159696.7A patent/EP2781939B1/en active Active
  • 2013-03-18 ES ES13159696.7T patent/ES2561756T3/es active Active
  • 2013-09-13 TW TW106127321A patent/TWI651550B/zh active
  • 2013-09-13 TW TW102133209A patent/TWI615640B/zh active
  • 2013-09-13 CN CN201310419470.7A patent/CN103558654B/zh active Active
  • 2013-09-13 JP JP2013190688A patent/JP2014182368A/ja active Pending
• 2014
  • 2014-03-18 KR KR1020157029097A patent/KR101819810B1/ko active Active
  • 2014-03-18 US US14/777,265 patent/US9581737B2/en active Active
  • 2014-03-18 WO PCT/EP2014/055391 patent/WO2014147060A1/en not_active Ceased
• 2016
  • 2016-10-14 US US15/294,290 patent/US10288777B2/en active Active
  • 2016-11-08 JP JP2016217699A patent/JP6340058B2/ja active Active

Patent Citations (7)

Also Published As

Similar Documents

Legal Events