WO2014132895A1 - Filé contenant une fibre en polyméthylpentène, et structure de fibre constituée dudit filé - Google Patents

Filé contenant une fibre en polyméthylpentène, et structure de fibre constituée dudit filé Download PDF

Info

Publication number
WO2014132895A1
WO2014132895A1 PCT/JP2014/054195 JP2014054195W WO2014132895A1 WO 2014132895 A1 WO2014132895 A1 WO 2014132895A1 JP 2014054195 W JP2014054195 W JP 2014054195W WO 2014132895 A1 WO2014132895 A1 WO 2014132895A1
Authority
WO
WIPO (PCT)
Prior art keywords
fiber
polymethylpentene
spun yarn
acid
yarn
Prior art date
Application number
PCT/JP2014/054195
Other languages
English (en)
Japanese (ja)
Inventor
鹿野秀和
▲はま▼中省吾
荒西義高
Original Assignee
東レ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 東レ株式会社 filed Critical 東レ株式会社
Priority to JP2014512200A priority Critical patent/JP6308127B2/ja
Publication of WO2014132895A1 publication Critical patent/WO2014132895A1/fr

Abstract

L'objet de la présente invention est de fournir un filé présentant d'excellentes caractéristiques en termes de légèreté, de propriétés de maintien au chaud, de propriétés de séchage rapide et de résistance à la chaleur lors du repassage, et pouvant être utilisé de manière appropriée comme structure de fibre telle qu'un tissu tissé, tricoté ou non tissé. L'invention concerne un filé contenant une fibre de polyméthylpentène comprenant une résine à base de polyméthylpentène comme composant principal et présentant une finesse de monofibre allant de 1 à 20 dtex, et présentant un coefficient de torsion (K) allant de 1,3 à 6,5 tel qu'il a été calculé selon la formule (I) : K = T ÷ N1/2 [T étant un nombre de torsions (torsions/25,4 mm) et N étant un titrage anglais du fil de coton].
PCT/JP2014/054195 2013-02-28 2014-02-21 Filé contenant une fibre en polyméthylpentène, et structure de fibre constituée dudit filé WO2014132895A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2014512200A JP6308127B2 (ja) 2013-02-28 2014-02-21 ポリメチルペンテン繊維を含有してなる紡績糸およびそれからなる繊維構造体

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2013-038946 2013-02-28
JP2013038946 2013-02-28

Publications (1)

Publication Number Publication Date
WO2014132895A1 true WO2014132895A1 (fr) 2014-09-04

Family

ID=51428163

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2014/054195 WO2014132895A1 (fr) 2013-02-28 2014-02-21 Filé contenant une fibre en polyméthylpentène, et structure de fibre constituée dudit filé

Country Status (3)

Country Link
JP (1) JP6308127B2 (fr)
TW (1) TW201443303A (fr)
WO (1) WO2014132895A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
TWI609109B (zh) * 2015-02-12 2017-12-21 和明紡織股份有限公司 超高撚度之纖維製造方法

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR102487915B1 (ko) * 2022-01-25 2023-01-13 주식회사 피피 리사이클된 합성섬유의 방적사를 이용한 메디컬용 기능성 원단의 제조방법 및 이를 이용한 비염색 기능성 메디컬 의류

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH02175902A (ja) * 1988-12-27 1990-07-09 Daiwabo Co Ltd 靴下
JPH02175939A (ja) * 1988-12-27 1990-07-09 Daiwabo Co Ltd 紡績糸および編織物
JPH09157960A (ja) * 1995-12-08 1997-06-17 Kuraray Co Ltd 複合繊維
JP2000192335A (ja) * 1998-12-22 2000-07-11 Japan Vilene Co Ltd 極細繊維発生可能繊維、これから発生した極細繊維及びこの極細繊維を用いた繊維シート
JP2004183113A (ja) * 2002-11-29 2004-07-02 Toyobo Co Ltd 伸縮嵩高性短繊維織編物及びその製造方法
JP2008274468A (ja) * 2007-04-27 2008-11-13 Toray Ind Inc 紡績糸
WO2013141033A1 (fr) * 2012-03-23 2013-09-26 東レ株式会社 Fibre conjuguée à base de polyméthylpentène ou fibre poreuse de polyméthylpentène et structure fibreuse les comprenant

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH02175902A (ja) * 1988-12-27 1990-07-09 Daiwabo Co Ltd 靴下
JPH02175939A (ja) * 1988-12-27 1990-07-09 Daiwabo Co Ltd 紡績糸および編織物
JPH09157960A (ja) * 1995-12-08 1997-06-17 Kuraray Co Ltd 複合繊維
JP2000192335A (ja) * 1998-12-22 2000-07-11 Japan Vilene Co Ltd 極細繊維発生可能繊維、これから発生した極細繊維及びこの極細繊維を用いた繊維シート
JP2004183113A (ja) * 2002-11-29 2004-07-02 Toyobo Co Ltd 伸縮嵩高性短繊維織編物及びその製造方法
JP2008274468A (ja) * 2007-04-27 2008-11-13 Toray Ind Inc 紡績糸
WO2013141033A1 (fr) * 2012-03-23 2013-09-26 東レ株式会社 Fibre conjuguée à base de polyméthylpentène ou fibre poreuse de polyméthylpentène et structure fibreuse les comprenant

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
TWI609109B (zh) * 2015-02-12 2017-12-21 和明紡織股份有限公司 超高撚度之纖維製造方法

Also Published As

Publication number Publication date
TW201443303A (zh) 2014-11-16
JPWO2014132895A1 (ja) 2017-02-02
JP6308127B2 (ja) 2018-04-11

Similar Documents

Publication Publication Date Title
TWI725267B (zh) 偏心芯鞘複合纖維及混纖絲
JP6299222B2 (ja) ポリメチルペンテン複合繊維およびそれからなる繊維構造体
JP2014167185A (ja) ポリメチルペンテン中空繊維を含有してなる紡績糸およびそれからなる繊維構造体
JP6562073B2 (ja) 可染性ポリオレフィン繊維およびそれからなる繊維構造体
KR102335576B1 (ko) 가염성 폴리올레핀 섬유로 이루어지는 가연가공사
JP7056153B2 (ja) ポリマーアロイ繊維およびそれからなる繊維構造体
EP3741885A1 (fr) Fibre de polyoléfine pouvant être teinte et structure fibreuse comprenant celle-ci
JP6308127B2 (ja) ポリメチルペンテン繊維を含有してなる紡績糸およびそれからなる繊維構造体
JP7290025B2 (ja) 可染性ポリオレフィン芯鞘型複合繊維およびそれからなる繊維構造体
JP2018204157A (ja) 吸湿性に優れた芯鞘型複合繊維、仮撚糸および繊維構造体
JP7406697B2 (ja) 芯鞘型ポリマーアロイ繊維、それを含む繊維集合物、及びその製造方法
JP7172258B2 (ja) 編地
JP3719258B2 (ja) ソフトストレッチ糸および製造方法ならびに布帛
JP2020084369A (ja) ポリマーアロイ繊維およびそれからなる繊維構造体
JP2019099986A (ja) 複合繊維およびそれからなる繊維構造体

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2014512200

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14756521

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14756521

Country of ref document: EP

Kind code of ref document: A1