WO2014119377A1 - 二次電池用負極およびその製造方法、それを用いた二次電池 - Google Patents
二次電池用負極およびその製造方法、それを用いた二次電池 Download PDFInfo
- Publication number
- WO2014119377A1 WO2014119377A1 PCT/JP2014/050719 JP2014050719W WO2014119377A1 WO 2014119377 A1 WO2014119377 A1 WO 2014119377A1 JP 2014050719 W JP2014050719 W JP 2014050719W WO 2014119377 A1 WO2014119377 A1 WO 2014119377A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- group
- negative electrode
- enyl
- substituted
- groups
- Prior art date
Abstract
本発明は一般式(1)で表される酸無水物を含むリチウム二次電池用負極に関し、高温環境下におけるサイクル特性、保存特性に優れる二次電池を提供する。(式中、 X1、X2およびXは、それぞれ互いに独立に、炭素数1~50の炭化水素基または単結合を表し、 R1およびR2は、それぞれ互いに独立に、炭素数1~6の炭化水素基または水素を表し、 m1およびm2は、それぞれ互いに独立に、1または2を表し、 n1、n2およびnは、それぞれ互いに独立に、0または1を表し、 ただし、nが1を表す場合、X1はR1と共に環状構造を形成していてもよく、X2はR2と共に環状構造を形成していてもよく、 ただし、nが0を表す場合、X1、X2、R1およびR2は共に全体で環状構造を形成していてもよい。)
Description
本発明は非水電解液二次電池に関する発明である。更に詳細には、リチウム二次電池あるいはリチウムイオン二次電池に関し、特に、高温における充放電サイクル寿命、容量保持特性、ならびに、保存後の抵抗上昇の問題を改善した、非水電解液二次電池に関するものである。
負極に炭素材料、酸化物、リチウム合金またはリチウム金属を用い、正極にリチウム含有遷移金属複合酸化物を用い、更に鎖状又は環状のカーボネート系の溶媒を含んだ電解液を有する非水電解液リチウムイオンまたはリチウム二次電池は、高いエネルギー密度を実現できることから携帯電話、ノートパソコン用などの電源として注目されている。また最近では、出力特性の向上、保存特性などの長期信頼性の向上によりハイブリッド自動車(HEV)などのモーター駆動の電源としても注目されている。これらの二次電池においては、電極表面と前記溶媒分子との反応を抑制する目的で、電解液中に複数の添加剤を加え、充放電過程の電気化学反応を利用し、電極表面に添加剤由来の保護皮膜(又は皮膜)と呼ばれる膜を形成し二次電池の基本特性や信頼性を向上させることが知られている。この皮膜は、充放電効率、サイクル寿命、安全性に大きな影響を及ぼすことから電池の高性能化には電極表面の皮膜の形成・制御が不可欠であることが知られている。前記皮膜を形成させるために、様々な添加剤が電解液に適用されてきた。
中でも、特許文献1~4に示すような環状の酸無水物を溶解した電解液を用いることで、電池のサイクル特性が向上することが知られている。また、近年は特許文献5に示されるように、分子内に酸無水物基(-CO-O-CO-)とスルホニル基(-SO2-)を有するスルホン化合物添加することで、電池特性が向上することが記載されている。しかしながら、これらの文献には、本願発明で使用される酸無水物は、記載も示唆もされていない。
加えて、特許文献6および7には、ステアリン酸無水物、オレイン酸無水物、無水コハク酸、無水酢酸などが使用されている。しかしながら、これらの文献にも、本願発明で使用される酸無水物は、記載も示唆もされていない。
上述したように、酸無水物を電解液の添加剤に用いた二次電池は非常に優れた電池特性を示す。しかしながら、次のような課題も有していた。特許文献1~5では、酸無水物を電解液添加剤として使用しているが、電解液添加剤として使用するためには、用いる添加剤が非水系電解液に可溶である必要がある。すなわち、これまでは非水系電解液に溶けない化合物は添加剤として使用することが出来なかった。また、非水系電解液に不溶な化合物を電解液に混ぜ、注液すると、不溶な添加剤がノズルに詰まり、注液不良を生じることも判明した。
以上のような理由から、非水系電解液に溶解しない酸無水物は、これまで、使用が困難であった。しなしながら、これらの酸無水物の中にも、高性能の非水電解液二次電池を得るにあたって好適なものは多いと考えられる。
本発明は上記事情に鑑みてなされたものであり、その目的は、非水系電解液に溶解しない酸無水物を使用して、サイクル特性および保存特性などの電池特性に優れる二次電池を製造することである。
上記課題を解決するために本発明者らは、非水系電解液に不溶であることを指標として、各種の酸無水物を鋭意検討した結果、一般式(1)で示される酸無水物がリチウム二次電池用負極に適することを見出した。
本発明によれば、サイクル特性および保存特性などの電池特性に優れる二次電池が提供される。
より具体的には、非水系電解液に不溶な添加剤を電解液添加剤として用いる場合、たとえ電解液に不溶であったとしても、本発明の酸無水物であれば、負極に適用することで、優れた電池特性を実現できる。
以下、本発明の負極およびこの負極を使用することができる二次電池の例を、各構成要素ごとに説明する。
[負極]
<負極活物質層>
負極は、例えば負極活物質が負極用結着剤によって負極集電体に結着されてなる。本実施形態における負極活物質は、リチウムの吸蔵及び放出が可能なものであれば、本発明の効果を著しく損なわない限り任意のものを用いることができる。負極は、集電体上に負極活物質層を設けて構成されたものを用いる。
<負極活物質層>
負極は、例えば負極活物質が負極用結着剤によって負極集電体に結着されてなる。本実施形態における負極活物質は、リチウムの吸蔵及び放出が可能なものであれば、本発明の効果を著しく損なわない限り任意のものを用いることができる。負極は、集電体上に負極活物質層を設けて構成されたものを用いる。
負極活物質としては、リチウムイオンの吸蔵放出が可能な材料であれば他に制限は無く、公知の負極活物質を任意に用いることができる。例えば、コークス、アセチレンブラック、メゾフェーズマイクロビーズ、グラファイト等の炭素質材料;リチウム金属;リチウム-シリコン、リチウム-スズ等のリチウム合金、チタン酸リチウムなどを使用することが好ましい。これらの中でもサイクル特性及び安全性が良好でさらに連続充電特性も優れている点で、炭素質材料を使用するのが最も好ましい。なお、負極活物質は1種を単独で用いてもよく、2種以上を任意の組み合わせ及び比率で併用しても良い。
さらに、負極活物質の粒径は、本発明の効果を著しく損なわない限り任意であるが、初期効率、レ-ト特性、サイクル特性等の電池特性が優れる点で、通常1μm以上、好ましくは15μm以上であり、通常50μm以下、好ましくは30μm以下程度である。また、例えば、上記の炭素質材料をピッチ等の有機物で被覆した後で焼成したもの、CVD法等を用いて表面に上記炭素質材料よりも非晶質の炭素を形成したものなども、炭素質材料として好適に使用することができる。ここで、被覆に用いる有機物としては、軟ピッチから硬ピッチまでのコールタールピッチ;乾留液化油等の石炭系重質油;常圧残油、減圧残油等の直留系重質油;原油、ナフサ等の熱分解時に副生する分解系重質油(例えばエチレンヘビーエンド)等の石油系重質油が挙げられる。また、これらの重質油を200~400℃で蒸留して得られた固体状残渣物を、1~100μmに粉砕したものも使用することができる。さらに塩化ビニル樹脂、フェノール樹脂、イミド樹脂なども使用することができる。負極活物質層は、例えば、上述の負極活物質をロール成形してシート電極としたり、圧縮成形によりペレット電極としたりすることも可能であるが、通常は、正極活物質層の場合と同様に、上述の負極活物質と、結着剤と、必要に応じて各種の助剤等とを、溶媒でスラリー化してなる塗布液を、集電体に塗布し、乾燥することにより製造することができる。
また、ケイ素を含む負極活物質としては、例えば、シリコンやシリコン化合物等が挙げられる。シリコンとしては、例えば、単体ケイ素が挙げられる。シリコン化合物としては、例えば、シリコン酸化物、ケイ酸塩、ニッケルシリサイドやコバルトシリサイドなどの遷移金属とケイ素との化合物等などが挙げられる。シリコン化合物には、負極活物質自体の繰り返し充放電に対する膨脹収縮を緩和する役目があり、充放電サイクル特性の観点から好ましく用いられる。さらにシリコン化合物の種類によってはシリコン間の導通を確保する役目もあり、このような観点から、シリコン化合物としてシリコン酸化物が好ましく用いられる。シリコン酸化物は、特に限定されるものではないが、例えば、SiOx(0<x<2)で表される。シリコン酸化物は、Liを含んでもよく、Liを含むシリコン酸化物は、例えばSiLiyOz(y>0、2>z>0)で表される。また、シリコン酸化物は微量の金属元素や非金属元素を含んでも良い。シリコン酸化物は、例えば、窒素、ホウ素およびイオウの中から選ばれる一種または二種以上の元素を、例えば0.1~5質量%含有することができる。微量の金属元素や非金属元素を含有することで、シリコン酸化物の電気伝導性を向上させることができる。また、シリコン酸化物は結晶であってもよく、非晶質であってもよい。また、負極活物質は、シリコン又はシリコン酸化物に加えて、リチウムイオンを吸蔵、放出し得る炭素材料を含むことが好ましい。炭素材料は、シリコンやシリコン酸化物と複合化させた状態で含有させることもできる。炭素材料は、シリコン酸化物と同様に、負極活物質自体の繰り返し充放電に対する膨脹収縮を緩和し、負極活物質であるシリコン間の導通を確保する役目がある。したがって、シリコン、シリコン酸化物、及び炭素材料が共存することにより、より良好なサイクル特性が得られる。
炭素材料としては、黒鉛、非晶質炭素、ダイヤモンド状炭素、カーボンナノチューブ、またはこれらの複合物を用いることができる。ここで、結晶性の高い黒鉛は、電気伝導性が高く、銅などの金属からなる正極集電体との接着性および電圧平坦性が優れている。一方、結晶性の低い非晶質炭素は、体積膨張が比較的小さいため、負極全体の体積膨張を緩和する効果が高く、かつ結晶粒界や欠陥といった不均一性に起因する劣化が起きにくい。負極活物質中の炭素材料の含有率は、2質量%以上50質量%以下とすることが好ましく、2質量%以上30質量%以下とすることがより好ましい。
シリコンとシリコン化合物とを含有する負極活物質の作製方法としては、シリコン化合物としてシリコン酸化物を用いる場合には、例えば、単体ケイ素とシリコン酸化物を混合し、高温減圧下にて焼結させる方法が挙げられる。また、シリコン化合物として遷移金属とケイ素との化合物を用いる場合には、例えば、単体ケイ素と遷移金属を混合、溶融させる方法や、単体ケイ素の表面に遷移金属を蒸着等により被覆する方法が挙げられる。
上記で述べた作製方法に加えて、炭素との複合化を組み合わせることもできる。例えば、高温非酸素雰囲気下で有機化合物の気体雰囲気中に単体ケイ素とシリコン化合物の混合焼結物を導入する方法や、高温非酸素雰囲気下で単体ケイ素とシリコン酸化物の混合焼結物と炭素の前駆体樹脂を混合する方法により、単体ケイ素とシリコン酸化物の核の周囲に炭素からなる被覆層を形成することができる。これにより充放電に対する体積膨張の抑制及びサイクル特性のさらなる改善効果が得られる。
本実施形態における負極活物質としてシリコンを用いる場合は、シリコン、シリコン酸化物及び炭素材料を含む複合体(以下、Si/SiO/C複合体とも称す)からなることが好ましい。さらに、シリコン酸化物は、その全部または一部がアモルファス構造を有することが好ましい。アモルファス構造のシリコン酸化物は、他の負極活物質である炭素材料やシリコンの体積膨張を抑制することができる。このメカニズムは明確ではないが、シリコン酸化物がアモルファス構造であることにより、炭素材料と電解液の界面への皮膜形成に何らかの影響があるものと推定される。また、アモルファス構造は、結晶粒界や欠陥といった不均一性に起因する要素が比較的少ないと考えられる。なお、シリコン酸化物の全部または一部がアモルファス構造を有することは、エックス線回折測定(一般的なXRD測定)にて確認することができる。具体的には、シリコン酸化物がアモルファス構造を有しない場合には、シリコン酸化物に固有のピークが観測されるが、シリコン酸化物の全部または一部がアモルファス構造を有する場合は、シリコン酸化物に固有のピークがブロードとなって観測される。
Si/SiO/C複合体において、シリコンは、その全部または一部がシリコン酸化物中に分散していることが好ましい。シリコンの少なくとも一部をシリコン酸化物中に分散させることで、負極全体としての体積膨張をより抑制することができ、電解液の分解も抑制することができる。なお、シリコンの全部または一部がシリコン酸化物中に分散していることは、透過型電子顕微鏡観察(一般的なTEM観察)とエネルギー分散型X線分光法測定(一般的なEDX測定)を併用することで確認することができる。具体的には、サンプルの断面を観察し、シリコン酸化物中に分散しているシリコン部分の酸素濃度を測定し、酸化物となっていないことを確認することができる。
Si/SiO/C複合体において、例えば、シリコン酸化物の全部または一部がアモルファス構造であり、シリコンはその全部または一部がシリコン酸化物中に分散している。このようなSi/SiO/C複合体は、例えば、特開2004-47404号公報で開示されているような方法で作製することができる。すなわち、Si/SiO/C複合体は、例えば、シリコン酸化物をメタンガスなどの有機物ガスを含む雰囲気下でCVD処理を行うことで得ることができる。このような方法で得られるSi/SiO/C複合体は、シリコンを含むシリコン酸化物からなる粒子の表面がカーボンで被覆された形態となる。また、シリコンはシリコン酸化物中にナノクラスター化している。
Si/SiO/C複合体において、シリコン、シリコン酸化物および炭素材料の割合は、特に制限されるものではない。シリコンは、Si/SiO/C複合体に対し、5質量%以上90質量%以下とすることが好ましく、20質量%以上50質量%以下とすることがより好ましい。シリコン酸化物は、Si/SiO/C複合体に対し、5質量%以上90質量%以下とすることが好ましく、40質量%以上70質量%以下とすることがより好ましい。炭素材料は、Si/SiO/C複合体に対し、2質量%以上50質量%以下とすることが好ましく、より好ましくは2質量%以上30質量%以下である。
また、Si/SiO/C複合体は、単体ケイ素、シリコン酸化物及び炭素材料の混合物からなることができ、単体ケイ素とシリコン酸化物と炭素材料とをメカニカルミリングで混合することでも作製することができる。例えば、Si/SiO/C複合体は、それぞれの単体ケイ素、シリコン酸化物および炭素材料が粒子状のものを混合して得ることができる。例えば、単体ケイ素の平均粒子径は、炭素材料の平均粒子径およびシリコン酸化物の平均粒子径よりも小さい構成とすることができる。このようにすれば、充放電時に伴う体積変化の小さい単体ケイ素が相対的に小粒径となり、体積変化の大きい炭素材料やシリコン酸化物が相対的に大粒径となるため、デンドライト生成および合金の微粉化がより効果的に抑制される。
また、単体ケイ素の平均粒子径は、例えば20μm以下とすることができ、15μm以下とすることが好ましい。また、シリコン酸化物の平均粒子径が炭素材料の平均粒子径の1/2以下であることが好ましく、単体ケイ素の平均粒子径がシリコン酸化物の平均粒子径の1/2以下であることが好ましい。さらに、シリコン酸化物の平均粒子径が炭素材料の平均粒子径の1/2以下であり、かつ単体ケイ素の平均粒子径がシリコン酸化物の平均粒子径の1/2以下であることがより好ましい。平均粒子径をこのような範囲に制御すれば、体積膨脹の緩和効果がより有効に得ることができ、エネルギー密度、サイクル寿命と効率のバランスに優れた二次電池を得ることができる。より具体的には、シリコン酸化物の平均粒子径を黒鉛の平均粒子径の1/2以下とし、単体ケイ素の平均粒子径をシリコン酸化物の平均粒子径の1/2以下とすることが好ましい。またより具体的には、単体ケイ素の平均粒子径は、例えば20μm以下とすることができ、15μm以下とすることが好ましい。また、負極活物質として、上述のSi/SiO/C複合体の表面をシランカップリング剤によって処理したものを用いてもよい。
<負極用結着剤>
負極用結着剤としては、特に制限されるものではないが、例えば、ポリフッ化ビニリデン、ビニリデンフルオライド-ヘキサフルオロプロピレン共重合体、ビニリデンフルオライド-テトラフルオロエチレン共重合体、スチレン-ブタジエン共重合ゴム、ポリテトラフルオロエチレン、ポリプロピレン、ポリエチレン、ポリイミド、ポリアミドイミド等を用いることができる。これらの中でも、結着性が強いことから、ポリイミド、ポリアミドイミド、ポリアクリル酸(アルカリで中和されたリチウム塩、ナトリウム塩、カリウム塩を含む)、カルボキシメチルセルロース(アルカリで中和されたリチウム塩、ナトリウム塩、カリウム塩を含む)が好ましい。使用する負極用結着剤の量は、トレードオフの関係にある「十分な結着力」と「高エネルギー化」の観点から、負極活物質100質量部に対して、2~10質量部が好ましい。
負極用結着剤としては、特に制限されるものではないが、例えば、ポリフッ化ビニリデン、ビニリデンフルオライド-ヘキサフルオロプロピレン共重合体、ビニリデンフルオライド-テトラフルオロエチレン共重合体、スチレン-ブタジエン共重合ゴム、ポリテトラフルオロエチレン、ポリプロピレン、ポリエチレン、ポリイミド、ポリアミドイミド等を用いることができる。これらの中でも、結着性が強いことから、ポリイミド、ポリアミドイミド、ポリアクリル酸(アルカリで中和されたリチウム塩、ナトリウム塩、カリウム塩を含む)、カルボキシメチルセルロース(アルカリで中和されたリチウム塩、ナトリウム塩、カリウム塩を含む)が好ましい。使用する負極用結着剤の量は、トレードオフの関係にある「十分な結着力」と「高エネルギー化」の観点から、負極活物質100質量部に対して、2~10質量部が好ましい。
<負極用集電体>
負極用集電体の材質としては、公知のものを任意に用いることができるが、例えば、銅、ニッケル、SUS等の金属材料が用いられる。中でも加工し易さとコストの点から特に銅が好ましい。また、集電体は予め粗面化処理しておくのが好ましい。さらに、集電体の形状も任意であり、箔状、平板状、メッシュ状等が挙げられる。また、エキスパンドメタルやパンチングメタルのような穴あきタイプの集電体を使用することもできる。また、集電体として薄膜を使用する場合の好ましい厚さ、形状も任意である。
負極用集電体の材質としては、公知のものを任意に用いることができるが、例えば、銅、ニッケル、SUS等の金属材料が用いられる。中でも加工し易さとコストの点から特に銅が好ましい。また、集電体は予め粗面化処理しておくのが好ましい。さらに、集電体の形状も任意であり、箔状、平板状、メッシュ状等が挙げられる。また、エキスパンドメタルやパンチングメタルのような穴あきタイプの集電体を使用することもできる。また、集電体として薄膜を使用する場合の好ましい厚さ、形状も任意である。
<負極の作製方法>
負極の作製方法としては、例えば、負極集電体上に、負極活物質と負極用結着剤を含む負極活物質層を形成することで作製できる。負極活物質層の形成方法としては、例えば、ドクターブレード法、ダイコーター法、CVD法、スパッタリング法などが挙げられる。予め負極活物質層を形成した後に、蒸着、スパッタ等の方法でアルミニウム、ニッケルまたはそれらの合金の薄膜を形成して、負極集電体としてもよい。
負極の作製方法としては、例えば、負極集電体上に、負極活物質と負極用結着剤を含む負極活物質層を形成することで作製できる。負極活物質層の形成方法としては、例えば、ドクターブレード法、ダイコーター法、CVD法、スパッタリング法などが挙げられる。予め負極活物質層を形成した後に、蒸着、スパッタ等の方法でアルミニウム、ニッケルまたはそれらの合金の薄膜を形成して、負極集電体としてもよい。
本発明によれば、一般式(1)で示される酸無水物を負極スラリーに添加して分散し、このスラリーを塗布し、乾燥することによって、負極活物質の表面に酸無水物が付着する。本発明によれば、これまで非水系電解液に溶解しないために、被膜形成剤として使用することが出来なかった化合物を、負極活物質の表面に付着させることで、電池特性を向上することが可能になる。この負極活物質の表面には酸無水物が存在しているため、電池のサイクル低下、保存特性の低下、内部ガスが発生することによる膨れを抑制することにより、優れた非水系電解液二次電池を提供することができる。このメカニズムは明らかではないが、負極表面に付着した酸無水物が、初回充電時に何らかの反応により皮膜を形成するためと推察している。
より具体的には、本発明の酸無水物を負極活物質の表面上に付着させ、恐らく、初回充電時に皮膜が形成されるため、二次電池の負極表面が制御され、電解液溶媒の分解が抑制される。この結果、二次電池のサイクル特性、容量保存特性などを向上でき、抵抗上昇を抑制できる。
<酸無水物>
式(1)の酸無水物において、基R1およびR2は、それぞれ互いに独立に、炭素数1~6の炭化水素基または水素を表し、炭素数1~6の炭化水素基の好ましい例としては、ブロモ、クロロ、フルオロおよびヨードなどのハロゲン;メチル、エチル、プロピル、ブチル、ペンチル、ヘキシル、ヘプチル、オクチル、ノニル、デシル、ウンデシル、ドデシル、トリデシル、テトラデシルおよびペンタデシルなどのアルキル基;メトキシ、エトキシ、プロポキシ、ブトキシ、ペントキシ、ヘキシルオキシ、ヘプチルオキシ、オクチルオキシ、ノニルオキシ、デシルオキシ、ウンデシルオキシ、ドデシルオキシ、トリデシルオキシおよびテトラデシルオキシなどのアルコキシ基;ビニル、プロパ-1-および-2-エニル、ブタ-1-、-2-および-3-エニル、ペンタ-1-、-2-、-3-および-4-エニル、ヘキサ-1-、-2-、-3-、-4-および-5-エニル、ヘプタ-1-、-2-、-3-、-4-、-5-および-6-エニル、オクタ-1-、-2-、-3-、-4-、-5-、-6-および-7-エニル、ノナ-1-、-2-、-3-、-4-、-5-、-6-、-7-および-8-エニル、デカ-1-、-2-、-3-、-4-、-5-、-6-、-7-、-8-および-9-エニルなどのアルケニル基;エチニルおよびプロパルギル基などのアルキニル基;置換または無置換のシクロヘキシル基;フェニル、トリル、キシリル、ベンジル、トリチル、スチリル、ナフチル、デカヒドロナフチル、テトラリルおよびナフトキノリルなどのアリール基;フリル、チエニル、ピリジル、キノリルおよびモルホリノなどのヘテロ環基;ニトロ、ニトロソ、シアノ、イソシアノ、シアナト、イソシアナト、アミノおよびアミドなどの含窒素基;ヒドロキシ、カルボキシル、アシルおよびアルコキシカルボニルなどの含酸素基;シリル、モノメチルシリル、ジメチルシリル、トリメチルシリル、モノフェニルシリル、ジフェニルシリルおよびトリフェニルシリルなどの含ケイ素基;および、チオアルキルおよびチオアルコキシなどの含イオウ基が挙げられる。
式(1)の酸無水物において、基R1およびR2は、それぞれ互いに独立に、炭素数1~6の炭化水素基または水素を表し、炭素数1~6の炭化水素基の好ましい例としては、ブロモ、クロロ、フルオロおよびヨードなどのハロゲン;メチル、エチル、プロピル、ブチル、ペンチル、ヘキシル、ヘプチル、オクチル、ノニル、デシル、ウンデシル、ドデシル、トリデシル、テトラデシルおよびペンタデシルなどのアルキル基;メトキシ、エトキシ、プロポキシ、ブトキシ、ペントキシ、ヘキシルオキシ、ヘプチルオキシ、オクチルオキシ、ノニルオキシ、デシルオキシ、ウンデシルオキシ、ドデシルオキシ、トリデシルオキシおよびテトラデシルオキシなどのアルコキシ基;ビニル、プロパ-1-および-2-エニル、ブタ-1-、-2-および-3-エニル、ペンタ-1-、-2-、-3-および-4-エニル、ヘキサ-1-、-2-、-3-、-4-および-5-エニル、ヘプタ-1-、-2-、-3-、-4-、-5-および-6-エニル、オクタ-1-、-2-、-3-、-4-、-5-、-6-および-7-エニル、ノナ-1-、-2-、-3-、-4-、-5-、-6-、-7-および-8-エニル、デカ-1-、-2-、-3-、-4-、-5-、-6-、-7-、-8-および-9-エニルなどのアルケニル基;エチニルおよびプロパルギル基などのアルキニル基;置換または無置換のシクロヘキシル基;フェニル、トリル、キシリル、ベンジル、トリチル、スチリル、ナフチル、デカヒドロナフチル、テトラリルおよびナフトキノリルなどのアリール基;フリル、チエニル、ピリジル、キノリルおよびモルホリノなどのヘテロ環基;ニトロ、ニトロソ、シアノ、イソシアノ、シアナト、イソシアナト、アミノおよびアミドなどの含窒素基;ヒドロキシ、カルボキシル、アシルおよびアルコキシカルボニルなどの含酸素基;シリル、モノメチルシリル、ジメチルシリル、トリメチルシリル、モノフェニルシリル、ジフェニルシリルおよびトリフェニルシリルなどの含ケイ素基;および、チオアルキルおよびチオアルコキシなどの含イオウ基が挙げられる。
基R1およびR2において、1個以上のCH2基は、それぞれ互いに独立に、-CH=CH-、-C≡C-、-O-、-CO-、-CO-O-、-O-CO-、-S-、-SO2-、-NY1-または-SiY1Y2-で置き換えられていてもよい。
ただし、Y1およびY2は、それぞれ互いに独立に、H、炭素数1~5のアルキル基、炭素数1~5のアルコキシ基、炭素数2~5のアルケニル基または炭素数2~5のアルキニル基を表す。
また、基R1およびR2において、1個以上の-CH=基は、それぞれ互いに独立に、-N=で置き換えられていてもよい。
更に、基R1およびR2において、1個以上の水素原子は、それぞれ互いに独立に、ブロモ、クロロ、フルオロおよびヨードから選ばれるハロゲン;メチル、エチル、プロピル、ブチル、ペンチル、ヘキシル、ヘプチル、オクチル、ノニル、デシル、ウンデシル、ドデシル、トリデシル、テトラデシルおよびペンタデシルから選ばれるアルキル基;メトキシ、エトキシ、プロポキシ、ブトキシ、ペントキシ、ヘキシルオキシ、ヘプチルオキシ、オクチルオキシ、ノニルオキシ、デシルオキシ、ウンデシルオキシ、ドデシルオキシ、トリデシルオキシおよびテトラデシルオキシから選ばれるアルコキシ基;ビニル、プロパ-1-および-2-エニル、ブタ-1-、-2-および-3-エニル、ペンタ-1-、-2-、-3-および-4-エニル、ヘキサ-1-、-2-、-3-、-4-および-5-エニル、ヘプタ-1-、-2-、-3-、-4-、-5-および-6-エニル、オクタ-1-、-2-、-3-、-4-、-5-、-6-および-7-エニル、ノナ-1-、-2-、-3-、-4-、-5-、-6-、-7-および-8-エニル、デカ-1-、-2-、-3-、-4-、-5-、-6-、-7-、-8-および-9-エニルから選ばれるアルケニル基;エチニルおよびプロパルギル基から選ばれるアルキニル基;置換または無置換のシクロヘキシル基;フェニル、トリル、キシリル、ベンジル、トリチル、スチリル、ナフチル、デカヒドロナフチル、テトラリルおよびナフトキノリルから選ばれるアリール基;フリル、チエニル、ピリジル、キノリルおよびモルホリノから選ばれるヘテロ環基;ニトロ、ニトロソ、シアノ、イソシアノ、シアナト、イソシアナト、アミノおよびアミドから選ばれる含窒素基;ヒドロキシ、カルボキシル、アシルおよびアルコキシカルボニルから選ばれる含酸素基;シリル、モノメチルシリル、ジメチルシリル、トリメチルシリル、モノフェニルシリル、ジフェニルシリルおよびトリフェニルシリルから選ばれる含ケイ素基;または、チオアルキルおよびチオアルコキシから選ばれる含イオウ基で置換されていてもよい。
以上の中でも、基R1およびR2の好ましい例としては、水素;ブロモ、クロロ、フルオロおよびヨードなどのハロゲン;メチル、エチル、プロピル、ブチル、ペンチル、ヘキシル、ヘプチルおよびオクチルなどのアルキル基;メトキシ、エトキシ、プロポキシ、ブトキシ、ペントキシ、ヘキシルオキシ、ヘプチルオキシおよびオクチルオキシなどのアルコキシ基;ビニル、プロパ-1-および-2-エニル、ブタ-1-、-2-および-3-エニル、ペンタ-1-、-2-、-3-および-4-エニル、ヘキサ-1-、-2-、-3-、-4-および-5-エニルなどのアルケニル基;フェニル、トリル、キシリル、ベンジル、トリチル、スチリル、ナフチル、デカヒドロナフチル、テトラリルおよびナフトキノリルなどのアリール基;フリル、チエニル、ピリジル、キノリルおよびモルホリノなどのヘテロ環基;ニトロ、ニトロソ、シアノ、イソシアノ、シアナト、イソシアナト、アミノおよびアミドなどの含窒素基;ヒドロキシ、カルボキシル、アシルおよびアルコキシカルボニルなどの含酸素基;または、シリル、モノメチルシリル、ジメチルシリル、トリメチルシリル、モノフェニルシリル、ジフェニルシリルおよびトリフェニルシリルなどの含ケイ素基が挙げられる。
より好ましくは、水素、メチル、エチル、ビニル、フェニルが挙げられる。
式(1)の酸無水物において、基X1、X2およびXは、それぞれ互いに独立に、炭素数1~50の炭化水素基または単結合を表し、炭素数1~50の炭化水素基の好ましい例としては、炭素数1~30で2価の脂肪族炭化水素基および炭素数4~40で2価の芳香族炭化水素基が挙げられる。
好ましい脂肪族炭化水素基の例としては、限定することなく、置換または無置換の直鎖状アルキレン基;置換または無置換の分岐状アルキレン基;置換または無置換の環状アルキレン基;置換または無置換のシクロヘキシレン基;または、置換または無置換のデカヒドロナフチレン基が挙げられる。
好ましい芳香族基の例としては、限定することなく、置換または無置換のフェニレン基;置換または無置換のトリレン基;置換または無置換のキシリレン基;置換または無置換のベンジリデン基;置換または無置換のピリジレン基;置換または無置換のフリレン基;置換または無置換のチエニレン基;置換または無置換のテトラリレン基;置換または無置換のナフトキノリレン基;置換または無置換のナフチレン基;または、置換または無置換のキノリレン基が挙げられる。
より好ましくは、単結合、炭素数1~4の直鎖状アルキレン基または環状アルキレン基またはシクロヘキシレン基、フェニレン基が挙げられる。
ただし、基X1、X2およびXにおいて、1個以上のCH2基は、それぞれ互いに独立に、-CH=CH-、-C≡C-、-O-、-CO-、-CO-O-、-O-CO-、-S-、-SO2-、-NY1-または-SiY1Y2-で置き換えられていてもよい。
なお、Y1およびY2は、それぞれ互いに独立に、H、炭素数1~5のアルキル基、炭素数1~5のアルコキシ基、炭素数2~5のアルケニル基または炭素数2~5のアルキニル基を表す。
また、基X1、X2およびXにおいて、1個以上の-CH=基は、それぞれ互いに独立に、-N=で置き換えられていてもよい。
更に、基X1、X2およびXにおいて、1個以上の水素原子は、それぞれ互いに独立に、ブロモ、クロロ、フルオロおよびヨードから選ばれるハロゲン;メチル、エチル、プロピル、ブチル、ペンチル、ヘキシル、ヘプチル、オクチル、ノニル、デシル、ウンデシル、ドデシル、トリデシル、テトラデシルおよびペンタデシルから選ばれるアルキル基;メトキシ、エトキシ、プロポキシ、ブトキシ、ペントキシ、ヘキシルオキシ、ヘプチルオキシ、オクチルオキシ、ノニルオキシ、デシルオキシ、ウンデシルオキシ、ドデシルオキシ、トリデシルオキシおよびテトラデシルオキシから選ばれるアルコキシ基;ビニル、プロパ-1-および-2-エニル、ブタ-1-、-2-および-3-エニル、ペンタ-1-、-2-、-3-および-4-エニル、ヘキサ-1-、-2-、-3-、-4-および-5-エニル、ヘプタ-1-、-2-、-3-、-4-、-5-および-6-エニル、オクタ-1-、-2-、-3-、-4-、-5-、-6-および-7-エニル、ノナ-1-、-2-、-3-、-4-、-5-、-6-、-7-および-8-エニル、デカ-1-、-2-、-3-、-4-、-5-、-6-、-7-、-8-および-9-エニルから選ばれるアルケニル基;エチニルおよびプロパルギル基から選ばれるアルキニル基;置換または無置換のシクロヘキシル基;フェニル、トリル、キシリル、ベンジル、トリチル、スチリル、ナフチル、デカヒドロナフチル、テトラリルおよびナフトキノリルから選ばれるアリール基;フリル、チエニル、ピリジル、キノリルおよびモルホリノから選ばれるヘテロ環基;ニトロ、ニトロソ、シアノ、イソシアノ、シアナト、イソシアナト、アミノおよびアミドから選ばれる含窒素基;ヒドロキシ、カルボキシル、アシルおよびアルコキシカルボニルから選ばれる含酸素基;シリル、モノメチルシリル、ジメチルシリル、トリメチルシリル、モノフェニルシリル、ジフェニルシリルおよびトリフェニルシリルから選ばれる含ケイ素基;または、チオアルキルおよびチオアルコキシから選ばれる含イオウ基で置換されていてもよい。
本発明の1つの実施形態によれば、一般式(1)において、nが1を表すことが好ましくは、この場合、一般式(1)の酸無水物は、好ましくは、分子の中央が単結合またはビスフェニルで連結されている構造を有する。
nが1を表す場合、好ましくは、X1はR1と共に環状構造を形成しており、X2はR2と共に環状構造を形成している。
nが1を表す場合、好ましくは、Xは、単結合、置換または無置換の直鎖状アルキレン基、置換または無置換の分岐状アルキレン基、または、置換または無置換の環状アルキレン基を表す。
nが1を表す場合、好ましくは、上記環状構造は、それぞれ互いに独立に、置換または無置換で3価の環状脂肪族炭化水素基、置換または無置換で3価の環状ヘテロ脂肪族炭化水素基、置換または無置換で3価の芳香族炭化水素基、または、置換または無置換で3価のヘテロ芳香族炭化水素基を表す。
以上の基および構造において、1個以上のCH2基は、それぞれ互いに独立に、-CH=CH-、-C≡C-、-O-、-CO-、-CO-O-、-O-CO-、-S-、-SO2-、-NY1-または-SiY1Y2-で置き換えられていてもよい。
ただし、Y1およびY2は、それぞれ互いに独立に、H、炭素数1~5のアルキル基、炭素数1~5のアルコキシ基、炭素数2~5のアルケニル基または炭素数2~5のアルキニル基を表す。
nが1を表す場合、以上の基および構造において、1個以上の-CH=基は、それぞれ互いに独立に、-N=で置き換えられていてもよい。
nが1を表す場合、以上の基および構造において、1個以上の水素原子は、それぞれ互いに独立に、ブロモ、クロロ、フルオロおよびヨードから選ばれるハロゲン;メチル、エチル、プロピル、ブチル、ペンチル、ヘキシル、ヘプチル、オクチル、ノニル、デシル、ウンデシル、ドデシル、トリデシル、テトラデシルおよびペンタデシルから選ばれるアルキル基;メトキシ、エトキシ、プロポキシ、ブトキシ、ペントキシ、ヘキシルオキシ、ヘプチルオキシ、オクチルオキシ、ノニルオキシ、デシルオキシ、ウンデシルオキシ、ドデシルオキシ、トリデシルオキシおよびテトラデシルオキシから選ばれるアルコキシ基;ビニル、プロパ-1-および-2-エニル、ブタ-1-、-2-および-3-エニル、ペンタ-1-、-2-、-3-および-4-エニル、ヘキサ-1-、-2-、-3-、-4-および-5-エニル、ヘプタ-1-、-2-、-3-、-4-、-5-および-6-エニル、オクタ-1-、-2-、-3-、-4-、-5-、-6-および-7-エニル、ノナ-1-、-2-、-3-、-4-、-5-、-6-、-7-および-8-エニル、デカ-1-、-2-、-3-、-4-、-5-、-6-、-7-、-8-および-9-エニルから選ばれるアルケニル基;エチニルおよびプロパルギル基から選ばれるアルキニル基;置換または無置換のシクロヘキシル基;フェニル、トリル、キシリル、ベンジル、トリチル、スチリル、ナフチル、デカヒドロナフチル、テトラリルおよびナフトキノリルから選ばれるアリール基;フリル、チエニル、ピリジル、キノリルおよびモルホリノから選ばれるヘテロ環基;ニトロ、ニトロソ、シアノ、イソシアノ、シアナト、イソシアナト、アミノおよびアミドから選ばれる含窒素基;ヒドロキシ、カルボキシル、アシルおよびアルコキシカルボニルから選ばれる含酸素基;シリル、モノメチルシリル、ジメチルシリル、トリメチルシリル、モノフェニルシリル、ジフェニルシリルおよびトリフェニルシリルから選ばれる含ケイ素基;または、チオアルキルおよびチオアルコキシから選ばれる含イオウ基で置換されていてもよい。
本発明の他の実施形態によれば、一般式(1)において、nが0を表すことが好ましくは、この場合、一般式(1)の酸無水物においては、好ましくは、分子の中央が全体として環構造を形成している。
nが0を表す場合、好ましくは、X1、X2、R1およびR2は共に全体で環状構造を形成している。
nが0を表す場合、好ましくは、上記環状構造は、それぞれ互いに独立に、置換または無置換で4価の環状脂肪族炭化水素基、置換または無置換で4価の環状ヘテロ脂肪族炭化水素基、置換または無置換で4価の芳香族炭化水素基、または、置換または無置換で4価のヘテロ芳香族炭化水素基を表す。
以上の基および構造において、1個以上のCH2基は、それぞれ互いに独立に、-CH=CH-、-C≡C-、-O-、-CO-、-CO-O-、-O-CO-、-S-、-SO2-、-NY1-または-SiY1Y2-で置き換えられていてもよい。
ただし、Y1およびY2は、それぞれ互いに独立に、H、炭素数1~5のアルキル基、炭素数1~5のアルコキシ基、炭素数2~5のアルケニル基または炭素数2~5のアルキニル基を表す。
nが0を表す場合、以上の基および構造において、1個以上の-CH=基は、それぞれ互いに独立に、-N=で置き換えられていてもよい。
nが0を表す場合、好ましくは、以上の基および構造において、1個以上の水素原子は、それぞれ互いに独立に、ブロモ、クロロ、フルオロおよびヨードから選ばれるハロゲン;メチル、エチル、プロピル、ブチル、ペンチル、ヘキシル、ヘプチル、オクチル、ノニル、デシル、ウンデシル、ドデシル、トリデシル、テトラデシルおよびペンタデシルから選ばれるアルキル基;メトキシ、エトキシ、プロポキシ、ブトキシ、ペントキシ、ヘキシルオキシ、ヘプチルオキシ、オクチルオキシ、ノニルオキシ、デシルオキシ、ウンデシルオキシ、ドデシルオキシ、トリデシルオキシおよびテトラデシルオキシから選ばれるアルコキシ基;ビニル、プロパ-1-および-2-エニル、ブタ-1-、-2-および-3-エニル、ペンタ-1-、-2-、-3-および-4-エニル、ヘキサ-1-、-2-、-3-、-4-および-5-エニル、ヘプタ-1-、-2-、-3-、-4-、-5-および-6-エニル、オクタ-1-、-2-、-3-、-4-、-5-、-6-および-7-エニル、ノナ-1-、-2-、-3-、-4-、-5-、-6-、-7-および-8-エニル、デカ-1-、-2-、-3-、-4-、-5-、-6-、-7-、-8-および-9-エニルから選ばれるアルケニル基;エチニルおよびプロパルギル基から選ばれるアルキニル基;置換または無置換のシクロヘキシル基;フェニル、トリル、キシリル、ベンジル、トリチル、スチリル、ナフチル、デカヒドロナフチル、テトラリルおよびナフトキノリルから選ばれるアリール基;フリル、チエニル、ピリジル、キノリルおよびモルホリノから選ばれるヘテロ環基;ニトロ、ニトロソ、シアノ、イソシアノ、シアナト、イソシアナト、アミノおよびアミドから選ばれる含窒素基;ヒドロキシ、カルボキシル、アシルおよびアルコキシカルボニルから選ばれる含酸素基;シリル、モノメチルシリル、ジメチルシリル、トリメチルシリル、モノフェニルシリル、ジフェニルシリルおよびトリフェニルシリルから選ばれる含ケイ素基;または、チオアルキルおよびチオアルコキシから選ばれる含イオウ基で置換されていてもよい。
nが0または1のいずれを表す場合においても、前記環状構造の好ましい例としては、シクロブタン、ジメチルシクロブタン、テトラメチルシクロブタン、シクロペンタン、シクロヘキサン、シクロヘプタンおよびデカヒドロナフタレンから選ばれる環状完全飽和脂肪族炭化水素;シクロブテン、ジメチルシクロブテン、テトラメチルシクロブテン、シクロペンテン、シクロヘキセン、シクロヘプテンおよびテトラリンから選ばれる環状部分飽和脂肪族炭化水素;ベンゼン、トルエンおよびキシレンから選ばれるベンゼン類;ビス(フェニル)メタン、ビス(フェニル)エタン、ビス(フェニル)プロパン、ビス(フェニル)ブタン、ビス(フェニル)シクロヘキサン、ビス(フェニル)フェニルエタン、ビス(フェニル)ヘキサフルオロプロパン、ビス(フェニル)ジフェニルメタン、ビス(フェニル)ジクロロエチレンおよびビス(フェニル)スルホンから選ばれるジフェニルメタン;ビシクロオクタン、ビシクロヘプタン、ビシクロオクタ-エン、ビシクロヘプタ-エン、トリシクロオクタン、トリシクロデカン、トリシクロオクタ-エンおよびトリシクロデカ-エンから選ばれる橋かけ環状炭化水素;ビシクロヘキシル、ターシクロヘキシル、クォーターシクロヘキシル、ビフェニル、ターフェニルおよびクォーターフェニルから選ばれる環集合炭化水素;テトラヒドロフラン、ピペリジン、ピペラジン、モルホリン、キヌクリジン、ピロリジン、アゼチジン、オキセタン、アゼチジン-2-オン、アジリジンおよびトロパンから選ばれるヘテロ脂肪族炭化水素;ピロール、フラン、チオフェン、イミダゾール、ピラゾール、オキサゾール、イソオキサゾール、チアゾールおよびイソチアゾールから選ばれる5員環ヘテロ芳香族炭化水素;ピリジン、ピリミジン、ピリダジン、ピラジンおよびトリアジンから選ばれる6員環ヘテロ芳香族炭化水素;キノリン、イソキノリン、キナゾリン、フタラジン、プテリジン、クマリン、クロモン、ベンゾジアゼピン、インドール、ベンズイミダゾール、ベンゾフラン、プリン、アクリジン、フェノキサジンおよびフェノチアジンから選ばれる多環ヘテロ芳香族炭化水素;および、ペンタレン、インデン、ナフタレン、アズレン、ヘプタレン、ビフェニレン、インダセン、アセナフチレン、ナフタセン、フルオレン、フェナレン、フェナントレン、アントラセン、トリフェニレン、ピレン、クリセン、テトラセン、ピセン、ペリレン、ペンタフェン、ペンタセン、トリフェニレン、テトラフェニレン、ヘキサフェン、コロネンおよびオバレンから選ばれる縮合系芳香族炭化水素が挙げられる。
中でも、好ましくは、メチル、エチル、プロピル、ブチル、メトキシ、エトキシ、ビニル、フェニル、シクロブタン、シクロペンタン、シクロヘキサン、シクロブテン、シクロペンテン、シクロヘキセン、シクロヘプテン、ビシクロヘキシル、ビフェニルが挙げられる。
また、一般式(1)で表される酸無水物は左右対称な構造を有することが好ましい。
より具体的には、一般式(1)で表される酸無水物の好ましい例として、限定することなく、下式から成る群より選ばれる化合物が挙げられる。
ここで、非水系電解液に対する不溶性の指標として、以上で説明してきた一般式(1)で表される酸無水物は、好ましくは、特定の値の溶解度パラメータ(sp値)を有する溶媒に不溶であることが望ましい。具体的には、8.8~11.5の範囲内のsp値を有する溶媒に、一般式(1)で表される酸無水物が不溶であることが望ましい。
これは、次の理由による。即ち、有機溶媒の溶解度パラメータ(sp値)は、ヘキサン(7.3)、ジエチルエーテル(7.4)、ジエチルカーボネート(8.8)、トルエン(8.9)、ジメチルカーボネート(9.9)、酢酸エチル(9.1)、テトラヒドロフラン(9.1)、アセトン(10.0)、1,4-ジオキサン(10.0)、N-メチルピロリドン(11.3)、イソプロピルアルコール(11.5)、アセトニトリル(11.9)、ジメチルホルムアミド(12.0)、ジメチルスルホキシド(12.0)、γ-ブチロラクトン(12.6)、エタノール(12.7)、プロピレンカーボネート(13.3)、エチレンカーボネート(14.7)、メタノール(14.5)、水(23.4)であることが知られている。電解液溶媒は一般的に、ジメチルカーボネート、ジエチルカーボネート、プロピレンカーボネート、エチレンカーボネートの混合物であることが多い。この値から算出される非水系電解液のsp値は、8.8~11.5の範囲内に入る。よって、非水系電解液に溶解しないとは、sp値が8.8~11.5の溶媒に不溶であると言い換えることができるからである。
[正極]
<正極活物質層>
正極活物質層は、正極活物質を含み、正極活物質が正極用結着剤によって正極集電体上に結着した構造を有するものである。正極活物質は、充電時にリチウムイオンを電解液中へ放出し、放電時に電解液中からリチウムを吸蔵するものであり、LiMnO2、LixMn2O4(0<x<2)等の層状構造を持つマンガン酸リチウム、又はスピネル構造を有するマンガン酸リチウム;LiCoO2、LiNiO2、又はこれらの遷移金属の一部を他の金属で置き換えたもの;LiNi1/3Co1/3Mn1/3O2等の特定の遷移金属が半数を超えないリチウム遷移金属酸化物;これらのリチウム遷移金属酸化物において化学量論組成よりもLiを過剰にしたもの等が挙げられる。特に、LiαNiβCoγAlδO2(1≦α≦1.2、β+γ+δ=1、β≧0.7、γ≦0.2)又はLiαNiβCoγMnδO2(1≦α≦1.2、β+γ+δ=1、β≧0.6、γ≦0.2)が好ましい。正極活物質は、1種を単独で、又は2種以上を組み合わせて使用することができる。
<正極活物質層>
正極活物質層は、正極活物質を含み、正極活物質が正極用結着剤によって正極集電体上に結着した構造を有するものである。正極活物質は、充電時にリチウムイオンを電解液中へ放出し、放電時に電解液中からリチウムを吸蔵するものであり、LiMnO2、LixMn2O4(0<x<2)等の層状構造を持つマンガン酸リチウム、又はスピネル構造を有するマンガン酸リチウム;LiCoO2、LiNiO2、又はこれらの遷移金属の一部を他の金属で置き換えたもの;LiNi1/3Co1/3Mn1/3O2等の特定の遷移金属が半数を超えないリチウム遷移金属酸化物;これらのリチウム遷移金属酸化物において化学量論組成よりもLiを過剰にしたもの等が挙げられる。特に、LiαNiβCoγAlδO2(1≦α≦1.2、β+γ+δ=1、β≧0.7、γ≦0.2)又はLiαNiβCoγMnδO2(1≦α≦1.2、β+γ+δ=1、β≧0.6、γ≦0.2)が好ましい。正極活物質は、1種を単独で、又は2種以上を組み合わせて使用することができる。
上記正極活物質を結着して一体化する正極結着剤としては、具体的には、上記負極結着剤と同様のものを用いることができる。正極結着剤としては、汎用性、低コストの観点から、ポリフッ化ビニリデンが好ましい。使用する正極結着剤の量は、正極活物質100質量部に対して、2~10質量部であることが好ましい。正極結着剤の含有量が2質量部以上であれば、活物質同士あるいは活物質と集電体との密着性が向上し、サイクル特性が良好になり、10質量部以下であれば、活物質比率が向上し、正極容量を向上させることができる。
上記正極活物質層には、正極活物質のインピーダンスを低下させる目的で、導電補助材を添加してもよい。導電補助材としては、グラファイト、カーボンブラック、アセチレンブラック等の炭素質微粒子を用いることができる。
<正極用結着剤>
正極用結着剤としては、特に制限されるものではないが、例えば、ポリフッ化ビニリデン、ビニリデンフルオライド-ヘキサフルオロプロピレン共重合体、ビニリデンフルオライド-テトラフルオロエチレン共重合体、スチレン-ブタジエン共重合ゴム、ポリテトラフルオロエチレン、ポリプロピレン、ポリエチレン、ポリイミド、ポリアミドイミド等を用いることができる。これらの中でも、結着性が強いことから、ポリイミド、ポリアミドイミド、ポリアクリル酸(アルカリで中和されたリチウム塩、ナトリウム塩、カリウム塩を含む)、カルボキシメチルセルロース(アルカリで中和されたリチウム塩、ナトリウム塩、カリウム塩を含む)が好ましい。使用する正極用結着剤の量は、トレードオフの関係にある「十分な結着力」と「高エネルギー化」の観点から、負極活物質100質量部に対して、2~10質量部が好ましい。
正極用結着剤としては、特に制限されるものではないが、例えば、ポリフッ化ビニリデン、ビニリデンフルオライド-ヘキサフルオロプロピレン共重合体、ビニリデンフルオライド-テトラフルオロエチレン共重合体、スチレン-ブタジエン共重合ゴム、ポリテトラフルオロエチレン、ポリプロピレン、ポリエチレン、ポリイミド、ポリアミドイミド等を用いることができる。これらの中でも、結着性が強いことから、ポリイミド、ポリアミドイミド、ポリアクリル酸(アルカリで中和されたリチウム塩、ナトリウム塩、カリウム塩を含む)、カルボキシメチルセルロース(アルカリで中和されたリチウム塩、ナトリウム塩、カリウム塩を含む)が好ましい。使用する正極用結着剤の量は、トレードオフの関係にある「十分な結着力」と「高エネルギー化」の観点から、負極活物質100質量部に対して、2~10質量部が好ましい。
<正極用集電体>
正極用集電体は、結着剤により一体化される正極活物質を含む正極活物質層を支持し、外部端子との導通を可能とする導電性を有するものであればよく、具体的には、上記負極集電体と同様のものを用いることができる。
正極用集電体は、結着剤により一体化される正極活物質を含む正極活物質層を支持し、外部端子との導通を可能とする導電性を有するものであればよく、具体的には、上記負極集電体と同様のものを用いることができる。
<正極の作製方法>
正極電極の製造方法としては、特に制限はないが例えば、表面処理Mn系正極の粉体のみ、あるいは、表面処理Mn系正極の粉体とリチウムニッケル複合酸化物の粉体を、導電補助材および結着剤と共に、結着剤を溶解しうる適当な分散媒で混合(スラリー法)した上で、アルミ箔等の集電体上に塗布し、溶剤を乾燥した後、プレス等により圧縮して成膜する。尚、導電補助材としては特に制限は無く、カーボンブラック、アセチレンブラック、天然黒鉛、人工黒鉛、炭素繊維等の通常用いられるものを用いることができる。
正極電極の製造方法としては、特に制限はないが例えば、表面処理Mn系正極の粉体のみ、あるいは、表面処理Mn系正極の粉体とリチウムニッケル複合酸化物の粉体を、導電補助材および結着剤と共に、結着剤を溶解しうる適当な分散媒で混合(スラリー法)した上で、アルミ箔等の集電体上に塗布し、溶剤を乾燥した後、プレス等により圧縮して成膜する。尚、導電補助材としては特に制限は無く、カーボンブラック、アセチレンブラック、天然黒鉛、人工黒鉛、炭素繊維等の通常用いられるものを用いることができる。
[電解液]
電解液は、非プロトン性溶媒として、環状カーボネート類、鎖状カーボネート類、脂肪族カルボン酸エステル類、γ-ラクトン類、環状エーテル類、鎖状エーテル類およびそれらのフッ素誘導体、からなる群から選択された一以上の溶媒を含むことができる。具体的には、たとえばプロピレンカーボネート(PC)、エチレンカーボネート(EC)、ブチレンカーボネート(BC)、ビニレンカーボネート(VC)等の環状カーボネート類、ジメチルカーボネート(DMC)、ジエチルカーボネート(DEC)、エチルメチルカーボネート(EMC)、ジプロピルカーボネート(DPC)等の鎖状カーボネート類、ギ酸メチル、酢酸メチル、プロピオン酸エチル等の脂肪族カルボン酸エステル類、γ-ブチロラクトン等のγ-ラクトン類、1,2-ジエトキシエタン(DEE)、エトキシメトキシエタン(EME)等の鎖状エーテル類、テトラヒドロフラン、2-メチルテトラヒドロフラン等の環状エーテル類、ジメチルスルホキシド、1,3-ジオキソラン、ホルムアミド、アセトアミド、ジメチルホルムアミド、アセトニトリル、プロピルニトリル、ニトロメタン、エチルモノグライム、リン酸トリエステル、トリメトキシメタン、ジオキソラン誘導体、スルホラン、メチルスルホラン、1,3-ジメチル-2-イミダゾリジノン、3-メチル-2-オキサゾリジノン、プロピレンカーボネート誘導体、テトラヒドロフラン誘導体、エチルエーテル、N-メチルピロリドン、フッ素化カルボン酸エステル、メチル-2,2,2-トリフルオロエチルカーボネート、メチル-2,2,3,3,3-ペンタフルオロプロピルカーボネート、トリフルオロメチルエチレンカーボネート、モノフルオロメチルエチレンカーボネート、ジフルオロメチルエチレンカーボネート、4,5-ジフルオロ-1,3-ジオキソラン-2-オン、モノフルオロエチレンカーボネートなどのうち、一種または二種以上を混合して使用することができる。
電解液は、非プロトン性溶媒として、環状カーボネート類、鎖状カーボネート類、脂肪族カルボン酸エステル類、γ-ラクトン類、環状エーテル類、鎖状エーテル類およびそれらのフッ素誘導体、からなる群から選択された一以上の溶媒を含むことができる。具体的には、たとえばプロピレンカーボネート(PC)、エチレンカーボネート(EC)、ブチレンカーボネート(BC)、ビニレンカーボネート(VC)等の環状カーボネート類、ジメチルカーボネート(DMC)、ジエチルカーボネート(DEC)、エチルメチルカーボネート(EMC)、ジプロピルカーボネート(DPC)等の鎖状カーボネート類、ギ酸メチル、酢酸メチル、プロピオン酸エチル等の脂肪族カルボン酸エステル類、γ-ブチロラクトン等のγ-ラクトン類、1,2-ジエトキシエタン(DEE)、エトキシメトキシエタン(EME)等の鎖状エーテル類、テトラヒドロフラン、2-メチルテトラヒドロフラン等の環状エーテル類、ジメチルスルホキシド、1,3-ジオキソラン、ホルムアミド、アセトアミド、ジメチルホルムアミド、アセトニトリル、プロピルニトリル、ニトロメタン、エチルモノグライム、リン酸トリエステル、トリメトキシメタン、ジオキソラン誘導体、スルホラン、メチルスルホラン、1,3-ジメチル-2-イミダゾリジノン、3-メチル-2-オキサゾリジノン、プロピレンカーボネート誘導体、テトラヒドロフラン誘導体、エチルエーテル、N-メチルピロリドン、フッ素化カルボン酸エステル、メチル-2,2,2-トリフルオロエチルカーボネート、メチル-2,2,3,3,3-ペンタフルオロプロピルカーボネート、トリフルオロメチルエチレンカーボネート、モノフルオロメチルエチレンカーボネート、ジフルオロメチルエチレンカーボネート、4,5-ジフルオロ-1,3-ジオキソラン-2-オン、モノフルオロエチレンカーボネートなどのうち、一種または二種以上を混合して使用することができる。
本実施形態の二次電池用電解液において、さらに電解質としてリチウム塩を含む構成とすることができる。こうすることにより、リチウムイオンを移動物質とすることができるため、電池特性を向上させることができる。リチウム塩としてたとえばリチウムイミド塩、LiPF6、LiBF4、LiAsF6、LiSbF6、LiClO4、LiAlCl4、LiN(CnF2n+1SO2)(CmF2m+1SO2)(n、mは自然数)の中から選択された一以上の物質を含む構成とすることができる。また、特にLiPF6またはLiBF4を用いることが好ましい。これらを用いることにより、リチウム塩の電気伝導率を高めることができ、二次電池のサイクル特性をさらに向上させることができる。
[セパレータ]
セパレータとしては、特に制限されるものではないが、ポリプロピレン、ポリエチレン等の多孔質フィルムや不織布を用いることができる。また、セパレータとしては、それらを積層したものを用いることもできる。
セパレータとしては、特に制限されるものではないが、ポリプロピレン、ポリエチレン等の多孔質フィルムや不織布を用いることができる。また、セパレータとしては、それらを積層したものを用いることもできる。
[外装体]
外装体としては、特に制限されるものではないが、例えば、ラミネートフィルムを用いることができる。ラミネートフィルムとしては、電解液に安定でかつ十分な水蒸気バリア性を持つものであれば、適宜選択することができる。ラミネートフィルムとしては、例えば、外装体として、アルミニウム、シリカ、アルミナをコーティングしたポリプロピレン、ポリエチレン等のラミネートフィルムを用いることができる。特に、体積膨張を抑制する観点から、アルミニウムラミネートフィルムが好ましい。
外装体としては、特に制限されるものではないが、例えば、ラミネートフィルムを用いることができる。ラミネートフィルムとしては、電解液に安定でかつ十分な水蒸気バリア性を持つものであれば、適宜選択することができる。ラミネートフィルムとしては、例えば、外装体として、アルミニウム、シリカ、アルミナをコーティングしたポリプロピレン、ポリエチレン等のラミネートフィルムを用いることができる。特に、体積膨張を抑制する観点から、アルミニウムラミネートフィルムが好ましい。
外装体としてラミネートフィルムを用いた二次電池の場合、外装体として金属缶を用いた二次電池に比べて、ガスが発生すると電極素子の歪みが非常に大きくなる。これは、ラミネートフィルムが金属缶に比べて二次電池の内圧により変形しやすいためである。さらに、外装体としてラミネートフィルムを用いた二次電池を封止する際には、通常、電池内圧を大気圧より低くするため、内部に余分な空間がなく、ガスが発生した場合にそれが直ちに電池の体積変化や電極素子の変形につながる場合がある。
本実施形態に係る二次電池では、上記問題を克服することができる。それにより、安価かつ積層数の変更によるセル容量の設計の自由度に優れた、積層ラミネート型のリチウムイオン二次電池を提供することができる。ラミネートフィルムの代表的な層構成としては、金属薄膜層と熱融着性樹脂層とが積層された構成が挙げられる。また、ラミネートフィルムの代表的な層構成としては、その他にも、金属薄膜層の熱融着樹脂層と反対側の面に、さらにポリエチレンテレフタレートなどのポリエステルやナイロン等のフィルムからなる保護層が積層された構成が挙げられる。電池要素を封止する場合、熱融着性樹脂層を対向させて電池要素が包囲される。金属薄膜層としては、例えば、厚さ10~100μmの、Al、Ti、Ti合金、Fe、ステンレス、Mg合金などの箔が用いられる。熱融着性樹脂層に用いられる樹脂は、熱融着が可能な樹脂であれば特に制限はない。例えば、ポリプロピレン、ポリエチレン、これらの酸変成物、ポリフェニレンサルファイド、ポリエチレンテレフタレートなどのポリエステル、ポリアミド、エチレン-酢酸ビニル共重合体、エチレン-メタクリル酸共重合体やエチレン-アクリル酸共重合体を金属イオンで分子間結合させたアイオノマー樹脂などが、熱融着性樹脂層として用いられる。熱融着性樹脂層の厚さは10~200μmが好ましく、より好ましくは30~100μmである。
[電池構成]
二次電池の構成は、特に制限されるものではないが、例えば、正極および負極が対向配置された電極素子と、電解液と、が外装体に内包されている積層ラミネート型とすることができる。図1は、積層ラミネート型の二次電池が有する電極素子の構造を示す模式的断面図である。この電極素子は、平面構造を有する正極1の複数および負極3の複数が、セパレータ2を挟みつつ交互に積み重ねられて形成されている。各正極1が有する正極集電体1bは、正極活物質層1aに覆われていない端部で互いに溶接されて電気的に接続され、さらにその溶接箇所に正極端子4が溶接されている。各負極3が有する負極集電体3bは、負極活物質層3aに覆われていない端部で互いに溶接されて電気的に接続され、さらにその溶接箇所に負極端子6が溶接されている。さらに、正極端子4は正極タブ5に、負極端子6は負極タブ7に溶接されている。このような平面的な積層構造を有する電極素子は、Rの小さい部分(捲回構造の巻き芯に近い領域)がないため、捲回構造を持つ電極素子に比べて、充放電に伴う電極の体積変化に対する悪影響を受けにくいという利点がある。すなわち、体積膨張を起こしやすい活物質を用いた電極素子として有効である。一方で、捲回構造を持つ電極素子では電極が湾曲しているため、体積変化が生じた場合にその構造が歪みやすい。特に、ケイ素酸化物のように充放電に伴う体積変化が大きい負極活物質を用いた場合、捲回構造を持つ電極素子を用いた二次電池では、充放電に伴う容量低下が大きい。
二次電池の構成は、特に制限されるものではないが、例えば、正極および負極が対向配置された電極素子と、電解液と、が外装体に内包されている積層ラミネート型とすることができる。図1は、積層ラミネート型の二次電池が有する電極素子の構造を示す模式的断面図である。この電極素子は、平面構造を有する正極1の複数および負極3の複数が、セパレータ2を挟みつつ交互に積み重ねられて形成されている。各正極1が有する正極集電体1bは、正極活物質層1aに覆われていない端部で互いに溶接されて電気的に接続され、さらにその溶接箇所に正極端子4が溶接されている。各負極3が有する負極集電体3bは、負極活物質層3aに覆われていない端部で互いに溶接されて電気的に接続され、さらにその溶接箇所に負極端子6が溶接されている。さらに、正極端子4は正極タブ5に、負極端子6は負極タブ7に溶接されている。このような平面的な積層構造を有する電極素子は、Rの小さい部分(捲回構造の巻き芯に近い領域)がないため、捲回構造を持つ電極素子に比べて、充放電に伴う電極の体積変化に対する悪影響を受けにくいという利点がある。すなわち、体積膨張を起こしやすい活物質を用いた電極素子として有効である。一方で、捲回構造を持つ電極素子では電極が湾曲しているため、体積変化が生じた場合にその構造が歪みやすい。特に、ケイ素酸化物のように充放電に伴う体積変化が大きい負極活物質を用いた場合、捲回構造を持つ電極素子を用いた二次電池では、充放電に伴う容量低下が大きい。
ところが、平面的な積層構造を持つ電極素子には、電極間にガスが発生した際に、その発生したガスが電極間に滞留しやすい問題点がある。これは、捲回構造を持つ電極素子の場合には電極に張力が働いているため電極間の間隔が広がりにくいのに対して、積層構造を持つ電極素子の場合には電極間の間隔が広がりやすいためである。外装体がアルミラミネートフィルムであった場合、この問題は特に顕著となる。
本発明では、一般式(1)で表される酸無水物を負極活物質表面に付着させ、恐らく、皮膜が形成されるため、上記の問題を解決することができ、高エネルギー型の負極を用いた積層ラミネート型のリチウムイオン二次電池においても、長寿命駆動が可能となる。
従って、本発明の1実施形態の二次電池は、正極および負極が対向配置された電極素子と、電解液と、前記電極素子および前記電解液を内包する外装体とを有する積層ラミネート型の二次電池であって、前記負極は、リチウムと合金可能な金属(a)およびリチウムイオンを吸蔵、放出し得る金属酸化物(b)の少なくとも1つを含む負極活物質を含み、かつ負極用結着剤によって負極集電体と結着されており、負極活物質表面に一般式(1)で表される酸無水物が付着されているか、または、皮膜が形成されている。但し、一般式(1)で表される酸無水物は、捲回構造を持つ電極素子を用いた二次電池においても有効である。
[発明の他の実施形態]
上記実施の形態において、表面処理Mn系正極を主とした正極活物質に、LiCoO2等の一般的に正極活物質として知られている化合物を混合して用いることもできる。また、安全性等のためにLi2CO3等の通常用いられる添加物質をさらに加えることもできる。
上記実施の形態において、表面処理Mn系正極を主とした正極活物質に、LiCoO2等の一般的に正極活物質として知られている化合物を混合して用いることもできる。また、安全性等のためにLi2CO3等の通常用いられる添加物質をさらに加えることもできる。
また、上記実施の形態において、電池の外装体としては、角型、ペーパー型、積層型、円筒型、コイン型など種々の形状を採用することが出来る。外装材料その他の構成部材は特に限定されるものではなく、電池形状に応じて選定すればよい。一例を挙げると、フィルム状外装体を、ポリエチレンテレフタレートなどの耐熱性樹脂膜に直接あるいは接着剤を介して前述の熱融着性樹脂膜をラミネートしたフィルム、あるいは熱融着性樹脂膜単独フィルムなどで構成することができる。
また、電解液は、スルホニル基を少なくとも2個有する環式スルホン酸エステルに加え、一以上のスルホニル基を有する化合物をさらに含む構成とすることもできる。
以下に本発明の実施例を具体的に説明するが、本発明はこれらに限定されるものではない。
[負極の製作]
負極シートをカーボン:PVDF=90:10(質量%)の比率となるように混合し、NMPに分散させた。さらに、酸無水物をカーボンに対して0.5質量%添加し、さらに分散させた。得られた酸無水物混合スラリーを、厚さ20μmの銅箔上に塗布して乾燥後、さらにプレスすることで、負極を製作した。
負極シートをカーボン:PVDF=90:10(質量%)の比率となるように混合し、NMPに分散させた。さらに、酸無水物をカーボンに対して0.5質量%添加し、さらに分散させた。得られた酸無水物混合スラリーを、厚さ20μmの銅箔上に塗布して乾燥後、さらにプレスすることで、負極を製作した。
[正極の製作]
マンガン酸リチウム、LiNi0.8Co0.2O2および導電性付与剤を乾式混合し、バインダーであるPVDFを溶解させたN-メチル-2-ピロリドン(NMP)中に均一に分散させて、スラリーを作製した。導電性付与剤としては、カーボンブラックを用いた。そのスラリーを厚さ25μmのアルミ金属箔上に塗布後、NMPを蒸発させ、さらに正極シートをプレスすることで、正極を製作した。正極中の固形分比率はマンガン酸リチウム:LiNi0.8Co0.2O2:導電性付与剤:PVDF=72:8:10:10(質量%)の混合比(a=10)とした。
マンガン酸リチウム、LiNi0.8Co0.2O2および導電性付与剤を乾式混合し、バインダーであるPVDFを溶解させたN-メチル-2-ピロリドン(NMP)中に均一に分散させて、スラリーを作製した。導電性付与剤としては、カーボンブラックを用いた。そのスラリーを厚さ25μmのアルミ金属箔上に塗布後、NMPを蒸発させ、さらに正極シートをプレスすることで、正極を製作した。正極中の固形分比率はマンガン酸リチウム:LiNi0.8Co0.2O2:導電性付与剤:PVDF=72:8:10:10(質量%)の混合比(a=10)とした。
[ラミネートセル製作]
ポリプロピレン樹脂(封着層、厚み70μm)、ポリエチレンテレフタレート(20μm)、アルミニウム(50μm)、ポリエチレンテレフタレート(20μm)の順に積層した構造を有するラミネートフィルムを所定の大きさに2枚切り出し、その一部分に上記の積層電極体の大きさに合った底面部分と側面部分とを有する凹部を形成した。これらを対向させて上記の積層電極体を包み込み、周囲を熱融着させてフィルム外装電池を作製した。最後の1辺を熱融着封口する前に、EC/DEC=30/70(体積比)からなるカーボネート系非水電解溶媒に支持塩としてのLiPF6を1mol/Lの濃度で溶解させた電解液を注液した後、0.1気圧まで減圧しつつ積層電極体に含浸させ、封止することで、アルミラミネート型の二次電池を製作した。
ポリプロピレン樹脂(封着層、厚み70μm)、ポリエチレンテレフタレート(20μm)、アルミニウム(50μm)、ポリエチレンテレフタレート(20μm)の順に積層した構造を有するラミネートフィルムを所定の大きさに2枚切り出し、その一部分に上記の積層電極体の大きさに合った底面部分と側面部分とを有する凹部を形成した。これらを対向させて上記の積層電極体を包み込み、周囲を熱融着させてフィルム外装電池を作製した。最後の1辺を熱融着封口する前に、EC/DEC=30/70(体積比)からなるカーボネート系非水電解溶媒に支持塩としてのLiPF6を1mol/Lの濃度で溶解させた電解液を注液した後、0.1気圧まで減圧しつつ積層電極体に含浸させ、封止することで、アルミラミネート型の二次電池を製作した。
[電池特性評価]
アルミラミネート電池は、室温(25℃)において、終止電圧4.3Vまで充電し、次に2.5Vまで放電した。その後、60℃において定電流電圧でサイクル充放電および保存特性評価を行い、容量維持率を評価した。
アルミラミネート電池は、室温(25℃)において、終止電圧4.3Vまで充電し、次に2.5Vまで放電した。その後、60℃において定電流電圧でサイクル充放電および保存特性評価を行い、容量維持率を評価した。
(実施例1)
一般式(1)で示される酸無水物として、式(2)で示される化合物を炭素に対して0.5質量%添加して負極を製作した。負極を所定の大きさに切りだし、上述の方法でアルミラミネートセルを製作した。
一般式(1)で示される酸無水物として、式(2)で示される化合物を炭素に対して0.5質量%添加して負極を製作した。負極を所定の大きさに切りだし、上述の方法でアルミラミネートセルを製作した。
(実施例2~4)
酸無水物として、それぞれ、式(4)、(5)および(7)で示される化合物を用いたこと以外は、実施例1と同様にしてアルミラミネート型二次電池を製作した。
酸無水物として、それぞれ、式(4)、(5)および(7)で示される化合物を用いたこと以外は、実施例1と同様にしてアルミラミネート型二次電池を製作した。
(実施例5~8)
酸無水物として、それぞれ、式(2)、(4)、(5)および(7)で示される化合物を1.0質量%用いたこと以外は、実施例1と同様にしてアルミラミネート型二次電池を製作した。
酸無水物として、それぞれ、式(2)、(4)、(5)および(7)で示される化合物を1.0質量%用いたこと以外は、実施例1と同様にしてアルミラミネート型二次電池を製作した。
(比較例1)
負極製作時に、負極スラリーに酸無水物を添加することなく、負極を製作したこと以外は、実施例1と同様の方法でアルミラミネートセルを製作した。
負極製作時に、負極スラリーに酸無水物を添加することなく、負極を製作したこと以外は、実施例1と同様の方法でアルミラミネートセルを製作した。
<評価>
実施例1~8および比較例1で作製した二次電池について、高温環境下におけるサイクル特性、保存特性を評価した。具体的には、二次電池に対し、60℃に保った恒温槽中で2.5Vから4.1Vの電圧範囲で200回充放電を繰り返す試験を行った。そして、(200サイクル目の放電容量)/(5サイクル目の放電容量)(単位:%)を維持率として算出した。また保存特性は、(高温保管前容量)/(2週間後保管後容量)(単位:%)を膨れ率として算出した。その結果を表1に示す。なお、維持率については、95%以上で「◎」、90%以上95%未満で「○」、90%未満で△とした。
実施例1~8および比較例1で作製した二次電池について、高温環境下におけるサイクル特性、保存特性を評価した。具体的には、二次電池に対し、60℃に保った恒温槽中で2.5Vから4.1Vの電圧範囲で200回充放電を繰り返す試験を行った。そして、(200サイクル目の放電容量)/(5サイクル目の放電容量)(単位:%)を維持率として算出した。また保存特性は、(高温保管前容量)/(2週間後保管後容量)(単位:%)を膨れ率として算出した。その結果を表1に示す。なお、維持率については、95%以上で「◎」、90%以上95%未満で「○」、90%未満で△とした。
本実施形態は、例えば、電源を必要とするあらゆる産業分野、ならびに電気的エネルギーの輸送、貯蔵および供給に関する産業分野にて利用することができる。具体的には、携帯電話、ノートパソコンなどのモバイル機器の電源;電気自動車、ハイブリッドカー、電動バイク、電動アシスト自転車などの電動車両を含む、電車や衛星や潜水艦などの移動・輸送用媒体の電源;UPSなどのバックアップ電源;太陽光発電、風力発電などで発電した電力を貯める蓄電設備;などに、利用することができる。
[付記]
本出願は、以下の事項にも関する。
[付記]
本出願は、以下の事項にも関する。
(付記1)正極および負極が対向配置された電極素子と、非水溶媒系電解液とを備えるリチウム二次電池であって、該負極の活物質の表面上には一般式(1)で表される酸無水物が施されているリチウム二次電池。
(付記2)少なくとも前記負極および前記非水溶媒系電解液を内包する外装体を備え、該外装体はラミネートフィルムである付記1に記載のリチウム二次電池。
(付記3)前記電極素子において、前記正極および前記負極がセパレータを介して積層配置されている付記1または2に記載の積層ラミネート型リチウム二次電池。
(付記4)正極および負極が対向配置された電極素子と、非水溶媒系電解液とを備えるリチウム二次電池であって、該負極の活物質の表面上には一般式(1)で表される酸無水物が施されているリチウム二次電池を2個以上使用する組電池。
(付記5)正極および負極が対向配置された電極素子と、非水溶媒系電解液とを備えるリチウム二次電池であって、該負極の活物質の表面上には一般式(1)で表される酸無水物が施されているリチウム二次電池、または、該リチウム二次電池を2個以上使用する組電池をモータ駆動用電源として搭載する車両。
1a 正極活物質層
1b 正極集電体
2 セパレータ
3a 負極活物質層
3b 負極集電体
4 正極端子
5 正極タブ
6 負極端子
7 負極タブ
1b 正極集電体
2 セパレータ
3a 負極活物質層
3b 負極集電体
4 正極端子
5 正極タブ
6 負極端子
7 負極タブ
Claims (10)
- 一般式(1)で表される酸無水物は左右対称な構造を有する請求項1に記載のリチウム二次電池用負極。
- nが1を表し、X1はR1と共に環状構造を形成しており、X2はR2と共に環状構造を形成しており、
Xは、単結合、置換または無置換の直鎖状アルキレン基、置換または無置換の分岐状アルキレン基、または、置換または無置換の環状アルキレン基を表し、
該環状構造は、それぞれ互いに独立に、置換または無置換で3価の環状脂肪族炭化水素基、置換または無置換で3価の環状ヘテロ脂肪族炭化水素基、置換または無置換で3価の芳香族炭化水素基、または、置換または無置換で3価のヘテロ芳香族炭化水素基を表し、
以上の基および構造において、1個以上のCH2基は、それぞれ互いに独立に、-CH=CH-、-C≡C-、-O-、-CO-、-CO-O-、-O-CO-、-S-、-SO2-、-NY1-または-SiY1Y2-で置き換えられていてもよく、
ただし、Y1およびY2は、それぞれ互いに独立に、H、炭素数1~5のアルキル基、炭素数1~5のアルコキシ基、炭素数2~5のアルケニル基または炭素数2~5のアルキニル基を表し、
以上の基および構造において、1個以上の-CH=基は、それぞれ互いに独立に、-N=で置き換えられていてもよく、
以上の基および構造において、1個以上の水素原子は、それぞれ互いに独立に、ブロモ、クロロ、フルオロおよびヨードから選ばれるハロゲン;メチル、エチル、プロピル、ブチル、ペンチル、ヘキシル、ヘプチル、オクチル、ノニル、デシル、ウンデシル、ドデシル、トリデシル、テトラデシルおよびペンタデシルから選ばれるアルキル基;メトキシ、エトキシ、プロポキシ、ブトキシ、ペントキシ、ヘキシルオキシ、ヘプチルオキシ、オクチルオキシ、ノニルオキシ、デシルオキシ、ウンデシルオキシ、ドデシルオキシ、トリデシルオキシおよびテトラデシルオキシから選ばれるアルコキシ基;ビニル、プロパ-1-および-2-エニル、ブタ-1-、-2-および-3-エニル、ペンタ-1-、-2-、-3-および-4-エニル、ヘキサ-1-、-2-、-3-、-4-および-5-エニル、ヘプタ-1-、-2-、-3-、-4-、-5-および-6-エニル、オクタ-1-、-2-、-3-、-4-、-5-、-6-および-7-エニル、ノナ-1-、-2-、-3-、-4-、-5-、-6-、-7-および-8-エニル、デカ-1-、-2-、-3-、-4-、-5-、-6-、-7-、-8-および-9-エニルから選ばれるアルケニル基;エチニルおよびプロパルギル基から選ばれるアルキニル基;置換または無置換のシクロヘキシル基;フェニル、トリル、キシリル、ベンジル、トリチル、スチリル、ナフチル、デカヒドロナフチル、テトラリルおよびナフトキノリルから選ばれるアリール基;フリル、チエニル、ピリジル、キノリルおよびモルホリノから選ばれるヘテロ環基;ニトロ、ニトロソ、シアノ、イソシアノ、シアナト、イソシアナト、アミノおよびアミドから選ばれる含窒素基;ヒドロキシ、カルボキシル、アシルおよびアルコキシカルボニルから選ばれる含酸素基;シリル、モノメチルシリル、ジメチルシリル、トリメチルシリル、モノフェニルシリル、ジフェニルシリルおよびトリフェニルシリルから選ばれる含ケイ素基;または、チオアルキルおよびチオアルコキシから選ばれる含イオウ基で置換されていてもよい請求項1または2に記載のリチウム二次電池用負極。 - nが0を表し、X1、X2、R1およびR2は共に全体で環状構造を形成しており、
該環状構造は、それぞれ互いに独立に、置換または無置換で4価の環状脂肪族炭化水素基、置換または無置換で4価の環状ヘテロ脂肪族炭化水素基、置換または無置換で4価の芳香族炭化水素基、または、置換または無置換で4価のヘテロ芳香族炭化水素基を表し、
以上の基および構造において、1個以上のCH2基は、それぞれ互いに独立に、-CH=CH-、-C≡C-、-O-、-CO-、-CO-O-、-O-CO-、-S-、-SO2-、-NY1-または-SiY1Y2-で置き換えられていてもよく、
ただし、Y1およびY2は、それぞれ互いに独立に、H、炭素数1~5のアルキル基、炭素数1~5のアルコキシ基、炭素数2~5のアルケニル基または炭素数2~5のアルキニル基を表し、
以上の基および構造において、1個以上の-CH=基は、それぞれ互いに独立に、-N=で置き換えられていてもよく、
以上の基および構造において、1個以上の水素原子は、それぞれ互いに独立に、ブロモ、クロロ、フルオロおよびヨードから選ばれるハロゲン;メチル、エチル、プロピル、ブチル、ペンチル、ヘキシル、ヘプチル、オクチル、ノニル、デシル、ウンデシル、ドデシル、トリデシル、テトラデシルおよびペンタデシルから選ばれるアルキル基;メトキシ、エトキシ、プロポキシ、ブトキシ、ペントキシ、ヘキシルオキシ、ヘプチルオキシ、オクチルオキシ、ノニルオキシ、デシルオキシ、ウンデシルオキシ、ドデシルオキシ、トリデシルオキシおよびテトラデシルオキシから選ばれるアルコキシ基;ビニル、プロパ-1-および-2-エニル、ブタ-1-、-2-および-3-エニル、ペンタ-1-、-2-、-3-および-4-エニル、ヘキサ-1-、-2-、-3-、-4-および-5-エニル、ヘプタ-1-、-2-、-3-、-4-、-5-および-6-エニル、オクタ-1-、-2-、-3-、-4-、-5-、-6-および-7-エニル、ノナ-1-、-2-、-3-、-4-、-5-、-6-、-7-および-8-エニル、デカ-1-、-2-、-3-、-4-、-5-、-6-、-7-、-8-および-9-エニルから選ばれるアルケニル基;エチニルおよびプロパルギル基から選ばれるアルキニル基;置換または無置換のシクロヘキシル基;フェニル、トリル、キシリル、ベンジル、トリチル、スチリル、ナフチル、デカヒドロナフチル、テトラリルおよびナフトキノリルから選ばれるアリール基;フリル、チエニル、ピリジル、キノリルおよびモルホリノから選ばれるヘテロ環基;ニトロ、ニトロソ、シアノ、イソシアノ、シアナト、イソシアナト、アミノおよびアミドから選ばれる含窒素基;ヒドロキシ、カルボキシル、アシルおよびアルコキシカルボニルから選ばれる含酸素基;シリル、モノメチルシリル、ジメチルシリル、トリメチルシリル、モノフェニルシリル、ジフェニルシリルおよびトリフェニルシリルから選ばれる含ケイ素基;または、チオアルキルおよびチオアルコキシから選ばれる含イオウ基で置換されていてもよい請求項1または2に記載のリチウム二次電池用負極。 - 前記環状構造は、シクロブタン、ジメチルシクロブタン、テトラメチルシクロブタン、シクロペンタン、シクロヘキサン、シクロヘプタンおよびデカヒドロナフタレンから選ばれる環状完全飽和脂肪族炭化水素;シクロブテン、ジメチルシクロブテン、テトラメチルシクロブテン、シクロペンテン、シクロヘキセン、シクロヘプテンおよびテトラリンから選ばれる環状部分飽和脂肪族炭化水素;ベンゼン、トルエンおよびキシレンから選ばれるベンゼン類;ビス(フェニル)メタン、ビス(フェニル)エタン、ビス(フェニル)プロパン、ビス(フェニル)ブタン、ビス(フェニル)シクロヘキサン、ビス(フェニル)フェニルエタン、ビス(フェニル)ヘキサフルオロプロパン、ビス(フェニル)ジフェニルメタン、ビス(フェニル)ジクロロエチレンおよびビス(フェニル)スルホンから選ばれるジフェニルメタン;ビシクロオクタン、ビシクロヘプタン、ビシクロオクタ-エン、ビシクロヘプタ-エン、トリシクロオクタン、トリシクロデカン、トリシクロオクタ-エンおよびトリシクロデカ-エンから選ばれる橋かけ環状炭化水素;ビシクロヘキシル、ターシクロヘキシル、クォーターシクロヘキシル、ビフェニル、ターフェニルおよびクォーターフェニルから選ばれる環集合炭化水素;テトラヒドロフラン、ピペリジン、ピペラジン、モルホリン、キヌクリジン、ピロリジン、アゼチジン、オキセタン、アゼチジン-2-オン、アジリジンおよびトロパンから選ばれるヘテロ脂肪族炭化水素;ピロール、フラン、チオフェン、イミダゾール、ピラゾール、オキサゾール、イソオキサゾール、チアゾールおよびイソチアゾールから選ばれる5員環ヘテロ芳香族炭化水素;ピリジン、ピリミジン、ピリダジン、ピラジンおよびトリアジンから選ばれる6員環ヘテロ芳香族炭化水素;キノリン、イソキノリン、キナゾリン、フタラジン、プテリジン、クマリン、クロモン、ベンゾジアゼピン、インドール、ベンズイミダゾール、ベンゾフラン、プリン、アクリジン、フェノキサジンおよびフェノチアジンから選ばれる多環ヘテロ芳香族炭化水素;または、ペンタレン、インデン、ナフタレン、アズレン、ヘプタレン、ビフェニレン、インダセン、アセナフチレン、ナフタセン、フルオレン、フェナレン、フェナントレン、アントラセン、トリフェニレン、ピレン、クリセン、テトラセン、ピセン、ペリレン、ペンタフェン、ペンタセン、トリフェニレン、テトラフェニレン、ヘキサフェン、コロネンおよびオバレンから選ばれる縮合系芳香族炭化水素より誘導される請求項1~4のいずれか1項に記載のリチウム二次電池用負極。
- 一般式(1)で表される酸無水物は、溶解度パラメータ(sp値)が8.8~11.5の溶媒に不溶である請求項1~6のいずれか1項に記載のリチウム二次電池用負極。
- 請求項1~7のいずれか1項に記載の酸無水物が負極活物質の表面に付着しているか、または、皮膜を形成している請求項1~7のいずれか1項に記載のリチウム二次電池用負極。
- 該負極活物質に対する該酸無水物の量は、0.001質量%以上および5.0質量%以下である請求項8に記載のリチウム二次電池用負極。
- 一般式(1)で表される酸無水物を含むリチウム二次電池用負極を製造する方法であって、
該酸無水物を分散してスラリーを調製する工程と、
該スラリーを塗布し、乾燥する工程と
を含む製造方法。
X1、X2およびXは、それぞれ互いに独立に、炭素数1~50の炭化水素基または単結合を表し、
R1およびR2は、それぞれ互いに独立に、炭素数1~6の炭化水素基または水素を表し、
m1およびm2は、それぞれ互いに独立に、1または2を表し、
n1、n2およびnは、それぞれ互いに独立に、0または1を表し、
ただし、nが1を表す場合、X1はR1と共に環状構造を形成していてもよく、X2はR2と共に環状構造を形成していてもよく、
ただし、nが0を表す場合、X1、X2、R1およびR2は共に全体で環状構造を形成していてもよい。)