WO2014098370A1 - 탄소나노튜브를 포함하는 초경합금의 제조방법, 이에 의해 제조된 초경합금 및 초경합금을 포함하여 이루어지는 초경 절삭공구 - Google Patents

탄소나노튜브를 포함하는 초경합금의 제조방법, 이에 의해 제조된 초경합금 및 초경합금을 포함하여 이루어지는 초경 절삭공구 Download PDF

Info

Publication number
WO2014098370A1
WO2014098370A1 PCT/KR2013/010004 KR2013010004W WO2014098370A1 WO 2014098370 A1 WO2014098370 A1 WO 2014098370A1 KR 2013010004 W KR2013010004 W KR 2013010004W WO 2014098370 A1 WO2014098370 A1 WO 2014098370A1
Authority
WO
WIPO (PCT)
Prior art keywords
cemented carbide
carbon nanotubes
powder
carbon nanotube
producing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/KR2013/010004
Other languages
English (en)
French (fr)
Inventor
김경태
하국현
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Korea Institute of Machinery and Materials KIMM
Original Assignee
Korea Institute of Machinery and Materials KIMM
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Korea Institute of Machinery and Materials KIMM filed Critical Korea Institute of Machinery and Materials KIMM
Publication of WO2014098370A1 publication Critical patent/WO2014098370A1/ko
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

본 발명은 탄소나노튜브를 포함하는 초경합금을 제조하는 방법에 관한 것이다. 구체적으로, 본 발명은 (a) 탄소나노튜브와 금속 분말로부터 탄소나노튜브-금속 복합체를 형성하는 단계; (b) 상기 단계 (a)에서 얻어진 탄소나노튜브-금속 복합체를 경질상 분말과 혼합하는 단계; (c) 상기 단계 (b)에서 얻어진 혼합 분말을 성형하는 단계; 및 (d) 상기 단계 (c)에서 얻어진 성형체를 소결하는 단계를 포함한다. 본 발명의 제조방법에 따르면, 초경합금에 포함되는 탄소나노튜브와 전이금속 탄화물 간의 반응을 최소화하여 탄소나노튜브 첨가에 따른 인성 증가 효과를 최대화하여 경도뿐만 아니라 인성이 뛰어난 초경합금을 제조할 수 있으며, 상기 제조방법에 의해 제조된 탄소나노튜브를 포함하는 초경합금은 고경도 및 고인성을 가지기 때문에 절삭 공구, 금형, 내마모 부재, 내열 구조 재료 등에 유용하게 사용 가능하다.

Description

탄소나노튜브를 포함하는 초경합금의 제조방법, 이에 의해 제조된 초경합금 및 초경합금을 포함하여 이루어지는 초경 절삭공구
본 발명은 초경합금의 제조방법, 이에 의해 제조된 초경합금 및 초경합금을 포함하여 이루어지는 초경 절삭공구에 관한 것으로, 보다 상세하게는 탄소나노튜브를 포함하는 초경합금의 제조방법, 이에 의해 제조된 초경합금 및 초경합금을 포함하여 이루어지는 초경 절삭공구에 관한 것에 관한 것이다.
초경합금이란 금속의 경도가 대단히 높은 원소 주기율표 상의 Ⅳ·Ⅴ·Ⅵ족의 전이금속 탄화물 등의 경질상 분말과 인성이 우수한 Fe, Co, Ni 등의 철족 금속 분말을 함께 소결하여 만든 합금으로서, 실온부터 고온까지 기계적 성질이 특히 우수하여 절삭공구, 내마모 부품 및 금형 등에 사용되고 있는 WC-Co계 합금을 대표적인 예로 들 수 있다.
초경합금의 기계적 특성은 화학적 조성, 전이금속 탄화물 등의 경질상 입자의 입도 분포 및 합금 중의 탄소량, 미세조직, 기공도, 결함 등에 의하여 영향을 받는데, 그 중에서도 경질상 입자의 크기와 경질상 입자 사이의 연질상인 금속층의 두께(mean free path)는 초경합금의 기계적 특성을 결정하는 가장 중요한 변수로서 높은 경도를 얻기 위해 기계적 특성 향상을 위해 경질상 입자의 크기를 감소시키고, 경질상 입자 사이의 금속층의 두께를 얇게 할 필요가 있다.
그러나, 수백 나노미터크기의 경질상 입자를 사용하거나 경질상 입자 사이의 금속층의 두께를 감소시키게 되면 경도는 향상되지만 상대적으로 인성이 감소하는 문제가 발생한다. 본 발명에서는 이를 해결하기 위하여 초경합금에 탄소나노튜브(carbon nanotube, CNT)를 금속 바인더내에 균질하게 분산시켜 금속층의 강도를 향상시키는 동시에 결정립계 사이를 CNT로 결합시켜 크랙 발생과 전파를 효과적으로 방어함으로서 기존의 인성저하 문제점을 해결하고자 한다.
하지만, 전이금속 탄화물 등의 경질상 분말, 금속 분말 및 탄소나노튜브를 한꺼번에 기계적으로 혼합하고, 이후 성형 및 소결 과정을 거쳐 초경합금을 만들 경우, 소결시 전이금속 탄화물이 탄소나노튜브와 반응을 일으켜 탄화물을 형성하거나, 텅스텐 카바이드의 화학양론비를 변화시키기 때문에 오히려 초경합금의 경도가 감소할 뿐만 아니라 탄소나노튜브의 응집문제 또한 해결할 수 없는 문제점이 발생할 수 있다. 대한민국 공개특허 제 10-2011-0044474호 (공개일 2011년 4월29일)에는 ‘나노구조 금속탄화물-탄소나노튜브 복합재료 및 그 제조방법’이 개시된 바 있으며, 금속탄화물과 탄소나노튜브를 한꺼번에 서로 혼합하여 복합재료를 제조하고 있는데 금속 탄화물의 입성장을 막을 수 있는 장점은 있으나, 개시된 미세조직과 같이 조대한 금속탄화물의 비정상입자성장이 발생하고 탄소나노튜브가 응집되거나 금속탄화물과 반응하는 문제를 해결하는 방안에 대한 언급이 없다. 따라서 종래의 발명으로부터 탄소나노튜브에 의한 금속 바인더 강화를 통한 인성증대효과와 연질상을 강하게 만들고 내마모성을 증대시키는 역할을 부여하는 본 발명의 효과를 기대하기 어렵다.
탄소나노튜브 첨가에 의한 경도와 인성향상효과가 나타나기 위해서는 금속 바인더 내부에 탄소나노튜브를 균일하게 분산시키는 것이 필수적이다. 또한 초경합금의 대표적인 응용분야인 절삭공구의 경우 최근 피절삭재의 강도와 경도가 높아짐에 따라 피삭재와의 마찰에 대한 높은 내마모성과 마찰시 발생하는 열을 효율적으로 배출할 수 있는 높은 열전도도의 재료가 요구되고 있다. 이러한 문제를 해결하기 위해서 흑연면과 동일한 마찰계수를 가지고 500 W/m ·K이상의 높은 열전도도를 가진 탄소나노튜브가 초경합금에 활용되어 그 특성을 발현한다면 우수한 물성의 초경 신소재 개발이 가능할 것으로 기대된다.
본 발명이 해결하고자 하는 기술적 과제는 탄소나노튜브를 포함하는 초경합금의 제조시 탄소나노튜브가 경질상 입자와 반응하는 것을 최소화하여 탄소나노튜브가 바인더내에 균질하게 분산된 초경합금을 제조할 수 있는 초경합금의 제조방법, 그에 의해 제조된 초경합금 및 그 초경합금을 포함하여 이루어지는 초경 절삭공구를 제공하는 것이다.
상기 기술적 과제를 달성하기 위해, 본 발명은 (a) 탄소나노튜브와 금속 분말로부터 탄소나노튜브-금속 복합체를 형성하는 단계; (b) 상기 단계 (a)에서 얻어진 탄소나노튜브-금속 복합체를 전이금속 탄화물 분말과 혼합하는 단계; (c) 상기 단계 (b)에서 얻어진 혼합 분말을 성형하는 단계; 및 (d) 상기 단계 (c)에서 얻어진 성형체를 소결하는 단계를 포함하는 탄소나노튜브를 포함한 초경합금의 제조방법, 그에 의해 제조되는 탄소나노튜브를 포함한 초경합금 및 그 초경합금을 포함하여 이루어지는 초경 절삭공구를 제안한다.
본 발명에 따르면, 초경합금에 포함되는 탄소나노튜브와 전이금속 탄화물 간의 반응을 최소화하여 탄소나노튜브 첨가에 따른 인성 증가 효과를 최대화하여 경도뿐만 아니라 인성이 뛰어난 초경합금을 제조할 수 있다. 또한, 탄소나노튜브의 내마모성과 우수한 열전도도에 의하여 고내마모성, 고열전도도 절삭공구용 차세대 재료로 사용될 수 있다.
도 1은 본 발명에 따른 탄소나노튜브를 포함한 초경합금 제조방법의 순서도이다.
도 2는 본 발명에 따른 탄소나노튜브를 포함한 초경합금 제조방법에 의해 제조될 수 있는 초경합금의 미세구조를 나타내는 개념도이다.
도 3은 본 발명에 따른 실시예 도중에 얻어지는 탄소나노튜브-Co 복합체 분말에 대한 주사전자현미경(SEM) 사진이다.
도 4는 본 발명에 따른 실시예 도중에 얻어지는 WC/탄소나노튜브-Co 분말에 대한 주사전자현미경(SEM) 사진이다.
도 5는 본 발명에 따른 실시예 도중에 얻어지는 WC/탄소나노튜브-Co 분말에 X-선 회절(XRD) 분석 결과이다.
도 6는 본 발명의 실시예에서 제조한 탄소나노튜브를 포함한 초경합금의 표면 미세구조를 나타내는 주사전자현미경(SEM) 사진이다.
도 7은 본 발명의 실시예 및 비교예에서 제조한 초경합금에 대한 경도(HV) 측정 결과를 나타내는 그래프이다.
도 8는 본 발명의 실시예 및 비교예에서 제조한 초경합금에 대한 파괴 인성(KIC) 측정 결과를 나타내는 그래프이다.
이하, 본 발명을 상세하게 설명한다.
도 1은 본 발명에 따른 탄소나노튜브를 포함한 초경합금의 제조 방법을 나타내는 순서도로서, 도 1에 도시하는 바와 같이 본 발명에 따른 탄소나노튜브를 포함한 초경합금의 제조방법은 (a) 탄소나노튜브와 금속 분말로부터 탄소나노튜브-금속 복합체를 형성하는 단계; (b) 단계 (a)에서 얻어진 탄소나노튜브-금속 복합체를 경질상 분말과 혼합하는 단계; (c) 단계 (b)에서 얻어진 혼합 분말을 성형하는 단계; 및 (d) 단계 (c)에서 얻어진 성형체를 소결하는 단계를 포함할 수 있다. 본 발명에 따른 탄소나노튜브를 포함한 초경합금의 제조방법에 의할 경우, 도 2에서와 같은 미세구조를 나타내는 초경합금을 제조할 수 있다.
이하에서는 본 발명의 바람직한 실시 형태에 따른 메탈폼 제조 방법을 각 단계별로 더욱 구체적으로 설명한다.
본 제조방법의 단계 (a)는 탄소나노튜브와 금속 분말로부터 탄소나노튜브-금속 복합체를 형성하는 단계이다.
이때, 탄소나노튜브-금속 복합체를 형성하기 위한 금속 분말은 철(Fe) 분말, 코발트(Co) 분말, 니켈(Ni) 분말 또는 이들의 혼합 분말인 것이 바람직하다.
또한, 탄소나노튜브-금속 복합체를 형성하기 위한 탄소나노튜브의 기계적 특성, 형상, 순도 등은 특별히 한정되지 않으나, 10∼50 GPa급의 강도와 0.5∼1.0 TPa급의 탄성계수를 가지며, 10 이상 ∼1,000 이하의 가로 세로비(aspect ratio)를 가지며, 95% 이상의 순도와 500~1800W/m·K의 열전도도를 가지는 것이 바람직하다.
탄소나노튜브-금속 복합체를 형성하기 위한 방법은, 복합체를 형성할 수 있는 방법이기만 하면 특별히 제한되지 않지만, 탄소나노튜브와 금속 분말을 볼밀(ball mill), 유성밀(planetary mill), 어트리션밀(attrition mill) 등을 이용한 밀링(milling)을 통해 기계적으로 혼합하는 방법이나 탄소나노튜브와 금속 전구체를 이용한 방법이 바람직하다.
여기서, 탄소나노튜브와 금속 전구체를 이용한 방법의 구체적인 예시로서 탄소나노튜브와 금속 전구체의 혼합 용액을 제조한 후, 건조, 하소 및 환원공정을 통해 탄소나노튜브-금속 복합체를 형성하는 방법 또는 탄소나노튜브와 금속 전구체의 혼합 용액을 제조한 후, 산화제를 이용한 산화 공정을 수행한 후 환원공정을 거쳐 탄소나노튜브-금속 복합체를 형성하는 방법 등을 들 수 있다. 주지할 사항은 탄소나노튜브가 금속분말 내부에 분산된 형태의 금속 바인더 분말의 제조가 중요하다는 점이다. 그 이유는 WC와 반응을 통해 금속 바인더에 포함된 탄소나노튜브가 분해되지 않게 하고 탄소함량을 일정하게 유지하게 하기 위해서이다. 바인더의 최종조성은 Ni, Co, Fe를 단독으로 사용하거나 두 가지 이상을 적절한 비율로 혼합하여 사용할 수 있다.
본 제조방법의 단계 (b)는 단계 (a)에서 얻어진 탄소나노튜브-금속 복합체를 경질상 분말과 혼합하는 단계이다.
여기서, 경질상 분말은 탄화텅스텐(WC), 탄화티타늄(TiC), 질화티타늄(TiN), 탄질화티타늄(TiCN) 및 질화티타늄알루미늄(TiAlN)으로부터 선택되는 하나 이상의 분말인 것이 바람직하다. 또한, 경질상 분말은 분말 상태 그대로 단계 (a)에서 얻어진 탄소나노튜브-금속 복합체와 혼합할 수도 있지만, 텅스텐, 티타늄 등의 염 상태의 분말을 탄화시키는 공정에 단계 (a)에서 얻어진 탄소나노튜브-금속 복합체를 첨가하여 복합분말을 형성할 수 있다.
단계 (b)를 수행함에 있어서, 탄소나노튜브-금속 복합체 및 경질상 분말만을 혼합하는 것도 가능하나, 그 외에 결합제, 이형제, 분산제, 가소제 등의 공지의 유기 첨가제를 추가하여 혼합할 수도 있다.
본 제조방법의 단계 (c)는 단계 (b)에서 얻어진 혼합 분말을 성형하는 단계이다. 본 단계에서 사용되는 성형 방법은 프레스 성형, 냉간 정수압 프레스 성형, 분말 사출 성형 등의 성형 등 소결에 제공하기에 적합한 형상을 지니는 성형체를 얻을 수 있는 방법인 이상 그 제한이 없으나, 프레스 성형이 성형체 제조의 용이성 측면에서 바람직하다.
프레스 성형으로 성형제를 제조할 경우, 이에 사용하는 장치의 종류는 특별히 제의 구성 등에 특별한 제한은 없지만, 30 MPa 이상의 압력에서 성형을 하는 것이 바람직하다. 30 MPa 미만의 성형 압력으로 프레스 성형을 수행할 경우, 제조되는 성형체가 충분한 밀도를 가지지 못해 결과적으로 고밀도로 치밀화된 소결체를 얻을 수 없는 문제점이 있다.
한편, 상기 성형체는 펠릿(pellet), 바(bar) 등 사용하고자 하는 용도에 적합하게 그 형태의 제약 없이 제조될 수 있다.
본 제조방법의 단계 (d)는 단계 (c)에서 얻어진 성형체를 소결하는 단계이다.
소결이 이루어지는 온도 범위는, 제조하고자 하는 초경합금 각각의 시스템에 따라 달라질 수 있으며, 액상 소결이 이루어지는 온도 범위에서 소결성 및 경제성 등을 고려하여 적절히 선택할 수 있다. 예를 들면, WC-Co 시스템의 경우에는 1350 ℃ 이상 1500℃ 이하의 온도에서 소결하는 것이 일반적이다.
한편, 소결시 소결 온도를 일정하게 유지하는 것도 가능하고, 소결 온도 범위의 상한과 하한에서 소결 온도를 서서히 승온 또는 강온 시켜도 무방하다.
소결 시간은, 소결성 및 경제적 측면을 고려하여 2 시간 내지 6 시간인 것이 바람직하다.
그리고, 소결 분위기와 관련해서는, 대기압 또는 진공 하에서 소결을 행할 수도 있으나 환원 가스, 불활성 가스 등의 분위기에서 소결을 해도 좋다.
또한, 본 발명은 상기 탄소나노튜브를 포함한 초경합금의 제조방법에 의해 제조된 탄소나노튜브를 포함한 초경합금을 제공한다.
본 발명에 따른 초경합금에 있어서, 탄소나노튜브는 경질상을 제외한 부피를 기준으로 할 때, 0.5 vol% 이상 5 vol% 이하의 함량으로 초경합금에 포함되는 것이 바람직하다. 처음에는 탄소나노튜브의 첨가량이 증가할수록 인성이 증가하지만, 탄소나노튜브가 5 vol%를 초과하여 첨가되는 경우 금속 바인더 함량의 상대적인 감소에 따라 오히려 인성이 감소하는 문제가 생긴다. 그리고, 0.5 vol% 미만으로 첨가되면, 인성 향상 효과가 미미하다.
본 발명에 따른 초경합금은 고경도 및 고인성을 가진다. 구체적으로, 비커스 경도(HV)가 2000 이상이고, 파괴 인성(KIC)이 4 MPa·m1/2 이상인 것이 바람직하다. 비커스 경도(HV)를 2000 이상으로 함으로써 우수한 내마모성을 도모할 수 있으며, 파괴 인성(KIC)을 4 MPa·m1/2 이상으로 함으로써, 본 발명에 따른 초경합금을 이용해 각종 부재를 제조할 경우에 우수한 내균열성 및 내치핑성을 기대할 수 있다. 한편, 필요한 경우에는 지나친 고경도화에 의한 인성의 저하를 막기 위해 비커스 경도(HV)를 2200 이하로 할 수 있다.
그리고, 본 발명은 상기 탄소나노튜브를 포함한 초경합금을 포함하여 이루어지는 초경 절삭공구를 제공한다.
상기에서 설명한 초경합금은 경도 및 인성의 측면에서 뛰어나기 때문에 절삭공구, 금형, 내마모 부재, 내열 구조 재료 등에 유용하게 사용 가능하다. 특히, 절삭날을 피절삭물에 대어서 절삭 가공하는 절삭공구로서 상기 절삭날이 본 발명에 따른 초경합금으로 이루어지는 절삭 공구에 바람직하게 사용될 수 있다. 이와 같이, 본 발명에 따른 초경합금을 절삭공구의 절삭날로서 사용할 경우, 절삭날의 온도가 과잉 상승하는 일이 발생하지 않게 되어 피절삭재의 가공면이 매끄럽고 광택이 나도록 마무리 가능하다. 나아가, 경질 피복층을 상기 절삭공구에 추가로 형성시키게 되면 내마모성 및 강도가 향상되기 때문에, 인코넬 등의 니켈기 합금, 코발트기 합금, 인코로이 등의 철기 합금 등의 내열 합금의 가공시 매우 효과적으로 사용될 수 있다.
아래에서 본 발명은 실시예를 기초로 하여 상세하게 설명한다. 제시된 실시예는 예시적인 것으로 본 발명의 범위를 제한하기 위한 것은 아니다.
<실시예> 탄소나노튜브를 포함하는 WC/탄소나노튜브-Co 초경합금의 제조
탄소나노튜브를 Co 분말 내부에 포함시키기 위하여 화학공정을 이용하여 탄소나노튜브 표면을 둘러싸는 형태로 Co 나노입자를 형성시킨 후 이들을 기계적으로 밀링하여 탄소나노튜브 0.5 vol.% 및 Co 분말 99.5 vol.%로 이루어지며, 도 3에 나타내는 바와 같이 탄소나노튜브가 Co 분말 내부에 포함되어 있는 탄소나노튜브-Co 복합체 분말을 합성하였다. 다음으로, 200nm급의 나노 WC 분말 10 wt.%를 상기 탄소나노튜브-Co 복합체 분말 90 wt.%와 기계적 밀링 공정을 통해 혼합하여 도 4에서 나타내는 형상을 가진 WC/탄소나노튜브-Co 분말을 합성하였다. 이렇게 합성된 WC/탄소나노튜브-Co 분말은 도 5에서 알 수 있는 바와 같이 명확한 WC 상이 유지되고 있음을 확인할 수 있다. 그리고나서 상기에서 합성된 WC/탄소나노튜브-Co 분말을 에어 프레서를 이용해서 가압 성형하여 펠릿을 얻었다. 상기 펠릿을 1400℃에서 2시간 동안 수소분위기에서 소결하여 WC/탄소나노튜브-Co 초경합금을 제조하였다. 이와 같이 제조된 WC/탄소나노튜브-Co 초경합금은 도 6에서 같이 500nm급의 WC 결정립이 Co바인더에 의해 연결된 미세조직을 나타낸다.
<비교예> 탄소나노튜브를 포함하지 않는 WC-Co 초경합금의 제조
200nm급의 나노 WC 분말 10 wt.%를 Co 분말 90 wt.%와 기계적 밀링 공정을 통해 혼합하였다. 이렇게 얻어진 혼합 분말을 에어 프레서를 이용해서 가압 성형하여 펠릿을 얻었다. 상기 펠릿을 1400℃에서 2시간 동안 수소분위기에서 소결하여 WC-Co 초경합금을 제조하였다.
<실험예> 실시예 및 비교예에서 제조된 초경합금의 기계적 특성 관찰
비커스 경도(HV)의 측정 결과, 비교예의 경우 평균 2060이 측정되었고 탄소나노튜브가 첨가된 경우에는 2070이 측정되었다(도 7 참조). 파괴 인성(KIC)의 측정 결과, 비교예의 경우 2.5 MPa·m1/2이 측정되었고, 실시예의 경우 4.5 MPa·m1/2 이 측정되었다(도 8 참조).
즉, 탄소나노튜브 첨가에 따라 경도는 크게 향상되지 않았지만, 파괴 인성(KIC)은 1.8배 이상으로 현저히 향상되었음을 확인할 수 있다. 이는 탄소나노튜브에 의한 Co 바인더 기지의 강화효과와 크랙(Crack)의 전파를 방해하는 효과가 나타난 것으로 판단되며, 입도 500nm의 WC 평균 결정립과 99.2%의 소결밀도를 동일하게 나타내는 실시예와 비교예를 서로 비교하였다는 점에서 탄소나노튜브에 의한 인성 향상 효과임에 틀림이 없다고 보인다.
결론적으로, 본 발명에 따라 탄소나노튜브가 포함된 초경합금을 제조할 경우, 탄소나노튜브 첨가에 따른 인성 향상 효과를 극대화할 수 있음을 확인할 수 있었다.

Claims (17)

  1. (a) 탄소나노튜브와 금속 분말로부터 탄소나노튜브-금속 복합체를 형성하는 단계;
    (b) 상기 단계 (a)에서 얻어진 탄소나노튜브-금속 복합체를 경질상 분말과 혼합하는 단계;
    (c) 상기 단계 (b)에서 얻어진 혼합 분말을 성형하는 단계; 및
    (d) 상기 단계 (c)에서 얻어진 성형체를 소결하는 단계를 포함하는 탄소나노튜브를 포함한 초경합금의 제조방법.
  2. 제1항에 있어서,
    상기 단계 (a)의 금속 분말은 Fe, Co 및 Ni으로부터 선택되는 하나 이상의 분말인 것인 탄소나노튜브를 포함한 초경합금의 제조방법.
  3. 제1항에 있어서,
    상기 단계 (a)는 밀링(milling) 공정에 의해 수행되는 것인 탄소나노튜브를 포함한 초경합금의 제조방법.
  4. 제3항에 있어서,
    상기 밀링(milling) 공정은 볼밀링(ball milling), 유성 밀링(planetary milling) 또는 어트리션 밀링(attrition milling)으로부터 선택되는 것인 탄소나노튜브를 포함한 초경합금의 제조방법.
  5. 제1항에 있어서,
    상기 단계 (b)의 경질상 분말은 WC, TiC, TiN, TiCN 및 TiAlN으로부터 선택되는 하나 이상의 분말인 것인 탄소나노튜브를 포함한 초경합금의 제조방법.
  6. 제1항에 있어서,
    상기 단계 (a)의 금속 분말은 Fe, Co 및 Ni으로부터 선택되는 하나의 분말이거나 둘 이상의 혼합 분말이고, 단계 (b)의 경질상 분말은 WC 분말인 것인 탄소나노튜브를 포함한 초경합금의 제조방법.
  7. 제1항에 있어서,
    상기 단계 (a)의 금속 분말은 Co 분말이고, 단계 (b)의 경질상 분말은 WC 분말인 것인 탄소나노튜브를 포함한 초경합금의 제조방법.
  8. 제1항에 있어서,
    상기 단계 (c)는 프레스 성형, 냉간 정수압 프레스 성형 또는 분말 사출 성형을 이용하여 수행되는 것인 탄소나노튜브를 포함한 초경합금의 제조방법.
  9. 제7항에 있어서,
    상기 단계 (d)는 1350 ℃ 내지 1500 ℃의 온도에서 2 시간 내지 6 시간 유지되는 것인 탄소나노튜브를 포함한 초경합금의 제조방법.
  10. 제7항에 있어서,
    상기 단계 (d)는 진공 또는 환원가스 분위기에서 수행되는 것인 탄소나노튜브를 포함한 초경합금의 제조방법.
  11. 제1항의 제조방법에 의해 제조된 탄소나노튜브를 포함한 초경합금.
  12. 제11항에 있어서, 탄소나노튜브가 경질상을 제외한 부피를 기준으로 0.5 vol% 내지 5 vol% 포함된 것인 탄소나노튜브를 포함한 초경합금.
  13. 제11항에 있어서,
    탄소나노튜브는 금속 바인더 기지 내에 분산되어 존재하는 것인 초경합금.
  14. 제11항에 있어서, 경도(HV)가 2000 이상이고, 인성(KIC)이 4 MPa·m1/2 이상인 것인 탄소나노튜브를 포함한 초경합금.
  15. 제11항에 있어서, 초경 절삭공구에 사용되는 것을 특징으로 하는 탄소나노튜브를 포함한 초경합금.
  16. 제11항에 기재된 탄소나노튜브를 포함한 초경합금을 포함하여 이루어지는 초경 절삭공구.
  17. 제16항에 있어서, 절삭날을 포함하며 상기 절삭날은 제11항에 기재된 탄소나노튜브를 포함한 초경합금으로 이루어진 것인 초경 절삭공구.
PCT/KR2013/010004 2012-12-21 2013-11-06 탄소나노튜브를 포함하는 초경합금의 제조방법, 이에 의해 제조된 초경합금 및 초경합금을 포함하여 이루어지는 초경 절삭공구 Ceased WO2014098370A1 (ko)