WO2014061608A1 - Hydraulic rotary machine - Google Patents
Hydraulic rotary machine Download PDFInfo
- Publication number
- WO2014061608A1 WO2014061608A1 PCT/JP2013/077824 JP2013077824W WO2014061608A1 WO 2014061608 A1 WO2014061608 A1 WO 2014061608A1 JP 2013077824 W JP2013077824 W JP 2013077824W WO 2014061608 A1 WO2014061608 A1 WO 2014061608A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- sliding
- cylinder
- caf
- sliding surface
- cylinder block
- Prior art date
Abstract
Description
摺動板ライニング:外径Φ97mm×内径Φ54mm
摺動部面積:51cm2
相手材:FCD
摺速:10.8m/sec
試験圧力:0.5MPaから0.5MPaずつ試験機のシリンダ圧力を上昇(各圧力で15分運転)
油温:50℃
潤滑油:油圧作動油(VG46) Testing machine: JIS constant speed type friction testing machine (JIS D4311)
Sliding plate lining: Outer diameter Φ97mm x Inner diameter Φ54mm
Sliding part area: 51 cm 2
Opponent material: FCD
Sliding speed: 10.8m / sec
Test pressure: Increase the tester cylinder pressure by 0.5MPa from 0.5MPa (run for 15 minutes at each pressure)
Oil temperature: 50 ° C
Lubricating oil: Hydraulic fluid (VG46)
試験片:外径18mm×厚さ10mm(ライニング厚み 1mm)
発振周波数:20kHz
振幅:±37μm
水温:50℃ Tester: Ultrasonic erosion tester Test piece: Outer diameter 18mm x Thickness 10mm (lining thickness 1mm)
Oscillation frequency: 20 kHz
Amplitude: ± 37 μm
Water temperature: 50 ° C
2,31,41 ケーシング
5,42 回転軸
8,44 シリンダブロック(第1の部材、第2の部材)
8A,44B 摺動面(第2の摺動面)
9,45 シリンダ
9A,45A 摺動面(第1の摺動面)
10,46 シリンダポート(油路)
11,49 ピストン(第2の部材)
11B,49B 摺動面(第2の摺動面)
11C 第1の給油路
12,50 弁板(第1の部材)
12A,50B,50C 摺動面(第1の摺動面)
12B,12C,50D,50E 給排ポート(油路)
13 シュー(第1の部材)
13A 摺動面(第1の摺動面)
13B 第2の給油路(油路)
14,34 斜板(第2の部材)
14A,34B,34D 摺動面(第2の摺動面)
21 摺動層
35 斜板支持部材(第1の部材)
35A 傾転摺動面(第1の摺動面)
35B 第2の給油路(油路)
51 ヘッドカバー(第2の部材)
51A 傾転摺動面(第2の摺動面) 1 Hydraulic motor (hydraulic rotating machine)
2, 31, 41
8A, 44B Sliding surface (second sliding surface)
9, 45
10,46 Cylinder port (oil passage)
11, 49 Piston (second member)
11B, 49B Sliding surface (second sliding surface)
11C 1st
12A, 50B, 50C Sliding surface (first sliding surface)
12B, 12C, 50D, 50E Supply / discharge port (oil passage)
13 Shoe (first member)
13A Sliding surface (first sliding surface)
13B Second oil supply passage (oil passage)
14, 34 Swash plate (second member)
14A, 34B, 34D Sliding surface (second sliding surface)
21 Sliding
35A Tilt sliding surface (first sliding surface)
35B Second oil supply passage (oil passage)
51 Head cover (second member)
51A Tilt sliding surface (second sliding surface)
Claims (10)
- 第1の摺動面(9A,12A,13A,35A,45A,50B,50C)を有する第1の部材(8,12,13,35,44,50)と、
前記第1の摺動面(9A,12A,13A,35A,45A,50B,50C)に対して摺動する第2の摺動面(8A,11B,14A,34B,34D,44B,49B,51A)を有する第2の部材(8,11,14,34,44,49,51)とを備え、
前記第1の摺動面(9A,12A,13A,35A,45A,50B,50C)と第2の摺動面(8A,11B,14A,34B,34D,44B,49B,51A)とのうちの少なくとも何れかの摺動面には、油液が流通する油路(10,11C,12B,12C,13B,35B,46,50D,50E)の一端側が開口する構成としてなる液圧回転機において、
前記第1の摺動面(9A,12A,13A,35A,45A,50B,50C)と第2の摺動面(8A,11B,14A,34B,34D,44B,49B,51A)とのうちの一方の摺動面は、焼結銅合金からなる摺動層(21)を形成し、
該摺動層(21)は、CuおよびSnを主成分とすると共に残りの成分を残部とした組成からなり、
前記残部の成分は、2~6重量%のCaF2を必須成分とし、かつ、該CaF2の平均粒径を40μm~350μmの範囲に規制し、
前記第1の摺動面(9A,12A,13A,35A,45A,50B,50C)と第2の摺動面(8A,11B,14A,34B,34D,44B,49B,51A)とのうちの他方の摺動面は、鉄鋼系材料の摺動層により構成したことを特徴とする液圧回転機。 A first member (8, 12, 13, 35, 44, 50) having a first sliding surface (9A, 12A, 13A, 35A, 45A, 50B, 50C);
Second sliding surfaces (8A, 11B, 14A, 34B, 34D, 44B, 49B, 51A) sliding with respect to the first sliding surfaces (9A, 12A, 13A, 35A, 45A, 50B, 50C) ) Having a second member (8, 11, 14, 34, 44, 49, 51),
Of the first sliding surfaces (9A, 12A, 13A, 35A, 45A, 50B, 50C) and the second sliding surfaces (8A, 11B, 14A, 34B, 34D, 44B, 49B, 51A) In a hydraulic rotating machine configured such that at least one sliding surface has an opening on one end side of an oil passage (10, 11C, 12B, 12C, 13B, 35B, 46, 50D, 50E) through which oil flows.
Of the first sliding surfaces (9A, 12A, 13A, 35A, 45A, 50B, 50C) and the second sliding surfaces (8A, 11B, 14A, 34B, 34D, 44B, 49B, 51A) One sliding surface forms a sliding layer (21) made of sintered copper alloy,
The sliding layer (21) is composed of a composition having Cu and Sn as main components and the remaining components as the balance,
The remaining component is 2 to 6% by weight of CaF 2 as an essential component, and the average particle size of the CaF 2 is regulated in the range of 40 μm to 350 μm,
Of the first sliding surfaces (9A, 12A, 13A, 35A, 45A, 50B, 50C) and the second sliding surfaces (8A, 11B, 14A, 34B, 34D, 44B, 49B, 51A) The other sliding surface is constituted by a sliding layer of a steel-based material. - 前記摺動層(21)の前記残部の成分は、前記CaF2を必須成分とすることに加えて、Pb、Ni、Be、P、Fe、Zn、Al、Si、Mn、Mg、S、Ti、V、Cr、Wのうちの少なくとも1つ以上の成分を含んだ組成としてなる請求項1に記載の液圧回転機。 The remaining components of the sliding layer (21) include Pb, Ni, Be, P, Fe, Zn, Al, Si, Mn, Mg, S, Ti in addition to the CaF 2 as an essential component. The hydraulic rotating machine according to claim 1, wherein the hydraulic rotating machine has a composition containing at least one component of V, Cr, W.
- 前記摺動層(21)の前記主成分は、前記Cuに加えて、11~13重量%の前記Snを含む組成とし、
前記摺動層(21)の前記残部の成分は、前記CaF2に加えて、4~6重量%の前記Niを含む組成としてなる請求項2に記載の液圧回転機。 The main component of the sliding layer (21) has a composition containing 11 to 13% by weight of Sn in addition to Cu.
The hydraulic rotating machine according to claim 2, wherein the remaining component of the sliding layer (21) has a composition containing 4 to 6 wt% of the Ni in addition to the CaF 2 . - 前記摺動層(21)の前記主成分は、前記Cuに加えて、11~13重量%の前記Snを含む組成とし、
前記摺動層(21)の前記残部の成分は、前記CaF2に加えて、1~3重量%の前記Pbと、4~6重量%の前記Niを含む組成としてなる請求項2に記載の液圧回転機。 The main component of the sliding layer (21) has a composition containing 11 to 13% by weight of Sn in addition to Cu.
Component of the remainder of the sliding layer (21), in addition to the CaF 2, 1 - 3% by weight of the Pb, 4 to 6 wt% of claim 2 comprising a composition comprising the Ni Hydraulic rotating machine. - 前記摺動層(21)の前記残部の成分は、前記CaF2を必須成分とすることに加えて、PbとNiとを必須成分とし、前記CaF2は、粒径が40μm~350μmの範囲のものが90~100重量%となるように規制してなる請求項1に記載の液圧回転機。 The remaining component of the sliding layer (21) includes Pb and Ni as essential components in addition to the CaF 2 as essential components, and the CaF 2 has a particle size in the range of 40 μm to 350 μm. 2. The hydraulic rotating machine according to claim 1, wherein the pressure is regulated so as to be 90 to 100% by weight.
- 中空なケーシング(2,31,41)と、該ケーシング(2,31,41)内に回転可能に設けられた回転軸(5,42)と、該回転軸(5,42)と共に回転するように前記ケーシング(2,31,41)内に設けられ周方向に離間して軸方向に延びる複数のシリンダ(9,45)と該各シリンダ(9,45)に対応した位置で端面に開口したシリンダポート(10,46)とが形成されたシリンダブロック(8,44)と、該シリンダブロック(8,44)の各シリンダ(9,45)内に往復動可能に挿嵌された複数のピストン(11,49)と、前記ケーシング(2,31,41)とシリンダブロック(8,44)との間に設けられ前記シリンダポート(10,46)を介して前記各シリンダ(9,45)と連通する給排ポート(12B,12C,50D,50E)が形成された弁板(12,50)とを備え、
前記第1の部材は、前記油路となる前記給排ポート(12B,12C,50D,50E)が形成された前記弁板(12,50)であり、
前記第2の部材は、前記弁板(12,50)と摺動し前記油路となる前記シリンダポート(10,46)が形成された前記シリンダブロック(8,44)である請求項1に記載の液圧回転機。 A hollow casing (2, 31, 41), a rotating shaft (5, 42) rotatably provided in the casing (2, 31, 41), and rotating together with the rotating shaft (5, 42) A plurality of cylinders (9, 45) provided in the casing (2, 31, 41) and extending in the axial direction and spaced apart from each other in the circumferential direction and opened to the end face at positions corresponding to the cylinders (9, 45) Cylinder block (8, 44) in which cylinder ports (10, 46) are formed, and a plurality of pistons removably inserted into cylinders (9, 45) of the cylinder block (8, 44) (11, 49) and each cylinder (9, 45) provided between the casing (2, 31, 41) and the cylinder block (8, 44) via the cylinder port (10, 46). Supply / exhaust port (12 Comprising 12C, 50D, 50E) the valve plate formed is a (12,50),
The first member is the valve plate (12, 50) in which the supply / discharge port (12B, 12C, 50D, 50E) serving as the oil passage is formed,
The said 2nd member is the said cylinder block (8,44) in which the said cylinder port (10,46) which slides with the said valve plate (12,50) and becomes the said oil path was formed. The hydraulic rotating machine described. - 中空なケーシング(2,31)と、該ケーシング(2,31)内に回転可能に設けられた回転軸(5)と、該回転軸(5)と共に回転するように前記ケーシング(2,31)内に設けられ周方向に離間して軸方向に延びる複数のシリンダ(9)と該各シリンダ(9)に対応した位置で端面に開口したシリンダポート(10)とが形成されたシリンダブロック(8)と、該シリンダブロック(8)の各シリンダ(9)内に往復動可能に挿嵌され内部に第1の給油路(11C)が形成された複数のピストン(11)と、前記ケーシング(2,31)とシリンダブロック(8)との間に設けられ前記シリンダポート(10)を介して前記各シリンダ(9)と連通する給排ポート(12B,12C)が形成された弁板(12)と、前記各ピストン(11)の突出端側に揺動可能に取付けられ内部に前記第1の給油路(11C)に接続される第2の給油路(13B)が形成された複数のシュー(13)と、前記シリンダブロック(8)を挟んで前記弁板(12)とは反対側の位置に設けられ前記各シュー(13)が摺動する斜板(14,34)とを備え、
前記第1の部材は、前記油路となる前記第2の給油路(13B)が形成された前記各シュー(13)であり、
前記第2の部材は、前記各シュー(13)が摺動する前記斜板(12)である請求項1に記載の液圧回転機。 A hollow casing (2, 31), a rotary shaft (5) rotatably provided in the casing (2, 31), and the casing (2, 31) so as to rotate together with the rotary shaft (5) A cylinder block (8) formed with a plurality of cylinders (9) extending in the axial direction and spaced apart in the circumferential direction, and a cylinder port (10) opened at the end face at a position corresponding to each cylinder (9) ), A plurality of pistons (11) having a first oil supply passage (11C) formed therein and removably inserted in the cylinders (9) of the cylinder block (8), and the casing (2 31) and a cylinder block (8), and a valve plate (12) formed with supply / discharge ports (12B, 12C) communicating with the cylinders (9) via the cylinder port (10) And each piston (1 ) And a plurality of shoes (13) each having a second oil supply passage (13B) connected to the first oil supply passage (11C) and swingably attached to the protruding end side of the cylinder block; (8) provided with a swash plate (14, 34) provided at a position opposite to the valve plate (12) across which the shoes (13) slide;
The first member is each shoe (13) in which the second oil supply passage (13B) to be the oil passage is formed,
The hydraulic rotating machine according to claim 1, wherein the second member is the swash plate (12) on which the shoes (13) slide. - 中空なケーシング(2,31,41)と、該ケーシング(2,31,41)内に回転可能に設けられた回転軸(5,42)と、該回転軸(5,42)と共に回転するように前記ケーシング(2,31,41)内に設けられ周方向に離間する複数のシリンダ(9,45)と該各シリンダ(9,45)に対応した位置で端面に開口したシリンダポート(10,46)とが形成されたシリンダブロック(8,44)と、該シリンダブロック(8,44)の各シリンダ(9,45)内に往復動可能に挿嵌された複数のピストン(11,49)とを備え、
前記第1の部材は、前記油路となる前記シリンダポート(10,46)が形成された前記シリンダブロック(8,44)であり、
前記第2の部材は、前記シリンダブロック(8,44)の前記シリンダ(9,45)に対して摺動する前記ピストン(11,49)である請求項1に記載の液圧回転機。 A hollow casing (2, 31, 41), a rotating shaft (5, 42) rotatably provided in the casing (2, 31, 41), and rotating together with the rotating shaft (5, 42) A plurality of cylinders (9, 45) provided in the casing (2, 31, 41) and spaced apart in the circumferential direction, and cylinder ports (10, 10) opened at end faces at positions corresponding to the cylinders (9, 45) 46) and a plurality of pistons (11, 49) that are removably inserted into the cylinders (9, 45) of the cylinder block (8, 44). And
The first member is the cylinder block (8, 44) in which the cylinder port (10, 46) serving as the oil passage is formed,
The hydraulic rotating machine according to claim 1, wherein the second member is the piston (11, 49) that slides relative to the cylinder (9, 45) of the cylinder block (8, 44). - 中空なケーシング(31)と、該ケーシング(31)内に回転可能に設けられた回転軸(5)と、該回転軸(5)と共に回転するように前記ケーシング(31)内に設けられ周方向に離間して軸方向に延びる複数のシリンダ(9)と該各シリンダ(9)に対応した位置で端面に開口したシリンダポート(10)とが形成されたシリンダブロック(8)と、該シリンダブロック(8)の各シリンダ(9)内に往復動可能に挿嵌された複数のピストン(11)と、前記ケーシング(31)とシリンダブロック(8)との間に設けられ前記シリンダポート(10)を介して前記各シリンダ(9)と連通する給排ポート(12B,12C)が形成された弁板(12)と、前記各ピストン(11)の突出端側に揺動可能に取付けられた複数のシュー(13)と、前記シリンダブロック(8)側となる一端面側に前記各シュー(13)が摺動すると共に他端面側に凸湾曲面状の摺動面(34D)が形成され、斜板支持点を傾転中心として傾転可能に設けられた斜板(34)と、該斜板(34)の摺動面(34D)と摺動する凹湾曲面状の傾転摺動面(35A)が形成され内部に前記シリンダポート(10)から吐出される油液が流通する給油路(35B)が形成された斜板支持部材(35)とを備え、
前記第1の部材は、前記油路となる前記給油路(35B)が形成された前記斜板支持部材(35)であり、
前記第2の部材は、前記斜板支持部材(35)に対して摺動する前記斜板(34)である請求項1に記載の液圧回転機。 A hollow casing (31), a rotation shaft (5) rotatably provided in the casing (31), and a circumferential direction provided in the casing (31) so as to rotate together with the rotation shaft (5) A cylinder block (8) formed with a plurality of cylinders (9) extending in the axial direction and spaced apart from each other, and a cylinder port (10) opened at an end surface at a position corresponding to each cylinder (9), and the cylinder block A plurality of pistons (11) inserted in each cylinder (9) of (8) so as to be able to reciprocate, and the cylinder port (10) provided between the casing (31) and the cylinder block (8). And a plurality of valve plates (12) formed with supply / exhaust ports (12B, 12C) communicating with the cylinders (9) via the cylinders and swingably attached to the protruding end sides of the pistons (11). No shoe (1 ), And each shoe (13) slides on one end surface side which is the cylinder block (8) side, and a convex curved surface-shaped sliding surface (34D) is formed on the other end surface side. And a tilted sliding surface (35A) having a concave curved surface that slides on the sliding surface (34D) of the swash plate (34). A swash plate support member (35) formed with an oil supply passage (35B) formed therein through which oil liquid discharged from the cylinder port (10) flows,
The first member is the swash plate support member (35) in which the oil supply passage (35B) to be the oil passage is formed,
The hydraulic rotating machine according to claim 1, wherein the second member is the swash plate (34) that slides with respect to the swash plate support member (35). - 中空なケーシング(41)と、該ケーシング(41)内に回転可能に設けられ先端がドライブディスク(42A)となった回転軸(42)と、該回転軸(42)と共に回転するように前記ケーシング(41)内に設けられ周方向に離間して軸方向に延びる複数のシリンダ(45)と該各シリンダ(45)に対応した位置で端面に開口したシリンダポート(46)とが形成されたシリンダブロック(44)と、該シリンダブロック(44)の各シリンダ(45)内に往復動可能に挿嵌され突出端側が前記回転軸(42)のドライブディスク(42A)に揺動可能に支持された複数のピストン(49)と、前記シリンダブロック(44)側となる一端面側に該シリンダブロック(44)が摺動すると共に他端面側に凸湾曲面状の摺動面(50B)が形成され、弁板支持点を傾転中心として前記シリンダブロック(44)と共に傾転可能に設けられる弁板(50)と、該弁板(50)の摺動面(50C)と摺動する凹湾曲面状の傾転摺動面(51A)が形成されたヘッドカバー(51)とを備え、
前記第1の部材は、前記シリンダポート(46)を介して前記各シリンダ(45)と連通する前記油路となる給排ポート(50D)が形成された前記弁板(50)であり、
前記第2の部材は、前記弁板(50)が摺動する前記ヘッドカバー(51)である請求項1に記載の液圧回転機。 A hollow casing (41), a rotating shaft (42) provided rotatably in the casing (41) and having a tip serving as a drive disk (42A), and the casing rotating with the rotating shaft (42) A cylinder provided in (41) and formed with a plurality of cylinders (45) spaced apart in the circumferential direction and extending in the axial direction, and cylinder ports (46) opened at end faces at positions corresponding to the cylinders (45). A block (44) and each cylinder (45) of the cylinder block (44) are removably inserted into the cylinder (45), and the protruding end side is swingably supported by the drive disk (42A) of the rotating shaft (42). The plurality of pistons (49) and the cylinder block (44) slide on one end surface side which is the cylinder block (44) side, and the convex curved sliding surface (50B) on the other end surface side. A valve plate (50) formed so as to be tiltable together with the cylinder block (44) with the valve plate support point as a tilt center, and a recess sliding with the sliding surface (50C) of the valve plate (50). A head cover (51) formed with a curved sliding surface (51A),
The first member is the valve plate (50) in which a supply / discharge port (50D) serving as the oil passage communicating with the cylinders (45) via the cylinder port (46) is formed,
The hydraulic rotary machine according to claim 1, wherein the second member is the head cover (51) on which the valve plate (50) slides.