WO2014010733A1 - Feuille contenant une couche photoréactive et procédé permettant de fabriquer une feuille contenant une couche photoréactive - Google Patents

Feuille contenant une couche photoréactive et procédé permettant de fabriquer une feuille contenant une couche photoréactive Download PDF

Info

Publication number
WO2014010733A1
WO2014010733A1 PCT/JP2013/069190 JP2013069190W WO2014010733A1 WO 2014010733 A1 WO2014010733 A1 WO 2014010733A1 JP 2013069190 W JP2013069190 W JP 2013069190W WO 2014010733 A1 WO2014010733 A1 WO 2014010733A1
Authority
WO
WIPO (PCT)
Prior art keywords
polyolefin
layer
release agent
photoreactive
material layer
Prior art date
Application number
PCT/JP2013/069190
Other languages
English (en)
Japanese (ja)
Inventor
悠司 豊田
平松　剛
Original Assignee
日東電工株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日東電工株式会社 filed Critical 日東電工株式会社
Publication of WO2014010733A1 publication Critical patent/WO2014010733A1/fr

Abstract

La présente invention concerne une feuille contenant une couche photoréactive, ladite feuille comprenant un film transmettant la lumière, ledit film transmettant la lumière ayant été traité de manière antiadhésive par un antiadhésif sans silicone, collé à au moins une surface d'une couche photoréactive obtenue en procédant à la photoréaction d'une composition photoréactive. La force de pelage du film transmettant la lumière par rapport à la couche photoréactive est inférieure ou égale à 1,0 N/25 mm.
PCT/JP2013/069190 2012-07-13 2013-07-12 Feuille contenant une couche photoréactive et procédé permettant de fabriquer une feuille contenant une couche photoréactive WO2014010733A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2012-157924 2012-07-13
JP2012157924 2012-07-13

Publications (1)

Publication Number Publication Date
WO2014010733A1 true WO2014010733A1 (fr) 2014-01-16

Family

ID=49916172

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2013/069190 WO2014010733A1 (fr) 2012-07-13 2013-07-12 Feuille contenant une couche photoréactive et procédé permettant de fabriquer une feuille contenant une couche photoréactive

Country Status (2)

Country Link
JP (1) JP2014031005A (fr)
WO (1) WO2014010733A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2017002196A (ja) * 2015-06-11 2017-01-05 大日本印刷株式会社 積層体の製造方法

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR102268328B1 (ko) * 2014-10-21 2021-06-24 삼성디스플레이 주식회사 광투과 점착 필름 및 이를 포함하는 표시 장치
JP6647890B2 (ja) * 2016-02-02 2020-02-14 リンテック株式会社 シート状積層体およびシート状積層体の製造方法
JP6954100B2 (ja) * 2017-12-25 2021-10-27 三菱ケミカル株式会社 離型フィルム及び粘着体

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004322408A (ja) * 2003-04-23 2004-11-18 Nitto Denko Corp 光反応性組成物シートの製造方法および製造装置
WO2011016539A1 (fr) * 2009-08-07 2011-02-10 日東電工株式会社 Agent anti-adhésif, matériau anti-adhésif et ruban adhésif sensible à la pression
WO2011043214A1 (fr) * 2009-10-05 2011-04-14 日東電工株式会社 Agent décapant, matériau de décollement et ruban adhésif
WO2012053503A1 (fr) * 2010-10-19 2012-04-26 日東電工株式会社 Agent anti-adhérent, matériau de démoulage et ruban adhésif
WO2012053502A1 (fr) * 2010-10-19 2012-04-26 日東電工株式会社 Agent de démoulage, matériau de démoulage et ruban adhésif
WO2012105340A1 (fr) * 2011-02-04 2012-08-09 日東電工株式会社 Agent de séparation, agent de démoulage et ruban adhésif
WO2012105341A1 (fr) * 2011-02-04 2012-08-09 日東電工株式会社 Agent de séparation, agent de démoulage et ruban adhésif
WO2012105339A1 (fr) * 2011-02-04 2012-08-09 日東電工株式会社 Agent antiadhésif, son procédé de fabrication, matière antiadhésive et ruban adhésif sensible à la pression
WO2012105338A1 (fr) * 2011-02-04 2012-08-09 日東電工株式会社 Agent de démoulage

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004322408A (ja) * 2003-04-23 2004-11-18 Nitto Denko Corp 光反応性組成物シートの製造方法および製造装置
WO2011016539A1 (fr) * 2009-08-07 2011-02-10 日東電工株式会社 Agent anti-adhésif, matériau anti-adhésif et ruban adhésif sensible à la pression
WO2011043214A1 (fr) * 2009-10-05 2011-04-14 日東電工株式会社 Agent décapant, matériau de décollement et ruban adhésif
WO2012053503A1 (fr) * 2010-10-19 2012-04-26 日東電工株式会社 Agent anti-adhérent, matériau de démoulage et ruban adhésif
WO2012053502A1 (fr) * 2010-10-19 2012-04-26 日東電工株式会社 Agent de démoulage, matériau de démoulage et ruban adhésif
WO2012105340A1 (fr) * 2011-02-04 2012-08-09 日東電工株式会社 Agent de séparation, agent de démoulage et ruban adhésif
WO2012105341A1 (fr) * 2011-02-04 2012-08-09 日東電工株式会社 Agent de séparation, agent de démoulage et ruban adhésif
WO2012105339A1 (fr) * 2011-02-04 2012-08-09 日東電工株式会社 Agent antiadhésif, son procédé de fabrication, matière antiadhésive et ruban adhésif sensible à la pression
WO2012105338A1 (fr) * 2011-02-04 2012-08-09 日東電工株式会社 Agent de démoulage

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2017002196A (ja) * 2015-06-11 2017-01-05 大日本印刷株式会社 積層体の製造方法

Also Published As

Publication number Publication date
JP2014031005A (ja) 2014-02-20

Similar Documents

Publication Publication Date Title
JP5925478B2 (ja) 粘着剤および粘着テープ
JP5989995B2 (ja) 剥離剤、離型材および粘着テープ
JP5101111B2 (ja) 半導体基板加工用粘着シート
JP6804843B2 (ja) セパレータ付き光学用表面保護フィルム
KR20150026841A (ko) 투명 도전성 필름용 캐리어 필름 및 적층체
US20120070659A1 (en) Pressure-sensitive adhesive sheet
WO2011016539A1 (fr) Agent anti-adhésif, matériau anti-adhésif et ruban adhésif sensible à la pression
WO2008075570A1 (fr) Feuille adhésive sensible à la pression
JP6538432B2 (ja) 透明導電性フィルム用キャリアフィルム及び積層体
JP6046500B2 (ja) 薬液処理用保護シート
JP7063690B2 (ja) 粘着シート
WO2011043214A1 (fr) Agent décapant, matériau de décollement et ruban adhésif
JP2014015004A (ja) 離型材およびその製造方法、並びに粘着テープ
JP2018515642A (ja) 架橋に発光ダイオードを使用する架橋感圧性接着剤の調製方法
WO2014010733A1 (fr) Feuille contenant une couche photoréactive et procédé permettant de fabriquer une feuille contenant une couche photoréactive
TWI712503B (zh) 透明導電性膜用載膜及積層體
JP5548109B2 (ja) 粘着シート用基材フィルムの製造方法、粘着シート用基材フィルムおよび粘着シート
JP4339645B2 (ja) 離型シート及び粘着体
WO2012105340A1 (fr) Agent de séparation, agent de démoulage et ruban adhésif
WO2012105338A1 (fr) Agent de démoulage
JP2004224991A (ja) 粘着剤組成物および有機ｅｌ表示装置
JP5276826B2 (ja) 光重合反応とレドックス重合反応とを併用して得られる暗色化されたアクリル系粘弾性体層の製造方法、及び粘着テープ又はシート
WO2005025863A1 (fr) Feuille de protection et composites adhesifs autocollants
WO2012105339A1 (fr) Agent antiadhésif, son procédé de fabrication, matière antiadhésive et ruban adhésif sensible à la pression
WO2016121875A1 (fr) Film protecteur de surface optique ayant un séparateur

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 13816184

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase