WO2014008983A1 - Dlc beschichtungen mit erhöhter korrosionsbeständigkeit - Google Patents

Dlc beschichtungen mit erhöhter korrosionsbeständigkeit Download PDF

Info

Publication number
WO2014008983A1
WO2014008983A1 PCT/EP2013/001851 EP2013001851W WO2014008983A1 WO 2014008983 A1 WO2014008983 A1 WO 2014008983A1 EP 2013001851 W EP2013001851 W EP 2013001851W WO 2014008983 A1 WO2014008983 A1 WO 2014008983A1
Authority
WO
WIPO (PCT)
Prior art keywords
component
layer
nitriding
corrosion resistance
treatment chamber
Prior art date
Application number
PCT/EP2013/001851
Other languages
English (en)
French (fr)
Inventor
Albert Peter Gerhard Janssen
Original Assignee
Oerlikon Trading Ag, Trübbach
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Oerlikon Trading Ag, Trübbach filed Critical Oerlikon Trading Ag, Trübbach
Publication of WO2014008983A1 publication Critical patent/WO2014008983A1/de

Abstract

Die Erfindung betrifft ein Verfahren zur Behandlung einer Komponente zur Härtung, Erhöhung der Korrosionsbeständigkeit, Herabsetzung der Reibung und Schwärzung der Oberfläche, wobei das Verfahren folgende Schritte umfasst: - Bereitstellung der zu behandelnden Komponente - Härtung der Komponente vorzugsweise mittels Induktionshärtung - Erzeugung einer Stickstoffdiffusionsschicht mittels Nitrierung - Erzeugung einer Verbindungsschicht mit ε- und γ'-Eisennitriden ebenfalls mittels Nitrierung - Beschichtung der Komponente mit einer amorphen Kohlenstoffschicht

Description

DLC Beschichturtgen mit erhöhter Korrosionsbeständigkeit
Die vorliegende Erfindung bezieht sich auf ein Verfahren zur Schwärzung von Metalloberflächen, wobei gleichzeitig Korrosionsbeständigkeit und Härte erreicht werden soll bei niedriger bzw. herabgesetzter Reibung.
Anwendung findet das erfinderische Verfahren auf Produkte z.B. aus der Automobilindustrie auf der Basis von niedrig legierten Kohlenstoff Stahl, insbesondere auf Produkte deren Materialstärke 2mm nicht übersteigt.
Typischerweise werden solche Teile heutzutage zunächst mittels Induktionserwärmen gehärtet. Die dabei entstehende Martensitstruktur führt zu einer Härte von ca. 2000 MPa. In wässrigen Umgebungen neigen die entsprechenden Oberflächen jedoch zur interkristallinen Korrosion. Würde man nun auf die derart gehärtete Oberfläche eine Kohlenstoffschicht aufbringen, so wäre die dadurch entstehende Oberfläche zwar hart, schwarz und reibungsvermindert, jedoch nicht korrosionsbeständig. Um dem entgegenzuwirken werden die Oberflächen in der Regel nach dem Induktionshärten mit einer 20 bis 25pm dicken Chromschicht mittels Galvanik überzogen. Anschliessend wird die Oberfläche poliert um die bei dem Galvanikverfahren entstehenden Risse zuzuschmieren. Anschliessend wird die Komponente dann noch mit einer DLC -Schicht bedeckt, welche der Oberfläche die schwarze Farbe verleiht und die Reibung herabsetzt.
DLC bedeutet dabei Diamond Like Carbon, (diamantähnlicher Kohlenstoff). Dies sind amorphe Kohlenstoffschichten bei denen im Nanometerbereich grafitähnliche und diamantähnliche Strukturen nebeneinander vorkommen, d.h. der Kohlenstoff in sogenannter sp2 und sp3 Hybridisierung vorkommt. Ein hoher sp3-Anteil führt zu einer harten, diamantähnlichen Schicht. Ein hoher sp2-Anteil führt zu einer weichen graphitähnlichen Schicht. Nachteilig bei diesem Verfahren sind allerdings die vor allem dabei entstehenden hohen Produktionskosten die im Wesentlichen auf die notwendige Galvanik zurückgehen. Aus diesem Grund ist die Anwendung dieses Verfahrens derzeit auf sogenannte High-End Produkte beschränkt. Das Galvanikverfahren ist nicht nur Kostenintensiv sondern belastet aufgrund der dafür notwendigen Lösungsmittel in erheblichem Masse die Umwelt. Auch aus diesem Grund möchte man von dieser Technologie möglichst wegkommen.
BESTÄTIGUNGSKOPIE Gemäss einem alternativen Ansatz wird die zu behandelnde Oberfläche zunächst nitriert und dann mit einer DLC-Schicht beschichtet. Durch das Nitrieren zu kombinieren mit DLC wird eine gewisse Korrosionsbeständigkeit erzielt. Weiterhin verleiht die DLC-Schicht der Oberfläche die gewünschte Farbe und setzt die Reibung herab. Problematisch ist allerdings, dass durch ein solches Verfahren nicht die oftmals notwendige Härte erreicht wird.
Es besteht daher das Bedürfnis nach einem Verfahren mit dem eine Schwärzung von Metalloberflächen erreicht wird, wobei gleichzeitig Korrosionsbeständigkeit und Härte erreicht werden soll bei niedriger bzw. herabgesetzter Reibung.
Der Erfindung liegt die Aufgabe zugrunde, ein solches Verfahren anzugeben. Erfindungsgemäss wird die Aufgabe Komponenten mit einer Stärke von nicht mehr als zwei Millimeter dadurch gelöst, dass die Komponente zunächst beispielsweise mittels Induktionshärten gehärtet wird. Anschliessend wird die Komponente nitriert um die Oberfläche korrosionsbeständig zu machen. Durch das Nitrieren wird die Härte der Komponente zu einem gewissen Grad wieder herabgesetzt. Die durch die Nitrierung entstehende Verbindungs- und Diffusionsschicht verleiht aber der dünnen Komponente beidseitig zusätzliche Stabilität. Anschliessend wird die Komponente mit einer DLC-Schicht beschichtet, die der Oberfläche eine schwarze Farbe verleiht und die die Reibung der Oberfläche herabsetzt.
Die Erfindung wird nun im Detail beispielhaft und mit Hilfe der Figur näher erläutert.
Figur 1 zeigt schematisch den Schichtaufbau einer mit dem erfindungsgemässen Verfahren behandelten Komponente.
Im Beispiel sei die Komponente ein Rohr mit 1.6mm Wanddicke aus niedrig legierten Stahl mit Perlit-Gefüge. Das Rohr wird zunächst in einem Induktionsofen soweit erhitzt, dass der Perlit in Austenit umwandelt. Hierzu sind zwischen 700°C und 1100°C notwendig. Dabei ist darauf zu achten, dass das Rohr genügend lange und gleichmässig erhitzt wird, so dass die Umwandlung in Austenit vollständig vor sich geht. Anschliessend erfolgt das Abschrecken, beispielsweise indem das Rohr mit gekühltem Stickstoff oder Ammoniak umströmt wird, so dass ein tetragonal verzerrtes Eisengitter (Martensit) erzeugt wird in dem Kohlenstoff eingelagert ist. Eine Einteilung des Abschreckens in Intervalle um Zugrisse und Schalenrisse zu vermeiden ist dabei nicht unbedingt notwendig, da das Rohr dünn genug ist. Nach dem Abschrecken ist das gehärtete Rohr spröde. Erfindungsgemäss kann aber auf das beim Härten sonst übliche Anlassen verzichtet werden, da das Rohr nun nitriert wird und bei dieser Nitrierung das Rohr auf ca. 450° erhitzt wird. Zum Nitrieren eignet sich beispielsweise das Plasmanitrieren oder das Gasnitrieren. Beim Plasmanitrieren wird das Rohr in eine Behandlungskammer gegeben, welche zunächst evakuiert wird und in die anschliessen Ammoniak eingelassen wird. Mittels Plasmagenerator wird nun über dem Rohr ein Plasma gezündet, in welchem Ammoniak zu Stickstoff und Wasserstoff dissoziiert. Der Stickstoff diffundiert in die Oberfläche des Rohres ein und bildet dort eine 0.3 bis 0.4 mm dicke Diffusionsschicht, wobei an der Oberfläche direkt eine ca. 20pm dicke sogenannte Verbindungsschicht mit ε- und γ'-Eisennitriden entsteht. Um die Korrosionsbeständigkeit dieser Verbindungsschicht weiter zu erhöhen kann diese oxidiert werden. Hierzu kann beispielsweise eine Dampfbeaufschlagung verwendet werden die die Eisenanteile korrodieren lässt und so eine Oxidschutzschicht gebildet wird.
Im Vergleich zur Induktionshärtung würde die Härte konkret auf ca. 900MPa absinken, allerdings verleiht die durch die Nitrierung entstehende Verbindungs- und Diffusionsschicht der dünnen Komponente beidseitig wieder zusätzlich Stabilität. Anschliessend wird die Komponente mit einer 2pm dicken DLC-Schicht, beispielsweise mittels PECVD beschichtet, die der Oberfläche eine schwarze Farbe verleiht und die die Reibung der Oberfläche herabsetzt. Diese Beschichtung kann in derselben Behandlungskammer stattfinden wie die Plasmanitrierung. Die Herabsetzung der Reibung der Oberfläche kann beispielsweise dadurch erreicht werden, dass in die DLC-Schicht ein Wasserstoffanteil von 16at% bis 20at% eingebaut wird, wodurch es verstärkt zur sp2 Hybridisierung der Kohlenstoffverbindungen kommt.
Aufgrund des Verfahrens entsteht ein wie in Figur 1 schematisch als Teilbereich dargestelltes Rohr dessen Substrat 3 zu einem grossen Prozentsatz Martensit-Gefüge aufweisst, in dessen Oberfläche Stickstoff eindiffundiert ist und somit eine Diffusionsschicht 5 bildet. Auf der Diffusionsschicht 5 ist eine durch das Nitrieren entstandene Verbindungschicht 7, deren äusserer Bereich vorzugsweise oxidiert ist. Auf dieser Verbindungschicht 7 ist eine DLC-Schicht vorgesehen, die der dem Rohr ein schwarzes Finish verleiht und die die Reibung der Oberfläche herabsetzt.
Bemerkenswert an dem oben beschriebenen Verfahren ist auch, dass sämtliche Verfahrensschritte in ein und derselben Behandlungskammer durchgeführt werden können. Die Behandlungskammer sollte hierzu einen Induktionsofen, einen Plasmagenerator für das Nitrieren und die PECVD Beschichtung sowie Gaszugänge für das Ammoniak umfassen. Während mittels Induktion das Rohr erhitzt wird kann dann schon damit begonnen werden, die Behandlungskammer zu evakuieren. Zum Abschrecken kann man dann gekühltes Ammoniak in die Behandlungskammer strömen lassen: Dies hat den Vorteil dass das zur Abschreckung verwendete Fluidum nicht mehr vollständig abgepumpt werden muss, weil es für den darauffolgenden Plasma-Nitierschritt sowieso benötigt wird.

Claims

Ansprüche
1. Verfahren zur Behandlung einer Komponente zur Härtung, Erhöhung der Korrosionsbeständigkeit, Herabsetzung der Reibung und Schwärzung der Oberfläche, wobei das Verfahren folgende Schritte umfasst:
- Bereitstellung der zu behandelnden Komponente
- Härtung der Komponente vorzugsweise mittels Induktionshärtung
- Erzeugung einer Stickstoffdiffusionsschicht mittels Nitrierung
- Erzeugung einer Verbindungsschicht mit e- und γ'-Eisennitriden ebenfalls mittels Nitrierung - Beschichtung der Komponente mit einer amorphen Kohlenstoffschicht
2. Verfahren nach Anspruch 1 , dadurch gekennzeichnet, dass es sich bei der Nitrierung um eine Plasmanitrierung handelt.
3. Verfahren nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass die Verbindungsschicht oxidiert wird, beispielsweise zur Erhöhung der Korrosionsbeständigkeit.
4. Verfahren nach einem der vorangehenden Ansprüche, dadurch gekennzeichnet dass die Härtung zumindest eine Aufheizung und zumindest eine Abschreckung umfasst, wobei für die Abschreckung ein Fluid verwendet wird welches im Nitrierschritt ebenfalls zur Verwendung kommt.
5. Verfahren nach Anspruch 5, dadurch gekennzeichnet, dass das Fluid Ammoniak zumindest umfasst.
6. Verfahren nach einem der vorangehenden Ansprüche, dadurch gekennzeichnet, dass die Nitrierung unmittelbar auf die Induktionshärtung ohne ein dazwischen liegendes Anlassen durchgeführt wird.
7. Verfahren nach einem der vorangehenden Ansprüche, dadurch gekennzeichnet, dass die beschriebenen Verfahrensschritte alle in derselben Behandlungskammer durchgeführt werden.
8. Anwendung eines Verfahrens nach einem der vorangehenden Ansprüche auf eine Komponente welche eine maximale Dicke von 2.0mm hat.
9. Behandlungskammer zum Durchführen eines der Verfahren nach Ansprüche 1 bis 8, dadurch gekennzeichnet, dass die Behandlungskammer eine Induktionsheizung zum Durchführen der Induktionshärtung und einen Plasmagenerator, sowie Mittel zur Evakuation und Gaseinlässe für Prozessgase umfasst.
10. Komponente (1) deren Substrat (3) Martensit-Gefüge zumindest teilweise aufweisst, in deren Oberfläche Stickstoff eindiffundierter Stickstoff eine Diffusionsschicht (5) bildet wobei auf der Diffusionsschicht (5) ist eine durch das Nitrieren entstandene Verbindungschicht (7) vorhanden ist, deren äusserer Bereich vorzugsweise oxidiert ist und auf dieser Verbindungschicht (7) ist eine DLC-Schicht (9) vorgesehen, die der Komponente ein schwarzes Finish verleiht und die die Reibung der Oberfläche im Vergleich zum Substrat (3) herabsetzt.
PCT/EP2013/001851 2012-07-11 2013-06-24 Dlc beschichtungen mit erhöhter korrosionsbeständigkeit WO2014008983A1 (de)