Classifications

• • D—TEXTILES; PAPER
  • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
  • D06N—WALL, FLOOR, OR LIKE COVERING MATERIALS, e.g. LINOLEUM, OILCLOTH, ARTIFICIAL LEATHER, ROOFING FELT, CONSISTING OF A FIBROUS WEB COATED WITH A LAYER OF MACROMOLECULAR MATERIAL; FLEXIBLE SHEET MATERIAL NOT OTHERWISE PROVIDED FOR
  • D06N7/00—Flexible sheet materials not otherwise provided for, e.g. textile threads, filaments, yarns or tow, glued on macromolecular material
• • D—TEXTILES; PAPER
  • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
  • D06N—WALL, FLOOR, OR LIKE COVERING MATERIALS, e.g. LINOLEUM, OILCLOTH, ARTIFICIAL LEATHER, ROOFING FELT, CONSISTING OF A FIBROUS WEB COATED WITH A LAYER OF MACROMOLECULAR MATERIAL; FLEXIBLE SHEET MATERIAL NOT OTHERWISE PROVIDED FOR
  • D06N7/00—Flexible sheet materials not otherwise provided for, e.g. textile threads, filaments, yarns or tow, glued on macromolecular material
  • D06N7/0002—Wallpaper or wall covering on textile basis
• • D—TEXTILES; PAPER
  • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
  • D06N—WALL, FLOOR, OR LIKE COVERING MATERIALS, e.g. LINOLEUM, OILCLOTH, ARTIFICIAL LEATHER, ROOFING FELT, CONSISTING OF A FIBROUS WEB COATED WITH A LAYER OF MACROMOLECULAR MATERIAL; FLEXIBLE SHEET MATERIAL NOT OTHERWISE PROVIDED FOR
  • D06N7/00—Flexible sheet materials not otherwise provided for, e.g. textile threads, filaments, yarns or tow, glued on macromolecular material
  • D06N7/0092—Non-continuous polymer coating on the fibrous substrate, e.g. plastic dots on fabrics
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
  • B32B17/02—Layered products essentially comprising sheet glass, or glass, slag, or like fibres in the form of fibres or filaments
  • B32B17/04—Layered products essentially comprising sheet glass, or glass, slag, or like fibres in the form of fibres or filaments bonded with or embedded in a plastic substance
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
  • C08J5/04—Reinforcing macromolecular compounds with loose or coherent fibrous material
  • C08J5/06—Reinforcing macromolecular compounds with loose or coherent fibrous material using pretreated fibrous materials
  • C08J5/08—Reinforcing macromolecular compounds with loose or coherent fibrous material using pretreated fibrous materials glass fibres
• • D—TEXTILES; PAPER
  • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
  • D06N—WALL, FLOOR, OR LIKE COVERING MATERIALS, e.g. LINOLEUM, OILCLOTH, ARTIFICIAL LEATHER, ROOFING FELT, CONSISTING OF A FIBROUS WEB COATED WITH A LAYER OF MACROMOLECULAR MATERIAL; FLEXIBLE SHEET MATERIAL NOT OTHERWISE PROVIDED FOR
  • D06N2201/00—Chemical constitution of the fibres, threads or yarns
  • D06N2201/08—Inorganic fibres
  • D06N2201/082—Glass fibres
• • D—TEXTILES; PAPER
  • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
  • D06N—WALL, FLOOR, OR LIKE COVERING MATERIALS, e.g. LINOLEUM, OILCLOTH, ARTIFICIAL LEATHER, ROOFING FELT, CONSISTING OF A FIBROUS WEB COATED WITH A LAYER OF MACROMOLECULAR MATERIAL; FLEXIBLE SHEET MATERIAL NOT OTHERWISE PROVIDED FOR
  • D06N2209/00—Properties of the materials
  • D06N2209/12—Permeability or impermeability properties
  • D06N2209/126—Permeability to liquids, absorption
• • E—FIXED CONSTRUCTIONS
  • E04—BUILDING
  • E04F—FINISHING WORK ON BUILDINGS, e.g. STAIRS, FLOORS
  • E04F13/00—Coverings or linings, e.g. for walls or ceilings
  • E04F13/07—Coverings or linings, e.g. for walls or ceilings composed of covering or lining elements; Sub-structures therefor; Fastening means therefor
  • E04F13/08—Coverings or linings, e.g. for walls or ceilings composed of covering or lining elements; Sub-structures therefor; Fastening means therefor composed of a plurality of similar covering or lining elements
  • E04F13/14—Coverings or linings, e.g. for walls or ceilings composed of covering or lining elements; Sub-structures therefor; Fastening means therefor composed of a plurality of similar covering or lining elements stone or stone-like materials, e.g. ceramics concrete; of glass or with an outer layer of stone or stone-like materials or glass
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/24—Structurally defined web or sheet [e.g., overall dimension, etc.]
  • Y10T428/24802—Discontinuous or differential coating, impregnation or bond [e.g., artwork, printing, retouched photograph, etc.]
  • Y10T428/2481—Discontinuous or differential coating, impregnation or bond [e.g., artwork, printing, retouched photograph, etc.] including layer of mechanically interengaged strands, strand-portions or strand-like strips
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
  • Y10T442/20—Coated or impregnated woven, knit, or nonwoven fabric which is not [a] associated with another preformed layer or fiber layer or, [b] with respect to woven and knit, characterized, respectively, by a particular or differential weave or knit, wherein the coating or impregnation is neither a foamed material nor a free metal or alloy layer
  • Y10T442/2041—Two or more non-extruded coatings or impregnations
  • Y10T442/2098—At least two coatings or impregnations of different chemical composition
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
  • Y10T442/20—Coated or impregnated woven, knit, or nonwoven fabric which is not [a] associated with another preformed layer or fiber layer or, [b] with respect to woven and knit, characterized, respectively, by a particular or differential weave or knit, wherein the coating or impregnation is neither a foamed material nor a free metal or alloy layer
  • Y10T442/2738—Coating or impregnation intended to function as an adhesive to solid surfaces subsequently associated therewith
  • Y10T442/2754—Pressure-sensitive adhesive

Definitions

• the present invention relates to a repositionable wall covering, based on glass fibers, whose final adhesion to the wall can be obtained, after laying, by applying water or a water-based paint composition.
• Fiberglass wallcoverings have been known for many, many years. They are easy to apply and relatively inexpensive, can be painted with water-based paints, are leachable after painting, and resist better than wallpaper in tearing, fire and moisture.
• the installation of a conventional glass fiber wall covering typically comprises the following successive steps:
• the present invention aims to facilitate and shorten substantially the bonding phase (steps 1 - 3). It offers a pre-glued fiberglass wall covering with a special adhesive system.
• This adhesive allows easy application of the glass textile to the wall without sizing or prior humidification.
• the final fixation is then done at the time of application of the paint. This penetrates through the openings of the glass textile and, after drying, the glue firmly to the wall. The user thus saves the gluing step and the drying step of the glue.
• the present invention is based on the idea of trying to combine on the same wall covering both the self-adhesive / repositionable function (EasyFix ® ) and the final bonding function by moistening (activating) a latent adhesive (EasyGlue ® ).
• the present invention therefore relates to a self-adhesive wall covering comprising
• PSA pressure sensitive adhesive
• the present invention also relates to a method for laying such a self-adhesive wall covering.
• wall covering is meant a flat product in the form of a strip of a width generally between a few tens of centimeters and about one meter, stored and sold in the form of a roll.
• This coating is intended to be stuck on the walls of a room or a building or on other surfaces such as the ceiling, excluding floors.
• the term "closed-structure glass textile” means a textile, woven or non-woven, having a permeability to the passage of air, measured according to ISO 9237, at 200 Pa at most equal to 50 L / (m 2 .s).
• Such a glass textile has no openings visible to the naked eye and therefore has a closed appearance, uniform, more or less structured.
• Such a textile may be a glass cloth (woven structure) or a glass cloth (non-woven or non-woven structure). It is preferably a glass cloth. Its cohesion is ensured in known manner by a polymeric binder. This polymeric binder must be both insoluble in water, but sufficiently hydrophilic to pass the water required to activate the latent adhesive applied to one side of the glass fabric.
• Such water-permeable polymeric binders are known in the art and are generally based on hydrolyzed starches, hydrophilic acrylic resins, especially anionic styrenic / acrylic resins, and / or styrene-butadiene rubber (SBR).
• hydrophilic acrylic resins especially anionic styrenic / acrylic resins, and / or styrene-butadiene rubber (SBR).
• Textile glass used for the present invention are commercially available and are marketed by the applicant for example under the name NOVELIO ®.
• Their basis weight is advantageously between 80 and 450 g / m 2 , preferably between 100 and 300 g / m 2 and in particular between 150 and 250 g / m 2 .
• the adhesive coating is applied on one side of the glass textile. It may have a monolayer structure, i.e., the adhesive composition used in its formation may contain both the pressure sensitive adhesive (PSA) and the latent water activatable adhesive.
• the water-activatable latent adhesive is then present in the adhesive coating (B) at 5 to 150 g / m 2 , preferably 50 to 120 g / m 2 , particularly 80 at 100 g / m 2 , and the PSA at 5 and 80 g / m 2 , preferably 10 to 50 g / m 2 , in particular 25 to 40 g / m 2 .
• the adhesive coating has a bi-layer or multi-layer structure in which the PSA and the water-activatable latent adhesive are present as two separate adhesive layers, applied separately from two different adhesive compositions.
• Each of these layers may, independently of the other, be continuous or discontinuous, the term "discontinuous" encompassing both the layers consisting of a plurality of distinct elements and the layers having a plurality of openings distributed more or less regularly over the entire surface of the diaper.
• the layer containing the water-activatable latent adhesive is preferably that deposited directly on the glass textile, and the layer containing the PSA component is deposited, in a second step, on the layer of latent adhesive.
• the adhesive coating (B) therefore comprises
• (B2) a second layer, continuous or discontinuous, formed by a PSA, said second layer being deposited on the first layer (B1) and / or adjacent thereto.
• the second layer (B2) can of course extend beyond the first layer and be in direct contact with the glass fabric in the areas between the discrete elements or in the areas corresponding to the openings of the first layer.
• the first layer is formed by a first set of straight lines parallel to each other
• the second layer is formed by another set of straight lines parallel to each other. but perpendicular to the first.
• the first adhesive layer (B1) that is to say that formed by the latent adhesive activated by water, is a continuous layer deposited on the whole of one side of the glass textile (A). This continuity of the adhesive activatable by water ensures a definitive, satisfactory and regular adhesion, without blistering or areas of lesser adhesion.
• a second adhesive layer (B2) discontinuous consisting of separate elements.
• the ratio of the surface area B2 to the area of the surface B1 is preferably less than 0.5, in particular less than 0.3 and most preferably less than 0.1.
• This embodiment may be of interest for example when the presence of PSA may weaken the adhesion of the activatable adhesive by the water of the first layer.
• initial tack sufficient to adhere by simple contact / pressure on a clean and dry wall and not to peel off under the effect of its own weight. In known manner, this tack must not exceed a certain value so that the wall covering remains easily peelable and repositionable until it has been moistened.
• the adhesive coating (B), whether in single-layer or multilayer form, advantageously has an initial adhesion force of between 0.2 and 2 N. This adhesion strength is measured as described in the examples. below.
• the tack is exclusively due to the pressure-sensitive adhesive and the adjustment of this adhesive force is part of the general knowledge of the skilled person who will know how to choose the nature and the concentrations of the different ingredients of the sensitive adhesive.
• pressure such as polymers, tackifier, fillers etc.
• the geometry or thickness of the PSA layer may be selected from the group consisting of polymers, tackifier, fillers etc.
• the pressure-sensitive adhesives usable in the present invention are known. They can be deposited in the form of a liquid composition based on organic solvent or water (latex) or they can be hot melt polymers, that is to say polymers of low molecular weight which, at molten state, have a sufficiently low viscosity to spread appropriately.
• PSAs are generally based on an elastomeric resin which may contain a tackifier (tackifier).
• the polymer resin is conventionally chosen from acrylic resins, butyl rubber, ethylene / vinyl acetate copolymers (EVA), natural rubber, vinyl ethers, and block copolymers based on styrene such as styrene-based copolymers.
• styrene-based copolymers such as styrene-based copolymers.
• SBS butadiene-styrene
• SEBS styrene-ethylene-butylene-styrene
• SEP styrene-ethylene-propylene
• SIS styrene-isoprene-styrene
• EVA and block copolymers based on styrene have the advantage of being hot melt elastomers and can therefore be applied as a solvent-free composition.
• the second adhesive layer that is to say that formed by PSA, advantageously has a dry surface weight of between 1 and 80 g / m 2 , preferably between 2 and 50 g / m 2 , and in particular between 4 and 40 g / m 2 .
• This second pressure-sensitive adhesive layer is deposited on and / or adjacent to a first layer formed by the water-activatable latent adhesive.
• This latent adhesive when in the dry state, is completely inactive, that is to say devoid of stickiness.
• any adhesive conventionally used for bonding wallpapers and other wall coverings such as starch-based adhesives, in particular potato starch, corn starch or wheat starch, may be used in principle.
• starches modified by hydrolysis or baking dextrins, cyclodextrins, mono- and oligosaccharides, cellulose alkyl ethers and cellulose hydroxyalkyl ethers, polyethylene glycol, hydrophilic polyurethanes, polyacrylamides, aqueous vinyl adhesives such as homopolymers of preferably poly (vinyl acetate) (PVAC) plasticized, partially hydrolysed polyvinyl acetate, polyvinyl alcohol, polyvinylpyrrolidone, copolymers of vinylpyrrolidone and vinyl, copolymers of maleic anhydride and methyl vinyl ether or copolymers of vinyl acetate and maleates or acrylates.
• PVAC poly (vinyl acetate)
• the water-activatable latent adhesive can
• Such a latent, water-activatable adhesive may contain, in a known manner, salts for increasing its affinity for water.
• This adhesive is used in customary amounts, generally between 5 and 150 g / m 2 , preferably between 50 and 120 g / m 2 , in particular between 80 and 100 g / m 2 , these indications corresponding to the weight per unit area. dry state.
• the wallcovering of the present invention allows the implementation of an extremely simple and fast process made possible by the dual functionality of the adhesive layer containing both a pressure-sensitive adhesive and a water-activatable latent adhesive. .
• the method of laying the wall covering comprises the following successive steps:
• the support preferably a wall or ceiling, must be clean and dry to ensure good initial adhesiveness of the coating.
• pressure may be applied, for example, using a marbling knife or roller to adhere it to the support prior to the water activation step. .
• Activation of the latent adhesive is done by applying water over the entire surface of the wall covering.
• This application of water can be done by any appropriate means, for example by spraying or using a roller.
• At least one layer of water-based paint preferably with a paint roller, is applied to the wallcovering which is brought into contact with the support and possibly stuck.
• a Novelio ® closed glass sheet with a surface weight of 180 g / m 2 and an air permeability of 10 L / (m 2 ⁇ s) is applied to a continuous layer of a latent adhesive which can be activated at water-based homopolymer of vinyl acetate and dextrin sold by Arkema under the name Craymul ® 4366.
• This layer is applied at a rate of 80-90 g / m 2.
• a second continuous layer of a pressure sensitive adhesive based on an acrylic resin (Craymul ® 4508) sold by Arkema is about 30 g / m 2 .
• the double adhesive layer obtained in this way has an initial tackiness of about 0.47 N, sufficient to attach the wall covering to the wall by a simple hand pressure. It is repositionable several times. After applying a coat of water-based acrylic paint (SilverPro AS-60) and drying, a satisfactory final fixing is obtained.
• a sample of the glass cloth is glued on a plasterboard (5 cm x 10 cm) fixed on a support.
• a controlled pressure of 2500 kg is exerted.
• the pressure is manual (paint roller).
• a 2 cm wide strip (length 10 cm) is cut with a cutter in the fabric sample and this strip is subjected to a peel test at 90 ° C. on a traction device marketed by the company. Zwick.
• the peel rate is 20 mm / minute.
• the results in the table below correspond to the mean value ⁇ standard deviation, calculated over three tests.
• the fabric according to the invention has self-adhesiveness of satisfactory properties, comparable to those of the open structure to glass cloth EasyFix ®.
• the glass fabric according to the invention thus combines the advantages of products of the state of the art, namely a quick and easy installation, the absence of bonding walls and coating, and a relatively easy takeoff.

Landscapes

• Engineering & Computer Science (AREA)
• Textile Engineering (AREA)
• Adhesives Or Adhesive Processes (AREA)
• Laminated Bodies (AREA)
• Finishing Walls (AREA)
• Synthetic Leather, Interior Materials Or Flexible Sheet Materials (AREA)
• Reinforced Plastic Materials (AREA)

Priority Applications (6)

Applications Claiming Priority (2)

Publications (1)

Family

ID=48656236

Family Applications (1)

Country Status (8)

Cited By (2)

Families Citing this family (11)

Citations (13)

Family Cites Families (28)

• 2012
  • 2012-06-04 FR FR1255158A patent/FR2991358B1/fr active Active
• 2013
  • 2013-05-30 CN CN201380029183.3A patent/CN104520497B/zh not_active Expired - Fee Related
  • 2013-05-30 WO PCT/FR2013/051215 patent/WO2013182783A1/fr not_active Ceased
  • 2013-05-30 EP EP13730012.5A patent/EP2855762B1/fr not_active Not-in-force
  • 2013-05-30 US US14/405,198 patent/US9359720B2/en not_active Expired - Fee Related
  • 2013-05-30 DK DK13730012.5T patent/DK2855762T3/en active
  • 2013-05-30 JP JP2015515565A patent/JP6039798B2/ja not_active Expired - Fee Related
  • 2013-05-30 RU RU2014154245A patent/RU2630097C2/ru active

Patent Citations (13)

Also Published As

Similar Documents

Legal Events