Classifications

• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B15/00—Layered products comprising a layer of metal
  • B32B15/04—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material
  • B32B15/08—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material of synthetic resin
  • B32B15/088—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material of synthetic resin comprising polyamides
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29D—PRODUCING PARTICULAR ARTICLES FROM PLASTICS OR FROM SUBSTANCES IN A PLASTIC STATE
  • B29D24/00—Producing articles with hollow walls
  • B29D24/002—Producing articles with hollow walls formed with structures, e.g. cores placed between two plates or sheets, e.g. partially filled
  • B29D24/005—Producing articles with hollow walls formed with structures, e.g. cores placed between two plates or sheets, e.g. partially filled the structure having joined ribs, e.g. honeycomb
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B27/00—Layered products comprising a layer of synthetic resin
  • B32B27/06—Layered products comprising a layer of synthetic resin as the main or only constituent of a layer, which is next to another layer of the same or of a different material
  • B32B27/08—Layered products comprising a layer of synthetic resin as the main or only constituent of a layer, which is next to another layer of the same or of a different material of synthetic resin
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B27/00—Layered products comprising a layer of synthetic resin
  • B32B27/12—Layered products comprising a layer of synthetic resin next to a fibrous or filamentary layer
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B27/00—Layered products comprising a layer of synthetic resin
  • B32B27/18—Layered products comprising a layer of synthetic resin characterised by the use of special additives
  • B32B27/20—Layered products comprising a layer of synthetic resin characterised by the use of special additives using fillers, pigments, thixotroping agents
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B27/00—Layered products comprising a layer of synthetic resin
  • B32B27/34—Layered products comprising a layer of synthetic resin comprising polyamides
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B3/00—Layered products comprising a layer with external or internal discontinuities or unevennesses, or a layer of non-planar shape; Layered products comprising a layer having particular features of form
  • B32B3/10—Layered products comprising a layer with external or internal discontinuities or unevennesses, or a layer of non-planar shape; Layered products comprising a layer having particular features of form characterised by a discontinuous layer, i.e. formed of separate pieces of material
  • B32B3/12—Layered products comprising a layer with external or internal discontinuities or unevennesses, or a layer of non-planar shape; Layered products comprising a layer having particular features of form characterised by a discontinuous layer, i.e. formed of separate pieces of material characterised by a layer of regularly- arranged cells, e.g. a honeycomb structure
• • E—FIXED CONSTRUCTIONS
  • E04—BUILDING
  • E04C—STRUCTURAL ELEMENTS; BUILDING MATERIALS
  • E04C2/00—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels
  • E04C2/30—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by the shape or structure
  • E04C2/34—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by the shape or structure composed of two or more spaced sheet-like parts
  • E04C2/36—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by the shape or structure composed of two or more spaced sheet-like parts spaced apart by transversely-placed strip material, e.g. honeycomb panels
  • E04C2/365—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by the shape or structure composed of two or more spaced sheet-like parts spaced apart by transversely-placed strip material, e.g. honeycomb panels by honeycomb structures
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2255/00—Coating on the layer surface
  • B32B2255/02—Coating on the layer surface on fibrous or filamentary layer
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
  • B32B2262/02—Synthetic macromolecular fibres
  • B32B2262/0261—Polyamide fibres
  • B32B2262/0269—Aromatic polyamide fibres
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
  • B32B2262/10—Inorganic fibres
  • B32B2262/101—Glass fibres
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
  • B32B2262/10—Inorganic fibres
  • B32B2262/106—Carbon fibres, e.g. graphite fibres
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
  • B32B2262/14—Mixture of at least two fibres made of different materials
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2305/00—Condition, form or state of the layers or laminate
  • B32B2305/02—Cellular or porous
  • B32B2305/024—Honeycomb
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2305/00—Condition, form or state of the layers or laminate
  • B32B2305/07—Parts immersed or impregnated in a matrix
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2305/00—Condition, form or state of the layers or laminate
  • B32B2305/22—Fibres of short length
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2607/00—Walls, panels
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/24—Structurally defined web or sheet [e.g., overall dimension, etc.]
  • Y10T428/24149—Honeycomb-like

Definitions

• This invention pertains to a fiber-reinforced thermoplastic honeycomb and articles made from the honeycomb.
• thermoplastic honeycomb prepared by a continuous or semi-continuous process.
• a pre-corrugated or non-corrugated web of fiber-reinforced or non-reinforced thermoplastic is laid up and consolidated into a honeycomb layer by layer, each layer representing a half cell height of the finished honeycomb.
• US Patent Number 5,421 ,935 to Dixon and Turner describes a method and apparatus for forming a honeycomb structure in which a plurality of thermoplastic layers are fused together at selected locations.
• the thermoplastic layers at each of the selected locations are melted together to form a welded portion which includes first and second exterior surfaces.
• the welding of the thermoplastic layers is controlled so that no more than one of the exterior surfaces is melted. This partial melting of one layer prevents undesirable welding to adjacent layers.
• US Patent Number 5,421 ,935 to Landi and Wilson describes a resilient panel having anisotropic flexing characteristics in which thermal compression bonding techniques have been used to laminate a plurality of sheets of thermoplastic polyurethane material together with bonds that are in strip form, spaced at regular intervals, and staggered between alternate sheets of material.
• the laminated stack was then cut into slices of appropriate thickness, and the slices were expanded to form a honeycombed core which, while held in spread apart disposition, was thermally pre-formed and made ready to receive facing materials.
• the above three patents all involve at least a two step process. The first step is the making of a thermoplastic web and the second step involves conversion of the web into a honeycomb. There is an ongoing need to provide a single step process and a product having improved mechanical properties.
• thermoplastic honeycomb core comprising from 40 to 90 weight percent of an aliphatic polyamide polymer and from 10 to 60 weight percent of discontinuous fibers distributed evenly throughout the polymer wherein
• the fibers are carbon, glass, para-aramid or a combination thereof, and
• the fibers have a length of from 0.5 to 10 mm.
• FIG 1 A is a partial planar view of a prior art thermoplastic
• FIG 1 B is a detailed view of a portion of honeycomb shown in FIG.
• FIG 2A is a partial planar view of a thermoplastic honeycomb of this invention.
• FIG 2B is a detailed view of a portion of honeycomb shown in FIG. 2A.
• FIG 3 is an elevation view of a honeycomb core.
• FIG 4 is a representation of another view of a hexagonal cell shaped honeycomb.
• FIG 5 is an illustration of honeycomb provided with facesheet(s).
• This invention pertains to a fiber-reinforced thermoplastic
• honeycomb core comprising from 40 to 90 weight percent of an aliphatic polyamide polymer and from 10 to 60 weight percent of discontinuous fibers distributed evenly throughout the polymer. The weight percent is based on the total weight of fiber plus polymer.
• the honeycomb is free of fused cell walls.
• FIG 1 A shows generally at 10 a partial planar view of a prior art thermoplastic honeycomb.
• the honeycomb is made from a plurality of thermoplastic webs 1 1 that have been expanded into a honeycomb structure.
• the individual webs are fused or bonded together in regions as shown at 12. This fused region forms the fused cell walls of adjacent cells.
• An example of fused cell walls are shown at 12a between cells 13 and 14.
• FIG 1 B is a more detailed view 15 of a portion of honeycomb in the region of the fused cell walls of cells 13 and 14 as shown in FIG. 1A.
• the inner cell walls of cells 13 and 14 are shown at 16 and 17 respectively.
• the outer cell walls of cells 13 and 14 are shown at 18 and 19 respectively.
• the fused cell walls are shown at 12a.
• This technology is further detailed in US Patent Number 5,421 ,935.
• FIG 2A shows generally at 20 a partial planar view of a
• thermoplastic honeycomb of this invention Representative cells 23 and 24 are shown.
• FIG 2B is a more detailed view 25 of a portion of honeycomb in the region of the cell 23 and 24 as shown in FIG 2A. Unlike cells 13 and 14 in FIG 1 B there are no outer cell wall equivalents to 18 and 19.
• the honeycomb of this invention has only inner cell walls 26 and 27. That is to say that the honeycomb is free of fused cell walls like 12 and 12a.
• the fibers of this invention have a length of from 0.5 to 10 mm. In some embodiments, the fibers have a length of from 2 to 7 mm or even from 3 to 5 mm.
• the fibers comprise from 5 to 60 weight percent of the weight of polymer plus fiber. In some embodiments, the fibers comprise from 15 to 50 weight percent and in other
• fibers from 20 to 40 weight percent.
• the fibers are distributed evenly throughout the polymer. In one embodiment, the fibers are randomly oriented within the polymer. In another embodiment, at least 20 percent of the fibers are oriented in a particular direction. Fiber orientation may be achieved through specific die configurations when extruding the fiber-polymer blend.
• the fibers are of carbon, glass, para-aramid or a combination thereof.
• Suitable glass fibers include E-glass and S-glass fiber.
• E-Glass is a commercially available low alkali glass. One typical composition consists of 54 weight % SiO 2 , 14 weight % AI 2 O 3 , 22 weight % CaO/MgO, 10 weight % B2O3 and less then 2 weight % Na2O K 2 O. Some other materials may also be present at impurity levels.
• S-Glass is a commercially available magnesia-alumina-silicate glass. This composition is stiffer, stronger, more expensive than E-glass and is commonly used in polymer matrix composites.
• Para-aramid is a polyamide wherein at least 85% of the amide (-
• CONH- linkages are attached directly to two aromatic rings.
• Suitable aramid fibers are described in Man-Made Fibres - Science and
• a preferred para-aramid is poly(p-phenylene
• PPD-T terephthalamide
• terephthaloyl chloride As a general rule, other diamines and other diacid chlorides can be used in amounts up to as much as about 10 mole percent of the p-phenylene diamine or the terephthaloyl chloride, or perhaps slightly higher, provided only that the other diamines and diacid chlorides have no reactive groups which interfere with the polymerization reaction.
• PPD-T also, means copolymers resulting from incorporation of other aromatic diamines and other aromatic diacid chlorides such as, for example, 2,6-naphthaloyl chloride or chloro- or dichloroterephthaloyl chloride or 3,4'-diaminodiphenylether.
• Another suitable fiber is one based on aromatic copolyamide prepared by reaction of terephthaloyl chloride (TPA) with a 50/50 mole ratio of p-phenylene diamine (PPD) and 3, 4'-diaminodiphenyl ether (DPE).
• TPA terephthaloyl chloride
• PPD p-phenylene diamine
• DPE 3, 4'-diaminodiphenyl ether
• Yet another suitable fiber is that formed by polycondensation reaction of two diamines, p-phenylene diamine and 5-amino-2-(p- aminophenyl) benzimidazole with terephthalic acid or anhydrides or acid chloride derivatives of these monomers.
• Additives can be used with the aramid and it has been found that up to as much as 10 percent or more, by weight, of other polymeric material can be blended with the aramid.
• Copolymers can be used having as much as 10 percent or more of other diamine substituted for the diamine of the aramid or as much as 10 percent or more of other diacid chloride substituted for the diacid chloride or the aramid.
• Kevlar® fibers which are available from E. I. du Pont de Nemours & Co. , Wilmington, DE (“herein DuPont”) and Twaron® fibers, which are available from Teijin Aramid BV, Arnhem, Netherlands.
• Carbon fiber used in this invention may be in the form of short cut or chopped fiber, also known as floe. Floe is made by cutting continuous filament fibers into short lengths without significant fibrillation. An example of a suitable length range is from 1 .5 mm to 20 mm.
• Carbon fibers suitable for use in this invention can be made from either polyacrylonitrilie (PAN) or pitch precursor using known technological methods, for example as described in: J.B. Donnet and R. C. Bansal. Carbon Fibers, Marcel Dekker, 1984. Suppliers of chopped carbon fibers include Hexcel
• the fibers may be carbon nanotubes (CNT's) or other nanofibers either used alone or in combination with other fibers that have a length of at least 1 micrometer.
• CNT's carbon nanotubes
• other nanofibers either used alone or in combination with other fibers that have a length of at least 1 micrometer.
• the polymer is an aliphatic polyamide. Suitable polyamides include nylon 6, nylon 66 or polyphthalamide. The polymer comprises from 40 to 90 weight percent of the weight of polymer plus fiber. In some
• the polymer comprises from 50 to 85 weight percent and in other embodiments from 60 to 80 weight percent.
• Such materials are available under the tradename ZYTEL® from DuPont.
• honeycomb of this invention is made by an extrusion process.
• Pellets or flake comprising a blend of fibres evenly distributed in a polymer are fed via an extruder through a die.
• the die has the desired shape of the honeycomb core.
• Hexagonal, square, over-expanded and flex-core cells are among the most common cell shapes.
• Such cell types are well known in the art and reference can be made to Honeycomb Technology pages 14 to 20 by T. Bitzer (Chapman & Hall, publishers, 1997) for additional information on possible geometric cell types.
• thermoplastic honeycomb described above may be any thermoplastic honeycomb described above.
• FIG 3 is an elevation view 30 of the honeycomb shown in FIG 2A and shows the two exterior surfaces, or faces 31 formed at both ends of the cells.
• the core also has edges 32.
• FIG 4 is a three-dimensional view of the thermoplastic honeycomb. The "T" dimension or the thickness of the honeycomb is shown at 40 in FIG 4.
• FIG 5 shows a structural sandwich panel 50 assembled from a thermoplastic honeycomb core 51 with facesheets 52 attached to the two exterior surfaces of the core.
• the preferred facesheet material is a polymeric film or sheet such as a thermoplastic film.
• the facesheets may be a prepreg, a fibrous sheet impregnated with thermoset or thermoplastic resin. In other embodiments, the facesheets may be metallic. In some circumstances an adhesive film 53 is also used. There may be at least two facesheets on either side of the core.
• an extruded sheet structure was made from a blend of 57 weight percent polyamide 66 reinforced with 43 weight percent short glass fibers, commercially available from E.I du Pont de Nemours and Company as Zytel® 70G43L.
• the sheet structure was produced by extruding the fiber-reinforced polyamide onto a belt using a Davis- Standard Model DS15 38mm (1 .5 inches) single-screw extruder.
• the extruder contained four heat zones. Zones 1 and 2 were set to a temperature of 285 degrees C, and zones 3 and 4 were set to a
• a sheet structure was made from an unreinforced polyamide 66, commercially available from E.I. du Pont de Nemours and Company of Wilmington, DE as Zytel® E51 HSB.
• the sheet structure was produced by extruding the polyamide onto a belt using a Davis-Standard Model DS15 38mm (1 .5 inches) single-screw extruder.
• the extruder contained four heat zones. Zones 1 and 2 were set to a temperature of 285 degrees C, and zones 3 and 4 were set to a temperature of 282 degrees C.
• the initial screw speed was set to 76rpm, and the exit roll temperature was set to 66 degrees C. Two sheets of different thicknesses were produced under these conditions and tested in the machine direction according to ASTM D882-10, as shown in Table 1 .
• Table 1 Table 1
• polymeric blends were produced from commercially available polymeric materials listed in Table 2. These materials are available from E.I du Pont de Nemours and Company, Wilmington, DE. The polymeric blends and fiber-polymer formulations made from these raw materials are listed in Table 3. The fiber lengths are in the range of from 3 to 5 mm. Also shown in Table 3 is the weight percent of reinforcing fiber in the final fiber-polymer formulation, the remaining weight percent being the polyamide nylon 6,6.
• the fiber-polymer formulations were produced by pre-blending the commercially available component pellets to the desired weight percent ratios. The blended pellets were then fed into a loss-in-weight feed hopper that fed the pellets into a 30mm single-screw extruder. The material was fed at a speed of 30 pounds per hour under a barrel temperature set-point of 240 degrees C. The screw used was a 25mm auger-type screw. The final fiber-polymer formulation was then extruded through a 4.76mm (3/16") hole die and into a water bath for instantaneous cooling. The extruded rope was then fed through a pelletizer. The pellets were collected and dried overnight at 95 degrees C in a Blue M oven.
• the material was then fed into a Nissei 6oz FN3000 single-screw injection molding machine.
• the machine was set to a temperature of 290 degrees C with an injection pressure of 60MPa to make all-purpose tensile bars.
• Honeycomb structures can be produced in a similar way to
• a fiber-polymer blend can comprise from 40-90% of Zytel® 70G43L and from 10-60% of of Zytel® E51 HSB.
• a fiber-polymer formulation in pellet form can be prepared by blending 75 weight percent of Zytel® 70G43L and 25 weight percent of Zytel® E51 HSB as per Example 4.
• the blended pellets can be fed directly to an extruder or to a pelletizing machine for later use as a feedstock for an extruder.
• the extruder has a die that will produce a honeycomb stucture, the dimensions of the die being such that after extrusion and cooling the honeycomb is of the desired dimensions.
• the extruded structure can also be expanded or stretched at some immediate point after the die while the polymer is still in its softened stage to increase the overall size of the structure.
• the extruded structure can either be cut to the final dimensions or can have facesheet layers added to the top and bottom, either after the polymer has hardened or while in its softened stage. Such a honeycomb is free of fused cell walls.
• Comparative Example C can be prepared as per Example 1 1 except that only Zytel® E51 HSB ,which contains no reinforcing fibers, is used.
• Example 1 1 will have higher mechanical strength properties such as toughness, shear and compression when compared with Comparative Example C due to the presence of discontinuous reinforcing fibers.

Landscapes

• Engineering & Computer Science (AREA)
• Architecture (AREA)
• Civil Engineering (AREA)
• Structural Engineering (AREA)
• Mechanical Engineering (AREA)
• Laminated Bodies (AREA)

Priority Applications (5)

Applications Claiming Priority (2)

Publications (1)

Family

ID=48576542

Family Applications (1)

Country Status (6)

Cited By (1)

Families Citing this family (4)

Citations (6)

Family Cites Families (6)

• 2013
  • 2013-05-17 WO PCT/US2013/041493 patent/WO2013180978A1/en not_active Ceased
  • 2013-05-17 JP JP2015515034A patent/JP6224092B2/ja not_active Expired - Fee Related
  • 2013-05-17 EP EP13726950.2A patent/EP2855141A1/en not_active Withdrawn
  • 2013-05-17 CN CN201380026236.6A patent/CN104334338A/zh active Pending
  • 2013-05-17 CA CA 2874328 patent/CA2874328A1/en not_active Abandoned
  • 2013-05-17 US US14/401,649 patent/US20150104605A1/en not_active Abandoned

Patent Citations (6)