WO2013086990A1 - Die casting device and method for amorphous alloy - Google Patents

Die casting device and method for amorphous alloy Download PDF

Info

Publication number
WO2013086990A1
WO2013086990A1 PCT/CN2012/086494 CN2012086494W WO2013086990A1 WO 2013086990 A1 WO2013086990 A1 WO 2013086990A1 CN 2012086494 W CN2012086494 W CN 2012086494W WO 2013086990 A1 WO2013086990 A1 WO 2013086990A1
Authority
WO
WIPO (PCT)
Prior art keywords
die
amorphous alloy
sealing chamber
chamber
die casting
Prior art date
Application number
PCT/CN2012/086494
Other languages
English (en)
French (fr)
Inventor
Faliang Zhang
Original Assignee
Shenzhen Byd Auto R&D Company Limited
Byd Company Limited
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenzhen Byd Auto R&D Company Limited, Byd Company Limited filed Critical Shenzhen Byd Auto R&D Company Limited
Priority to US14/365,826 priority Critical patent/US20140352907A1/en
Priority to EP12858511.4A priority patent/EP2790853A4/en
Publication of WO2013086990A1 publication Critical patent/WO2013086990A1/en
Priority to US14/971,761 priority patent/US20160121392A1/en

Links

Classifications

    • BPERFORMING OPERATIONS; TRANSPORTING
    • B22CASTING; POWDER METALLURGY
    • B22DCASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
    • B22D18/00Pressure casting; Vacuum casting
    • B22D18/02Pressure casting making use of mechanical pressure devices, e.g. cast-forging
    • BPERFORMING OPERATIONS; TRANSPORTING
    • B22CASTING; POWDER METALLURGY
    • B22DCASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
    • B22D17/00Pressure die casting or injection die casting, i.e. casting in which the metal is forced into a mould under high pressure
    • B22D17/08Cold chamber machines, i.e. with unheated press chamber into which molten metal is ladled
    • B22D17/10Cold chamber machines, i.e. with unheated press chamber into which molten metal is ladled with horizontal press motion
    • BPERFORMING OPERATIONS; TRANSPORTING
    • B22CASTING; POWDER METALLURGY
    • B22DCASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
    • B22D17/00Pressure die casting or injection die casting, i.e. casting in which the metal is forced into a mould under high pressure
    • B22D17/02Hot chamber machines, i.e. with heated press chamber in which metal is melted
    • B22D17/04Plunger machines
    • BPERFORMING OPERATIONS; TRANSPORTING
    • B22CASTING; POWDER METALLURGY
    • B22DCASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
    • B22D17/00Pressure die casting or injection die casting, i.e. casting in which the metal is forced into a mould under high pressure
    • B22D17/08Cold chamber machines, i.e. with unheated press chamber into which molten metal is ladled
    • B22D17/12Cold chamber machines, i.e. with unheated press chamber into which molten metal is ladled with vertical press motion
    • BPERFORMING OPERATIONS; TRANSPORTING
    • B22CASTING; POWDER METALLURGY
    • B22DCASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
    • B22D17/00Pressure die casting or injection die casting, i.e. casting in which the metal is forced into a mould under high pressure
    • B22D17/14Machines with evacuated die cavity
    • BPERFORMING OPERATIONS; TRANSPORTING
    • B22CASTING; POWDER METALLURGY
    • B22DCASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
    • B22D17/00Pressure die casting or injection die casting, i.e. casting in which the metal is forced into a mould under high pressure
    • B22D17/20Accessories: Details
    • B22D17/22Dies; Die plates; Die supports; Cooling equipment for dies; Accessories for loosening and ejecting castings from dies
    • B22D17/2227Die seals
    • BPERFORMING OPERATIONS; TRANSPORTING
    • B22CASTING; POWDER METALLURGY
    • B22DCASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
    • B22D27/00Treating the metal in the mould while it is molten or ductile ; Pressure or vacuum casting
    • B22D27/20Measures not previously mentioned for influencing the grain structure or texture; Selection of compositions therefor
    • BPERFORMING OPERATIONS; TRANSPORTING
    • B22CASTING; POWDER METALLURGY
    • B22DCASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
    • B22D29/00Removing castings from moulds, not restricted to casting processes covered by a single main group; Removing cores; Handling ingots
    • BPERFORMING OPERATIONS; TRANSPORTING
    • B22CASTING; POWDER METALLURGY
    • B22DCASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
    • B22D35/00Equipment for conveying molten metal into beds or moulds
    • B22D35/04Equipment for conveying molten metal into beds or moulds into moulds, e.g. base plates, runners
    • BPERFORMING OPERATIONS; TRANSPORTING
    • B22CASTING; POWDER METALLURGY
    • B22DCASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
    • B22D41/00Casting melt-holding vessels, e.g. ladles, tundishes, cups or the like
    • CCHEMISTRY; METALLURGY
    • C22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22CALLOYS
    • C22C1/00Making non-ferrous alloys
    • C22C1/11Making amorphous alloys
    • CCHEMISTRY; METALLURGY
    • C22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22CALLOYS
    • C22C16/00Alloys based on zirconium
    • CCHEMISTRY; METALLURGY
    • C22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22CALLOYS
    • C22C30/00Alloys containing less than 50% by weight of each constituent
    • CCHEMISTRY; METALLURGY
    • C22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22CALLOYS
    • C22C45/00Amorphous alloys
    • CCHEMISTRY; METALLURGY
    • C22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22CALLOYS
    • C22C45/00Amorphous alloys
    • C22C45/10Amorphous alloys with molybdenum, tungsten, niobium, tantalum, titanium, or zirconium or Hf as the major constituent

Definitions

  • the present disclosure relates to the field of amorphous alloy, more particularly to a die casting device and a die casting process for amorphous alloy.
  • Amorphous alloy materials are also termed as metallic glass. Due to special structure of atoms constituting the alloy, the amorphous alloy may possess excellent physical and chemical properties, such as high yield strength, high hardness, super-elasticity, high erosion resistance and high anti-corrosive performance etc., different from conventional crystalline metal material.
  • the amorphous alloy also possess excellent die casting performance due to the special structure and chemical property. Because amorphous structure has to be formed during molding, heterogeneous nucleation has to be prevented from happening for the amorphous alloy. Because the amorphous alloy normally contains active elements such as zirconium, aluminum, magnesium, titanium, rare earths etc., the active elements may be reactive with nonmetallic gas elements to form the nucleus of heterogeneous nucleation, which may hinder the forming of the amorphous structure or decrease the critical size of the amorphous alloy tremendously.
  • active elements such as zirconium, aluminum, magnesium, titanium, rare earths etc.
  • U.S. Pat. No. 6,021,840 presents a vacuum die casting technology, which may prevent molten amorphous alloy and alloy elements during molding from oxidization by forming vacuum.
  • vacuum technology especially with the formation of high leveled vacuum as proposed, for example, in U.S. Pat. No. 6,021,840, up to lOOOum Hg, costs relating thereto is increased and the die casting period for the amorphous alloy is extended, which may decrease manufacturing efficiency. Meanwhile, the vacuum system has to be maintained with a sealing system which may tremendously impact the continuity and convenience of operators and increase complexity of manufacture.
  • a die casting apparatus for an amorphous alloy may need to be provided, which may have a simplified structure using positive pressure protecting gas without the need to form high degree vacuum, thus reducing manufacturing and maintenance costs.
  • a die casting method for an amorphous alloy may need to be provided, which may have a simplified operating process with lowered cost in addition to increased efficiency and shortened manufacturing period.
  • a die casting apparatus for an amorphous alloy may comprise: a stationary die and a movable die defining a die chamber when mated with each other; a sealed cabin defining a sealing chamber, the sealing chamber having a feeding port; a protecting gas supplying device connected with the sealed cabin for supplying the protecting gas into the sealing chamber so that the protecting gas inside the sealing chamber has a positive pressure; a melting device disposed within the sealed cabin for receiving and melting amorphous alloy fed from the feeding port; a feed sleeve communicated with the die chamber having a molten material inlet, with a plunger positioned therein for injecting the molten amorphous alloy from the melting device into the die chamber via the molten material inlet; a driving device connected with the plunger for driving the plunger in the feed sleeve; and a gas purifying device communicated with the sealed cabin for purifying the gas from the sealed cabin.
  • a method of die casting an amorphous alloy may comprise the steps of: purifying a sealing chamber defined in a sealed cabin; supplying protecting gas into the sealing chamber to maintain the protecting gas in the sealing chamber to a positive pressure; feeding amorphous alloy into a melting device disposed inside the sealing chamber to obtain the molten amorphous alloy while the protecting gas filled within the sealing chamber overflowing outside; feeding the molten amorphous alloy into a die chamber defined by a mated stationary die and a movable die via a feed sleeve with a plunger positioned therein; and opening the mated stationary and movable dies to extract at least a component formed at least partially of the amorphous alloy from inside the die chamber while the protecting gas filled within the sealing chamber overflowing outside.
  • the sealing chamber may be purified first and then filled with protecting gas having positive pressure, so that no external gas may be entered therein during material feeding or component exporting, which may effectively isolate the molten amorphous alloy from contacting with the air.
  • protecting gas having positive pressure may effectively isolate the molten amorphous alloy from contacting with the air.
  • heterogeneous nucleation may be prevented and the critical size of the amorphous alloy may be increased tremendously.
  • vacuum suction may not be needed, which may reduce manufacturing and maintenance costs accordingly.
  • Fig. 1 is a schematic view of a vertical type die casting apparatus for an amorphous alloy according to an embodiment of the present disclosure
  • Fig. 2 is a schematic view of a horizontal type die casting apparatus for an amorphous alloy according to an embodiment of the present disclosure.
  • Fig. 3 is schematic diagram of a method of die casting an amorphous alloy according to a third embodiment of the present disclosure.
  • a structure in which a first feature is "on" a second feature may include an embodiment in which the first feature directly contacts the second feature and may include an embodiment in which an additional feature is prepared between the first feature and the second feature so that the first feature does not directly contact the second feature.
  • a die casting apparatus 100 for an amorphous alloy may be explained in detail with reference to accompanying figures, where Fig. 1 shows a schematic view of a vertical type, and Fig. 2 shows a horizontal type. It should be noted that the die casting apparatus 100 may be used for die casting other active metals with similar properties to the amorphous alloy, such as titanium alloy, or magnesium alloy etc.
  • the die casting apparatus 100 may comprise a stationary die 1, a movable die 2, a sealed cabin 4, a protecting gas supplying device (not shown), a melting device 5, a feed sleeve 6, a driving device 8 and a purifying device 10.
  • the stationary die 1 and the movable die 2 may be closed or opened, and define a die chamber when the stationary die 1 and the movable die 2 may be mated with each other.
  • a sealing chamber 40 may be defined in the sealed cabin 4 and the sealed cabin 4 may have a feeding port 41 to feed the amorphous alloy inside the sealing chamber 40.
  • the protecting gas supplying device may be connected with the sealed cabin 4 to supply the protecting gas to the sealing chamber 40, and the protecting gas inside the sealing chamber 40 may have a positive pressure, which may effectively prevent external harmful gases from entering into the sealing chamber 40.
  • the protecting gas may be at least one of inert gases, such as helium, neon, argon, krypton, xenon, radon or the combination thereof.
  • the melting device 5 may be disposed in the sealed cabin 4 for receiving and melting the amorphous alloy fed from the feeding port 41.
  • the feed sleeve 6 may be communicated with the die chamber 3, and the feed sleeve 6 may be formed with a molten material inlet 60, and a plunger 7 for injecting the molten amorphous alloy into the die chamber 3.
  • the driving device 8 may be connected with the plunger 7 for moving thereof inside the feed sleeve 6, so that the molten amorphous alloy may be injected from the feed sleeve 6 to the die chamber 3 for die casting.
  • the purifying device 10 may be connected with the sealed cabin 4 for purifying the harmful gases inside the sealing chamber
  • the gas inside the sealing chamber 40 may contain harmful gases such as N 2 , 0 2 ,
  • the die casting apparatus 100 may be formed with an output port 13 for outputting or exporting the amorphous alloy after die casting. It should be noted that the output port 13 may be formed on the sealed cabin 4 when the die casting apparatus 100 is a vertical type as shown in Fig. 1, and the output port 13 may be formed on the stationary die 1 and/or the movable die when the die casting apparatus 100 is a horizontal one, as shown in Fig. 2. The details thereof will be described in detail hereinafter.
  • the stationary die 1 and the movable die 2 are mated with each other to form the die chamber 3, and the purifying device 10 may purify the harmful gases in the sealing chamber 40 so that the harmful gases in the sealing chamber 40 may have a concentration lower than a predetermined value.
  • the protecting gas supplying device may supply the protecting gas to the sealing chamber 40 until the protecting gas inside the sealing chamber 40 may have a positive pressure, which may mean that the pressure inside the sealing chamber 40 is higher than environmental pressure.
  • the amorphous alloy may be sent to the melting device 5 from the feeding port 41.
  • the feeding port 41 is closed, and the amorphous alloy is melted in the melting device 5 to be sent to the feed sleeve 6 via the molten material inlet 60, and the driving device 8 may drive the plunger 7 to inject the molten amorphous alloy into the die chamber 3, and the molten amorphous alloy may be shaped inside the die chamber 3.
  • the stationary die 1 and the movable die 2 may be opened, and the amorphous alloy after die casting may be extracted from the output port 13.
  • the protecting gas supplying device may supply the protecting gas to the sealing chamber 40 and the protecting gas may maintain the positive pressure so that the amorphous alloy may be effectively prevented from contacting with the environmental air when the amorphous alloy is fed to the melting device 5 via the feeding port 41 or when the amorphous alloy after die casting is extracted via the output port
  • the sealing chamber 40 may not need to be performed with vacuum suction repeatedly, thus shortening manufacturing period, achieving continuous production and enhancing manufacturing efficiency.
  • the die casting apparatus 100 has a simplified structure. By using the protecting gas with positive pressure, high-level vacuum suction may not be needed, thus further reducing manufacturing and maintenance costs accordingly.
  • the purifying device 10 may be a vacuum suction device 101, a gas purifier 102 or the combination thereof.
  • the purifying device 10 may be the combination of the vacuum suction device 101 and the gas purifier 102.
  • the sealing chamber 40 may be vacuum suctioned and the protecting gas may be filled in the sealing chamber 40 by the protecting gas supplying device, and the residual harmful gases in the sealing chamber 40 are repeatedly processed by the gas purifier 102 to control the harmful gases to a concentration satisfying process requirement, thus greatly decreasing the demands of the protecting gas, reducing costs while increasing lifespan of the purifying device 10.
  • the purifying device 10 may be the vacuum suction device 101. At this time, the sealed chamber 40 may be performed with vacuum suction and then filled with protecting gas, so that the concentration of the harmful gases in the sealing chamber 40 may be maintained to minimum. And in one embodiment, the purifying device 10 may be the gas purifier 102 only, and the protecting gas may be filled in the sealing chamber 40 after the harmful gases in the sealing chamber 40 are purified by the gas purifier 102 to reduce the concentration of the harmful gases in the sealing chamber 40.
  • the die casting apparatus 100 may be configured as a horizontal one where the stationary die 1 and the movable die 2 are disposed outside the sealing cabin 4.
  • the stationary die 1 and the movable die 2 may be disposed at the left side of the sealed cabin 4 and deployed in a direction for the left to right.
  • the feed sleeve 6 may be disposed at the right side of the stationary die 1.
  • the right end of the feed sleeve 6 may be disposed inside the sealing chamber 40, and the left end thereof may be projected out of the sealing chamber 40 to be communicated with the die chamber 3.
  • the plunger 7 may be reciprocally moved in the feed sleeve 6 to inject the molten amorphous alloy into the die chamber 3.
  • the output port 13 may be disposed on the movable die 2 facing the left end of the feed sleeve 6.
  • the die casting apparatus 100 may be configured into a vertical one with the stationary die 1 and the movable die 2 being disposed inside the sealed cabin 4.
  • the stationary die 1 and the movable die 2 may be vertically provided in the sealing chamber 4 in a direction from bottom to upward.
  • the feed sleeve 6 may be provided at the lower side of the stationary die 1 and communicated with the die chamber 3.
  • the feed sleeve 7 may be moved in the vertical direction in the feed sleeve 6 to inject the molten amorphous alloy into the die chamber 3.
  • the output port 13 may be disposed at the upper right portion of the sealing chamber 40. However, the present disclosure is not limited hereto.
  • the output port 13 may be disposed at a top left portion or top portion of the sealing chamber 40. At this time, the gravity of the protecting gas may effectively prevent the environmental air from entering into the sealing chamber 40.
  • a vacuum sealing member 11 may be disposed between the stationary die 1 and the movable die 2 to further increase the sealing performance of the die chamber 3.
  • the feed sleeve 6 may be communicated with the die chamber 3 via a communicating passage (not shown) formed in the stationary die 1. Therefore, the simplified structure may avoid the molten amorphous alloy from being exposed when transporting from the feed sleeve 6 to the die chamber 3.
  • the protecting gas in the sealing chamber 40 may have a pressure between 1 atmospheric pressure (atm) and 1.1 atmospheric pressure, so that the amorphous alloy may be effectively prevented from contacting with the air when the amorphous alloy is fed to the melting device 5 via the feeding port 41 or when the amorphous alloy after die casting is extracted from the output port 13.
  • the protecting gas may have a density not less than that of the environmental air, so that the environmental gas may not be introduced into the sealing chamber 40 due to gravity when the amorphous alloy is fed to the melting device 5 via the feeding port 41 or when the amorphous alloy after die casting is extracted from the output port 13, and the protecting gas may not overflow outside easily, thus effectively preventing the protecting gas from being polluted by the environmental air.
  • the melting device 5 may comprise a crucible 50 and a heating device 51 for heating the crucible 50.
  • the heating device 51 may be an induction heating device, an electric arc heating device or a resistor heating device.
  • the die casting apparatus 100 may further comprise a die chamber vacuum suction device 12 communicated with the die chamber 3 for performing vacuum suction to the die chamber 3, which may further decrease the concentration of the harmful gases and enhance discharging efficiency during die casting.
  • a die chamber vacuum suction device 12 communicated with the die chamber 3 for performing vacuum suction to the die chamber 3, which may further decrease the concentration of the harmful gases and enhance discharging efficiency during die casting.
  • the contact of the molten amorphous alloy with the air may be isolated, avoiding the nucleus of heterogeneous nucleation formed by the reaction of the molten amorphous alloy with the harmful gases which may hardly form the amorphous alloy or greatly reduce the critical size of the amorphous alloy.
  • the porosity of the die casted component of amorphous alloy may be decreased, which may enhance the die casting quality.
  • the method may be implemented by the die casting apparatus shown in Fig. 1 as well as the die casting apparatus shown in Fig. 2.
  • the method may comprise the following steps. Firstly, the sealing chamber 40 in the sealed cabin 4 of the die casting apparatus 100 may be purified, so that the harmful gases in the sealing chamber 40 may have a concentration less than a predetermined value (step SI 00). Then, the protecting gas may be supplied into the sealing chamber 40 to maintain the protecting gas in the sealing chamber 40 to a positive pressure (step S200).
  • the amorphous alloy may be fed into the melting device 5 disposed inside the sealing chamber 40 via the feeding port 41 formed on the sealing chamber 40 to obtain the molten amorphous alloy while the protecting gas filled within the sealing chamber 40 at least partially overflowing outside, so that the environmental air may not enter into the sealing chamber 40 (step S300).
  • the molten amorphous alloy may be fed into the die chamber 3 defined by the mated stationary die 1 and the movable die 2 via the feed sleeve 6 with the plunger 7 positioned therein (step S400).
  • the plunger 7 may inject the molten amorphous alloy into the die chamber 3.
  • the mated stationary and movable dies 1 and 2 may be opened to extract at least a component (not shown) formed at least partially of the amorphous alloy from inside the die chamber 3 while the protecting gas filled within the sealing chamber 40 overflowing outside via the output port 13 (step S500).
  • the die casting process may be continuous, for example, the amorphous alloy may be fed into the melting device 5 while the molten amorphous alloy may be injected into the die chamber 3.
  • the harmful gases may have a concentration less than a predetermined value, and a part of the protecting gas may overflow outside when the amorphous alloy is fed to the melting device 5 via the feeding port 41 or when the amorphous alloy after die casting is extracted via the output port 13, so that the environmental air may not enter into the sealing chamber 40, thus nucleus of heterogeneous nucleation formed by the reaction between the molten amorphous alloy and the harmful gases may be prevented, and the critical size of the amorphous alloy may be greatly increased.
  • the sealing chamber 40 may not need to be performed with vacuum suction repeatedly, since the protecting gas in the sealing chamber 40 may maintain the positive pressure, thus shortening manufacturing period, achieving continuous production and enhancing die casting efficiency.
  • the feeding port may be opened or closed at any time, thus further enhancing manufacturing efficiency and lowering costs accordingly.
  • the purifying device 10 may be a vacuum suction device 101, a gas purifier 102 or the combination thereof.
  • the sealing chamber 40 may be vacuum suctioned so that the harmful gases in the sealing chamber 40 may have a concentration lower than a predetermined value, then the protecting gas is filled in the sealing chamber 40, and the residual harmful gases in the sealing chamber 40 are repeatedly processed by the gas purifier 102, to control the harmful gases to a concentration satisfying process requirement, thus greatly decreasing the demands of the protecting gas.
  • the protecting gas in the sealing chamber 40 may have a positive pressure between 1 atmospheric pressure (atm) and 1.1 atmospheric pressure, so that the amorphous alloy may be effectively prevented from contacting with the environmental air when the amorphous alloy is fed to the melting device 5 via the feeding port 41 or when the amorphous alloy after die casting is extracted from the output port 13.
  • the protecting gas in the sealing chamber 40 may have the positive pressure, the sealing chamber 40 may not need to be repeatedly vacuum suctioned, thus saving time.
  • the melting step may be synchronized with other steps, thus saving the waiting time for the melting of the amorphous alloy. In the embodiments shown in Figs. 1 and 2, the manufacturing period has been shortened to about 20 seconds.
  • the manufacturing period is about 120 seconds since the sealing chamber has to be performed with vacuum suction and the melting steps cannot be synchronized with other steps.
  • the method according to an embodiment of the present disclosure may have shortened the die casting period, thus enhancing production efficiency and decreasing manufacturing costs.
  • the protecting gas may be at least one of the inert gases, thus avoiding the reaction of the molten amorphous alloy with the harmful gases.
  • the protecting gas may have a density not less than that of the air, so that environmental gas may not be introduced into the sealing chamber 40 due to gravity when the amorphous alloy is fed to the melting device 5 via the feeding port 41 or when the amorphous alloy after die casting is extracted from the output port 13, and the protecting gas may not overflow outside easily, thus effectively preventing the protecting gas from being polluted by the environmental air.
  • the amorphous alloy may be Zr a AlbCu c Md, where M is at least one selected from a group consisting of Nb, Sc, Ta, Ni, Co, Y, Ag, Fe, Sn, Hf, Ti, Be and rare earths, and a, b, and c are atomic percentage, and 30 ⁇ a ⁇ 70, 5 ⁇ b ⁇ 35, 5 ⁇ c ⁇ 40, and 5 ⁇ d ⁇ 30.
  • impurity elements contained in the amorphous alloy which are less than 5% in atomic percentage.
  • the impurities may be Si, P, Be, Mg, B, O etc.
  • the amorphous alloy may possess properties which are resistant to the harmful gases so that cast may be obtained with high quality.
  • the gas in the sealing chamber 40 may contain the harmful gases, for example, at least one of N 2 , 0 2 , H 2 0 and C0 2 , that may have a concentration less than 10000 ppm. In one embodiment, the harmful gases may have a concentration less than lOOOppm.
  • the method may further comprise a step of performing vacuum suction to the die chamber 3 before the molten amorphous alloy may be injected into the die chamber
  • the contact of the molten amorphous alloy with the air may be isolated, avoiding the nucleus of heterogeneous nucleation formed by the reaction of the molten amorphous alloy with the harmful gases which may hardly form the amorphous alloy or greatly reduce the critical size of the amorphous alloy.
  • the porosity of the die casted component of amorphous alloy may be decreased, which may enhance the die casting quality.
  • the output port 13 and the feeding port 41 may be alternately opened, so that the environmental air may not enter into the sealing chamber 40 caused by convection of the protecting gas in the sealing chamber 40 with the environmental air.
  • the stationery die 1 and the movable die 2 may be mated with each other to form the die chamber 3.
  • the sealing chamber 40 of the sealed cabin 4 may be performed with vacuum suction so that the harmful gases in the sealing chamber 40 may have a concentration less than a predetermined value.
  • the protecting gas supplying device supplies the protecting gas into the sealing chamber 40 so that the protecting gas may have a positive pressure between 1 atm and 1.1 atm, and the gas purifier 102 may repeatedly process the residual harmful gases in the sealing chamber 40.
  • the feeding port 41 is opened to send the amorphous alloy into the melting device 5. And this time, because the protecting gas has a pressure larger than the atmospheric pressure, a part of the protecting gas overflows outside the sealing chamber 40 through the feeding port 41, to avoid the environmental air from entering into the sealing chamber 40.
  • the amorphous alloy is heated in the crucible 50 to melt the amorphous alloy by the heating device 51. And the molten amorphous alloy is sent to the feed sleeve 6 from the molten material inlet 60.
  • the die chamber 3 may be performed with vacuum suction by the die chamber vacuum suction device 12. And the plunger 7 injects the molten amorphous alloy in the feed sleeve 6 under the driving of the driving device 8, so that the amorphous alloy may be die casted in the die chamber 3 after vacuum suction.
  • the feeding port 41 may be opened for feeding the amorphous alloy at any steps, then the amorphous alloy is melted in the crucible 50 by the heating device 51, so that the molten amorphous alloy may be injected into the feed sleeve 6 via the molten material inlet 60 at any time.
  • the feeding port 41 and the output port 13 may be alternately opened, which may effectively prevent environmental air from entering into the sealing chamber 40 by the convection of the protecting gas in the sealing chamber 40 with the environmental air.

Landscapes

  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Chemical & Material Sciences (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Furnace Details (AREA)
  • Crystals, And After-Treatments Of Crystals (AREA)
  • Molds, Cores, And Manufacturing Methods Thereof (AREA)
PCT/CN2012/086494 2011-12-15 2012-12-13 Die casting device and method for amorphous alloy WO2013086990A1 (en)

Priority Applications (3)

Application Number Priority Date Filing Date Title
US14/365,826 US20140352907A1 (en) 2011-12-15 2012-12-13 Die casting device and method for amorphous alloy
EP12858511.4A EP2790853A4 (en) 2011-12-15 2012-12-13 SHELL MOLDING DEVICE AND METHOD FOR AMORPHOUS ALLOY
US14/971,761 US20160121392A1 (en) 2011-12-15 2015-12-16 Die casting device and method for amorphous alloy

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN201110421420.3 2011-12-15
CN201110421420.3A CN102527982B (zh) 2011-12-15 2011-12-15 非晶合金压铸设备及非晶合金压铸工艺

Related Child Applications (2)

Application Number Title Priority Date Filing Date
US14/365,826 A-371-Of-International US20140352907A1 (en) 2011-12-15 2012-12-13 Die casting device and method for amorphous alloy
US14/971,761 Division US20160121392A1 (en) 2011-12-15 2015-12-16 Die casting device and method for amorphous alloy

Publications (1)

Publication Number Publication Date
WO2013086990A1 true WO2013086990A1 (en) 2013-06-20

Family

ID=46336700

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2012/086494 WO2013086990A1 (en) 2011-12-15 2012-12-13 Die casting device and method for amorphous alloy

Country Status (4)

Country Link
US (2) US20140352907A1 (zh)
EP (1) EP2790853A4 (zh)
CN (1) CN102527982B (zh)
WO (1) WO2013086990A1 (zh)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2015058611A1 (en) 2013-10-23 2015-04-30 Byd Company Limited Metal forming apparatus
US20150174652A1 (en) * 2013-12-25 2015-06-25 Hong Fu Jin Precision Industry (Shenzhen) Co., Ltd Pressure casting machine
EP3075466A4 (en) * 2013-11-30 2016-11-30 Inst Metal Res Chinese Acad Sc DEVICE AND METHOD FOR CASTING FORMING AMORPHOUS ALLOY ELEMENTS
US10563289B2 (en) 2017-06-29 2020-02-18 Companhia Brasileira De Metalurgia E Mineracão Process for refining niobium-based ferroalloys
EP3542924A4 (en) * 2016-11-18 2020-06-10 Dongguan Eontec Co., Ltd. CONTINUOUS PRECISION MOLDING DEVICE AND METHOD FOR AMORPHOUS ALLOY OR COMPOSITE THEREOF

Families Citing this family (31)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102534437A (zh) 2011-12-15 2012-07-04 比亚迪股份有限公司 一种非晶合金及其制备方法
CN102527982B (zh) * 2011-12-15 2015-05-13 比亚迪股份有限公司 非晶合金压铸设备及非晶合金压铸工艺
US10197335B2 (en) 2012-10-15 2019-02-05 Apple Inc. Inline melt control via RF power
JP5993898B2 (ja) * 2013-07-11 2016-09-14 クルーシブル インテレクチュアル プロパティ エルエルシーCrucible Intellectual Property Llc 溶融合金閉じ込めのための不均等な間隔の誘導コイル
CN104550825B (zh) * 2013-10-23 2017-02-15 比亚迪股份有限公司 金属成型设备
CN203578719U (zh) * 2013-11-30 2014-05-07 中国科学院金属研究所 非晶合金构件铸造成型设备
CN104668503B (zh) * 2013-11-30 2017-05-31 中国科学院金属研究所 一种非晶合金构件铸造成型设备和工艺
CN104190896B (zh) * 2014-09-26 2016-07-06 东莞帕姆蒂昊宇液态金属有限公司 非晶合金的电弧熔融压铸方法
US9873151B2 (en) 2014-09-26 2018-01-23 Crucible Intellectual Property, Llc Horizontal skull melt shot sleeve
CN104690245A (zh) * 2015-03-18 2015-06-10 东莞台一盈拓科技股份有限公司 非晶合金用卧式压铸机
CN106312021B (zh) * 2015-06-17 2018-02-06 和昌精密股份有限公司 铸锻成型方法及其装置
CN105689684B (zh) * 2016-03-11 2018-02-06 无锡建凌电器有限公司 一种五金零件铸造工作台
CN107398535A (zh) * 2016-05-20 2017-11-28 核工业西南物理研究院 一种新型镁合金甩带炉
CN106424637B (zh) * 2016-11-15 2019-03-05 中国科学院金属研究所 一种块状非晶态合金高真空压铸成形设备和工艺
CN106555139B (zh) * 2017-02-14 2018-03-13 深圳市锆安材料科技有限公司 一种非晶合金快速成型装置及成型方法
CN108453203B (zh) * 2017-02-20 2020-06-19 比亚迪股份有限公司 非晶合金压铸件模锻装置和非晶合金零件及其成型设备与成型方法
CN107236913B (zh) * 2017-05-18 2019-04-26 中国科学院金属研究所 一种锆基非晶合金及其制备方法
CN107414050A (zh) * 2017-07-10 2017-12-01 许昌锦荣食品有限公司 一种块状非晶态合金高真空压铸成形设备
CN107803478A (zh) * 2017-11-30 2018-03-16 佛山市高明建强科技有限公司 一种卧式压铸机
CN108177352A (zh) * 2017-12-22 2018-06-19 贵州贵航汽车零部件股份有限公司 密封垫压合装置
DE102018115815A1 (de) * 2018-06-29 2020-01-02 Universität des Saarlandes Vorrichtung und Verfahren zur Herstellung eines aus einem amorphen oder teilamorphen Metall gebildeten Gussteils sowie Gussteil
CN110923481A (zh) * 2018-09-20 2020-03-27 天津大学 非晶薄膜/高熵合金复合材料及其制备方法
CN111112572B (zh) * 2018-10-31 2022-06-14 惠州比亚迪实业有限公司 非晶合金压铸成型的模具、装置、方法和非晶合金压铸件
CN109332635A (zh) * 2018-12-07 2019-02-15 蚌埠隆华压铸机有限公司 一种卧式冷室压铸机
CN110227810A (zh) * 2019-07-26 2019-09-13 上海驰声新材料有限公司 全真空压铸机的产品送出装置及产品送出方法
CN112974759B (zh) * 2021-02-05 2021-11-30 株洲宜安新材料研发有限公司 一种武器专用高强度非晶合金压铸工艺
CN113477897A (zh) * 2021-05-18 2021-10-08 施俊峰 一种铝合金压铸件设备
CN113275535B (zh) * 2021-05-25 2022-03-29 江南大学 一种提高金属基复合材料性能的成型压铸工艺
CN113500177A (zh) * 2021-06-30 2021-10-15 施俊峰 一种自动收料的金属零部件加工设备
US20230070081A1 (en) * 2021-08-17 2023-03-09 City University Of Hong Kong Metallic glass
CN116786784B (zh) * 2023-06-13 2024-02-06 安徽辉隆集团辉铝新材料科技有限公司 一种高强度轻量化新能源汽车骨架铝型材成型装置

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6021840A (en) * 1998-01-23 2000-02-08 Howmet Research Corporation Vacuum die casting of amorphous alloys
JP2004155050A (ja) * 2002-11-06 2004-06-03 Seiko Epson Corp 射出成型機の材料供給装置ならびにその制御方法
CN201023131Y (zh) * 2007-04-04 2008-02-20 比亚迪股份有限公司 一种压铸大块非晶合金的装置
CN101293277A (zh) * 2008-06-13 2008-10-29 清华大学 一种非晶镁合金差压压射成型方法及其设备
CN201308981Y (zh) * 2008-11-27 2009-09-16 比亚迪股份有限公司 一种非晶合金压铸给料设备及非晶合金压铸机
CN101596585A (zh) * 2008-06-04 2009-12-09 詹姆斯·康 用于非晶合金的立式压铸机
CN102527982A (zh) * 2011-12-15 2012-07-04 比亚迪股份有限公司 非晶合金压铸设备及非晶合金压铸工艺

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5860468A (en) * 1993-07-28 1999-01-19 Cook; Arnold J. Vacuum die casting
JP3808167B2 (ja) * 1997-05-01 2006-08-09 Ykk株式会社 金型で加圧鋳造成形された非晶質合金成形品の製造方法及び装置
US6070643A (en) * 1997-09-12 2000-06-06 Howmet Research Corporation High vacuum die casting
CN1207421C (zh) * 2002-12-17 2005-06-22 哈尔滨工业大学 大过冷液相区与高热稳定性的多组元大块非晶合金材料
JP4339135B2 (ja) * 2004-01-15 2009-10-07 Ykk株式会社 非晶質合金成形用の射出鋳造装置
CN100473472C (zh) * 2004-05-28 2009-04-01 日本碍子株式会社 金属玻璃的成形方法
JP4688146B2 (ja) * 2005-06-09 2011-05-25 日本碍子株式会社 ダイキャスト装置
JP4688145B2 (ja) * 2005-06-09 2011-05-25 日本碍子株式会社 ダイキャスト装置及びダイキャスト方法
US20120111525A1 (en) * 2010-11-05 2012-05-10 Bochiechio Mario P High temperature die casting apparatus and method therefor

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6021840A (en) * 1998-01-23 2000-02-08 Howmet Research Corporation Vacuum die casting of amorphous alloys
JP2004155050A (ja) * 2002-11-06 2004-06-03 Seiko Epson Corp 射出成型機の材料供給装置ならびにその制御方法
CN201023131Y (zh) * 2007-04-04 2008-02-20 比亚迪股份有限公司 一种压铸大块非晶合金的装置
CN101596585A (zh) * 2008-06-04 2009-12-09 詹姆斯·康 用于非晶合金的立式压铸机
CN101293277A (zh) * 2008-06-13 2008-10-29 清华大学 一种非晶镁合金差压压射成型方法及其设备
CN201308981Y (zh) * 2008-11-27 2009-09-16 比亚迪股份有限公司 一种非晶合金压铸给料设备及非晶合金压铸机
CN102527982A (zh) * 2011-12-15 2012-07-04 比亚迪股份有限公司 非晶合金压铸设备及非晶合金压铸工艺

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
See also references of EP2790853A4 *

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2015058611A1 (en) 2013-10-23 2015-04-30 Byd Company Limited Metal forming apparatus
EP3041621A4 (en) * 2013-10-23 2017-01-18 BYD Company Limited Metal forming apparatus
KR101852697B1 (ko) * 2013-10-23 2018-04-26 비와이디 컴퍼니 리미티드 금속 성형 장치
EP3075466A4 (en) * 2013-11-30 2016-11-30 Inst Metal Res Chinese Acad Sc DEVICE AND METHOD FOR CASTING FORMING AMORPHOUS ALLOY ELEMENTS
US20150174652A1 (en) * 2013-12-25 2015-06-25 Hong Fu Jin Precision Industry (Shenzhen) Co., Ltd Pressure casting machine
JP2015123504A (ja) * 2013-12-25 2015-07-06 鴻富錦精密工業(深▲セン▼)有限公司 ダイカスト装置
US9643243B2 (en) * 2013-12-25 2017-05-09 Ji Zhun Precision Industry (Hui Zhou) Co., Ltd. Pressure casting machine
EP3542924A4 (en) * 2016-11-18 2020-06-10 Dongguan Eontec Co., Ltd. CONTINUOUS PRECISION MOLDING DEVICE AND METHOD FOR AMORPHOUS ALLOY OR COMPOSITE THEREOF
US10563289B2 (en) 2017-06-29 2020-02-18 Companhia Brasileira De Metalurgia E Mineracão Process for refining niobium-based ferroalloys

Also Published As

Publication number Publication date
US20160121392A1 (en) 2016-05-05
US20140352907A1 (en) 2014-12-04
EP2790853A1 (en) 2014-10-22
CN102527982B (zh) 2015-05-13
CN102527982A (zh) 2012-07-04
EP2790853A4 (en) 2015-08-05

Similar Documents

Publication Publication Date Title
US20160121392A1 (en) Die casting device and method for amorphous alloy
AU2004242667B2 (en) Die casting machine and casting method by thereof machine
US9771634B2 (en) Processes for producing low nitrogen essentially nitride-free chromium and chromium plus niobium-containing nickel-based alloys and the resulting chromium and nickel-based alloys
CN101596585A (zh) 用于非晶合金的立式压铸机
CN1569362A (zh) 镁合金真空压力铸造机
CN110958921A (zh) 用于反重力模具填充的方法和装置
CN100346910C (zh) 真空熔铸装置
JP4414861B2 (ja) 活性高融点金属含有合金の長尺鋳塊製造法
KR20090126171A (ko) 경금속의 진공용해장치 및 이를 이용한 진공용해방법
KR101220439B1 (ko) 알루미늄-아연 합금 잉곳의 연속 주조방법
EP1042088A1 (en) Melting and pouring of specialty metals
CN212371158U (zh) 一种变形镁合金铸锭坯的铸造装置
JP4263366B2 (ja) 希土類磁石スクラップの溶解方法及び溶解装置
KR102079468B1 (ko) 비정질 합금의 정련방법 및 진공 액상 성형 장치
CN114369737A (zh) 一种向高温合金熔体中添加微量o、n、s、c的方法
CN204035524U (zh) 一种制备高纯铜及铜合金铸锭的装置
CN105087954A (zh) 一种合金钢电渣炉直接使用无帽口电极坯制造方法
JPS6352983B2 (zh)
CN111957924A (zh) 一种变形镁合金铸锭坯的铸造装置和低压反重力铸造方法
CN104785746A (zh) 注粉吹氩压力铸造工艺
CN103949617A (zh) 一种制备高纯铜及铜合金铸锭的装置及方法
CN219254101U (zh) 铸造设备及悬浮熔炼设备
CN112210673B (zh) 一种电子束表面热解去除高温合金中夹杂物的方法
CN116287826B (zh) 一种铝钨合金的生产方法
JP5328998B1 (ja) 金属ガラスの鋳造装置及びそれを用いた鋳造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 12858511

Country of ref document: EP

Kind code of ref document: A1

REEP Request for entry into the european phase

Ref document number: 2012858511

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 2012858511

Country of ref document: EP

NENP Non-entry into the national phase

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 14365826

Country of ref document: US