WO2012127908A1 - 巻線型コイル部品の製造方法 - Google Patents

巻線型コイル部品の製造方法 Download PDF

Info

Publication number
WO2012127908A1
WO2012127908A1 PCT/JP2012/052391 JP2012052391W WO2012127908A1 WO 2012127908 A1 WO2012127908 A1 WO 2012127908A1 JP 2012052391 W JP2012052391 W JP 2012052391W WO 2012127908 A1 WO2012127908 A1 WO 2012127908A1
Authority
WO
WIPO (PCT)
Prior art keywords
magnetic material
core
magnetic
resin sheet
winding
Prior art date
Application number
PCT/JP2012/052391
Other languages
English (en)
French (fr)
Inventor
前田英一
Original Assignee
株式会社村田製作所
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社村田製作所 filed Critical 株式会社村田製作所
Publication of WO2012127908A1 publication Critical patent/WO2012127908A1/ja

Abstract

　巻芯部と、巻芯部の両端に連接された磁性体からなる一対の鍔部とを備えたコア部材の巻芯部に巻線を巻回してなる巻線型コイル部品を、小型、低背化した場合にも、コア部材の変形や損傷を招くことなく、効率よく製造することが可能な巻線型コイル部品の製造方法を提供する。 磁性体材料充填樹脂シート１１ａと磁性体シート１４とを積層する工程を経て、磁性体材料充填樹脂シートの貫通孔１２に充填された、焼成後に巻芯部となる磁性体材料１３が、焼成後に鍔部となる磁性体シート１４に挟まれた構造を有する未焼成のコア部材を複数含む積層体を形成し、この積層体を所定の位置でカットして、個々の未焼成コア部材に分割した後、未焼成コア部材を焼成することによりコア部材を形成し、このコア部材に巻線を巻回する。　磁性体材料充填樹脂シートと、非磁性体材料充填樹脂シートと、磁性体シートとを積層して積層体を形成する。

Description

巻線型コイル部品の製造方法
　本発明は、コイル部品の製造方法に関し、詳しくは、巻芯部と、巻芯部の両端に連接された一対の鍔部とを備えたコア部材に巻線を巻回した構造を有する巻線型コイル部品の製造方法に関する。
　巻線型コイル部品の一つに、例えば、図１(ａ)，(ｂ)に示すような巻線型コイル部品がある。なお、図１(ａ)は、巻線型コイル部品の断面図、(ｂ)は底面図である。
　この巻線型コイル部品１０は巻芯部１と、該巻芯部１の両端に連接された一対の鍔部２ａ、２ｂとを有する、フェライト磁器からなるコア部材３を備えている。そして、巻線４は、巻芯部１に巻回され、さらに該巻線４はエポキシ樹脂等の熱硬化樹脂を主成分とする保護部材５により外装されている。
　また、コア部材３の一方の主面に実装用電極６ａ、６ｂが形成されており、巻線４の両端が実装用電極６ａ、６ｂに引き出され、はんだ等で接合されている。
　そして、このような巻線型コイル部品１０を構成するコア部材３は、一般的に、成型あるいは切削加工の方法で作製されている。
　成型による方法は、例えば、成型後にコア部材の形状をなすよう予め巻芯部、鍔部を構成できるように構成された金型に、フェライトスプレー粉末を充填し、プレス成型してコア部材を作製する方法である。
　また、切削加工による方法は、例えば、コア部材となるべき素体から、切削用砥石を用いて切削加工してコア部材を作製する方法である。
　しかし、近年の電気機器、電子機器の小型化に伴い、巻線型コイル部品についても小型、低背化が求められており、コア部材も、高さが低く、また鍔部の厚みの薄いものが要求されるに至っているのが実情である。
　しかしながら、成型による方法の場合には、コア部材が小型化すると金型へのフェライト粉末の充填が困難になり、均一な成型体を得ることが難しいという問題点がある。
　また、切削加工による方法の場合にも、鍔部の厚みが薄くなると強度が問題になり、また、一対の鍔の間隔が狭い（巻芯部の高さが低い）ものは切削加工を行うことが困難になるという問題がある。
　すなわち、従来の成型や、切削加工による方法では、積層コイル部品の小型、低背化に十分に対応することができないという問題点がある。
　そこで、このような問題点を解消することが可能な技術として、特許文献１に記載されているような積層コイル部品の製造方法が提案されている。
　すなわち、特許文献１には、例えば、その請求項１４や明細書の段落００２７に、巻芯部と、該巻芯部の両端に連接された一対の鍔部とを有するコア部材（ドラムコア）を作製する方法として、焼結した後に軟磁性フェライトとなるグリーンシートの面上に、焼結した後に軟磁性フェライトとなるペースト、および、焼結した後に常磁性フェライトとなるペーストをスクリーン印刷した印刷パターンの積層体を巻芯部とし、さらに焼結した後に軟磁性フェライトとなるグリーンシートを積層して、上記巻芯部の周囲に溝部を有するシート積層体を形成した後、シート積層体を切断して個々の素片（未焼成コア部材）に分割し、この素片を焼結してフェライトドラムコアを作製する方法が開示されている。
　しかしながら、特許文献１に開示された方法では、グリーンシートの面上にスクリーン印刷で、焼結した後に巻芯部となるパターンを形成し、さらにグリーンシートを積層して熱圧着を行い、これを外周刃切断もしくは打ち抜き加工によって素片（未焼成コア部材）に分離するようにしているため、グリーンシートや印刷パターンを積層することにより形成される積層体は、巻芯部となる領域の周囲に溝部（一対の鍔部に挟まれた、巻線が保持される空間領域となる領域）を備えているため、圧着や、切断もしくは打ち抜き加工を行う際に変形や欠けなどの欠陥が発生しやすいという問題点がある。
特開２０１０－１４１１９１号公報
　本発明は、上記課題を解決するものであり、コア部材の巻芯部に巻線を巻回してなる巻線型コイル部品を、小型化したり、低背化したりする場合にも、コア部材の変形や損傷を招くことなく、効率よく製造することが可能な巻線型コイル部品の製造方法を提供することを目的とする。
　上記課題を解決するために、本発明の巻線型コイル部品の製造方法は、
　巻線が巻回される磁性体からなる巻芯部と、前記巻芯部の両端に連接された磁性体からなる一対の鍔部とを備えたコア部材を具備する巻線型コイル部品の製造方法であって、
　焼成工程で燃焼して消失する樹脂を主体とする樹脂シートの複数の位置に貫通孔を形成するとともに、形成した前記貫通孔に磁性体材料を充填して、磁性体材料充填樹脂シートを形成する工程と、
　前記磁性体材料充填樹脂シートと、磁性体材料を主体とする磁性体シートとを積層して、前記磁性体材料充填樹脂シートの前記貫通孔に充填された、焼成後に巻芯部となる磁性体材料が、焼成後に鍔部となる前記磁性体シートに挟まれた構造を有する未焼成のコア部材を複数含む積層体を形成する工程と、
　前記積層体を所定の位置でカットして、個々の未焼成コア部材に分割する工程と、
　前記未焼成コア部材を焼成してコア部材を得る工程と、
　前記コア部材に巻線を巻回する工程と
　を具備することを特徴としている。
　また、本発明の他の巻線型コイル部品の製造方法は、
　巻線が巻回される巻芯部であって、軸芯方向についてみた場合に、所定の領域が非磁性体からなり、その他の領域が磁性体からなる巻芯部と、前記巻芯部の両端に連接された磁性体からなる一対の鍔部とを備えたコア部材を具備する巻線型コイル部品の製造方法であって、
　焼成工程で燃焼して消失する樹脂を主体とする樹脂シートの複数の位置に貫通孔を形成するとともに、形成した前記貫通孔に磁性体材料を充填して、磁性体材料充填樹脂シートを形成する工程と、
　焼成工程で燃焼して消失する樹脂を主体とする樹脂シートの複数の位置に貫通孔を形成するとともに、形成した前記貫通孔に非磁性体材料を充填して、非磁性体材料充填樹脂シートを形成する工程と、
　前記磁性体材料充填樹脂シートと、前記非磁性体材料充填樹脂シートと、磁性体材料を主体とする磁性体シートとを積層して、前記磁性体材料充填樹脂シートの前記貫通孔に充填された、焼成後に巻芯部となる磁性体材料層と、前記非磁性体材料充填樹脂シートの前記貫通孔に充填された、焼成後に巻芯部となる非磁性体材料層とが柱状積層体を形成し、かつ、前記柱状積層体が、焼成後に鍔部となる前記磁性体シートに挟まれた構造を有する、未焼成のコア部材を複数含む積層体を形成する工程と、
　前記積層体を所定の位置でカットして、個々の未焼成コア部材に分割する工程と、
　前記未焼成コア部材を焼成してコア部材を得る工程と、
　前記コア部材に巻線を巻回する工程と
　を具備することを特徴としている。
　また、本発明の巻線型コイル部品の製造方法においては、前記樹脂シートが、前記コア部材を構成する磁性体材料の焼結温度よりも焼結温度の高いセラミック材料を含有していることが好ましい。
　また、前記樹脂シートに形成される前記貫通孔の平面形状が楕円形であることが好ましい。
　また、前記磁性体シートとして、前記コア部材の前記鍔部に、前記巻芯部に巻回された前記巻線を前記鍔部の外側に導く際に巻線を通過させる切り欠き部を形成するための切り込みを施した磁性体シートを用いることが好ましい。
　本発明（請求項１）の巻線型コイル部品の製造方法は、樹脂シートの複数の位置に貫通孔を形成するとともに、形成した貫通孔に磁性体材料を充填して、磁性体材料充填樹脂シートを形成し、この磁性体材料充填樹脂シートと、磁性体シートとを積層する工程を経て、焼成後に巻芯部となる磁性体材料が、焼成後に鍔部となる磁性体シートに挟まれた構造を有する未焼成のコア部材を複数含む積層体を形成し、この積層体を所定の位置でカットして、個々の未焼成コア部材に分割した後、未焼成コア部材を焼成することによりコア部材を形成し、このコア部材に巻線を巻回するようにしているので、小型、低背の巻線型コイル部品を効率よく製造することができる。
　すなわち、本発明においては、焼成後に得られるコア部材の一対の鍔部に挟まれた領域（巻芯部に巻線を巻回したときに、巻線が保持される領域）に、樹脂シートに存在する状態で積層体の圧着、圧着後の積層体のカットが行われるとともに、カットされた未焼成コア部材が、巻芯部の周囲の領域に、樹脂シートに存在する状態で焼成工程に供されることになるため、コア部材の鍔部の厚みが薄く、上下の鍔部の間隔が小さい場合にも、製造工程でコア部材の鍔部などに変形や欠けなどの欠陥を生じることが抑制、防止される。
　その結果、小型化、低背化された巻線型コイル部品を効率よく製造することが可能になる。
　また、本発明（請求項２）の巻線型コイル部品の製造方法は、樹脂シートの貫通孔に磁性体材料を充填した磁性体材料充填樹脂シートと、樹脂シートの貫通孔に非磁性体材料を充填した非磁性体材料充填樹脂シートと、磁性体シートとを積層して、磁性体材料層と非磁性体材料層とが焼成後に巻芯部となる柱状積層体を形成し、かつ、柱状積層体が、焼成後に鍔部となる磁性体シートに挟まれた構造を有する未焼成のコア部材を複数含む積層体を形成し、この積層体を所定の位置でカットして、個々の未焼成コア部材に分割した後、未焼成コア部材を焼成することによりコア部材を形成し、このコア部材に巻線を巻回するようにしているので、軸芯方向についてみた場合に、所定の領域が非磁性体からなり、その他の領域が磁性体からなる巻芯部と、磁性体からなる鍔部とを備えたコア部材の巻芯部に巻線が巻回された構造を有する巻線型コイル部品を効率よく製造することができる。
　すなわち、この請求項２の巻線型コイル部品の製造方法の場合にも、焼成後に得られるコア部材の一対の鍔部に挟まれた領域（巻芯部に巻線を巻回したときに、巻線が保持される領域）に、樹脂シートに存在する状態で積層体の圧着、圧着後の積層体のカットが行われるとともに、カットされた未焼成コア部材が、巻芯部の周囲の領域に、樹脂シートに存在する状態で焼成工程に供されることになるため、コア部材の鍔部の厚みが薄く、上下の鍔部の間隔が小さい場合にも、製造工程でコア部材の鍔部などに変形や欠けなどの欠陥を生じることが抑制、防止される。
　その結果、軸芯方向についてみた場合に、所定の領域が非磁性体からなり、その他の領域が磁性体からなる巻芯部と、磁性体からなる鍔部とを備えたコア部材の巻芯部に巻線が巻回された構造を有する巻線型コイル部品を、効率よく製造することが可能になる。
　また、上述の請求項１の巻線型コイル部品の製造方法と同様に、小型化、低背化された巻線型コイル部品を効率よく製造することが可能になる。
　また、本発明の巻線型コイル部品の製造方法において、樹脂シートとして、コア部材を構成する磁性体材料の焼結温度よりも焼結温度の高いセラミック材料を含有する樹脂シートを用いることにより、樹脂シートの成形性、形状安定性を向上させることが可能になり、より形状精度の高いコア部材を形成することができる。
　本発明においては、磁性体材料の焼結温度よりも焼結温度の高いセラミック材料を含有させる割合は、樹脂成分の２０～５０体積％とすることが、成形性、形状安定性を向上させる見地から好ましい。
　また、樹脂シートに形成される貫通孔の平面形状を楕円形とすることにより、巻芯部の平面断面の形状が円形である場合に比べて、同じ平面断面積で、大きな巻線スペースを確保することができるコア部材を得ることが可能になり、有意義である。
　すなわち、巻線型コイル部品においては、鍔部に外部電極を形成するための領域を確保するために、鍔部の平面形状は通常正方形ではなく、長方形とされるため、巻芯部の平面断面の形状を楕円形にすることにより、巻線を鍔部から外側に突出させることなく巻回することが可能な巻線のターン数を増やすことが可能になり、同じ平面面積とした場合における、取得インダクタンスを大きくすることができる。
　また、磁性体シートとして、コア部材の鍔部に、巻芯部に巻回された巻線を鍔部の外側に導く際に巻線を通過させる切り欠き部を形成するための切り込みを施した磁性体シートを用いることにより、巻線を鍔部から外側に突出させることなく、切り欠き部を経て導出させて鍔部の外側表面に形成された実装用電極に接続することが可能になり、実装面積を小さくすることが可能になる。
　なお、切り込みは、貫通孔が形成されるようなものであってもよく、また、積層体を所定の位置でカットして、個々の未焼成コア部材に分割する工程で、磁性体シートの所定の位置に切り欠き部が形成されることになるような切り込みであってもよい。
本発明の実施例１にかかる巻線型コイル部品を示す図であり、(ａ)は正面断面図、(ｂ)は底面図である。 本発明の実施例１にかかる巻線型コイル部品の製造方法を説明する図であり、(ａ)は樹脂シートに円形の貫通孔を形成した状態を示す図、(ｂ)は貫通孔に磁性体ペーストを充填した状態を示す図である。 本発明の実施例１にかかる巻線型コイル部品の製造方法を説明する図であり、(ａ)は磁性体シートと、磁性材料充填樹脂シートとを積層する態様を説明する図、(ｂ)は積層した後の状態を示す図である。 本発明の実施例２にかかる巻線型コイル部品の製造方法を説明する図である。 本発明の実施例２にかかる巻線型コイル部品の構成を示す底面図である。 本発明の実施例３にかかる巻線型コイル部品の製造方法を説明する図である。 本発明の実施例３にかかる巻線型コイル部品の構成を示す底面図である。 本発明の実施例４にかかる巻線型コイル部品の製造方法を説明する図である。 本発明の実施例４にかかる巻線型コイル部品の製造方法を説明する図であって、磁性体シートと、磁性材料充填樹脂シートと、非磁性体材料充填樹脂シートとを積層する態様を説明する図である。 本発明の実施例４にかかる巻線型コイル部品の構成を示す正面断面図である。
　以下に本発明の実施の形態を示して、本発明の特徴とするところをさらに詳しく説明する。
　この実施例１では、従来の技術を説明するにあたっても用いた図１(ａ)，(ｂ)に示すような構造を有する巻線型コイル部品（巻線型インダクタ）を製造する場合を例にとって説明する。
　なお、この巻線型コイル部品１０は、巻芯部１と、該巻芯部１の両端に連接された一対の鍔部２ａ，２ｂとを有する、フェライト磁器からなるコア部材３を備えており、巻芯部１に巻線４が巻回され、さらに該巻線４はエポキシ樹脂等の熱硬化樹脂を主成分とする保護部材５により外装された構造を有するものである。また、コア部材３の一方の主面（この実施例では鍔部２ｂの下面）に実装用電極６ａ，６ｂが形成されており、巻線４の両端が実装用電極６ａ，６ｂに引き出され、はんだ等で接合されている。
　(１)磁性体シートの作製
　セラミック素原料（フェライト素原料）として、Ｆｅ2Ｏ3、ＺｎＯ、ＮｉＯ、ＣｕＯを用意し、Ｆｅ2Ｏ3を４８．０ｍｏｌ％、ＺｎＯを１６．０ｍｏｌ％、ＮｉＯを３０．０ｍｏｌ％、ＣｕＯを６．０ｍｏｌ％の比率で秤量した。
　そして、これら秤量物を純水、およびＰＳＺボールとともにボールミルに入れて、４８時間湿式混合し、磁性体原料スラリーを得た。そして、この原料スラリーをスプレードライヤーにより乾燥した後、７００℃で２時間仮焼して仮焼物（磁性体材料）を得た。　
　次に、この仮焼物をエタノール（有機溶剤）、およびＰＳＺボールとともに再びボールミルに投入し、１６時間湿式粉砕した後、所定量のバインダー（この実施例ではポリビニルブチラール系バインダー）、および可塑剤を添加し、さらに２時間混合してセラミックスラリーを得た。
　それから、このセラミックスラリーをドクターブレード法により、厚みが３０～１００μｍとなるようにシート状に成形して、磁性体シートを得た。
　(２)磁性体ペーストの作製
　上記(１)で作製した仮焼物（磁性体材料）に純水などの溶媒を加え、ＰＳＺボールとともにボールミルに入れて、湿式で十分に粉砕した。次に、この粉砕物を脱水乾燥し、例えば、エチルセルロース樹脂とα―テルピネオールからなる有機ビヒクルと混合し、三本ロールミルで混練することにより、磁性体ペーストを作製した。
　(３)樹脂シートの作製
　所定量のバインダー（ポリビニルブチラール系バインダー）、およびアルミナ（Ａｌ2Ｏ3）粉末を、エタノール（有機溶剤）、およびＰＳＺボールとともにボールミルに投入し、所定時間湿式混合することによりスラリー（樹脂スラリー）を調製した。
　それから、この樹脂スラリーをドクターブレード法により、厚みが３０～１００μｍとなるようにシート状に成形して、樹脂シートを作製した。
　樹脂シートは、成形性を高めるために配合されたＡｌ2Ｏ3を含んでいる。
　なお、磁性体材料の焼結温度よりも焼結温度の高いセラミック材料としてのＡｌ2Ｏ3は、樹脂成分である上記バインダーの２０～５０体積％の範囲で含有させることが、成形性、形状安定性を向上させる見地から好ましい。
　なお、Ａｌ2Ｏ3は、焼成温度が上記(１)で作製した磁性体材料（仮焼物）に比べて高く、コア部材の焼成の際にも焼結しないため、コア部材の焼成後に簡単に除去することができる。
　ただし、成形性を高めるために配合される粉末としては、Ａｌ2Ｏ3以外にも、コア部材を構成する磁性体材料の焼結温度よりも焼結温度の高い、種々のセラミック材料（例えば、ジルコニア（ＺｒＯ2）、イットリア（Ｙ2Ｏ3）、ムライトなど）を用いることが可能である。
　なお、Ａｌ2Ｏ3粉末などのセラミック粉末を含有させずに、樹脂のみで樹脂シートを形成することも可能である。
　(４)インダクタの作製
　図２(ａ)に示すように、上記(３)で作製した樹脂シート１１に、所定の大きさの円形の貫通孔１２を形成した。
　そして、形成した貫通孔１２に、図２(ｂ)に示すように、上記(２)で作製した磁性体ペースト（磁性体材料）１３を印刷、充填することにより、磁性体材料充填樹脂シート１１ａを作製した。
　それから、作製した磁性材料充填樹脂シート１１ａの所定枚数と、上記(１)で作製した磁性体シート１４の所定枚数とを、図３(ａ)に示すように、磁性体材料充填樹脂シート１１ａが磁性体シート１４により挟み込まれるような態様で積層した後、９８ＭＰａの圧力条件で圧着し、図３(ｂ)に示すように、複数の未焼成コア部材３ａを含む積層体（未焼成積層体）１５を得た。
　次に、この積層体１５を所定の位置で切断線Ｌに沿ってカットして、個々の未焼成コア部材に分割した後、３００～４００℃の温度で十分脱脂し、１０００～１１５０℃で２～５時間、焼成することにより焼成済みのコア部材を得た。
　それから、焼成済みのコア部材をφ０．１ｍｍのＰＳＺビーズと純水とともにポリ塩化ビニル樹脂製のポットに入れてバレル研磨し、コア部材に付着したＡｌ2Ｏ3粉末を除去し、図１(ａ)，(ｂ)に示すようなコア部材３を得た。
　次に、鍔部２ａ，２ｂにＡｇペーストを塗布し、焼き付けることにより、図１(ａ)，(ｂ)に示すような実装用電極６ａ，６ｂを形成した。
　そして、コア部材３の巻芯部１に巻線４を巻回して、その端末を実装用電極６ａ，６ｂと接合した後、エポキシ樹脂等の熱硬化樹脂を主成分とする保護部材５を巻線４の周囲に配設することにより、図１(ａ)，(ｂ)に示すような巻線型コイル部品（巻線型インダクタ）１０を得た。
　得られた巻線型コイル部品（巻線型インダクタ）１０は、平面寸法が２．０×１．６ｍｍ、高さが０．７ｍｍであり、インダクタンス値は、ターン数を調整することにより４．７μＨに設定した。
　また、この巻線型インダクタ１０の実装用電極６ａ，６ｂ間の直流抵抗Ｒｄｃを測定した結果、０．８Ωであった。
　上記のように、印刷、積層工法を使用し、焼成後に巻芯部となる部分の周囲に、樹脂を主体としたシート（樹脂シート）が存在する積層体を形成し、この積層体をカットして、個々の未焼成コア部材に分割した後、焼成してコア部材を得るようにしているので、コア部材の鍔部の厚みが薄く、上下の鍔部の間隔が小さい場合にも、製造工程でコア部材の鍔部などに変形や欠けなどの欠陥を生じることを防止して、小型化、低背化された巻線型コイル部品（巻線型インダクタ）を効率よく製造することができる。
　また、印刷、積層工法を用いているので、軸芯部の断面形状を任意に形成することができる。
　この実施例２では、図４に示すように、樹脂シート１１に、所定の大きさの楕円形の貫通孔１２ａを形成し、この楕円形の貫通孔１２ａに、磁性体ペースト１３を印刷・充填することにより、磁性材料充填樹脂シート１１ａを作製した。
　そして、この磁性材料充填樹脂シート１１ａを用いたことを除いて、上記実施例１の場合と同じ方法、同じ条件で、図５に示すような巻線型コイル部品（巻線型インダクタ）１０を作製した。なお、図５は、得られた巻線型コイル部品（巻線型インダクタ）１０の構成を示す底面図である。
　この実施例２の方法によれば、図５に示すように、巻芯部１の平面断面形状が楕円形の巻線型コイル部品（巻線型インダクタ）１０が得られる。なお、図５において、図１(ｂ)と同じ符号を付した部分は同一部分を示している。
　巻線型コイル部品において、鍔部は、外部電極を形成する領域を確保するために、通常は正方形ではなく、長方形に形成されることが多いため、この実施例２の巻線型コイル部品（巻線型インダクタ）１０のように、巻芯部１の平面断面形状を楕円形にすることにより、巻線を鍔部２ｂ（図５）から外側に突出させることなく巻回することができる巻線のターン数を増やすことが可能になり、同じ平面面積とした場合における、取得インダクタンスを大きくすることができる。
　この実施例３では、磁性体シートとして、図６に示すように、個々のコア部材の鍔部のコーナー部となる位置に、巻芯部に巻回された巻線を鍔部の外側に導く際に巻線を通過させるための切り欠き部１７（図７参照）となる切り込み１６を施した磁性体シート１４ａを作製した。
　なお、この実施例３では切り込み１６として、方形の貫通孔１７ａが形成されるような切り込みを形成した。
　そして、この磁性体シート１４ａを用いたことを除いて、上記実施例１の場合と同じ方法、同じ条件で、巻線型コイル部品（巻線型インダクタ）１０（図７参照）を作製した。なお、図７は、得られた巻線型コイル部品（巻線型インダクタ）１０の構成を示す底面図である。
　図７に示すように、この巻線型コイル部品（巻線型インダクタ）１０では、巻線４を引き出して実装用電極６ａ，６ｂに接続するにあたって、切り欠き部１７から巻線４を引き出すようにしているので、コア部材３の外周から巻線４がはみ出すことを防止することが可能になり、製品の実装面積を小さくすることができる。
　(１)非磁性体ペーストの作製
　Ｆｅ2Ｏ3を４８．０ｍｏｌ％、ＺｎＯを４６．０ｍｏｌ％、ＣｕＯを６．０ｍｏｌ％の比率で秤量した。
　次いで、これら秤量物を純水、およびＰＳＺボールとともにボールミルに入れて、４８時間湿式混合し、非磁性体原料スラリーを得た。そして、この原料スラリーをスプレードライヤーにより乾燥した後、７００℃で２時間仮焼して仮焼物を得た。　
　次に、この仮焼物を純水、およびＰＳＺボールとともに、ボールミルに入れて、湿式で十分に粉砕し、得られた粉砕物を脱水、乾燥して、非磁性体乾燥粉末を得た。
　それから得られた非磁性体乾燥粉末を、例えば、エチルセルロース樹脂、α―テルピネオールからなる有機ビヒクルと混合し、三本ロールミルで混練することにより非磁性体ペーストを作製した。
　(２)インダクタの作製
　図８に示すように、実施例１で用いたものと同じ樹脂シート１１に、所定の大きさの円形の貫通孔１２を形成した。そして、形成した貫通孔１２に、上記(１)で作製した非磁性体ペースト１８を印刷、充填することにより、非磁性体材料充填樹脂シート１１ｂを作製した。
　また、上記実施例１の場合と同様にして、実施例１で作製したものと同じ磁性体材料充填樹脂シート１１ａを作製した。
　そして、この非磁性材料充填樹脂シート１１ｂを、実施例１で作製したものと同じ磁性材料充填樹脂シート１１ａと組み合わせて用い、実施例１に準じる方法で、図１０に示すような、巻芯部１を、軸芯方向についてみた場合に、所定の領域が非磁性体Ａからなり、その他の領域（非磁性体Ａの上下両側の領域）が磁性体Ｂからなる巻芯部１と、磁性体Ｂからなる鍔部２ａ，２ｂとを備えたコア部材３を備えた巻線型コイル部品（巻線型インダクタ）１０を作製した。なお、図１０において、図１(ａ)，(ｂ)と同一符号を付した部分は同一部分を示す。
　以下、その製造方法について説明する。
　まず、上述のようにして作製した非磁性体材料充填樹脂シート１１ｂと、実施例１で作製したものと同じ磁性体材料充填樹脂シート１１ａとを、図９に示すように、非磁性体材料充填樹脂シート１１ｂが、その両主面側から磁性体材料充填樹脂シート１１ａにより挟まれるような態様で積層して、９８ＭＰａで圧着し、複数の未焼成コア部材を含む積層体（未焼成積層体）を得た。
　なお、積層体（未焼成積層体）を構成する非磁性体材料充填樹脂シート１１ｂは、１枚であっても複数枚であってもよく、また、その両主面側に配設される磁性材料充填樹脂シート１１ａもそれぞれ１枚であっても複数枚であってもよい。
　次に、この積層体を所定の位置で切断線に沿ってカットして、個々の未焼成コア部材に分割した。そして、未焼成コア部材を３００～４００℃の温度で十分脱脂した後、１０００～１１５０℃で２～５時間、焼成した。
　それから、焼成済みのコア部材をφ０．１ｍｍのＰＳＺビーズと純水とともにポリ塩化ビニル樹脂製のポットに入れてバレル研磨し、コア部材に付着したＡｌ2Ｏ3粉末を除去し、図１０に示すようなコア部材３を得た。
　次に、鍔部２ａ，２ｂにＡｇペーストを塗布し、焼き付けることにより、図１(ａ)，(ｂ)に示すような実装用電極６ａ，６ｂを形成した。
　それから、巻線４を巻芯部１に巻回して、その端末を実装用電極６ａ，６ｂと接合した後、エポキシ樹脂等の熱硬化樹脂を主成分とする保護部材５を巻線の周囲に配設することにより、図１０に示すような巻線型コイル部品（巻線型インダクタ）１０を得た。なお、図１０において、図１(ａ)，(ｂ)と同一符号を付した部分は同一部分を示す。
　図１０に示す巻線型コイル部品（巻線型インダクタ）１０は、巻芯部１が、軸芯方向についてみた場合に、非磁性体Ａからなる中央領域１ａ、磁性体Ｂからなる上部領域１ｂおよび下部領域１ｃから構成されており、磁性体層（上部および下部領域１ｂ，１ｃ）の間に非磁性体層（中央領域１ａ）が挟まれているため、開磁路構造となり、直流重畳特性を向上させることが可能になる。
　なお、この実施例４の巻線型コイル部品の製造方法によれば、巻芯部の軸心方向の一部に非磁性体層が配設されたコア部材を、鍔部などの変形や損傷を招くことなく、効率よく製造することができる。
　なお、この実施例４では、非磁性体材料充填樹脂シート１１ｂは、巻芯部の軸芯方向の中央領域に配設されているが、中央より上側あるいは下側の領域に配設することも可能であり、その具体的な位置や厚みなどには特別の制約はない。また、非磁性体層を軸方向の複数の位置に配設することも可能である。
　なお、本発明は、上記実施例に限定されるものではなく、磁性体材料充填樹脂シートおよび非磁性体材料充填樹脂シートを形成する方法、磁性体材料充填樹脂シートまたは、磁性材料充填樹脂シートと非磁性体材料充填樹脂シートの積層態様、具体的なコア部材の形状や寸法、樹脂シートの構成材料、樹脂シートに含ませる、コア部材を構成する磁性体材料よりも焼結温度の高いセラミック材料の種類、樹脂シートに形成される貫通孔の平面形状、磁性体シートの構成材料、磁性体シートへの切り込みの態様などに関し、発明の範囲内において、種々の応用、変形を加えることが可能である。
　１　　　　　　　　　巻芯部
　２ａ，２ｂ　　　　　一対の鍔部
　３　　　　　　　　　コア部材
　３ａ　　　　　　　　未焼成コア部材
　４　　　　　　　　　巻線
　５　　　　　　　　　保護部材
　６ａ，６ｂ　　　　　実装用電極
　１０　　　　　　　　巻線型コイル部品
　１１　　　　　　　　樹脂シート
　１１ａ　　　　　　　磁性体材料充填樹脂シート
　１１ｂ　　　　　　　非磁性体材料充填樹脂シート
　１２　　　　　　　　円形の貫通孔
　１２ａ　　　　　　　楕円形の貫通孔　
　１３　　　　　　　　磁性体ペースト
　１４　　　　　　　　磁性体シート
　１５，１５ａ　　　　積層体（未焼成積層体）
　１６　　　　　　　　切り込み
　１７　　　　　　　　切り欠き部
　１７ａ　　　　　　　磁性体シートに形成された方形の貫通孔
　１８　　　　　　　　非磁性体ペースト
　Ａ　　　　　　　　　非磁性体
　Ｂ　　　　　　　　　磁性体
　Ｌ　　　　　　　　　切断線

Claims (5)

  1. 　巻線が巻回される磁性体からなる巻芯部と、前記巻芯部の両端に連接された磁性体からなる一対の鍔部とを備えたコア部材を具備する巻線型コイル部品の製造方法であって、
    　焼成工程で燃焼して消失する樹脂を主体とする樹脂シートの複数の位置に貫通孔を形成するとともに、形成した前記貫通孔に磁性体材料を充填して、磁性体材料充填樹脂シートを形成する工程と、
    　前記磁性体材料充填樹脂シートと、磁性体材料を主体とする磁性体シートとを積層して、前記磁性体材料充填樹脂シートの前記貫通孔に充填された、焼成後に巻芯部となる磁性体材料が、焼成後に鍔部となる前記磁性体シートに挟まれた構造を有する、未焼成のコア部材を複数含む積層体を形成する工程と、
    　前記積層体を所定の位置でカットして、個々の未焼成コア部材に分割する工程と、
    　前記未焼成コア部材を焼成してコア部材を得る工程と、
    　前記コア部材に巻線を巻回する工程と
    　を具備することを特徴とする巻線型コイル部品の製造方法。
  2. 　巻線が巻回される巻芯部であって、軸芯方向についてみた場合に、所定の領域が非磁性体からなり、その他の領域が磁性体からなる巻芯部と、前記巻芯部の両端に連接された磁性体からなる一対の鍔部とを備えたコア部材を具備する巻線型コイル部品の製造方法であって、
    　焼成工程で燃焼して消失する樹脂を主体とする樹脂シートの複数の位置に貫通孔を形成するとともに、形成した前記貫通孔に磁性体材料を充填して、磁性体材料充填樹脂シートを形成する工程と、
    　焼成工程で燃焼して消失する樹脂を主体とする樹脂シートの複数の位置に貫通孔を形成するとともに、形成した前記貫通孔に非磁性体材料を充填して、非磁性体材料充填樹脂シートを形成する工程と、
    　前記磁性体材料充填樹脂シートと、前記非磁性体材料充填樹脂シートと、磁性体材料を主体とする磁性体シートとを積層して、前記磁性体材料充填樹脂シートの前記貫通孔に充填された、焼成後に巻芯部となる磁性体材料層と、前記非磁性体材料充填樹脂シートの前記貫通孔に充填された、焼成後に巻芯部となる非磁性体材料層とが柱状積層体を形成し、かつ、前記柱状積層体が、焼成後に鍔部となる前記磁性体シートに挟まれた構造を有する、未焼成のコア部材を複数含む積層体を形成する工程と、
    　前記積層体を所定の位置でカットして、個々の未焼成コア部材に分割する工程と、
    　前記未焼成コア部材を焼成してコア部材を得る工程と、
    　前記コア部材に巻線を巻回する工程と
    　を具備することを特徴とする巻線型コイル部品の製造方法。
  3. 　前記樹脂シートが、前記コア部材を構成する磁性体材料の焼結温度よりも焼結温度の高いセラミック材料を含有していることを特徴とする請求項１または２記載の巻線型コイル部品の製造方法。
  4. 　前記樹脂シートに形成される前記貫通孔の平面形状が楕円形であることを特徴とする請求項１～３のいずれかに記載の巻線型コイル部品の製造方法。
  5. 　前記磁性体シートとして、前記コア部材の前記鍔部に、前記巻芯部に巻回された前記巻線を前記鍔部の外側に導く際に巻線を通過させる切り欠き部を形成するための切り込みを施した磁性体シートを用いることを特徴とする請求項１～４のいずれかに記載の巻線型コイル部品の製造方法。
PCT/JP2012/052391 2011-03-22 2012-02-02 巻線型コイル部品の製造方法 WO2012127908A1 (ja)