WO2012105665A1 - テキスタイル/樹脂積層構造ハウジング及びその製造装置 - Google Patents

テキスタイル/樹脂積層構造ハウジング及びその製造装置 Download PDF

Info

Publication number
WO2012105665A1
WO2012105665A1 PCT/JP2012/052434 JP2012052434W WO2012105665A1 WO 2012105665 A1 WO2012105665 A1 WO 2012105665A1 JP 2012052434 W JP2012052434 W JP 2012052434W WO 2012105665 A1 WO2012105665 A1 WO 2012105665A1
Authority
WO
WIPO (PCT)
Prior art keywords
textile
mold
thermocompression
layer
resin
Prior art date
Application number
PCT/JP2012/052434
Other languages
English (en)
French (fr)
Inventor
渡邊　泰
秀治 城野
Original Assignee
Art&Tech株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Art&Tech株式会社 filed Critical Art&Tech株式会社
Publication of WO2012105665A1 publication Critical patent/WO2012105665A1/ja

Abstract

テキスタイル層の基盤樹脂層に対する密着性を向上させ且つテキスタイル層の皺の発生や絵柄のゆがみを無くすことができるテキスタイル/樹脂積層構造ハウジングの製造装置を提供する。この製造装置は、プレス機と、射出成型機20とを備える。プレス機は、一方の面にA-PETシート2が熱圧着されたテキスタイル層4の熱圧着体をテキスタイル層を表にして受容するメス金型10と、熱圧着体を成形するために熱圧着体を固定金型の中に押し込むように固定金型に向けて移動されるオス金型11とを備える。射出成形機20は、成形された熱圧着体をテキスタイル層を表にして受容するメス金型12と、メス金型12に受容された熱圧着体に向けて移動される射出成形オス金型22と、メス金型12に受容された熱圧着体と射出成形オス金型22とで規定される空間に基盤樹脂層の原料を射出する射出ユニットとを備える。A-PETシート2は、射出された基盤樹脂層の原料が固化した後に剥がされる。

Description

テキスタイル／樹脂積層構造ハウジング及びその製造装置
　本発明は、テキスタイル／樹脂積層構造ハウジング及びその製造装置に関し、特に、基盤樹脂層の上にテキスタイル層が積層されたテキスタイル／樹脂積層構造ハウジング及びその製造装置に関する。
　電子機器や家電等のハウジング及び自動車内装品のハウジングの技術分野において、そのハウジングは、外面に加飾材が積層された樹脂成形によって作られる場合が多く、近年、樹脂成形ハウジングに施されるさまざまな加飾材が他の製品からの差別化に欠かせない要素となっている。このような状況において、一部の企業は、同一製品でも、樹脂成形ハウジングに多様な加飾材を施すことで顧客が自由に製品の加飾デザインを選択することができるようになっている。
　樹脂成形ハウジングの加飾方法としては、樹脂シートに塗装、転写、グラビア印刷を施す技術があり（例えば、特許文献１参照）、また、装飾性に優れた繊維（テキスタイル）を含む装飾材をインモールド成形によって樹脂容器の表面に形成した樹脂成形体が提案されている（例えば、特許文献２参照）。この樹脂成形体は、互いに接合された基材フィルム及びテキスタイル素材からなる装飾材が被装飾体の表面に融着されている。装飾材は、一例として、基材フィルムが覆われたテキスタイル素材からなり、基材フィルムの素材がポリエステル樹脂、ナイロン等のポリアミド樹脂、ポリオレフィン樹脂、ポリスチレン樹脂等からなる。
　また、被装飾体に加飾材としてのテキスタイル素材を接着する技術として、テキスタイル素材を金型キャビティ面上に張設した後キャビティ内に溶融樹脂を加圧注入することにより、加飾材に溶融樹脂を浸透させて両者を投錨状態に積層圧着する技術がある（例えば、特許文献３参照）。
特開２０００−２５１６８号公報 特開２０１０−３６３６６号公報 特開２００５−４７１６１号公報
　しかしながら、特許文献１の技術では、塗装による加飾は、加飾部が平面的でしかない上に塗装工程で使用される揮発性有機化合物（ＶＯＣ）が健康被害を引き起こし、転写による加飾は、プラスチック成形筐体から塗料が剥離し易い場合が多く、グラビア印刷による加飾は、絵柄毎に金型ロールを準備する必要性から個別少量生産には適していない。
　また、特許文献２の技術では、テキスタイル素材を覆う基材フィルムが耐衝撃性に劣ると共に傷がつき易いのに加えて、インモールド成形時の高温下における耐性が低く且つ被装飾体に対するテキスタイル素材の接着性が劣り、製品のハウジングを形成するには装飾材が融着された被装飾体にさらなるハウジング加工工程を施す必要がある。
　特許文献３の技術では、被装飾材に対するテキスタイル素材の密着性が十分でない上に、必ずしも製品の多様化のための多種少量生産性及び各製品への汎用性が考慮されていない。また、特許文献３の技術では、溶融樹脂の加圧注入時にテキスタイル素材に皺がよったり絵柄がゆがんだりし易く量産時の歩留まりが悪い。
　本発明の目的は、テキスタイル層の基盤樹脂層に対する密着性を向上させ且つテキスタイル層の皺の発生や絵柄のゆがみを無くすことができるテキスタイル／樹脂積層構造ハウジングの製造装置を提供すると共に、テキスタイル層の基盤樹脂層に対する密着性及びテキスタイル層の皺の発生や絵柄のゆがみがないテキスタイル／樹脂積層構造ハウジングをを提供することにある。
　上記目的を達成するために、請求項１に記載のテキスタイル／樹脂積層構造ハウジングの製造装置は、一方の面にＡ−ＰＥＴシートが熱圧着されたテキスタイル層の熱圧着体を前記テキスタイル層を表にして受容する固定金型と、前記熱圧着体を成形するために当該受容された熱圧着体を前記固定金型の中に押し込むように前記固定金型に向けて移動される可動金型と、前記成形された熱圧着体を前記テキスタイル層を表にして受容する他の固定金型と、前記他の固定金型に受容された熱圧着体に向けて移動される射出成形金型と、前記他の固定金型に受容された熱圧着体と前記射出成形金型とで規定される空間に基盤樹脂層の原料を射出する射出ユニットとを備え、前記Ａ−ＰＥＴシートは、前記射出された基盤樹脂層の原料が固化した後に剥がされることを特徴とする。
　請求項２に記載のテキスタイル／樹脂積層構造ハウジングの製造装置は、一方の面にＡ−ＰＥＴシートが熱圧着されたテキスタイル層の熱圧着体を前記テキスタイル層を表にして受容する固定金型と、前記熱圧着体を成形するために当該受容された熱圧着体を前記固定金型の中に押し込むように前記固定金型に向けて移動される可動金型と、前記固定金型に押し込まれた熱圧着体に向けて移動される射出成形金型と、前記他の固定金型に受容された熱圧着体と前記射出成形金型とで規定される空間に基盤樹脂層の原料を射出する射出ユニットとを備え、前記Ａ−ＰＥＴシートは、前記射出された基盤樹脂層の原料が固化した後に剥がされることを特徴とする。
　請求項１１に記載のテキスタイル／樹脂積層構造ハウジングは、上記テキスタイル／樹脂積層構造ハウジングの製造装置によって製造されることを特徴とする。
　請求項１又は２に記載のテキスタイル／樹脂積層構造ハウジングの製造装置によれば、テキスタイル層の基盤樹脂層に対する密着性を向上させ且つテキスタイル層の皺の発生や絵柄のゆがみを無くすことができる。
　請求項１１に記載のテキスタイル／樹脂積層構造ハウジングは、テキスタイル層の基盤樹脂層に対する密着性が優れ且つテキスタイル層の皺の発生や絵柄のゆがみがない。
本発明の実施の形態に係るテキスタイル／樹脂積層構造ハウジングの外観斜視図である。 図１の線ＩＩ−ＩＩに沿うテキスタイル／樹脂積層構造ハウジングの断面図である。 本発明の実施の形態に係るテキスタイル／樹脂積層構造ハウジングの製造装置を説明するのに用いられる図である。 本発明の他の実施の形態に係るテキスタイル／樹脂積層構造ハウジングの外観斜視図である。 図４の線Ｖ−Ｖに沿うテキスタイル／樹脂積層構造ハウジングの断面図である。 図４の線ＶＩ−ＶＩに沿うテキスタイル／樹脂積層構造ハウジングの断面図である。
　以下、本発明を図面を参照しながら詳述する。
　図１は、本発明の実施の形態に係るテキスタイル／樹脂積層構造ハウジングの外観斜視図である。
　図１において、テキスタイル／樹脂積層構造ハウジング１（以下、単に「ハウジング１」という場合もある）は、逆舟形構造のリモコン装置用上部ケーシングであり、逆舟形構造の底部に２つの開口部６を有する。
　図２は、図１の線ＩＩ−ＩＩに沿うテキスタイル／樹脂積層構造ハウジングの断面図である。
　ハウジング１は、テキスタイル層４と、テキスタイル層４の各繊維の隙間に浸潤しつつテキスタイル層４に固着された基盤樹脂層５とを備える。
　テキスタイル層４は、織物、編物等の繊維製品を含むテキスタイルからなる。このテキスタイルとしては、ポリエステル織物、編物、レース、カーボン繊維が挙げられる。
　このテキスタイルは、さまざまなデザインが容易に得られると共に繊維生地の立体感がそのまま現出される。また、テキスタイルの使用は、ハウジング１のデザイン性の自由度を高めることができるのに加えて、ハウジング１の強度を高める効果を有する。
　基盤樹脂層５は、熱可塑性合成樹脂、好ましくは射出成形用合成樹脂からなり、具体的には、ＡＢＳ（アクリルブチルスチレン）樹脂、ＰＣ（ポリカーボネート）樹脂、ＡＢＳ−ＰＣ樹脂、ＰＭＭＡ（ポリメタクリルアクリレート）樹脂（アクリル樹脂）の群から選択された１つの素材、好ましくはＡＢＳ樹脂からなり、厚さは、製品に応じて任意に設定され、本実施の形態では、約２ｍｍである。基盤樹脂層５の原料は、後述する図３の射出成形機２０で加熱溶融され、後述するように、Ａ−ＰＥＴシート（詳細は後述する）が熱圧着されたテキスタイル層４の熱圧着体がテキスタイル層４を表にして装着された後述する図３における金型ダイ２２の中に射出されて、テキスタイル層４の各繊維の隙間に浸潤しながらテキスタイル層４に固着されている（図３）。基盤樹脂層５は、冷却固化時におけるテキスタイル層４と基盤樹脂層５の収縮によりテキスタイル層４との固着がより強固になっている。
　図１のハウジング１によれば、基盤樹脂層５がテキスタイル層４の各繊維の隙間に浸潤しつつテキスタイル層４に固着されているので、アンカー効果により、テキスタイル層４の基盤樹脂層５に対する密着性を向上させると共にテキスタイル層４の各繊維がハウジング１の強度を向上させることができる。また、図１のハウジング１によれば、ハウジング１の表面の絵柄をテキスタイル４の変更によりさまざまに選択することができる。
　図１のハウジング１は、テキスタイル層４を表とする逆舟形構造としたが、このハウジング１は、基盤樹脂層５を表とする逆舟形構造としてもよい。これらのハウジング１は、用途がリモコン構造上部ケーシングに限定されない。
　図３は、本発明の実施の形態に係るテキスタイル／樹脂積層構造ハウジングの製造装置を説明するのに用いられる図である。
　図３では、プレス機により工程Ｉ及びＩＩが実施されると共に、射出成形機により工程ＩＩＩ及びＩＶが実施される。最後に、適宜な方法により工程Ｖが実施される。
　まず、後述するＡ−ＰＥＴシート２が熱圧着されたテキスタイル層４の熱圧着体を準備し、図３の工程Ｉにおいて、Ａ−ＰＥＴシート２及びテキスタイル層４の熱圧着体をテキスタイル層４を表にしてプレス機のメス金型１０（固定金型）の上に載置する。この熱圧着体は、予め所定の形状に切断されていてもよい。
　Ａ−ＰＥＴシート２は、非晶質ポリエチレンテレフタレートからなる。これにより、Ａ−ＰＥＴシート２をテキスタイル層４に積層する際に接着剤を不要とすることができる。
　次いで、工程ＩＩにおいて、工程Ｉで載置されたＡ−ＰＥＴシート２及びテキスタイル層４の熱圧着体をメス金型１０の中に押し込むようにプレス機のオス金型１１（可動金型）をメス金型１０に向かって移動する。これにより、Ａ−ＰＥＴシート２及びテキスタイル層４の熱圧着体をメス金型１０及びオス金型１１により規定される形状に成形し、この後、成形された熱圧着体がプレス機から取り出される。このとき、成形された熱圧着体の周囲をレーザカッタや切断用金型（切断ユニット）で切断してバリ取りを行ってもよい。
　続いて、図３の工程ＩＩＩにおいて、プレス機で成形されたＡ−ＰＥＴシート２及びテキスタイル層４の熱圧着体をテキスタイル層４を表にしてメス金型２２（他の固定金型）内に装着した上で、金型ダイ２２内に受容された熱圧着体に向けて射出成形オス金型１２（射出成型金型）を移動すると共に、射出成形機２０の射出孔２０ａを射出成形オス金型１２の射出成形孔１２ａに押し当てた上で、射出スクリュー２１を時計回りに回転させてタンク３０内の基盤樹脂層５の原料３１を当該熱圧着体と射出成形オス金型１２とで規定される空間に射出する。このとき、基盤樹脂層５の原料３１はテキスタイル層４の各繊維の隙間に浸潤し、原料３１の冷却固化時におけるテキスタイル層４と基盤樹脂層５の収縮によりテキスタイル層４との固着がより強固になる。
　次いで、工程ＩＶにおいて、射出成形された基盤樹脂層５の原料３１が冷却して固化した後、射出機２０及び射出成形オス金型１２がメス金型１０から離間されて、ハウジング１が取り出される。
　最後に、Ａ−ＰＥＴシート２を剥がして、所望のテキスタイル／樹脂積層構造ハウジング１が完成する。
　メス金型１０及びオス金型１１はプレス機を構成すると共に、メス金型２２、射出成形オス金型１２、及び射出機２０は射出成形機を構成し、プレス機及び射出成形機はハウジング１の製造装置を構成する。変形例として、プレス機と射出成形機とが一体となっていて、メス金型１０がメス金型２２として使用されてもよい。この場合は、メス金型１０の中で成形された透明アクリルシート層２及びテキスタイル層４の積層体に向けて射出成形オス金型１２が移動される。
　図３のテキスタイル／樹脂積層構造ハウジングの製造装置によれば、工程ＩＩＩにおいて、基盤樹脂層５の原料３１がテキスタイル層４の各繊維の隙間に浸潤し、原料３１の冷却固化時におけるテキスタイル層４と基盤樹脂層５の収縮によりテキスタイル層４との固着がより強固になるのに加えて、ハウジング１の製造工程を簡略化させると共に、表面コーティング塗装工程を省くことができる。さらに、基盤樹脂層５の素材として、高温でしか成形できないポリカーボネートを用いることができる。
　また、図３のテキスタイル／樹脂積層構造ハウジングの製造装置によれば、装飾性に優れたテキスタイル層４の基盤樹脂層５に対する密着性を向上させ且つ基盤樹脂層５の射出成形時にテキスタイル層４に皺の発生や絵柄のゆがみを無くすことができる。
　図３のテキスタイル／樹脂積層構造ハウジングの製造装置は、ハウジング１を、テキスタイル層４を表とする逆舟形構造としているが、このハウジング１は、基盤樹脂層５を表とする逆舟形構造としてもよい。これらのハウジング１は、用途がリモコン装置用上部ケーシングに限定されない。
　図４は、本発明の他の実施の形態に係るテキスタイル／樹脂積層構造ハウジングの外観斜視図である。
　図４において、テキスタイル／樹脂積層構造ハウジング４０（以下、単に「ハウジング４０」という場合もある）は、逆盆構造のケーシングであり、逆盆構造の底部に１つの突出部４１と１つの開口部４２を有する。
　図４のハウジング４０の構造及びその製造装置は、上述した図１のハウジング１の構造及びその製造装置と同様であり、同じ構成要素には同一の参照番号が付されている。
　突出部４１の断面は、図４の線Ｖ−Ｖに沿う断面図として図５で示されると共に、開口部４２の断面は、図４の線ＶＩ−ＶＩに沿う断面図として図６で示される。
　本発明の実施の形態及び他の実施の形態においては、テキスタイル／樹脂構造ハウジング１及び４０は、リモコン装置用上部ケーシングとして記載されているが、本発明の実施の形態の他の適用技術分野としては、表面コーティング層を有するインモールド成形による加飾品が対象であり、具体的には、容器やステーショナリを含む雑貨品、携帯電話やノートパソコンを含む電子機器や家電製品等のハウジング、建築物や自動車の内外装品のハウジング、航空機の内装ハウジングが挙げられる。
１　テキスタイル／樹脂積層構造ハウジング
２　Ａ−ＰＥＴシート
４　テキスタイル層
５　基盤樹脂層
６　開口部
１０　メス金型
１１　オス金型
１２　射出成形オス金型
２０　射出機
２１　射出スクリュー
２２　メス金型
３０　タンク
３１　原料
４０　テキスタイル／樹脂積層構造ハウジング
４１　突出部
４２　開口部

Claims (9)

  1. 　一方の面にＡ−ＰＥＴシートが熱圧着されたテキスタイル層の熱圧着体を前記テキスタイル層を表にして受容する固定金型と、前記熱圧着体を成形するために当該受容された熱圧着体を前記固定金型の中に押し込むように前記固定金型に向けて移動される可動金型と、前記成形された熱圧着体を前記テキスタイル層を表にして受容する他の固定金型と、前記他の固定金型に受容された熱圧着体に向けて移動される射出成形金型と、前記他の固定金型に受容された熱圧着体と前記射出成形金型とで規定される空間に基盤樹脂層の原料を射出する射出ユニットとを備え、前記Ａ−ＰＥＴシートは、前記射出された基盤樹脂層の原料が固化した後に剥がされることを特徴とするテキスタイル／樹脂積層構造ハウジングの製造装置。
  2. 　一方の面にＡ−ＰＥＴシートが熱圧着されたテキスタイル層の熱圧着体を前記テキスタイル層を表にして受容する固定金型と、前記熱圧着体を成形するために当該受容された熱圧着体を前記固定金型の中に押し込むように前記固定金型に向けて移動される可動金型と、前記固定金型に押し込まれた熱圧着体に向けて移動される射出成形金型と、前記他の固定金型に受容された熱圧着体と前記射出成形金型とで規定される空間に基盤樹脂層の原料を射出する射出ユニットとを備え、前記Ａ−ＰＥＴシートは、前記射出された基盤樹脂層の原料が固化した後に剥がされることを特徴とするテキスタイル／樹脂積層構造ハウジングの製造装置。
  3. 　さらに、前記成形された熱圧着体の周縁を切断する切断ユニットを備える請求項１又は２記載のテキスタイル／樹脂積層構造ハウジングの製造装置。
  4. 　前記基盤樹脂層は熱可塑性合成樹脂からなることを特徴とする請求項１から３のいずれか１項に記載のテキスタイル／樹脂積層構造ハウジングの製造装置。
  5. 　前記熱可塑性合成樹脂は射出成形用合成樹脂からなることを特徴とする請求項４に記載のテキスタイル／樹脂積層構造ハウジングの製造装置。
  6. 　前記射出成形用合成樹脂は、ＡＢＳ、ＰＣ、ＰＭＭＡ、及びＰＣ−ＡＢＳの群から選択された１つの素材からなることを特徴とする請求項５に記載のテキスタイル／樹脂積層構造ハウジングの製造装置。
  7. 　前記射出成形用合成樹脂はＡＢＳ又はＰＭＭＡからなることを特徴とする請求項６に記載のテキスタイル／樹脂積層構造ハウジングの製造装置。
  8. 　前記Ａ−ＰＥＴシートは、非晶質ポリエチレンテレフタレートからなることを特徴とする請求項１から７のいずれか１項に記載のテキスタイル／樹脂積層構造ハウジングの製造装置。
  9. 　請求項１又は２に記載のテキスタイル／樹脂積層構造ハウジングの製造装置によって製造されたテキスタイル／樹脂積層構造ハウジング。
PCT/JP2012/052434 2011-01-31 2012-01-27 テキスタイル/樹脂積層構造ハウジング及びその製造装置 WO2012105665A1 (ja)