WO2011122369A1 - 低融点ガラス組成物及びそれを用いた導電性ペースト材料 - Google Patents

低融点ガラス組成物及びそれを用いた導電性ペースト材料 Download PDF

Info

Publication number
WO2011122369A1
WO2011122369A1 PCT/JP2011/056526 JP2011056526W WO2011122369A1 WO 2011122369 A1 WO2011122369 A1 WO 2011122369A1 JP 2011056526 W JP2011056526 W JP 2011056526W WO 2011122369 A1 WO2011122369 A1 WO 2011122369A1
Authority
WO
WIPO (PCT)
Prior art keywords
glass
conductive paste
lead
melting
point glass
Prior art date
Application number
PCT/JP2011/056526
Other languages
English (en)
French (fr)
Inventor
潤 濱田
Original Assignee
セントラル硝子株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by セントラル硝子株式会社 filed Critical セントラル硝子株式会社
Priority to CN201180009596.6A priority Critical patent/CN102762509B/zh
Publication of WO2011122369A1 publication Critical patent/WO2011122369A1/ja

Abstract

開示されているのは、質量％でＳｉＯ2を１～１５、Ｂ2Ｏ3を１８～３０、Ａｌ2Ｏ3を０～１０、ＺｎＯを２５～４３、ＲＯ（ＭｇＯ＋ＣａＯ＋ＳｒＯ＋ＢａＯ）を８～３０、Ｒ2Ｏ（Ｌｉ2Ｏ＋Ｎａ2Ｏ＋Ｋ2Ｏ）を６～１７含むＳｉＯ2－Ｂ2Ｏ3－ＺｎＯ－ＲＯ－Ｒ2Ｏ系無鉛低融点ガラスである。このガラスを含む導電性ペーストを結晶Ｓｉ太陽電池に使用すると、高い集電効率が得られる。

Description

低融点ガラス組成物及びそれを用いた導電性ペースト材料
　本発明は、特に結晶シリコン太陽電池に形成される電極において、良好な電気特性が得られ、また、シリコン半導体基板との密着性が良好な無鉛導電性ペースト材料に良好な低融点ガラス組成物に関する。
発明の背景
半導体シリコン基板を用いた電子部品として、図１に示すような太陽電池素子が知られている。図１に示すように、太陽電池素子は、厚みが２００μｍ程度のｐ型半導体シリコン基板１の受光面側にｎ型半導体シリコン層２を形成し、受光面側表面に受光効率をあげるための窒化珪素膜などの反射防止膜３、さらにその反射防止膜３上に半導体と接続した表面電極４が形成されている。また、ｐ型半導体シリコン基板１の裏側には、アルミニウム電極層５が一様に形成されている。
このアルミニウム電極層５は、一般に、アルミニウム粉末、ガラスフリット、エチルセルロースやアクリル樹脂などのバインダーを含む有機ビヒクルとからなるアルミニウムペースト材料を、スクリーン印刷などを用いて塗布し、６００～９００℃程度の温度で短時間焼成することで形成される。
このアルミニウムペーストの焼成において、アルミニウムがｐ型半導体シリコン基板１に拡散することで、アルミニウム電極層５とｐ型半導体シリコン基板１との間にＢＳＦ（Ｂａｃｋ Ｓｕｒｆａｃｅ Ｆｉｅｌｄ）層６と呼ばれるＳｉ－Ａｌ共晶層が形成され、さらにはアルミニウムの拡散による不純物層ｐ+層７が形成される。
このｐ+層７は、ｐｎ接合の光起電力効果によって生成したキャリアの再結合による損失を抑制する効果をもたらし、太陽電池素子の変換効率向上に寄与する。
このＢＳＦ効果に関しては、アルミニウムペーストに含まれるガラスフリットとして、鉛を含有するガラスを用いることで高い効果を得ることが可能であるということが開示されている（例えば特許文献１、２参照）。
特開２００７－５９３８０号公報 特開２００３－１６５７４４号公報
しかしながら、鉛成分はガラスを低融点とする上で重要な成分ではあるものの、人体や環境に与える弊害が大きい。上記特開２００７－５９３８０号公報や特開２００３－１６５７４４号公報に開示されているガラスフリットは、鉛成分を含むという問題がある。
本発明は、シリコン半導体基板を用いる太陽電池用の導電性ペーストに含まれる低融点ガラスにおいて、その組成が、実質的に鉛成分を含まず、質量％で、ＳｉＯ2を１～１５、Ｂ2Ｏ3を１８～３０、Ａｌ2Ｏ3を０～１０、ＺｎＯを２５～４３、ＲＯ（ＭｇＯ、ＣａＯ、ＳｒＯ、ＢａＯより選択される１種以上の合計）を８～３０、及びＲ2Ｏ（Ｌｉ2Ｏ、Ｎａ2Ｏ、Ｋ2Ｏより選択される１種以上の合計）を６～１７、含むことを特徴とするＳｉＯ2－Ｂ2Ｏ3－ＺｎＯ－ＲＯ－Ｒ2Ｏ系無鉛低融点ガラス（第１ガラス）を提供する。
第１ガラスは、３０℃～３００℃における熱膨張係数が８０×１０-7／℃　～　１３０×１０-7／℃、軟化点が４００℃以上５５０℃以下であることを特徴とする無鉛低融点ガラス（第２ガラス）であってもよい。
　また、本発明は、第１又は第２ガラスを含むことを特徴とする、導電性ペースト、太陽電池素子、又は電子材料用基板を提供する。
本発明による導電性ペーストを使用できる一般的な結晶Ｓｉ太陽電池セルの概略断面図である。
詳細な説明
本発明の無鉛低融点ガラスフリットを含む導電性ペースト材料を使用することで、高いＢＳＦ効果を得ることができる。また、シリコン半導体基板との良好な密着性を得ることができる。さらに、実質的に鉛成分を含まないため人体や環境に与える弊害がない。
本発明の導電性ペースト材料は、アルミニウム粉末とエチルセルロースやアクリル樹脂などのバインダーを含む有機ビヒクルに加えて、ガラスフリットを含み、ガラスフリットが実質的に鉛成分を含まず、質量％でＳｉＯ2を１～１５、Ｂ2Ｏ3を１８～３０、Ａｌ2Ｏ3を０～１０、ＺｎＯを２５～４３、ＲＯ（ＭｇＯ＋ＣａＯ＋ＳｒＯ＋ＢａＯ）を８～３０、Ｒ2Ｏ（Ｌｉ2Ｏ＋Ｎａ2Ｏ＋Ｋ2Ｏ）を６～１７含むＳｉＯ2－Ｂ2Ｏ3－ＺｎＯ－ＲＯ－Ｒ2Ｏ系無鉛低融点ガラスであることを特徴とする。
　本発明のガラスフリットにおいて、ＳiＯ2はガラス形成成分であり、別のガラス形成成分であるＢ2Ｏ3と共存させることにより、安定したガラスを形成することができるもので、１～１５％（質量％、以下においても同様である）の範囲で含有させる。１５％を越えると、ガラスの軟化点が上昇し、成形性、作業性が困難となる。より好ましくは、２～１４％の範囲である。
Ｂ2Ｏ3はガラス形成成分であり、ガラス溶融を容易とし、ガラスの熱膨張係数において過度の上昇を抑え、かつ、焼付け時にガラスに適度の流動性を与え、ガラスの誘電率を低下させるものである。ガラス中に１８～３０％の範囲で含有させる。１８％未満ではガラスの流動性が不充分となり、焼結性が損なわれる。他方３０％を越えるとガラスの安定性を低下させる。より好ましくは１９～２７％の範囲である。
Ａｌ2Ｏ3は、ガラスの結晶化を抑制して安定化させる成分である。ガラス中に０～１０％の範囲で含有させることが好ましい。１０％を超えるとガラスの軟化点が上昇し、成形性、作業性が困難となる。
ＺｎＯはガラスの軟化点を下げる成分もので、ガラス中に２５～４３％の範囲で含有させる。２５％未満では上記作用を発揮し得ず、４３％を超えるとガラスが不安定となり結晶を生じ易い。好ましくは２８～４２％の範囲である。
ＲＯ（ＭｇＯ＋ＣａＯ＋ＳｒＯ＋ＢａＯ）はガラスの軟化点を下げ、適度に流動性を与えるもので、ガラス中に８～３０％の範囲で含有させる。８％未満ではガラスの軟化点の低下が不十分で、焼結性が損なわれる。他方３０％を越えるとガラスの熱膨張係数が高くなりすぎる。より好ましくは１０～２７％の範囲である。
Ｒ2Ｏ（Ｌi2Ｏ、Ｎａ2Ｏ、Ｋ2Ｏ）はガラスの軟化点を下げ、適度に流動性を与え、熱膨張係数を適宜範囲に調整するものであり、６～１７％の範囲で含有させる。６％未満ではガラスの軟化点の低下が不十分で、焼結性が損なわれる。他方１７％を越えると熱膨張係数を過度に上昇させる。より好ましくは８～１５％の範囲である。
この他にも、ＣｕＯ、ＴｉＯ2、Ｉｎ2Ｏ3、Ｂｉ2Ｏ3、ＳｎＯ2、ＴｅＯ2などの一般的酸化物を加えてもよい。
本発明の低融点ガラスは実質的にＰｂＯを含まない。ここで、実質的にＰｂＯを含まないとは、ＰｂＯがガラス原料中に不純物として混入する程度の量を意味する。例えば、低融点ガラス中における０．３質量％以下の範囲であれば、先述した弊害、すなわち人体、環境に対する影響、絶縁特性等に与える影響は殆どなく、実質的にＰｂＯの影響を受けないことになる。
本発明に依れば、前記低融点ガラスの３０℃～３００℃における熱膨張係数が８０×１０-7／℃　～　１３０×１０-7／℃、軟化点が４００℃以上５５０℃以下であることを特徴とする導電性ペースト材料が提供される。熱膨張係数が８０×１０-7／℃　～　１３０×１０-7／℃を外れると電極形成時に剥離、基板の反り等の問題が発生する。好ましくは、８５×１０-7／℃　～　１２５×１０-7／℃の範囲である。
また、軟化点が５５０℃を越えると焼成時に十分に流動しないためシリコン半導体基板との密着性が悪くなるなどの問題が発生する。好ましくは、４２０℃以上５２０℃以下である。
また、上記の導電性ペースト材料を太陽電池素子又は電子材料用基板に使用することができる。
以下、実施例に基づき、説明する。
（導電性ペースト材料）
　まず、ガラス粉末は、実施例に記載した所定組成となるように各種無機原料を秤量、混合して原料バッチを作製する。この原料バッチを白金ルツボに投入し、電気加熱炉内で１０００～１３００℃、１～２時間で加熱溶融して表１の実施例１～５、表２の比較例１～４に示す組成のガラスを得た。ガラスの一部は型に流し込み、ブロック状にして熱物性(熱膨張係数、軟化点)測定用に供した。残余のガラスは急冷双ロール成形機にてフレーク状とし、粉砕装置で平均粒径１～４μｍ、最大粒径１０μｍ未満の粉末状に整粒した。
　次いで、αテルピネオールとブチルカルビトールアセテートからなるペーストオイルにバインダーとしてのエチルセルロースと上記ガラス粉、また導電性粉末としてアルミニウム粉末を所定比で混合し、粘度、５００±５０ポイズ程度の導電性ペーストを調製した。
なお、軟化点は、熱分析装置ＴＧ―ＤＴＡ（リガク（株）製）を用いて測定した。また、熱膨張係数は、熱膨張計を用い、５℃/分で昇温したときの３０～３００℃での伸び量から求めた。
　次に、ｐ型半導体シリコン基板１を準備し、その上部に上記で作製した導電性ペーストをスクリーン印刷した。これらの試験片を、１４０℃のオーブンで１０分間乾燥させ、次に電気炉にて８００℃条件下で１分間焼成し、ｐ型半導体シリコン基板１にアルミニウム電極層５とＢＳＦ層６を形成した構造を得た。
　このようにして得られたサンプルについて、電極間のオーム抵抗に影響を及ぼすアルミニウム電極層５の表面抵抗を４探針式表面抵抗測定器で測定した。
次に、アルミニウム電極層５のｐ型半導体シリコン基板１との密着性を調べるために、メンディングテープ（ニチバン製）をアルミニウム電極層５に貼り付け、剥離したときのアルミニウム電極層５の剥がれ状態を目視にて評価した。
その後、アルミニウム電極層５を形成したｐ型半導体シリコン基板１を水酸化ナトリウム水溶液に浸漬して、アルミニウム電極層５およびＢＳＦ層６をエッチングすることでｐ+層７を表面に露出させ、ｐ+層７の表面抵抗を４探針式表面抵抗測定器で測定した。
ｐ+層７の表面抵抗とＢＳＦ効果には相関があり、ｐ+層７の表面抵抗が低いほどＢＳＦ効果が高く、太陽電池素子としての変換効率が高いとされている。ここでは、ｐ+層７の表面抵抗の目標値を３５Ω／□以下とした。
　　（結果）
　無鉛低融点ガラス組成および、各種試験結果を表に示す。
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-T000002
 　表１における実施例１～５に示すように、本発明の組成範囲内においては、ｐ型半導体シリコン基板１との密着性も良好である。更には、太陽電池素子の変換効率に関係するｐ+層７の抵抗値も低く結晶Ｓｉ太陽電池用の導電性ペーストとして好適である。
　また、軟化点が４００℃～５５０℃であり、好適な熱膨張係数８０×１０-7／℃　～　１３０×１０-7／℃を有している。
　他方、本発明の組成範囲を外れる表２における比較例１～４は、ｐ型半導体シリコン基板１との良好な密着性が得られない、ｐ+層７の抵抗値が高い、または溶解後にガラスが潮解性を示すなど、結晶Ｓｉ太陽電池用の導電性ペーストとしては適用し得ない。
１　ｐ型半導体シリコン基板
２　ｎ型半導体シリコン層
３　反射防止膜
４　表面電極
５　アルミニウム電極層
６　ＢＳＦ層
７　Ｐ+層

Claims (6)

  1. シリコン半導体基板を用いる太陽電池用の導電性ペーストに含まれる低融点ガラスにおいて、その組成が、実質的に鉛成分を含まず、質量％で、
    ＳｉＯ2を１～１５、
    Ｂ2Ｏ3を１８～３０、
    Ａｌ2Ｏ3を０～１０、
    ＺｎＯを２５～４３、
    ＲＯ（ＭｇＯ、ＣａＯ、ＳｒＯ、ＢａＯより選択される１種以上の合計）を８～３０、及び、
    Ｒ2Ｏ（Ｌｉ2Ｏ、Ｎａ2Ｏ、Ｋ2Ｏより選択される１種以上の合計）を６～１７、含むことを特徴とするＳｉＯ2－Ｂ2Ｏ3－ＺｎＯ－ＲＯ－Ｒ2Ｏ系無鉛低融点ガラス。
  2. ３０℃～３００℃における熱膨張係数が８０×１０-7／℃　～　１３０×１０-7／℃、軟化点が４００℃以上５５０℃以下であることを特徴とする請求項１に記載の無鉛低融点ガラス。
  3. 質量％で、ＳｉＯ2を２～１４、Ｂ2Ｏ3を１９～２７、ＺｎＯを２８～４２、ＲＯを１０～２７、Ｒ2Ｏを８～１５含むことを特徴とする、請求項１または請求項２に記載の無鉛低融点ガラス。
  4. 請求項１または請求項２の無鉛低融点ガラスを含むことを特徴とする導電性ペースト。
  5. 請求項１または請求項２の無鉛低融点ガラスを含むことを特徴とする太陽電池素子。
  6. 請求項１または請求項２の無鉛低融点ガラスを含むことを特徴とする電子材料用基板。
PCT/JP2011/056526 2010-03-28 2011-03-18 低融点ガラス組成物及びそれを用いた導電性ペースト材料 WO2011122369A1 (ja)