WO2011104501A2 - Ensemble panneaux composites insonorisants contenant des matières à changement de phase - Google Patents

Ensemble panneaux composites insonorisants contenant des matières à changement de phase Download PDF

Info

Publication number
WO2011104501A2
WO2011104501A2 PCT/GB2011/000245 GB2011000245W WO2011104501A2 WO 2011104501 A2 WO2011104501 A2 WO 2011104501A2 GB 2011000245 W GB2011000245 W GB 2011000245W WO 2011104501 A2 WO2011104501 A2 WO 2011104501A2
Authority
WO
WIPO (PCT)
Prior art keywords
panel assembly
composite panel
assembly according
acoustic
acoustic composite
Prior art date
Application number
PCT/GB2011/000245
Other languages
English (en)
Other versions
WO2011104501A3 (fr
Inventor
Michael Trevor Berry
Janet Susan Scanlon
Original Assignee
Michael Trevor Berry
Janet Susan Scanlon
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from GBGB1003004.7A external-priority patent/GB201003004D0/en
Priority claimed from GB1015418A external-priority patent/GB2474544A/en
Application filed by Michael Trevor Berry, Janet Susan Scanlon filed Critical Michael Trevor Berry
Publication of WO2011104501A2 publication Critical patent/WO2011104501A2/fr
Publication of WO2011104501A3 publication Critical patent/WO2011104501A3/fr

Abstract

L'invention concerne un carreau insonorisant qui comprend une plaque comportant des perforations et une région intérieure, la région intérieure comprenant une matière de remplissage et une barrière acoustique, et la matière de remplissage étant une matière de stockage de chaleur latente. Cette matière de remplissage peut être placée dans une ou plusieurs première(s) région(s) de la plaque, et les perforations peuvent être formées dans une ou plusieurs deuxième(s) région(s) de la plaque. La ou les première(s) région(s) peu(ven)t être séparée(s) de la ou des deuxième(s) région(s) par une barrière. La première région peut se situer autour d'une région périphérique de la plaque, et la deuxième région peut constituer une région centrale de la plaque. La ou les première(s) région(s) peu(ven)t constituer une ou plusieurs partie(s) de la plaque n'incluant par la ou les deuxième(s) région(s). La plaque peut comprendre une pluralité de parties ondulées, la matière de remplissage étant placée dans des espaces formés par la structure centrale ondulée et des perforations de la région de la plaque se situant entre les parties ondulées. La barrière acoustique peut être en contact avec la partie de la plaque comportant les perforations. La barrière acoustique peut être un matelas, un molleton ou un tapis acoustique. La matière de stockage de chaleur latente peut comprendre du ciment magnésien et une matière à changement de phase, le ciment magnésien étant formé à partir d'oxyde de magnésium, de chlorure de magnésium et d'eau. En particulier, le rapport molaire chlorure de magnésium/eau est supérieur ou égal à 1:17, ce qui correspond à un état de dissolution du chlorure de magnésium dans l'eau et permet d'obtenir une solution présentant une valeur de Baume inférieure ou égale à 26°, respectivement. Le rapport molaire chlorure de magnésium/oxyde de magnésium est compris dans la plage d'environ 1:1 à environ 1:5. La matière de stockage de chaleur latente peut comprendre en outre des matières de charge et/ou des agents intumescents, et/ou des liants secondaires. La matière de stockage de chaleur latente peut comprendre un liant de PFA et une matière à changement de phase, le liant incluant une poudre inerte sèche, du phosphogypse, un sel alcalin d'un métal quelconque et de l'eau. Cette matière de stockage de chaleur latente peut comprendre en outre des matières de charge et/ou des agents intumescents.
PCT/GB2011/000245 2010-02-23 2011-02-23 Ensemble panneaux composites insonorisants contenant des matières à changement de phase WO2011104501A2 (fr)

Applications Claiming Priority (18)

Application Number Priority Date Filing Date Title
GBGB1003004.7A GB201003004D0 (en) 2009-10-15 2010-02-23 Acoustic tile comprising phase change material
GB1003004.7 2010-02-23
GB1006127.3 2010-04-13
GBGB1006127.3A GB201006127D0 (en) 2009-10-15 2010-04-13 Phase change materials with improved fire-retardant properties
GB1006119.0 2010-04-13
GBGB1006119.0A GB201006119D0 (en) 2009-10-15 2010-04-13 Phase change materials with improved fire-retardant properties
GB1008025A GB2474534A (en) 2009-10-15 2010-05-14 Latent heat storage materials
GB1008025.7 2010-05-14
GB1008191.7 2010-05-17
GB201008191A GB2468231B (en) 2009-10-15 2010-05-17 Encasements comprising phase change materials
GB1010853.8 2010-06-28
GB201010853A GB2467886B (en) 2009-10-15 2010-06-28 Acoustic tile comprising phase change materials
GB1011530.1 2010-07-08
GB201011530A GB201011530D0 (en) 2010-07-08 2010-07-08 Encasements comprising phase change materials
GB1015418A GB2474544A (en) 2009-10-15 2010-09-15 Latent heat storage panel
GB1015418.5 2010-09-15
GB1017444.9 2010-10-15
GB1017444A GB2474578A (en) 2009-10-15 2010-10-15 Latent heat storage material formulations

Publications (2)

Publication Number Publication Date
WO2011104501A2 true WO2011104501A2 (fr) 2011-09-01
WO2011104501A3 WO2011104501A3 (fr) 2011-10-27

Family

ID=42712110

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/GB2011/000245 WO2011104501A2 (fr) 2010-02-23 2011-02-23 Ensemble panneaux composites insonorisants contenant des matières à changement de phase

Country Status (2)

Country Link
GB (1) GB201011530D0 (fr)
WO (1) WO2011104501A2 (fr)

Cited By (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10367948B2 (en) 2017-01-13 2019-07-30 Shure Acquisition Holdings, Inc. Post-mixing acoustic echo cancellation systems and methods
USD865723S1 (en) 2015-04-30 2019-11-05 Shure Acquisition Holdings, Inc Array microphone assembly
EE01478U1 (et) * 2018-09-06 2019-11-15 Aikkon Acoustic Oue Moodul modulaarse akustilise ripplaesüsteemi jaoks
US10655939B1 (en) 2016-02-10 2020-05-19 Consolidate Nuclear Security, LLC Thermal protection barrier for delaying access
US10728653B2 (en) 2013-03-01 2020-07-28 Clearone, Inc. Ceiling tile microphone
USD944776S1 (en) 2020-05-05 2022-03-01 Shure Acquisition Holdings, Inc. Audio device
US11297426B2 (en) 2019-08-23 2022-04-05 Shure Acquisition Holdings, Inc. One-dimensional array microphone with improved directivity
US11297423B2 (en) 2018-06-15 2022-04-05 Shure Acquisition Holdings, Inc. Endfire linear array microphone
US11303981B2 (en) 2019-03-21 2022-04-12 Shure Acquisition Holdings, Inc. Housings and associated design features for ceiling array microphones
US11302347B2 (en) 2019-05-31 2022-04-12 Shure Acquisition Holdings, Inc. Low latency automixer integrated with voice and noise activity detection
US11310596B2 (en) 2018-09-20 2022-04-19 Shure Acquisition Holdings, Inc. Adjustable lobe shape for array microphones
US11400688B1 (en) 2016-02-10 2022-08-02 Consolidated Nuclear Security, LLC Thermal protection barrier
US11438691B2 (en) 2019-03-21 2022-09-06 Shure Acquisition Holdings, Inc. Auto focus, auto focus within regions, and auto placement of beamformed microphone lobes with inhibition functionality
US11445294B2 (en) 2019-05-23 2022-09-13 Shure Acquisition Holdings, Inc. Steerable speaker array, system, and method for the same
US11523212B2 (en) 2018-06-01 2022-12-06 Shure Acquisition Holdings, Inc. Pattern-forming microphone array
US11552611B2 (en) 2020-02-07 2023-01-10 Shure Acquisition Holdings, Inc. System and method for automatic adjustment of reference gain
US11558693B2 (en) 2019-03-21 2023-01-17 Shure Acquisition Holdings, Inc. Auto focus, auto focus within regions, and auto placement of beamformed microphone lobes with inhibition and voice activity detection functionality
US11678109B2 (en) 2015-04-30 2023-06-13 Shure Acquisition Holdings, Inc. Offset cartridge microphones
US11706562B2 (en) 2020-05-29 2023-07-18 Shure Acquisition Holdings, Inc. Transducer steering and configuration systems and methods using a local positioning system
US11785380B2 (en) 2021-01-28 2023-10-10 Shure Acquisition Holdings, Inc. Hybrid audio beamforming system
WO2023242332A1 (fr) * 2022-06-17 2023-12-21 Norsk Hydro Asa Produit composite
US11891805B2 (en) 2018-12-18 2024-02-06 Csr Building Products Limited Panel mounting system

Citations (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3969291A (en) 1974-03-06 1976-07-13 Sumitomo Chemical Company, Limited Intumescent fire-retardant coating compositions containing amide-polyphosphates
GB2007689A (en) 1977-10-10 1979-05-23 Montedison Spa Intumescent paints
EP0139401A1 (fr) 1983-08-23 1985-05-02 Dixon International Limited Matériau intumescent
US5435376A (en) 1992-08-17 1995-07-25 Microtek Laboratories, Inc. Flame resistant microencapsulated phase change materials
GB2344341A (en) 1998-12-02 2000-06-07 Anthony Michael Psyllides Forming mixture and constructional material
US6099894A (en) 1998-07-27 2000-08-08 Frisby Technologies, Inc. Gel-coated microcapsules
US20030211796A1 (en) 2002-05-13 2003-11-13 Basf Akitengesellshaft Flame-inhibiting finishing of articles containing organic latent-heat storage materials
US20050040152A1 (en) 2002-02-01 2005-02-24 Markus Koschenz Thermoactive wall and ceiling element
WO2008063904A2 (fr) 2006-11-16 2008-05-29 Maya Magstone, Inc. Ciment à l'oxychlorure de magnésium
WO2009059908A2 (fr) 2007-11-07 2009-05-14 Basf Se Compositions de stockage thermique et fabrication de ces dernières
EP2060389A1 (fr) 2007-11-14 2009-05-20 Van Cauwenberge NV Panneaux stratifiés pour des systèmes de revêtements de sol, de mur et de plafond

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE102004005912A1 (de) * 2004-02-05 2005-08-25 Basf Ag Schallabsorbierende Formkörper
DE102007025303B4 (de) * 2007-05-30 2014-06-26 Haacke Treuhand Gmbh Bauelement für die Innendämmung von Gebäuden und Verfahren zu seiner Herstellung
DE202008007790U1 (de) * 2008-06-11 2009-10-29 Tac Technologieagentur Chemnitz Gmbh Wärmespeicheranordnung

Patent Citations (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3969291A (en) 1974-03-06 1976-07-13 Sumitomo Chemical Company, Limited Intumescent fire-retardant coating compositions containing amide-polyphosphates
GB2007689A (en) 1977-10-10 1979-05-23 Montedison Spa Intumescent paints
EP0139401A1 (fr) 1983-08-23 1985-05-02 Dixon International Limited Matériau intumescent
US5435376A (en) 1992-08-17 1995-07-25 Microtek Laboratories, Inc. Flame resistant microencapsulated phase change materials
US6171647B1 (en) 1998-07-27 2001-01-09 Frisby Technologies, Inc. Gel-coated microcapsules
US6099894A (en) 1998-07-27 2000-08-08 Frisby Technologies, Inc. Gel-coated microcapsules
US6270836B1 (en) 1998-07-27 2001-08-07 Frisby Technologies, Inc. Gel-coated microcapsules
GB2344341A (en) 1998-12-02 2000-06-07 Anthony Michael Psyllides Forming mixture and constructional material
US20050040152A1 (en) 2002-02-01 2005-02-24 Markus Koschenz Thermoactive wall and ceiling element
US20030211796A1 (en) 2002-05-13 2003-11-13 Basf Akitengesellshaft Flame-inhibiting finishing of articles containing organic latent-heat storage materials
WO2008063904A2 (fr) 2006-11-16 2008-05-29 Maya Magstone, Inc. Ciment à l'oxychlorure de magnésium
WO2009059908A2 (fr) 2007-11-07 2009-05-14 Basf Se Compositions de stockage thermique et fabrication de ces dernières
EP2060389A1 (fr) 2007-11-14 2009-05-20 Van Cauwenberge NV Panneaux stratifiés pour des systèmes de revêtements de sol, de mur et de plafond

Cited By (40)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11601749B1 (en) 2013-03-01 2023-03-07 Clearone, Inc. Ceiling tile microphone system
US11240597B1 (en) 2013-03-01 2022-02-01 Clearone, Inc. Ceiling tile beamforming microphone array system
US11743638B2 (en) 2013-03-01 2023-08-29 Clearone, Inc. Ceiling-tile beamforming microphone array system with auto voice tracking
US11743639B2 (en) 2013-03-01 2023-08-29 Clearone, Inc. Ceiling-tile beamforming microphone array system with combined data-power connection
US10728653B2 (en) 2013-03-01 2020-07-28 Clearone, Inc. Ceiling tile microphone
US11303996B1 (en) 2013-03-01 2022-04-12 Clearone, Inc. Ceiling tile microphone
US11240598B2 (en) 2013-03-01 2022-02-01 Clearone, Inc. Band-limited beamforming microphone array with acoustic echo cancellation
US11297420B1 (en) 2013-03-01 2022-04-05 Clearone, Inc. Ceiling tile microphone
US11950050B1 (en) 2013-03-01 2024-04-02 Clearone, Inc. Ceiling tile microphone
US11678109B2 (en) 2015-04-30 2023-06-13 Shure Acquisition Holdings, Inc. Offset cartridge microphones
US11832053B2 (en) 2015-04-30 2023-11-28 Shure Acquisition Holdings, Inc. Array microphone system and method of assembling the same
US11310592B2 (en) 2015-04-30 2022-04-19 Shure Acquisition Holdings, Inc. Array microphone system and method of assembling the same
USD940116S1 (en) 2015-04-30 2022-01-04 Shure Acquisition Holdings, Inc. Array microphone assembly
USD865723S1 (en) 2015-04-30 2019-11-05 Shure Acquisition Holdings, Inc Array microphone assembly
US11400688B1 (en) 2016-02-10 2022-08-02 Consolidated Nuclear Security, LLC Thermal protection barrier
US10655939B1 (en) 2016-02-10 2020-05-19 Consolidate Nuclear Security, LLC Thermal protection barrier for delaying access
US10367948B2 (en) 2017-01-13 2019-07-30 Shure Acquisition Holdings, Inc. Post-mixing acoustic echo cancellation systems and methods
US11477327B2 (en) 2017-01-13 2022-10-18 Shure Acquisition Holdings, Inc. Post-mixing acoustic echo cancellation systems and methods
US11800281B2 (en) 2018-06-01 2023-10-24 Shure Acquisition Holdings, Inc. Pattern-forming microphone array
US11523212B2 (en) 2018-06-01 2022-12-06 Shure Acquisition Holdings, Inc. Pattern-forming microphone array
US11770650B2 (en) 2018-06-15 2023-09-26 Shure Acquisition Holdings, Inc. Endfire linear array microphone
US11297423B2 (en) 2018-06-15 2022-04-05 Shure Acquisition Holdings, Inc. Endfire linear array microphone
EE01478U1 (et) * 2018-09-06 2019-11-15 Aikkon Acoustic Oue Moodul modulaarse akustilise ripplaesüsteemi jaoks
US11310596B2 (en) 2018-09-20 2022-04-19 Shure Acquisition Holdings, Inc. Adjustable lobe shape for array microphones
US11891805B2 (en) 2018-12-18 2024-02-06 Csr Building Products Limited Panel mounting system
US11558693B2 (en) 2019-03-21 2023-01-17 Shure Acquisition Holdings, Inc. Auto focus, auto focus within regions, and auto placement of beamformed microphone lobes with inhibition and voice activity detection functionality
US11303981B2 (en) 2019-03-21 2022-04-12 Shure Acquisition Holdings, Inc. Housings and associated design features for ceiling array microphones
US11438691B2 (en) 2019-03-21 2022-09-06 Shure Acquisition Holdings, Inc. Auto focus, auto focus within regions, and auto placement of beamformed microphone lobes with inhibition functionality
US11778368B2 (en) 2019-03-21 2023-10-03 Shure Acquisition Holdings, Inc. Auto focus, auto focus within regions, and auto placement of beamformed microphone lobes with inhibition functionality
US11800280B2 (en) 2019-05-23 2023-10-24 Shure Acquisition Holdings, Inc. Steerable speaker array, system and method for the same
US11445294B2 (en) 2019-05-23 2022-09-13 Shure Acquisition Holdings, Inc. Steerable speaker array, system, and method for the same
US11688418B2 (en) 2019-05-31 2023-06-27 Shure Acquisition Holdings, Inc. Low latency automixer integrated with voice and noise activity detection
US11302347B2 (en) 2019-05-31 2022-04-12 Shure Acquisition Holdings, Inc. Low latency automixer integrated with voice and noise activity detection
US11297426B2 (en) 2019-08-23 2022-04-05 Shure Acquisition Holdings, Inc. One-dimensional array microphone with improved directivity
US11750972B2 (en) 2019-08-23 2023-09-05 Shure Acquisition Holdings, Inc. One-dimensional array microphone with improved directivity
US11552611B2 (en) 2020-02-07 2023-01-10 Shure Acquisition Holdings, Inc. System and method for automatic adjustment of reference gain
USD944776S1 (en) 2020-05-05 2022-03-01 Shure Acquisition Holdings, Inc. Audio device
US11706562B2 (en) 2020-05-29 2023-07-18 Shure Acquisition Holdings, Inc. Transducer steering and configuration systems and methods using a local positioning system
US11785380B2 (en) 2021-01-28 2023-10-10 Shure Acquisition Holdings, Inc. Hybrid audio beamforming system
WO2023242332A1 (fr) * 2022-06-17 2023-12-21 Norsk Hydro Asa Produit composite

Also Published As

Publication number Publication date
GB201011530D0 (en) 2010-08-25
WO2011104501A3 (fr) 2011-10-27

Similar Documents

Publication Publication Date Title
WO2011104501A2 (fr) Ensemble panneaux composites insonorisants contenant des matières à changement de phase
GB2467886A (en) Acoustic tile comprising phase change material
GB2474578A (en) Latent heat storage material formulations
US10364185B2 (en) Light-weight, fire-resistant composition and assembly
US4723385A (en) Fire resistant wall construction
JP2010007326A (ja) 耐火被覆構造
CN102765959A (zh) 一种蓄能节能型泡沫石膏水泥复合材料及其制备方法
KR101932135B1 (ko) 건축물 외벽 단열층의 화재확산 방지를 위한 내화성 표면마감재의 조성물 및 시공방법
CN202347723U (zh) 轻质水泥复合环保隔音墙板
JP2007196465A (ja) 不燃性蓄熱パネル
CN102322111B (zh) 一种氯氧镁水泥发泡轻质墙板及制备方法和设备
CA3010162A1 (fr) Panneaux de construction resistants au feu pourvus de quantites accrues d'additifs antiretrait et de densites reduites
KR100760149B1 (ko) 건축용 내장재 제조방법
JPH07300913A (ja) 軽量断熱防火パネル
CN202347725U (zh) 一种新型保温隔音复合墙板
KR102193350B1 (ko) 글라스 울 복합패널
JP2008279713A (ja) 不燃板及び不燃板の製造方法
JP2014109119A (ja) 中空壁の防火区画貫通部構造
JP2915800B2 (ja) 木造建築の外断熱用パネルおよび外断熱構造
JPH0640729Y2 (ja) プラスチック外装壁構造
CN101285335B (zh) 外墙内隔热保温的酚醛-石膏围护构件材料
JPH032452A (ja) 住宅用軽量部材パネル
TR2024002022U5 (tr) Poli̇i̇zosi̇yanurat duvar isi yalitim si̇stemi̇
CN101585681A (zh) 中空隔板原料
JPH066559U (ja) 耐火屋根構造

Legal Events

Date Code Title Description
NENP Non-entry into the national phase in:

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 11711115

Country of ref document: EP

Kind code of ref document: A2