Classifications

• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
  • C07C69/00—Esters of carboxylic acids; Esters of carbonic or haloformic acids
  • C07C69/52—Esters of acyclic unsaturated carboxylic acids having the esterified carboxyl group bound to an acyclic carbon atom
  • C07C69/533—Monocarboxylic acid esters having only one carbon-to-carbon double bond
  • C07C69/54—Acrylic acid esters; Methacrylic acid esters
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
  • C07C43/00—Ethers; Compounds having groups, groups or groups
  • C07C43/02—Ethers
  • C07C43/20—Ethers having an ether-oxygen atom bound to a carbon atom of a six-membered aromatic ring
  • C07C43/215—Ethers having an ether-oxygen atom bound to a carbon atom of a six-membered aromatic ring having unsaturation outside the six-membered aromatic rings
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
  • C07C59/00—Compounds having carboxyl groups bound to acyclic carbon atoms and containing any of the groups OH, O—metal, —CHO, keto, ether, groups, groups, or groups
  • C07C59/40—Unsaturated compounds
  • C07C59/58—Unsaturated compounds containing ether groups, groups, groups, or groups
  • C07C59/72—Unsaturated compounds containing ether groups, groups, groups, or groups containing six-membered aromatic rings and other rings
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07D—HETEROCYCLIC COMPOUNDS
  • C07D207/00—Heterocyclic compounds containing five-membered rings not condensed with other rings, with one nitrogen atom as the only ring hetero atom
  • C07D207/02—Heterocyclic compounds containing five-membered rings not condensed with other rings, with one nitrogen atom as the only ring hetero atom with only hydrogen or carbon atoms directly attached to the ring nitrogen atom
  • C07D207/44—Heterocyclic compounds containing five-membered rings not condensed with other rings, with one nitrogen atom as the only ring hetero atom with only hydrogen or carbon atoms directly attached to the ring nitrogen atom having three double bonds between ring members or between ring members and non-ring members
  • C07D207/444—Heterocyclic compounds containing five-membered rings not condensed with other rings, with one nitrogen atom as the only ring hetero atom with only hydrogen or carbon atoms directly attached to the ring nitrogen atom having three double bonds between ring members or between ring members and non-ring members having two doubly-bound oxygen atoms directly attached in positions 2 and 5
  • C07D207/448—Heterocyclic compounds containing five-membered rings not condensed with other rings, with one nitrogen atom as the only ring hetero atom with only hydrogen or carbon atoms directly attached to the ring nitrogen atom having three double bonds between ring members or between ring members and non-ring members having two doubly-bound oxygen atoms directly attached in positions 2 and 5 with only hydrogen atoms or radicals containing only hydrogen and carbon atoms directly attached to other ring carbon atoms, e.g. maleimide
  • C07D207/452—Heterocyclic compounds containing five-membered rings not condensed with other rings, with one nitrogen atom as the only ring hetero atom with only hydrogen or carbon atoms directly attached to the ring nitrogen atom having three double bonds between ring members or between ring members and non-ring members having two doubly-bound oxygen atoms directly attached in positions 2 and 5 with only hydrogen atoms or radicals containing only hydrogen and carbon atoms directly attached to other ring carbon atoms, e.g. maleimide with hydrocarbon radicals, substituted by hetero atoms, directly attached to the ring nitrogen atom
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07D—HETEROCYCLIC COMPOUNDS
  • C07D249/00—Heterocyclic compounds containing five-membered rings having three nitrogen atoms as the only ring hetero atoms
  • C07D249/02—Heterocyclic compounds containing five-membered rings having three nitrogen atoms as the only ring hetero atoms not condensed with other rings
  • C07D249/08—1,2,4-Triazoles; Hydrogenated 1,2,4-triazoles
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07D—HETEROCYCLIC COMPOUNDS
  • C07D333/00—Heterocyclic compounds containing five-membered rings having one sulfur atom as the only ring hetero atom
  • C07D333/02—Heterocyclic compounds containing five-membered rings having one sulfur atom as the only ring hetero atom not condensed with other rings
  • C07D333/04—Heterocyclic compounds containing five-membered rings having one sulfur atom as the only ring hetero atom not condensed with other rings not substituted on the ring sulphur atom
  • C07D333/06—Heterocyclic compounds containing five-membered rings having one sulfur atom as the only ring hetero atom not condensed with other rings not substituted on the ring sulphur atom with only hydrogen atoms, hydrocarbon or substituted hydrocarbon radicals, directly attached to the ring carbon atoms
  • C07D333/14—Radicals substituted by singly bound hetero atoms other than halogen
  • C07D333/16—Radicals substituted by singly bound hetero atoms other than halogen by oxygen atoms
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07D—HETEROCYCLIC COMPOUNDS
  • C07D333/00—Heterocyclic compounds containing five-membered rings having one sulfur atom as the only ring hetero atom
  • C07D333/02—Heterocyclic compounds containing five-membered rings having one sulfur atom as the only ring hetero atom not condensed with other rings
  • C07D333/04—Heterocyclic compounds containing five-membered rings having one sulfur atom as the only ring hetero atom not condensed with other rings not substituted on the ring sulphur atom
  • C07D333/06—Heterocyclic compounds containing five-membered rings having one sulfur atom as the only ring hetero atom not condensed with other rings not substituted on the ring sulphur atom with only hydrogen atoms, hydrocarbon or substituted hydrocarbon radicals, directly attached to the ring carbon atoms
  • C07D333/14—Radicals substituted by singly bound hetero atoms other than halogen
  • C07D333/18—Radicals substituted by singly bound hetero atoms other than halogen by sulfur atoms
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07D—HETEROCYCLIC COMPOUNDS
  • C07D403/00—Heterocyclic compounds containing two or more hetero rings, having nitrogen atoms as the only ring hetero atoms, not provided for by group C07D401/00
  • C07D403/14—Heterocyclic compounds containing two or more hetero rings, having nitrogen atoms as the only ring hetero atoms, not provided for by group C07D401/00 containing three or more hetero rings
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07D—HETEROCYCLIC COMPOUNDS
  • C07D417/00—Heterocyclic compounds containing two or more hetero rings, at least one ring having nitrogen and sulfur atoms as the only ring hetero atoms, not provided for by group C07D415/00
  • C07D417/14—Heterocyclic compounds containing two or more hetero rings, at least one ring having nitrogen and sulfur atoms as the only ring hetero atoms, not provided for by group C07D415/00 containing three or more hetero rings
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07D—HETEROCYCLIC COMPOUNDS
  • C07D471/00—Heterocyclic compounds containing nitrogen atoms as the only ring hetero atoms in the condensed system, at least one ring being a six-membered ring with one nitrogen atom, not provided for by groups C07D451/00 - C07D463/00
  • C07D471/22—Heterocyclic compounds containing nitrogen atoms as the only ring hetero atoms in the condensed system, at least one ring being a six-membered ring with one nitrogen atom, not provided for by groups C07D451/00 - C07D463/00 in which the condensed systems contains four or more hetero rings
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07D—HETEROCYCLIC COMPOUNDS
  • C07D487/00—Heterocyclic compounds containing nitrogen atoms as the only ring hetero atoms in the condensed system, not provided for by groups C07D451/00 - C07D477/00
  • C07D487/02—Heterocyclic compounds containing nitrogen atoms as the only ring hetero atoms in the condensed system, not provided for by groups C07D451/00 - C07D477/00 in which the condensed system contains two hetero rings
  • C07D487/04—Ortho-condensed systems
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07D—HETEROCYCLIC COMPOUNDS
  • C07D495/00—Heterocyclic compounds containing in the condensed system at least one hetero ring having sulfur atoms as the only ring hetero atoms
  • C07D495/02—Heterocyclic compounds containing in the condensed system at least one hetero ring having sulfur atoms as the only ring hetero atoms in which the condensed system contains two hetero rings
  • C07D495/04—Ortho-condensed systems
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07D—HETEROCYCLIC COMPOUNDS
  • C07D519/00—Heterocyclic compounds containing more than one system of two or more relevant hetero rings condensed among themselves or condensed with a common carbocyclic ring system not provided for in groups C07D453/00 or C07D455/00
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
  • C09K11/00—Luminescent materials, e.g. electroluminescent or chemiluminescent
  • C09K11/06—Luminescent materials, e.g. electroluminescent or chemiluminescent containing organic luminescent materials
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K50/00—Organic light-emitting devices
  • H10K50/10—OLEDs or polymer light-emitting diodes [PLED]
  • H10K50/11—OLEDs or polymer light-emitting diodes [PLED] characterised by the electroluminescent [EL] layers
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K85/00—Organic materials used in the body or electrodes of devices covered by this subclass
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K85/00—Organic materials used in the body or electrodes of devices covered by this subclass
  • H10K85/10—Organic polymers or oligomers
  • H10K85/111—Organic polymers or oligomers comprising aromatic, heteroaromatic, or aryl chains, e.g. polyaniline, polyphenylene or polyphenylene vinylene
  • H10K85/115—Polyfluorene; Derivatives thereof
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K85/00—Organic materials used in the body or electrodes of devices covered by this subclass
  • H10K85/60—Organic compounds having low molecular weight
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K85/00—Organic materials used in the body or electrodes of devices covered by this subclass
  • H10K85/60—Organic compounds having low molecular weight
  • H10K85/615—Polycyclic condensed aromatic hydrocarbons, e.g. anthracene
  • H10K85/626—Polycyclic condensed aromatic hydrocarbons, e.g. anthracene containing more than one polycyclic condensed aromatic rings, e.g. bis-anthracene
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K85/00—Organic materials used in the body or electrodes of devices covered by this subclass
  • H10K85/60—Organic compounds having low molecular weight
  • H10K85/649—Aromatic compounds comprising a hetero atom
  • H10K85/654—Aromatic compounds comprising a hetero atom comprising only nitrogen as heteroatom
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K85/00—Organic materials used in the body or electrodes of devices covered by this subclass
  • H10K85/60—Organic compounds having low molecular weight
  • H10K85/649—Aromatic compounds comprising a hetero atom
  • H10K85/655—Aromatic compounds comprising a hetero atom comprising only sulfur as heteroatom
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K85/00—Organic materials used in the body or electrodes of devices covered by this subclass
  • H10K85/60—Organic compounds having low molecular weight
  • H10K85/649—Aromatic compounds comprising a hetero atom
  • H10K85/656—Aromatic compounds comprising a hetero atom comprising two or more different heteroatoms per ring
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K85/00—Organic materials used in the body or electrodes of devices covered by this subclass
  • H10K85/60—Organic compounds having low molecular weight
  • H10K85/649—Aromatic compounds comprising a hetero atom
  • H10K85/657—Polycyclic condensed heteroaromatic hydrocarbons
  • H10K85/6572—Polycyclic condensed heteroaromatic hydrocarbons comprising only nitrogen in the heteroaromatic polycondensed ring system, e.g. phenanthroline or carbazole
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K85/00—Organic materials used in the body or electrodes of devices covered by this subclass
  • H10K85/60—Organic compounds having low molecular weight
  • H10K85/649—Aromatic compounds comprising a hetero atom
  • H10K85/657—Polycyclic condensed heteroaromatic hydrocarbons
  • H10K85/6576—Polycyclic condensed heteroaromatic hydrocarbons comprising only sulfur in the heteroaromatic polycondensed ring system, e.g. benzothiophene
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
  • C07C2603/00—Systems containing at least three condensed rings
  • C07C2603/93—Spiro compounds
  • C07C2603/94—Spiro compounds containing "free" spiro atoms
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
  • C09K2211/00—Chemical nature of organic luminescent or tenebrescent compounds
  • C09K2211/14—Macromolecular compounds
  • C09K2211/1408—Carbocyclic compounds
  • C09K2211/1416—Condensed systems
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
  • C09K2211/00—Chemical nature of organic luminescent or tenebrescent compounds
  • C09K2211/14—Macromolecular compounds
  • C09K2211/1408—Carbocyclic compounds
  • C09K2211/1425—Non-condensed systems
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
  • C09K2211/00—Chemical nature of organic luminescent or tenebrescent compounds
  • C09K2211/14—Macromolecular compounds
  • C09K2211/1441—Heterocyclic
  • C09K2211/1458—Heterocyclic containing sulfur as the only heteroatom
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
  • C09K2211/00—Chemical nature of organic luminescent or tenebrescent compounds
  • C09K2211/14—Macromolecular compounds
  • C09K2211/1441—Heterocyclic
  • C09K2211/1466—Heterocyclic containing nitrogen as the only heteroatom
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
  • C09K2211/00—Chemical nature of organic luminescent or tenebrescent compounds
  • C09K2211/14—Macromolecular compounds
  • C09K2211/1441—Heterocyclic
  • C09K2211/1475—Heterocyclic containing nitrogen and oxygen as heteroatoms
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K10/00—Organic devices specially adapted for rectifying, amplifying, oscillating or switching; Organic capacitors or resistors having potential barriers
  • H10K10/40—Organic transistors
  • H10K10/46—Field-effect transistors, e.g. organic thin-film transistors [OTFT]
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K2102/00—Constructional details relating to the organic devices covered by this subclass
  • H10K2102/10—Transparent electrodes, e.g. using graphene
  • H10K2102/101—Transparent electrodes, e.g. using graphene comprising transparent conductive oxides [TCO]
  • H10K2102/103—Transparent electrodes, e.g. using graphene comprising transparent conductive oxides [TCO] comprising indium oxides, e.g. ITO
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K30/00—Organic devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K30/00—Organic devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation
  • H10K30/50—Photovoltaic [PV] devices
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K50/00—Organic light-emitting devices
  • H10K50/10—OLEDs or polymer light-emitting diodes [PLED]
  • H10K50/14—Carrier transporting layers
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K50/00—Organic light-emitting devices
  • H10K50/80—Constructional details
  • H10K50/868—Arrangements for polarized light emission
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K85/00—Organic materials used in the body or electrodes of devices covered by this subclass
  • H10K85/10—Organic polymers or oligomers
  • H10K85/111—Organic polymers or oligomers comprising aromatic, heteroaromatic, or aryl chains, e.g. polyaniline, polyphenylene or polyphenylene vinylene
  • H10K85/113—Heteroaromatic compounds comprising sulfur or selene, e.g. polythiophene
  • H10K85/1135—Polyethylene dioxythiophene [PEDOT]; Derivatives thereof
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K85/00—Organic materials used in the body or electrodes of devices covered by this subclass
  • H10K85/10—Organic polymers or oligomers
  • H10K85/141—Organic polymers or oligomers comprising aliphatic or olefinic chains, e.g. poly N-vinylcarbazol, PVC or PTFE
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
  • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
  • Y02E10/00—Energy generation through renewable energy sources
  • Y02E10/50—Photovoltaic [PV] energy
  • Y02E10/549—Organic PV cells

Definitions

• This invention relates to electroluminescent materials.
• A represents a linear aromatic molecular core
• S represents flexible spacer units
• B represents crosslinking groups such as methacrylate groups
• A represents a linear aromatic molecular core
• S represents flexible spacer units
• B represents crosslinking groups such as methacrylate groups
• these reactive mesogen materials may be patterned into the active light emitting layers in electroluminescent devices such as organic light emitting diodes (OLEDS) and organic diode lasers.
• OLEDS organic light emitting diodes
• the core aromatic structure A is a fluorene ring system:
• the present invention provides materials of that general structure that have commercially useful lifetimes.
• the invention comprises OLED compounds of the general structure:
• rod-like nuclei A comprise a condensed aromatic ring structure in turn comprising fluorene ring structures condensed with at least one additional fluorene ring structures wherein the fluorene ring systems comprised by the condensed aromatic structure are substituted at the 9-position, and in which the 9-positions of the fluorenes are not susceptible to oxidation.
• the additional fluorine ring systems may comprise benzene, naphthalene, indene, or other fluorene ring systems.
• S may represent a flexible spacer comprising a chain of single bonded atoms.
• the chain may comprise an alkyl chain.
• the alkyl chain may contain one or more hetero atoms.
• B may represent a crosslinking chemical group, which may be a methacrylate group, a l,4-pentadien-3-yl group, an ethacrylate group, a vinyloxy group, an alk lvinyloxy group, an ethylmaleato group, an ethylfumarato group, an N-maleimido group, a vinylmaleato group, a vinylfumarato group, or a N-(2-vinyloxymaleimido) group.
• a crosslinking chemical group which may be a methacrylate group, a l,4-pentadien-3-yl group, an ethacrylate group, a vinyloxy group, an alk lvinyloxy group, an ethylmaleato group, an ethylfumarato group, an N-maleimido group, a vinylmaleato group, a vinylfumarato group, or a N-(2-vinyl
• A may represent a substantially linear, covalently bonded chain, which may be a chain of aromatic or heteroaromatic diradicals represented by the general formula:
• the Ar may each be independently chosen from an aromatic or heteroaromatic diradical, and may comprise a 1 ,4-phenylene, a biphenyl-4,4'-diyl, a terphen-4,4"-diyl, a naphthalene- 1,4-diyl, a thiophene-2,5-diyl, a pyrimidine-2,5-diyl, a perylene-3,10-diyl, a pyrene-2,7-diyl, a 2,2'-dithiophen-5,5'-diyl, an oxazole-2,5-diyl, a thieno[3,2- b]thiophene-2,5-diyl, a dithieno[3,2-b:2',3'-d]thiophene-2,6-diyl, a thiazolo[5,4- d]thiazole-2,5
• Ar may also be selected from the diradicals:
• R is an alkyl group and may be chosen from methyl, ethyl, propyl, butyl, isopropyl, sec-butyl, isobutyl, tert-butyl, 2-amyl, 3-amyl, 2- methyl-2 -butyl, 3-methyl-3-amyl, 3-ethyl-3-amyl, or neo-pentyl.
• R is fluoro (yielding trifluoromethyl substituents), branched, cyclo, or straight chained alkyl groups, alkyl groups substituted with some number of fluorine groups or alkyl groups in which one or more carbons are substituted with hetero atoms.
• one or more of the fluorene ring residues in the condensed aromatic ring system may be substituted as shown in the two examples shown below:
• R is alkyl, fluorene substituted alkyl, branched alkyl, cycloalkyl, or alkyl in which one or more carbons are substituted by hetero atoms, and has the same meaning as the examples shown above.
• the invention also comprises a light emitting or charge transporting material of the general structure:
• A is a substantially rigid, rod-shaped molecular core comprising a chain of aromatic or heteroaromatic diradicals represented by the general formula:
• Fl comprises a fluorene-2,7-diyl diradical spiro substituted at the 9 position on the fluorene ring with an alicyclic ring system, wherein the alicyclic substituent has no hydrogen substituted on the two carbon atoms immediately adjacent the carbon atom at position 9 in the fluorene ring system,
• Ar is chosen independently from aromatic or heteroaromatic diradicals or single bonds
• the material may be liquid crystalline
• 'n' may be between 1 and 10.
• the material may be a polymer.
• the invention also comprises a light emitting or charge transporting polymer of the general structure:
• A is a substantially linear, covalently bonded chain comprising a chain of aromatic or heteroaromatic diradicals represented by the general formula:
• the Ar may each be independently chosen from an aromatic or heteroaromatic diradical, and may comprise a 1,4-phenylene, a biphenyl-4,4'-diyl, a terphen-4,4"-diyl, a naphthalene- 1,4-diyl, a thiophene-2,5-diyl, a pyrimidine-2,5-diyl, a perylene-3,10-diyl, a pyrene-2,7-diyl, a 2,2'-dithiophen-5,5'-diyl, an oxazole-2,5-diyl, a thieno[3,2- b]thiophene-2,5-diyl, a dithieno[3,2-b:2',3'-d]thiophene-2,6-diyl, a thiazolo[5,4- d]thiazole-2,5-d
• substituent may be independently selected for each occurrence structure from one of the following spiro or bicyclospiro groups:
• Ar may also be selected from the diradicals:
• each Fl may be independently chosen from:
• substituents may independently be one of structures 10 through 26 from above.
• R is an alkyl group and may be chosen from methyl, ethyl, propyl, butyl, isopropyl, sec-butyl, isobutyl, tert-butyl, 2-amyl, 3-amyl, 2- methyl-2-butyl, 3-methyl-3-amyl, 3-ethyl-3-amyl, or neo-pentyl.
• T are polymer chain terminating units.
• T may be independently selected from hydrogen, halogen, aryl, or aryl substituted with a cyano, hydroxyl, glycidyl ether, acrylate ester, methacrylate ester, ethenyl, ethynyl, maleimide, nadimide, trialkylsiloxy, or trifluorovinyl ether moieties.
• Three-dimensional models of the materials described above show them to be no more bulky than similar material in which the fluorene 9-positions are substituted with straight chain alkyl groups. Therefore, the nematic phase in these materials should be just as stable as in the previous materials.
• the preferred embodiment of the above materials is one in which all of the R groups are alkyls.
• the spiro[cyclopentane-l,9'-fluorene]-2',7'diyl (Structure 22), spiro[cyclohexane-l,9'-fluorene]-2 ⁇ 7'diyl (Structure 23), spiro[cycloheptane-l,9'- fluorene]-2',7'diyl (Structure 24), spiro[bicyclo[2,2,l]heptane-7,9'-fluorene]-2',7'diyl (Structure 10), or spiro[bicyclo[3,3,l]nonane-9,9'-fluorene]-2',7'diyl (Structure 11) diradicals are chosen as the Fl units in the general formula of the invention because of their symmetry and ease of synthesis.
• R substituents are the same. This is because molecules in which the R substituents are different will show positional or
• the compounds of the invention containing diradicals Fl with structures 10 through 26 may be further substituted at positions (other than those that are substituted already with R groups) on the cycloaliphatic and bicycloaliphatic rings that are joined to the fluorene ring structures at their 9-positions.
• positions other than those that are substituted already with R groups
• compounds with substituents at these other positions are less preferred because of the potential for geometrical or stereoisomerism that will complicate their purification.
• An exception is that compounds with structures with structures
• R is as above and R' are preferably selected from alkyls ranging from CH 3 - to C5H11- in chain length, are useful.
• Emitter materials of the invention in which the n subscript in the formula for A is equal to between 3 and 6 are preferred. Lower n values lead to molecules with lower light emission efficiency. Higher n values lead to molecules that are more difficult to synthesise and or more difficult to purify.
• Materials according to this invention may be mixed together to form liquid crystalline mixtures. This can be very advantageous from the standpoint of optimising the properties of the materials. For instance, individual compounds of the invention may have liquid crystal to isotropic liquid transition temperature far below their melting points (monotropic liquid crystalline phases). In device fabrication applications this can lead to glassy or supercooled liquid films of the materials that are sufficiently
• thermodynamically unstable so as to lead to the danger of crystallisation within the film and subsequent destruction of useful electronic properties.
• Mixing multiple component compounds together can depress the melting point of the resulting mixtures below the liquid crystal to isotropic liquid transition temperatures or at least sufficiently suppress crystallisation so as to eliminate this problem.
• Another advantage of using mixtures of the materials of the invention is that it may allow materials with otherwise highly useful device application properties to be used even though they a have a particular property that renders them unusable as a pure material. For instance it may be desired to prepare a light emitting polymer film having a nematic liquid crystalline structure.
• a compound of the invention may be a light emitting material of very high efficiency and possess other useful properties, but at the same time may be found to possess a smectic rather than a nematic liquid crystalline phase.
• an important aspect of the invention is the preparation of mixtures of the compounds of the invention that have this spectral relationship between the constituent components.
• compound 28, which emits in the blue region of the spectrum can serve as a host for compound 27, which is a green light emitter.
• a polymer film prepared by the UV induced crosslinking of a solution of 5% compound 27 in compound 28 will exhibit considerably less self-absorption of the green light emitted by 27 than will a film prepared by UV crosslinking of pure 27.
• Another aspect of the invention relates to the balanced transport and insertion of positive and negative charge carriers into the electrically active regions or layers of devices. As an example, a typical (prior art) OLED configuration is shown in Figure 1.
• This device contains an anode 110 usually prepared as a conductive indium-tin oxide film on a glass substrate, a hole injection layer 120 that supports facile injection of holes into the hole transporting layer 130.
• the hole-transporting layer 130 in the case of this invention is a polymerised film of a compound or a mixture of compounds of the invention that is chosen for its high mobility for holes.
• the device further consists of a cathode 160 that injects electrons into electron transporting layer 150. There may be an optional electron injection layer (not shown) between cathode 160 and electron transporting layer 150. Electron transporting layer 150 and hole transporting layer 130 insert respectively electrons and holes into light emitting layer 140 where they recombine to form excitons and then light.
• the electron- transporting layer 150 of this invention is a polymerised film of a compound or mixture of compounds of the invention that is chosen for its high mobility for electrons.
• the light-emitting layer of this invention is also a polymerised film of a compound or mixture of compounds of the invention.
• a further function of electron transporting layer 150 is to prevent holes injected into 140 from continuing onward out the other side of 140 and eventually recombining with electrons at the surface of the cathode in a non-light emissive event.
• the material(s) of 150 are chosen so as to have a HOMO (highest occupied molecular orbital) energy level that is quite low as compared to the HOMO energy level of the light emitting layer 140.
• HOMO highest occupied molecular orbital
• the light-emitting layer 140 of device 100 will perform optimally if electron and hole mobilities in the material are approximately the same. Unfortunately most of the best light emitting materials according to the invention have considerably higher hole mobilities than electron mobilities. However, the ability to produce mixtures of the materials of the invention allows compound 37 and similar compounds to be blended into the light emitting materials of the invention to form mixtures with substantially equal hole and electron mobilities. These mixtures can then be polymerised by UV exposure to form optimised light emitting layers.
• Yet another advantage of using mixtures of the materials of the invention is that it allows the use of mixtures of reactive mesogen materials in which photoinitiated electron donor- acceptor interactions as opposed to ionic or free radical initiation are used to initiate polymerization. This may result in much more stable (in terms of shelf-life) reactive mesogen materials than in methacrylate-based systems, while at the same time maintaining low UV crosslinking fluences.
• at least one of the reactive mesogen materials is substituted with electron-rich crosslinking groups while at least one other component reactive mesogen material is substituted with electron-deficient crosslinking groups. Ultraviolet radiation incident on the material promotes the electron- deficient crosslinking groups on some reactive mesogen molecules into electronically excited states.
• Electron-deficient crosslinking groups include maleimides, maleates, fumarates, and other unsaturated esters. Electron donor groups include vinyl ethers, 1-propenyl ethers and other similar alkenyl ethers. Mixtures like these are advantageous in that the individual components are thermally and photochemically stable with excellent shelf- lives. However, when the materials are combined, the mixture has high photochemical sensitivity and requires only a relatively small UV dose for crosslinking.
• An examples of reactive mesogen mixtures of the invention containing both electron-deficient and electron donor crosslinking groups is a 50:50 mixture of compounds 38 and 39. Mixtures of this type need not contain components having the same molecular core structure as is the case in this example.
• the exemplary OLED device 100 may be fabricated as follows.
• a substrate of indium- tin oxide coated glass (30 ohms/square) is patterned into a pixel or multipixel pattern a standard process of coating photoresist onto the substrate, patterning it with a UV light exposure through a photomask, developing the material, and then etching the ITO with 20% HC1 / 5% HN0 3 .
• the photoresist is stripped from the ITO; the ITO is rinsed with D.I. water and then cleaned with an oxygen plasma.
• Hole injection layer 120 is formed by spin coating a 1.6% aqueous solution of Baytron P(AI 4083) polyethylene
• PEDT PSS dioxythiophene polystyrene sulfonate
• H.C. Starck GmbH onto the substrate glass over the patterned ITO.
• the substrate is then baked at 120°C.
• a 0.75% solution of compound 34 in chloroform is spin coated over the PEDT/PSS to form hole-transporting layer 130.
• the material is dried at 50°C for 30 minutes and annealed at 90°C for a minute.
• the material is then photocured using 351 nm. radiation from an argon ion laser at a fluence of 30 joules/cm .
• the light emitting layer 140 is formed by spin coating a chloroform solution consisting of 0.40 % compound 37, 0.35% compound 35 and 0.05% compound 36 over layer 130. This layer dried and exposed to crosslinking UV exposure in the same way as was layer 130.
• Next electron transporting layer 150 is formed by spin coating a 0.75% chloroform solution of compound 37 over layer 140. This layer is then dried and photocured in the same way as were the previous layers. Finally an aluminium cathode is vacuum deposited over layer 150 yielding the device 100 represented in the drawing.
• the hole transporting photoalignment layer 210 aligns the molecular long axes of the molecules in the spin coated liquid crystal layer from which hole injection layer 130 is formed by photocrosslinking.
• the alignment within 130 is such that the long axes of the liquid crystalline molecular core units within the polymer matrix forming the layer are parallel to each other and to the device substrate surface.
• the uniform alignment of the molecular cores in 130 aligns the long molecular axes of the liquid crystal molecules from which the light-emitting layer 140 is formed by acting as an alignment template.
• the alignment of layer 140 acts as a template for the alignment of the liquid crystal molecules from which the electron-transporting layer 150 is formed.
• all three liquid crystal polymer layers, 130, 140, and 150 end up being uniformly aligned by the insertion of the alignment layer 210 forming the new device 200.
• hole transporting, photoalignment layers like 210 is described in US Patent 7,118,787. These layers are formed by solvent casting, for instance from a 0.5% solution in cyclopentanone, a blend of a commercial photoalignment polymer, for instance a coumarin substituted polymethyl methacrylate like the material with structure 40, and a commercially available hole transporting material, for instance the triaryl substituted amine material (structure 41).
• the layer 210 is formed over the electron injection layer by solvent casting and the surface energy bias necessary to align the liquid crystal molecules is of the subsequent layers is induced by exposure to polarised UV light, for instance from the 300 nm spectral line of an argon ion laser.
• Devices like device 200 are useful because the light emitting, liquid crystalline polymer layers of the invention like 140 emit highly polarised light if they have their luminescent molecular cores uniformly aligned as they are in device 200.
• device 200 is an OLED that emits highly polarised light.
• OLEDs like 200 can find use as liquid crystal display backlights, in 3 -dimensional displays, and in any other applications where the efficient emission of highly polarised light is advantageous.
• Aligned light emitting liquid crystalline layers of the types used in device 200 may also be advantageously used in other devices, for instance, photoluminescent polarisers.
• the light emitting and charge transporting materials of the invention can be photopatterned like ordinary photoresists, they can easily and cost effectively be used to produce multicolour pixelated devices. For instance, a matrix array of green light emitting elements each having the structure of discrete device 100 may be fabricated on a glass substrate. Then a second array of the same number of blue light emitting elements may be fabricated with the same structure as 100, but by forming layer 140 by spin coating a chloroform solution consisting of 0.40 % compound 37, 0.35% compound 42 and 0.05% compound 35 over layer 130 rather than using the formulation for layer 140 as in the example above.
• an array of red light emitting elements equal in number to the green light emitting pixels may be fabricated with the same structure as 100, but by forming layer 140 by spin coating a chloroform solution consisting of 0.40 % compound 37, 0.35% compound 35 and 0.05% compound 43 over layer 130.
• the arrays of the three different coloured light emitting elements may be arranged such that groups of one green emitting, one blue emitting, and one red light emitting element form a full-colour pixel group as is used in colour flat panel displays. It should be obvious that some device layers such as the hole injecting layer 120, the hole transporting, photoalignment layer 210, and the cathode 160 may be common to light emitting elements of all three colours.
• a further advantage of the materials described in this invention over more conventional OLED emitter and charge transporting materials is the ability for multiple layers to be cast then photocured into insoluble, immobile liquid crystalline polymer materials one over the other.
• Other polymeric OLED emitters and charge transporting materials remain solvent soluble after deposition onto device substrates with the result that subsequent material depositions from solvent would wash them away. This renders the fabrication of multilayer structures as in device 100 impossible. It should be obvious that devices with even more layers than device 100 can be easily fabricated by adding more deposition and curing steps.
• HOMO and LUMO highest occupied or lowest unoccupied molecular orbital
• charge carrier mobilities are of general utility in plastic electronics.
• the equivalent of p-n junctions may be formed using the materials and processes of this invention and these may find utility in diodes, transistors, and photovoltaic devices.
• the capability of the materials of the invention to be photolithographically patterned allows large arrays of plastic electronic devices of virtually any size and description to be fabricated.
• the synthesis of the oxidation resistant materials of the invention proceeds through keto diester derivatives of alicyclic and bicyclic compounds such as VIII, XVIII, and XXVII in the following.
• the resulting intermediates are then ring-closed to the corresponding 9-spiro-substituted fluorenes diesters (XTV, XXIV, and XXXIII).
• the dieters may be converted to the desired alkyl substituted ring systems (for instance, XVII, XXVI, or XXXVI) by either reduction, or reaction with Grignard or alkyl lithium reagents followed by reduction.
• the spiro-substituted fluorenes are the dihalogenated (Scheme 5) to ready them for incorporation into the reactive mesogen backbones. Schemes 6, 8, 7, and 9 portray the synthesis of reactive mesogen LVII using a series of Stille and Suzuki coupling reactions.
• keto diester derivatives of alicyclic and bicyclic compounds such as VIII, XVIII, and XXVII in the following. These materials are produced by the alkylation of the enols of acetonedicarboxylic acid esters (VI and XVI). The keto componds are then converted to the corresponding bromo compounds (X, XX, and ⁇ ). The bromides then undergo the Miyaura borylation reaction to yield the alkylboronic acid pinacol esters (XI, XXI, and XXX). These compounds are then coupled to the appropriate biphenyl derivative V.
• the Suzuki coupling reaction is not usually successful using boronates of this type because of the competing ⁇ -elimination reaction. However, because the boronates in this case have no ⁇ -substituted hydrogens, the competing reaction is not possible.
• the resulting intermediates are then ring-closed to the corresponding 9-spiro-substituted fluorenes diesters (XTV, XXIV, and XXXIII).
• the diesters may be converted to the desired alkyl substituted ring systems (for instance, XVII, XXVI, or XXXVI) by either reduction, or reaction with Grignard or alkyl lithium reagents followed by reduction.
• Scheme 5 The spiro-substituted fluorenes are then dihalogenated (Scheme 5) to ready them for incorporation into the reactive mesogen backbones.
• Schemes 6, 8, 7, and 9 portray the synthesis of reactive mesogen LVII using a series of Stille and Suzuki coupling reactions.

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Engineering & Computer Science (AREA)
• Materials Engineering (AREA)
• Physics & Mathematics (AREA)
• Spectroscopy & Molecular Physics (AREA)
• Optics & Photonics (AREA)
• Electroluminescent Light Sources (AREA)
• Plural Heterocyclic Compounds (AREA)
• Nitrogen And Oxygen Or Sulfur-Condensed Heterocyclic Ring Systems (AREA)
• Organic Low-Molecular-Weight Compounds And Preparation Thereof (AREA)
• Liquid Crystal Substances (AREA)
• Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)

Priority Applications (8)

Applications Claiming Priority (2)

Related Child Applications (2)

Publications (1)

Family

ID=41350554

Family Applications (1)

Country Status (9)

Cited By (6)

Families Citing this family (9)

Citations (4)

Family Cites Families (2)

• 2009
  • 2009-09-30 GB GBGB0917083.8A patent/GB0917083D0/en not_active Ceased
• 2010
  • 2010-09-29 WO PCT/GB2010/001818 patent/WO2011039506A1/en not_active Ceased
  • 2010-09-29 CN CN2010800520858A patent/CN102695774A/zh active Pending
  • 2010-09-29 EP EP10773132.5A patent/EP2483368B1/en active Active
  • 2010-09-29 KR KR1020127011267A patent/KR101833074B1/ko active Active
  • 2010-09-29 PL PL10773132T patent/PL2483368T3/pl unknown
  • 2010-09-29 US US13/499,039 patent/US20130037752A1/en not_active Abandoned
  • 2010-09-29 JP JP2012531493A patent/JP2013506647A/ja active Pending
• 2012
  • 2012-04-18 IN IN3382DEN2012 patent/IN2012DN03382A/en unknown
• 2015
  • 2015-07-10 US US14/796,383 patent/US20160056389A1/en not_active Abandoned

Patent Citations (4)

Non-Patent Citations (2)

Also Published As

Similar Documents

Legal Events