WO2011001485A1 - Composition de résine thermodurcissable et photodurcissable - Google Patents

Composition de résine thermodurcissable et photodurcissable Download PDF

Info

Publication number
WO2011001485A1
WO2011001485A1 PCT/JP2009/006737 JP2009006737W WO2011001485A1 WO 2011001485 A1 WO2011001485 A1 WO 2011001485A1 JP 2009006737 W JP2009006737 W JP 2009006737W WO 2011001485 A1 WO2011001485 A1 WO 2011001485A1
Authority
WO
WIPO (PCT)
Prior art keywords
resin
group
compound
manufactured
resin composition
Prior art date
Application number
PCT/JP2009/006737
Other languages
English (en)
Japanese (ja)
Inventor
伊藤信人
岡本大地
有馬聖夫
Original Assignee
太陽インキ製造株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 太陽インキ製造株式会社 filed Critical 太陽インキ製造株式会社
Priority to CN200980160288.6A priority Critical patent/CN102472970B/zh
Priority to KR1020117031423A priority patent/KR101382071B1/ko
Publication of WO2011001485A1 publication Critical patent/WO2011001485A1/fr

Abstract

L’invention concerne : une composition de résine photodurcissable et thermodurcissable qui permet la formation d’une pellicule de revêtement durci présentant une résistance PCT, une résistance HAST, une résistance au placage anélectrolytique d’or et une résistance aux chocs thermiques, qui sont des propriétés importantes nécessaires aux enduits protecteurs de brasure des ensembles semi-conducteurs ; une pellicule séchée produite à partir de la composition et un produit durci de la composition et une carte de circuit imprimé sur laquelle est formée une pellicule de revêtement (par ex. un enduit protecteur de brasure) comprenant la pellicule séchée ou le produit durci. Elle concerne spécifiquement une composition de résine photodurcissable et thermodurcissable qui peut être développée avec une solution alcaline aqueuse, qui contient une résine contenant un groupe carboxyle, un initiateur de photopolymérisation, un élastomère contenant un groupe vinyle et un composé mercapto. De préférence, la résine contenant un groupe carboxyle n’est pas dérivée d’une résine époxy.
PCT/JP2009/006737 2009-07-02 2009-12-10 Composition de résine thermodurcissable et photodurcissable WO2011001485A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN200980160288.6A CN102472970B (zh) 2009-07-02 2009-12-10 光固化性热固化性树脂组合物
KR1020117031423A KR101382071B1 (ko) 2009-07-02 2009-12-10 광경화성 열경화성 수지 조성물

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2009157993A JP5475350B2 (ja) 2009-07-02 2009-07-02 光硬化性熱硬化性樹脂組成物、そのドライフィルム及び硬化物並びにそれらを用いたプリント配線板
JP2009-157993 2009-07-02

Publications (1)

Publication Number Publication Date
WO2011001485A1 true WO2011001485A1 (fr) 2011-01-06

Family

ID=43410586

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2009/006737 WO2011001485A1 (fr) 2009-07-02 2009-12-10 Composition de résine thermodurcissable et photodurcissable

Country Status (5)

Country Link
JP (1) JP5475350B2 (fr)
KR (1) KR101382071B1 (fr)
CN (1) CN102472970B (fr)
TW (1) TWI438236B (fr)
WO (1) WO2011001485A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2012159657A (ja) * 2011-01-31 2012-08-23 Asahi Kasei E-Materials Corp 光硬化型樹脂組成物及びそれを用いたパターン形成された基材の製造方法、並びに該基材を備える電子部品
WO2013164409A1 (fr) 2012-05-04 2013-11-07 Kendlbacher Andreas Dispositif de découpe d'os au jet

Families Citing this family (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101877992B1 (ko) * 2012-07-30 2018-07-13 동우 화인켐 주식회사 착색 감광성 수지 조성물
CN104641293B (zh) * 2012-09-18 2019-04-19 旭化成株式会社 感光性树脂组合物
CN104516201A (zh) * 2013-09-30 2015-04-15 太阳油墨（苏州）有限公司 光固化性树脂组合物、干膜和固化物、以及印刷电路板
KR102192236B1 (ko) * 2015-03-17 2020-12-16 동우 화인켐 주식회사 착색 감광성 수지 조성물, 이를 포함하는 컬러필터 및 표시장치
KR102558400B1 (ko) * 2015-03-31 2023-07-24 닛산 가가쿠 가부시키가이샤 감광성 무전해도금 하지제
TWI731964B (zh) * 2016-04-28 2021-07-01 日商琳得科股份有限公司 保護膜形成用複合片
CN106632969B (zh) * 2016-12-26 2019-05-28 铃鹿复合建材（上海）有限公司 含羟基聚氨酯水分散体及其制备方法和应用
CN108250397B (zh) * 2018-01-11 2020-08-11 重庆文理学院 一种水性四氢枞酸封端聚氨酯树脂、制备方法、及其应用
JP7048723B2 (ja) * 2018-03-29 2022-04-05 富士フイルム株式会社 感光性転写材料、電極保護膜、積層体、静電容量型入力装置、及び、タッチパネルの製造方法
KR102191705B1 (ko) * 2018-11-30 2020-12-16 한국다이요잉크 주식회사 Uv led 경화형 잉크 조성물
WO2021006290A1 (fr) * 2019-07-11 2021-01-14 共栄社化学株式会社 Composition de résine durcissable, film durci, corps moulé en résine revêtue et film multicouche

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2000002091A1 (fr) * 1998-07-07 2000-01-13 Kansai Paint Co., Ltd. Composition de resist de soudage a base d'eau
JP2000214584A (ja) * 1999-01-27 2000-08-04 Taiyo Ink Mfg Ltd 光硬化性・熱硬化性樹脂組成物とこれを用いて形成したソルダ―レジスト皮膜や樹脂絶縁層を有するプリント配線板
JP2005062451A (ja) * 2003-08-12 2005-03-10 Kyocera Chemical Corp 感光性熱硬化型樹脂組成物
JP2007268782A (ja) * 2006-03-30 2007-10-18 Nippon Steel Chem Co Ltd 積層体
JP2008225244A (ja) * 2007-03-14 2008-09-25 Hitachi Chem Co Ltd 感光性樹脂組成物、これを用いた感光性エレメント、レジストパターンの形成方法及びプリント配線板の製造方法
JP2008287227A (ja) * 2007-04-17 2008-11-27 Asahi Kasei Electronics Co Ltd 感光性樹脂組成物及び積層体
JP2008299294A (ja) * 2007-06-04 2008-12-11 Taiyo Ink Mfg Ltd 光硬化性・熱硬化性樹脂組成物及びそれを用いて得られるプリント配線
JP2009014745A (ja) * 2006-03-16 2009-01-22 Fujifilm Holdings Corp 感光性組成物、感光性フィルム、感光性積層体、永久パターン形成方法、及びプリント基板

Family Cites Families (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2006285179A (ja) * 2005-03-09 2006-10-19 Fuji Photo Film Co Ltd 感光性永久レジストフィルム及び永久パターン形成方法
JP4663679B2 (ja) * 2007-05-08 2011-04-06 太陽ホールディングス株式会社 光硬化性樹脂組成物、ドライフィルム、硬化物、及びプリント配線板
JP4616863B2 (ja) * 2007-06-04 2011-01-19 太陽ホールディングス株式会社 感光性樹脂組成物及びそれを用いて得られるフレキシブル配線板
JP5513711B2 (ja) * 2007-10-01 2014-06-04 太陽ホールディングス株式会社 感光性樹脂組成物及びその硬化物
JP5464314B2 (ja) * 2007-10-01 2014-04-09 山栄化学株式会社 無機フィラー及び有機フィラー含有硬化性樹脂組成物、並びにレジスト膜被覆プリント配線板及びその製造方法
TWI395059B (zh) * 2007-12-21 2013-05-01 Taiyo Holdings Co Ltd A photohardenable thermosetting resin composition and a dry film and a printed circuit board using the same

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2000002091A1 (fr) * 1998-07-07 2000-01-13 Kansai Paint Co., Ltd. Composition de resist de soudage a base d'eau
JP2000214584A (ja) * 1999-01-27 2000-08-04 Taiyo Ink Mfg Ltd 光硬化性・熱硬化性樹脂組成物とこれを用いて形成したソルダ―レジスト皮膜や樹脂絶縁層を有するプリント配線板
JP2005062451A (ja) * 2003-08-12 2005-03-10 Kyocera Chemical Corp 感光性熱硬化型樹脂組成物
JP2009014745A (ja) * 2006-03-16 2009-01-22 Fujifilm Holdings Corp 感光性組成物、感光性フィルム、感光性積層体、永久パターン形成方法、及びプリント基板
JP2007268782A (ja) * 2006-03-30 2007-10-18 Nippon Steel Chem Co Ltd 積層体
JP2008225244A (ja) * 2007-03-14 2008-09-25 Hitachi Chem Co Ltd 感光性樹脂組成物、これを用いた感光性エレメント、レジストパターンの形成方法及びプリント配線板の製造方法
JP2008287227A (ja) * 2007-04-17 2008-11-27 Asahi Kasei Electronics Co Ltd 感光性樹脂組成物及び積層体
JP2008299294A (ja) * 2007-06-04 2008-12-11 Taiyo Ink Mfg Ltd 光硬化性・熱硬化性樹脂組成物及びそれを用いて得られるプリント配線

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2012159657A (ja) * 2011-01-31 2012-08-23 Asahi Kasei E-Materials Corp 光硬化型樹脂組成物及びそれを用いたパターン形成された基材の製造方法、並びに該基材を備える電子部品
WO2013164409A1 (fr) 2012-05-04 2013-11-07 Kendlbacher Andreas Dispositif de découpe d'os au jet

Also Published As

Publication number Publication date
CN102472970B (zh) 2016-10-19
TWI438236B (zh) 2014-05-21
KR101382071B1 (ko) 2014-04-04
JP2011013487A (ja) 2011-01-20
TW201102405A (en) 2011-01-16
KR20120031023A (ko) 2012-03-29
JP5475350B2 (ja) 2014-04-16
CN102472970A (zh) 2012-05-23

Similar Documents

Publication Publication Date Title
JP5427632B2 (ja) 積層構造体及びそれに用いる感光性ドライフィルム
JP5422427B2 (ja) 積層構造体及びそれに用いる感光性ドライフィルム
JP5583941B2 (ja) 光硬化性樹脂組成物、そのドライフィルム及び硬化物並びにそれらを用いたプリント配線板
JP5475350B2 (ja) 光硬化性熱硬化性樹脂組成物、そのドライフィルム及び硬化物並びにそれらを用いたプリント配線板
JP5099851B2 (ja) 光硬化性熱硬化性樹脂組成物、そのドライフィルム及び硬化物並びにそれらを用いたプリント配線板
JP5356934B2 (ja) 光硬化性熱硬化性樹脂組成物、そのドライフィルム及び硬化物並びにそれらを用いたプリント配線板
JP5250479B2 (ja) 光硬化性熱硬化性樹脂組成物、そのドライフィルム及び硬化物並びにそれらを用いたプリント配線板
JP5619443B2 (ja) 光硬化性熱硬化性樹脂組成物、そのドライフィルム及び硬化物並びにそれらを用いたプリント配線板
JP6061449B2 (ja) 光硬化性熱硬化性樹脂組成物、そのドライフィルム及び硬化物並びにそれらを用いたプリント配線板
JP5567716B2 (ja) 積層構造体及びそれに用いる感光性ドライフィルム
JP5107960B2 (ja) ソルダーレジスト組成物、それを用いたドライフィルム及びプリント配線板
WO2011122027A1 (fr) Composition de résine thermodurcissable photodurcissable
JP5422319B2 (ja) 感光性樹脂組成物、そのドライフィルム及び硬化物並びにそれらを用いたプリント配線板
JP5439256B2 (ja) 光硬化性熱硬化性樹脂組成物
JP5216682B2 (ja) 光硬化性熱硬化性樹脂組成物、そのドライフィルム及び硬化物並びにそれらを用いたプリント配線板
JP5523592B2 (ja) 光硬化性熱硬化性樹脂組成物、そのドライフィルム及び硬化物並びにそれらを用いたプリント配線板
JP2011053421A (ja) 光硬化性熱硬化性樹脂組成物、そのドライフィルム及び硬化物並びにそれらを用いたプリント配線板
WO2010113478A1 (fr) Composition de résine durcissable et carte de câblage imprimée
WO2011010457A1 (fr) Composition de résine photodurcissable
JP5917602B2 (ja) 光硬化性樹脂組成物、そのドライフィルム及び硬化物並びにそれらを用いたプリント配線板
JP5514340B2 (ja) 光硬化性熱硬化性樹脂組成物、そのドライフィルム及び硬化物並びにそれらを用いたプリント配線板
WO2011034124A1 (fr) Composition de résine photosensible, film sec et produit durci à base de celle-ci et carte de câblage imprimé l'utilisant
JP5356935B2 (ja) 光硬化性熱硬化性樹脂組成物、そのドライフィルム及び硬化物並びにそれらを用いたプリント配線板
JP5439255B2 (ja) 光硬化性熱硬化性樹脂組成物
JP2011065088A (ja) 感光性樹脂組成物、そのドライフィルム及び硬化物並びにそれらを用いたプリント配線板

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 200980160288.6

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 09846779

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 20117031423

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 09846779

Country of ref document: EP

Kind code of ref document: A1