WO2010131016A2 - Paper filler composition - Google Patents
Paper filler composition Download PDFInfo
- Publication number
- WO2010131016A2 WO2010131016A2 PCT/GB2010/000982 GB2010000982W WO2010131016A2 WO 2010131016 A2 WO2010131016 A2 WO 2010131016A2 GB 2010000982 W GB2010000982 W GB 2010000982W WO 2010131016 A2 WO2010131016 A2 WO 2010131016A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- grinding
- cellulose
- particulate material
- inorganic particulate
- pulp
- Prior art date
Abstract
Description
Claims