WO2010117539A2 - Procédé d'oligomérisation de l'éthylène dilué - Google Patents
Procédé d'oligomérisation de l'éthylène dilué Download PDFInfo
- Publication number
- WO2010117539A2 WO2010117539A2 PCT/US2010/026889 US2010026889W WO2010117539A2 WO 2010117539 A2 WO2010117539 A2 WO 2010117539A2 US 2010026889 W US2010026889 W US 2010026889W WO 2010117539 A2 WO2010117539 A2 WO 2010117539A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- catalyst
- ethylene
- stream
- alumina
- cracking catalyst
- Prior art date
Abstract
Priority Applications (6)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR1020117025850A KR101358589B1 (ko) | 2009-03-31 | 2010-03-11 | 희석 에틸렌을 올리고머화하는 방법 |
JP2012503469A JP5553889B2 (ja) | 2009-03-31 | 2010-03-11 | 希薄エチレンをオリゴマー化する方法 |
EP10762053.6A EP2414310A4 (fr) | 2009-03-31 | 2010-03-11 | Procédé d'oligomérisation de l'éthylène dilué |
MX2011010303A MX2011010303A (es) | 2009-03-31 | 2010-03-11 | Proceso para oligomerizar etileno diluido. |
BRPI1013710A BRPI1013710A2 (pt) | 2009-03-31 | 2010-03-11 | processo para oligomerizar etileno, e, aparelho |
CN201080023632.XA CN102448913B (zh) | 2009-03-31 | 2010-03-11 | 稀乙烯的低聚方法 |
Applications Claiming Priority (6)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US12/416,032 | 2009-03-31 | ||
US12/416,029 | 2009-03-31 | ||
US12/416,026 | 2009-03-31 | ||
US12/416,026 US8748681B2 (en) | 2009-03-31 | 2009-03-31 | Process for oligomerizing dilute ethylene |
US12/416,029 US8575410B2 (en) | 2009-03-31 | 2009-03-31 | Process for oligomerizing dilute ethylene |
US12/416,032 US8021620B2 (en) | 2009-03-31 | 2009-03-31 | Apparatus for oligomerizing dilute ethylene |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2010117539A2 true WO2010117539A2 (fr) | 2010-10-14 |
WO2010117539A3 WO2010117539A3 (fr) | 2011-01-13 |
Family
ID=42936779
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2010/026889 WO2010117539A2 (fr) | 2009-03-31 | 2010-03-11 | Procédé d'oligomérisation de l'éthylène dilué |
Country Status (8)
Country | Link |
---|---|
EP (1) | EP2414310A4 (fr) |
JP (1) | JP5553889B2 (fr) |
KR (1) | KR101358589B1 (fr) |
CN (2) | CN102448913B (fr) |
BR (1) | BRPI1013710A2 (fr) |
MX (1) | MX2011010303A (fr) |
TW (1) | TWI412585B (fr) |
WO (1) | WO2010117539A2 (fr) |
Cited By (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2968010A1 (fr) * | 2010-11-25 | 2012-06-01 | IFP Energies Nouvelles | Procede de conversion d'une charge lourde en distillat moyen |
WO2013043314A1 (fr) * | 2011-09-23 | 2013-03-28 | Uop Llc | Procédé d'oligomérisation |
EP3045438A1 (fr) | 2015-01-19 | 2016-07-20 | Evonik Degussa GmbH | Fabrication combinée d'au moins de butène et d'octène à partir d'éthylène |
EP3045439A1 (fr) | 2015-01-19 | 2016-07-20 | Evonik Degussa GmbH | Fabrication combinee de butene et d'octene a partir d'ethylene |
DE102015200702A1 (de) | 2015-01-19 | 2016-07-21 | Evonik Degussa Gmbh | Herstellung von Butadien aus Ethen |
EP3255029A1 (fr) | 2016-06-10 | 2017-12-13 | Evonik Degussa GmbH | Oligomerisation de l'ethylene dans des conditions supercritiques |
CN110270337A (zh) * | 2018-03-14 | 2019-09-24 | 赢创德固赛有限公司 | 用于烯烃低聚的含Ni催化剂 |
EP3542898A1 (fr) * | 2018-03-14 | 2019-09-25 | Evonik Degussa GmbH | Procédé de production d'un catalyseur d'oligomérisation |
EP3549669A1 (fr) * | 2018-03-14 | 2019-10-09 | Evonik Degussa GmbH | Catalyseur d'oligomérisation à base d'oxyde de nickel et procédé d'oligomérisation des oléfines c3-c6 l'utilisant |
Families Citing this family (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2014151253A (ja) * | 2013-02-06 | 2014-08-25 | Jx Nippon Oil & Energy Corp | オレフィン低重合方法およびそれに用いる触媒 |
JP6228246B2 (ja) * | 2015-03-03 | 2017-11-08 | エボニック デグサ ゲーエムベーハーEvonik Degussa GmbH | エテンのオリゴマー化に使用される不均一系触媒の再生 |
FR3045652B1 (fr) * | 2015-12-22 | 2018-01-12 | Axens | Procede de fractionnement pour un procede d'oligomerisation d'olefines legeres |
US11253844B2 (en) * | 2018-03-14 | 2022-02-22 | Evonik Operations Gmbh | Oligomerization catalyst and process for the production thereof |
FR3105019B1 (fr) * | 2019-12-18 | 2022-07-22 | Ifp Energies Now | Reacteur gaz/liquide d’oligomerisation a zones successives de diametre variable |
CN113189717A (zh) * | 2021-05-12 | 2021-07-30 | 四川天邑康和通信股份有限公司 | 一种mpo/mtp型连接器的光纤及其制备方法 |
Family Cites Families (20)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4552644A (en) * | 1982-09-30 | 1985-11-12 | Stone & Webster Engineering Corporation | Duocracking process for the production of olefins from both heavy and light hydrocarbons |
DE3379335D1 (en) * | 1982-12-01 | 1989-04-13 | Mobil Oil Corp | Catalytic conversion of light-olefinic feedstocks in a fluidized-catalytic-cracking gas plant |
JPS60143830A (ja) * | 1983-08-01 | 1985-07-30 | コノコ・インコ−ポレ−テツド | オレフインのオリゴマ−化触媒の製造法 |
US4705907A (en) * | 1985-05-29 | 1987-11-10 | Showa Shell Sekiyu Kabushiki Kaisha | Production of liquid hydrocarbon from gas containing lower hydrocarbon |
US4891457A (en) * | 1985-09-13 | 1990-01-02 | Hartley Owen | Multistage process for converting olefins to heavier hydrocarbons |
US4717782A (en) * | 1985-09-13 | 1988-01-05 | Mobil Oil Corporation | Catalytic process for oligomerizing ethene |
GB2200302A (en) * | 1986-12-05 | 1988-08-03 | South African Inventions | Oligomerization catalyst |
AU595706B2 (en) * | 1987-06-11 | 1990-04-05 | Mobil Oil Corporation | Integrated process for gasoline production |
US4822477A (en) * | 1987-06-11 | 1989-04-18 | Mobil Oil Corporation | Integrated process for gasoline production |
US4859308A (en) * | 1988-01-19 | 1989-08-22 | Mobil Oil Corporation | Two-stage process for conversion of alkanes to gasoline |
US4835331A (en) * | 1988-05-23 | 1989-05-30 | Uop | Process for the oligomerization of olefinic hydrocarbons |
US5009851A (en) * | 1988-05-31 | 1991-04-23 | Mobil Oil Corporation | Integrated catalytic reactor system with light olefin upgrading |
US5034565A (en) * | 1988-09-26 | 1991-07-23 | Mobil Oil Corporation | Production of gasoline from light olefins in a fluidized catalyst reactor system |
US5068476A (en) * | 1989-04-28 | 1991-11-26 | Mobil Oil Corporation | Lubricant oligomers of C2 -C5 olefins |
WO1992019697A1 (fr) * | 1991-05-02 | 1992-11-12 | Exxon Research And Engineering Company | Procede et appareil de craquage catalytique |
EP0734766B1 (fr) * | 1995-03-29 | 2001-08-29 | Koa Oil Company, Limited | Catalyseur pour l'oligomérisation des oléfines, procédé pour le préparer et procédé d'oligomérisation d'oléfines utilisant ledit catalyseur |
JP2906086B2 (ja) * | 1995-04-27 | 1999-06-14 | エービービー ルーマス グローバル インコーポレイテッド | 使用済みfcc触媒を使用するオレフィン系炭化水素の転化法 |
US6660812B2 (en) * | 2000-07-13 | 2003-12-09 | Exxonmobil Chemical Patents Inc. | Production of olefin derivatives |
US6538169B1 (en) * | 2000-11-13 | 2003-03-25 | Uop Llc | FCC process with improved yield of light olefins |
US7525002B2 (en) * | 2005-02-28 | 2009-04-28 | Exxonmobil Research And Engineering Company | Gasoline production by olefin polymerization with aromatics alkylation |
-
2010
- 2010-03-11 CN CN201080023632.XA patent/CN102448913B/zh active Active
- 2010-03-11 WO PCT/US2010/026889 patent/WO2010117539A2/fr active Application Filing
- 2010-03-11 MX MX2011010303A patent/MX2011010303A/es active IP Right Grant
- 2010-03-11 JP JP2012503469A patent/JP5553889B2/ja active Active
- 2010-03-11 EP EP10762053.6A patent/EP2414310A4/fr not_active Withdrawn
- 2010-03-11 KR KR1020117025850A patent/KR101358589B1/ko active IP Right Grant
- 2010-03-11 BR BRPI1013710A patent/BRPI1013710A2/pt not_active IP Right Cessation
- 2010-03-11 CN CN201410454385.9A patent/CN104276911A/zh active Pending
- 2010-03-24 TW TW099108721A patent/TWI412585B/zh active
Non-Patent Citations (1)
Title |
---|
See references of EP2414310A4 * |
Cited By (21)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US10077218B2 (en) | 2010-11-25 | 2018-09-18 | IFP Energies Nouvelles | Process for converting a heavy feed into middle distillate |
WO2012069709A3 (fr) * | 2010-11-25 | 2012-12-20 | IFP Energies Nouvelles | Procede de conversion d'une charge lourde en distillat moyen. |
CN103221514A (zh) * | 2010-11-25 | 2013-07-24 | Ifp新能源公司 | 将重质原料转化成中间馏分的方法 |
RU2563655C2 (ru) * | 2010-11-25 | 2015-09-20 | Ифп Энержи Нувелль | Способ конверсии тяжелой фракции в средний дистиллят |
CN103221514B (zh) * | 2010-11-25 | 2016-04-13 | Ifp新能源公司 | 将重质原料转化成中间馏分的方法 |
FR2968010A1 (fr) * | 2010-11-25 | 2012-06-01 | IFP Energies Nouvelles | Procede de conversion d'une charge lourde en distillat moyen |
WO2013043314A1 (fr) * | 2011-09-23 | 2013-03-28 | Uop Llc | Procédé d'oligomérisation |
CN103814002A (zh) * | 2011-09-23 | 2014-05-21 | 环球油品公司 | 低聚方法 |
EP3045438A1 (fr) | 2015-01-19 | 2016-07-20 | Evonik Degussa GmbH | Fabrication combinée d'au moins de butène et d'octène à partir d'éthylène |
EP3045439A1 (fr) | 2015-01-19 | 2016-07-20 | Evonik Degussa GmbH | Fabrication combinee de butene et d'octene a partir d'ethylene |
DE102015200702A1 (de) | 2015-01-19 | 2016-07-21 | Evonik Degussa Gmbh | Herstellung von Butadien aus Ethen |
EP3255029A1 (fr) | 2016-06-10 | 2017-12-13 | Evonik Degussa GmbH | Oligomerisation de l'ethylene dans des conditions supercritiques |
US10189755B2 (en) | 2016-06-10 | 2019-01-29 | Evonik Degussa Gmbh | Oligomerization of ethene in supercritical mode |
CN110270337A (zh) * | 2018-03-14 | 2019-09-24 | 赢创德固赛有限公司 | 用于烯烃低聚的含Ni催化剂 |
EP3542898A1 (fr) * | 2018-03-14 | 2019-09-25 | Evonik Degussa GmbH | Procédé de production d'un catalyseur d'oligomérisation |
EP3549669A1 (fr) * | 2018-03-14 | 2019-10-09 | Evonik Degussa GmbH | Catalyseur d'oligomérisation à base d'oxyde de nickel et procédé d'oligomérisation des oléfines c3-c6 l'utilisant |
EP3549668A1 (fr) * | 2018-03-14 | 2019-10-09 | Evonik Degussa GmbH | Catalyseur contenant du ni avec un rapport defini d'ions ni vers alcali ou alcalinoterreux destiné à l'oligomérisation des oléfines |
US10850261B2 (en) | 2018-03-14 | 2020-12-01 | Evonik Operations Gmbh | Oligomerization catalyst and process for the production thereof |
US10882028B2 (en) | 2018-03-14 | 2021-01-05 | Evonik Operations Gmbh | Ni-containing catalyst for the oligomerization of olefins |
US10882027B2 (en) | 2018-03-14 | 2021-01-05 | Evonik Operations Gmbh | Process for producing an oligomerization catalyst |
CN110270337B (zh) * | 2018-03-14 | 2023-05-26 | 赢创运营有限公司 | 用于烯烃低聚的含Ni催化剂 |
Also Published As
Publication number | Publication date |
---|---|
EP2414310A4 (fr) | 2015-04-29 |
WO2010117539A3 (fr) | 2011-01-13 |
TW201040251A (en) | 2010-11-16 |
CN102448913A (zh) | 2012-05-09 |
TWI412585B (zh) | 2013-10-21 |
BRPI1013710A2 (pt) | 2016-04-05 |
JP5553889B2 (ja) | 2014-07-16 |
JP2012522109A (ja) | 2012-09-20 |
KR20120001795A (ko) | 2012-01-04 |
KR101358589B1 (ko) | 2014-02-04 |
CN104276911A (zh) | 2015-01-14 |
MX2011010303A (es) | 2011-10-11 |
CN102448913B (zh) | 2015-01-28 |
EP2414310A2 (fr) | 2012-02-08 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US8748682B2 (en) | Process for oligomerizing dilute ethylene | |
US8748681B2 (en) | Process for oligomerizing dilute ethylene | |
US8021620B2 (en) | Apparatus for oligomerizing dilute ethylene | |
JP5553889B2 (ja) | 希薄エチレンをオリゴマー化する方法 | |
JP2007125515A (ja) | 液化石油ガス製造用触媒、および、この触媒を用いた液化石油ガスの製造方法 | |
US20210016261A1 (en) | Olefin aromatization catalyst, preparation method and use thereof, and low-carbon olefin aromatization process | |
CN102822321B (zh) | 用于将轻循环油烷基化和氢化的方法和设备 | |
RU2283178C2 (ru) | Катализатор парового крекинга углеводородов для получения олефинов, способ его приготовления и способ получения олефинов с использованием этого катализатора | |
US20110243797A1 (en) | Apparatus for oligomerizing dilute ethylene | |
US20240109821A1 (en) | Process to produce propylene from refinery dry gas | |
CN107794080B (zh) | 费托合成石脑油的改质方法 | |
US20240067586A1 (en) | Process for converting olefins to distillate fuels with oligomerate recycle | |
US20230313048A1 (en) | Process for converting oxygenates to distillate fuels | |
US20240025821A1 (en) | Process for converting olefins to distillate fuels | |
JP7090470B2 (ja) | p-キシレンの製造方法 | |
US20230348341A1 (en) | Process for converting olefins to distillate fuels | |
JP7090471B2 (ja) | p-キシレンの製造方法 | |
Zuo et al. | The application of all-inorganic solid base materials in heterogeneous catalysis: A mini review | |
RU2204546C1 (ru) | Способ получения углеводородов из оксидов углерода и водорода | |
Souza et al. | Catalytic cracking of C5+ gasoline over HY zeolite | |
WO2024050427A1 (fr) | Processus de conversion d'oléfines en combustibles de distillat avec régénération | |
US20110245567A1 (en) | Process for oligomerizing dilute ethylene | |
Zuo et al. | From bench to industry, the application of all-inorganic solid base materials in traditional heterogeneous catalysis: a mini review | |
Zhang et al. | Conversion of bio-syngas to liquid hydrocarbon over CuCoMn-Zeolite bifunctional catalysts | |
CN118105973A (zh) | 用于活化脱氢催化剂的方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
WWE | Wipo information: entry into national phase |
Ref document number: 201080023632.X Country of ref document: CN |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 10762053 Country of ref document: EP Kind code of ref document: A2 |
|
REEP | Request for entry into the european phase |
Ref document number: 2010762053 Country of ref document: EP |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2010762053 Country of ref document: EP |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2012503469 Country of ref document: JP Ref document number: MX/A/2011/010303 Country of ref document: MX |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
ENP | Entry into the national phase |
Ref document number: 20117025850 Country of ref document: KR Kind code of ref document: A |
|
REG | Reference to national code |
Ref country code: BR Ref legal event code: B01A Ref document number: PI1013710 Country of ref document: BR |
|
ENP | Entry into the national phase |
Ref document number: PI1013710 Country of ref document: BR Kind code of ref document: A2 Effective date: 20110930 |