WO2008111383A1 - アルミ改質コロイダルシリカ及びその製造方法 - Google Patents
アルミ改質コロイダルシリカ及びその製造方法 Download PDFInfo
- Publication number
- WO2008111383A1 WO2008111383A1 PCT/JP2008/053095 JP2008053095W WO2008111383A1 WO 2008111383 A1 WO2008111383 A1 WO 2008111383A1 JP 2008053095 W JP2008053095 W JP 2008053095W WO 2008111383 A1 WO2008111383 A1 WO 2008111383A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- colloidal silica
- aluminum
- producing
- modified colloidal
- disclosed
- Prior art date
Abstract
(課題)高純度であるとともに、酸性領域でも安定なアルミ改質コロイダルシリカ及びその製造方法、並びに前記アルミ改質コロイダルシリカを、100°C以下の低温で製造できる簡便な製造方法を提供すること。
(解決手段)以下の工程(1)~(3)を含むアルカリ金属含有量がそれぞれ50ppm以下であるアルミ改質コロイダルシリカの製造方法とする。
(1)アルコキシド法により得られるコロイダルシリカであって、pHが6~10であるコロイダルシリカに、Al2O3/SiO2のモル比が0.00005~0.01の範囲になるように、アルミン酸塩水溶液を添加する工程
(2)工程(1)で得られたコロイダルシリカを60~100°Cに一定時間維持する工程
(3)工程(2)で得られたコロイダルシリカ中のアルカリイオンを必要に応じて除去してアルミ改質コロイダルシリカを得る工程
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2009503952A JP5221517B2 (ja) | 2007-03-13 | 2008-02-22 | アルミ改質コロイダルシリカ及びその製造方法 |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2007064094 | 2007-03-13 | ||
JP2007-064094 | 2007-03-13 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2008111383A1 true WO2008111383A1 (ja) | 2008-09-18 |
Family
ID=39759325
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2008/053095 WO2008111383A1 (ja) | 2007-03-13 | 2008-02-22 | アルミ改質コロイダルシリカ及びその製造方法 |
Country Status (3)
Country | Link |
---|---|
JP (1) | JP5221517B2 (ja) |
TW (1) | TW200902445A (ja) |
WO (1) | WO2008111383A1 (ja) |
Cited By (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2009197078A (ja) * | 2008-02-20 | 2009-09-03 | Jgc Catalysts & Chemicals Ltd | ハードコート層形成用塗料組成物および光学物品 |
WO2010150677A1 (ja) * | 2009-06-24 | 2010-12-29 | 日揮触媒化成株式会社 | シリカ系微粒子分散ゾルの製造方法、シリカ系微粒子分散ゾル、該分散ゾルを含む塗料組成物、硬化性塗膜および硬化性塗膜付き基材 |
JP2012162426A (ja) * | 2011-02-08 | 2012-08-30 | Jgc Catalysts & Chemicals Ltd | シリカ系微粒子の分散ゾル、該分散ゾルの製造方法および塗料組成物 |
WO2013183644A1 (ja) | 2012-06-04 | 2013-12-12 | ディップソール株式会社 | アルミ変性コロイダルシリカを含有した3価クロム化成処理液 |
CN105586004A (zh) * | 2015-12-31 | 2016-05-18 | 江苏天恒纳米科技股份有限公司 | 一种铝改性的硅溶胶的制备方法 |
CN111194344A (zh) * | 2017-05-15 | 2020-05-22 | 沙特阿拉伯石油公司 | 用于地下地层中的水和气体封堵的组合物和方法 |
CN111320178A (zh) * | 2020-03-02 | 2020-06-23 | 正大能源材料(大连)有限公司 | 一种用于合成sapo-34分子筛的金属改性硅溶胶及其制备方法 |
CN113135573A (zh) * | 2021-05-26 | 2021-07-20 | 山东银丰纳米新材料有限公司 | 一种锆改性的阳离子型硅溶胶及其制备方法 |
CN115403050A (zh) * | 2022-08-17 | 2022-11-29 | 苏州博来纳润电子材料有限公司 | 一种高纯有机铝改性酸性硅溶胶及其制备方法和应用 |
Families Citing this family (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP5839993B2 (ja) * | 2009-11-16 | 2016-01-06 | 日揮触媒化成株式会社 | シリカ・アルミナゾルの製造方法、シリカ・アルミナゾル、該ゾルを含む透明被膜形成用塗料および透明被膜付基材 |
CN113174234A (zh) * | 2020-11-12 | 2021-07-27 | 常州泰特耐特新材料科技有限公司 | 一种增强型芳纶浆粕的制备方法 |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH06199515A (ja) * | 1992-09-25 | 1994-07-19 | Nissan Chem Ind Ltd | 酸性シリカゾルの製造方法 |
JP2000247625A (ja) * | 1999-03-04 | 2000-09-12 | Nippon Chem Ind Co Ltd | 高純度シリカゾル及びその製造方法 |
JP2005162533A (ja) * | 2003-12-02 | 2005-06-23 | Fuso Chemical Co Ltd | 変性コロイダルシリカの製造方法 |
JP2006036605A (ja) * | 2004-07-29 | 2006-02-09 | Catalysts & Chem Ind Co Ltd | 高純度水性シリカゾルの製造方法 |
-
2008
- 2008-02-22 JP JP2009503952A patent/JP5221517B2/ja active Active
- 2008-02-22 WO PCT/JP2008/053095 patent/WO2008111383A1/ja active Application Filing
- 2008-03-12 TW TW97108600A patent/TW200902445A/zh unknown
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH06199515A (ja) * | 1992-09-25 | 1994-07-19 | Nissan Chem Ind Ltd | 酸性シリカゾルの製造方法 |
JP2000247625A (ja) * | 1999-03-04 | 2000-09-12 | Nippon Chem Ind Co Ltd | 高純度シリカゾル及びその製造方法 |
JP2005162533A (ja) * | 2003-12-02 | 2005-06-23 | Fuso Chemical Co Ltd | 変性コロイダルシリカの製造方法 |
JP2006036605A (ja) * | 2004-07-29 | 2006-02-09 | Catalysts & Chem Ind Co Ltd | 高純度水性シリカゾルの製造方法 |
Cited By (18)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2009197078A (ja) * | 2008-02-20 | 2009-09-03 | Jgc Catalysts & Chemicals Ltd | ハードコート層形成用塗料組成物および光学物品 |
WO2010150677A1 (ja) * | 2009-06-24 | 2010-12-29 | 日揮触媒化成株式会社 | シリカ系微粒子分散ゾルの製造方法、シリカ系微粒子分散ゾル、該分散ゾルを含む塗料組成物、硬化性塗膜および硬化性塗膜付き基材 |
JP2011026183A (ja) * | 2009-06-24 | 2011-02-10 | Jgc Catalysts & Chemicals Ltd | シリカ系微粒子分散ゾルの製造方法、シリカ系微粒子分散ゾル、該分散ゾルを含む塗料組成物、硬化性塗膜および硬化性塗膜付き基材 |
EP2447211A1 (en) * | 2009-06-24 | 2012-05-02 | JGC Catalysts and Chemicals Ltd. | Method for producing silica-based fine particle-dispersed sol, silica-based fine particle-dispersed sol, coating composition containing the silica-based fine particle-dispersed sol, curable coating film, and base with curable coating film |
EP2447211A4 (en) * | 2009-06-24 | 2013-03-06 | Jgc Catalysts & Chemicals Ltd | METHOD FOR PRODUCING SOLICIDE WITH SILICONE BASED FINE PARTICLE SAMPLE, SOLICIUM BASED FINE PARTICLE SAMPLE METALISATION, SOLICIUM BASED SOLID COATING COMPOSITIONS WITH SOL SOLID BASED SOLVENT DISPERSIBILITY, HARDENABLE COATING FILM AND BASE WITH THE HARDENABLE COATING FILM |
US9441139B2 (en) | 2009-06-24 | 2016-09-13 | Jgc Catalysts And Chemicals Ltd. | Process for producing silica-based fine particle dispersion sols, silica-based fine particle dispersion sol, coating composition containing the dispersion sol, curable coating film, and substrate having the curable coating film |
US9039828B2 (en) | 2009-06-24 | 2015-05-26 | Jgc Catalysts And Chemicals Ltd. | Process for producing silica-based fine particle dispersion sols, silica-based fine particle dispersion sol, coating composition containing the dispersion sol, curable coating film, and substrate having the curable coating film |
JP2012162426A (ja) * | 2011-02-08 | 2012-08-30 | Jgc Catalysts & Chemicals Ltd | シリカ系微粒子の分散ゾル、該分散ゾルの製造方法および塗料組成物 |
US9206321B2 (en) | 2012-06-04 | 2015-12-08 | Dipsol Chemicals Co., Ltd. | Trivalent chromium-conversion processing solution containing aluminum-modified colloidal silica |
WO2013183644A1 (ja) | 2012-06-04 | 2013-12-12 | ディップソール株式会社 | アルミ変性コロイダルシリカを含有した3価クロム化成処理液 |
CN105586004A (zh) * | 2015-12-31 | 2016-05-18 | 江苏天恒纳米科技股份有限公司 | 一种铝改性的硅溶胶的制备方法 |
CN111194344A (zh) * | 2017-05-15 | 2020-05-22 | 沙特阿拉伯石油公司 | 用于地下地层中的水和气体封堵的组合物和方法 |
CN111194344B (zh) * | 2017-05-15 | 2022-08-30 | 沙特阿拉伯石油公司 | 用于地下地层中的水和气体封堵的组合物和方法 |
CN111320178A (zh) * | 2020-03-02 | 2020-06-23 | 正大能源材料(大连)有限公司 | 一种用于合成sapo-34分子筛的金属改性硅溶胶及其制备方法 |
CN111320178B (zh) * | 2020-03-02 | 2021-08-27 | 正大能源材料(大连)有限公司 | 一种用于合成sapo-34分子筛的金属改性硅溶胶及其制备方法 |
CN113135573A (zh) * | 2021-05-26 | 2021-07-20 | 山东银丰纳米新材料有限公司 | 一种锆改性的阳离子型硅溶胶及其制备方法 |
CN115403050A (zh) * | 2022-08-17 | 2022-11-29 | 苏州博来纳润电子材料有限公司 | 一种高纯有机铝改性酸性硅溶胶及其制备方法和应用 |
CN115403050B (zh) * | 2022-08-17 | 2024-04-12 | 浙江博来纳润电子材料有限公司 | 一种高纯有机铝改性酸性硅溶胶及其制备方法和应用 |
Also Published As
Publication number | Publication date |
---|---|
JPWO2008111383A1 (ja) | 2010-06-24 |
TW200902445A (en) | 2009-01-16 |
JP5221517B2 (ja) | 2013-06-26 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2008111383A1 (ja) | アルミ改質コロイダルシリカ及びその製造方法 | |
SG140529A1 (en) | Catalyst and process for preparing isoolefins | |
WO2010037709A3 (de) | Herstellung von solar-silicium aus siliciumdioxid | |
AU2008250569A8 (en) | Disinfectant based on aqueous, hypochlorous acid (HOCl)-containing solutions, method for the production thereof, and use thereof | |
WO2009078366A1 (ja) | α-リポ酸ナノ粒子およびその調製方法 | |
TW200708008A (en) | Method and system for transmission control protocol (TCP) traffic smoothing | |
WO2009010263A3 (de) | Prozess zur herstellung von bariumsulfat | |
WO2008093422A1 (ja) | 細長い形状を有するシリカゾルの製造方法 | |
UA93682C2 (ru) | Композиция порошкообразной извести, способ получения композиции порошкообразной извести (варианты) и применение композиции порошкообразной извести для очистки дымовых газов | |
EA201100569A1 (ru) | СПОСОБ ПОЛУЧЕНИЯ SiOВЫСОКОЙ ЧИСТОТЫ ИЗ РАСТВОРОВ СИЛИКАТОВ | |
HK1081521A1 (en) | Aqueous solution of non-collodial silicic acid andboric acid | |
NZ514753A (en) | Silica-based sols | |
EA201100567A1 (ru) | СПОСОБ ПОЛУЧЕНИЯ SiOВЫСОКОЙ ЧИСТОТЫ ИЗ РАСТВОРОВ СИЛИКАТОВ | |
MX2010005422A (es) | Un dispositivo de comunicacion inalambrica y metodo. | |
ZA200710628B (en) | Process for preparing low-by-product methylglycine-N, N-diacetic acid tri (alkali metal) salts | |
WO2012113650A3 (de) | Verfahren zur herstellung wässriger kolloidaler silikasole hoher reinheit aus alkalimetallsilikatlösungen | |
WO2003013435A3 (en) | N-acetyl-d-glucosamine and process for producing n-acetyl-d-glucosamine | |
WO2007057201A3 (de) | Dexpanthenol-, calciumionen- und phosphatfreie pharmazeutische zusammensetzung sowie verwendung von calcium-chelatbildner und ophthalmologisch verträglichem viskositätsregler | |
WO2009124770A3 (de) | Verfahren zum herstellen einer ecke eines rahmenförmigen abstandhalters für isolierglasscheiben und nach dem verfahren hergestellte abstandhalter und isolierglasscheiben | |
AU2003242650A1 (en) | Aluminum-containing precipitated silicic acid having an adjustable bet/ctab ratio | |
MX2014009002A (es) | Nuevo proceso para la preparacion de silices precipitadas. | |
MX2007013085A (es) | Metodos para formar una sal de metal alcalino. | |
NZ594684A (en) | Aqueous sol containing colloidal silica-based particles having high axial ratio and high specific surface area | |
NO20060611L (no) | Stabile ikke-dihydratazitromycin oralsuspensjoner | |
TW200622777A (en) | Manufacturing-order giving system and method thereof |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 08711863 Country of ref document: EP Kind code of ref document: A1 |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2009503952 Country of ref document: JP |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 08711863 Country of ref document: EP Kind code of ref document: A1 |