WO2008083244A1 - Tire compositions and components containing silated core polysulfides - Google Patents

Abstract

Sulfur-containing silane coupling agents, and organic polymers containing carbon-carbon double bonds. These silanes can be carried on organic and inorganic fillers. The invention also relates to tire compositions and articles of manufacture, particularly tires, made from elastomer compositions.

Description

TIRE COMPOSITIONS AND COMPONENTS CONTAINING SILATED CORE POLYSULFIDES

The present application is directed to an invention which was developed pursuant to a joint research agreement within meaning of 35 U.S.C^KBCc). The joint research agreement dated May 7, 2001 as amended, between Continental AG, and General Electric Company, on behalf of GE Advanced Materials, Silicones Division, now Momentive Performance Materials

Inc.

CROSS-REFERENCE TO RELATED APPLICATIONS This application claims priority to U.S. Application No. 11/617,663 filed December 28,

2006, the content of which is incorporated herein by reference in its entirety.

The present application is related to the following applications, filed December 28, 2006, with the disclosures of each of the applications being incorporated by reference herein in their entireties: Application No. 11/617,683, filed December 28, 2006, entitled Tire Compositions And

Components Containing Silated Cyclic Core Polysufides.

Application No. 11/617,649, filed December 28, 2006, entitled Tire Compositions And Components Containing Free-Flowing Filler Compositions.

Application No. 11/617,678, filed December 28, 2006, entitled Tire Compositions And Components Containing Free-Flowing Filler Compositions.

Application No. 11/617,659, filed December 28, 2006, entitled Tire Compositions and Components Containing Blocked Mercaptosilane Coupling Agent.

Application No. 11/648,460, filed December 28, 2006, entitled Free-Flowing Filler Composition And Rubber Composition Containing Same. Application No. 11/647,903, filed December 28, 2006, entitled Free-Flowing Filler

Composition And Rubber Composition Containing Same.

Application No. 11/647,780, filed December 28, 2006, entitled Blocked Mercaptosilane Coupling Agents, Process For Making And Uses In Rubber.

Application No. 11/648,287, filed December 28, 2006, entitled Silated Core Polysulfides, Their Preparation And Use In Filled Elastomer Compositions.

Application No. 11/647,901, filed December 28, 2006, entitled Silated Cyclic Core Polysulfides, Their Preparation And Use In Filled Elastomer Compositions.

1. Field of the Invention The present invention generally relates to silated core polysulfides compositions, processes for their preparation, and tire compositions and tire components comprising the same. 2. Background of the Invention

Sulfur-containing coupling agents used for mineral-filled elastomers involve silanes in which two alkoxysilylalkyl groups are bound, each to one end of a chain of sulfur atoms. The two alkoxysilyl groups are bonded to the chain of sulfur atoms by two similar, and in most cases, identical, hydrocarbon fragments. The general silane structures just described, hereinafter referred to as "simple bis polysulfide silanes," usually contain a chain of three methylene groups as the two mediating hydrocarbon units. In some cases, the methylene chain is shorter, containing only one or two methylenes per chain. The use of these compounds is primarily as coupling agents for mineral-filled elastomers. These coupling agents function by chemically bonding silica or other mineral fillers to polymer when used in rubber applications. Coupling is accomplished by chemical bond formation between the silane sulfur and the polymer and by hydrolysis of the alkoxysilyl groups and subsequent condensation with silica hydroxyl groups. The reaction of the silane sulfur with the polymer occurs when the S-S bonds are broken and the resulting fragment adds to the polymer. A single linkage to the polymer occurs for each silyl group bonded to the silica. This linkage contains a single, relatively weak C-S and/or S-S bond(s) that forms the weak link between the polymer and the silica. Under high stress, this single C-S and/or S-S linkages may break and therefore contribute to wear of the filled elastomer.

The use of polysulfide silanes coupling agents in the preparation of rubber is well known. These silanes contain two silicon atoms, each of which is bound to a disubstituted hydrocarbon group, and three other groups of which at least one is removable from silicon by hydrolysis. Two such hydrocarbon groups, each with their bound silyl group, are further bound to each end of a chain of at least two sulfur atoms. These structures thus contain two silicon atoms and a single, continuous chain of sulfur atoms of variable length. Hydrocarbon core polysulfide silanes that feature a central molecular core isolated from the silicon in the molecule by sulfur-sulfur bonds are known in the art. Polysufide silanes containing a core that is an aminoalkyl group separated from the silicon atom by a single sulfur and a polysulfide group and where the polysulfide group is bonded to the core at a secondary carbon atom are also know in the art. As well as core fragments in which only two polysulfide groups are attached to the core.

When the polysulfide groups are attached directly to an aromatic core, the reactivity with the polymer (rubber) is reduced. The aromatic core is sterically bulky which inhibits the reaction. Compositions in which the polysulfides are attached directly to cyclic aliphatic fragments derived by vinyl cyclohexene contain more than one silated core and form large rings. The cyclohexyl core is sterically more hindered than the aromatic core and is less reactive. A t oug t ese compos t ons can rm more t an one su ur n age to the polymer rubber for each attachment of the coupling agent to the silica through the silyl group, their effectiveness is low due to the low reactivity.

Without being bound by theory, the low reactivity is due to the attachment of the polysulfide to the secondary carbon of cyclic core structure. The positioning of the polysulfide group is not optimal for reaction with the accelerators and reaction with the polymer.

The present invention overcomes the deficiencies of the aforementioned compositions involving silane coupling agents in several ways. The silanes of the present invention described herein are not limited to two silyl groups nor to one chain of sulfur atoms. In fact the molecular architecture in which multiple polysulfide chains are oriented in a noncollinear configuration (i.e., branched, in the sense that the branch points occur within the carbon backbone interconnecting the polysulfide chains) is novel.

The silanes of the present invention have advantages over that in the prior art by providing multiple points of sulfur attachment to polymer per point of silicon attachment to filler. The silanes described herein may be asymmetric with regard to the groups on the two ends of the sulfur chains. The silyl groups, rather than occurring at the ends of the molecule, tend to occur more centrally and are chemically bonded to the core through carbon-carbon or carbon-silicon bonds. The core also contains multiple polysulfide groups that are attached to a primary carbon atom. The attachment decreases significantly the steric hindrance of the core, and increases the reactivity of the polysulfides with the polymer. This distinction is what allows silane silicon to become and remain bonded (through the intermediacy of a sequence of covalent chemical bonds) to polymer at multiple points using the silanes of the present invention.

Also, without being bound by theory, silated core silanes of the present invention include a Y-core structure. This Y-core structure is believed to enable bonding the polymer at two different points or crosslinking on two different polymer chains, and also enables attachment, such as by bonding, to a filler.

The examples presented herein demonstrate that the silanes of the present invention impart a desirable balance of physical properties (performance to mineral-filled elastomer compositions) and better wear characteristics to articles manufactured from these elastomers. Improvements in rolling resistance are also apparent for elastomers used in tire applications.

SUMMARY OF THE INVENTION

In a first embodiment of the present invention, silated core polysulfides of the general Formula (1) [Y¹R¹S_x-]_m[G¹(R²SiX¹X²X³)J_n[G²]₀[R³Y²]_p (1) are provided, wherein each occurrence of G is independently selected from a polyvalent hydrocarbon species having from 1 to about 30 carbon atoms and containing a polysulfide group represented by Formula (2)

[(CH₂)_b-]_cR⁴[-(CH₂)_dS_x-]_e; (2) each occurrence of G² is independently selected from a polyvalent hydrocarbon species of 1 to about 30 carbon atoms and containing a polysulfide group represented by Formula (3) [(CH₂)_b-]_cR⁵[-(CH₂)_dS_x-]_e; (3) each occurrence of R¹ and R³ are independently selected from a divalent hydrocarbon fragment having from 1 to about 20 carbon atoms that include branched and straight chain alkyl, alkenyl, alkynyl, aryl or aralkyl groups in which one hydrogen atom was substituted with a Y¹ or Y² group; each occurrence of Y¹ and Y² is independently selected from, but not limited to silyl (- SiX¹X²X³), carboxylic acid (-C(O)OH), ester (-C(=O)OR⁶), in which R⁶ is any monovalent hydrocarbon group having from 1 to 20 carbon atoms, and includes branched or straight chain alkyl, alkenyl, aryl or aralkyl groups, hydrogen and the like; each occurrence of R² is a straight chain hydrocarbon represented by -(CH₂)_f-; each occurrence of R⁴ is chosen independently from a polyvalent hydrocarbon fragment of 1 to about 28 carbon atoms that was obtained by substitution of hydrogen atoms equal to the sum of a + c + e, and include cyclic, branched and straight chain alkyl, alkenyl, alkynyl, aryl and aralkyl groups in which a + c + e -1 hydrogens have been replaced, or a polyvalent heterocarbon fragment from 1 to 27 carbon atoms; each occurrence of R⁵ is independently selected from a polyvalent hydrocarbon fragment of 1 to about 28 carbon atoms that was obtained by substitution of hydrogen atoms equal to the sum of c + e, and include cyclic, branched and straight chain alkyl, alkenyl, alkynyl, aryl and aralkyl groups in which c + e - 1 hydrogens have been replaced, or a polyvalent heterocarbon fragment from 1 to 27 carbon atoms; each occurrence of X¹ is independently selected from hydrolyzable groups selected from -Cl, -Br, -OH, -OR⁶, and R⁶C(=O)O-, wherein R⁶ is any monovalent hydrocarbon group having from 1 to 20 carbon atoms, and includes branched or straight chain alkyl, alkenyl, aryl or aralkyl groups; each occurrence of X² and X³ is independently selected from hydrogen, any of R⁶ as listed above, any of X¹ as listed above, and -OSi containing groups that result from the condensation of silanols; and each occurrence of the subscripts, a, b, c, d, e, f, m, n, o, p, and x, is independently given by a is 1 to about 3; b is 1 to about 5; c is 1 to about 3; d is 1 to about 5; e is 1 to about 3; f is 0 to about 5; m is 1 to about 100, n is 1 to about 15; o is 0 to about 10; p is 1 to about 100, and x is 1 to about 10.

In a second embodiment of the present invention, a process for the preparation of the silated core polysulfide composition comprising reacting a hydrocarbon or heterocarbon containing vinyl groups with HSiX¹X²X³, wherein each of X¹, X² and X³ are as defined above, the resultant silylated hydrocarbon or silylated heterocarbon is reacted with a thioacid, the acyl group is removed, and the mercapto groups are reacted with base and sulfur and followed by the reaction of a halo containing hydrocarbon silane is disclosed.

In accordance with a third embodiment of the present invention, a rubber composition is provided comprising (a) a rubber component; (b) an inorganic filler; and a silated core polysulfide composition having the general formula

[Y¹R¹S_x-]_m[G¹(R²SiX¹X²X³)_a]_n[G²]₀[R³Y²]p wherein Y¹, R¹ S, G¹' R² , X¹, X² , X³ , G² , R³, Y², a, o, p, x, m, and n have the aforestated meanings. The present invention is also directed to tire compositions for forming tire components, the compositions being formed by combining:

(a) a silated core polysulfide of the general formula

[Y¹R¹S_x-]_m[G¹(R²SiX¹X²X³)_a]_n[G²]o[R³Y²]p wherein: each occurrence of G¹ is independently selected from a polyvalent hydrocarbon species having from 1 to about 30 carbon atoms containing a polysulfide group represented by the general formula:

[(CH₂)_b-]_cR⁴[-(CH₂)_dS_x-]_e; each occurrence of G² is independently selected from a polyvalent hydrocarbon species of 1 to about 30 carbon atoms containing a polysulfide group represented by the general formula:

[(CH₂)_b-]_cR⁵[-(CH₂)_dS_x-]_e; each occurrence of R¹ and R³ is independently selected from a divalent hydrocarbon fragment having from 1 to about 20 carbon atoms; each occurrence of Y¹ and Y² is independently selected from silyl (-SiX¹X²X³), hydrogen, carboxylic acid, and ester (-C(=O)OR⁶) wherein R⁶ is a monovalent hydrocarbon group having from 1 to 20 carbon atoms; each occurrence of R² is a straight chain hydrocarbon represented by -(CH₂)_f-; each occurrence of R⁴ is independently selected from a polyvalent hydrocarbon fragment of 1 to about 28 carbon atoms; each occurrence of R is independently selected from a polyvalent hydrocarbon fragment of 1 to about 28 carbon atoms; each occurrence of X¹ is independently selected from -Cl, -Br, -OH, -OR⁶, and R⁶C(=O)O-, wherein R⁶ is a monovalent hydrocarbon group having from 1 to 20 carbon atoms; each occurrence of X² and X³ is independently selected from hydrogen, R⁶, wherein R⁶ is a monovalent hydrocarbon group having from 1 to 20 carbon atoms, X¹, wherein X¹ is independently selected from -Cl, -Br, -OH, -OR⁶, and R⁶C(=O)O-, wherein R⁶ is a monovalent hydrocarbon group having from 1 to 20 carbon atoms , and -OSi containing groups that result from the condensation of silanols; and each occurrence of the subscripts, a, b, c, d, e, f, m, n, o, p, and x, is independently given wherein a, c and e are 1 to about 3; b is 1 to about 5; d is 1 to about 5; f is 0 to about 5; m and p are 1 to about 100; n is 1 to about 15; o is 0 to about 10; and x is 1 to about 10;

(b) at least one vulcanizable rubber selected from natural rubbers, synthetic polyisoprene rubbers, polyisobutylene rubbers, polybutadiene rubbers, and random styrene-butadiene rubbers (SBR); and

(c) an active filler including at least one of active filler selected from carbon blacks, silicas, silicon based fillers, and metal oxides present in a combined amount of at least 35 parts by weight per 100 parts by weight of total vulcanizable rubber, of which at least 10 parts by weight is carbon black, silica, or a combination thereof; and wherein the tire composition is formulated to be vulcanizable to form a tire component compound having a Shore A Hardness of not less than 40 and not greater than 95 and a glass- transition temperature Tg (E"_max) not less than -80 ⁰C and not greater than 0 ⁰C.

The present invention is also directed to tires at least one component of which comprises cured tire compositions obtained from rubber compositions according to the present invention. The present invention is also directed to tire components, cured and uncured, including, but not limited to, tire treads, including any tire component produced from any composition including at least a silated core polysulfide.

The compositions of the present invention exhibit excellent dispersion of filler and can achieve excellent workability, and improved productivity in vulcanization.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention is further described in the detailed description that follows by way of non-limiting examples of exemplary embodiments of the present invention, wherein: Fig. 1 shows HPLC analysis of the product of Example 1.

DETAILED DESCRIPTIONS OF THE PRESENT INVENTION The silated core polysulfides of the present invention are represented by Formula (1) [Y^'Sx-lmtG'CR'SiX'X'X^Jn^otR'Y^p (1) wherein each occurrence of G¹ is independently selected from a polyvalent hydrocarbon species having from 1 to about 30 carbon atoms and containing a polysulfide group represented by Formula (2)

[(CH₂)_b -]_cR⁴[-(CH₂)_dS_x-]_e; (2) each occurrence of G² is independently selected from a polyvalent hydrocarbon species of 1 to about 30 carbon atoms and containing a polysulfide group represented by Formula (3) [(CH₂)_b-]_cR⁵[-(CH₂)_dS_x-]_e; (3) each occurrence of R¹ and R³ are independently selected from a divalent hydrocarbon fragment having from 1 to about 20 carbon atoms that include branched and straight chain alkyl, alkenyl, alkynyl, aryl or aralkyl groups in which one hydrogen atom was substituted with a Y¹ or Y² group; each occurrence of Y¹ and Y² is independently selected from, but not limited to silyl (- SiX¹X²X³), carboxylic acid (-C(=O)OH), ester (-C(=O)OR⁶), wherein R⁶ is a monovalent hydrocarbon group having from 1 to 20 carbon atoms, and includes branched or straight chain alkyl, alkenyl, aryl or aralkyl groups, hydrogen and the like; each occurrence of R² is a straight chain hydrocarbon represented by -(CH₂)_f-; each occurrence of R⁴ is chosen independently from a polyvalent hydrocarbon fragment of 1 to about 28 carbon atoms that was obtained by substitution of hydrogen atoms equal to the sum of a + c + e, and include cyclic, branched and straight chain alkyl, alkenyl, alkynyl, aryl and aralkyl groups in which a + c + e -1 hydrogens have been replaced or a polyvalent heterocarbon fragment from 1 to 27 carbon atoms; each occurrence of R⁵ is independently selected from a polyvalent hydrocarbon fragment of 1 to about 28 carbon atoms that was obtained by substitution of hydrogen atoms equal to the sum of c + e, and include cyclic, branched and straight chain alkyl, alkenyl, alkynyl, aryl and aralkyl groups in which c + e - 1 hydrogens have been replaced or a polyvalent heterocarbon fragment from 1 to 27 carbon atoms; each occurrence of X¹ is independently selected from any of hydrolyzable groups selected from -Cl, -Br, -OH, -OR⁶, and R⁶C(=O)O-, wherein R⁶ is any monovalent hydrocarbon group having from 1 to 20 carbon atoms, and includes branched or straight chain alkyl, alkenyl, aryl or aralkyl groups; eac occurrence o an s n epen ent y se ecte om y rogen, any o as ste above, any of X¹ as listed above, and -OSi containing groups that result from the condensation of silanols; and each occurrence of the subscripts, a, b, c, d, e, f, m, n, o, p, and x, is independently given by a is 1 to about 3; b is 1 to about 5; c is 1 to about 3; d is 1 to about 5; e is 1 to about 3; f is 0 to about 5; m is 1 to about 100, n is 1 to about 15; o is 0 to about 10; p is 1 to about 100, and x is 1 to about 10.

The term, "heterocarbon", as used herein, refers to any hydrocarbon structure in which the carbon-carbon bonding backbone is interrupted by bonding to hetero atoms, such as atoms of nitrogen, sulfur, phosphorus and/or oxygen, or in which the carbon-carbon bonding backbone is interrupted by bonding to groups of atoms containing sulfur, nitrogen and/or oxygen, such as cyanurate (C₃N₃). Heterocarbon fragments also refer to any hydrocarbon in which a hydrogen or two or more hydrogens bonded to carbon are replaced with a sulfur, oxygen or nitrogen atom, such as a primary amine (-NH₂), and oxo (=O), and the like. Thus, R⁴ and R⁵ include, but are not limited to branched, straight-chain, cyclic, and/or polycyclic polyvalent aliphatic hydrocarbons, optionally containing ether functionality via oxygen atoms each of which is bound to two separate carbon atoms, polysulfϊde functionality, in which the polysulfide group (-S_x-) is bonded to two separate carbon atoms on G¹ or G² to form a ring, tertiary amine functionality via nitrogen atoms each of which is bound to three separate carbon atoms, cyano (CN) groups, and/or cyanurate (C3N3) groups; aromatic hydrocarbons; and arenes derived by substitution of the aforementioned aromatics with branched or straight chain alkyl, alkenyl, alkynyl, aryl and/or aralkyl groups.

As used herein, "alkyl" includes straight, branched and cyclic alkyl groups; "alkenyl" includes any straight, branched, or cyclic alkenyl group containing one or more carbon-carbon double bonds, where the point of substitution can be either at a carbon-carbon double bond or elsewhere in the group; and "alkynyl" includes any straight, branched, or cyclic alkynyl group containing one or more carbon-carbon triple bonds and optionally also one or more carbon- carbon double bonds as well, where the point of substitution can be either at a carbon-carbon triple bond, a carbon-carbon double bond, or elsewhere in the group. Examples of alkyls include, but are not limited to methyl, ethyl, propyl, isobutyl. Examples of alkenyls include, but are not limited to vinyl, propenyl, allyl, methallyl, ethylidenyl norbornane, ethylidene norbornyl, ethylidenyl norbornene, and ethylidene norbornenyl. Some examples of alkynyls include, but are not limited to acetylenyl, propargyl, and methylacetylenyl.

As used herein, "aryl" includes any aromatic hydrocarbon from which one hydrogen atom has been removed; "aralkyl" includes any of the aforementioned alkyl groups in which one or more hydrogen atoms have been substituted by the same number of like and/or different aryl

(as defined herein) substituents; and "arenyl" includes any of the aforementioned aryl groups in which one or more hydrogen atoms have been substituted by the same number of like and/or different alkyl (as defined herein) substituents. Some examples of aryls include, but are not limited to phenyl and naphthalenyl. Examples of aralkyls include, but are not limited to benzyl and phenethyl, and some examples of arenyls include, but are not limited to tolyl and xylyl.

As used herein, "cyclic alkyl", "cyclic alkenyl", and "cyclic alkynyl" also include bicyclic, tricyclic, and higher cyclic structures, as well as the aforementioned cyclic structures further substituted with alkyl, alkenyl, and/or alkynyl groups. Representative examples include, but are not limited to norbornyl, norbornenyl, ethylnorbornyl, ethylnorbornenyl, ethylcyclohexyl, ethylcyclohexenyl, cyclohexylcyclohexyl, and cyclododecatrienyl, and the like.

Representative examples of X¹ include, but are not limited to methoxy, ethoxy, propoxy, isopropoxy, butoxy, phenoxy, benzyloxy, hydroxy, chloro, and acetoxy. Representative examples of X² and X³ include the representative examples listed above for X¹ as well as hydrogen, methyl, ethyl, propyl, isopropyl, sec-butyl, phenyl, vinyl, cyclohexyl, and higher straight-chain alkyl, such as butyl, hexyl, octyl, lauryl, and octadecyl.

Representative examples of R¹ and R³ include the terminal straight-chain alkyls further substituted terminally at the other end, such as -CH₂-, -CH₂CH₂-, -CH₂CH₂CH₂-, and -CH₂CH₂CH₂CH₂CH₂CH₂CH₂CH₂-, and their beta-substituted analogs, such as -CH₂(CH₂)_UCH(CH₃)-, where u is zero to 17; the structure derivable from methallyl chloride, -CH₂CH(CH₃)CH₂-; any of the structures derivable from divinylbenzene, such as -CH₂CH₂(C₆H₄)CH₂CH₂- and -CH₂CH₂(C₆H₄)CH(CH₃)-, where the notation C₆H₄ denotes a disubstituted benzene ring; any of the structures derivable from diallylether, such as -CH₂CH₂CH₂OCH₂CH₂CH₂- and -CH₂CH₂CH₂OCH₂CH(CH₃)-; any of the structures derivable from butadiene, such as -CH₂CH₂CH₂CH₂-, -CH₂CH₂CH(CH₃)-, and -CH₂CH(CH₂CH₃)-; any of the structures derivable from piperylene, such as -CH₂CH₂CH₂CH(CH₃)-, -CH₂CH₂CH(CH₂CH₃)-, and -CH₂CH(CH₂CH₂CH₃)-; any of the structures derivable from isoprene, such as -CH₂CH(CH₃)CH₂CH₂-, -CH₂CH(CH₃)CH(CH₃)-, -CH₂C(CH₃)(CH₂CH₃)-, - CH₂CH₂CH(CH₃)CH₂-, -CH₂CH₂C(CH₃)₂- and -CH₂CH[CH(CH₃)₂]-; any of the isomers of -CH₂CH₂-norbornyl-, -CH₂CH₂-cyclohexyl-; any of the diradicals obtainable from norbornane, cyclohexane, cyclopentane, tetrahydrodicyclopentadiene, or cyclododecene by loss of two hydrogen atoms; the structures derivable from limonene, -CH₂CH(4-methyl-l-C₆H₉-)CH₃, where the notation C₆H₉ denotes isomers of the trisubstituted cyclohexane ring lacking substitution in the 2 position; any of the monovinyl-containing structures derivable from trivinylcyclohexane, such as -CH₂CH₂(vinylC₆H₉)CH₂CH₂- and -CH₂CH₂(vinylC₆H₉)CH(CH₃)-, where the notation C₆H₉ denotes any isomer of the trisubstituted cyclohexane ring; any of the monounsaturated structures derivable from myrcene containing a trisubstituted C=C, such as

-CH₂CH[CH₂CH₂CH=C(CH₃)₂]CH₂CH₂-, -CH₂CH[CH₂CH₂CH=C(CHS)₂]CH(CH₃)-,

-CH₂C[CH₂CH₂CH=C(CH₃)₂](CH₂CH₃)-, -CH₂CH₂CH[CH₂CH₂CH=C(CH₃)₂]CH₂-, -CH₂CH₂(C-)(CH₃)[CH₂CH₂CH=C(CH₃)₂], and

-CH₂CH[CH(CH₃)[CH₂CH₂CH=C(CH₃)₂]]-; and any of the monounsaturated structures derivable from myrcene lacking a trisubstituted C=C, such as

-CH₂CH(CH=CH₂)CH₂CH₂CH₂C(CH₃)₂-, -CH2CH(CH=CH2)CH₂CH₂CH[CH(CH₃)₂]-,

-CH₂C(=CH-CH₃)CH₂CH₂CH₂C(CH3)₂-, -CH₂C(=CH-CH₃)CH₂CH₂CH[CH(CH₃)₂]-, -CH₂CH₂C(=CH₂)CH₂CH₂CH2C(CH3)₂-, -CH₂CH₂C(=CH₂)CH₂CH₂CH[CH(CH₃)₂]-,

-CH₂CH=C(CH₃)₂CH₂CH₂CH₂C(CH₃)₂-, and -CH₂CH=C(CH₃)₂CH₂CH₂CH[CH(CH₃)₂] .

Representative examples of tridentate G¹ include, but are not limited to, structures derivable from nonconjugated terminal diolefins, such as -CH₂(CH₂)_?+i CH(CH₂-)- and

-CH(CH₃)(CH₂)_?CH(CH₂-)₂, in which q is zero to 20; any of the structures derivable from divinylbenzene, such as -CH₂CH₂(C₆H₄)CH(CH₂-)- and -CH₂CH₂(C₆Hr)CH₂CH₂-, where the notation C₆H₄ denotes a disubstituted benzene ring and C₆H₃- denotes a trisubstituted ring; structures derivable from butadiene, such as -CH₂(CH-)CH₂CH₂-; any of the structures derivable from isoprene, such as -CH₂(C-XCH₃)CH₂CH₂- and

-CH₂CH(CH₃)(CH-)CH₂-; any structures derivable from trivinylcyclohexane, such as -CH₂(CH-)(vinylC₆H₉)CH₂CH₂-; (-CH₂CH₂)₃C₆H₉, and (-CH₂CH₂)₂C₆H₉CH(CH₃)-, where the notation C₆H₉ denotes any isomer of the trisubstituted cyclohexane ring; any of the structures derivable from myrcene, such as,

-CH₂(C-)[CH₂CH₂CH=C(CH₃)₂]CH₂CH₂-, and

-CH₂CH[CH₂CH₂CH=C(CH₃)₂](CH-)CH₂-; the structures derivable from trimethylolalkanes, such as CH₃CH₂CH₂C(CHr)₃ and CH₃CH₂C(CH₂-)₃; glyceryl, whose structure is -CH₂(CH-

)CH₂-, and its methyl analog, whose structure is -CH₂(-CCH₃)CH₂-; and the triethanolamine derivative, (-CH₂CH₂)₃N.

Representative examples of polyvalent G¹ include, but are not limited to, structures derivable from nonconjugated terminal diolefins, such as -CH(CH₂-) (CH₂)_qCH(CH₂-)-, in which q is from 1 to 20; any of the structures derivable from divinylbenzene, such as

-CH₂(CH-XC₆H₄)CH(CH₂-)-, where the notation C₆H₄ denotes a disubstituted benzene ring; any of the structures derivable from diallylether, such as -CH₂(CH-)CH₂OCH₂CH(CH₂-)-; any of the structures derivable from butadiene, such as -CH₂(CH-)(CH-)CH₂-; any of the structures derivable from piperylene, such as -CH₂(CH-)(CH-)CH₂(CH₃)-; any of the structures derivable from isoprene, such as -CH₂(C-)(CH₃)(CH-)CH₂-; any of the vinyl-containing structures derivable from trivinylcyclohexane, such as -CH₂(CH-)(vinylC6H9)(CH-)CH₂-, -CH₂CH₂C₆H₉[(CH-)CH₂-]₂, -CH(CH₃)C₆H₉[(CH-)CH₂-]₂, and C₆H₉[(CH-)CH₂-]₃, where the notation C₆H₉ denotes any isomer of the trisubstituted cyclohexane ring; any of the saturated structures derivable from trivinylcyclohexane, such as -CH₂(CH-)C₆H₉[CH₂CH₂-]₂, and - CH₂(CH-)C₆H₉[CH(CH₃)-][CH₂CH₂-], where the notation C₆H₉ denotes any isomer of the trisubstituted cyclohexane ring; any of the monounsaturated structures derivable from myrcene containing a trisubstituted C=C, such as -CH₂(C-)[CH₂CH₂CH=C(CH₃)₂]CH₂CH₂-, -CH₂CH[CH₂CH₂CH=C(CH₃)₂](CH-)CH₂-; and pentaerythrityl, whose structure is C(CH₂-)₄. Representative examples of didentate G² include, but are not limited to, structures derivable from nonconjugated terminal diolefins, such as -CH₂(CH₂)^_+I CH₂(CH₂-) and CH₂(CH₃)(CH₂)_?CH(CH₂-)₂, in which q is zero to 20; any of the structures derivable from divinylbenzene, such as -CH₂CH₂(C₆H₄)CH₂CH₂-, where the notation C₆H₄ denotes a disubstituted benzene ring; any of the structures derivable from butadiene, such as -CH₂CH₂CH₂CH₂-; any of the structures derivable from isoprene, such as

-CH₂(CH)(CH₃)CH₂CH₂-, and -CH₂CH(CH₃)CH₂CH₂-; any structures derivable from trivinylcyclohexane, such as -CH₂CH₂(vinylC₆H₉)CH₂CH₂-, and

(-CH₂CH₂)C₆H₉CH₂CH₃, where the notation C₆H₉ denotes any isomer of the trisubstituted cyclohexane ring; any of the structures derivable from myrcene, such as, -CH₂(CH)[CH₂CH₂CH=C(CH₃)₂]CH₂CH₂-; and the diethanolamine derivative, (-CH₂CH₂)NCH₃.

Representative examples of tridentate G² include, but are not limited to, structures derivable from nonconjugated terminal diolefins, such as -CH₂(CH₂)₉₊i CH(CH₂-)- in which q is zero to 20; structures derivable from trivinylcyclohexane, such as (-CH₂CH₂)₃CόH₉, where the notation C₆H₉ denotes any isomer of the trisubstituted cyclohexane ring; the structures derivable from trimethylolalkanes, such as CH₃CH₂CH₂C(CH₂-)₃ and CH₃CH₂C(CHr)₃; and the triethanolamine derivative, (-CH₂CH₂)₃N.

Representative examples of silated core polysulfide silanes of the present invention include, but are note limited to, any of the isomers of 2-triethoxysilyl-l,3-bis-(3-triethoxysilyl-l- propyltetrathia)propane, 4-(2-triethoxysilyl-l-ethyl)-l,2-bis-(13-triethoxysilyl-3,4,5,6- tetrathiatridecyl)cyclohexane; 4-(2-triethoxysilyl-l-ethyl)-l,2-bis-(13-triethoxysilyl-3,4,5,6- tetrathiatridecyl)cyclohexane; 4-(2-diethoxymethylsilyl- 1 -ethyl)- 1 ,2-bis-( 13-triethoxysilyl- 3,4,5,6-tetrathiatridecyl)cyclohexane; 4-(2-triethoxysilyl-l -ethyl)- l,2-bis-(l O-triethoxysilyl- 3,4,5,6,7-pentathiadecyl)cyclohexane; l-(2-triethoxysilyl-l-ethyl)-2,4-bis-(10-triethoxysilyl- 3,4,5,6,7-pentathiadecyl)cyclohexane; 4-(2-triethoxysilyl- 1 -ethyl)- 1 ,2-bis-(9-triethoxysilyl- 3,4,5,6-tetrathianonyl)cyclohexane; 1 -(2-triethoxysilyl- 1 -ethyl)-2,4-bis-(9-triethoxysilyl-3,4,5,6- tetrathianonyl)cyclohexane; 2-(2-triethoxysilyl- 1 -ethyl)- 1 ,4-bis-(9-triethoxysilyl-3,4,5,6- tetrathianonyl)cyclohexane; 4-(2-triethoxysilyl- 1 -ethyl)- 1 ,2-bis-(8-triethoxysilyl-3,4,5- trithiaoctyl)cyclohexane; 1 -(2-triethoxysilyl- 1 -ethyl)-2,4-bis-(8-triethoxysilyl-3,4,5- trithiaoctyl)cyclohexane; 2-(2-triethoxysilyl-l-ethyl)-l,4-bis-(8-triethoxysilyl-3,4,5- trithiaoctyl)cyclohexane; 4-(2-triethoxysilyl- 1 -ethyl)- 1 ,2-bis-(7-triethoxysilyl-3,4- dithiaheptyl)cyclohexane; 2-(2-triethoxysilyl- 1 -ethyl)- 1 ,4-bis-(7-triethoxysilyl-3,4- dithiaheptyl)cyclohexane; 1 -(2-triethoxysilyl- 1 -ethyl)-2,4-bis-(7-triethoxysilyl-3,4- dithiaheptyl)cyclohexane; 2-(2-triethoxysilyl- 1 -ethyl)- 1 -(7-triethoxysilyl-3 ,4-dithiaheptyl)-2-(8- triethoxysilyl-3,4,5-trithiaoctyl)cyclohexane; 4-(2-triethoxysilyl-l -ethyl)- l,2-bis-(9- triethoxysilyl-3,4,5,6-tetrathianonyl)benzene; bis-[2-[4-(2-triethoxysilyl-l-ethyl)-2~(9- triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexyl]ethyl] tetrasulfide; bis-[2-[4-(2-triethoxysilyl- 1 - ethyl)-2-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexyl]ethyl] trisulfide; bis-[2-[4-(2- triethoxysilyl- 1 -ethyl)-2-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexyl]ethyl] disulfide; bis- [2-[4-(2-triethoxysilyl-l-ethyl)-2-(7-triethoxysilyl-3,4-dithiaheptyl)cyclohexyl]ethyl] disulfide; bis-2-[4-(2-triethoxysilyl-l-ethyl)-2-(7-triethoxysilyl-3,4-dithiaheptyl)cyclohexyl]ethyl] trisulfide; bis-[2-[4-(2-triethoxysilyl-l-ethyl)-2-(7-triethoxysilyl-3,4- dithiaheptyl)cyclohexyl]ethyl tetrasulfide; bis-[2-[4-(2-triethoxysilyl- 1 -ethyl)-2~(9- triethoxysilyl-3,4,5,6-tetrathianonyl)phenyl]ethyl] tetrasulfide; bis-2-[4-(2-triethoxysilyl- 1 - ethyl)-3-bis-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexyl]ethyl] trisulfide; bis-[2-[4-(2- diiethoxymethylsilyl-l-ethyl)-2-(7-triethoxysilyl-3,4-dithiaheptyl)cyclohexyl]ethyl disulfide.

The silated core polysulfide silanes of the present invention also include any isomer of (2-triethoxysilylethyl)-bis-(7-triethoxysilyl-3,4-dithiaheptyl)cyclohexane or any isomer of (2- triethoxysilylethyl)~bis-(7-triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexane. In another embodiment of the present invention the Formulae (1), (2) and (3), are described wherein each occurrence of R¹ and R³ are independently selected from a divalent hydrocarbon fragment having from 1 to about 5 carbon atoms that include branched and straight chain alkyl, alkenyl, alkynyl, aryl or aralkyl groups in which one hydrogen atom was substituted with a Y¹ or Y² group; each occurrence of Y¹ and Y² is chosen independently from silyl (-SiX',X²,X³); each occurrence of R² is a straight chain hydrocarbon represented by -(CH₂)_f - where f is an integer from about 0 to about 3; each occurrence of R⁴ is chosen independently from a polyvalent hydrocarbon fragment of 3 to about 10 carbon atoms that was obtained by substitution of hydrogen atoms equal to the sum of a + c + e, and include cyclic alkyl or aryl in which a + c + e -1 hydrogens have been replaced; each occurrence of R⁵ is chosen independently from a polyvalent hydrocarbon fragment of 3 to about 10 carbon atoms that was obtained by substitution of hydrogen atoms equal to the sum of c + e, and include branched and straight chain alkyl, alkenyl, alkynyl, aryl and aralkyl groups in which c + e - 1 hydrogens have been replaced; each occurrence of X¹ is chosen independently from any of hydrolyzable groups selected from - OH, and -OR⁶, in which R⁶ is any monovalent hydrocarbon group having from 1 to 5 carbon atoms, and includes branched or straight chain alkyl, alkenyl, aryl or aralkyl groups; each occurrence of X² and X³ is chosen independently R⁶ as defined for this embodiment, any of X¹ as defined for this embodiment, and -OSi containing groups that result from the condensation of silanols; each occurrence of the subscripts, a, b, c, d, e, f, m, n, o, p, and x, is independently given by a is 1 to about 2; b is 1 to about 3; c is 1; d is 1 to about 3; e is 1; f is O to about 3; m is 1, n is 1 to about 10; o is 0 to about 1 ; p is 1, and x is 1 to about 4.

In another embodiment, 30 to 99 weight percent of the silated core polysulfide of the present invention is blended with 70 to 1 weight percent of another silane, including silanes of the structure represented in Formula (4)

[X¹X²X³SiR¹S_xR³SiX¹X²X³] (4) wherein each occurrence of R¹ and R³ are chosen independently from a divalent hydrocarbon fragment having from 1 to about 20 carbon atoms that include branched and straight chain alkyl, alkenyl, alkynyl, aryl or aralkyl groups in which one hydrogen atom was substituted with independently a -SiX¹X²X³ group, wherein X¹ is chosen independently from any of hydrolyzable groups selected from -Cl, -Br, -OH, -OR⁶, and R⁶C(=O)O-, in which R⁶ is any monovalent hydrocarbon group having from 1 to 20 carbon atoms, and includes branched or straight chain alkyl, alkenyl, aryl or aralkyl group, and X² and X³ are independently taken from hydrogen, R⁶ as defined above, any of X¹ as defined above, and -OSi containing groups that result from the condensation of silanols.

Representative examples of the silanes described by Formula 4 are listed in U.S. Patent 3,842,111, which is incorporated herein by reference, and include bis-(3-triethoxysilylpropyl) disulfide; bis-(3-triethoxysilylpropyl) trisulfide; bis-(3-triethoxysilylpropyl) tetrasulfide; bis-(3- triethoxysilylpropyl) pentasulfide; bis-(3-diethoxymethylsilylpropyl) disulfide; bis-(3- ethoxydimethylsilylpropyl) disulfide; bis-(triethoxysilylmethyl) disulfide; bis-(4- triethoxysilylbenzyl) disulfide; bis-(3-triethoxysilylphenyl) disulfide and the like. The bonding of sulfur to a methylene group on R⁴ and R⁵ is desired because the methylene group mitigates excessive steric interactions between the silane and the filler and polymer. Two successive methylene groups mitigate steric interactions even further and also add flexibility to the chemical structure of the silane, thereby enhancing its ability to accommodate the positional and orientational constraints imposed by the morphologies of the surfaces of both the rubber and filler at the interphase, at the molecular level. The silane flexibility becomes increasingly important as the total number of silicon and sulfur atoms bound to G¹ and G² increases from 3 to 4 and beyond. Structures in which the polysulfide group is bonded directly to secondary and tertiary carbon atoms, ring structures, especially aromatic structures, are rigid and sterically hindered. The accelerators and curatives cannot readily orient themselves with the polysulfide group to affect reaction and the silated core polysulfide cannot readily orient itself to meet available binding sites on silica and polymer. This would tend to leave sulfur groups unbound to polymer, thereby reducing the efficiency by which the principle of multiple bonding of silane to polymer via multiple sulfur groups on silane, is realized.

The function of the other silanes in the blend is to occupy sites on the surface of the silica which aid in dispersing the silica and coupling with the polymer.

PROCESS FOR PREPARING SILATED CORE POLYSULFIDES In another embodiment of the present invention, the silated core polysulfides are prepared by (a) reacting a hydrosilane of the structure, HSi(X¹X²X³), with a hydrocarbon containing reactive double bonds; (b) reacting the intermediate product from (a) with a sulfuring agent, selected from the group R⁶C(=O)SH, where R⁶ is as previously defined, in the presence of a free radical agent; (c) deblocking the mercapto group using a proton donator; (d) reacting the intermediate mercaptan in (c) with a mixture of base and sulfur; and (e) reacting the intermediate in (d) with a substituted or unsubstituted hydrocarbon containing a leaving group selected from chlorine, bromine or iodine.

The structure of the hydrocarbon containing reactive double bonds in (a) can be represented by the chemical structure shown of Formula (5)

[CH₂=CH(CH₂)_g-]_cR⁴[-(CH₂)_hCH=CH₂]_e (5) (CH₂),CH=CH₂ wherein each occurrence is described supra and the subscripts g, h and i are independently given by g is about 0 to 3; h is 0 to about 3; and i is 0 to about 3.

The free radical reagent includes oxidizing agents that are capable of converting the thiocarboxylic acid to a thiocarboxylic acid radical, i.e. R⁶C(=O)S*, and include, but are not limited to oxygen, peroxides, hydroperoxides, and the like. The proton donor species are any hydrogen containing heterocarbon or substituted heterocarbon that is capable of reacting with the thiocarboxylic acid ester intermediate in (c) to generate an unblocked mercaptan. Representative examples of these hydrogen donor species include, but are not limited to, alcohols, such as methanol, ethanol, isopropyl alcohol, propanol, and the like; amines such as ammonia, methyl amine, propyl amine, diethanol amine, and the like; mercaptans, such as propyl mercaptans, butyl mercaptan, and the like.

The structure of the substituted or unsubstituted hydrocarbon containing a leaving group is represented by Formulae (6) and (7)

Y¹R¹Z (6) Y²R³Z (7) wherein each occurrence of Y¹, Y², R¹, and R³ are as previously defined and Z is selected from the group Cl, Br and I.

The reactions may be carried out in the presence or absence of organic solvents, including alcohols, ethers, hydrocarbon solvents, and the like. Representative examples of suitable organic solvents include, but are not limited to, ethanol, methanol, isopropyl alcohol, tetrahydrofuran, diethyl ether, hexanes, cyclohexane, toluene, xylenes, and mixtures thereof, and the like.

USE IN RUBBER COMPOSITIONS In one embodiment of the present invention, there is provided a rubber composition, such as a tire composition, comprising: (a) a rubber;

(b)the silated core polysulfide of the present invention (Formula 1); (c) a filler. In another embodiment of the present invention, there is provided a cured rubber composition, such as a cured tire composition, comprising: (a) a rubber;

(b)a silated core polysulfide of the present invention (Formula 1); (c) a filler; (d)curatives; and

(e) optionally, other additives.

The rubbers useful with the coupling agents described herein include sulfur vulcanizable rubbers including conjugated diene homopolymers and copolymers, and copolymers of at least one conjugated diene and aromatic vinyl compound. . Rubbers useful in the present invention include natural or synthetic elastomers, including polyisoprene rubbers, polyisobutylene rubbers, polybutadiene rubbers and styrenebutadiene rubbers. Preferably the rubbers are vulcanizable and suitable for tire compositions and tires, and components of tires. Suitable organic polymers for preparation of rubber compositions are well known in the art and are described in various textbooks including The Vanderbilt Rubber Handbook, Ohm, R.F., R.T. Vanderbilt Company, Inc., 1990 and in the Manual for the Rubber Industry, Kemperman, T and Koch, S. Jr., Bayer AG, LeverKusen, 1993, the disclosures of which are incorporated by reference herein in their entireties..

One example of a suitable polymer for use herein is solution-prepared styrene-butadiene rubber (SSBR). This solution prepared SSBR typically has a bound styrene content in a range of 5 to 50, preferably 9 to 36, percent. Other useful polymers include emulsion-prepared styrenebutadiene rubber (ESBR), natural rubber (NR), ethylene-propylene copolymers and terpolymers (EP, EPDM), acrylonitrile-butadiene rubber (NBR), polybutadiene (BR), and so forth.

In another embodiment, the rubber composition is comprised of at least one diene-based elastomer, or rubber. Suitable conjugated dienes include, but are not limited to, isoprene and 1,3-butadiene and suitable vinyl aromatic compounds include, but are not limited to, styrene and alpha methyl styrene. Polybutadiene may be characterized as existing primarily, typically about 90% by weight, in the cis-l,4-butadiene form, but other compositions may also be used for the purposes described herein.

Thus, the rubber is a sulfur curable rubber. Such diene based elastomer, or rubber, may be selected, for example, from at least one of cis-l,4-polyisoprene rubber (natural and/or synthetic), emulsion polymerization prepared styrene/butadiene copolymer rubber, organic solution polymerization prepared styrene/butadiene rubber, 3,4-polyisoprene rubber, isoprene/butadiene rubber, styrene/isoprene/butadiene terpolymer rubber, cis-l,4-polybutadiene, medium vinyl polybutadiene rubber (35-50 percent vinyl), high vinyl polybutadiene rubber (50- 75 percent vinyl), styrene/isoprene copolymers, emulsion polymerization prepared styrene/butadiene/acrylonitrile terpolymer rubber and butadiene/acrylonitrile copolymer rubber. For some applications, an emulsion polymerization derived styrene/butadiene (ESBR) having a relatively conventional styrene content of about 20 to 28 percent bound styrene, or an ESBR having a medium to relatively high bound styrene content of about 30 to 45 percent may be used. Emulsion polymerization prepared styrene/butadiene/acrylonitrile terpolymer rubbers containing 2 to 40 weight percent bound acrylonitrile in the terpolymer are also contemplated as diene based rubbers for use in this invention.

A particulate filler, particulate composition, includes a particle or grouping of particles to form aggregates or agglomerates, including reinforcement filler or particles, including without limitation, those containing or made from organic molecules, oligomers, and/or polymers, e.g., poly(arylene ether) resins, or functionalized reinforcement filler or particle. The term functionalized is intended to include any particles treated with an organic molecule, polymer, oligomer, or otherwise (collectively, treating agent(s)), thereby chemically bonding the treating agent(s) to the particle. The particulate filler of the present invention can be essentially inert to the silane with which it is admixed, or it can be reactive therewith. The particulate filler which may also be added to the crosslinkable elastomer compositions of the present invention includes siliceous fillers, carbon black, and so forth. The filler materials useful herein include, but are not limited to, metal oxides such as silica (pyrogenic and/or precipitated), titanium dioxide, aluminosilicate and alumina, clays and talc, carbon black, and so forth. Particulate, precipitated silica is also sometimes used for such purpose, particularly when the silica is used in conjunction with a silane. In some cases, a combination of silica and carbon black is utilized for reinforcing fillers for various rubber products, including treads for tires. Alumina can be used either alone or in combination with silica. The term, alumina, can be described herein as aluminum oxide, or Al₂O₃. The fillers may be hydrated or in anhydrous form.

The silated core polysulfide silane(s) may be premixed or pre-reacted with the filler particles, or added to the rubber mix during the rubber and filler processing, or mixing stages. If the silated core polysulfide silanes and filler are added separately to the rubber mix during the rubber and filler mixing, or processing stage, it is considered that the silated core polysulfide silane(s) then combine(s) in an in-situ fashion with the filler.

The vulcanized rubber composition should contain a sufficient amount of filler to contribute a reasonably high modulus and high resistance to tear. In one embodiment of the present invention, the combined weight of the filler may be as low as about 5 to about 120 parts per hundred parts rubber (phr), or about 5 to 100 pphr. In another embodiment, the combined weight of the filler is from about 25 to about 85 phr and at least one precipitated silica is utilized as a filler. The silica may be characterized by having a BET surface area, as measured using nitrogen gas, in the range of about 40 to about 600 m²/g. In another embodiment of the invention, the silica has a BET surface area in a range of about 50 to about 300 m²/g. The BET method of measuring surface area is described in the Journal of the American Chemical Society, Volume 60, page 304 (1930) ), which is incorporated by reference herein in its entirety. The silica typically may also be characterized by having a dibutylphthalate (DBP) absorption value in a range of about 100 to about 350, and more usually about 150 to about 300. Further, the silica, as well as the aforesaid alumina and aluminosilicate, may be expected to have a CTAB surface area in a range of about 100 to about 220. The CTAB surface area is the external surface area as evaluated by cetyl trimethylammonium bromide with a pH of about 9. The method is described in ASTM D 3849, which is incorporated by reference in its entirety..

Mercury porosity surface area is the specific surface area determined by mercury porosimetry. Using this method, mercury is penetrated into the pores of the sample after a thermal treatment to remove volatiles. Set up conditions may be suitably described as using about a 100 mg sample; removing volatiles during about 2 hours at about 105 ⁰C and ambient atmospheric pressure; ambient to about 2000 bars pressure measuring range. Such evaluation may be performed according to the method described in Winslow, Shapiro in ASTM bulletin, p.39 (1959) or according to DIN 66133, which are incorporated by reference in their entireties. For such an evaluation, a CARLO-ERBA Porosimeter 2000 might be used. The average mercury porosity specific surface area for the silica should be in a range of about 100 to about 300 m²/g.

In one embodiment, a suitable pore size distribution for the silica, alumina and aluminosilicate according to such mercury porosity evaluation is considered herein to be such that five percent or less of its pores have a diameter of less than about 10 nm, about 60 to about 90 percent of its pores have a diameter of about 10 to about 100 nm, about 10 to about 30 percent of its pores have a diameter at about 100 to about 1,000 nm, and about 5 to about 20 percent of its pores have a diameter of greater than about 1,000 nm.

In a second embodiment the silica might be expected to have an average ultimate particle size, for example, in the range of about 10 to about 50 nm as determined by the electron microscope, although the silica particles may be even smaller, or possibly larger, in size. Various commercially available silicas may be considered for use in this invention such as, from PPG Industries under the HI-SIL trademark with designations HI-SIL 210, 243, etc.; silicas available from Rhone-Poulenc, with, for example, designation of ZEOSIL 1165MP; silicas available from Degussa with, for example, designations VN2 and VN3, etc. and silicas commercially available from Huber having, for example, a designation of HUBERSIL7 8745.

In still another embodiment of the invention, the compositions may utilize fillers such as silica, alumina and/or aluminosilicates in combination with carbon black reinforcing pigments. The compositions may comprise a filler mix of about 15 to about 95 weight percent of the siliceous filler, and about 5 to about 85 weight percent carbon black, wherein the carbon black has a CTAB value in a range of about 80 to about 150. More typically, it is desirable to use a weight ratio of siliceous fillers to carbon black of at least about 3/1 in one embodiment, and at least about 10/1 in another embodiment. Thus, the weight ratio may range from about 3/1 to about 30/1 for siliceous fillers to carbon black. In another embodiment of the invention, the filler can be comprised of about 60 to about

95 weight percent of said silica, alumina and/or aluminosilicate and, correspondingly, about 40 to about 5 weight percent carbon black. The siliceous filler and carbon black may be pre-blended or blended together in the manufacture of the vulcanized rubber. In yet another embodiment of the present invention, the rubber compositions of the present invention are prepared by mixing one or more of the silated core polysulfide silanes with the organic polymer before, during or after the compounding of the filler into the organic polymer. In another embodiment, the silated core polysulfide silanes are added before or during the compounding of the filler into the organic polymer, because these silanes facilitate and improve the dispersion of the filler. In another embodiment, the total amount of silated core polysulfide silane present in the resulting combination should be about 0.05 to about 25 parts by weight per hundred parts by weight of organic polymer (phr); and 1 to 10 phr in another embodiment. In yet another embodiment, fillers can be used in quantities ranging from about 5 to about 120 phr, and still in another embodiment, fillers can be used in quantities ranging from about 25 to about 110 phr, or about 25 to about 105 phr.

Preferred compositions include those compositions useful for the manufacture of tires or tire components, including vehicle tires, and include rubber compositions that include at least one vulcanizable rubber, a silated core polysulfide, and at least one active filler such as, by way of nonlimiting example, carbon blacks, silicas, silicon based fillers, and metal oxides present either alone or in combinations. For example, an active filler may be selected from the group described above (e.g., carbon blacks, silicas, silicon based fillers, and metal oxides) and may be, but does not have to be, present in a combined amount of at least 35 parts by weight per 100 parts by weight of total vulcanizable rubber, of which at least 10 parts can be carbon black, silica, or some combination thereof, and wherein said compositions can be formulated so that they are vulcanizable to form a tire component compound. The tire component compounds may have a Shore A Hardness of not less than 40 and not greater than 95 and a glass-transition temperature Tg (E"_max) not less than -80 ⁰C and not greater than 0 ⁰C. The Shore A Hardness is measured in accordance with DIN 53505. The glass-transition temperature Tg (E"_max) is measured in accordance with DIN 53513 with a specified temperature sweep of -80 ⁰C to +80 ⁰C and a specified compression of 10 + 0.2 % at 10 Hz. Preferably, the rubber comprises vulcanizable rubbers selected from natural rubbers, synthetic polyisoprene rubbers, polyisobutylene rubbers, polybutadiene rubbers, random styrene-butadiene rubbers (SBR), and mixtures thereof. Moreover, an active filler includes a filler that is interactive with the rubber or tire composition and itself, and changes properties of the rubber or tire composition. Moreover, an active filler includes a filler that is interactive with the rubber or tire composition and itself, and changes properties of the rubber or tire composition.

In practice, sulfur vulcanized rubber products, such as tire components, typically are prepared by thermomechanically mixing rubber and various ingredients in a sequentially step-wise manner followed by shaping and curing the compounded rubber to form a vulcanized product. First, for the aforesaid mixing of the rubber and various ingredients, typically exclusive of sulfur and sulfur vulcanization accelerators (collectively, curing agents), the rubber(s) and various rubber compounding ingredients typically are blended in at least one, and often (in the case of silica filled low rolling resistance tires) two or more, preparatory thermomechanical mixing stage(s) in suitable mixers. Such preparatory mixing is referred to as nonproductive mixing or nonproductive mixing steps or stages. Such preparatory mixing usually is conducted at temperatures of about 140 ⁰C to about 200 ⁰C, and for some compositions, about 15O ⁰C to about 180 ⁰C. Subsequent to such preparatory mix stages, in a final mixing stage, sometimes referred to as a productive mix stage, curing agents, and possibly one or more additional ingredients, are mixed with the rubber compound or composition, at lower temperatures of typically about 50 ⁰C to about 130 ⁰C in order to prevent or retard premature curing of the sulfur curable rubber, sometimes referred to as scorching. The rubber mixture, also referred to as a rubber compound or composition, typically is allowed to cool, sometimes after or during a process intermediate mill mixing, between the aforesaid various mixing steps, for example, to a temperature of about 50 ⁰C or lower. When it is desired to mold and to cure the rubber, the rubber is placed into the appropriate mold at a temperature of at least about 130 ⁰C and up to about 200 ⁰C which will cause the vulcanization of the rubber by the S-S bond-containing groups (i.e., disulfide, trisulfide, tetrasulfide, etc.; polysulfide) on the silated core polysulfide silanes and any other free sulfur sources in the rubber mixture. Thermomechanical mixing refers to the phenomenon whereby under the high shear conditions in a rubber mixer, the shear forces and associated friction occurring as a result of mixing the rubber compound, or some blend of the rubber compound itself and rubber compounding ingredients in the high shear mixer, the temperature autogeneously increases, i.e. it "heats up". Several chemical reactions may occur at various steps in the mixing and curing processes.

The first reaction is a relatively fast reaction and is considered herein to take place between the filler and the silicon alkoxide group of the silated core polysulfides. Such reaction may occur at a relatively low temperature such as, for example, at about 120 ⁰C. The second reaction is considered herein to be the reaction which takes place between the sulfur-containing portion of the silated core polysulfide silane, and the sulfur vulcanizable rubber at a higher temperature; for example, above about 140 ⁰C.

Another sulfur source may be used, for example, in the form of elemental sulfur, such as but not limited to S₈. A sulfur donor is considered herein as a sulfur containing compound which liberates free, or elemental sulfur, at a temperature in a range of about 140 ⁰C to about 190 ⁰C. Such sulfur donors may be, for example, although are not limited to, polysulfide vulcanization accelerators and organosilane polysulfϊdes with at least two connecting sulfur atoms in its polysulfide bridge. The amount of free sulfur source addition to the mixture can be controlled or manipulated as a matter of choice relatively independently from the addition of the aforesaid silated core polysulfide silane. Thus, for example, the independent addition of a sulfur source may be manipulated by the amount of addition thereof and by the sequence of addition relative to the addition of other ingredients to the rubber mixture.

In one embodiment of the invention, the rubber composition may therefore comprise about 100 parts by weight of at least one sulfur vulcanizable rubber selected from conjugated diene homopolymers and copolymers, and copolymers of at least one conjugated diene and aromatic vinyl compound, and about 5 to 120 parts, or about 5 to 100 parts, preferably about 25 to 80 parts per hundred parts by weight per 100 parts by weight rubber of at least one particulate filler, up to about 5 parts by weight per 100 parts by weight rubber of a curing agent, and about 0.05 to about 25 parts per hundred parts of polymer of at least one silated core polysulfide silane as described in the present invention.

In another embodiment of the present invention, the filler comprises from about 1 to about 85 weight percent carbon black based on the total weight of the filler and up to about 20 parts by weight of at least one silated core polysulfide silane based on the total weight of the filler, including In another embodiment, the filler composition comprises from about 1 to about 85 weight percent carbon black based on the total weight of the filler composition and up to about 20 parts by weight of at least one silated core polysulfide silane of the present invention based on the total weight of the filler composition, including about 2 to about 20 parts by weight of at least one silated core polysulfide silane of the present invention based on the total weight of the filler composition.

In still another embodiment, the rubber composition is prepared by first blending rubber, filler and silated core polysulfide silane, or rubber, filler pretreated with all or a portion of the silated core polysulfide silane and any remaining silated core polysulfide silane, in a first thermomechanical mixing step to a temperature of about 140⁰C to about 200⁰C for about 2 to about 20 minutes, hi another embodiment, filler pretreated with all or a portion of the silated core polysulfide silane and any remaining silated core polysulfide silane, in a first thermomechanical mixing step to a temperature of about 14O ⁰C to about 2OQ⁰C for about 4 to 15 minutes. Optionally, the curing agent is then added in another thermomechanical mixing step at a temperature of about 50 ⁰C and mixed for about 1 to about 30 minutes. The temperature is then heated again to between about 130⁰C and about 200⁰C and curing is accomplished in about 5 to about 60 minutes.

In another embodiment of the present invention, the process may also comprise the additional steps of preparing an assembly of a tire or sulfur vulcanizable rubber with a tread comprised of the rubber composition prepared according to this invention and vulcanizing the assembly at a temperature in a range of about 130 ⁰C to about 200 ⁰C.

Other optional ingredients may be added in the rubber compositions of the present invention including curing aids, i.e. sulfur compounds, activators, retarders and accelerators, processing additives such as oils, plasticizers, tackifying resins, silicas, other fillers, pigments, fatty acids, zinc oxide, waxes, antioxidants and antiozonants, peptizing agents, reinforcing materials such as, for example, carbon black, and so forth. Such additives are selected based upon the intended use and on the sulfur vulcanizable material selected for use, and such selection is within the knowledge of one of skill in the art, as are the required amounts of such additives known to one of skill in the art.

The vulcanization may be conducted in the presence of additional sulfur vulcanizing agents. Examples of suitable sulfur vulcanizing agents include, for example elemental sulfur (free sulfur) or sulfur donating vulcanizing agents, for example, an amino disulfide, polymeric polysulfide or sulfur olefin adducts which are conventionally added in the final, productive, rubber composition mixing step. The sulfur vulcanizing agents, which can be those common in the art, are used, or added in the productive mixing stage, in an amount ranging from about 0.4 to about 3 phr, or even, in some circumstances, up to about 8 phr, with a range of from about 1.5 to about 2.5 phr and all subranges therebetween in one embodiment from 2 to about 2.5 phr and all subranges therebetween in another embodiment.

Optionally, vulcanization accelerators, i.e., additional sulfur donors, may be used herein. It is appreciated that may include the following examples, benzothiazole, alkyl thiuram disulfide, guanidine derivatives and thiocarbamates. Representative of such accelerators can be, but not limited to, mercapto benzothiazole (MBT), tetramethyl thiuram disulfide(TMTD), tetramethyl thiuram monosulfide (TMTM), benzothiazole disulfide (MBTS), diphenylguanidine (DPG), zinc dithiocarbamate (ZBEC), alkylphenoldisulfide, zinc iso-propyl xanthate (ZIX), N-dicyclohexyl-2-benzothiazolesulfenamide (DCBS), N-cyclohexyl-2-benzothiazolesulfenamide (CBS), N-tert-buyl-2-benzothiazolesulfenamide (TBBS), N-tert-buyl-2- benzothiazolesul enimide (TBSI), tetrabenzylthiuram disulfide (TBzTD), tetraethylthiuram disulfide (TETD), N-oxydiethylenebenzothiazole-2-sulfenamide, N,N-diphenylthiourea, dithiocarbamylsulfenamide, N,N-diisopropylbenzothiozole-2-sulfenamide, zinc-2-mercaptotoluimidazole, dithiobis(N-methyl piperazine), dithiobis(N-beta-hydroxy ethyl piperazine) and dithiobis(dibenzyl amine). Other additional sulfur donors, may be, for example, thiuram and morpholine derivatives. Representative of such donors are, for example, but not limited to, dimorpholine disulfide, dimorpholine tetrasulfide, tetramethyl thiuram tetrasulfide, benzothiazyl-2,N-dithiomorpholide , thioplasts, dipentamethylenethiuram hexasulfide, and disulfidecaprolactam. Accelerators are used to control the time and/or temperature required for vulcanization and to improve the properties of the vulcanizate. In one embodiment, a single accelerator system may be used, i.e., a primary accelerator. Conventionally, a primary accelerator(s) is used in total amounts ranging from about 0.5 to about 4 phr and all subranges therebetween in one embodiment, and from about 0.8 to about 1.5, phr and all subranges therebetween in another embodiment. Combinations of a primary and a secondary accelerator might be used with the secondary accelerator being used in smaller amounts (of about 0.05 to about 3 phr and all subranges therebetween) in order to activate and to improve the properties of the vulcanizate. Delayed action accelerators may be used. Vulcanization retarders might also be used. Suitable types of accelerators are amines, disulfides, guanidines, thioureas, thiazoles, thiurams, sulfenamides, dithiocarbamates and xanthates. In one embodiment, the primary accelerator is a sulfenamide. If a second accelerator is used, the secondary accelerator can be a guanidine, dithiocarbamate and/or thiuram compounds. Preferably, tetrabenzylthiuram disulfide is utilized as a secondary accelerator in combination with N-tert-buyl-2-benzothiazolesulfenamide with or without diphenylguanidine. Tetrabenzylthiuram disulfide is a preferred accelerator as it does not lead to the production of nitrosating agents, such as, for example, tetramethylthiuram disulfide.

Typical amounts of tackifier resins, if used, comprise about 0.5 to about 10 phr and all subranges therebetween, usually about 1 to about 5 phr and all subranges therebetween. Typical amounts of processing aids comprise about 1 to about 50 phr and all subranges therebetween. Such processing aids can include, for example, aromatic, napthenic, and/or paraffinic processing oils. Typical amounts of antioxidants comprise about 1 to about 5 phr. Representative antioxidants may be, for example, diphenyl-p-phenylenediamine and others, such as, for example, those disclosed in the Vanderbilt Rubber Handbook (1978), pages 344-346. Typical amounts of antiozonants, comprise about 1 to about 5 phr and all subranges therebetween. Typical amounts of fatty acids, if used, which can include stearic acid, comprise about 0.5 to about 3 phr and all subranges therebetween. Typical amounts of zinc oxide comprise about 2 to about 5 phr. Typical amounts of waxes comprise about 1 to about 5 phr and all subranges therebetween. Often microcrystalline waxes are used. Typical amounts of peptizers comprise about 0.1 to about 1 phr and all subranges therebetween. Typical peptizers may be, for example, pentachlorothiophenol and dibenzamidodiphenyl disulfide. The rubber compositions of this invention can be used for various purposes. For example, it can be used for various tire compounds, weather stripping, and shoe soles. In one embodiment of the present invention, the rubber compositions described herein are particularly useful in tire treads, but may also be used for all other parts of the tire as well and can comprise various tire components and various tire component compounds. The tires can be built, shaped, molded and cured by various methods which are known and will be readily apparent to those having skill in such art.

The tire compositions are formulated so that they are vulcanizable to form a tire component compound, the compound having a Shore A Hardness of not less than 40 and not greater than 95 and a glass-transition temperature Tg (E"_maχ) not less than -80 ⁰C and not greater than 0 ⁰C. The Shore A Hardness according to the present invention is measured in accordance with DIN 53505. The glass-transition temperature Tg (E"_max) is measured in accordance with DIN 53513 with a specified temperature sweep of -80 ⁰C to +80 ⁰C and a specified compression of 10 + 0.2 % at 10 Hz.".

In another embodiment, the silated core polysulfide of the present invention may be loaded on a carrier, or filler, such as, for example, a porous polymer, carbon black, silica or the like, so that they are in a dry free flowing form for convenient delivery to rubber. In one embodiment, the carrier would be part of the inorganic filler to be used in the rubber.

In one embodiment of the invention, a dry free flowing composition comprises a silane in accordance with this invention in admixture with one or more of the aforesaid carrier materials, e.g., in a weight ratio of from about 0.1 to about 60 weight percent. The BET surface area of such carriers as silica can vary widely and in one embodiment can vary from about 100m²/g to about 300m²/g. Another property of such carriers is their DOP adsorption, an oil adsorption index. In the case of nonporous carriers such as silica, the DOP adsorption can range from about lOOml/lOOgm to about 400ml/100gm. Porous carriers such as foamed polyolefins can advantageously absorb from about 10ml to about 250ml/100gm (from about 9 to about 70 weight percent) of the silane of the present invention.

The filler can be essentially inert to the silane with which it is admixed as is the case with carbon black or organic polymers, or it can be reactive therewith, e.g., the case with carriers possessing metal hydroxyl surface functionality, e.g., silicas and other siliceous particulates which possess surface silanol functionality. All references cited are specifically incorporated herein by reference as they are relevant to the present invention.

EXAMPLES The examples presented below demonstrate significant advantages of the silanes described herein relative to those of the currently practiced art, in their performance as coupling agents in silica-filled rubber.

Example 1 Preparation of (2-triethoxysilylethyl)-bis-(7-triethoxysilyl-3,4-dithiaheptyl)cyclohexane

This example illustrates the preparation of a silated core disulide from a silane containing two vinyl groups through the formation of an intermediate thioacetate silane.

The preparation of the (2-trimethoxysilylethyl)divinylcyclohexane was prepared by hydrosilation. Into a 5 L, three-neck round bottomed flask equipped with magnetic stir bar, temperature probe/controller, heating mantle, addition funnel, condenser, and air inlet were charged 1,2,4-trivinylcyclohexane (2,001.1 grams, 12.3 moles) and VCAT catalysts (1.96 grams, 0.01534 gram platinum). Air was bubbled into the vinyl silane by means of the air inlet where the tube was below the surface of the silane. The reaction mixture was heated to 11O⁰C and the trimethoxysilane (1,204 grams, 9.9 moles) was added over a 3.5 hour period. The temperature of the reaction mixture increased to a maximum value of 13O⁰C. The reaction mixture was cooled to room temperature and l,3,5-trimethyl-2,4,6-tris(3,5-di-tert-butyl-4-hydroxylbenzyl)benzene (3 grams, 0.004 mole) was added. The reaction mixture was distilled at 122°C and 1 mmHg pressure to give 1,427 grams of (2-trimethoxysilylethyl)divinylcyclohexane, The yield was 51 percent.

The (2-triethoxysilylethyl)divinylcyclohexane was prepared by transesterification. Into a 3 L, three-neck round bottomed flask equipped with magnetic stir bar, temperature probe/controller, heating mantle, addition funnel, distilling head and condenser, and nitrogen inlet were charged (2-trimethoxysilylethyl)divinylcyclohexane (284 grams, 2.33 moles), sodium ethoxide in ethanol (49 grams of 21% sodium ethoxide, purchased from Aldrich Chemical) and ethanol (777 grams, 16.9 moles). The reaction mixture was heated and the methanol and ethanol were removed by distillation at atmospheric pressure. The crude product was then distilled at 106⁰C and under reduced pressure of 0.4 mmHg to give 675 grams of product, 89 percent yield. The (2-triethoxysilylethyl)-bis-(3-thia-4-oxopentyl)cyclohexane was prepared by addition of thioacetic acid to the divinylsilane. Into a 1 L, three-neck round bottomed flask equipped with magnetic stir bar, temperature probe/controller, heating mantle, addition funnel, condenser, air inlet and a sodium hydroxide scrubber, was charged thioacetic acid (210 grams, 2.71 moles). The (2-triethoxysilylethyl)divinylcyclohexane (400 grams, 1.23 moles) was added slowly over a period of 30 minutes and at room temperature by means of an addition funnel. The reaction was an exothermic reaction. The temperature of the mixture increased to 94.6⁰C. The mixture was stirred for 2.5 hours and allowed to cool to 38.8°C. Additional thioacetic acid (10 grams, 0.13 moles) was added and a slight exothermal reaction was observed. The reaction mixture was stirred overnight (18 hours) at about 25⁰C. Analysis indicated that the reaction mixture contained less than 2 percent thioacetic acid. Its overall purity was 91 percent. The reaction mixture was further purified by a distillation using a Kugel apparatus under reduced pressure.

The dimercaptosilane intermediate was prepared by removing the acetyl groups from (2- triethoxysilylethyl)-bis-(3-thia-4-oxopentyl)cyclohexane. Into a 5 L, three-neck round bottomed flask equipped with magnetic stir bar, temperature probe/controller, heating mantle, addition funnel, distilling head and condenser, 10-plate Oldershaw column and nitrogen inlet were charged (2-triethoxysilylethyl)bis-(3-thia-4-oxopentyl)cyclohexane (2,000 grams, 4.1 moles), ethanol (546.8 grams, 11.8 moles) and sodium ethoxide in ethanol (108 grams of a 21% sodium ethoxide in ethanol). The pH of the reaction mixture was about 8. The reaction mixture was heated to 88° C for 24 hours to remove the ethyl acetate and ethanol from the reaction mixture. Twice ethanol (1 liter) was added to the mixture and the pH of the reaction mixture was increase to about 10 by the addition of 21% sodium ethoxide in ethanol (21 grams) and heated an additional 6.5 hours. The reaction mixture was cooled and then pressure filtered. The reaction mixture was stripped at a temperature less than 95° C and 1 mmHg pressure. The stripped product was filtered to give (2-triethoxysilylethyl)bis(2-mercaptoethyl)cyclohexane (1398 grams, 3.5 moles, 86% yield).

The product, (2-triethoxysilylethyl)-bis-(7-triethoxysilyl-3 ,4-dithiaheptyl)cyclohexane, related oligomers and polysulfϊdes, and bis-(3-triethoxysilylpropyl)polysulfide mixture, was prepared by reacting the dimercaptan silane with base, sulfur and 3-chloropropyltriethoxysilane. Into a 3 liter, round bottom flask equipped with a mechanical stirrer, temperature probe/controller, heating mantle, addition funnel, distilling head and Friedrich condenser, and nitrogen inlet was charged (2-triethoxysilylethyl)-bis-(2-mercaptoethyl)cyclohexane (504.3 grams, 1.28 moles). With rapid stirring, a solution of 21% sodium ethoxide in ethanol (829 grams, 2.56 moles), an additional 150 grams of ethanol and sulfur (sublimed powder form Aldrich Chemical, 86.4 grams, 2.7 moles). The solution was refluxed 3.5 hours and then 3- chloropropyltriethoxysilane (616.5 grams, 2.56 moles) over a period of 1.5 hours and then refluxed 17.5 hours. The solution was cooled and pressure filtered through a 2 micron and then a 0.1 micron filter. The filtrate was then stripped at 60 ⁰C and 9 mniHg to remove the ethanol. The product (1027 grams) was analyzed by HPLC and the chromatogram is shown in Figure 1.

One isomer of (2-triethoxysilylethyl)-bis-(7-triethoxysilyl-3,4-dithiaheptyl)cyclohexane has the following structure:

Example 2.

Preparation of (2 -triethoxysilylethyl)~bis-(7-triethoxysilyl-3,4,5,6- tetrathianonyl)cyclohexane

The dimercaptan silane intermediate, (2-triethoxysilylethyl)bis(2- mercaptoethyl)cyclohexane, was prepared by the procedure described in Example 1.

The product, (2-triethoxysilylethyl)~bis-(7-triethoxysilyl-3,4,5,6- tetrathianonyl)cyclohexane, related oligomers and polysulfides, and bis- (triethoxysilylpropyl)polysulfide mixture, was prepared by reacting the dimercaptan silane with base, sulfur and 3-chloropropyltriethoxysilane. Into a 5 liter, round bottom flask equipped with a mechanical stirrer, temperature probe/controller, heating mantle, addition funnel, distilling head and Friedrich condenser, and nitrogen inlet was charged (2-triethoxysilylethyl)-bis-(2- mercaptoethyl)cyclohexane (596.3 grams, 1.5 moles). With rapid stirring, a solution of 21% sodium ethoxide in ethanol (979.0 grams, 3.0 moles), an additional 600 grams of ethanol and sulfur (sublimed powder form Aldrich Chemical, 290.0 grams, 9.1 moles). The solution was refluxed overnight and then 3-chloropropyltriethoxysilane (740.0 grams, 3.07 moles) was added and refluxed for 16 hours. The solution was cooled and pressure filtered through a 0.1 micron filter. The filtrate was then stripped using a Rotavapor to remove the ethanol. The product (1,375 grams) was analyzed by HPLC, NMR and GC.

One isomer of (2-triethoxysilylethyl)~bis-(7-triethoxysilyl-3,4,5,6- tetrathianonyl)cyclohexane has the following structure:

Comparative Example A-E, Examples 3-7 The Use of Silanes in Low Rolling Resistant Tire Tread Formulation.

A model low rolling resistance passenger tire tread formulation as described in

Table 1 and a mix procedure were used to evaluate representative examples of the silanes of the present invention. The silane in Example 2 was mixed as follows in a "B" BANBURY®

(Farrell Corp.) mixer with a 103 cu. in. (1690 cc) chamber volume. The mixing of the rubber was done in two steps. The mixer was turned on with the mixer at 80 rpm and the cooling water at 71° C. The rubber polymers were added to the mixer and ram down mixed for 30 seconds. The silica and the other ingredients in Masterbatch of Table 1 except for the silane and the oils were added to the mixer and ram down mixed for 60 seconds. The mixer speed was reduced to 35 rpm and then the silane and oils of the Masterbatch were added to the mixer and ram down for 60 seconds. The mixer throat was dusted down and the ingredients ram down mixed until the temperature reached 149°C. The ingredients were then mixed for an addition 3 minutes and 30 seconds. The mixer speed was adjusted to hold the temperature between 152 and 157°C. The rubber was dumped (removed from the mixer), a sheet was formed on a roll mill set at about 85°C to 88°C, and then allowed to cool to ambient temperature. In the second step, Masterbatch was recharged into the mixer. The mixer's speed was

80 rpm, the cooling water was set at 71⁰C and the batch pressure was set at 6MPa. The Masterbatch was ram down mixed for 30 seconds and then the temperature of the Masterbatch was brought up to 149°C, and then the mixer's speed was reduce to 32 rpm. The rubber was mixed for 3 minutes and 20 seconds at temperatures between 152°C and 157° C. After mixing, the rubber was dumped (removed from the mixer), a sheet was formed on a roll mill set at about 85°C to 88°C, and then allowed to cool to ambient temperature.

The rubber Masterbatch and the curatives were mixed on a 15 cm x 33 cm two roll mill that was heated to between 48°C and 52°C. The sulfur and accelerators were added to the rubber (Masterbatch) and thoroughly mixed on the roll mill and allowed to form a sheet. The sheet was cooled to ambient conditions for 24 hours before it was cured. The curing condition was 160⁰C for 20 minutes. Silane from Example 2 was compounded into the tire tread formulation according to the above procedure. The performance of the silane prepared in Example 2 was compared to the performance of silanes which are practiced in the prior art, bis-

(3-triethoxysilyl-l-propyl)disulfide (TESPD), and propyltriethoxysilane, Comparative Examples A-E. The test procedures were described in the following ASTM methods:

Mooney Scorch ASTM D 1646 Mooney Viscosity ASTM D 1646

Oscillating Disc Rheometer (ODR) ASTM D2084

Storage Modulus, Loss Modulus,

Tensile and Elongation ASTM D412 and D224

DIN Abrasion DIN Procedure 53516 Heat Buildup ASTM D623

Percent Permanent Set ASTM D623

Shore A Hardness ASTM D2240

The results of this procedure are tabulated below in Table 1.

Table 1

Table 1, listing Examples 3 -7, presents the performance parameters of hydrocarbon core polysulfide silanes of the present invention, TESPD, and propyltriethoxysilane. The physical properties of the rubber compounded with silane from Example 2 are consistently and substantially higher than the control silanes. Also, TMQ represents 2,2,4-trimethyl-l,2- dihydroquinoline.

The silated core polysulfide silanes of the present invention impart superior performance to silica-filled elastomer compositions, including better coupling of the silica to the rubber, as illustrated by the higher reinforcement index . The better reinforcing index translate into performance improvements for the elastomer compositions and articles manufactured from these elastomers.

Comparative Example F, Examples 8 and 9

The Use of Silanes in Low Rolling Resistant Tire Tread Formulation. A model low rolling resistance passenger tire tread formulation as described in Table 2 and a mix procedure were used to evaluate representative examples of the silanes of the present invention. The silane in Examples 8 and 9 are mixed as follows in an instrumented OOC" BANBURY® (Farrell Corp.) mixer with a 158 cu. in. (2,600 cc) chamber volume. The mixing of the rubber was done in three steps. The mixer was turned on with the mixer at 80 rpm and the cooling water at 71° C. The rubber polymers were added to the mixer and ram down mixed for 30 seconds. The silica and the silane were added to the mixer and ram down mixed for 30 seconds. The other ingredients in Masterbatch of Table 2 except for the oils were added to the mixer and ram down mixed for 60 seconds. The mixer speed was reduced to 65 rpm and then the oils of the Masterbatch were added to the mixer and ram down mixed for 60 seconds. The mixer throat was dusted down and the ingredients ram down mixed until the temperature reached 150° C. The ingredients were then mixed for an additional 3 minutes and 30 seconds. The mixer speed was adjusted to hold the temperature between 150 and 155° C. The rubber was dumped (removed from the mixer), a sheet was formed on a roll mill set at about 85° to 90° C, and then allowed to cool to ambient temperature.

In the second step, Masterbatch was recharged into the mixer. The mixer's speed was 80 rpm, the cooling water was set at 71° C and the ram pressure was set at 25 psi. The Masterbatch was ram down mixed for 150 seconds while the temperature of the Masterbatch was brought up to 150° C, and then the mixer's speed was reduce to 50 rpm and the rubber was mixed for 40 seconds at temperatures between 150 and 155° C. After mixing, the rubber was dumped (removed from the mixer), a sheet was formed on a roll mill set at about 85° to 90° C, and then allowed to cool to ambient temperature.

In the third step, the mixer's speed was set to 50 rpm, the cooling water was set at 71° C and the ram pressure was set at 25 psi. The rubber Masterbatch and the curatives were ram down mixed for 190 seconds while the temperature of the Final Mix was brought up to 115° C. After mixing, the rubber was dumped (removed from the mixer), a sheet was formed on a roll mill set at about 85° to 90° C, and then allowed to cool to ambient temperature. The curing condition was 160° C for 20 minutes. The silated cyclic core polysulfides from Examples 8 and 9 were compounded into the tire tread formulation according to the above procedure and its performance was compared to the performance of a silane which are practiced in the prior art, bis-(3-triethoxysilyl-l-propyl)disulfide (TESPD). Comparative Example F. The test procedures were described in the following ASTM methods:

Mooney Scorch ASTM D 1646 Mooney Viscosity ASTM D1646

Rheometer (MDR 2000) DIN 53529

Storage Modulus, Loss Modulus,

Tensile and Elongation DIN 53504-R1

Shore A Hardness DIN 53505 Rebound DIN 53512, ASTM D1054

The results of this procedure are tabulated below in Table 2.

Table 2, listing Comparative Example F and Examples 8 and 9, presents the performance parameters of bis-(3-triethoxysilylpropyl) disulfide, silicated core polysulfide of the present invention and silated core polysulfide of the present invention in combination with the thiuram, Tetrabenzylthiuram disulfide (TBzTD). The physical properties of the rubber compounded with silated core polysulfides from Examples 8 and 9 are consistently and substantially higher than the control silane.

The silated core polysulfide of the present invention imparts higher performance to silica- filled elastomer compositions, including better coupling of the silica to the rubber, as illustrated by the higher reinforcement index. The better reinforcing indices translate into performance improvements for the elastomer compositions and articles manufactured from these elastomers

The performance of silica-filled elastomer compositions with a conventional cure package is further enhanced when the silated core polysulfide of the present invention is added in combination with a thiuram accelerator, as illustrated by an increase in 300% modulus, in the reinforcement index, and in rebound. TBzTD is considered to be superior to other thiurams which produce nitrosating agents (e.g. Tetramethylthiuram disulfide). These indices translate into performance improvements for wear and rolling resistance for the elastomer compositions and articles manufactured from these elastomers.

Certain performance properties of silica-filled elastomer compositions with a conventional cure package are further enhanced when the silated core polysulfide of the present invention is added in combination with dithiocarbamate accelerators (e.g., Zinc dibenzyldithiocarbamate) or xanthate accelerators (e.g. zinc iso-propylxanthate). However, these accelerators produce less desirable properties in crosslinking and scorch.

It is noted that the foregoing examples have been provided merely for the purpose of explanation and are in no way to be construed as limiting of the present invention. While the present invention has been described with reference to exemplary embodiments, it is understood that the words which have been used herein are words of description and illustration, rather than words of limitation. Changes may be made, within the purview of the appended claims, as presently stated and as amended, without departing from the scope and spirit of the present invention in its aspects. Although the present invention has been described herein with reference to particular means, materials and embodiments, the present invention is not intended to be limited to the particulars disclosed herein; rather, the present invention extends to all functionally equivalent structures, methods and uses, such as are within the scope of the appended claims.

Claims

What is claimed is:

1. A tire composition for forming a tire component, the composition being formed by combining:

(a) a silated core polysulfide of the general formula [Y¹R¹S_x-]_m[G¹(R²SiX¹X²X³)_a]_n[G²]₀[R³Y²]_p wherein: each occurrence of G¹ is independently selected from a polyvalent hydrocarbon species having from 1 to about 30 carbon atoms containing a polysulfide group represented by the general formula: [(CH₂)_b-]_cR⁴[-(CH₂)_dS_x-]_e; each occurrence of G² is independently selected from a polyvalent hydrocarbon species of 1 to about 30 carbon atoms containing a polysulfide group represented by the general formula:

[(CH₂)_b-]_cR⁵[-(CH₂)_dS_x-]_e; each occurrence of R¹ and R³ is independently selected from a divalent hydrocarbon fragment having from 1 to about 20 carbon atoms; each occurrence of Y¹ and Y² is independently selected from silyl (-SiX¹X²X³), hydrogen, carboxylic acid, and ester (-C(=O)OR⁶) wherein R⁶ is a monovalent hydrocarbon group having from 1 to 20 carbon atoms; each occurrence of R² is a straight chain hydrocarbon represented by -(CH₂)_f-; each occurrence of R⁴ is independently selected from a polyvalent hydrocarbon fragment of 1 to about 28 carbon atoms; each occurrence of R⁵ is independently selected from a polyvalent hydrocarbon fragment of 1 to about 28 carbon atoms; each occurrence of X¹ is independently selected from -Cl, -Br, -OH, -OR⁶, and R⁶C(=O)O-, wherein R⁶ is a monovalent hydrocarbon group having from 1 to 20 carbon atoms; each occurrence of X² and X³ is independently selected from hydrogen, R⁶, wherein R⁶ is a monovalent hydrocarbon group having from 1 to 20 carbon atoms, X¹, wherein X¹ is independently selected from -Cl, -Br, -OH, -OR⁶, and R⁶C(=O)O-, wherein R⁶ is a monovalent hydrocarbon group having from 1 to 20 carbon atoms , and -OSi containing groups that result from the condensation of silanols; and each occurrence of the subscripts, a, b, c, d, e, f, m, n, o, p, and x, is independently given wherein a, c and e are 1 to about 3; b is 1 to about 5; d is 1 to about 5; f is 0 to about 5; m and p are 1 to about 100; n is 1 to about 15; o is 0 to about 10; and x is 1 to about 10; (b) at least one vulcanizable rubber selected from natural rubbers, synthetic polyisoprene rubbers, polyisobutylene rubbers, polybutadiene rubbers, and random styrene-butadiene rubbers (SBR); and

(c) an active filler including at least one of active filler selected from carbon blacks, silicas, silicon based fillers, and metal oxides present in a combined amount of at least 35 parts by weight per 100 parts by weight of total vulcanizable rubber, of which at least 10 parts by weight is carbon black, silica, or a combination thereof; and wherein the tire composition is formulated to be vulcanizable to form a tire component compound having a Shore A Hardness of not less than 40 and not greater than 95 and a glass- transition temperature Tg (E"_max) not less than -80 ⁰C and not greater than 0 ⁰C.

2. The tire composition of Claim 1 wherein R¹ and R³ are branched or straight chain alkyl, alkenyl, alkynyl, aryl or aralkyl groups in which one hydrogen atom is substituted with a Y¹ or Y² group.

3. The tire composition of Claim 1 wherein R⁶ is branched or straight chain alkyl, alkenyl, aryl or aralkyl.

4. The tire composition of Claim 1 wherein R⁴ is cyclic, branched or straight chain alkyl, alkenyl, alkynyl, aryl, or aralkyl in which a + c + e - 1 hydrogens have been replaced.

5. The tire composition of Claim 1 wherein R⁴ and R⁵ are polyvalent heterocarbon fragments from 1 to 27 carbon atoms.

6. The tire composition of Claim 1 wherein R⁵ is cyclic, branched or straight chain alkyl, alkenyl, alkynyl, aryl, or aralkyl in which a + c + e - 1 hydrogens have been replaced.

7. The tire composition of Claim 6 wherein the heteroatom of R⁴ and R⁵ is selected from sulfur, oxygen, nitrogen, and mixtures thereof.

8. The tire composition of Claim 1 wherein the alkyl, alkynyl, aryl, araalkyl and arenyl of R⁴ in which a + c + e - 1 hydrogens have been replaced is selected from methyl, ethyl, propyl, and isobutyl, vinyl, propenyl, allyl, methallyl, ethylidenyl norbornane, ethylidene norbornyl, ethylidenyl norbornene, ethylidene norbornenyl, acetylenyl, and propargyl, methylacetylenyl, phenyl, naphthalenyl, benzyl, phenethyl, tolyl, xylyl, norbornyl, norbornenyl, ethylnorbornyl, ethylnorbornenyl, cyclohexyl, ethylcyclohexyl, ethylcyclohexenyl, cyclohexylcyclohexyl, and cyclododecatrienyl.

9. The tire composition of Claim 1 wherein the alkyl, alkynyl, aryl, araalkyl and arenyl of R⁵ in which c + e - 1 hydrogens have been replaced is selected from methyl, ethyl, propyl, and isobutyl, vinyl, propenyl, allyl, methallyl, ethylidenyl norbornane, ethylidene norbornyl, ethylidenyl norbornene, ethylidene norbornenyl, acetylenyl, propargyl, methylacetylenyl, phenyl, naphthalenyl, benzyl, phenethyl, tolyl, xylyl, norbornyl, norbornenyl, ethylnorbornyl, ethylnorbornenyl, cyclohexyl, ethylcyclohexyl, ethylcyclohexenyl, cyclohexylcyclohexyl, and cyclododecatrienyl.

10. The tire composition of Claim 1 wherein cyclic structure of R⁴, R⁵, and R⁶ is selected from bicyclic, tricyclic, higher cyclic structures, cyclic structures substituted with alkyl, alkenyl, and/or alkynyl groups.

11. The tire composition of Claim 1 wherein X¹ is selected methoxy, ethoxy, propoxy, isopropoxy, butoxy, phenoxy, benzyloxy, hydroxy, chloro, and acetoxy.

12. The tire composition of Claim 1 wherein X² and X³ are selected from methoxy, ethoxy, propoxy, isopropoxy, butoxy, phenoxy, benzyloxy, hydroxy, chloro, acetoxy, hydrogen, methyl, ethyl, propyl, isopropyl, sec-butyl, phenyl, vinyl, cyclohexyl, straight-chain alkyl, butyl, hexyl, octyl, lauryl, and octadecyl.

13. The tire composition of Claim 1 wherein R¹ and R³ are terminal straight-chain alkyls substituted terminally at the end with -CH₂-, -CH₂CH₂-, -CH₂CH₂CH₂-, d - CH₂CH₂CH₂CH₂CH₂CH₂CH₂CH₂-, beta-substituted analogs, and mixtures thereof.

14. The tire composition of Claim 13 wherein the beta substituted analog is -

CH₂(CH₂)_HCH(CH₃)-, where u is zero to 17.

15. The tire composition of Claim 13 wherein R¹ and R³ are structures derived from methallyl chloride, divinylbenzene, diallylether, butadiene, piperylene, isoprene, diradicals, limonene, monovinyl-containing structures derived from trivinylcyclohexane, monounsaturated structures derived from myrcene containing a trisubstituted C=C, monounsaturated structures derived from myrcene lacking a trisubstituted C=C, and mixtures thereof.

16. The tire composition of Claim 1 wherein G¹ is derived from nonconjugated terminal diolefins.

17. The tire composition of Claim 16 wherein G¹ is selected from - CH₂(CH₂ViCH(CH₂-)- , -CH(CH₃)(CH₂)₉CH(CH₂-)₂, wherein q is zero to 20.

18. The tire composition of Claim 17 wherein G¹ is derived from divinylbenzene, butadiene, isoprene, trivinylcyclohexane, myrcene, triethanolamine derivative, and mixtures thereof.

19. The tire composition of Claim 16 wherein G¹ is -CH(CH₂-)(CH₂)_qCH(CH₂-)-, in which q is from 1 to 20.

20. The tire composition of Claim 19 wherein G¹ is derived from divinylbenzene, diallylether, butadiene, piperylene, isoprene, trivinylcyclohexane myrcene, and mixtures thereof.

21. The tire composition of Claim 1 wherein G² is derived from nonconjugated terminal diolefins.

22. The tire composition of Claim 21 wherein G² is selected from -

CH₂(CH₂ViCH₂(CH₂-) and CH₂(CH₃)(CH₂)₉CH(CH₂-)₂, wherein q is zero to 20.

23. The tire composition of Claim 22 wherein G² is derived from divinylbenzene, butadiene, isoprene, trivinylcyclohexane, myrcene, and mixtures thereof.

24. The tire composition of Claim 1 wherein G² is -CH₂(CH₂VICH(CH₂-)- wherein q is zero to 20.

25. The tire composition of Claim 24 wherein G² is derived from trivinylcyclohexane, trimethylolalkanes, triethanolamine, and mixtures thereof.

26. The tire composition of Claim 1 wherein the silated core polysulfide is any of the isomers of 2-triethoxysilyl-l,3-bis-(3-triethoxysilyl-l-propyltetrathia)propane, 4-(2- triethoxysilyl-l-ethyl)-l,2-bis-(13-triethoxysilyl-3,4,5,6-tetrathiatridecyl)cyclohexane; 4-(2- triethoxysilyl- 1 -ethyl)- 1 ,2-bis-( 13-triethoxysilyl-3,4,5,6-tetrathiatridecyl)cyclohexane; 4-(2- diethoxymethylsilyl- 1 -ethyl)- 1 ,2-bis-( 13-triethoxysilyl-3,4,5,6-tetrathiatridecyl)cyclohexane; 4- (2-triethoxysilyl-l-ethyl)-l,2-bis-(10-triethoxysilyl-3,4,5,6,7-pentathiadecyl)cyclohexane; l-(2- triethoxysilyl-l-ethyl)-2,4-bis-(10-triethoxysilyl-3,4,5,6,7-pentathiadecyl)cyclohexane; 4-(2- triethoxysilyl- 1 -ethyl)- 1 ,2-bis-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexane; 1 -(2- triethoxysilyl- 1 -ethyl)-2,4-bis-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexane; 2-(2- triethoxysilyl-l-ethyl)-l,4-bis-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexane; 4-(2- triethoxysilyl-l-ethyl)-l,2-bis-(8-triethoxysilyl-3,4,5-trithiaoctyl)cyclohexane; l-(2- triethoxysilyl-l-ethyl)-2,4-bis-(8-triethoxysilyl-3,4,5-trithiaoctyl)cyclohexane; 2-(2- triethoxysilyl- 1 -ethyl)- 1 ,4-bis-(8-triethoxysilyl-3 ,4,5-trithiaoctyl)cyclohexane; 4-(2- triethoxysilyl- 1 -ethyl)- 1 ,2-bis-(7-triethoxysilyl-3,4-dithiaheptyl)cyclohexane; 2-(2-triethoxysilyl- 1 -ethyl)- 1 ,4-bis-(7-triethoxysilyl-3,4-dithiaheptyl)cyclohexane; 1 -(2-triethoxysilyl- 1 -ethyl)-2,4- bis-(7-triethoxysilyl-3,4-dithiaheptyl)cyclohexane; 2-(2-triethoxysilyl-l-ethyl)-l-(7- triethoxysilyl-3,4-dithiaheptyl)-2-(8-triethoxysilyl-3,4,5-trithiaoctyl)cyclohexane; 4-(2- triethoxysilyl- 1 -ethyl)- 1 ,2-bis-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)benzene; bis-[2-[4-(2- triethoxysilyl-l-ethyl)-2~(9-triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexyl]ethyl] tetrasulfide; bis-[2-[4-(2-triethoxysilyl-l-ethyl)-2-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexyl]ethyl] trisulfide; bis-[2-[4-(2-triethoxysilyl-l-ethyl)-2-(9-triethoxysilyl-3,4,5,6- tetrathianonyl)cyclohexyl]ethyl] disulfide; bis-[2-[4-(2-triethoxysilyl-l-ethyl)-2— (7- triethoxysilyl-3,4-dithiaheptyl)cyclohexyl]ethyl] disulfide; bis-2-[4-(2-triethoxysilyl-l-ethyl)-2- (7-triethoxysilyl-3,4-dithiaheptyl)cyclohexyl]ethyl] trisulfide; bis-[2-[4-(2-triethoxysilyl- 1 - ethyl)-2-(7-triethoxysilyl-3,4-dithiaheptyl)cyclohexyl]ethyl tetrasulfide; bis-[2-[4-(2- triethoxysilyl-l-ethyl)-2-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)phenyl]ethyl] tetrasulfide; bis- 2-[4-(2-triethoxysilyl-l-ethyl)-3-bis-(9-triethoxysilyl-3,4,5,6-tetrathianonyl)cyclohexyl]ethyl] trisulfide; bis-[2-[4-(2-diethoxymethylsilyl-l-ethyl)-2~(7-triethoxysilyl-3,4- dithiaheptyl)cyclohexyl] ethyl disulfide, and mixtures thereof.

27. The tire composition of Claim 1 wherein R¹ and R³ are independently selected from a divalent hydrocarbon fragment having from 1 to about 5 carbon atoms

28. The tire composition of Claim 27 wherein R¹ and R³ are that are branched and/or straight chain alkyl, alkenyl or alkynyl groups in which one hydrogen atom was substituted with a Y¹ or Y² group.

29. The tire composition of Claim 27 wherein Y¹ and Y² are silyl (-SiX¹ ,X², X³), hydrogen, carboxylic acid, ester (-C(=O)OR⁶) wherein R⁶ is a monovalent hydrocarbon group having from 1 to 5 carbon atoms.

30. The tire composition of Claim 27 wherein R² is a straight chain hydrocarbon represented by -(CH₂)_f- where f is an integer from about 0 to about 3.

31. The tire composition of Claim 27 wherein R⁴ is a polyvalent hydrocarbon fragment of 3 to about 10 carbon atoms.

32. The tire composition of Claim 27 wherein R⁵ is a polyvalent hydrocarbon fragment of 3 to about 10 carbon atoms.

33. The tire composition of Claim 27 wherein X¹ is independently selected from hydrolyzable -OH, and -OR⁶, wherein R⁶ is a monovalent hydrocarbon group having from 1 to 5 carbon atoms.

34. The tire composition of Claim 27 wherein X² and X³ are independently selected from

R⁶, wherein R⁶ is a monovalent hydrocarbon group having from 1 to 5 carbon atoms, X¹ , wherein X¹ is independently selected from hydrolyzable -OH, -OR⁶, wherein R⁶ is a monovalent hydrocarbon group having from 1 to 5 carbon atoms, and -OSi containing groups that result from the condensation of silanols.

35. The tire composition of Claim 27 wherein each occurrence of the subscripts, a, b, c, d, e, f, m, n, o, p, and x, is independently given by a is 1 to about 2; b and d are 1 to about 3; c and e are 1; f is 0 to about 3; m and p are 1, n is 1 to about 10; o is 0 to about 1; and x is 1 to about 4.

36. A tire composition formed by combining from about 30 to about 99 weight percent of the tire composition of Claim 1 and about 70 to about 1 weight percent of a silane of the general formula:

[X¹X²X³SiR¹S_xR³SiX¹X²X³] wherein each occurrence of R¹ and R³ is independently selected from a divalent hydrocarbon fragment having from 1 to about 20 carbon atoms that include branched and straight chain alkyl, alkenyl, alkynyl, aryl or aralkyl groups wherein one hydrogen atom was substituted with a Y¹ or

Y² group; each occurrence of Y¹ and Y² is independently selected from silyl (-SiX¹X²X³), each occurrence of X¹ is independently selected from -Cl, -Br, -OH, -OR⁶, and R⁶C(=O)O-, wherein R⁶ is a monovalent hydrocarbon group having from 1 to 20 carbon atoms , and includes branched or straight chain alkyl, alkenyl, aryl or aralkyl group, each occurrence of

X² and X³ is independently selected from hydrogen, R⁶, X¹, and -OSi containing groups that result from the condensation of silanols; and x is 1 to about 10.

37. The tire composition of Claim 36 wherein the silane is selected from bis-(3- triethoxysilylpropyl) disulfide; bis-(3-triethoxysilylpropyl) trisulfϊde; bis-(3-triethoxysilylpropyl) tetrasulfide; bis-(3-triethoxysilylpropyl) pentasulfide; bis-(3-diethoxymethylsilylpropyl) disulfide; bis-(3-ethoxydimethylsilylpropyl) disulfide; bis-(triethoxysilylmethyl) disulfide; bis- (4-triethoxysilylbenzyl) disulfide, bis-(3-triethoxysilylphenyl) disulfide, and mixtures thereof.

38. The tire composition of Claim 1, further comprising curative and, optionally, at least one other additive selected from sulfur compounds, activators, retarders, accelerators, processing additives, oils, plasticizers, tackifying resins, silicas, fillers, pigments, fatty acids, zinc oxide, waxes, antioxidants and antiozonants, peptizing agents, reinforcing materials, and mixtures thereof.

39. The tire composition of Claim 1, wherein the at least one vulcanizable rubber is at least one natural rubber.

40. The tire composition of Claim 1, wherein the at least one vulcanizable rubber is at least one emulsion polymerization derived rubber.

41. The tire composition of Claim 1, wherein the at least one vulcanizable rubber is at least one solvent polymerization derived rubber.

42. The tire composition of Claim 41, wherein the solvent polymerization derived rubber is styrene/butadiene rubber containing from about 5 to about 50 percent vinyl content.

43. The tire composition of Claim 41, wherein the solvent polymerization derived rubber is styrene/butadiene rubber containing from about 9 to about 36 percent vinyl content.

44. The tire composition of Claim 1, wherein the at least one vulcanizable rubber is prepared from conjugated diene selected from isoprene, 1,3 -butadiene, styrene, and alpha methyl styrene, and mixtures thereof.

45. The tire composition of Claim 1, wherein the at least one vulcanizable rubber is formed from polybutadiene of which about 90 weight percent is in the cis-l,4-butadiene form.

46. The tire composition of Claim 1, wherein the at least one vulcanizable rubber is selected from cis-l,4-polyisoprene rubber, emulsion polymerization prepared styrene/butadiene copolymer rubber, organic solution polymerization prepared styrene/butadiene rubber, 3,4- polyisoprene rubber, isoprene/butadiene rubber, styrene/isoprene/butadiene terpolymer rubber, cis-l,4-polybutadiene, medium vinyl polybutadiene rubber, wherein the medium vinyl polybutadiene rubber has about 35 to 50 weight percent vinyl, high vinyl polybutadiene rubber wherein the high vinyl polybutadiene rubber has about 50 to 75 weight percent vinyl, styrene/isoprene copolymers, emulsion polymerization prepared styrene/butadiene/acrylonitrile terpolymer rubber and butadiene/acrylonitrile copolymer rubber.

47. The tire composition of Claim 40 wherein the emulsion polymerization derived styrene/butadiene has a styrene content of about 20 to about 28 weight percent.

48. The tire composition of Claim 47 wherein the emulsion polymerization derived styrene/butadiene has a styrene content of about 30 to about 45 weight percent.

49. The tire composition of Claim 1 wherein the at least one vulcanizable rubber comprises emulsion polymerization prepared styrene/butadiene/acrylonitrile terpolymer rubber containing from about 2 to about 40 weight percent acrylonitrile.

50. The tire composition of Claim 1 wherein the total amount of silated core polysulfide present in the rubber composition is from about 0.05 to about 25 parts by weight per hundred parts by weight of rubber.

51. The tire composition of Claim 1 wherein the total amount of silated core polysulfide present in the rubber composition is from about 1 to about 10 parts by weight per hundred parts by weight of rubber.

52. The tire composition of Claim 1 further including at least one accelerator.

53. The tire composition of Claim 52 wherein the at least one accelerator comprises tetrabenzylthiuram disulfide.

54. The tire composition according to claim 52 wherein the at least one accelerator comprises tetrabenzylthiuram disulfide and diphenyleneguanidine

55. The tire composition according to claim 52 wherein the at least one accelerator comprises tetrabenzylthiuram disulfide, diphenyleneguanidine and N-tert-buyl-2- benzothiazolesulfenamide.

56. The tire composition according to claim 1 wherein the silated core polysulfide comprises any isomer of (2-triethoxysilylethyl)-bis-(7-triethoxysilyl-3 ,4- dithiaheptyl)cyclohexane.

57. The tire composition according to claim 1 wherein the silated core polysulfide comprises any isomer of (2-triethoxysilylethyl)--bis-(7-triethoxysilyl-3,4,5,6- tetrathianonyl)cyclohexane.

58. A tire at least one component of which comprises the cured tire composition obtained from the tire composition of Claim 1.

59. A tire tread which comprises the cured tire composition obtained from the tire composition of Claim 1.

60. A tire component comprising the cured tire composition obtained from the tire composition of claim 1.

61. An uncured tire component comprising a tire composition obtained from the tire composition of claim 1.