WO2007040692A1 - Vetement protecteur recouvert de polymeres - Google Patents
Vetement protecteur recouvert de polymeres Download PDFInfo
- Publication number
- WO2007040692A1 WO2007040692A1 PCT/US2006/025454 US2006025454W WO2007040692A1 WO 2007040692 A1 WO2007040692 A1 WO 2007040692A1 US 2006025454 W US2006025454 W US 2006025454W WO 2007040692 A1 WO2007040692 A1 WO 2007040692A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- glove
- hollow member
- elastomeric coating
- elastic
- laminate
- Prior art date
Abstract
L'invention concerne un vêtement protecteur recouvert de polymères. Le vêtement peut être configuré pour s'adapter autour du bras, de la jambe, du pied ou de la main d'un porteur. Par exemple, dans un mode de réalisation, le vêtement protecteur comprend un gant. Le gant comprend un élément creux définissant une ouverture destinée à recevoir une main. L'élément creux est fabriqué à partir d'un stratifié élastique. Le stratifié élastique peut comprendre au moins une toile non tissée. L'élément creux comprend en outre un revêtement élastomérique qui recouvre au moins une partie de l'élément creux. Dans un mode de réalisation, par exemple, le revêtement élastomérique recouvre une partie de paume et des parties de doigts du gant.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US11/229,021 | 2005-09-16 | ||
US11/229,021 US20070083980A1 (en) | 2005-09-16 | 2005-09-16 | Polymer-coated protective garment |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2007040692A1 true WO2007040692A1 (fr) | 2007-04-12 |
Family
ID=37507760
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2006/025454 WO2007040692A1 (fr) | 2005-09-16 | 2006-06-29 | Vetement protecteur recouvert de polymeres |
Country Status (2)
Country | Link |
---|---|
US (1) | US20070083980A1 (fr) |
WO (1) | WO2007040692A1 (fr) |
Cited By (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN102429332A (zh) * | 2011-12-30 | 2012-05-02 | 上海瑞斯达防护制品有限公司 | 一种pvc耐切割防护手套 |
EP2641492A1 (fr) * | 2012-03-20 | 2013-09-25 | W.L.Gore & Associates Gmbh | Gant respirable |
EP2641493A1 (fr) * | 2012-03-20 | 2013-09-25 | W.L. Gore & Associates GmbH | Gant trempé respirable |
CN105725315A (zh) * | 2016-04-07 | 2016-07-06 | 东台世目防护用品有限公司 | 月牙形罗口浸胶手套及其制造方法 |
EP3069623A1 (fr) * | 2013-11-12 | 2016-09-21 | Guangxi Xi Nuo Sheng Glove Co., Ltd. | Structure de gant |
RU224990U1 (ru) * | 2023-09-02 | 2024-04-11 | Общество с ограниченной ответственностью "БРИЗ" | Рабочая перчатка |
Families Citing this family (39)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US9731319B2 (en) * | 2004-11-05 | 2017-08-15 | Tamicare Ltd. | Stretchable sheets comprising a variety of layers and zones and methods to produce such products |
US7552501B2 (en) * | 2005-04-29 | 2009-06-30 | Kimberly-Clark Worldwide, Inc. | Finger wipe with improved seam structure |
US7469427B2 (en) * | 2005-06-30 | 2008-12-30 | Kimberly-Clark Worldwide, Inc. | Stretchable and permeable non-woven protective gloves |
US20080178366A1 (en) * | 2007-01-26 | 2008-07-31 | Samir Daher | Cleaning glove |
US8375463B2 (en) * | 2007-03-23 | 2013-02-19 | Jennifer Pickering | Partial protective wear |
DE102007021014A1 (de) * | 2007-05-04 | 2008-11-06 | Paul Hartmann Ag | Bereichsweise mehrlagiger medizinischer Handschuh |
US9498009B2 (en) | 2007-07-16 | 2016-11-22 | Madgrip Holdings, Llc | Utility glove |
US9555567B2 (en) | 2007-07-16 | 2017-01-31 | Madgrip Holdings, Llc | Utility glove |
KR101098999B1 (ko) | 2009-02-02 | 2011-12-28 | 오종찬 | 부직포장갑의 제조를 위한 장치 |
US20100263107A1 (en) * | 2009-04-17 | 2010-10-21 | Ping-Hung Wang | Recovering Sleeve Adopted For A Hand Or A Foot |
US20100275341A1 (en) * | 2009-04-29 | 2010-11-04 | Ansell Healthcare Products Llc | Knitted Glove Having A Single Layer With A Plurality Of Yarns |
US20100325777A1 (en) * | 2009-06-26 | 2010-12-30 | Ansell Limited | Knitted Glove with Tacky Grip Coating |
US20110145967A1 (en) * | 2009-12-22 | 2011-06-23 | Summit Glove Inc. | Protective glove and method of manufacturing the same |
US10004286B2 (en) * | 2011-08-08 | 2018-06-26 | Ford Global Technologies, Llc | Glove having conductive ink and method of interacting with proximity sensor |
EP2614733B1 (fr) * | 2012-01-16 | 2018-11-14 | SHOWA GLOVE Co. | Gant |
US9198474B1 (en) * | 2012-02-29 | 2015-12-01 | Edwin Hacobian | Saturation, chemical, and impact-resistant protective glove |
US20130263354A1 (en) * | 2012-04-06 | 2013-10-10 | Nike, Inc. | Athletic Glove With Overlay |
US11141966B2 (en) | 2012-07-26 | 2021-10-12 | Warwick Mills, Inc. | Method of laminating a performance-enhancing layer to a seamless three dimensional glove |
WO2014018583A1 (fr) * | 2012-07-26 | 2014-01-30 | Warwick Mills, Inc. | Gant tridimensionnel ayant une couche d'amélioration de performance stratifiée sur celui-ci |
CA2808848A1 (fr) | 2013-03-07 | 2014-09-07 | Airboss-Defense | Gant de protection pour charge faible |
US10681944B2 (en) | 2013-07-22 | 2020-06-16 | Summit Glove Inc. | Protective device for use with a glove |
US11925221B2 (en) | 2013-07-22 | 2024-03-12 | Summit Glove Inc. | Protective device for use with a glove having textured grip |
US20150020284A1 (en) * | 2013-07-22 | 2015-01-22 | Summit Glove Inc. | Protective device for use with a glove |
US10750803B2 (en) | 2013-07-22 | 2020-08-25 | Summit Glove Inc. | Protective device for use with a glove |
US20170099891A1 (en) | 2013-07-22 | 2017-04-13 | Summit Glove Inc. | Protective device for use with a glove |
US11825887B2 (en) | 2013-07-22 | 2023-11-28 | Summit Glove Inc. | Protective device for use with a glove |
US9888733B2 (en) | 2013-07-22 | 2018-02-13 | Summit Glove Inc. | Protective device for use with a glove |
US10271596B2 (en) * | 2014-11-11 | 2019-04-30 | Glubbers Llc | Cold weather gloves and mittens |
US11234469B2 (en) * | 2015-07-16 | 2022-02-01 | Zeon Corporation | Dip-formed article and protective glove |
US11229248B2 (en) * | 2015-12-02 | 2022-01-25 | Showa Glove Co. | Supporting glove and method for manufacturing the supporting glove |
EP3445300A4 (fr) * | 2016-04-21 | 2020-01-01 | Fingertips Enterprises, LLC | Appareil de nettoyage de bout de doigt |
CN109414080B (zh) * | 2016-06-28 | 2022-07-15 | W.L.戈尔有限公司 | 用于制造透水汽或透气的三维手套或手套衬里的方法 |
US10645984B2 (en) | 2016-12-20 | 2020-05-12 | Summit Glove Inc. | Protective device for use with a glove |
USD897033S1 (en) | 2018-12-27 | 2020-09-22 | Thomas William Rann | Skincare applicator |
US11399583B2 (en) * | 2019-07-03 | 2022-08-02 | Niphan Tangpirounthum | Glove and a method for producing the same |
US10772695B2 (en) * | 2019-12-31 | 2020-09-15 | Henny Avitan | Glove with medicinal pads and differing thickness regions |
JP2022176103A (ja) * | 2021-05-14 | 2022-11-25 | ショーワグローブ株式会社 | 滑止手袋 |
US20230009381A1 (en) * | 2021-07-08 | 2023-01-12 | Marvin Ascencio | Makeup Removing Glove Assembly |
US20240138501A1 (en) * | 2022-10-31 | 2024-05-02 | Jeffrey D. Heyd | Hand protection device and method of use |
Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4660228A (en) * | 1985-06-08 | 1987-04-28 | Kanebo, Ltd. | Glove |
WO1991012132A1 (fr) * | 1990-02-16 | 1991-08-22 | W.L. Gore & Associates, Inc. | Tissu composite elastomere |
US5560044A (en) * | 1995-03-29 | 1996-10-01 | W. L. Gore & Associates, Inc. | Hand covering |
US5861074A (en) * | 1993-08-11 | 1999-01-19 | Clopay Plastic Products Company, Inc. | Method of making an elastic laminated sheet of an incrementally stretched nonwoven fibrous web and elastomeric film |
WO1999014044A1 (fr) * | 1997-09-15 | 1999-03-25 | Kimberly-Clark Worldwide, Inc. | Film elastique imper-respirant et lamine associe |
US20030050589A1 (en) * | 2000-04-06 | 2003-03-13 | Mcdevitt Jason P. | Disposable finger sleeve for appendages |
Family Cites Families (32)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3338992A (en) * | 1959-12-15 | 1967-08-29 | Du Pont | Process for forming non-woven filamentary structures from fiber-forming synthetic organic polymers |
US3502763A (en) * | 1962-02-03 | 1970-03-24 | Freudenberg Carl Kg | Process of producing non-woven fabric fleece |
US3341394A (en) * | 1966-12-21 | 1967-09-12 | Du Pont | Sheets of randomly distributed continuous filaments |
US3542615A (en) * | 1967-06-16 | 1970-11-24 | Monsanto Co | Process for producing a nylon non-woven fabric |
US3849241A (en) * | 1968-12-23 | 1974-11-19 | Exxon Research Engineering Co | Non-woven mats by melt blowing |
DE2048006B2 (de) * | 1969-10-01 | 1980-10-30 | Asahi Kasei Kogyo K.K., Osaka (Japan) | Verfahren und Vorrichtung zur Herstellung einer breiten Vliesbahn |
DE1950669C3 (de) * | 1969-10-08 | 1982-05-13 | Metallgesellschaft Ag, 6000 Frankfurt | Verfahren zur Vliesherstellung |
US4100324A (en) * | 1974-03-26 | 1978-07-11 | Kimberly-Clark Corporation | Nonwoven fabric and method of producing same |
US4340563A (en) * | 1980-05-05 | 1982-07-20 | Kimberly-Clark Corporation | Method for forming nonwoven webs |
US4374888A (en) * | 1981-09-25 | 1983-02-22 | Kimberly-Clark Corporation | Nonwoven laminate for recreation fabric |
US4443513A (en) * | 1982-02-24 | 1984-04-17 | Kimberly-Clark Corporation | Soft thermoplastic fiber webs and method of making |
US4818464A (en) * | 1984-08-30 | 1989-04-04 | Kimberly-Clark Corporation | Extrusion process using a central air jet |
US4720415A (en) * | 1985-07-30 | 1988-01-19 | Kimberly-Clark Corporation | Composite elastomeric material and process for making the same |
US4657802A (en) * | 1985-07-30 | 1987-04-14 | Kimberly-Clark Corporation | Composite nonwoven elastic web |
US4652487A (en) * | 1985-07-30 | 1987-03-24 | Kimberly-Clark Corporation | Gathered fibrous nonwoven elastic web |
US4655760A (en) * | 1985-07-30 | 1987-04-07 | Kimberly-Clark Corporation | Elasticized garment and method of making the same |
US4789699A (en) * | 1986-10-15 | 1988-12-06 | Kimberly-Clark Corporation | Ambient temperature bondable elastomeric nonwoven web |
US4781966A (en) * | 1986-10-15 | 1988-11-01 | Kimberly-Clark Corporation | Spunlaced polyester-meltblown polyetherester laminate |
US4981747A (en) * | 1988-09-23 | 1991-01-01 | Kimberly-Clark Corporation | Composite elastic material including a reversibly necked material |
US5226992A (en) * | 1988-09-23 | 1993-07-13 | Kimberly-Clark Corporation | Process for forming a composite elastic necked-bonded material |
US4965122A (en) * | 1988-09-23 | 1990-10-23 | Kimberly-Clark Corporation | Reversibly necked material |
US5114781A (en) * | 1989-12-15 | 1992-05-19 | Kimberly-Clark Corporation | Multi-direction stretch composite elastic material including a reversibly necked material |
US5407715A (en) * | 1990-11-28 | 1995-04-18 | Tactyl Technologies, Inc. | Elastomeric triblock copolymer compositions and articles made therewith |
US5112900A (en) * | 1990-11-28 | 1992-05-12 | Tactyl Technologies, Inc. | Elastomeric triblock copolymer compositions and articles made therewith |
US5385775A (en) * | 1991-12-09 | 1995-01-31 | Kimberly-Clark Corporation | Composite elastic material including an anisotropic elastic fibrous web and process to make the same |
US5244482A (en) * | 1992-03-26 | 1993-09-14 | The University Of Tennessee Research Corporation | Post-treatment of nonwoven webs |
US5587225A (en) * | 1995-04-27 | 1996-12-24 | Kimberly-Clark Corporation | Knit-like nonwoven composite fabric |
US5900452A (en) * | 1996-08-12 | 1999-05-04 | Tactyl Technologies, Inc. | S-EB-S block copolymer/oil aqueous dispersion and its use in forming articles |
US6969441B2 (en) * | 2000-05-15 | 2005-11-29 | Kimberly-Clark Worldwide, Inc. | Method and apparatus for producing laminated articles |
US6772441B2 (en) * | 2002-02-21 | 2004-08-10 | Alfred W. Lucas, Jr. | Soccer goalkeeper glove |
US20050130522A1 (en) * | 2003-12-11 | 2005-06-16 | Kaiyuan Yang | Fiber reinforced elastomeric article |
US20050127578A1 (en) * | 2003-12-11 | 2005-06-16 | Triebes Thomas G. | Method of making fiber reinforced elastomeric articles |
-
2005
- 2005-09-16 US US11/229,021 patent/US20070083980A1/en not_active Abandoned
-
2006
- 2006-06-29 WO PCT/US2006/025454 patent/WO2007040692A1/fr active Application Filing
Patent Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4660228A (en) * | 1985-06-08 | 1987-04-28 | Kanebo, Ltd. | Glove |
WO1991012132A1 (fr) * | 1990-02-16 | 1991-08-22 | W.L. Gore & Associates, Inc. | Tissu composite elastomere |
US5861074A (en) * | 1993-08-11 | 1999-01-19 | Clopay Plastic Products Company, Inc. | Method of making an elastic laminated sheet of an incrementally stretched nonwoven fibrous web and elastomeric film |
US5560044A (en) * | 1995-03-29 | 1996-10-01 | W. L. Gore & Associates, Inc. | Hand covering |
WO1999014044A1 (fr) * | 1997-09-15 | 1999-03-25 | Kimberly-Clark Worldwide, Inc. | Film elastique imper-respirant et lamine associe |
US20030050589A1 (en) * | 2000-04-06 | 2003-03-13 | Mcdevitt Jason P. | Disposable finger sleeve for appendages |
Cited By (14)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN102429332A (zh) * | 2011-12-30 | 2012-05-02 | 上海瑞斯达防护制品有限公司 | 一种pvc耐切割防护手套 |
CN104159461A (zh) * | 2012-03-20 | 2014-11-19 | W.L.戈尔有限公司 | 可呼吸的浸渍手套 |
EP2641493A1 (fr) * | 2012-03-20 | 2013-09-25 | W.L. Gore & Associates GmbH | Gant trempé respirable |
WO2013139787A1 (fr) * | 2012-03-20 | 2013-09-26 | W. L. Gore & Associates Gmbh | Gant perméable à l'air par trempage |
WO2013139788A1 (fr) * | 2012-03-20 | 2013-09-26 | W. L. Gore & Associates Gmbh | Gant respirant |
CN104144621A (zh) * | 2012-03-20 | 2014-11-12 | W.L.戈尔有限公司 | 可呼吸的手套 |
EP2641492A1 (fr) * | 2012-03-20 | 2013-09-25 | W.L.Gore & Associates Gmbh | Gant respirable |
CN104144621B (zh) * | 2012-03-20 | 2015-08-26 | W.L.戈尔有限公司 | 可呼吸的手套 |
CN104159461B (zh) * | 2012-03-20 | 2015-11-25 | W.L.戈尔有限公司 | 可呼吸的浸渍手套 |
EP3069623A1 (fr) * | 2013-11-12 | 2016-09-21 | Guangxi Xi Nuo Sheng Glove Co., Ltd. | Structure de gant |
EP3069623A4 (fr) * | 2013-11-12 | 2017-04-26 | Guangxi Xi Nuo Sheng Glove Co., Ltd. | Structure de gant |
US10342273B2 (en) | 2013-11-12 | 2019-07-09 | Guangxi Xi Nuo Sheng Glove Co., Ltd. | Glove |
CN105725315A (zh) * | 2016-04-07 | 2016-07-06 | 东台世目防护用品有限公司 | 月牙形罗口浸胶手套及其制造方法 |
RU224990U1 (ru) * | 2023-09-02 | 2024-04-11 | Общество с ограниченной ответственностью "БРИЗ" | Рабочая перчатка |
Also Published As
Publication number | Publication date |
---|---|
US20070083980A1 (en) | 2007-04-19 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US20070083980A1 (en) | Polymer-coated protective garment | |
US7469427B2 (en) | Stretchable and permeable non-woven protective gloves | |
US20060143767A1 (en) | Breathable protective articles | |
RU2438535C2 (ru) | Устойчивая к разрезам перчатка (варианты) | |
JP5475462B2 (ja) | 防風防水通気性のシーム付き物品 | |
US7624456B2 (en) | Windproof waterproof breathable seamed articles | |
US6934969B2 (en) | Anti-wicking protective workwear and methods of making and using same | |
US20080235850A1 (en) | Glove Having High Coefficient of Friction Regions | |
US5423090A (en) | Glove with floating puncture resistant pad | |
EP3337346B1 (fr) | Articles tridimensionnels sans soudure adaptables et procédés associés | |
NO329214B1 (no) | Med mellomrom forbundne ikke-vevede deponerbare kirurgiske laminater | |
US20080263738A1 (en) | Impact protection glove | |
US20080078046A1 (en) | Applicator for distributing a substance onto a target surface | |
EP2741627B1 (fr) | Vêtement protecteur sans couture | |
US6081927A (en) | Protective glove | |
WO2005046373A1 (fr) | Vetement de protection a renforts coudes elastomeres | |
BG3789U1 (bg) | Защитно облекло |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 06799982 Country of ref document: EP Kind code of ref document: A1 |