WO2007015523A1 - 湿度検知材 - Google Patents

湿度検知材 Download PDF

Info

Publication number
WO2007015523A1
WO2007015523A1 PCT/JP2006/315319 JP2006315319W WO2007015523A1 WO 2007015523 A1 WO2007015523 A1 WO 2007015523A1 JP 2006315319 W JP2006315319 W JP 2006315319W WO 2007015523 A1 WO2007015523 A1 WO 2007015523A1
Authority
WO
WIPO (PCT)
Prior art keywords
safranin
humidity
silica gel
ppm
supported
Prior art date
Application number
PCT/JP2006/315319
Other languages
English (en)
French (fr)
Inventor
Qiwei Wu
Xiaoqing Chen
Shigekazu Torigoe
Original Assignee
Torishige Sangyo Co., Ltd.
Qingdao Yuanhe Trading & Industrial Co., Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Torishige Sangyo Co., Ltd., Qingdao Yuanhe Trading & Industrial Co., Ltd. filed Critical Torishige Sangyo Co., Ltd.
Publication of WO2007015523A1 publication Critical patent/WO2007015523A1/ja

Abstract

　塩化コバルトを使用せず、塩化コバルトと同一色に変色可能な、人体に安全な湿度検知材を提供することにある。 　乾燥時には青色に、吸湿時には赤色またはピンク色に呈色して乾燥状態または吸湿状態を識別するための指示薬を、シリカゲルに担持している。指示薬としては、有機系色素であるサフラニンが好適である。サフラニンは、２０ｐｐｍ以上２００ｐｐｍ以下となるように担持されている。これにより、従来の塩化コバルトによる変色の認識を変えずに塩化コバルトを代替することができ、使用者は、違和感なく使用することができる。

Description

明 細 書
湿度検知材
技術分野
[0001] 本発明は、食品や電気部品等を保存する包装容器内の湿度を検知する検知材に 関し、より詳しくは、有機色素を使用した検知材に関する。
背景技術
[0002] 湿度を検知する検知材 (以下、湿度検知材）として、塩ィ匕コバルトを担持したシリカ ゲルが広く知られている。このシリカゲルは、乾燥時には青色を呈し、吸湿時には赤 色またはピンク色を呈する。これらの 2色の違いを識別することにより、シリカゲルが吸 湿した力否かを判定し、乾燥剤としての有効性を判断することができる。これらのシリ 力ゲルの色は、湿度検知材として長い間定着し、使用者は、色を見た瞬間に、乾燥 剤の状態を判断することができる。
[0003] ところで、塩ィ匕コバルトは、発癌性の可能性が指摘されており、人体の安全面から 塩ィ匕コバルトの使用が規制されつつある。この塩ィ匕コバルトの代替技術として、特許 文献 1には、酸塩基指示薬を使用することが記載されている。
また、酸塩基指示薬は様々なものがあり、湿度検知材以外にも、他の用途に利用さ れることが知られている（例えば、特許文献 2参照。 )0
[0004] 特許文献 1：特開 2002— 350419号公報
特許文献 2：特開昭 59— 142463号公報
発明の開示
発明が解決しょうとする課題
[0005] 特許文献 1に記載の酸塩基指示薬は、赤色、青色、黄色、緑色、橙色等、複数種 の湿度表示色に段階的に変色するものである。これにより、使用者は、乾燥時や吸 湿時の変色パターンを覚えて認識しなければならず、塩ィ匕コバルトによる変色の認識 を変えずに塩化コバルトを代替することができない。従って、使用者は、湿度検知材 を入手する時にその変色パターンを確認して、乾燥剤としての有効性を認識しなけ ればならず、使用しづらい。 [0006] さらに、特許文献 1に記載の酸塩基指示薬を使用しても、塩ィヒコバルトの色とは同 一色にはならず、塩ィ匕コノ レトと同じ青色と赤色 (またはピンク色）を再現することはで きない。
また、特許文献 2に記載の酸塩基指示薬は、酸素検知材として使用される色素であ り、湿度検知材として使用されるものではない。
[0007] 本発明が解決しょうとする課題は、塩ィ匕コバルトを使用せず、塩ィ匕コバルトと同一色 に変色可能な、人体に安全な湿度検知材を提供することにある。
課題を解決するための手段
[0008] 本発明の湿度検知材は、乾燥時には青色に、吸湿時には赤色またはピンク色に呈 色して乾燥状態または吸湿状態を識別するためのサフラニンを、シリカゲルに担持し てなることを特徴とする。本発明者は、シリカゲルにサフラニンを担持させたものは、 塩化コバルトを使用した従来の湿度検知材と同一色となるように呈色することを発見 し、本発明に至った。サフラニンを使用することにより、塩化コバルトと同一色 (青色と
、赤色またはピンク色）〖こ変色させることができる。
[0009] これにより、従来の塩ィ匕コバルトによる変色の認識を変えずに塩ィ匕コバルトをサフラ ニンに代替することができ、使用者は、色に関して違和感なくサフラニンを使用した 湿度検知材を使用することができる。また、従来の塩ィ匕コバルトをスムーズに代替す ることができ、環境対策にも良い。
[0010] ここで、色について説明する。「同一色」とは、サフラニンを担持した湿度検知材の 色と、塩化コバルトを担持した湿度検知材の色とが、同程度または違和感を感じない 程度の色調であり、両者を比較した場合に、乾燥状態および吸湿状態の識別性に違 和感が生じない色を意味する。具体的には、乾燥状態においては、前記両者が識別 できない程度に類似した青色を呈する（同一色)。また、吸湿状態においては、塩ィ匕 コバルトを担持した湿度検知材は、ピンク色を呈するが、サフラニンを担持した湿度 検知材は、ピンク〜赤色を呈し、艷やかな色となるが、違和感が生じることはないため 、同一色である。サフラニンを担持した湿度検知材の使用開始時は青色なので、使 用者は、従来の塩ィ匕コバルトを担持した湿度検知材の青色のイメージを全く変えるこ となく使用することとなる。 [0011] また、本発明者は、サフラニンの好適な使用量が微量であることと、その使用量の 許容範囲が非常に狭い範囲であることを発見した。
すなわち、サフラニンは、 20ppm以上 200ppm以下となるように担持されることが望 まし 、。湿度検知材全体におけるサフラニンの含量を 20ppm以上 200ppm以下とす れば、湿度検知材は、塩化コバルトを使用した湿度検知材と同一色となり、使用者は 、容易に湿度検知材の有効性を確認することができる。また、サフラニンの含量は非 常に微量であるため、他の指示薬等を使用する場合よりもコスト面で有利であると考 えられる。
[0012] ここで、サフラニンの担持量を 20ppm未満とすると、乾燥時または吸湿時において 、青色や、赤色またはピンク色が薄いものとなり、従来の塩ィ匕コノ レトを使用した湿度 検知材とは同一色にはならない。このため、使用者が使用しづらいものとなる。
また、サフラニンの担持量が 200ppmを超えると、乾燥時または吸湿時において、 青色や、赤色またはピンク色が非常に濃いものとなり、従来の塩ィ匕コバルトを使用し た湿度検知材と同一色とすることができない。また、色が濃くなつて、乾燥時と吸湿時 の判断も困難となる。従って、使用者が使用しづらいものとなる。
[0013] 一方、本発明の湿度検知材は、シリカゲル微粉砕物を紙または榭脂に担持してシ ート状または板状に形成したシート材と、乾燥時には青色に、吸湿時には赤色または ピンク色に呈色して乾燥状態または吸湿状態を識別するためのサフラニンを前記シ 一ト材に担持して形成した湿度検知部と、を備えたことを特徴とする。
[0014] 予めシリカゲルを紙または榭脂に担持しておけば、サフラニンを含んだ水溶液を紙 または榭脂に滴下するだけで湿度検知材を形成することができるため、製造が容易 である。また、塩ィ匕コバルトと同一色 (青色と、赤色またはピンク色）に変色させること ができるため、従来の塩ィ匕コノ レトによる変色の認識のまま使用することが可能となる 発明の効果
[0015] 本発明の最大の特徴は、乾燥時には青色に、吸湿時には赤色またはピンク色に呈 色して乾燥状態または吸湿状態を識別するためのサフラニンを、シリカゲルに担持し てなることを特徴とする。これにより、従来の塩ィ匕コバルトによる変色の認識を変えず に塩ィ匕コバルトを代替することができ、使用者は、違和感なく使用することができる。 図面の簡単な説明
[0016] [図 1]本発明の実施形態である湿度検知材を使用した乾燥剤を示す一部を切り欠い た斜視図である。
[図 2]本発明の実施形態である湿度検知材を示す図である。
符号の説明
[0017] 1 乾燥材
2 乾燥パック
2a 端部
2b 収納部
3 シリカゲノレ
4 湿度検知材
11 湿度検知材
12 シート材
14 湿度検知部
14a, 14b, 14c 湿度検知部
発明を実施するための最良の形態
[0018] 以下、本発明をその実施形態に基づいて説明する。
本発明の湿度検知材は、乾燥時には青色に、吸湿時には赤色またはピンク色に呈 色して乾燥状態または吸湿状態を識別するための指示薬を、シリカゲルに担持して いる。指示薬としては、有機系色素であるサフラニン (C H C1N )が好適であり、サ
20 19 4
フラニンは、 20ppm以上 200ppm以下となるように担持されて!、る。
[0019] シリカゲルは多孔質であり、この孔内に酸性物質 (硫酸等）とサフラニンを含浸して おけば、乾燥状態では pHは低いため、青色を呈する。湿度が高くなると、シリカゲル の吸湿作用により空気中の水蒸気を吸湿し、この吸湿量は、酸性物質の濃度、すな わち pHを変える（高くなる）こととなる。これにより、 pHの変化に対応して赤色または ピンク色へと変色する。すなわち、湿度検知材は、湿度の変化によって、変色するこ ととなる。同様に、乾燥すると、シリカゲル中の水分が減少して、 pHが低くなり、青色 へと戻る。
[0020] 以上のように、サフラニンを使用することにより、従来の塩ィ匕コバルトによる変色の認 識を変えずに塩化コバルトを代替することができ、使用者は、サフラニンを使用した 湿度検知材を使用しても色に関して違和感なく使用することができる。
[0021] 以下、実施例について説明する。
(実施例 1)
本発明の実施形態である湿度検知材の製造方法にっ 、て説明する。市販の粒状 シリカゲル (A型)を蒸気により水分を飽和状態とした後、事前にサフラニンを水に溶 力して得たサフラニン液をシリカゲルに含浸させて、最終製品中に 20ppm以上 200p pm以下となるように担持する。次に、硫酸により酸度を調整し、水洗後、乾燥して、青 色で粒状の湿度検知材 (最終製品）となる。ここで、 20ppm以上 200ppm以下とは、 質量 lkgの製品中に質量 20mg以上 200mg以下のサフラニンが担持されて 、ること を意味する。
[0022] ここで、サフラニンを水溶液の状態にして力 含浸することにより、サフラニンの使用 量を微量としながらも、均一に、且つ、シリカゲルの孔に担持することができる。粉状 のサフラニンを使用した場合、サフラニンの粒はシリカゲルの小孔に入り込まずに吸 着しないため、シリカゲルに担持することができない。これにより、シリカゲルは呈色し な力つたり、不均一となって呈色にばらつきを生じたりすることとなり好ましくない。
[0023] 次に、図面を用いて本発明をその実施形態に基づいて説明する。図 1は、本発明 の実施形態である湿度検知材を使用した乾燥剤を示す一部を切り欠いた斜視図で ある。
図 1に示すように、乾燥剤 1は、乾燥パック 2の内部に、シリカゲル 3と湿度検知材 4 とを有している。乾燥パック 2は、端部 2aと収容部 2bとから構成されており、シリカゲ ル 3と湿度検知材 4とを収容部 2bに収容した後に、熱融着して端部 2aが形成されて いる。シリカゲル 3および湿度検知材 4は、直径が概ね 2mm〜4mmの粒状であるが 、これに限定するものではなぐ適宜粒度を設計変更することができる。
[0024] 乾燥パック 2は、通気性を備えた榭脂製であり、収容部 2b内に水蒸気が入りこんで 、シリカゲル 3と湿度検知材 4を、吸湿または乾燥することができる。湿度検知材 4の 使用割合は、シリカゲル 3と湿度検知材 4との合計重量の約 10%としている。乾燥パ ック 2の大きさは、約 5cm X約 6cmである力 状況に合わせて変更することができる。
[0025] 次に、湿度検知材 4のサフラニンの担持量 (含有量)を 13段階に変えて、乾燥状態 および吸湿状態とした時の識別性試験を行った結果を表 1に示す。表 1の結果から、 製品中の担持量 (含有量）として、 20ppm以上 200ppm以下が好適であり、より好ま しくは、 50ppm以上 lOOppm以下と!/、う極めて狭!、範囲にぉ 、て特に有効である。 この範囲内においては、きれいに発色して艷やかであり、塩ィ匕コバルトを使用した従 来のシリカゲルの色とほぼ同一の色を再現することができる。従って、従来の塩化コ バルトによる変色の認識を変えずに塩化コバルトを代替することができ、使用者は、 違和感なく使用することができる。
[0026] [表 1]
Figure imgf000008_0001
[0027] また、その他の湿度検知材 4の性質として、吸湿率にっ 、ては、 RH (相対湿度） 20 %時においては 12%以上、 RH50%においては 28%以上、 RH90%では 38%以 上であり、塩ィ匕コバルトを使用した場合とほぼ同等の状態としてある。乾燥状態の含 水率は 2%以下である。
なお、本実施形態において担持させたシリカゲルは A型のものである力 B型や C 型のシリカゲルに担持して変色させることも可能である。
[0028] (実施例 2) 次に、本発明の他の実施形態である湿度検知材について図 2を用いて説明する。 湿度検知材 11は、シリカゲルの微粉砕物を紙に担持してシート状または板状に形 成したシート材 12と、このシート材 12に乾燥状態または吸湿状態を識別するための 指示薬としてのサフラニンを担持してなる三つの湿度検知部 14とを備えて 、る。サフ ラニンは、シート材 12のシリカゲルに 20ppm以上 200ppm以下となるように担持され ており、湿度検知部 14が湿度を検知することができる。ここで、 20ppm以上 200ppm 以下とは、質量 lkgのシリカゲル中に質量 20mg以上 200mg以下のサフラニンが担 持されて!ヽることを意味する。
[0029] サフラニンは、事前に水に溶かし、 目的の検出湿度において発色するように硫酸で 酸度を調整して得たサフラニン液をシート材 12に含浸させて、シリカゲルに担持して いる。シリカゲルは、 325メッシュ (44 m)以下の微粉砕物を使用しており、紙の製 造時にシリカゲルを混合して、紙全体に均一に担持して 、る。
以上のように、予めシリカゲルを紙に担持しておけば、サフラニンを含んだ水溶液を 紙または榭脂に滴下するだけで湿度検知材を形成することができる。ここで、シリカゲ ル微粉砕物として粒径が小さ 、ものが好ましぐ 325メッシュ（44 m)のものを使用 することにより、均一に紙または榭脂に担持させることができる力 100〜325メッシュ 程度の粒度でも担持して使用することは可能であると考えられる。
[0030] ここで、紙にシリカゲルを担持する方法としては、シート状または板状のシリカゲル を形成した後に紙に担持して 2層構造としても良ぐまた、紙にスポット状にシリカゲル を担持しても良い。
さらに、シート材 12のベース材料としては紙に限定することなぐ榭脂、布等も選択 することができる。また、湿度検知材 11の大きさは、約 8cm X 4cmとしている力 使用 状況にお 、て変更しても良 、。
[0031] 次に、湿度検知材 11の使用方法について説明する。シート材 12には、湿度検知 部 14a, 14b, 14cが設けられており、それぞれの湿度（RH)が 50%、 40%、 30%の 状態になったときに呈色 (変色)することにより湿度を検知する。各湿度の設定値は、 各湿度検知部 14a, 14b, 14cの酸度を調整することにより設定されている。これによ り、使用者は、湿度検知材 11を見て、湿度が 30%未満、 30%以上 40%未満、 40% 以上 50%未満、 50%を超えた場合の各状態において、表 2のように識別することが できる。なお、各境界域の湿度においては、青色から赤色またはピンク色へと変わる ため、やや薄い色となる。
[0032] [表 2]
Figure imgf000010_0001
なお、湿度検知部 14の個数は、 3箇所に限定されるものではなぐ検知可能な湿度 を適宜調整して、使用状況によりさらに多くの箇所に設けることも可能である。
[0033] 本実施形態においても、塩ィ匕コノ レトを使用した従来のシリカゲルの色と同一の色 を再現することができるため、使用者は、従来の色の認識を変えることなぐ湿度検知 材 11を使用することができる。
産業上の利用可能性
[0034] 本発明の湿度検知材および湿度検知材は、塩ィ匕コバルトを使用せずに、食品ゃ電 気部品等を保存する包装容器内の湿度を検知するための検知材として広く利用する ことができる。

Claims

請求の範囲
[1] 乾燥時には青色に、吸湿時には赤色またはピンク色に呈色して乾燥状態または吸 湿状態を識別するためのサフラニンを、シリカゲルに担持してなることを特徴とする湿 度検知材。
[2] 前記サフラニンは、 20ppm以上 200ppm以下となるように担持されている請求項 1 記載の湿度検知材。
[3] シリカゲル微粉砕物を紙、布または榭脂に担持してシート状または板状に形成した シート材と、
乾燥時には青色に、吸湿時には赤色またはピンク色に呈色して乾燥状態または吸 湿状態を識別するためのサフラニンを前記シート材に担持して形成した湿度検知部 と、を備えたことを特徴とする湿度検知材。
[4] シリカゲルに、乾燥時には青色に、吸湿時には赤色またはピンク色に呈色して乾燥 状態または吸湿状態を識別するためのサフラニンの水溶液を含浸させて、前記シリ 力ゲルに前記サフラニンを担持させることを含む湿度検知材の製造方法。
[5] 前記サフラニンを、 20ppm以上 200ppm以下となるように担持させる請求項 4記載 の湿度検知材の製造方法。
[6] シリカゲルの微粉砕物を紙、布または榭脂に担持させてシート状または板状にする こと、
前記シート状または板状に形成されたシート材に、乾燥時には青色に、吸湿時に は赤色またはピンク色に呈色して乾燥状態または吸湿状態を識別するためのサフラ ニンの水溶液を含浸させて、前記シリカゲルに前記サフラニンを担持させることを含 む湿度検知材の製造方法。
[7] 前記サフラニンを、 20ppm以上 200ppm以下となるように担持させる請求項 6記載 の湿度検知材の製造方法。
[8] 前記サフラニンの水溶液を、 目的の検出湿度において前記サフラニンが発色する ように、酸性物質で酸度を調整することを含む請求項 4から 7の 、ずれかの項に記載 の湿度検知材の製造方法。
PCT/JP2006/315319 2005-08-04 2006-08-02 湿度検知材 WO2007015523A1 (ja)