WO2005056852A2 - Nickel-containing alloys, method of manufacture thereof and articles derived therefrom - Google Patents
Nickel-containing alloys, method of manufacture thereof and articles derived therefrom Download PDFInfo
- Publication number
- WO2005056852A2 WO2005056852A2 PCT/US2004/031781 US2004031781W WO2005056852A2 WO 2005056852 A2 WO2005056852 A2 WO 2005056852A2 US 2004031781 W US2004031781 W US 2004031781W WO 2005056852 A2 WO2005056852 A2 WO 2005056852A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- nickel
- weight percent
- containing alloy
- equal
- titanium
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C19/00—Alloys based on nickel or cobalt
- C22C19/03—Alloys based on nickel or cobalt based on nickel
- C22C19/05—Alloys based on nickel or cobalt based on nickel with chromium
- C22C19/051—Alloys based on nickel or cobalt based on nickel with chromium and Mo or W
- C22C19/055—Alloys based on nickel or cobalt based on nickel with chromium and Mo or W with the maximum Cr content being at least 20% but less than 30%
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C19/00—Alloys based on nickel or cobalt
- C22C19/03—Alloys based on nickel or cobalt based on nickel
- C22C19/05—Alloys based on nickel or cobalt based on nickel with chromium
- C22C19/051—Alloys based on nickel or cobalt based on nickel with chromium and Mo or W
- C22C19/056—Alloys based on nickel or cobalt based on nickel with chromium and Mo or W with the maximum Cr content being at least 10% but less than 20%
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C19/00—Alloys based on nickel or cobalt
- C22C19/03—Alloys based on nickel or cobalt based on nickel
- C22C19/05—Alloys based on nickel or cobalt based on nickel with chromium
- C22C19/058—Alloys based on nickel or cobalt based on nickel with chromium without Mo and W
Definitions
- This disclosure is related to nickel-containing alloys, methods of manufacture thereof and the articles derived therefrom.
- High temperature alloys suitable for use in turbine nozzle and airfoil applications generally display high temperature strength, corrosion resistance, and properties such as castability and weldability.
- the process of optimizing one property generally results in the reduction of another.
- the process of alloy design generally results in compromises to achieve the best overall mix of properties to satisfy the various requirements of component design. In such a design process, rarely is any one property maximized. Rather, through development of a balanced chemistry and proper heat treatment, the best compromise among the desired properties is achieved.
- Cobalt containing alloys are found to be used for first stage turbine nozzle applications despite their susceptibility to thermal fatigue cracking. The reason for the acceptance of these alloys is the ease with which they can be repair welded. However, in latter stage nozzles, cobalt-based alloys have been found to be creep limited to the point where downstream creep of the nozzles can result in unacceptable reductions of turbine diaphragm clearances. Although cobalt- based alloys with adequate creep strength for these latter stage nozzle applications are available, they do not possess the desired weldability characteristics. It is therefore desirable to find other alloys that display creep resistance, hot corrosion resistance, castability and weldability, and that can be used in first stage and later stage turbine nozzle applications.
- a nickel -containing alloy comprising about 1.5 to about 4.5 weight percent aluminum; about 1.5 to about 4.5 weight percent titanium; up to about 3 weight percent niobium; about 14 to about 28 weight percent chromium; with the remainder being nickel.
- a nickel-containing alloy comprising about 1.6 to about 1.8 weight percent aluminum; about 2.2 to about 2.4 weight percent titanium; about 1.25 to 1.45 weight percent niobium; about 22 to about 23 weight percent chromium; about 18.5 to about 19.5 weight percent cobalt; about 0.08 to about 0.12 weight percent carbon; about 1.9 to about 2.1 weight percent tungsten; and about 0.002 to about 0.006 weight percent boron; up to 0.01 weight percent zirconium; with the remainder being nickel.
- Disclosed herein is a method for manufacturing an article comprising casting an alloy comprising about 1.5 to about 4.5 weight percent aluminum; about 1.5 to about 4.5 weight percent titanium; up to about 3 weight percent niobium; about 14 to about 28 weight percent chromium; about 10 to 23 weight percent cobalt; about 1 to about 3 weight percent of tungsten, rhenium, ruthenium, molybdenum, or a combination thereof; about 0.02 to about 0.15 weight percent of carbon; about 0.001 to about 0.025 weight percent of boron; up to 0.2 weight percent of zirconium, hafnium, or a combination thereof; into a mold; and solidifying the casting an alloy comprising about 1.5 to about 4.5 weight percent aluminum; about 1.5 to about 4.5 weight percent titanium; up to about 3 weight percent niobium; about 14 to about 28 weight percent chromium; about 10 to 23 weight percent cobalt; about 1 to about 3 weight percent of tungsten, rhenium, ruthenium, molybdenum
- the figure is graphical representation of the strain versus time for two samples subjected to a constant stress of 15 ksi at a temperature of 871 °C.
- the nickel-containing alloy can advantageously be used for both first stage and later stage turbine nozzle applications as well as for use in large buckets for turbines.
- the nickel-containing alloy comprises nickel, chromium, cobalt, tungsten, aluminum, titanium, niobium, and other necessary elements.
- the nickel-containing alloy has unique combination of concentrations of aluminum and titanium when compared with other similar alloys. This results in a decrease or elimination of the presence of undesirable phases such as the eta ( ⁇ ) phase with an hexagonal crystal structure and a formula of M Ti, where M is nickel or an alloy of nickel, such as nickel-cobalt, and the like. This decrease in the ⁇ phase, promotes an increase in the creep resistance, as well as renders the alloy metallurgically stable at high temperatures, e.g., above 600 C.
- the nickel -containing alloy comprises primarily nickel alloyed with chromium, titanium, aluminum, and niobium.
- Optional metals that may be added to the nickel- containing alloy are cobalt, carbon, zirconia, tungsten, boron, tantalum, hafnium, rhenium, ruthenium, molybdenum, or a combination comprising at least one of the foregoing metals.
- the nickel-containing alloy comprises aluminum and titanium in an amount of about 2 to about 9 weight percent (wt.%), of the nickel-containing alloy.
- wt.% weight percent
- an amount of aluminum combined with titanium of greater than or equal to about 2.5 wt.%, preferably greater than or equal to about 3.0 wt.%, and more preferably greater than or equal to about 4 wt.% of the nickel -containing alloy may be used.
- the aluminum content in the nickel-containing alloy is about 1.5 to about 4.5 wt.% of the nickel-containing alloy. Preferred values of aluminum are greater than or equal to about 1.6, with greater than or equal to about 1.7 more preferred. Preferred values of aluminum are less than or equal to about 4.00, with less than or equal to about 3 more preferred, and less than or equal to about 2.5 wt.% even more preferred.
- the titanium content in the nickel-containing alloy is about 1.5 to about 4.5 wt.%, of the nickel- containing alloy. Preferred values of titanium are greater than or equal to about 1.65, with greater than or equal to about 2 more preferred, and greater than or equal to about 2.25 wt.% even more preferred.
- titanium are less than or equal to about 4, with less than or equal to about 3.5 more preferred, and less than or equal to about 3 wt.% even more preferred.
- the atomic ratio of aluminum to titanium in the nickel- containing alloy is about 0.2 to about 1.5.
- An aluminum to titanium atomic ratio within this range generally permits the improvement of hot corrosion resistance, weldability, and castability.
- Other aluminum to titanium atomic ratios that may be utilized within this range are greater than or equal to about 0.3, preferably greater than or equal to about 0.4, and more preferably greater than or equal to about 0.5.
- a preferred value for the ⁇ ' phase is 15 to 45 volume percent.
- Strength in high temperature nickel- containing alloys generally derives from several different mechanisms such as the precipitation strengthening of a ⁇ ' phase, solid solution strengthening and carbide strengthening at grain boundaries.
- the ( ⁇ 1 ) phase consists of [Ni 3 (Al, Ti)]. Of these, precipitation strengthening of the ⁇ ' phase is the primary strengthening mechanism for the nickel-containing alloys.
- the content of the primary precipitation-strengthening elements i.e., titanium, aluminum, and niobium is maintained in an amount of about 2 to about 12 wt.%, of the nickel-containing alloy.
- the nickel-containing alloy is devoid of tantalum. It is generally desirable to have the niobium present in an amount of up to about 3 wt.%, of the nickel-containing alloy. Within this range, amounts of less than or equal to about 2.5, preferably less than or equal to about 2.0, and more preferably less than or equal to about 1.75 wt.% may be used. An exemplary value of niobium is about 1.35 wt.% of the nickel-containing alloy.
- Chromium is generally present in an amount of about 14 to about 28 wt.%, of the nickel-containing alloy. Within this range, it is generally desirable to use the chromium in amounts of greater than or equal to about 16, preferably greater than or equal to about 17, and more preferably greater than or equal to about 20 wt.%, of the nickel-containing alloy. Also desirable within this range, is an amount of less than or equal to about 27, preferably less than or equal to about 26, and more preferably less than or equal to about 25 wt.%, of the nickel-containing alloy. An exemplary amount of chromium is about 22 to about 23 wt.% of the total nickel-containing alloy.
- the nickel comprises the remaining weight percent of the nickel-containing alloy.
- the nickel is present in an amount of about 40 to about 70 wt.%, of the nickel- containing alloy. Within this range, it is generally desirable to use the nickel in amounts of greater than or equal to about 43, preferably greater than or equal to about 44, and more preferably greater than or equal to about 46 wt.%, of the nickel- containing alloy. Also desirable within this range, is an amount of less than or equal to about 65, preferably less than or equal to about 60, and more preferably less than or equal to about 55 wt.%, of the nickel-containing alloy. An exemplary amount of nickel is about 45 to about 55 wt.% of the nickel-containing alloy.
- optional metals that may be added to the nickel-containing alloy are cobalt, carbon, tungsten, zirconium and boron.
- Cobalt is generally added in amounts of about 10 to about 24 wt.%, of the total nickel-containing alloy. Within this range, amounts of greater than or equal to about 14, preferably greater than or equal to about 15, and more preferably greater than or equal to about 17 wt.%, of the nickel- containing alloy may be used. Also desirable for use within this range are amounts of less than or equal to about 23.5, preferably less than or equal to about 22.5, and more preferably less than or equal to about 21 wt.%, of the total nickel-containing alloy. An exemplary amount of cobalt is about 18.5 to about 19.5 wt.% of the total nickel- containing alloy.
- Carbon is generally added in amounts of less than 0.15 wt.%.
- a preferred amount of carbon is 0.02 to about 0.15 wt%.
- the carbon generally alloys with metals like titanium, tungsten and the like to form monocarbides. Generally the titanium and/or the tungsten in the monocarbide constitutes an amount of less than or equal to about 80 wt.% of the carbide phase.
- An exemplary amount of carbon is about 0.02 to about 0.15 wt.%, of the nickel-containing alloy.
- Tungsten may be present in amounts of less than or equal to about 3 wt.%, of the nickel-containing alloy.
- the tungsten may be substituted by molybdenum, rhenium, ruthenium, and the like if desired.
- An exemplary amount of tungsten is about 1.9 to about 2.1 wt.%, of the nickel-containing alloy.
- Boron may also be present in amounts of less than or equal to about 0.025 wt.%, of the nickel-containing alloy.
- a preferred amount of boron is about 0.001 to about 0.025 wt% of the nickel-containing alloy.
- the boron generally reacts with the metals in the nickel-containing alloy to form metal borides.
- An exemplary amount of boron in the nickel-containing alloy is about 0.002 to about 0.006 wt.%, of the nickel- containing alloy.
- Zirconium may also added in amounts of less than or equal to about 0.2 wt.%, of the nickel-containing alloy. Zirconium may be substituted with hafnium if desired. An exemplary amount of zirconium is about 0.01 wt.%, of the nickel-containing alloy.
- the nickel-containing alloy may be processed in one of several existing methods to form components for a gas turbine.
- components include rotating buckets (or blades), non-rotating nozzles (or vanes), shrouds, combustors, and the like.
- Preferred components for utilizing the nickel-containing alloy are nozzles and buckets in gas turbines.
- the turbine components may be formed by a variety of different processes such as, but not limited to, powder metallurgy processes (e.g., sintering, hot pressing, hot isostatic processing, hot vacuum compaction, and the like), ingot casting followed by directional solidification, investment casting, ingot casting followed by thermo-mechanical treatment, near-net-shape casting, chemical vapor deposition, physical vapor deposition, and the like.
- Preferred processes are ingot casting followed by directional solidification and investment casting.
- the components of the nickel-containing alloy in the form of a powder, particulates, or the like are heated to a temperature of about 1350 to about 1750°C, to melt the metal components.
- the molten metal may then be poured into a mold in a casting process to produce the desired shape.
- the casting process may involve investment casting, ingot casting, or the like.
- Investment casting is generally used to make parts that cannot be produced by normal manufacturing techniques, such as turbine buckets that have complex shapes, or turbine components that have to withstand high temperatures.
- the mold is made by making a pattern using wax or another material that can be melted away. This wax pattern is dipped in refractory slurry, which coats the wax pattern and forms a skin. This is dried and the process of dipping in the slurry and drying is repeated until a robust thickness is achieved. After this, the entire pattern is placed in an oven and the wax is melted away.
- the mold is pre-heated to about 1000°C to remove any residues of wax as well as to harden the binder.
- the pour in the pre-heated mold also ensures that the mold will fill completely.
- Pouring can be done using gravity, pressure, inert gas, or vacuum conditions.
- the preferred embodiment is to cast in vacuum.
- ingot casting may be used to form the turbine components.
- the melt in the mold is directionally solidified.
- Directional solidification generally results in elongated grains in the direction of growth, thus higher creep strength for the airfoil than an equiaxed cast.
- the cost of directional solidification is higher than that of the equiaxed casting.
- it can be either equiaxed or directional solidified. Following directional and/or equiaxed solidification, the castings are air cooled.
- the castings comprising the nickel-containing alloy may then optionally be subjected to different heat treatments in order to optimize the strength as well as to increase creep resistance.
- the casting is heat treated at temperatures of about 1095°C to about 1200°C to optimize the yield strength and to reduce creep resistance. This heat treatment is generally conducted for a time period of about 1 to about 6 hours. The preferred time period for the heat treatment is 4 hours.
- a heat treatment cycle may be used to reduce the creep resistance. The cycle comprises heating the casting to a temperature of about 1150°C for 4 hours, followed by 1000°C for 6 hours, followed by 900°C for 24 hours, and concluding with 700°C for 16 hours. This heat treatment yields significantly improved values of tensile strength and yield strength.
- the material is solution heat treated at a temperature of 750°C to about 850°C.
- the solution treatment is generally carried out for a time period of about 8 to about 36 hours. An exemplary time period is about 24 hours.
- the heat treatment and the solution heat treatment is used to reduce the presence of any undesirable phases such as the ⁇ phase.
- the casting may optionally be subjected to hot isostatic pressing (HIP).
- HIP hot isostatic pressing
- the hot isostatic pressing is generally preferred for its ability to facilitate substantially reduced porosity and reduced shrinkage in the production of such components.
- process conditions for hot isostatic pressing are chosen so as to achieve consolidation wherein the final composite has a porosity less than or equal to about 10 volume percent, and more preferably less than or equal to about 2 volume percent, based on the total volume of the composite article.
- This process generally involves the application of high pressure and temperatures through the medium of a pressurizing gas to remove internal porosity and voids, thus increasing density and improving the properties of the resultant composite.
- Hot isostatic pressing is generally conducted at temperatures of greater than or equal to about 1000°C, preferably greater than or equal to about 1050°C, more preferably greater than or equal to about 1 150°C.
- the gas pressures utilized during hot isostatic pressing are generally greater than or equal to about 100 mega Pascals (MPa), preferably greater than or equal to about 150 MPa, and more preferably greater than or equal to about 200 MPa.
- Preferred gases used for the process include, but are not limited to, argon, nitrogen, helium, xenon and combinations comprising one of the foregoing.
- the nickel-containing alloys may be advantageously used for large airfoils in large turbines.
- the samples were prepared by taking the various components of the samples shown in the Table 1 and heating them to temperature of 1550°C, to create a melt which was then cast. The samples were air cooled. The samples were annealed at 1 150 °C for 4 hours and aged at 780 °C for 24 hours. The samples were subjected to creep testing in a tensile testing machine at a temperature of 1600°F, under a stress of 15 kilograms per square inch (Ksi). The time taken to reach a strain of 1% was measured and recorded as a function of the samples ability to display creep resistance.
- the sample is a cylindrical dog-bone type standard creep sample with a total length of 4 inches and the gauge diameter of about 0.25 inch.
- the nickel-containing alloy that does not contain tantalum displays superior creep resistance properties over those that do, and hence may be advantageously used in high temperature applications such as in gas turbines and the like.
- the turbines comprising the nickel-containing alloys may be used in aircraft and spacecraft, land based power generation systems and craft that travel on and in water such as ships, submarines, barges, and the like.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Turbine Rotor Nozzle Sealing (AREA)
- Mold Materials And Core Materials (AREA)
Priority Applications (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN2004800354161A CN1886526B (zh) | 2003-09-30 | 2004-09-29 | 含镍合金、其制造方法和由其得到的制品 |
JP2006534011A JP4994843B2 (ja) | 2003-09-30 | 2004-09-29 | ニッケル含有合金、その製造方法、およびそれから得られる物品 |
EP04820347A EP1670962A2 (en) | 2003-09-30 | 2004-09-29 | Nickel-containing alloys, method of manufacture thereof and articles derived therefrom |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US10/675,367 US20050069450A1 (en) | 2003-09-30 | 2003-09-30 | Nickel-containing alloys, method of manufacture thereof and articles derived thereform |
US10/675,367 | 2003-09-30 |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2005056852A2 true WO2005056852A2 (en) | 2005-06-23 |
WO2005056852A3 WO2005056852A3 (en) | 2005-09-01 |
Family
ID=34377131
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2004/031781 WO2005056852A2 (en) | 2003-09-30 | 2004-09-29 | Nickel-containing alloys, method of manufacture thereof and articles derived therefrom |
Country Status (5)
Country | Link |
---|---|
US (1) | US20050069450A1 (ja) |
EP (1) | EP1670962A2 (ja) |
JP (1) | JP4994843B2 (ja) |
CN (1) | CN1886526B (ja) |
WO (1) | WO2005056852A2 (ja) |
Cited By (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US7727318B2 (en) | 2007-01-09 | 2010-06-01 | General Electric Company | Metal alloy compositions and articles comprising the same |
US7846243B2 (en) | 2007-01-09 | 2010-12-07 | General Electric Company | Metal alloy compositions and articles comprising the same |
US7931759B2 (en) | 2007-01-09 | 2011-04-26 | General Electric Company | Metal alloy compositions and articles comprising the same |
EP2319948A1 (en) * | 2009-10-21 | 2011-05-11 | General Electric Company | Nickel-containing alloys, method of manufacture thereof and articles derived therefrom |
EP2902516A1 (en) * | 2014-01-31 | 2015-08-05 | General Electric Company | A weld filler for nickel-base superalloys |
Families Citing this family (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN101429608B (zh) * | 2007-11-06 | 2010-09-29 | 江苏兴海特钢有限公司 | 排气阀用耐热合金的生产工艺 |
US10041153B2 (en) * | 2008-04-10 | 2018-08-07 | Huntington Alloys Corporation | Ultra supercritical boiler header alloy and method of preparation |
US8226886B2 (en) * | 2009-08-31 | 2012-07-24 | General Electric Company | Nickel-based superalloys and articles |
CN102443721B (zh) * | 2010-10-13 | 2013-10-09 | 中国科学院金属研究所 | 一种组织稳定性好、易加工的镍钴基高温合金 |
US8974865B2 (en) | 2011-02-23 | 2015-03-10 | General Electric Company | Component and a method of processing a component |
JP2013133505A (ja) * | 2011-12-27 | 2013-07-08 | Ihi Corp | ニッケル基単結晶超合金熱処理方法及びニッケル基単結晶超合金 |
CN105154719B (zh) * | 2015-10-19 | 2017-12-19 | 东方电气集团东方汽轮机有限公司 | 一种镍基高温合金及其制备方法 |
CN106807794B (zh) * | 2015-12-08 | 2019-03-08 | 中南大学 | 镍基高温合金热挤压工艺参数的确定方法与镍基高温合金的热挤压工艺 |
GB2576305B (en) * | 2018-08-02 | 2022-06-29 | Lpw Technology Ltd | Nickel-based alloy |
IT201800010450A1 (it) * | 2018-11-20 | 2020-05-20 | Nuovo Pignone Tecnologie Srl | Metodo per la produzione additiva di un articolo |
CN110093532B (zh) * | 2019-06-14 | 2020-04-21 | 中国华能集团有限公司 | 一种析出强化型镍基高铬高温合金及其制备方法 |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0053948A1 (en) * | 1980-12-10 | 1982-06-16 | Inco Europe Limited | Nickel-chromium-cobalt base alloys and castings thereof |
EP0302302A1 (en) * | 1987-08-06 | 1989-02-08 | General Electric Company | Nickel-base alloy |
EP1004684A1 (en) * | 1998-11-24 | 2000-05-31 | General Electric Company | Alloy for repairing turbine blades and their components, process thereof and the repaired article |
EP1195446A1 (en) * | 2000-10-04 | 2002-04-10 | General Electric Company | Ni based superalloy and its use as gas turbine disks, shafts, and impellers |
Family Cites Families (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3561955A (en) * | 1966-08-30 | 1971-02-09 | Martin Marietta Corp | Stable nickel base alloy |
GB1298942A (en) * | 1969-03-07 | 1972-12-06 | Int Nickel Ltd | Nickel-chromium-cobalt alloys |
US4039330A (en) * | 1971-04-07 | 1977-08-02 | The International Nickel Company, Inc. | Nickel-chromium-cobalt alloys |
US6416596B1 (en) * | 1974-07-17 | 2002-07-09 | The General Electric Company | Cast nickel-base alloy |
US3976480A (en) * | 1974-09-18 | 1976-08-24 | Hitachi Metals, Ltd. | Nickel base alloy |
US5240491A (en) * | 1991-07-08 | 1993-08-31 | General Electric Company | Alloy powder mixture for brazing of superalloy articles |
JPH09170402A (ja) * | 1995-12-20 | 1997-06-30 | Hitachi Ltd | ガスタービン用ノズル及びその製造法とそれを用いたガスタービン |
WO1997038144A1 (en) * | 1996-04-10 | 1997-10-16 | The Penn State Research Foundation | Improved superalloys with improved oxidation resistance and weldability |
US6258317B1 (en) * | 1998-06-19 | 2001-07-10 | Inco Alloys International, Inc. | Advanced ultra-supercritical boiler tubing alloy |
US20030111138A1 (en) * | 2001-12-18 | 2003-06-19 | Cetel Alan D. | High strength hot corrosion and oxidation resistant, directionally solidified nickel base superalloy and articles |
US6740177B2 (en) * | 2002-07-30 | 2004-05-25 | General Electric Company | Nickel-base alloy |
-
2003
- 2003-09-30 US US10/675,367 patent/US20050069450A1/en not_active Abandoned
-
2004
- 2004-09-29 JP JP2006534011A patent/JP4994843B2/ja not_active Expired - Fee Related
- 2004-09-29 EP EP04820347A patent/EP1670962A2/en not_active Withdrawn
- 2004-09-29 CN CN2004800354161A patent/CN1886526B/zh not_active Expired - Fee Related
- 2004-09-29 WO PCT/US2004/031781 patent/WO2005056852A2/en active Application Filing
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0053948A1 (en) * | 1980-12-10 | 1982-06-16 | Inco Europe Limited | Nickel-chromium-cobalt base alloys and castings thereof |
EP0302302A1 (en) * | 1987-08-06 | 1989-02-08 | General Electric Company | Nickel-base alloy |
EP1004684A1 (en) * | 1998-11-24 | 2000-05-31 | General Electric Company | Alloy for repairing turbine blades and their components, process thereof and the repaired article |
EP1195446A1 (en) * | 2000-10-04 | 2002-04-10 | General Electric Company | Ni based superalloy and its use as gas turbine disks, shafts, and impellers |
Cited By (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US7727318B2 (en) | 2007-01-09 | 2010-06-01 | General Electric Company | Metal alloy compositions and articles comprising the same |
US7846243B2 (en) | 2007-01-09 | 2010-12-07 | General Electric Company | Metal alloy compositions and articles comprising the same |
US7931759B2 (en) | 2007-01-09 | 2011-04-26 | General Electric Company | Metal alloy compositions and articles comprising the same |
EP2319948A1 (en) * | 2009-10-21 | 2011-05-11 | General Electric Company | Nickel-containing alloys, method of manufacture thereof and articles derived therefrom |
EP2902516A1 (en) * | 2014-01-31 | 2015-08-05 | General Electric Company | A weld filler for nickel-base superalloys |
Also Published As
Publication number | Publication date |
---|---|
WO2005056852A3 (en) | 2005-09-01 |
CN1886526A (zh) | 2006-12-27 |
EP1670962A2 (en) | 2006-06-21 |
JP4994843B2 (ja) | 2012-08-08 |
CN1886526B (zh) | 2010-09-01 |
JP2007510056A (ja) | 2007-04-19 |
US20050069450A1 (en) | 2005-03-31 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
KR102225271B1 (ko) | 코발트기 합금 재료 | |
JP6713071B2 (ja) | コバルト基合金積層造形体の製造方法 | |
EP2314727B1 (en) | Nickle-based superalloys and articles | |
US20100135847A1 (en) | Nickel-containing alloys, method of manufacture thereof and articles derived therefrom | |
EP2305848B1 (en) | Nickel-based superalloys and articles | |
JP5773596B2 (ja) | ニッケル基超合金及び物品 | |
JP5398123B2 (ja) | ニッケル系合金 | |
US20050069450A1 (en) | Nickel-containing alloys, method of manufacture thereof and articles derived thereform | |
Lapin | TiAl-based alloys: Present status and future perspectives | |
EP1903121B1 (en) | Nickel-based alloys and articles made therefrom | |
CA3061851C (en) | Cobalt based alloy additive manufactured article, cobalt based alloy product, and method for manufacturing same | |
JP2017532440A (ja) | ジルコニウム添加による強化超合金 | |
JP2007083307A (ja) | アルミニウム合金鋳造方法 | |
EP2305847A1 (en) | Nickle-based superalloys and articles | |
Erickson | Polycrystalline cast superalloys | |
US20040126266A1 (en) | Method for manufacturing composite articles and the articles obtained therefrom | |
Rajabi Nejad et al. | Influence of Withdrawal Rate on As-Cast Microstructure and Stress-Rupture Life of Directionally Solidified Rene80 Superalloy | |
Salwan et al. | Analysis on the Suitability of Powder Metallurgy Technique for Making Nickel Based Superalloys | |
WO2004038056A1 (en) | Heat treatment of alloys having elements for improving grain boundary strength | |
Peter et al. | A comparative study of Ti-Al and Ti-Nb alloys for advanced technological applications | |
CN109554581A (zh) | 一种镍基合金、其制备方法与制造物品 | |
El-Bagoury | INTERNATIONAL JOURNAL OF ENGINEERING SCIENCES & RESEARCH TECHNOLOGY NI BASED SUPERALLOY: CASTING TECHNOLOGY, METALLURGY, DEVELOPMENT, PROPERTIES AND APPLICATIONS |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
WWE | Wipo information: entry into national phase |
Ref document number: 200480035416.1 Country of ref document: CN |
|
AK | Designated states |
Kind code of ref document: A2 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NA NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW |
|
AL | Designated countries for regional patents |
Kind code of ref document: A2 Designated state(s): BW GH GM KE LS MW MZ NA SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IT LU MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
WWE | Wipo information: entry into national phase |
Ref document number: 2006534011 Country of ref document: JP |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2004820347 Country of ref document: EP |
|
WWP | Wipo information: published in national office |
Ref document number: 2004820347 Country of ref document: EP |