WO2005030865A1 - Wässrige dispersionen von copolymerisaten, ihre herstellung und verwendung - Google Patents
Wässrige dispersionen von copolymerisaten, ihre herstellung und verwendung Download PDFInfo
- Publication number
- WO2005030865A1 WO2005030865A1 PCT/EP2004/010491 EP2004010491W WO2005030865A1 WO 2005030865 A1 WO2005030865 A1 WO 2005030865A1 EP 2004010491 W EP2004010491 W EP 2004010491W WO 2005030865 A1 WO2005030865 A1 WO 2005030865A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- general formula
- range
- branched
- mol
- hydrogen
- Prior art date
Abstract
Description
Claims