WO2004076159A1 - 自動車内装パネルの製造法 - Google Patents

自動車内装パネルの製造法 Download PDF

Info

Publication number
WO2004076159A1
WO2004076159A1 PCT/JP2003/002184 JP0302184W WO2004076159A1 WO 2004076159 A1 WO2004076159 A1 WO 2004076159A1 JP 0302184 W JP0302184 W JP 0302184W WO 2004076159 A1 WO2004076159 A1 WO 2004076159A1
Authority
WO
WIPO (PCT)
Prior art keywords
adhesive
skin material
polyolefin
temperature
automobile interior
Prior art date
Application number
PCT/JP2003/002184
Other languages
English (en)
French (fr)
Inventor
Hirokazu Okamoto
Tetsuya Oda
Atsushi Kawata
Original Assignee
Sunstar Giken Kabushiki Kaisha
Honda Giken Kogyo Kabushiki Kaisha
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sunstar Giken Kabushiki Kaisha, Honda Giken Kogyo Kabushiki Kaisha filed Critical Sunstar Giken Kabushiki Kaisha
Priority to PCT/JP2003/002184 priority Critical patent/WO2004076159A1/ja
Priority to AU2003211760A priority patent/AU2003211760A1/en
Publication of WO2004076159A1 publication Critical patent/WO2004076159A1/ja

Abstract

　本発明は、リサイクルに供することができ、かつ自動車内装耐久性に適合する自動車内装パネルの製造法を提供する。　本発明の製造法は、ポリオレフィン基材にポリオレフィン積層体の表皮材を、接着剤を用い加熱下の真空成形法で接着することにより自動車内装パネルを製造する方法において、上記接着剤として、軟化温度８０～１４０℃のカルボン酸もしくはその無水基を含有するポリオレフィンと、カルボン酸もしくはその無水基を含有する軟化温度８０℃以上のスチレン−エチレン／ブテン−スチレンコポリマーの混合物に、潜在性硬化剤として融点１８０～２００℃のヒドラジド系ポリアミンを組合せ、これらを有機溶剤に分散せしめて成る一液型熱架橋性接着剤を用い、および上記表皮材を接着剤中のヒドラジド系ポリアミンの軟化点乃至融点以上の温度で加熱することを特徴とする。

Description

自動車內装パネルの製造法 技術分野
本発明は自動車内装パネルの製造法、 更に詳しくは、 該内装パネルに用いる表 皮材を全て熱可塑性のォレフィン系材料で構成せしめ、 力、つ製造手段の真空成形 明
法において、 ポリオレフィン系ー液型熱架橋性接着剤の架橋温度に合せ真空成形 の加熱条件を、 優れた耐熱性発現に合致するよう調整することにより、 自動車内 田
装耐久性に適合し、 表皮材をォレフィン系材料で構成することにより、 リサイク ルに供することができる自動車内装パネルを製造する方法に関する。 背景技術
従来より、 自動車内装パネルは、 基材としてアタリロニトリル/ブタジエン Z スチレン共重合体 （以下、 A B Sと略す） に、 ポリオレフイン宪泡体と熱可塑性 エラストマ一層を積層した表皮材を接着しており、 これら A B S基材と表皮材の 接着方法として、 一般に真空成形法が多用されている。 かかる真空成形法は、 た とえば A B S基材に接着剤を塗布した後、 成形可能な温度に加熱された表皮材 (予め接着面をブラィマー処理したもの) を真空状態で A B S基材側へ引き込む ことにより成形と接着を同時に行う工法である。
し力 し、 最近に至っては環境負荷の低減や環境保護の見地から、 自動車関係部 品においてもそのリサイクル化が望まれ、 特にリサイクル率が 9 5 %以上となる よう部品材料の検討が要求されている。
そこで、 上記基材として A B Sから熱可塑性のポリオレフインに切替える動き がなされているが、 ポリオレフインは極性が低く一般に接着性が困難であり、 ま たかかる材料の切替えによって、 従来より既存の真空成形設備や成形ライン条件 に大幅な変更が余儀なくされる可能性があった。
また使用される接着剤は、 優れたポリオレフイン接着が果せると同時に、 自動 車内装耐久性 （耐熱性） に合格することも必要である。 発明の開示
本発明者らは、 力かる基材の切替えによっても既存の真空成形設備や成形ライ ン条件に変更を加えることなく、 かつ要求される自動車内装耐久性に十分適合し うる自動車内装パネルの製造法を提供するため鋭意検討を進めたところ、 2種の 熱可塑性ォレフィン系ポリマーおよび特定の潜在性硬化剤を含有する一液型熱架 橋性接着剤を用い、 該潜在性硬化剤の軟化点乃至融点温度に合せ真空成形の加熱 条件を、 優れた耐熱性発現に合致するよう調整することにより、 所期目的の自動 車内装パネルが得られることを見出し、 本宪明を完成させるに至った。
すなわち、 本発明は、 ポリオレフイン基材にポリオレフイン積層体の表皮材を、 接着剤を用い加熱下の真空成形法で接着することにより自動車内装パネルを製造 する方法において、 上記接着剤として、
軟化温度 8 0 ~ 1 4 0 °Cのカルボン酸もしくはその無水基を含有するポリオレ フィンと、 カルボン酸もしくはその無水基を含有する軟化温度 8 0 °C以上のス チレンーェチレン Zプテン一スチレンコポリマーの混合物に、 潜在性硬化剤と して融点 1 8 0〜2 0 0 °Cのヒドラジド系ポリアミンを組合せ、 これらを有機 溶剤に分散せしめて成る一液型熱架橋性接着剤
を用い、 および上記表皮材を接着剤中のヒドラジド系ポリアミンの軟化点乃至融 点以上の温度で加熱することを特徴とする自動車内装パネルの製造法
を提供するものである。
本発明における上記カルボン酸もしくはその無水基を含有するポリオレフイン
(以下、 C O O H変性ポリオレフインと称す) としては、 不飽和二塩基酸 (たと えばマレイン酸、 フマル酸、 シトラコン酸、 メサコン酸等) もしくはその無水物 を導入して変性したポリプロピレン ( P P ) (以下、 C O O H変性 P Pと称す) が例示され、 特に軟化温度 8 0〜1 4 0 °C、 好ましくは 9 0〜1 2 0 °Cのものを 使用する。 軟化温度が 8 0 °C未満では、 自動車内装パネルとして必要とされる耐 熱条件を満足することができず、 また 1 4 0 °Cを越えると、 成形時の加熱温度で は十分に溶融せず、 接着性が不十分となる傾向にある。
また、 この C O OH変性ポリオレフインと混合して用いる上記カルボン酸もし くはその無水基を含有するスチレン一エチレン プテン一スチレンコポリマー (SEBS) とは、 上記の不飽和二塩基酸もしくはその無水物を導入して変性し た SEBS (以下、 。00^1変性3£83と称す） を指称し、 特に軟化温度 7 0 °C以上、 好ましくは 80 ~ 100 °Cのものを使用する。 軟化温度 70 °C未満で は、 自動車内装パネルとしての耐熱要件を満たすことが困難となる。
なお、 COOH変性ポリオレフインと COOH変性 SEB Sの混合比は重量比 で通常、 5 Z 1〜 3 Z 1の範囲で選定すればよい。
本発明における上記ヒドラジド系ポリアミンとしては、 融点 （mp) 180〜 2 00°Cのもの、 たとえばドデカンジカルボン酸ヒドラジド （mpl 84〜18 5°C) 、 ドデカンジォヒドラジド （mpl 89〜191°C) 、 セバシン酸ジヒドラ ジド (mpl 86〜188°C) 等が挙げられる。 使用量は通常、 上記 COOH変性 ポリオレフインおょぴ C O O H変性 SEBSの全力ルボキシル基に対-してアミノ 基のほぼ当量で選定すればよ 1/、。
本発明で用いる一液型熱架橋性接着剤は、 上記混合比の C O O H変性ポリオレ フィンおよび COOH変性 S EB Sと、 所定量のヒドラジド系ポリアミンとを適 当な有機溶剤 （トルエン、 キシレンなど） に分散した系で構成され、 さらに必要 に応じて通常の熱可塑性樹脂 （アクリル樹脂、 ビニール樹脂、 ポリアミド樹脂、 ポリエステル樹脂、 ポリオレフイン、 ポリウレタン、 S E B Sなど） や粘着付与 剤、 安定剤、 ォレフィン系密着剤、 染顔料等を適量添加してもよい。
本発明に係る自動車内装パネルの製造法は、 上記一液型熱架橋性接着剤を用い、 該接着剤中のヒドラジド系ポリアミンの軟化点乃至融点相当温度以上である 16 5-200 °Cに上記表皮材の加熱温度を設定したことを特徴とし、 および以下の 手順に従って実施することができる。
i ) 先ず、 ポリオレフィン基材面または表皮材側 (すなわち、 そのポリオレフ ィン発泡体面） に一液型熱架橋性接着剤を通常、 乾燥厚み 30〜100/imとな るように塗布し、 次いで 80 ~ 120でで 30〜 300秒の条件で乾燥する。 なお、一液型熱架橋性接着剤を表皮材側に塗布する場合、 予め表皮材のポリオ レフイン発泡体に一液型熱架橋性接着剤を塗布、 乾燥してプレコ一トしておくこ とが望ましく、 カかるプレコートした表皮材は、 そのまま、 次の成形工程に供す る力 \ あるいは室温乃至 60°C以下の温度で数ケ月間保存 （ストック） してから 供してもよく、 このストックの場合にも、 十分な接着力を発揮できるようになつ ている。
ところで、 ストック中の接着剤層の癒着 （すなわち、 プレコート表皮材をその 表皮層と接着剤層が接するように順次重ね合せて保管したときの粘着） を避ける ため、 接着剤層中の溶剤含有量を 2重量。 /0以下に調整しておくことが望ましく、 この調整には通常、 接着剤層の乾燥条件として 80〜120°CX 30〜300 秒が採用されてよい。
ii) 次に、 このように一液型熱架橋性接着剤を塗布、 乾燥した後、 ポリオレフ イン基材を 25°C以上、 好ましくは 45〜 90°Cの表面温度に保持しつつ、 一方、 接着剤中のヒドラジド系ポリアミンの軟ィヒ点乃至融点相当温度以上、 たとえば 1 65〜 200 °Cの温度で 30〜150秒間加熱し、 次いでこのようにそれぞれ加 熱状態のポリオレフィン基材に表皮材を重ね合せ、 0. 1 kg/cm2以上の圧力下 で 10秒以上の加熱圧着を行い、 成形と接着を同時に行う。 このようにして、 耐 熱接着性に優れた自動車内装パネルが得られる。 しかも、 上記一液型熱架橋性接 着剤のプレコートを採用すれば、 この成形ラインでの、 溶剤揮散による環境汚染 の防止を図ることができる。
なお、 上記プレコートした場合の癒着の有無は、 プレコ一ト表皮材の 2枚を重 ね合せ、 60°C中 10〜 10 Og/cm2の圧締カを負荷することによって実験的 に評価することができる。 発明を実施するための最良の形態
次に実施例を挙げて、 本発明をより具体的に説明する。
実施例 1
(1) 一液型熱架橋性接着剤の調製
COO H変性 P Pとして軟化温度 100。(の無水マレイン酸変性体 （東洋化成
(株） 製 「MTPP」 ） 100部 （重量部、 以下同様） ； COOH変性 SEBS として軟化温度 80°Cのマレイン酸変性体 （旭化成工業 （株） 製 「M— 194 3」 ） 25部；粘着付与剤として 3本石油化学 （株） 製 「ネオポリマー 140」 100部； ドデカンジォヒドラジド （mpl 89〜： L 91°C) 2部を混合溶剤 （キ シレン/シクロへキサン = 1 ： 1) 5 00部に加え、 60°Cで撹拌分散せしめ、 これに安定剤 3 0部を加えて一液型熱架橋性接着剤を得る。 この接着剤の貯蔵後 の粘度変化は、 以下の通りである。
調製直後： 3 0 OmPa · s
40°CX 1 0日貯蔵後： 3 6 OmPa■ s
(2) 接着剤の乾燥条件による残存溶剤量の測定
アルミユウム板に接着剤を乾燥膜厚 60 μ mにて塗布し、 下記表 1に示す条件 (温度 X時間） で乾燥したときの残存溶剤量 （％) を測定し、 結果を表 1に併
ID? ¾0
¾k 1
Figure imgf000006_0001
(3) プレコート表皮材の作成と癒着†生評価
ポリプロピレン発泡体とポリオレフイン層を積層してなる表皮材のポリプロピ レン発泡体面に、 接着剤を乾燥膜厚 6 Ο μιηにて塗布し、 下記表 2に示す条件
(温度 X時 で乾燥せしめプレコート表皮材を得る。 かかる乾燥したプレコ ート表皮材を 2枚直ちに重ね合せ、 5 Og/cm2の荷重を掛け、 60°C雰囲気中 で 48時間放置後、 引張速度 1 O OmmZ分で剥離強度 （N/2 5cm2) を測定す る。 結果を表 2に併記する。
表 2
温度 (。c〉
80 100 120
時間 (秒)、
60 2. 3 1. 8 1. 5
90 2. 2 1. 4 1. 4
1 8 0 2. 0 1. 4 1. 4
240 2. 0 0. 8 0. 9
300 2. 0 0. 7 0. 8 (4) 接着試験評価
表皮材は、 上記 (3) において接着剤を塗布し、 80°CX 90秒で乾燥した プレコート表皮材であって、 その作成後 20°CX 1日、 40°CX 15日または 40°CX 30日保管したものをそれぞれ使用する。
厚み 2瞧のポリプロピレン基材に上記プレコート表皮材を重ね合せ、 50g/ cra2X 30秒の条件で圧締せしめ （195°C加熱炉中で 120秒間加熱して） 、 接着試験パネルを得る。 このパネルを下記項目の接着試験評価に供す。
接着試験評価 (剥離試験は、 引張速度 20 OmraZ分で、 180° 角剥離強度 を ί¾定する）
i ) 初期剥離 (初期力ットなし）
接着試験パネルを室温で、 剥離強度 （N/25瞧） の測定に付す。
ii) 耐熱クリープ性
接着試験パネルを 20°C， 65%RHX 24時間養生後に、 100 °C雰囲気 中 100 g荷重を加え、 24時間後の剥離長さ (mm) を測定する。
iii) 耐湿老化性
接着試験パネルを 20 °C, 65%RHX 24時間養生後に、 50 °C, 95 %
RHX 500時間放置後、 100°C雰囲気中で剥離強度 （NZ25mm) を測定 する。
iv) 耐熱老化性
接着試験パネルを 20°C, 65%RHX 24時間養生後に、 110 °C X 10
00時間放置後、 100°C雰囲気中で剥離強度 (N/25瞧） を測定する。 結果は、 以下の通りである。 表 3
Figure imgf000008_0001
表中、 FMB ：表皮材の材料破壌、 B A F：基材の材料破壌、 C F：接着剤層
産業上の利用の可能性
上記の実施例結果から、 本発明の製造法によって、 自動車内装耐久性に適合す る優れた耐久性を具備し、 かつオールポリオレフィン系材料で構成することで、 リサイクル可能な自動車内装パネルの製造実現が認められる。

Claims

請 求 の 範 囲
1 . ポリオレフイン基材にポリオレフイン積層体の表皮材を、 接着剤を用い加熱 下の真空成形法で接着することにより自動車内装パネルを製造する方法において、 上記接着剤として、
軟化温度 8 0〜1 4 0 °Cのカルボン酸もしくはその無水基を含有するポリオレ フィンと、 カルボン酸もしくはその無水基を含有する軟化温度 8 0 °C以上のス チレン一エチレン/プテン一スチレンコポリマーの混合物に、 潜在性硬化剤と して融点 1 8 0〜2 0 0。。のヒドラジド系ポリアミンを組合せ、 これらを有機 溶剤に分散せしめて成る—液型熱架橋性接着剤
を用い、 およぴ上記表皮材を接着剤中のヒドラジド系ポリアミンの軟化点乃至融 点以上の温度で加熱することを特徴とする自動車内装パネルの製造法。
2 . —液型熱架橋性接着剤を表皮材のポリオレフイン発泡体に塗布、 乾燥した後、 1 6 5〜 2 0 0。Cの温度で 3 0〜1 5 0秒間加熱する請求の範囲 1に記載の製造 法。
3 . 予め表皮材のポリオレフイン発泡体に一液型熱架橋性接着剤を塗布、 乾燥し てプレコ一トしておく請求の範囲 1または 2に記載の製造法。
4 . 乾燥条件として 8 0〜： L 2 0 °C X 3 0〜3 0 0秒を採用し、 接着剤層中の 残存溶剤量を 2重量％以下に調整する請求の範囲 3に記載の製造法。
5 . プレコートした表皮材が、 その 2枚を重ね合せ、 保存しても癒着することが ない請求の範囲 4に記載の製造法。
PCT/JP2003/002184 2003-02-27 2003-02-27 自動車内装パネルの製造法 WO2004076159A1 (ja)