WO2001066489A1 - Versatz zur herstellung eines feuerfesten keramischen formkörpers, daraus gebildeter formkörper und dessen verwendung - Google Patents
Versatz zur herstellung eines feuerfesten keramischen formkörpers, daraus gebildeter formkörper und dessen verwendung Download PDFInfo
- Publication number
- WO2001066489A1 WO2001066489A1 PCT/EP2001/002362 EP0102362W WO0166489A1 WO 2001066489 A1 WO2001066489 A1 WO 2001066489A1 EP 0102362 W EP0102362 W EP 0102362W WO 0166489 A1 WO0166489 A1 WO 0166489A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- component
- cao
- weight
- batch according
- mgo
- Prior art date
Abstract
Description
Claims