WO2001042253A2 - Phosphorus element-containing crosslinking agents and flame retardant phosphorus element-containing epoxy resin compositions prepared therewith - Google Patents
Phosphorus element-containing crosslinking agents and flame retardant phosphorus element-containing epoxy resin compositions prepared therewith Download PDFInfo
- Publication number
- WO2001042253A2 WO2001042253A2 PCT/US2000/033648 US0033648W WO0142253A2 WO 2001042253 A2 WO2001042253 A2 WO 2001042253A2 US 0033648 W US0033648 W US 0033648W WO 0142253 A2 WO0142253 A2 WO 0142253A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- composition
- epoxy resin
- phosphorus element
- formula
- crosslinking agent
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07F—ACYCLIC, CARBOCYCLIC OR HETEROCYCLIC COMPOUNDS CONTAINING ELEMENTS OTHER THAN CARBON, HYDROGEN, HALOGEN, OXYGEN, NITROGEN, SULFUR, SELENIUM OR TELLURIUM
- C07F9/00—Compounds containing elements of Groups 5 or 15 of the Periodic System
- C07F9/02—Phosphorus compounds
- C07F9/28—Phosphorus compounds with one or more P—C bonds
- C07F9/50—Organo-phosphines
- C07F9/53—Organo-phosphine oxides; Organo-phosphine thioxides
- C07F9/5325—Aromatic phosphine oxides or thioxides (P-C aromatic linkage)
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07F—ACYCLIC, CARBOCYCLIC OR HETEROCYCLIC COMPOUNDS CONTAINING ELEMENTS OTHER THAN CARBON, HYDROGEN, HALOGEN, OXYGEN, NITROGEN, SULFUR, SELENIUM OR TELLURIUM
- C07F9/00—Compounds containing elements of Groups 5 or 15 of the Periodic System
- C07F9/02—Phosphorus compounds
- C07F9/547—Heterocyclic compounds, e.g. containing phosphorus as a ring hetero atom
- C07F9/655—Heterocyclic compounds, e.g. containing phosphorus as a ring hetero atom having oxygen atoms, with or without sulfur, selenium, or tellurium atoms, as the only ring hetero atoms
- C07F9/65502—Heterocyclic compounds, e.g. containing phosphorus as a ring hetero atom having oxygen atoms, with or without sulfur, selenium, or tellurium atoms, as the only ring hetero atoms the oxygen atom being part of a three-membered ring
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G59/00—Polycondensates containing more than one epoxy group per molecule; Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups
- C08G59/18—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing
- C08G59/20—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing characterised by the epoxy compounds used
- C08G59/22—Di-epoxy compounds
- C08G59/30—Di-epoxy compounds containing atoms other than carbon, hydrogen, oxygen and nitrogen
- C08G59/304—Di-epoxy compounds containing atoms other than carbon, hydrogen, oxygen and nitrogen containing phosphorus
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G59/00—Polycondensates containing more than one epoxy group per molecule; Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups
- C08G59/18—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing
- C08G59/20—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing characterised by the epoxy compounds used
- C08G59/32—Epoxy compounds containing three or more epoxy groups
- C08G59/3254—Epoxy compounds containing three or more epoxy groups containing atoms other than carbon, hydrogen, oxygen or nitrogen
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G59/00—Polycondensates containing more than one epoxy group per molecule; Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups
- C08G59/18—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing
- C08G59/40—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing characterised by the curing agents used
- C08G59/4007—Curing agents not provided for by the groups C08G59/42 - C08G59/66
- C08G59/4071—Curing agents not provided for by the groups C08G59/42 - C08G59/66 phosphorus containing compounds
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K5/00—Use of organic ingredients
- C08K5/49—Phosphorus-containing compounds
- C08K5/51—Phosphorus bound to oxygen
- C08K5/52—Phosphorus bound to oxygen only
- C08K5/521—Esters of phosphoric acids, e.g. of H3PO4
- C08K5/523—Esters of phosphoric acids, e.g. of H3PO4 with hydroxyaryl compounds
-
- H—ELECTRICITY
- H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
- H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
- H05K1/00—Printed circuits
- H05K1/02—Details
- H05K1/03—Use of materials for the substrate
- H05K1/0313—Organic insulating material
- H05K1/032—Organic insulating material consisting of one material
- H05K1/0326—Organic insulating material consisting of one material containing O
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/31504—Composite [nonstructural laminate]
- Y10T428/31511—Of epoxy ether
Definitions
- This invention relates to new crosslinking agents for epoxy resin compositions, more particularly to phosphorus element-containing compounds useful as crosslinking agents for epoxy resin compositions to yield non-halogenated, ignition resistant phosphorus element-containing epoxy resin formulations.
- the new phosphorus element-containing crosslinking agents of the present invention are based on isomeric mixtures of tris(2-hydroxyphenyl)phosphine oxides having the following general chemical structure of Formula I:
- R may be independently a hydrogen or a C ⁇ -C 10 alkyl group such as methyl, ethyl, propyl, and butyl.
- the flame retardant epoxy resin formulations of this invention are advantageously used for making laminates for printed wiring boards and composite materials.
- an epoxy-containing formulation is applied to or impregnated into a substrate by rolling, dipping, spraying, other known techniques and/or combinations thereof.
- the substrate is typically a woven or nonwoven fiber mat containing, for instance, glass fibers or paper.
- the impregnated substrate is "B-staged” by heating at a temperature sufficient to draw off solvent in the epoxy formulation and optionally to partially cure the epoxy formulation, so that the impregnated substrate can be handled easily.
- the "B-staging” step is usually carried out at a temperature of from 90°C to 210°C and for a time of from 1 minute to 15 minutes.
- the impregnated substrate that results from B-staging is called a "prepreg".
- the temperature is most commonly 100°C for composites and 130°C to 200°C for electrical laminates.
- One or more sheets of prepreg are stacked or laid up in alternating layers with one or more sheets of a conductive material, such as copper foil, if an electrical laminate is desired.
- a conductive material such as copper foil
- the laid-up sheets are pressed at high temperature and pressure for a time sufficient to cure the resin and form a laminate.
- the temperature of this lamination step is usually between 100°C and 230°C, and is most often between 165°C and 190°C.
- the lamination step may also be carried out in two or more stages, such as a first stage between 100°C and 150°C and a second stage at between 165°C and 190°C.
- the pressure is usually between 50 N/cm " and 500 N/cm .
- the lamination step is usually carried out for a time of from 1 to 200 minutes, and most often for 45 to 90 minutes.
- the lamination step may optionally be carried out at higher temperatures for shorter times (such as in continuous lamination processes) or for longer times at lower temperatures (such as in low energy press processes).
- the resulting laminate for example a copper-clad laminate, may be post-treated by heating for a time at high temperature and ambient pressure.
- the temperature of post-treatment is usually between 120°C and 250°C.
- the post-treatment time usually is between 30 minutes and 12 hours. It is conventional in the preparation of epoxy-containing laminates to incorporate into the epoxy resin composition various additives to improve the flame - retardancy of the resulting laminate.
- halogen- containing additives such as tetrabromo-diphenylolpropane, or epoxy resins prepared by reacting diglycidyl ether of bisphenol-A with tetrabromodiphenylolpropane.
- V-0 in the standard "Underwriters Laboratory” test method UL 94
- levels of such bromine-containing flame retardant additives are required which provide a bromine content of from 10 weight percent to 25 weight percent based on the total polymer weight in the product.
- halogen-containing fire-retardant additives such as tetrabromodiphenylolpropane are effective, they are considered by some to be undesirable from an environmental standpoint, and in recent years there has been increasing interest in the formulation of halogen-free epoxy resins, which are able to meet the fire retardancy requirements.
- Proposals have been made to use phosphorus-based flame retardants instead of halogenated fire retardants in epoxy resin formulations as described in. for example, EP A 0384939, EP A 0384940, EP A 0408990, DE A 4308184, DE A 4308185, DE A 4308187, WO A 96/07685, and WO A 96/07686.
- a phosphorus flame retardant is pre-reacted with an epoxy resin to form a di- or multifunctional epoxy resin which is then cured with an amino cross-linker such as dicyandiamide, sulfanilamide, or some other nitrogen element-containing cross-linker to form the network.
- phosphorus-based fire retardant additives which may be useful for replacing halogen-containing fire-retardant additives.
- AmgardTM V19 and AntiblazeTM 1045 are commercially available phosphonic acid ester fire retardant materials. These phosphonic acid esters, may be solids or liquids. Alkyl and aryl substituted phosphonic acid esters are compatible with epoxy resins. In particular lower (that is, C]-C 4 ) alkyl esters of phosphonic acid are of value because they contain a high proportion of phosphorus, and are thus able to impart good fire retardant properties upon resins in which they are incorporated.
- the phosphonic acid esters are not satisfactory as a substitute for halogenated flame retardants in epoxy resins for the production of electrical laminates, because the use of phosphonic acid esters in amounts sufficient to provide the necessary flame retardancy increases the tendency of the resulting cured epoxy resin to absorb moisture.
- the moisture absorbency of the cured laminate board is very significant, because laminates containing high levels of moisture tend to blister and fail, when introduced to a bath of liquid solder at temperatures around 260°C. a typical step in the manufacture of printed wiring boards.
- EP A 0754728 describes the production of a flame retardant epoxy resin system by blending an epoxy resin with a cyclic phosphonate as a flame retardant and incorporating the cyclic phosphonate into the cured resin.
- the epoxide resin and phosphonate mixture is crosslinked with a polyamine such as triethylamine, tetra amine.
- polyamido amines, multi basic acids or their anhydrides for example phthalic anhydride or hexahydrophthalic anhydride.
- EP A 0,754,728 indicates that large quantities, such as in excess of 18 weight percent, of the phosphorus additive are needed in order for the resin system to meet UL 94 V-0.
- WO 99/00451 discloses flame retardant epoxy resin compositions utilizing phosphonic acid esters.
- WO 99/00451 discloses the reaction of a phosphonic acid ester with an epoxy resin in the presence of a catalyst and a nitrogen-containing crosslinking agent.
- the crosslinking agent has an amine functionality of at least 2 and is preferably dicyandiamide.
- the epoxy resins described in WO 99/00451 have improved flame retardant properties at low levels of phosphonic acid ester flame retardant.
- Tg and flame retardant properties there is still a need in the industry for a flame retardant epoxy resin with improved Tg and flame retardant properties.
- halogen-containing phenol compounds such as tetrabromobisphenol-A (TBBA) are well known materials used in epoxy resins, specifically for use in the manufacture of FR-4 laminates for printed circuit boards.
- Halogen-containing compounds, specifically bromine-containing materials have the disadvantages of corrosive acidic components, for example HBr, released at high temperatures. It would be desirous to provide a non-halogenated material as a fire retardant additive to replace halogen-containing phenol compounds such as TBBA.
- Ar is an phenyl ring and the X moieties have an active hydrogen and include an amine, hydroxy, carboxy. anhydride and thiol moieties.
- JP 61,134,395 [86,134,395] teaches the use of tris(3- hydroxyphenyl)phosphine oxide having the following chemical structural formula: as a crosslinking agent for epoxy resins.
- the prior art describes the use of phosphates [OP(OR) 3 ] and other compounds with P-O-C units in epoxy resin formulations. Such resins do not provide a satisfactory resistance to water uptake. It would be desirous to provide compounds such as triarylphosphine oxides which do not contain P-O-C bonds, and therefore, do not suffer the disadvantages of the prior art compounds having P-O-C units. It would be desirous to provide phosphorus compounds with P-C linkages having superior resistance to water uptake when compared to phosphorus compounds with P-O-C units.
- Phosphorus-containing compounds have been used heretofore in a variety of epoxy-based polymer systems including for example FR-4 laminates for printed circuit boards, container coatings, as well as high-molecular weight epoxy-based thermoplastics.
- a driving force for this work has been the search for non-halogenated alternatives to brominated epoxy resins.
- brominated flame retardants have been deemed environmentally unsound and the use of brominated flame retardants in flame retardant epoxy resins applications has been continually threatened by legislation. Thus, there is a need to address this issue.
- non-brominated flame retardants have been used as replacements for tetrabromobisphenol-A (TBBA) in FR-4 laminates for printed circuit boards. Although most of these materials are found to meet the requirements for ignition and heat resistance, excessive moisture uptake in the board is found to be the main problem with their use. The presence of excess moisture cause the laminate boards to fail blister resistance testing. Phosphorus-containing species (phosphates, phosphonates. and phosphoramides) that contained P-O and P-N bonds, are believed to be the cause of excessive moisture uptake due to their polarity. Thus, it is desired to provide materials that contain P-C bonds instead of P-O or P-N bonds in FR-4 laminate applications. It would be advantageous if such materials would reduce the amount of water absorbed by the finished laminate board. It is desired to provide compounds, which improve resistance to moisture uptake in the laminate boards, while maintaining the requirements of excellent Tg and ignition resistance.
- TBBA tetrabromobisphenol-A
- the present invention is directed to epoxy resins which meet the desirable standards of fire retardancy without the need for halogen-containing flame retardants, or at least employing significantly lower levels of such halogen-containing flame retardants than is conventional in the art.
- One aspect of the present invention is directed to new phosphorus element- containing crosslinking agents for epoxy resin compositions, more particularly crosslinking agents based on an isomeric mixture of two or more isomers of tris(2- hydroxyphenyl)phosphine oxides having the general chemical structure of Formula I as follows:
- R is independently a hydrogen or a Ci-Cio alkyl group such as methyl, ethyl, propyl, and butyl.
- Another aspect of the present invention is directed to curable epoxy resin compositions containing a curable epoxy resin and, as a phosphorus element-containing crosslinking agent, an effective curing amount of a tris(2-hydroxyphenyl)phosphine oxide having the general chemical structure of Formula I as follows:
- R is independently a hydrogen or a Cl -CIO alkyl group such as methyl, ethyl, propyl, and butyl.
- Yet another aspect of the present invention is directed to preparing a non- halogenated, ignition resistant epoxy resin formulation useful for making laminates for printed wiring boards and composite materials using the above phosphorus element - containing crosslinking agent of Formula I.
- Hydroxyphenylphosphine oxides such as those having the above general Formula I, which contain less hydrophilic phosphorus-phenyl units, are advantageously used for the synthesis of epoxy-based thermosets.
- Compounds of Formula I can be incorporated into epoxy-based polymers via covalent linkages. Improvements in glass transition temperatures and ignition resistance are realized when the resultant phosphorus-containing polymers are compared to conventional bisphenol-A based epoxy thermoplastics.
- the phenol-functionalized phosphine oxide species of the present invention may be useful as replacements for tetrabromobisphenol-A in FR-4 laminates applications.
- Still another aspect of the present invention is directed to a compound which includes the glycidyl ether derivatives of Formula I, shown as the following chemical structural Formula V: Formula V
- Yet another aspect of the present invention is directed to epoxy vinyl ester resins produced by reacting the compound of Formula V above with carboxylic acids which contain an unsaturated functionality to produce the compounds as shown in the following chemical structure of Formula VIII:
- R 1 is a moiety containing an unsaturated functionality such as a moiety having the following formula:
- R" is a hydrogen or an alkyl group from C ⁇ -C 2 o and R'" may be a hydrogen, an alkyl group from C 1 -C20, or a carboxylic acid group or ester derivatives thereof.
- R' may be a methacrylate, acrylate. maleate, fumarate.
- the present invention is directed to a new phosphorus element-containing crosslinking agent advantageously used in epoxy-based formulations for preparing a flame retardant epoxy resin composition substantially free of halogen.
- the cross linkers of the present invention are preferably used as curing agents for epoxy formulations used in FR-4 laminates for printed circuit boards.
- the flame retardant composition includes (I) a non-halogenated epoxy resin material and (II) a phosphorus element-containing crosslinking agent.
- a resin which is "substantially free of halogen” means that the resin is completely free of halogen, that is 0 percent halogen, or that the resin contains some minor amount of halogen that does not affect the properties or performance of the resin, and is not detrimental to the resin.
- resins which have not been halogenated with a halogen- containing compound are "substantially free of halogen”.
- substantially free of halogen generally means that the resin contains less than 10 weight percent, preferably less than 5 weight percent, more preferably less than 1 weight percent, even more preferably less than 0.5 weight percent and most preferably zero weight percent of a halogen in the resin composition.
- the amount of the phosphorus element in the epoxy resin composition is from 0.2 weight percent to 5 weight percent, preferably from 0.5 weight percent to 3.5 weight percent, even more preferably from 1 weight percent to 3 weight percent, and most preferably from 1.5 weight percent to 2.8 weight percent, based on the total of the solid resin composition.
- the phosphorus element-containing crosslinking agent (II) of the present invention is preferably one or more compounds, or an isomeric mixture of two or more isomer compounds, having the following general chemical structural Formula I:
- R is independently a hydrogen or a Ci-Cio alkyl group including for example, methyl, ethyl, propyl, and butyl.
- crosslinkers (II) of the present invention may include those having the following chemical structural Formulas II-IV:
- the compounds of Formulas III and IV above are specific compounds wherein a CH 3 group is in the 5 position of the phenyl ring as shown in Formula III or wherein a hydrogen is in the 3, 4. 5. and 6 positions of the phenyl ring as shown in Formula IV; and such compounds are described in Synthetic Communications, 1987, 17(4), 465-468.
- the compounds of Formulas III and IV have not been used as crosslinkers for epoxy resins, particularly for making flame retardant compositions.
- the crosslinkers of the above Formula II are preferably used in the present invention.
- Formula II represents an isomeric mixture of two or more different triaryl phosphine oxide isomer compounds wherein the R group is a methyl and the methyl can be in the 3, 4, 5 or 6 position in each of the phenyl rings.
- the isomeric mixture of Formula II is new.
- a more preferred embodiment of the isomeric mixture of Formula II used in the present invention is when the mixture contains at least one of the isomers having at least one 2-hydroxy-4-methyl phenyl moiety and/or at least one of the isomers having at least one 2- hydroxy-5-methylphenyl moiety.
- the ratio of 2-hydroxy-4-methylphenyl moiety to the 2-hydroxy-5-methyl phenyl moiety is generally dependent on the moiety ratios of the starting precursor; and the ratio can range from 99: 1 to 1:99 and preferably, the ratio is from 70:30 to 30:70
- the cross-linker (II) of the present invention is preferably used in the epoxy resin composition in an amount of from 50 percent to 150 percent of the stoichiometric amount needed to cure the epoxy resin and more preferably from 75 percent to 125 percent of the stoichiometric amount needed to cure the epoxy resin, even more preferably from 85 percent to 110 percent of the stoichiometric amount needed to cure the epoxy resin.
- Formulations that use the crosslinking agent of Formula II yield laminates with excellent glass transition temperatures (Tg) of from 50 °C to 180°C and an ignition resistance of V-0/V- 1.
- Formulations made using the crosslinker of Formula II yield laminates have a Tg of preferably greater than 120°C, more preferably greater than 135°C, and most preferably greater than 150°C.
- the crosslinker of Formula II also provides good resistance to water uptake for a phosphorus-containing additive/comonomer, with a moisture pickup of preferably less than 1 percent, more preferably less than 0.5 percent, and most preferably less than 0.3 percent after 40 minutes exposure time in a steam autoclave (known in the industry as the "pressure cooker test").
- a steam autoclave known in the industry as the "pressure cooker test”
- the compounds of Formulas I-IV may be prepared by a method described in Synthetic Communications, 1987, 17(4), pp. 465-468.
- the method of preparation of the compounds of the present invention involves the reaction of a corresponding precursor such as a triarylphosphate, with lithium diisopropyl amide in tetrahydrofuran (THF) solvent at -78 °C.
- a corresponding precursor such as a triarylphosphate
- lithium diisopropyl amide in tetrahydrofuran (THF) solvent at -78 °C.
- THF tetrahydrofuran
- triarylphosphate precursors such as tris(p,m- cresyl)phosphate and triphenylphosphate can be used as starting materials to prepare, on an industrial scale, the compounds of Formula II and Formula IV, respectively.
- the crosslinker of Formula II is preferably soluble in aprotic and/or protic solvents commonly used for making epoxy resin formulations, particularly for use in laminate applications.
- the solvents include for example acetone, methylethyl ketone, methanol, ethanol, Dowanol PM*, N-methylpyrrolidone, dimethylforamide.
- the solubility of the crosslinker is preferably greater than 30 percent solids content, more preferably greater than 40 percent solids contents and most preferably greater than 50 percent solids contents.
- the compounds of Formulas III and IV are high melting crystalline solids which are useful as crosslinking agents in other applications such as coatings, adhesives and composites.
- An additional embodiment of the present invention is a compound which includes the glycidyl ether derivatives of Formula I, shown as the following chemical structural Formula V: Formula V
- the compounds of Formula V can be produced by epoxidizing the compounds of Formula I using well known techniques in the art such as reacting the compounds of Formula I with an epihalohydrin such as epichlorohydrin to prepare the epoxy resin.
- an epihalohydrin such as epichlorohydrin
- the resulting epoxy resin of Formula V can be advantageously used per se as an epoxy resin base material, such as those described herein as the non-halogenated epoxy resin materials of component (I), for making a flame retardant composition which is curable with any curing agent.
- the curing agent used can also be the phosphorus element-containing crosslinking agent (II) disclosed herein as Formula I.
- the compound of Formula V may also be used in combination with other phosphorus element-containing compounds.
- the combination of the compounds of Formula V and Formula I produce curable compositions which can be used in applications such as flame retardant coatings, laminates, composites and adhesives. More beneficially, the compounds of Formula V can be used in laminate applications to produce laminates which have a reduced water up-take because of the P-C bonds as opposed to those compounds having a P-O-C bonds.
- the previously described epoxy resin compound of Formula V can be further reacted with a carboxylic acid material which contains an unsaturated functionality to make a vinyl ester resin as shown in the following chemical structure of Formula VIII:
- R 1 is a moiety containing an unsaturated functionality such as a moiety having the following formula:
- R" is a hydrogen or an alkyl group from C ⁇ -C 20 and R'" may be a hydrogen, an alkyl group from C1-C20, or a carboxylic acid group or ester derivatives thereof.
- R' may be a methacrylate, acrylate, maleate, fumarate.
- the epoxy vinyl ester resins of Formula VIII is produced by reacting a carboxylic acid material having an unsaturated functionality such as acrylic acid, methacrylic acid, maleic acid, fumaric acid.
- the amount of carboxylic acid material used is sufficient to completely react the acid functionality with all of the epoxy groups, that is, stoichiometric amounts using techniques well known in the art.
- the epoxy vinyl ester resins may also be used with commonly reactive diluents such as styrene, divinyl benzene, and p-methyl styrene and other reactive diluents known in the art.
- the diluents are used for ease of fabricating, for example, composites; and for improving the properties of the final composites produced.
- the compounds of Formula VIII are advantageously used to produce compositions which can be used in applications such as flame retardant coatings, laminates, composites and adhesives.
- the crosslinking agent (also referred to as a "hardener” or “curing agent” herein) of the present invention may be used alone, or in combination with one or more second different crosslinking agents, that is, a co-crosslinking agent (VII).
- the co-crosslinking agent used in the present invention may be selected from a multifunctional phenolic crosslinker, a nitrogen-containing crosslinker, styrenic maleic anhydride (SMA) or other phosphorus element-containing compounds.
- the composition of the present invention may include, as an additional crosslinking agent or co-crosslinker (VII), a multi-functional phenolic cross-linker which contains at least two or more functionalities.
- additional crosslinking agent or co-crosslinker VII
- a multi-functional phenolic cross-linker which contains at least two or more functionalities.
- the multi-functional phenolic cross-links are preferably novolacs or cresol novolacs obtained by the condensation of phenols, cresols, xylenols or other alkyl phenols with formaldehyde.
- the resoles may also be used as the multi-functional phenolic cross-linker.
- the cross-linker has the following chemical structural Formula VI:
- R is hydrogen or a C1-C 3 alkyl, for example, methyl and "n” is 0 or an integer from 1 to 10. "n” preferably has an average value of from 0 to 5.
- the composition of the present invention may include as an additional crosslinking agent, a nitrogen-containing cross-linker (VII). used as a subsidiary cross-linker in addition to the phosphorus element-containing cross-linker (II). and with or without the multi-functional phenolic cross-linker.
- the nitrogen-containing co- crosslinking agent preferably has an amine functionality of at least 2. Suitable multi- functional cross-linkers are described in numerous references such as Vol. 6 Encyclopedia of Poly. Sci. & Eng., "Epoxy resins" at 348-56 (J. Wiley & Sons 1986).
- suitable nitrogen-containing co-crosslinkers useful in the present invention may be found in WO 99/00451 ; and include for example, include polyamines, polyamides, sulpfhanilamide, diaminodiphenylsulfone and diaminodiphenyl methane and dicyandiamide, substituted dicyandiamide, 2,4-diamino-6-phenyl-l ,3,5-triazin.
- the preferred nitrogen-containing co-crosslinkers are dicyandiamide, sulfainilamide and, 2, 4-diamino-6-phenyl-l , 3, 5-triazine, more preferable sulfanilamide issued.
- co-crosslinkers (VII) useful in the present invention are described in U.S. Patent Application Serial No.
- the co-crosslikers are present in an amount to cross-link less than 40 percent of stoichiometric amount needed to cure the epoxy resin.
- the amount of the co-crosslinking agent in the epoxy resin is from 0 to 40 percent of the stoichiometric quantity needed to cure the epoxy content of the epoxy resin in the formulation.
- the non-halogenated epoxy resin material (I) of the present invention may be selected from: (A) a non-halogenated epoxy resin; (B) a non-halogenated, phosphorus element-containing epoxy resin; (C) a mixture of:(l) a non-halogenated, non-phosphorus element-containing epoxy resin, and (2) a phosphorus element-containing compound; (D) the reaction product of: (1) a non-halogenated epoxy resin; and (2) a phosphorus element- containing compound; or (E) a combination of two or more of components (A) to (D).
- the non-halogenated epoxy resin material (I) used in the present invention is a material which possesses on average more than 1 and preferably at least 1.8, more preferably at least 2 epoxy groups per molecule.
- the epoxy resin material may be any saturated or unsaturated aliphatic, cycloaliphatic, aromatic or heterocyclic compound which possesses more than one 1 ,2-epoxy group.
- the non-halogenated epoxy resins (A) useful in the present invention include polyepoxides.
- the polyepoxide compound useful in the present invention is suitably a compound which possesses an average of from 1.9 to 2.1 1,2-epoxy groups per molecule.
- the polyepoxide compound is saturated or unsaturated aliphatic, cycloaliphatic, aromatic or heterocyclic compound which possesses more than one 1,2-epoxy group.
- the polyepoxide compound can be substituted with one or more substituents which are non reactive with the isocyanate groups such as lower alkyls and halogens.
- Such polyepoxide compounds are well known in the art.
- polyepoxide compounds useful in the practice of the present invention are described in the Handbook of Epoxy Resins by H.E. Lee and K. Neville published in 1967 by McGraw Hill, New York and U.S. Patent No. 4,066,628.
- suitable aromatic polyepoxides are bisphenol-A, bisphenol-F, bisphenol-AD.
- bisphenol-S tetramethyl bisphenol-A, tetramethyl bisphenol-F, tetramethyl bisphenol-AD, tetramethyl bisphenol-S, tetrabromobisphenol-A, tetrachlorobisphenol-A, biphenols such as 4,4'-biphenol or 3,3',5,5'-tetramethyl-4,4'-biphenol, and dihydroxynaphthalene.
- Suitable aliphatic polyepoxides are diglycidyl esters of hexahydrophthalic acid and diglycidyl esters of dicarboxylic acids, epoxidized polybutadiene, epoxidized soyabean oil, and epoxidized diols.
- Cycloaliphatic epoxides include, for example, 3,4-epoxy-6-methylcyclohexyl carboxylate and 3,4-epoxycyclohexyl carboxylate.
- heterocyclic epoxy compounds are diglycidylhydantoin or triglycidyl isocyanurate (TGIC).
- Preferred polyepoxides are glycidyl compounds of bisphenol-A, of bisphenol- F, of tetrabromobisphenol-A and of 3,3',5,5'-tetramethyl-4,4-biphenol. Mixtures of any two or more polyepoxides can also be used in the practice of the present invention
- DHQEP as an effective flame retardant and thermal stabilizer for epoxy resins is described in Cho, Ching-sheng/Chen, Leo-wang/Chiu. Yie-shun; Polymer Bulletin 41, 45-52 (1998),
- the epoxy resin material (I) used in the present invention may (C) a mixture of (1) an epoxy compound containing at least two epoxy groups, and (2) a phosphorus-containing compound. It is possible to add the phosphorus- containing compound (C) and the epoxy resin compound (C) to the overall composition of the present invention in order to form the epoxy resin material (I) in-situ.
- the epoxy resin material (I) which is added to the overall composition of the present invention may be (D) the reaction product of (1) an epoxy resin and (2) a phosphorus-containing Dl compound capable of reacting with the epoxy resin.
- the aforementioned epoxy resin (Cl) or (Dl) is preferably one which has no lower alkyl aliphatic substituents.
- epoxy resins (Cl) or (Dl) are epoxy novolac resins (sometimes referred to as epoxidised novolac resins, a term which is intended to embrace both epoxy phenol novolac resins and epoxy cresol novolac resins).
- epoxy novolac resins sometimes referred to as epoxidised novolac resins, a term which is intended to embrace both epoxy phenol novolac resins and epoxy cresol novolac resins.
- Such epoxy compounds have the following general chemical structural Formula VII:
- R is hydrogen or a C ⁇ -C 3 alkyl, for example, methyl and "n” is 0 or an integer from 1 to 10. "n” preferably has an average value of from 0 to 5.
- Epoxy novolac resins are readily commercially available, for example under the trade names D.E.N.TM (Trademark of The Dow Chemical Company), QuatrexTM, TactixTM.
- the materials of commerce generally comprise mixtures of various species of the above formula and a convenient way of characterizing such mixtures is by reference to the average, n * . of the values of n for the various species.
- Preferred epoxy novolac resins for use in accordance with the present invention are those in which n' has a value of from 2.05 to 10. more preferably from 2.5 to 5.
- the phosphorus-containing compound or monomer (C2) or (D2) contains some reactive groups such as a phenolic group, an acid group, an amino group, an acid anhydride group, or a phosphinate group (P-H) which can react with the epoxy groups of the epoxy resin compound (Cl) or (Dl).
- the phosphorus- containing monomer (C2) or (D2) used in the present invention is for example, 9,10-dihydro- 9-oxa-10-phosphaphenanthrene-10-oxide such as "Sanko-HCA” commercially available from SANKO of Japan or "Struktol Polydis PD 3710" commercially available from Schill- Seilacher of Germany; 10-(2',5'-dihydroxyphenyl)-9.10-dihydro-9-oxa-10- phosphaphenanthrene-10-oxide (HCA-HQ); bis(4-hydroxyphenyl)phosphine oxide; tris(2- hydro xyphenyl)phosphine oxide; dimethyl- 1 -bis(4-hydroxyphenyl)- 1 -phenylmethylphonate; an isomeric mixture of tris(2-hydroxymethylphenyl)phosphine oxides; or tris(2-hydroxy-5- methylphenyl) phos
- the phosphorus-containing compound (C2) or (D2) of the present invention may contain on average one or more than one functionality capable of reacting with the epoxy groups.
- Such phosphorus-containing compound preferably contains on average 0.9 to 3 functional groups capable of reacting with epoxy resin.
- compositions of the present invention preferably contain a catalyst (III) capable of promoting the reaction of the cross-linker of the present invention, and/or the phosphorus-containing compounds with the epoxy resin and promoting the curing of the epoxy resin.
- a catalyst (III) capable of promoting the reaction of the cross-linker of the present invention, and/or the phosphorus-containing compounds with the epoxy resin and promoting the curing of the epoxy resin.
- Suitable catalyst materials useful in the present invention include for example compounds containing or amine, phosphine. ammonium, phosphonium, arsonium or sulfonium moieties. Particularly preferred catalysts are heterocyclic nitrogen- containing compounds.
- the catalysts (III) (as distinguished from cross-linkers) preferably contain on average no more than 1 active hydrogen moiety per molecule. Active hydrogen moieties include hydrogen atoms bonded to an amine group, a phenolic hydro xyl group, or a carboxylic acid group.
- the amine and phosphine moieties in catalysts are preferably tertiary amine or phosphine moieties; and the ammonium and phosphonium moieties are preferably quaternary ammonium and phosphonium moieties.
- preferred tertiary amines that may be used as catalysts are those mono- or polyamines having an open-chain or cyclic structure which have all of the amine hydrogen replaced by suitable substituents, such as hydrocarbyl radicals, and preferably aliphatic, cycloaliphatic or aromatic radicals.
- amines examples include, among others, 1 ,8- diazabicyclo (5.4.0)undec-7-en (DBU), methyl diethanol amine, triethylamine, tributylamine, dimethyl benzylamine, triphenylamine, tricyclohexyl amine, pyridine and quinoline.
- DBU 1 ,8- diazabicyclo (5.4.0)undec-7-en
- methyl diethanol amine triethylamine, tributylamine, dimethyl benzylamine, triphenylamine, tricyclohexyl amine, pyridine and quinoline.
- Preferred amines are the trialkyl, tricycloalkyl and triaryl amines, such as triethylamine, triphenylamine, tri-(2,3-dimethylcyclohexyl)amine, and the alkyl dialkanol amines, such as methyl diethanol amines and the trialkanolamines
- tertiary amines for example, amines that in aqueous solutions give a pH less than 10 in aqueous solutions of 1 M concentration, are particularly preferred.
- Especially preferred tertiary amine catalysts are benzyldimethylamine and tris-(dimethylaminomethyl) phenol.
- suitable heterocyclic nitrogen-containing catalysts (III) include those described in U.S. Patent No. 4,925,901.
- heterocyclic secondary and tertiary amines or nitrogen-containing catalysts which can be employed herein include, for example, imidazoles, benzimidazoles, imidazolidines, imidazolines, oxazoles, pyrroles, thiazoles, pyridines, pyrazines, morpholines, pyridazines, pyrimidines, pyrrolidines, pyrazoles, quinoxalines, quinazolines, phthalozines, quinolines, purines, indazoles, indoles, indolazines, phenazines, phenarsazines, phenothiazines, pyrrolines, indolines, piperidines, piperazines and combinations thereof.
- alkyl-substituted imidazoles Especially preferred are the alkyl-substituted imidazoles; 2.5-chloro- 4-ethyl imidazole; and phenyl- substituted imidazoles, and mixtures thereof. Even more preferred are N-methylimidazole; 2-methylimidazole; 2-ethyl-4-methylimidazole; 1,2- dimethylimidazole; and 2-methylimidazole. Especially preferred is 2-phenylimidazole.
- a Lewis acid (IV) is also employed in the composition of the present invention, especially when the catalyst (III) is, particularly a heterocyclic nitrogen- containing compound.
- heterocyclic nitrogen-containing catalysts(III) which are preferably used in combination with Lewis acids (IV) are those described in EP-A-526488, EP A 0458502 & GB A 9421405.3.
- suitable Lewis acids useful in the present invention include halides, oxides, hydroxides and alkoxides of zinc, tin, titanium, cobalt, manganese, iron, silicon, aluminium, and boron, for example Lewis acids of boron, and anhydrides of Lewis acids of boron, for example boric acid, metaboric acid, optionally substituted boroxines (such as trimethoxyboroxine), optionally substituted oxides of boron, alkyl borates, boron halides, zinc halides (such as zinc chloride) and other Lewis acids that tend to have a relatively weak conjugate base.
- the Lewis acid is a Lewis acid of boron, or an anhydride of a Lewis acid of boron, for example boric acid, metaboric acid, an optionally substituted boroxine (such as trimethoxy boroxine, trimethyl boroxine or triethyl boroxine), an optionally substituted oxide of boron, or an alkyl borate.
- the most preferred Lewis acid is boric acid.
- the amount of the Lewis acid employed is preferably at least 0.1 moles of Lewis acid per mole of heterocyclic nitrogen compound, more preferably at least 0.3 moles of Lewis acid per mole of heterocyclic nitrogen-containing compound.
- the formulation preferably contains no more than 3 moles of Lewis acid per mole of catalyst and more preferably contains no more that 2 moles of Lewis acid per mole of catalyst.
- the total amount of the catalyst is from 0.1 weight percent to 3 weight percent, based on the total weight of the composition, preferably from 0.1 weight percent to 2 percent.
- compositions of the present invention may also optionally contain one or more additional flame retardant additives (V), including for example, red phosphorous or liquid or solid phosphorus-containing compounds, for example, ammonium polyphosphate, a phosphite, or phosphazenes, nitrogen-containing fire retardants and/or synergists, for example melamines, urea, cynamide, guanidine, cyanuric acid, isocyanuric acid and derivatives of those nitrogen-containing compounds, halogenated flame retardants, halogenated epoxy resins (especially brominated epoxy resins) synergistic phosphorus- halogen containing chemicals or compounds containing salts of organic acids, inorganic metal hydrates, boron or antimony.
- additional flame retardant additives are given in a paper presented at "Flame retardants - 101 Basic Dynamics - Past efforts create future opportunities", Fire Retardants Chemicals Association, Baltimore Marriot inner harbour hotel, Baltimore Maryland, March 24-27 1996.
- the phosphorus element-containing fire retardants are generally present in amounts such that the total phosphorous content of the epoxy resin composition is from 0 2 weight percent to 5 weight percent
- non-epoxy, phosphorus additives which can be used in the present invention may include for example phosphorus-guanamine having the following chemical structure
- R ⁇ -R 8 may be the same or different and represent H, CH , C2H5
- the phosphorus-quanarmne above is found to be a highly suitable alternative to brominated epoxy resins for printed circuit board (PCB) applications as described in Buser, Antonius Johannes Wilhelmus / Schutyser, Jan Andre Jozef, Akzo Nobel N V European Pat 0825217 Al (25 02 1998) and Buser, Antonius Johannes Wilhelmus / Schutyser, Jan Andre Jozef, Akzo Nobel N V European Pat WO 98/07731 (26 02 98)
- Another phosphorus additive useful in the present invention is "Antiblaze #1045" available from Albright and Wilson Antiblaze #1045 is a cyclic phosphonate dimei containing 20 8 percent phosphorous and has the following structure
- amino t ⁇ azine phosphates are also phosphorus additives which may be used in the present invention where Ri, R 2 and R 3 is independently H or a C ⁇ -C 40 alkyl group such as methyl.
- the composition of the present invention may also include other inorganic fillers (VI), for example fillers such as aluminum trihydroxide, for example "Martinal OL- 104" from Martinswerke GmbH; magnesium hydroxide, for example "Zerogen 30" available from Martinswerke GmbH; and ammonium polyphosphate, for example "Exolit 700" available from Clariant GmbH.
- VI inorganic fillers
- fillers such as aluminum trihydroxide, for example "Martinal OL- 104" from Martinswerke GmbH; magnesium hydroxide, for example "Zerogen 30" available from Martinswerke GmbH; and ammonium polyphosphate, for example "Exolit 700" available from Clariant GmbH.
- the aforementioned inorganic fillers can be added to the composition of the present invention to improve the flame retardant properties of the composition.
- Solvents (VIII) may also optionally be used in the composition of the present invention.
- a solvent it may include for example, propylene glycolmethylether (Dowanol PMTM), methoxypropylacetate (Dowanol PMATM), methylethylketone (MEK), acetone, methanol, and combinations thereof.
- the amount of solvent present in the epoxy resin composition of the present invention is generally form 0 weight percent to 50 weight percent; preferably from 10 weight percent to 40 weight percent and more preferably from 10 weight percent to 35 weight percent, depending on the end use application of the epoxy resin composition.
- halogenated epoxy resin IX, provided the halogenated epoxy resin is added in an amount such that the halogen content of the overall epoxy resin composition of the present invention is less than 10 weight percent.
- compositions of the present invention can be produced by mixing all the components together in any order.
- the compositions of the present invention can be produced by preparing a first composition comprising the epoxy resin, and the second composition comprising the crosslinking agent.
- Either the first or the second composition may also comprise a phosphorus-containing compound a curing catalysts a multi-functional phenolic co-crosslinking agent and/or a nitrogen-containing co-crosslinking agents. All other components may be present in the same composition, or some may be present in the first, and some in the second.
- the first composition is then mixed with the second composition, and cured to produce a fire retardant epoxy resin.
- compositions of the present invention can be used to make composite materials by techniques well known in the industry much as by pultrusion, moulding, encapsulation, or coating.
- the present invention is particularly useful for making B-staged prepregs and laminates by well known techniques in the industry.
- Example 1 A number of preferred embodiments of the present invention are illustrated, in the following specific Examples. Example 1
- Formula II Product from the above synthesis (known as Formula II) were used to prepare two solutions. Firstly, Formula II was dissolved into methyl ethyl ketone (MEK) to produce a solution at 45 percent solids content. Secondly, Formula II was dissolved into dimethyl foramide (DMF) to produce a solution at 50 percent solids content.
- MEK methyl ethyl ketone
- DMF dimethyl foramide
- the Formula II solutions where then mixed with two types of epoxy resins and quantities of boric acid solution and 2-methyl imidazole (2-MI) solution in the portions indicated below to produce varnishes shown as Examples 2, 3 and 4:
- the IPC test methods employed in the Examples herein are the electrical laminate industry standard (The Institute For Interconnection And Packaging Electronic Circuits, 3451 Church Street, Evanston, Illinois 60203), as follows:
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
AU20897/01A AU2089701A (en) | 1999-12-13 | 2000-12-11 | Phosphorus element-containing crosslinking agents and flame retardant phosphoruselement-containing epoxy resin compositions prepared therewith |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US17029899P | 1999-12-13 | 1999-12-13 | |
US60/170,298 | 1999-12-13 |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2001042253A2 true WO2001042253A2 (en) | 2001-06-14 |
WO2001042253A3 WO2001042253A3 (en) | 2001-10-25 |
Family
ID=22619342
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2000/033648 WO2001042253A2 (en) | 1999-12-13 | 2000-12-11 | Phosphorus element-containing crosslinking agents and flame retardant phosphorus element-containing epoxy resin compositions prepared therewith |
Country Status (3)
Country | Link |
---|---|
US (3) | US6403220B1 (US06969756-20051129-C00007.png) |
AU (1) | AU2089701A (US06969756-20051129-C00007.png) |
WO (1) | WO2001042253A2 (US06969756-20051129-C00007.png) |
Cited By (12)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2002066485A2 (en) * | 2001-02-15 | 2002-08-29 | Pabu Services, Inc. | Novel hydroxyaryl phosphine oxides, glycidyl ethers and epoxy compositions, composites and laminates derived therefrom |
US6887950B2 (en) | 2001-02-15 | 2005-05-03 | Pabu Services, Inc. | Phosphine oxide hydroxyaryl mixtures with novolac resins for co-curing epoxy resins |
WO2008097674A1 (en) * | 2007-02-08 | 2008-08-14 | Basf Corporation | Crosslinkers containing phosphorous |
WO2008127744A2 (en) * | 2007-02-08 | 2008-10-23 | Basf Corporation | Film-forming material containing phosphorous and methods of producing coating compositions containing phosphorous |
US7671170B2 (en) | 2007-02-08 | 2010-03-02 | Basf Coatings Ag | Film-forming material containing phosphorous |
US7674874B2 (en) | 2007-02-08 | 2010-03-09 | Basf Coatings Ag | Methods of producing coating compositions containing phosphorous |
WO2011031834A1 (en) | 2009-09-11 | 2011-03-17 | Chemtura Corporation | Hydroxyphenyl phosphine oxide mixtures and their use as flame retardants for epoxy resins |
WO2011031420A2 (en) | 2009-09-11 | 2011-03-17 | Chemtura Corporation | Tris(hydroxoxyphenyl) phosphine oxides and their use as flame retardants for epoxy resins |
US8194374B2 (en) | 2009-04-16 | 2012-06-05 | Schweitzser Engineering Laboratories, Inc. | Differential element with harmonic blocking and harmonic restraint operating in parallel |
US8192603B2 (en) | 2008-12-29 | 2012-06-05 | Basf Coatings Gmbh | Electrocoat composition and process replacing phosphate pretreatment |
US8815066B2 (en) | 2008-12-29 | 2014-08-26 | Basf Coatings Gmbh | Coating composition with phosphorous-containing resins and organometallic compounds |
US9382638B2 (en) | 2008-12-29 | 2016-07-05 | Basf Corporation | Electrocoat composition and process replacing phosphate pretreatment |
Families Citing this family (31)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6592999B1 (en) * | 2001-07-31 | 2003-07-15 | Ppg Industries Ohio, Inc. | Multi-layer composites formed from compositions having improved adhesion, coating compositions, and methods related thereto |
US6641923B2 (en) * | 2001-07-31 | 2003-11-04 | Ppg Industries Ohio, Inc. | Weldable coating compositions having improved intercoat adhesion |
EP1513890A1 (en) * | 2002-05-30 | 2005-03-16 | Dow Global Technologies Inc. | Halogen free ignition resistant thermoplastic resin compositions |
US20040101689A1 (en) * | 2002-11-26 | 2004-05-27 | Ludovic Valette | Hardener composition for epoxy resins |
US20040147711A1 (en) * | 2003-01-23 | 2004-07-29 | Christiansen Walter H. | Epoxy resin compositions, methods of preparing, and articles made therefrom |
US6887574B2 (en) * | 2003-06-06 | 2005-05-03 | Dow Global Technologies Inc. | Curable flame retardant epoxy compositions |
WO2005007742A1 (ja) * | 2003-07-22 | 2005-01-27 | Matsushita Electric Works, Ltd. | 印刷配線板用樹脂組成物、プリプレグ、積層板、及びこれを用いたプリント配線板 |
US20050075024A1 (en) * | 2003-10-01 | 2005-04-07 | Ranken Paul F. | Flame retardant epoxy prepregs, laminates, and printed wiring boards of enhanced thermal stability |
KR100587483B1 (ko) | 2005-03-11 | 2006-06-09 | 국도화학 주식회사 | 난연성 고내열 에폭시수지 조성물 |
US9603244B2 (en) * | 2006-09-29 | 2017-03-21 | Hitachi Chemical Company, Ltd | Thermosetting resin composition and prepreg and laminate obtained with the same |
WO2008099940A1 (ja) * | 2007-02-16 | 2008-08-21 | Sumitomo Bakelite Co., Ltd. | 回路基板の製造方法、半導体製造装置、回路基板及び半導体装置 |
EP2217637B1 (en) * | 2007-11-29 | 2011-05-11 | Dow Global Technologies LLC | Dimethylformamide-free formulations using dicyanadiamide as curing agent for thermosetting epoxy resins |
US20090258161A1 (en) * | 2008-04-10 | 2009-10-15 | Japp Robert M | Circuitized substrate with P-aramid dielectric layers and method of making same |
EP2346939A1 (en) * | 2008-10-29 | 2011-07-27 | Icl-ip America Inc. | Phosphorus-containing flame retardant epoxy resin composition, prepeg and laminate thereof |
US8961768B2 (en) | 2008-12-29 | 2015-02-24 | Basf Corporation | Metal containing integrated electrocoat for better corrosion resistance |
SG181461A1 (en) | 2009-12-02 | 2012-07-30 | Dow Global Technologies Llc | Epoxy resin compositions |
WO2011068645A1 (en) | 2009-12-02 | 2011-06-09 | Dow Global Technologies Inc. | Coating compositions |
US9006312B2 (en) | 2009-12-02 | 2015-04-14 | Dow Global Technologies Llc | Composite compositions |
TWI477527B (zh) * | 2010-04-20 | 2015-03-21 | Hong Tai Electric Ind Co Ltd | Halogen-free flame retardant resin composition |
TWI494340B (zh) * | 2010-08-02 | 2015-08-01 | Taiwan Union Technology Corp | 環氧樹脂組成物及其製成的預浸材和印刷電路板 |
WO2012064703A1 (en) | 2010-11-12 | 2012-05-18 | Albemarle Corporation | Dopo-derived flame retardant and synthetic hydrogarnets for epoxy resin compositions |
JP5591176B2 (ja) * | 2011-04-27 | 2014-09-17 | 新日鉄住金化学株式会社 | リン及び窒素含有エポキシ樹脂 |
US9145488B2 (en) | 2011-05-19 | 2015-09-29 | Chemtura Corporation | Aluminum phosphorus acid salts as epoxy resin cure inhibitors |
US20130143984A1 (en) * | 2011-06-09 | 2013-06-06 | Basf Se | Production of cured epoxy resins with flame-retardant phosphonates |
TWI426116B (zh) * | 2011-10-07 | 2014-02-11 | Hong Tai Electric Ind Co Ltd | 黏著劑組成物、黏著層及其積層結構 |
ES2688532T3 (es) | 2013-01-18 | 2018-11-05 | Basf Se | Composiciones de recubrimiento a base de dispersión acrílica |
CN104693691B (zh) * | 2013-12-04 | 2018-01-09 | 上海杰事杰新材料(集团)股份有限公司 | 一种无卤阻燃乙烯基酯树脂复合物及其制备方法 |
KR101827475B1 (ko) * | 2014-09-30 | 2018-03-22 | 코오롱인더스트리 주식회사 | 난연성 에폭시 수지, 이의 제조방법 및 이를 포함하는 난연성 에폭시 수지 조성물 |
US9534108B2 (en) | 2015-03-13 | 2017-01-03 | Chemtura Corporation | Flame retardant epoxy resins comprising phosphorus containing flame retardants |
US9879121B2 (en) | 2015-09-28 | 2018-01-30 | International Business Machines Corporation | Flame-retardant, cross-linked EPDM rubber |
CN115894860B (zh) * | 2022-12-16 | 2023-08-18 | 江南大学 | 一种超支化阻燃环氧树脂及其制备的环氧树脂组合物 |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4345059A (en) * | 1981-05-18 | 1982-08-17 | Fmc Corporation | Fire retardant epoxy resins containing 3-hydroxyalkylphosphine oxides |
US5036135A (en) * | 1989-07-19 | 1991-07-30 | Siemens Aktiengesellschaft | Heat curable, reaction resin mixtures |
US5086156A (en) * | 1989-10-06 | 1992-02-04 | Virginia Tech Intellectual Properties, Inc. | Novel phosphorus containing epoxy networks based on trihydrocarbyl phosphine oxides having active substituents |
Family Cites Families (19)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4066628A (en) | 1976-08-02 | 1978-01-03 | Mitsubishi Chemical Industries Ltd. | Oxazolidone catalyst |
US4380571A (en) * | 1981-05-18 | 1983-04-19 | Fmc Corporation | Fire retardant epoxy resins containing 3-hydroxyalkylphosphine oxides |
JPS61134395A (ja) * | 1984-12-03 | 1986-06-21 | Sumitomo Chem Co Ltd | リン含有エポキシ化合物およびその製法 |
NL8501838A (nl) * | 1985-06-26 | 1987-01-16 | Stork Friesland Bv | Semi-permeabele membranen op basis van sulfonaat-groepen bevattende polymeren. |
US5066735A (en) | 1987-11-16 | 1991-11-19 | The Dow Chemical Company | Curable composition containing a difunctional epoxy resin, a polyfunctional epoxy resin, a difunctional phenol and a polyfunctional phenol |
US4925901A (en) | 1988-02-12 | 1990-05-15 | The Dow Chemical Company | Latent, curable, catalyzed mixtures of epoxy-containing and phenolic hydroxyl-containing compounds |
EP0384940B1 (de) | 1989-03-03 | 1994-06-22 | Siemens Aktiengesellschaft | Epoxidharzmischungen |
DE58907952D1 (de) | 1989-03-03 | 1994-07-28 | Siemens Ag | Epoxidharz-Formmassen. |
US5112931A (en) | 1989-07-17 | 1992-05-12 | Miles Inc. | Blocked polyisocyanates for the production of powder coatings with flat finishes |
US4973631A (en) | 1989-10-06 | 1990-11-27 | Virginia Tech Intellectual Properties Inc. | Novel phosphorus containing epoxy networks |
ATE114661T1 (de) | 1990-04-02 | 1994-12-15 | Pfizer | Benzylphosphonsäure-tyrosinkinaseinhibitoren. |
SG43193A1 (en) | 1990-05-21 | 1997-10-17 | Dow Chemical Co | Latent catalysts cure-inhibited epoxy resin compositions and laminates prepared therfrom |
DE4308187A1 (de) | 1993-03-15 | 1994-09-22 | Siemens Ag | Epoxidharzmischungen |
TW294694B (US06969756-20051129-C00007.png) | 1994-09-09 | 1997-01-01 | Siemens Ag | |
TW297034B (US06969756-20051129-C00007.png) | 1994-09-09 | 1997-02-01 | Siemens Ag | |
GB9421405D0 (en) | 1994-10-21 | 1994-12-07 | Dow Chemical Co | Low voc laminating formulations |
EP0825217A1 (en) | 1996-08-23 | 1998-02-25 | Akzo Nobel N.V. | Adduct of bisepoxy compound and P-guanamine |
JP2000516659A (ja) | 1996-08-23 | 2000-12-12 | アクゾ ノーベル ナムローゼ フェンノートシャップ | エポキシ化合物と環式ホスファイトとの付加生成物 |
GB9713526D0 (en) | 1997-06-26 | 1997-09-03 | Dow Deutschland Inc | Flame retardant laminating formulations |
-
2000
- 2000-12-11 US US09/734,904 patent/US6403220B1/en not_active Expired - Lifetime
- 2000-12-11 AU AU20897/01A patent/AU2089701A/en not_active Abandoned
- 2000-12-11 WO PCT/US2000/033648 patent/WO2001042253A2/en active Application Filing
-
2002
- 2002-04-11 US US10/122,158 patent/US6740732B2/en not_active Expired - Lifetime
-
2004
- 2004-03-09 US US10/796,762 patent/US6969756B2/en not_active Expired - Fee Related
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4345059A (en) * | 1981-05-18 | 1982-08-17 | Fmc Corporation | Fire retardant epoxy resins containing 3-hydroxyalkylphosphine oxides |
US5036135A (en) * | 1989-07-19 | 1991-07-30 | Siemens Aktiengesellschaft | Heat curable, reaction resin mixtures |
US5086156A (en) * | 1989-10-06 | 1992-02-04 | Virginia Tech Intellectual Properties, Inc. | Novel phosphorus containing epoxy networks based on trihydrocarbyl phosphine oxides having active substituents |
Non-Patent Citations (2)
Title |
---|
DATABASE CHEMABS [Online] CHEMICAL ABSTRACTS SERVICE, COLUMBUS, OHIO, US; DHAWAN, BALRAM ET AL: "Metalation induced rearrangement of triaryl phosphates to tris(2-hydroxyaryl)phosphine oxides" retrieved from STN Database accession no. 108:56214 XP002162872 cited in the application & SYNTH. COMMUN. (1987), 17(4), 465-8, * |
DATABASE WPI Section Ch, Week 198631 Derwent Publications Ltd., London, GB; Class A21, AN 1986-201721 XP002162311 -& JP 61 134395 A (SUMITOMO CHEM IND KK), 21 June 1986 (1986-06-21) cited in the application * |
Cited By (20)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2002066485A2 (en) * | 2001-02-15 | 2002-08-29 | Pabu Services, Inc. | Novel hydroxyaryl phosphine oxides, glycidyl ethers and epoxy compositions, composites and laminates derived therefrom |
WO2002066485A3 (en) * | 2001-02-15 | 2002-10-31 | Pabu Services Inc | Novel hydroxyaryl phosphine oxides, glycidyl ethers and epoxy compositions, composites and laminates derived therefrom |
US6733698B2 (en) | 2001-02-15 | 2004-05-11 | Pabu Services, Inc. | Mixture of mono-, bis- and tris-(hydroxyaryl) phosphine oxides useful to make polyglycidyl ethers or in epoxy compositions |
US6887950B2 (en) | 2001-02-15 | 2005-05-03 | Pabu Services, Inc. | Phosphine oxide hydroxyaryl mixtures with novolac resins for co-curing epoxy resins |
US6955851B2 (en) | 2001-02-15 | 2005-10-18 | Pabu Services, Inc. | Hydroxyaryl phosphine oxides, glycidyl ethers and epoxy compositions, composites and laminates derived therefrom |
US7202311B2 (en) | 2001-02-15 | 2007-04-10 | Great Lakes Corporation | Phosphine oxide hydroxyarl mixtures with novolac resins for co-curing epoxy resins |
US7201957B2 (en) | 2001-02-15 | 2007-04-10 | Great Lakes Corporation | Phosphine oxide hydroxyaryl mixtures with novolac resins for co-curing epoxy resins |
US7671170B2 (en) | 2007-02-08 | 2010-03-02 | Basf Coatings Ag | Film-forming material containing phosphorous |
WO2008127744A2 (en) * | 2007-02-08 | 2008-10-23 | Basf Corporation | Film-forming material containing phosphorous and methods of producing coating compositions containing phosphorous |
WO2008127744A3 (en) * | 2007-02-08 | 2009-05-22 | Basf Corp | Film-forming material containing phosphorous and methods of producing coating compositions containing phosphorous |
WO2008097674A1 (en) * | 2007-02-08 | 2008-08-14 | Basf Corporation | Crosslinkers containing phosphorous |
US7674874B2 (en) | 2007-02-08 | 2010-03-09 | Basf Coatings Ag | Methods of producing coating compositions containing phosphorous |
US8192603B2 (en) | 2008-12-29 | 2012-06-05 | Basf Coatings Gmbh | Electrocoat composition and process replacing phosphate pretreatment |
US8815066B2 (en) | 2008-12-29 | 2014-08-26 | Basf Coatings Gmbh | Coating composition with phosphorous-containing resins and organometallic compounds |
US9382638B2 (en) | 2008-12-29 | 2016-07-05 | Basf Corporation | Electrocoat composition and process replacing phosphate pretreatment |
US8194374B2 (en) | 2009-04-16 | 2012-06-05 | Schweitzser Engineering Laboratories, Inc. | Differential element with harmonic blocking and harmonic restraint operating in parallel |
WO2011031834A1 (en) | 2009-09-11 | 2011-03-17 | Chemtura Corporation | Hydroxyphenyl phosphine oxide mixtures and their use as flame retardants for epoxy resins |
WO2011031421A1 (en) | 2009-09-11 | 2011-03-17 | Chemtura Corporation | Hydroxyphenyl phosphine oxide mixtures and their use as flame retardants for epoxy resins |
WO2011031420A2 (en) | 2009-09-11 | 2011-03-17 | Chemtura Corporation | Tris(hydroxoxyphenyl) phosphine oxides and their use as flame retardants for epoxy resins |
US8404161B2 (en) | 2009-09-11 | 2013-03-26 | Chemtura Corporation | Hydroxyphenyl phosphine oxide mixtures and their use as flame retardant's for epoxy resins |
Also Published As
Publication number | Publication date |
---|---|
US6403220B1 (en) | 2002-06-11 |
US6740732B2 (en) | 2004-05-25 |
WO2001042253A3 (en) | 2001-10-25 |
AU2089701A (en) | 2001-06-18 |
US20040171769A1 (en) | 2004-09-02 |
US20030031873A1 (en) | 2003-02-13 |
US6969756B2 (en) | 2005-11-29 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US6403220B1 (en) | Phosphorus element-containing crosslinking agents and flame retardant phosphorus element-containing epoxy resin compositions prepared therewith | |
EP1268665B1 (en) | Flame retardant phosphorus element-containing epoxy resin compositions | |
US9045508B2 (en) | Phosphorus-containing oligomer and method for producing the same, curable resin composition and cured product of the same, and printed wiring board | |
EP0991711A1 (en) | A flame retardant epoxy resin composition | |
EP1363922B1 (en) | Novel hydroxyaryl phosphine oxides mixture, glycidyl ethers and epoxy compositions, composites and laminates derived therefrom | |
US6353080B1 (en) | Flame retardant epoxy resin composition | |
CN101878239B (zh) | 环氧树脂配制物 | |
US7201957B2 (en) | Phosphine oxide hydroxyaryl mixtures with novolac resins for co-curing epoxy resins | |
US20060099458A1 (en) | 1, 4-Hydroquinone functionalized phosphinates and phosphonates | |
WO2006034445A1 (en) | 1,4-hydroquinone functionalized phosphynates and phosphonates | |
JP2007002053A (ja) | エポキシ樹脂組成物及びその硬化物 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A2 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CR CZ DE DK DM DZ EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG UZ YU ZA ZW |
|
AL | Designated countries for regional patents |
Kind code of ref document: A2 Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE TR BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
AK | Designated states |
Kind code of ref document: A3 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CR CZ DE DK DM DZ EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG UZ YU ZA ZW |
|
AL | Designated countries for regional patents |
Kind code of ref document: A3 Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE TR BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG |
|
REG | Reference to national code |
Ref country code: DE Ref legal event code: 8642 |
|
122 | Ep: pct application non-entry in european phase | ||
NENP | Non-entry into the national phase |
Ref country code: JP |