WO2001027048A1 - Article refractaire contenant du carbone dote d'un revetement protecteur - Google Patents

Article refractaire contenant du carbone dote d'un revetement protecteur Download PDF

Info

Publication number
WO2001027048A1
WO2001027048A1 PCT/EP2000/009859 EP0009859W WO0127048A1 WO 2001027048 A1 WO2001027048 A1 WO 2001027048A1 EP 0009859 W EP0009859 W EP 0009859W WO 0127048 A1 WO0127048 A1 WO 0127048A1
Authority
WO
WIPO (PCT)
Prior art keywords
protective coating
article
carbon
oxide
article according
Prior art date
Application number
PCT/EP2000/009859
Other languages
English (en)
Inventor
Cécile DESVIGNES
Gilbert Brandy
Original Assignee
Vesuvius Crucible Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Vesuvius Crucible Company filed Critical Vesuvius Crucible Company
Priority to BR0014661-7A priority Critical patent/BR0014661A/pt
Priority to EP00969452A priority patent/EP1252115A1/fr
Priority to AU79161/00A priority patent/AU7916100A/en
Priority to MXPA02003677A priority patent/MXPA02003677A/es
Priority to JP2001530071A priority patent/JP2003511341A/ja
Priority to KR1020027004586A priority patent/KR20020042710A/ko
Publication of WO2001027048A1 publication Critical patent/WO2001027048A1/fr

Abstract

L'invention concerne un article réfractaire contenant du carbone doté d'un revêtement protecteur. Ledit revêtement protecteur réduit l'oxydation de l'article pendant les opérations de préchauffe et de coulée. Une aide au mouillage à température élevée comprenant un oxyde de métal, le métal étant sélectionné parmi le groupe contenant de l'arsenic, de l'antimoine, du bismuth, du plomb, du vanadium et de l'étain, améliore le mouillage du revêtement protecteur sur l'article, et réduit donc les imperfections du revêtement protecteur coulé. Le revêtement protège l'article de l'oxydation et de la décarburation qui peuvent découler de l'utilisation de l'article à des températures élevées dans une atmosphère oxydante. L'aide au mouillage est un oxyde de métal, tel que l'oxyde de bismuth qui réduit la tension de surface du revêtement protecteur à une température élevée et favorise le recouvrement du revêtement protecteur sur la surface de l'article.
PCT/EP2000/009859 1999-10-14 2000-10-05 Article refractaire contenant du carbone dote d'un revetement protecteur WO2001027048A1 (fr)

Priority Applications (6)

Application Number Priority Date Filing Date Title
BR0014661-7A BR0014661A (pt) 1999-10-14 2000-10-05 Artigo refratário
EP00969452A EP1252115A1 (fr) 1999-10-14 2000-10-05 Article refractaire contenant du carbone dote d'un revetement protecteur
AU79161/00A AU7916100A (en) 1999-10-14 2000-10-05 Carbon-containing refractory article having a protective coating
MXPA02003677A MXPA02003677A (es) 1999-10-14 2000-10-05 Articulo refractario que contiene carbono con un recubrimiento protector.
JP2001530071A JP2003511341A (ja) 1999-10-14 2000-10-05 保護コーティングを有する炭素含有耐熱物品
KR1020027004586A KR20020042710A (ko) 1999-10-14 2000-10-05 보호성 피막을 보유한 탄소 함유 내화성 물품

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP99870209.6 1999-10-14
EP99870209 1999-10-14

Publications (1)

Publication Number Publication Date
WO2001027048A1 true WO2001027048A1 (fr) 2001-04-19

Family

ID=8243908

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2000/009859 WO2001027048A1 (fr) 1999-10-14 2000-10-05 Article refractaire contenant du carbone dote d'un revetement protecteur

Country Status (10)

Country Link
EP (1) EP1252115A1 (fr)
JP (1) JP2003511341A (fr)
KR (1) KR20020042710A (fr)
CN (1) CN1181000C (fr)
AR (1) AR026000A1 (fr)
AU (1) AU7916100A (fr)
BR (1) BR0014661A (fr)
MX (1) MXPA02003677A (fr)
TW (1) TW538014B (fr)
WO (1) WO2001027048A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2011020832A1 (fr) 2009-08-17 2011-02-24 Technische Universität Bergakademie Freiberg Produits réfractaires comprimés contenant du carbone ou liés à du carbone, à base d'oxyde d'aluminium et procédé de préparation

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20050037226A1 (en) * 2003-08-12 2005-02-17 Peascoe Meisner Roberta A. Alkali resistant refractories
CN1300260C (zh) * 2004-01-13 2007-02-14 中南大学 碳/碳复合材料抗氧化涂层的前躯体
CN1899997B (zh) * 2006-06-23 2010-05-12 吉林大学 在金属载体上制备玻璃陶瓷涂层的方法
CN102674902B (zh) * 2012-05-15 2013-08-28 陕西科技大学 一种C-AlPO4-莫来石/玻璃层梯度复合抗氧化涂层的制备方法
CN107686355A (zh) * 2017-09-18 2018-02-13 佛山市高捷工业炉有限公司 高强度坩埚的制备方法

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3460987A (en) * 1965-01-27 1969-08-12 English Electric Co Ltd Method of coating a ceramic-carbon material with glass and article
US5013697A (en) * 1990-06-21 1991-05-07 Johnson Matthey Inc. Sealing glass compositions
DE4216934A1 (de) * 1992-05-22 1993-11-25 Fleischmann Adolf A Fa Feuerfeste Auskleidung, insbesondere für Industrieöfen
WO1995018076A1 (fr) * 1993-12-29 1995-07-06 Cookson Matthey Ceramics & Materials Limited Email pour materiaux refractaires

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3460987A (en) * 1965-01-27 1969-08-12 English Electric Co Ltd Method of coating a ceramic-carbon material with glass and article
US5013697A (en) * 1990-06-21 1991-05-07 Johnson Matthey Inc. Sealing glass compositions
DE4216934A1 (de) * 1992-05-22 1993-11-25 Fleischmann Adolf A Fa Feuerfeste Auskleidung, insbesondere für Industrieöfen
WO1995018076A1 (fr) * 1993-12-29 1995-07-06 Cookson Matthey Ceramics & Materials Limited Email pour materiaux refractaires

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2011020832A1 (fr) 2009-08-17 2011-02-24 Technische Universität Bergakademie Freiberg Produits réfractaires comprimés contenant du carbone ou liés à du carbone, à base d'oxyde d'aluminium et procédé de préparation
DE102009037540A1 (de) 2009-08-17 2011-03-03 Technische Universität Bergakademie Freiberg Gepresste, kohlenstoffhaltige bzw. kohlenstoffgebundene Feuerfesterzeugnisse auf Aluminiumoxidbasis und Verfahren zu ihrer Herstellung

Also Published As

Publication number Publication date
BR0014661A (pt) 2002-06-11
AR026000A1 (es) 2002-12-26
TW538014B (en) 2003-06-21
CN1181000C (zh) 2004-12-22
KR20020042710A (ko) 2002-06-05
MXPA02003677A (es) 2002-08-30
CN1378524A (zh) 2002-11-06
AU7916100A (en) 2001-04-23
JP2003511341A (ja) 2003-03-25
EP1252115A1 (fr) 2002-10-30

Similar Documents

Publication Publication Date Title
US5856015A (en) Glaze for refractory materials
US3852107A (en) Protection of graphite electrodes
KR102051934B1 (ko) 고내열성 세라믹 코팅 조성물
US4540675A (en) Carbon-containing refractories with superior erosion and oxidation resistance
US2013625A (en) Refractory article
JP6841897B2 (ja) その表面に少なくとも１つのコーティングを有しているローラー炉用ローラー
RU2173308C2 (ru) Способ образования огнеупорной ремонтной массы и порошковая смесь для его осуществления
US5188989A (en) Coating mix to prevent oxidation of carbon substrates
EP1252115A1 (fr) Article refractaire contenant du carbone dote d'un revetement protecteur
KR100190912B1 (ko) 2층이상의코팅을가지는저융점금속의주조용기구
US20050233084A1 (en) Method for treating a contact surface for a mullite-based refractory recipient, and a coating made with this method
KR100332159B1 (ko) 산화물-기재 내화체의 보수방법 및 이를 위한 분말혼합물
KR101236300B1 (ko) 탄소함유 내화물용 산화방지 조성물 및 이를 사용하여탄소함유 내화물의 초기 산화를 억제하는 방법
JPH0261436B2 (fr)
KR101072523B1 (ko) 용선예비처리 설비용 내화벽돌
JPS6352986B2 (fr)
US20080179310A1 (en) Electric Arc Furnace Runner and Method of Forming an Expendable Lining of an Electric Arc Furnace Runner
JP3197781B2 (ja) アルミニウム−リチウム合金用耐火材
JPH0345583A (ja) 炭素質材の耐熱酸化防止用コーティング材
KR19980048902A (ko) 불꽃용사용 내화분말재료
JPS62212284A (ja) ジルコニア−炭素材質の酸化防止方法
KR19980047209A (ko) 산화방지용 저팽창성 도포제와 이를 이용한 도포방법
JPH05228617A (ja) アルミナ系耐火物の補修・延命化方法
JPH0426561A (ja) コーティング材
JPH05148014A (ja) アルミ−リチウム合金耐火材

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CR CU CZ DE DK DM DZ EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG US UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
WWE Wipo information: entry into national phase

Ref document number: 2000969452

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 1020027004586

Country of ref document: KR

ENP Entry into the national phase

Ref document number: 2001 530071

Country of ref document: JP

Kind code of ref document: A

WWE Wipo information: entry into national phase

Ref document number: PA/a/2002/003677

Country of ref document: MX

Ref document number: 00814172X

Country of ref document: CN

WWP Wipo information: published in national office

Ref document number: 1020027004586

Country of ref document: KR

WWE Wipo information: entry into national phase

Ref document number: 10089927

Country of ref document: US

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

WWP Wipo information: published in national office

Ref document number: 2000969452

Country of ref document: EP

WWW Wipo information: withdrawn in national office

Ref document number: 2000969452

Country of ref document: EP