Classifications

• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01D—SEPARATION
  • B01D39/00—Filtering material for liquid or gaseous fluids
• • C—CHEMISTRY; METALLURGY
  • C02—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
  • C02F—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
  • C02F1/00—Treatment of water, waste water, or sewage
  • C02F1/001—Processes for the treatment of water whereby the filtration technique is of importance
  • C02F1/003—Processes for the treatment of water whereby the filtration technique is of importance using household-type filters for producing potable water, e.g. pitchers, bottles, faucet mounted devices
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L2/00—Methods or apparatus for disinfecting or sterilising materials or objects other than foodstuffs or contact lenses; Accessories therefor
  • A61L2/0005—Methods or apparatus for disinfecting or sterilising materials or objects other than foodstuffs or contact lenses; Accessories therefor for pharmaceuticals, biologicals or living parts
  • A61L2/0011—Methods or apparatus for disinfecting or sterilising materials or objects other than foodstuffs or contact lenses; Accessories therefor for pharmaceuticals, biologicals or living parts using physical methods
  • A61L2/0017—Filtration
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L2/00—Methods or apparatus for disinfecting or sterilising materials or objects other than foodstuffs or contact lenses; Accessories therefor
  • A61L2/02—Methods or apparatus for disinfecting or sterilising materials or objects other than foodstuffs or contact lenses; Accessories therefor using physical phenomena
  • A61L2/022—Filtration
• • C—CHEMISTRY; METALLURGY
  • C02—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
  • C02F—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
  • C02F1/00—Treatment of water, waste water, or sewage
  • C02F1/28—Treatment of water, waste water, or sewage by sorption
• • C—CHEMISTRY; METALLURGY
  • C02—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
  • C02F—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
  • C02F1/00—Treatment of water, waste water, or sewage
  • C02F1/50—Treatment of water, waste water, or sewage by addition or application of a germicide or by oligodynamic treatment
• • C—CHEMISTRY; METALLURGY
  • C02—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
  • C02F—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
  • C02F2307/00—Location of water treatment or water treatment device
  • C02F2307/06—Mounted on or being part of a faucet, shower handle or showerhead

Definitions

• the invention relates to filters for removing microorganisms from liquid, methods for removing microorganisms from liquid, and methods for manufactu ⁇ ng filters
• the invention relates to filter technology for the removal of bacte ⁇ a and viruses from d ⁇ nking water under conditions encountered in faucet mounted filters and pour through filters.
• U.S. Patent No. 5,017,292 to DiLeo, et al. describes a composite membrane including a porous membrane substrate, a surface skin having ultrafiltration separation properties, and an intermediate porous zone having an average pore size smaller than that of the substrate.
• ion exchange resins Based on the theory of charge interaction as means of removing micro organisms from the water, positively charged ion exchange resins have been utilized for bacte ⁇ a adsorption by Daniels, "Developments In Industrial Microbiology", Vol. 13, Proceedings of the twenty- eighth General Meeting of the Society for Industrial Microbiology, pages 211-243 (1972).
• the fundamental framework of these ion exchange resins is an elastic three dimensional hydrocarbon network comprising lomzable groups, either cationic or anionic, chemically bonded to the backbone of a hydrocarbon framework
• the network is normally fixed, insoluble in common solvents and chemically inert.
• the lomzable functional groups attached to the matrix carry active ions with counter-ions which can be exchanged by the other counter-ions existed in water.
• Typical examples of commercially available ion exchange resms are the poly styrene cross-lmked with divmyl benzene (DVB), and the methacrylate copolymerized with DVB.
• DVD polystyrene
• a three dimensional network is formed first, and the functional groups are then introduced into benzene rings through chloromethylation. Since those lomzable groups are highly hydrophihc, the more the existence of those groups in resm structure, the more the resm will swell to restrict the flow of water.
• the ion exchange resms made by cross-linking the functional group carrying polymers have been successfully applied for the removal of both organic and inorganic ions in Angstrom size range but they are normally unsuitable for the relatively large sized micro-organisms. Also, the matrix swells and the flow resistance increases due to the pore narrowing.
• the filter includes an amount of particulate including magnesium peroxide or calcium peroxide immobilized on a substantially inert porous matrix.
• the filter media can be provided with an electropositive potential by modifying the surface of the particulate or inert porous matrix with a surface modifying agent.
• Hou, et al. "Capture of Latex Beads, Bacteria, Endotoxm, and Viruses by Charge-Modified Filters," Appl. Environ.
• U.S. Patent No. 4,352,884 to Nakashima, et al. discloses a earner for bioactive materials comp ⁇ sed of a substrate coated with a copolymer.
• the substrate may be one of various materials, including inorganic nature such as glass, activated carbon, silica, and alumina as well as organic polymers such as polystyrene, polyethylene, polyvinyl chlo ⁇ de, nylon, polyester, polymethyl methacrylate, and naturally occur ⁇ ng high polymers such as cellulose.
• the copolymer can be an acrylate or methacrylate monomer and a copolyme ⁇ zable unsaturated carboxyhc acid or unsaturated amme.
• U.S. Patent 3,898,188 to Rembawn, et al. and U.S. Patent 3,784,649 to Buckman, et al. describe the polymerization of a dihahde and a ditertiary amme to form poly-quaternary ammonium resm. These polymers have found utility as flocculants in the clarification of water supplies. The materials are also known to exhibit germicidal action or as an effective bactericidal and fungicidal agents.
• Faucet-mounted dnnkmg water filters are desc ⁇ bed by U.S. Patent No 5,525,214.
• faucet-mounted dnnkmg filters include a filtration media for removing chemical and mineral contaminants as well as larger microorganisms.
• Common filter media include carbon, which is often m the form of a porous block. Additional contaminants, such as lead, can be removed with the addition of selective adsorbents.
• the filtration media commonly used in faucet-mounted dnnkmg water filters have been combined with microfilters for the removal of small microorganisms and particles The microfiltration is usually accomplished as a result of the fine porosity of the carbon block, or with the use of a second filter, including a hollow fiber membrane material.
• a filter for removing microorganisms from a liquid includes a microorganism filtration media including a substrate having a reactive surface and a polymer covalently bonded to the reactive surface of the substrate.
• the polymer includes a plurality of cationic groups for attracting microorganisms in a liquid
• the filtration media exhibits an MS-2 virus removal coefficient m water of greater than 10 ml/g-sec
• the polymer which is covalently bonded to the substrate is preferably at least one of polyamide-polyamme polymer, polyamme polymer, and mixtures thereof.
• Exemplary polyamide-polyamme polymers include those polymers having at least one of the following repeating units:
• n for each of formulas I-HJ, is between about 10 and 100,000.
• the polyamide- polyamme polymer preferably has a number average molecular weight of between about 25,000 and about 2,000,000, and more preferably between about 500,000 and 1,500,000.
• the polymer can be provided as a mixture of separate polymers including repeating units of any one or more of formulas I-UJ, or as copolymers containing repeating units of any one of formulas I-HI or any combination of formulas I-IH.
• the polyamme polymer can include a reaction product of polyethylemmme and a cross-linking agent, such as, a di-epoxy cross-linking agent.
• the polyethylemmme polymer preferably has a repeating unit of the following formula:
• n is between about 10 and about 1,000,000.
• the polyethylemmme polymer preferably has a number average molecular weight of between about 800 and about 1,000,000.
• the di- epoxy cross-linking agent is preferably a diglycidyl ether such as the diglycidyl ether of 1, 4- butanediol.
• Substrate is preferably a substrate having a surface which is capable of reacting with the polymer to provide a covalent bond between the substrate and the polymer.
• the reactive surface of the substrate includes functional groups capable of reacting with reactive groups of the polymer, including epoxy groups and azetidmium groups.
• Exemplary functional groups which can be present on the substrate include hydroxyl groups, ammo groups and hydrosulfyl groups.
• the substrate can be provided m the form of a fibrous material and/or particulate matenal.
• Preferred materials include glass, silica (including diatomaceous earth), alumina, polystyrene, polypropylene, polyethylene, polyvinyl alcohol, polyamide, cellulose, and mixtures thereof.
• a preferred substrate includes glass fiber web
• the filtration media includes a charge density of at least about 0.001 mil - equivalent/gram filtration media.
• the filtration media preferably exhibits an extractables of less than 20 ppm nitrogen in extracted water, wherein the extractables is determined by a Hach DR-700 colorimeter after soaking two grams of filtration media into 250 ml nitrogen free water for two hours at room temperature.
• a method for removing microorganisms from water includes a step of reacting a polymer to a substrate surface to provide a filtration media exhibiting covalent bonding between the polymer and the substrate surface.
• the polymer includes a plurality of cationic groups for attracting microorganisms, and the filtration media exhibits an MS-2 virus removal coefficient in water of greater than 10 ml/g-sec.
• the method includes a step of passing water through the filtration media to remove microorganisms from the water.
• a faucet mount filter is provided by the invention.
• the faucet mount filter includes a housing having an inlet, an outlet, and an te ⁇ or region.
• the interior region contains a water treatment material.
• the water treatment material includes a filtration media having a substrate with a reactive surface and a polymer covalently bonded to the reactive surface of the substrate.
• the polymer includes a plurality of cationic groups for attracting microorganisms.
• the faucet mount filter includes a valve for controlling flow of water into the mlet of the housing, and an adapter for attaching the valve to a faucet.
• a pour through filter is provided by the invention.
• the pour through filter includes a housing having an mlet, an outlet, and an interior region.
• the mtenor region includes a pleated filtration media.
• the pleated filtration media includes a substrate having a reactive surface and a polymer covalently bonded to the reactive surface.
• the polymer includes a plurality of cationic groups for attracting microorganisms m water.
• the mte ⁇ or region can additionally include a layer of microorganism filtration media in combination with the pleated microorganism filtration media.
• the layer of microorganism filtration media can be provided around the pleated microorganism filtration media.
• a method for manufactunng a microorganism filtration media includes steps of providing a substrate, such as, as glass fiber web, coating the substrate with a polymer, and heating the coated substrate to dry and covalently react the polymer to the substrate.
• the polymer is preferably at least one of polyamide-polyamme polymer, polyamme polymer, and mixtures thereof, and is preferably provided at a solids content of between about 0.1 wt.% and about 10 wt.%.
• Figure 1 is a perspective view of a faucet mount filter according to the pnnciples of the invention
• Figure 2 is a sectional v ew of the faucet mount filter of Figure 1 taken along lines 2-2;
• FIG. 3 is a sectional view of an alternative embodiment of faucet mount filter according to the principles of the invention.
• Figure 4 is a sectional view of a pour through filter according to the pnnciples of the invention.
• Figure 5 is a graph of flow properties for glass media
• Figure 6 is a graph representing the effect of pH on polymer charge properties.
• the present invention relates to a filter which includes a microorganism filtration media for removing microorganisms including bactena and viruses
• a filter which includes a microorganism filtration media for removing microorganisms including bactena and viruses
• the microorganism filtration media can be referred to herein as the filtration media, and can be used m combination with other components of a filter.
• Microorganisms generally have a size of less than about 1 ⁇
• Conventional filters for use with drinking water typically remove contaminants having a size of 3 ⁇ or greater.
• Microorganisms which can be removed by the filtration media of the invention include bacteria and viruses.
• Bactena generally have a size between about 0.2 ⁇ and about 10 ⁇
• Particular species of bacteria which are sometimes found m dnnkmg water and which can be removed by the filter of the present invention include E coli, Salmonella typhi, other salmonellae, Shigella spp., Vibrio cholerae, Yersinia enterocohtica, Legionella, Pseudomonas aeruginosa, Aeromonas spp , Mycobacterium, atypical, and mixtures thereof.
• Viruses typically have a size of between about 10 nm and about 200 nm.
• Viruses sometimes found in dnnkmg water and which are of particular concern for removal therefrom by the filter of the invention include Adenoviruses, Enteroviruses, Hepatitis A, Hepatitis E, Norwalk virus, Rotavirus, Small round viruses (other than Norwalk virus), and mixtures thereof.
• viruses have coats which include protein polypeptides that contain ammo acids such as glutamic acid, aspartic acid, histidme, and tyrosme.
• ammo acids such as glutamic acid, aspartic acid, histidme, and tyrosme.
• these ammo acids contain weakly acidic and basic groups (i.e., carboxyl and ammo groups), which ionize to provide the viral capsid with an electrical charge.
• each ammo acid ionizing group in the polypeptide has a charactenstic disassociation constant The variation of disassociation constants among the various polypeptides ensures that most viruses have net charges that vary continuously with pH, and can be measured by lso-electnc focusing and are expressed as iso-elect ⁇ c point (IEP).
• the microorganism filtration media includes a porous substrate and a polymer composition covalently bonded to the substrate
• the microorganism filtration media can be referred to as a polymer modified filtration media
• the polymer modified filtration media allows liquid to flow therethrough.
• a preferred liquid which can be processed by the filter of the invention is water
• the polymer composition is covalently bonded to the substrate and includes groups which adsorb microorganisms present in the liquid. As liquid flows through the microorganism filtration media, microorganisms are adsorbed by the groups provided on the polymer. Furthermore, the covalent bond between the polymer and the substrate provides reduced leaching of the polymer from the filter into the liquid compared with filters prepared without the covalent bonding as shown in Example 11
• the substrate is preferably a porous substrate having a surface which is reactive to the polymer composition
• the substrate is preferably sufficiently porous to allow water to flow therethrough at desirable flow rates under the conditions of operation. It is expected that the presence of the polymer covalently bonded to the substrate will not significantly decrease the porosity of the substrate or flow rate of liquid through the substrate.
• the substrate which includes the polymer bonded thereto will provide a desirable degree of flow under the intended conditions of operation
• the flow rate of water through the faucet mount filter should be at least about one liter per minute under conditions of a water supply pressure of 60 psi or less and when the filtration media is provided within a volume of less than about one liter
• the substrate preferably includes a surface which is capable of reacting with the polymer to provide a covalent bond between the substrate and the polymer.
• the reactive surface of the substrate includes functional groups capable of reacting with reactive groups of the polymer, including epoxy groups and azetidmium groups.
• Exemplary functional groups on the reactive surface of the substrate include hydroxyl groups, ammo groups, and hydrosulfyl groups.
• the substrate can be provided in the form of fibrous mate ⁇ al and/or particulate matenal. Preferred matenals include glass, silica (including diatomaceous earth), alumina, polystyrene, polypropylene, polyethylene, polyvinyl alcohol, polyamide, cellulose, and mixtures thereof.
• the fibers have an average diameter of between about 0.2 ⁇ and about 25 ⁇ .
• the substrate can include mixtures of different diameter size fibers.
• Exemplary substrates prepared from fibers include woven fabrics, unwoven fabrics, and knitted fabrics.
• the substrate has an average pore size ranging from between about 0.5 ⁇ and about 2 ⁇ . If the pores are too small, it is believed that the flow rate through the filtration media for desired applications will be too low, or the pressure drop required to generate the desired flow rate will be too high.
• a preferred substrate is glass fiber.
• Preferred glass fiber substrates are available from Ahlstrom Technical Papers.
• a preferred glass fiber substrate for use in adsorbing virus includes grade 151 glass fiber from Ahlstrom Technical Papers.
• a preferred glass fiber substrate for the adsorption of bacteria includes grade 164.
• the particles are porous and have an average size of between about 5 ⁇ and about 50 ⁇ . In general, it is desirable for the particles to have an average pore size of between about 0.2 ⁇ and about 2 ⁇ for the reasons described above in the context of substrates prepared from fibers. In addition, it should be understood that the substrate can be prepared from a mixture of fibers and particles.
• the thickness of the substrate is preferably sufficiently small to reduce the incidence of polymer migration to a surface of the substrate in the formation of the filtration media.
• By providing the filtration media with a relatively thin thickness it has been found that the polymer can be relatively evenly distributed across the thickness of the filtration media.
• the filtration media is layered to provide at least two layers, and more preferably between about 2 and about 6 layers.
• the filtration media can be provided as a pleated media in order to increase the surface area that contacts the liquid.
• the thickness of the substrate is preferably between about 0.25 mm and about 1.5 mm
• the polymer which is chemically bonded to the substrate is preferably a polymer which does not wash away with the influent, and includes ionic groups that attract microorganisms
• the microorganism attracting groups are preferably positively charged groups when provided m a fluid having a pH commonly associated with the pH of dnnkmg water.
• the pH range of dnnkmg water will be between about 5 and about 9.
• Exemplary charged groups which have been found to be particularly effective in attracting microorganisms include primary amines, secondary amines, and tertiary amines.
• a first polymer which can be used in the polymer composition is a polymer containing cationic charges
• the first polymer can include cationic charges on the polymer backbone
• a preferred first polymer includes polyamide-polyamme polymer.
• the polyamide- polyamme polymer having cationic charges on its backbone is preferably a secondary amme based azetidmium polymer having repeating units of the following formula:
• Preferred polyamide-polyamme polymers having repeating units of formula I have an n value of between about 10 and about 100,000, and more preferably between about 1,000 and about 75,000.
• the polyamide-polyamme polymer preferably has a number average molecular weight of between about 25,000 and 2,000,000 and more preferably between about 500,000 and 1,500,000.
• the first polymer can be a copolymer including repeating units in addition to those identified as having formula I.
• a second polymer which can be used in the polymer composition includes a polymer having cationic charges.
• the cationic charges can be provided on pendant groups and/or on the backbone.
• a preferred second polymer includes polyamide-polyamme polymer.
• the polyamide-polyamme polymer having cationic charges on pendant groups is preferably a tertiary amme based epoxide polymer having repeating units of one or more of the following formula:
• Preferred polyamide-polyamme polymers having repeating units of formulas II and/or UJ preferably have an n value of between about 10 and about 100,000, and more preferably between about 1,000 and about 75,000.
• the polyamide-polyamme polymer preferably has a number average molecular weight of between about 25,000 and 2,000,000 and more preferably between about 500,000 and 1,500,000.
• the second polymer can be a copolymer including repeating units m addition to those identified in formulas II and HI.
• the copolymer can include both of the repeating units in formulas II and HJ.
• a third polymer can be used alone m the polymer composition for forming the filtration media, or m combination with the first polymer and/or the second polymer to provide increased charge density.
• the third polymer preferably has cationic groups for adsorption of microorganisms.
• the third polymer When the third polymer is used m combination with the first polymer and/or the second polymer, it preferably has a sufficiently low molecular weight to allow it to fill the gaps between the first polymer and/or second polymer on the substrate.
• An advantage to filling gaps between other polymers is increasing the density of charges in the microorganism filtration media.
• An exemplary polymer which can be used as the third polymer can be prepared from polyethyle mme (PEI). In general, polyethylemmme includes repeating units having the following formula:
• Preferred polyethylemmme polymers have an n value of between about 5 and about 500,000 and, more preferably between about 10 and about 100,000.
• the polyethylemmme polymer preferably has a number average molecular weight of between about 300 and about 1,000,000.
• the polyethylemmme polymer can be reacted with a cross-linking agent so that it will react with the substrate and become covalently bonded to the substrate and/or to the other polymers covalently bonded to the substrate.
• An exemplary crosslmking agent includes bifunctional crosshnkmg agents such as the diglycidyl ether of 1,4-butaned ⁇ ol. Di-epoxy crosshnkmg agents are preferred because they provide an epoxy group which can react with an ammo group m the polymer, and another epoxy group which can react with the substrate (such as , glass fiber).
• the polyethylemmme polymer with between about 5 wt. % and about 60 wt. % crosshnk g agent, and preferably between about 20 wt % and about 50 wt %.
• the third polymer differs from the first and second polymers in that it is a branched spherical polymer offering a morphology in structure difference and can be reacted with the other polymers.
• the reaction of the third polymer with the first polymer can be provided, for example, according to the general formula:
• the reaction of the third polymer with other polymers can result in polymer covalently bonded to the substrate and having primary, secondary, and tertiary amines in different ratios for adsorption of microorganisms.
• the charge density in the filtration media can be increased relative to the charge density if only one polymer is covalently bonded to the substrate.
• the addition of a third polymer further increases the charge density. It is expected that the increased charge density provides a better level of microorganism removal for a given mass of filtration media It is believed that the charge density of a filtration media corresponds to the number of groups available for microorganism adsorption. The charge density for a microorganism filtration media can be calculated knowing the charge density of the polymer and the weight percent of polymer on the substrate.
• the amount of polymer provided on the substrate is, on a dry basis, between about 0.05 wt. % and about 20 wt. %, and more preferably between about 0.3 wt. % and about 10 wt. %.
• Desirable polymers which can be reacted to the substrate include polymers having a charge density of between about 0.1 milhequivalent/gram and about 100 milhequivalent/gram.
• the charge density of the polymer is at least about 1 milhequivalent/gram.
• the resulting filtration media preferably has a charge density of at least about 0.001 milhequivalent/gram, and preferably in the range of about 0.01 milhequivalent/gram and about 100 milhequivalent gram. It is expected that the calculated charge density will generally correspond to a charge density determined by titration.
• the polymers include reactive groups which allow them to bond to the substrate.
• Reactive groups which bond to glass include azetidmium and epoxide groups.
• the following reaction is believed to represent the covalent bonding of a polymer containing azetidmium groups to glass:
• the azetidmium groups can be obtained by reacting a secondary amme with epichlorohyd ⁇ n.
• the third polymer can be reacted to the substrate (e.g., glass fiber) as a secondary coating after reaction of the first and/or second polymer to the substrate, or before the reaction of the first and/or second polymer to the substrate. It is expected that the reaction of the third polymer with the first and/or second polymers will result in pnmary, secondary, tertiary, and quaternary amines m different ratios.
• the filtration media will be better able to capture or adsorb microorganisms having different charge charactenstics as recorded from their lso-elect ⁇ c point measured by lso-elect ⁇ c focusing method discussed in Murray, Ph.D. Dissertation, Stanford University, 1978.
• the proportion of polymers provided in the polymer composition can be varied to provide increased charge density and, therefore, increased adsorptive capacity for the filtration media.
• Each of the first polymer, the second polymer, and the third polymer can be used alone or in combination with one or more of the other polymers
• the first polymer and the second polymer are provided at a weight ratio of about 1 :9 to about 9:1, and more preferably at a weight ratio of about 1:2 to about 2:1.
• the third polymer is used in combination with the first polymer and the second polymer, it is preferably provided at a weight ratio of first and second polymer to third polymer of between about 9:1 and about 1 :9, and more preferably at between about 3:1 and about 1:1.
• the third polymer is relatively less miscible with the first and second polymers compared with the miscibihty of the first and second polymers with each other. Accordingly, when reacting the first, second, and third polymers to the substrate, it is often desirable to react the first and second polymers to the substrate, and then react the third polymer to the substrate.
• the polymer composition is preferably reacted to the substrate under conditions which maximize the coverage of the polymer composition on the substrate. It is desirable to provide as much polymer on the substrate as possible m order to increase the charge density of the filtration media.
• the polymer composition is applied to the substrate m an aqueous bath. In general, it is preferable to provide the aqueous bath with a solids content of between about 0.1 wt. % and about 10 wt. %, and more preferably between about 1.0 wt. % and about 7 wt. %.
• the first and second polymers can be applied together, followed by application of the third polymer, the first and second polymer can be applied in an aqueous bath containing a weight percent solids of between about 0.1 and about 10, and then the third polymer can be applied in an aqueous bath containing a solids content of between about 0.1 and about 10.
• the polymers can be applied sequentially these same solids concentrations
• the substrate is contacted with the polymer bath for a sufficient amount of time to wet the surface of the substrate with the polymer. In general, sufficient wetting usually takes place withm about one second to about ten minutes after the substrate is contacted with the polymer bath.
• the polymer can be applied to the substrate by dipping the substrate into an aqueous bath, it should be appreciated that alternative techniques for applying the polymer to the substrate are available.
• the polymer can be applied as a spray to the substrate.
• the solids concentrations can be similar to those found in the desc ⁇ ption of application by aqueous bath.
• other solids concentrations can be utilized.
• the wetted substrate is dried and the polymer is allowed to react with the substrate and with other polymer present on the substrate.
• the wetted substrate is placed m an oven at between about 150° F and about 400° F to vaponze the water present and to d ⁇ ve the reaction of the polymer.
• the polymer- coated substrate is heated in a convective oven at a temperature between about 150° F and about 400° F for between about 1 minute and about 30 minutes. If desirable, the polymer-coated substrate can be allowed to d ⁇ p dry pnor to heat treatment.
• the pH of the polymer bath can be adjusted to accelerate the reaction.
• the pH is between about 5 and about 11, and more preferably between about 7 and about 9.
• the alkalinity serves to activate the glass fibers and additionally acts as a catalyst to accelerate reaction of the polymer on the glass fibers.
• microorganism removal coefficient is useful to evaluate the effectiveness of a filter for removing microorganisms from water.
• the equation and technique for determining the microorganism removal coefficient is desc ⁇ bed m example 9.
• microorganism filtration media according to the invention provide a microorganism removal coefficient of at least about 10 ml/g-sec.
• the microorganism filtration media according to the invention provide a microorganism removal coefficient of greater than about 500 ml/g-sec and more preferably greater than about 1,000 ml/g-sec.
• the microorganism removal coefficient is about between 100,000 and about 10,000,000 ml/g-sec.
• microorganism filtration media according to the invention can be utilized in many filter applications for providing virus removal from water.
• Exemplary environments include the filtration of water to provide dnnkmg water.
• Commercially available devices which are commonly used to filter municipal water can be characte ⁇ zed as faucet mounted filters and pour through filters.
• Portable filters are additionally available and can be used, according to the invention, for filtering river, stream, and/or lake water to provide dnnkmg water.
• a faucet mounted filter according to the invention is shown at reference numeral 10.
• the faucet mounted filter 10 is shown attached to a faucet 12 for treatment of household water.
• the faucet mounted filter 10 includes housing 20 which includes upper portion 22 and cap 24 which threads into upper portion 22.
• a first O-ring 26 is provided in channel 28 to create a water tight seal between upper portion 22 and cap 24.
• Replaceable filter cart ⁇ dge 40 is inserted into upper portion 22 from below, and cap 24 is threaded to upper portion 22 to secure cartridge 40 m housing 20.
• the cartridge 40 includes layers of filtration media 72 and 74 and carbon block 76.
• the layers of filtration media 72 and the layers of filtration media 74 are shown as a wrap of two layers of filtration media. It should be appreciated that the filtration media can include one layer or several layers of filtration media.
• the cartridge 40 can be provided with filtration media 72 but without filtration media 74, and vice versa.
• Support tube 70 is provided to hold the filtration media 72 relative to the carbon block 76.
• the support to 70 is preferably a porous tube which does not substantially rest ⁇ ct the flow of water therethrough, but supports the filtration media 74.
• the filtration media 72 and 74 and the carbon block 76 are preferably adhered together at the bottom and the top of the cartridge and to the top cap 62 and the cart ⁇ dge base 64 with adhesive
• the cart ⁇ dge 40 is shown with a carbon block 76, it should be understood that the carbon block can be replaced with another type of filter if the carbon block is not desired for a particular application. For example, it may be advantageous to replace the carbon block 76 with a pleated filtration media according to the invention.
• the flow of water through the cart ⁇ dge 40 can be diverted by rotating the housing 20 along the direction of the arrow shown m Figure 1.
• the valve body 30 attaches to the faucet 12 via threaded mounting member or nut 80 having threads 81.
• a retainer ring 82 is attached to valve body 30 so that the mounting member 80 is free to rotate.
• a washer 83 seals the retainer ⁇ ng 82 to the end of the faucet 12.
• the body retainer 87 holds the valve body onto the stem 91, and allows rotation of the housing relative to the valve body 30 along the direction of the arrow in Figure 1.
• the flow of water can be diverted to the filter or alternatively to the aerator 88 and outlet 84. Additional O-nngs 95 are provided to reduce leakage.
• the faucet mounted filter 100 includes many of the features identified m the faucet mounted filter 10. Water flows through the mlet opening 121 and into the annular space 102 between the housing 120 and the inner housing 104. The water then flows into the top channel 106 provided between the housing top 108 and the inner housing top 110. The water then flows through the passage 112 and into the inner annular channel 114 provided between the cart ⁇ dge 140 and the inner housing 104. The flow of the water through the cartridge 140 is similar to that descnbed above with respect to Figure 2.
• An advantage of the arrangement shown in Figure 3 is that the filter cartridge 140 and inner housing 104 serve to provide a more convenient replacement filter 130. Accordingly, the replacement filter 130 can easily be removed from the faucet mounted filter 100 by detaching the cap 124 from the upper portion 122, removing the used filter and introducing a new filter, and screwing the cap 124 to the upper portion 122.
• An advantage is that a single O- ⁇ ng 126 can be provided m the housing 120 between the filter 130 and the upper portion 122.
• a faucet mounted filter which can be modified to include the filtration media of the invention includes the faucet mounted filter descnbed in U.S. Patent No. 5,525,241, the disclosure of which is incorporated herein by reference m its entirety.
• a pour through filter cartridge is shown at reference numeral 200.
• the pour through filter cartridge 200 can be placed in a conventional carafe type filtration reservoir. These types of filtration reservoirs are available commercially from Recovery Engineering, Inc. and B ⁇ tia.
• the pour through filter cartridge 200 includes an outer shell 202 and an interior region 203 which includes a filter 205.
• the filter 205 includes a pleated filtration media 204 which is glued to the outer shell 202 with hot melt adhesive 206.
• a bottom cap 208 is glued to the bottom of the filtration media 204 by hot melt adhesive 209. Openings 212 are provided to allow water to exit the pour through filter cartridge 200.
• Loose media 220 such as granular carbon and/or ion exchange resm, can be placed in the mside the mte ⁇ or region 203 as part of the cartridge 200.
• a slotted cover 222 can be fastened to the top of the outer shell 202 to contain the loose media
• a separate cylinder of filtration media 224 can be wrapped outside of the pleated media 204
• a seal 230 is provided to prevent water from bypassing the cartridge 200. Accordingly, water provided in the upper region of a conventional carafe type filtration reservoir will flow through the opening 240 and into the interior region 203 of the cartridge 200. The water then flows through the filter 205 which includes the loose media 220 and outward through the filtration media 204 and 224 (if present) and exits through openings 242.
• the pleated filtration media 204 and the wrapped filtration media 224 are preferably provided from the polymer treated filtration media according to the invention.
• Polymer A is a secondary ammo based azetidmum type polymer. This polymer has a secondary amme inserted in polymeric amide groups and will be further reacted with epichlorohyd ⁇ n to form azetidium groups for cross-linking to hydroxyl or ammo groups as disclosed in U.S. Patent 2,926,154 and 2,926,116.
• Polymer B is a tertiary amme based epoxide type polymer formed by radical initiated polyme ⁇ zation of alkyl dialkyamme typically methyl dialkyl amme (MDAA).
• the tertiary amme can react with epichlorohyd ⁇ n to form glycidyl quaternary ammonium polymers, that can be stabilized as their chlorohyd ⁇ n form. They have been charactenzed as alkaline cunng wet strength resms. See U.S. patents 3,700,633, 3,772,076, 3,833,531.
• the above two polymers are compatible and can be mixed in different proportions and diluted to the required concentration with water, then alkaline adjusted to pH about 9.0 for dip coating the glass fiber media.
• Cross-linking reaction will start as soon as water molecules are removed from the media dunng drying.
• the polymenc coating in this case is the mixture of secondary, tertiary and quaternary in different proportion with their charge strength m pH range shown in Figure 6
• Both polymers A and B provide a charge density of about 3.0 milliequivalence/gram. However, we found it is the molecular structure differences and the location of charge sites maximizes their interaction toward microorganisms.
• the polymer reacted to the glass fiber should be provided in an amount which does not substantially interfere with the flow properties of the filtration media, but which provides a desired level of microorganism adsorption.
• it is desirable that the polymer is covalently bonded to the substrate so that polymer remains with the substrate and does not leech into the water or liquid which is being filtered. In general, it is desirable to provide enough polymer on the substrate to provide microorganism adsorption, but not use too much polymer to substantially restnct flow through the filtration media in its intended application
• Assay technique - MS-2 has no membranes and behaves very much like a small protem-DNA complex molecule, thus are quite stable in water over a wide range of temperatures.
• MS-2 are assayed according to the procedure by Hurst, C, "Appl. Environ. Microbiol. 60:3462 (1994).
• the bacteriophages and corresponding bacterial host strains used m this study were as follows: MS-2 (ATCC 15597-Bl) and its host Escherichia Coli C-3000 (ATCC 15597) were purchased from Ame ⁇ can Type Culture Collection, Rockville, Maryland.
• the basic medium used for propagation of host bacte ⁇ a were modified LB medium (medium 1065 ATCC). Bacteriophage plaque formation assays were performed in 10-cm diameter pet ⁇ plates, using the traditional double layer agar technique.
• the bottom agar layer consisted of LB medium containing 1% agar (Bacto agar, Difco).
• the top agar layer was based on LB medium containing 0.8% agar.
• the top agar layer of each plate consisted of 3 ml of top agar medium; 1 ml of MS2 diluted in LB medium; and 0.2 m. of a fresh culture of bacte ⁇ al host m LB medium Inoculation of the assay plates to allow plaque formation was performed for 16 hours 37°C. Viral titers were calculated as PFU (plaque forming unit) per ml of the diluted bacte ⁇ ophage.
• the E-Coh grown in proper conditions will have receptors that strongly attract MS-2 to form plaques. High accuracy can only be achieved m the proper ratio of the nght amount of MS-2 to E-Coh.
• Example 1 Effect of Virus Adsorption with Change in Virus Concentration and Polymer Coating
• Influent water containing bacteriophage MS-2 virus of 28 nm at concentrations of 2 x 10 9 , 8 x 10 7 , and 2 x 10 6 PFU/ml were passed through two layers of filtration media.
• the layers of filtration media can be charactenzed as type A filtration media (A), type B filtration media (B), mixed type A and B filtration media (AB), and sequentially applied type A and B filtration media (A then B).
• the mixed type A and B filtration media can be prepared by reacting a mixture of polymers A and B onto the filtration media to provide the AB filtration media. By reacting the A polymer onto the reaction media and then reacting the B polymer onto the reaction media, the A then B filtration media is produced.
• Type A filtration media was prepared by providing a web of glass fiber (grade 151 from Ahlstrom Technical Papers) and reacting a secondary amme based azetidmium polymer to the web of glass fiber.
• the secondary amme based azetidmium polymer has the following formula:
• the secondary amme based azetidmium polymer has a number average molecular weight of about 1,000,000 and is available in water at solid weight percent of 30% and a pH of between four and five. This polymer is referred to herein as the A polymer.
• the type B filtration media was prepared by reacting a tertiary amine based epoxide polymer to the web of glass fiber.
• the glass fiber used was grade 151 glass fiber from Ahlstrom Technical Papers.
• the tertiary amme based epoxide polymer has the following structure-
• the tertiary amme based epoxide has a number average molecular weight of about 1 ,000,000, and is available in water having a solid weight percent of about 20% and a pH of between four and five.
• This polymer is referred to herein as the B polymer.
• the AB filtration media was prepared by reacting a mixture of A polymer and B polymer to a web of grade 151 glass fiber from Ahlstrom Technical Papers.
• the A then B filtration media was prepared by reacting polymer A to a web of grade 151 glass fiber available from Ahlstrom Technical Papers. Once the polymer A has reacted to the glass fiber, polymer B is then reacted to the glass fiber.
• the filtration media identified in Table 1 refers to the weight percent of polymer provided in the polymer bath that was used to prepare the filtration media.
• the filtration media was prepared by providing a polymer bath having the indicated weight percent of polymer A and or B identified in Table 1 as a solids weight percent. The glass fiber was then immersed m the polymer bath. Once the glass fiber was determined to be fully wetted, it was removed and allowed to drip dry for approximately five minutes, and then placed in a convective oven at 300° F for approximately six minutes. The weight percent solids was altered for the samples The weight percent solids in the polymer bath is reported m the second column of Table 1. For example, the filtration media of sample number 1 was prepared from a bath including 1.5 wt.
• sample number 2 was prepared from a polymer bath including 3.0 wt. % polymer A.
• the ratio of polymer A to polymer B is 1 :1 on a weight basis.
• the flow rate of bacteriophage MS-2 virus through the filtration media was controlled at 200 ml/mm.
• the filtration media was cut to a 47 millimeter disc and placed m a 47 millimeter membrane filter holder.
• the pressure drop across the filter is less than 5 psi, and the effective filter surface area is approximately 12.5 cm 2 .
• the estimated contact time is about 0.1 seconds assuming 50% media porosity.
• the pH of the influent was maintained at about 9.
• sample numbers 1-4 show that the polymer concentration effect plateaus off at about the 6% level, and preferably at the 3% level.
• the type B filtration media is slightly better on capturing the virus than the type A filtration media. The best result can be seen in sample number 6 of 1 :1 weight ratio mixture of polymers A and B.
• the double coating process by coating a second layer of type B resm after type A prove to be advantageous as shown in sample number 5.
• the data demonstrates a relationship between charge density, virus concentration, and contact time requirement.
• the filtration media is relatively effective m removing virus of lower concentration around 10 6 PFU/ml by even a single polymer coating whereas a mixed polymer coating or longer contact time is advantageous for the removal of 10 9 PFU/ml virus to achieve results of higher than 4 log reduction.
• polymer C The adsorptive properties of filtration media including a third polymer (polymer C) was compared to that of filtration media including polymer A and filtration media including polymers A and B.
• Polymer C was prepared from a polyethylemmme (PEI) polymer have the following structure:
• the polyethylemmme polymer was provided having a number average molecular weight of 800 and in a water solution at a solids weight percent of 98%
• One part PEI polymer was emulsified (under strong mechanical agitation) with 0.5 part diglycidyl ether of 1 ,4-butaned ⁇ ol and allowed to form a colloidal solution.
• the polymer was then diluted to 1 wt. % solids to provide polymer C.
• Polymer C was applied to glass fiber according to the technique described in Example 1.
• the filtration media identified by sample numbers 9 and 10 in Table 2 were prepared by reacting polymer C onto AB filtration media.
• the polymer concentration used to form the filtration media are identified in Table 2. It should be understood that for sample numbers 9 and 10, polymers A and B were reacted to the glass fiber, then polymer C was reacted.
• Example 2 The procedure of Example 1 was repeated for the samples identified in Table 2. The flow rate of filtrate was provided at 200 ml/mm through two layers of filtration media. The contact time was approximately 0.165 seconds and the volume filtered was 500 ml. The results are reported in Table 2.
• Sample numbers 9 and 10 demonstrate the additional contribution of using a third polymer as a second coating. It is believed that polymer C patches the gaps between the large molecules (polymers A and B).
• This example illustrates the relationship between the adsorption time and the virus removal efficiency.
• the amount of filtration media and the flow rate are factors affecting the virus adsorption time.
• the efficiency of virus adsorption increases with increasing adsorption time by either reducing the flow rate or increasing the amount of filtration media.
• the general procedures identified in the above examples were followed while varying the contact time. It should be understood that the contact time is the time the filtrate is contact with the filtration media. Accordingly, the thickness or number of layers of filtration media and the flow rate were vaned to alter contact time. The results are reported in Table 3.
• sample numbers 1 and 2 are the results of testing conducted on one filtration media.
• Sample numbers 3-5 were the result of test conducted on another filtration media.
• Example 4 Effect of AB Concentration on MS-2 Removal This example illustrates the viral removal capability as a function of charge density of AB mixture on filtration media.
• the filtration media was prepared according to the general technique described in Example 1.
• the polymer bath was prepared from polymer A and polymer B provided at a 1 :1 wt. ratio at the weight percent solids identified in Table 4 for each of the samples.
• the glass fiber used was grade 151 glass fiber from Ahlstrom Technical Papers.
• the filtration media tested has a surface area of 12.5 cm 2 and thickness of 0.044 cm.
• the flow rate was 500 ml/mm and the contact time was 0.033 seconds
• Table 4 The results of this example are reported in Table 4.
• Virus breakthrough point is the level at which virus adsorption onto the filtration media no longer occurs at desirable levels. That is, it is believed that the sites for binding the virus have become tied up or saturated, and the virus begins flowing through the filtration media rather than being adsorbed onto the filtration media.
• This example demonstrates the effect of virus concentration on filter breakthrough point. It should be appreciated that the breakthrough point refers to the point where the filter starts to show the failure on capturing the organism. It differs from the previous Example 4 in that the capacity may not be fully utilized yet the efficiency on captu ⁇ ng the microorganism decreases due to loss in number of active sites.
• the samples were prepared according to Example 1.
• One layer of filtration media was subjected to a flow rate of 200 ml/mm which resulted in a contact time of 0.082 seconds
• the filtration media tested was prepared from grade 151 glass fiber available from Ahlstrom Technical Papers, and a bath containing 1.5 wt % A polymer and B mixed polymer wherein A polymer and B polymer were mixed at 50/50 ratio then reacted to 151 glass fiber.
• This example is provided to show the effect of filter porosity on virus absorption
• glass filter media having grade 164 and 151 from Ahlstrom Technical Papers were compared.
• the filtration media was prepared according to the technique descnbed m Example 1 where the polymer bath includes 1.5 wt % of polymer A and polymer B provided at a weight ratio of 1 : 1.
• the filtration media was provided as a single layer having a thickness of 0.04 mm and a surface area of 12.5 cm 2
• the flow rate through the filtration media was 500 ml mm and the contact time was 0.033 seconds
• Sample numbers 1-8 were prepared from glass fibers having grade 164.
• Sample numbers 9-15 were prepared using glass fibers having grade 151. The results of this example are reported in Table 6.
• Media grade 164 being relatively larger in pore size than that of 151 was found to be less effective on MS-2 adsorption under identical testing conditions. It is believed that the reduced effectiveness m microorganism captu ⁇ ng by filters of relatively larger pores can be compensated by providing a thicker media (i.e., more layers) or by cross-linking with more charged groups to improve the contact efficiency between the microorganism and their adsorptive groups on the filtration media.
• This example evaluates the performance of filtration media including polyethylemmme containing polymer (polymer C) in addition to the presence of polymers A and B.
• the glass fiber used was grade 151 from Ahlstrom Technical Papers.
• the technique for providing the polymer on the glass fiber was provided according to the technique descnbed in Example 2. The test was run at a flow rate of 1,000 ml/mm through two layers of filtration media to provide a contact time of 0.033 seconds. The results of this example are reported in Table 7.
• Table 7 The Effect of Third Polymer MS-2 Adsorption
• Heloxy 67 diepoxide from Shell Oil Co. was used to cross link the polyethylemmme grade FG (molecular weight 800) from BASF with the glass fiber.
• the coating solution of 1.5% by wt. concentration of polymer C provides substantially no change in liquid flow through the filtration media while improving the microorganism removal capacity significantly.
• polymer C is advantageous because of its low viscosity and its ability to provide additional charge contnbution on the filtration media without significantly reducing flow through the filtration media.
• This example demonstrates the effectiveness of the filtration media of the invention for absorbing bacteria.
• the test organism used for assessment of removal were, K.t., Klebsiella terngena (ATCC-33257). E.c, E coli (ATCC-15597) and B.d., Brevundomas diminuta (ATCC-11568). They were all prepared by overnight growth in LB broth (medium 1065 ATCC) to obtain the organism in the stationary growth phase The average bacte ⁇ a titer is around lxl 0 9 CFU/ml. Microbial challenges of specific concentration were prepared by adding the fresh cultured bacteria to de-ionized water at pH 9.0.
• the pet ⁇ film aerobic count plate from 3M has also been used m assaying three different types of aerobic bacte ⁇ um.
• the plate is a ready made culture medium system that contains standard nutnents, a cold water soluble gelling agent, and a tetrazo um indicator that facilitates colony enumeration.
• One ml samples are dispersed on the plate and the plate is incubated at 35°C for 48 hours The number of visible colonies will then be expressed in CFU/ml.
• the filter media applied for bacte ⁇ a removal utilizes a relatively open porosity of grade 164. Same procedure on cross-linking the polymers to grade 151 were applied to grade 164. Three different types of commonly known bacteria in water, Kt, Bd and Ec were dispersed in d.i. water at pH 9 as source of challenge respectively. The filfration was performed according to the conditions specified in Tables 8-1 through 8-3. After filte ⁇ ng a specific volume of bacte ⁇ a containing water, the filtrants were collected m a test tube. All three different types of bacteria were assayed by mixing 1 ml of the diluted filtrant with 10 ml Tryptic soy agar (TSA) and following the pour plate assay procedure.
• TSA Tryptic soy agar
• Glass fiber used in this example is grade 164 from Ahlstrom Technical Papers
• the results of this example are reported in Tables 8-1, 8-2, and 8-3 for K.t., E.c, and B.d., respectively.
• This example demonstrates the effectiveness of the filtration media of the invention for removing different species of bacteria from water.
• Polymer B' is a tertiary amme based epoxide type polymer formed by polymerizing methyl bis (3-ammo propyl amme) (MBAPA) with dicarboxylic acid as described in U.S. Pat. Nos. 4,537,657 and 4,501,862.
• MBAPA methyl bis (3-ammo propyl amme)
• the charge interaction between the chemical functional groups on the filtration media and the surface of the microorganism is considered a major force for removing microorganisms from the water. Therefore, the virus adsorptivity by the filter is expected to be directly related to the available charge density provided on the filtration media.
• the higher the charge density the higher the number of charged groups available for microorganism adsorption.
• the charge density of polymers A and B are 3 milh-equivalent per gram according to the polymer supplier.
• the estimated charge density per gram of filtration media are calculated and reported m Table 9 based upon the weight of polymer reacted on the media. In order to correlate the charge density with the microorganism removal capacity, we adopted the microorganism removal coefficiency as an index number.
• a useful index of microorganism removal coefficient is adapted from Kawabata, et al., Applied and Environmental Microbiology 46, pages 203-210, 1983. This index is available to evaluate the effectiveness of the filter on microorganism removal.
• the relation of the loganthm of viral microorganism counts to contact time can be characterized as generally linear m the early stage of contact which indicates the process follows first order rate.
• the removal coefficient as follows:
• N 0 is the initial number of microorganisms counts expressed m CFU/ml for bacte ⁇ a and PFU/ml for MS-2 virus
• N is the number of counts at contact line t
• V is the volume filtered
• W is the dry weight of filter material applied in filtration
• t is the contact time which are roughly estimated from the total volume of filter material divided by the flow rate and by assuming 50% porosity in filters.
• the MS-2 removal coefficient is calculated by passing 1 to 4 liters of water at pH 9 containing 1.8 x 10 6 PFU/ml of MS-2 through one layer of filtration media prepared from 151 glass fiber and polymeric AB mixture in different charge density at 100 ml/mm.
• the data is taken from example 4.
• the MS-2 removal coefficient calculated based on the above number are tabulated in Table 9 and expressed in ml/g-sec.
• the relationship between the charge density and MS-2 removal coefficient is shown in Table 9. It is believed that the decrease in virus removal coefficient with increasing volume of virus containing water passing through the filtration media is due to the gradual loss of active sites occupied by virus adsorption. The high charge density with more active groups are available for capturing the virus show less reduction in removal coefficient.
• the microorganism removal coefficient calculated based upon filter weight, contact time, volume filtered and microorganism concentration serves as a valuable index for identifying the extent of chemical functional groups provided in the filtration media.
• test water type No. 2 In order to satisfy the performance requirements of a "microbiological water punfier,” filtration media were tested in test water type No. 2 according to the "Guide Standard and Protocol for Testing Microbiological Water Punfiers" published by EPA in 1987. This water is intended for the stressed challenge phase of testing where units involve halogen disinfectant and was constituted with chemical and physical charactenstics as follows:
• TDS Total dissolved solid
• test was run similar to example 1 except for the use of a PUR® HikerTM filter cart ⁇ dge available from Recovery Engmeenng, Inc. as a pre-filter to avoid premature clogging caused by the A.C. fine dust particles.
• the granular activated carbon in the pre-filter was removed for this test.
• the interference caused by the added TOC and TDC in type no. 2 water on efficiency of microorganism reduction is quite obvious from the testing results.
• An additional layer of filter media has to be added in order to compensate the loss of charge sites or charge weakening due to the presence of sea salt and humic acid in EPA specified type 2 test water
• the humic acid in type 2 water was found to be also adsorbed by the filter mat ⁇ x.
• the competitive adsorption of both humic acid and virus toward the charge sites in the filter results in reduction in virus adsorption capacity, as shown m Table 10.
• Sample 5-7 demonstrate the using of combined A and B polymers for MS-2 adsorption in the presence of humic acid as competing molecules. Only through the use of A and B mixed polymer at higher concentration, we will be able to provide sufficient number of charge sites to satisfy the adsorption for both humic acid and microorganisms, as shown m Samples 8 to 11.
• Filtration media were tested by extraction tests to evaluate the amount of polymer which leaves the filtration media.
• the extraction tests were performed by soaking two grams of filtration media in 250 ml nifrogen free water for two hours at room temperature.
• a sample of extractant was digested using the persulfate method as described in "standard method for the examination of water and waste water," edited by Eaton et al., Apha, Washington, D.C.
• the method utilizes alkaline oxidation at 100°C to 110°C to convert nitrogen to nitrate. Total nitrogen is then determined by analyzing the nitrate using a Hach DR-700 colonmeter. The results are expressed as amount of nitrogen (ppm) in extracted water.
• the filtration media tested are identified below and m Table 11. The amount of nitrogen provided as a result of the extraction tests for each filtration media is provided in Table 11.
• All filtration media were prepared from grade 151 glass fiber available from Ahlstrom Technical Papers.
• the glass media was dipped into a polymer bath having the weight percent solids identified in Table 11. When two polymers were provided in the polymer bath, the polymers were provided at a weight ratio of 1 :1.
• Sample number one was prepared from a polymer bath including 3% by weight polymer A and polymer B'.
• Sample number 2 was prepared from a polymer bath including 1.5 wt. % polymer A and polymer B'.
• Sample number 3 was prepared from a polymer bath including 3.0 wt. % polymer B'.
• Sample number 4 was prepared from a polymer bath including 3.0 wt. % of a polymer similar to B' but without azitidium groups.
• Sample number 5 was prepared from a polymer bath including 3.0 wt. % polyethylemmme.
• Sample number 6 was prepared from a polymer bath including 3.0 wt. % of a polymer similar to polymer A but without azitidium groups.
• the filtration media were dried and cured at a temperature of 300° F for six minutes.
• sample numbers 4-6 it is believed that the polymers did not react to the glass fiber.
• the polymers in sample numbers 1-3 did react to the glass fiber by covalent bond.
• the extractables or leachables from the filter media are the functions of polymer concentrations, the type of cross-linker in polymer structure as well as the conditions of cross- linking. Polymers without a cross-linker are also expected to be adsorbed on glass fiber surface simply through charge interactions only without forming covalent-bond, especially when the silica on glass fiber surface are ionized m alkaline conditions.
• a standard pour-through type filter (PUR Plus produced by Recovery Engmee ⁇ ng, Inc) was modified and tested.
• the filter contains a pleated non-woven glass media, similar to the Ahlstrom 164 cited earlier examples, except that the media has a more open porosity, a binder, and laminated outer layers.
• This media was treated with 1.5% AB polymer mixture in the manner as before.
• sample number 1 two pleated polymer treated filtration medias were assembled series in the filter.
• This filter is tested by filling the upper reservoir with 1.25 liters of challenge water, and collecting a sample of the water after 1 liter has passed through the filter. This first liter requires approximately 5 minutes to pass through the filter, which is a typical rate of flow for this type of product in the market.
• a faucet-mount type filter (PUR Plus produced by Recovery Engineering, Inc.) was modified and tested.
• the filter contains a molded filter element consisting primarily of powdered activated carbon. This element is normally 2" outer diameter, with a 5/8" inner diameter and 2.5" long (right circular cylinder with a hole in the middle).
• the filter element was modified to have an outer diameter of 1.82 inches and then wrapped with a 24" long, 2.5" wide piece of 151 media treated with 1.5% AB resin. This wraps the block with four layers of the virus removal media.
• This filter is tested by pumping water at pH 9.0 with viruses through the filter at 60 psi.
• the table above summarizes the conditions and results. The results show the ability of a practical faucet mount filter to remove viruses in water even at very high concentrations (test 1 and 2). When the concentration is dropped (test 3), the capacity of the filter is very high, showing no sign of breakthrough after 80 gallons.

Landscapes

• Health & Medical Sciences (AREA)
• Life Sciences & Earth Sciences (AREA)
• Chemical & Material Sciences (AREA)
• Epidemiology (AREA)
• Animal Behavior & Ethology (AREA)
• General Health & Medical Sciences (AREA)
• Public Health (AREA)
• Veterinary Medicine (AREA)
• Engineering & Computer Science (AREA)
• Medicinal Chemistry (AREA)
• Biomedical Technology (AREA)
• Molecular Biology (AREA)
• Hydrology & Water Resources (AREA)
• Environmental & Geological Engineering (AREA)
• Water Supply & Treatment (AREA)
• Organic Chemistry (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Filtering Materials (AREA)
• Solid-Sorbent Or Filter-Aiding Compositions (AREA)
• Biological Treatment Of Waste Water (AREA)
• Water Treatment By Sorption (AREA)
• Polyamides (AREA)
• Separation Using Semi-Permeable Membranes (AREA)

Priority Applications (8)

Applications Claiming Priority (2)

Publications (1)

Family

ID=23409283

Family Applications (1)

Country Status (15)

Cited By (23)

Families Citing this family (75)

Citations (4)

Family Cites Families (58)

• 2000
  • 2000-07-20 EP EP00947568A patent/EP1198257A1/en not_active Withdrawn
  • 2000-07-20 CN CNB008105987A patent/CN1213769C/zh not_active Expired - Fee Related
  • 2000-07-20 JP JP2001511973A patent/JP2003505227A/ja not_active Withdrawn
  • 2000-07-20 CA CA002379565A patent/CA2379565A1/en not_active Abandoned
  • 2000-07-20 TR TR2002/00141T patent/TR200200141T2/xx unknown
  • 2000-07-20 BR BRPI0012609-8A patent/BR0012609B1/pt not_active IP Right Cessation
  • 2000-07-20 WO PCT/US2000/019787 patent/WO2001007090A1/en not_active Application Discontinuation
  • 2000-07-20 KR KR1020027000883A patent/KR20020029669A/ko not_active Application Discontinuation
  • 2000-07-20 MX MXPA02000795A patent/MXPA02000795A/es active IP Right Grant
  • 2000-07-20 AU AU61150/00A patent/AU6115000A/en not_active Abandoned
  • 2000-07-24 PE PE2000000738A patent/PE20010422A1/es not_active Application Discontinuation
  • 2000-07-31 US US09/628,632 patent/US6565749B1/en not_active Expired - Lifetime
  • 2000-10-24 TW TW089114629A patent/TW458785B/zh not_active IP Right Cessation
• 2002
  • 2002-01-18 MA MA26490A patent/MA25686A1/fr unknown
  • 2002-09-26 HK HK02107136.8A patent/HK1046649A1/zh unknown

Patent Citations (4)

Also Published As

Similar Documents

Legal Events