WO2000073239A1 - Verfahren zur herstellung keramischer grünkörper - Google Patents
Verfahren zur herstellung keramischer grünkörper Download PDFInfo
- Publication number
- WO2000073239A1 WO2000073239A1 PCT/DE2000/001588 DE0001588W WO0073239A1 WO 2000073239 A1 WO2000073239 A1 WO 2000073239A1 DE 0001588 W DE0001588 W DE 0001588W WO 0073239 A1 WO0073239 A1 WO 0073239A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- starting material
- extruder
- organic
- ceramic
- ceramic green
- Prior art date
Abstract
Description
Claims