WO1999041797A1 - Accumulateur aux ions lithium - Google Patents

Accumulateur aux ions lithium

Info

Publication number
WO1999041797A1
WO1999041797A1 PCT/JP1998/000608 JP9800608W WO9941797A1 WO 1999041797 A1 WO1999041797 A1 WO 1999041797A1 JP 9800608 W JP9800608 W JP 9800608W WO 9941797 A1 WO9941797 A1 WO 9941797A1
Authority
WO
WIPO (PCT)
Prior art keywords
active material
separator
electrode
negative electrode
positive electrode
Prior art date
Application number
PCT/JP1998/000608
Other languages
English (en)
Japanese (ja)
Inventor
Kouji Hamano
Yasuhiro Yoshida
Michio Murai
Takayuki Inuzuka
Hisashi Shiota
Shigeru Aihara
Daigo Takemura
Jun Aragane
Hiroaki Urushibata
Original Assignee
Mitsubishi Denki Kabushiki Kaisha
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsubishi Denki Kabushiki Kaisha filed Critical Mitsubishi Denki Kabushiki Kaisha
Priority to PCT/JP1998/000608 priority Critical patent/WO1999041797A1/fr
Publication of WO1999041797A1 publication Critical patent/WO1999041797A1/fr

Abstract

La présente invention concerne un accumulateur aux ions lithium dans lequel un pôle négatif et un pôle positif adhèrent de façon étanche à un séparateur sans boîtier d'emballage extérieur solide et sans qu'augmente la résistance entre les pôles, lequel accumulateur présente une haute densité d'énergie, peut être fabriqué sous n'importe quelle forme, notamment sous forme d'élément mince, et possède d'excellentes caractéristiques de charge et de décharge. L'accumulateur aux ions lithium comprend une électrode laminée composée: d'un pôle positif (3) que l'on forme en assemblant une couche de matière active de pôle positif (32) et un collecteur de courant de pôle positif (31); d'un pôle négatif (5) que l'on forme en assemblant une couche de matière active de pôle négatif (52) et un collecteur de courant de pôle négatif (51); d'un séparateur (4) placé entre la couche de matière active de pôle positif (32) et la couche de matière active de pôle négatif (52); et d'une résine adhésive (6) qui est placée dans certaines parties d'un espace formé entre chaque couche de matière active (32,52) et le séparateur (4), de façon que sont formés des espaces (7) qui relient chacune des couches de matière active (32,52) au séparateur (4). Un électrolyte contenant des ions lithium est retenu dans les espaces (7), le séparateur (4), la couche de matière active de pôle positif (32) et la couche de matière active de pôle négatif (52). Cette structure permet de faire adhérer de façon étanche les couches de matière active au séparateur grâce à la résine adhésive seule, sans qu'il soit nécessaire d'utiliser un boîtier d'emballage extérieur. L'électrolyte est retenu dans les espaces formés entre les régions de résine adhésive, ce qui permet d'assurer une bonne conduction d'ions entre les matières actives des pôles positif et négatif et le séparateur.
PCT/JP1998/000608 1998-02-16 1998-02-16 Accumulateur aux ions lithium WO1999041797A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PCT/JP1998/000608 WO1999041797A1 (fr) 1998-02-16 1998-02-16 Accumulateur aux ions lithium

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/JP1998/000608 WO1999041797A1 (fr) 1998-02-16 1998-02-16 Accumulateur aux ions lithium

Publications (1)

Publication Number Publication Date
WO1999041797A1 true WO1999041797A1 (fr) 1999-08-19

Family

ID=14207614

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP1998/000608 WO1999041797A1 (fr) 1998-02-16 1998-02-16 Accumulateur aux ions lithium

Country Status (1)

Country Link
WO (1) WO1999041797A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2016535923A (ja) * 2013-11-04 2016-11-17 エルジー・ケム・リミテッド 二次電池用接着層の形成方法
CN107431187A (zh) * 2015-03-17 2017-12-01 株式会社Lg化学 具有多孔粘合剂涂层的电极及其制造方法和包括该电极的锂二次电池

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS628471A (ja) * 1985-07-04 1987-01-16 Matsushita Electric Ind Co Ltd 空気ボタン電池
JPS6341864U (fr) * 1986-09-03 1988-03-18
JPS63184560U (fr) * 1987-05-19 1988-11-28
US5437692A (en) * 1994-11-02 1995-08-01 Dasgupta; Sankar Method for forming an electrode-electrolyte assembly
JPH09500485A (ja) * 1993-11-30 1997-01-14 ベル コミュニケーションズ リサーチ，インコーポレイテッド 電解質活性可能なリチウムイオン再充電可能電池セルおよびその製造方法
JPH09293518A (ja) * 1996-04-26 1997-11-11 Asahi Chem Ind Co Ltd 薄膜状電解質および該電解質を用いた電池

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS628471A (ja) * 1985-07-04 1987-01-16 Matsushita Electric Ind Co Ltd 空気ボタン電池
JPS6341864U (fr) * 1986-09-03 1988-03-18
JPS63184560U (fr) * 1987-05-19 1988-11-28
JPH09500485A (ja) * 1993-11-30 1997-01-14 ベル コミュニケーションズ リサーチ，インコーポレイテッド 電解質活性可能なリチウムイオン再充電可能電池セルおよびその製造方法
US5437692A (en) * 1994-11-02 1995-08-01 Dasgupta; Sankar Method for forming an electrode-electrolyte assembly
JPH09293518A (ja) * 1996-04-26 1997-11-11 Asahi Chem Ind Co Ltd 薄膜状電解質および該電解質を用いた電池

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2016535923A (ja) * 2013-11-04 2016-11-17 エルジー・ケム・リミテッド 二次電池用接着層の形成方法
US10193120B2 (en) 2013-11-04 2019-01-29 Lg Chem, Ltd. Method for forming adhesion layer for secondary battery
CN107431187A (zh) * 2015-03-17 2017-12-01 株式会社Lg化学 具有多孔粘合剂涂层的电极及其制造方法和包括该电极的锂二次电池
US20170365841A1 (en) * 2015-03-17 2017-12-21 Lg Chem, Ltd. Electrode with porous binder coating layer, method for manufacturing the same, and lithium secondary battery comprising the same
JP2018508939A (ja) * 2015-03-17 2018-03-29 エルジー・ケム・リミテッド 多孔性バインダーコーティング層を備えた電極、その製造方法及びそれを含むリチウム二次電池
US10468663B2 (en) 2015-03-17 2019-11-05 Lg Chem, Ltd. Electrode with porous binder coating layer, method for manufacturing the same, and lithium secondary battery comprising the same
CN107431187B (zh) * 2015-03-17 2021-03-16 株式会社Lg化学 具有多孔粘合剂涂层的电极、其制造方法和包括它的电池

Similar Documents

Publication Publication Date Title
JP3225864B2 (ja) リチウムイオン二次電池及びその製造方法
KR100279071B1 (ko) 리튬이온 2차전지
EP0954042B1 (fr) Accumulateur electrique aux ions lithium et sa fabrication
KR100287004B1 (ko) 리튬이온 2차전지 및 그 제조방법
EP0959513B1 (fr) Batterie secondaire aux ions de lithium et fabrication de cette derniere
US6291102B1 (en) Lithium ion secondary battery
JP3474853B2 (ja) リチウムイオン二次電池の製造方法
JP4008508B2 (ja) リチウムイオン二次電池の製造方法
WO1999048163A1 (fr) Batterie aux ions lithium et son procede de fabrication
KR101663351B1 (ko) 전기화학소자용 셀 및 이의 제조 방법
JP2008097991A (ja) 蓄電デバイス
JP2000030742A (ja) リチウムイオン二次電池要素
WO1999031751A1 (fr) Batterie auxiliaire au lithium et sa fabrication
JPH10284055A (ja) リチウムイオン二次電池用電極およびそれを用いたリチウムイオン二次電池
WO1999034469A1 (fr) Pile secondaire a ions de lithium
WO1999048162A1 (fr) Accumulateur aux ions lithium et son procede de fabrication
WO1999040645A1 (fr) Batterie au lithium et son procede de fabrication
WO1999031750A1 (fr) Adhesif pour elements, element l'utilisant et procede de fabrication d'elements
JPH11154534A (ja) リチウムイオン二次電池要素
JP2003151638A (ja) リチウムイオン二次電池
WO1999033136A1 (fr) Batterie secondaire a ions lithium, et sa fabrication
WO1999026308A1 (fr) Agent de liaison pour accumulateurs, et accumulateur le mettant en oeuvre
WO1999034470A1 (fr) Procede de fabrication d'une pile secondaire a ions de lithium
WO1999048164A1 (fr) Accumulateur et son procede de fabrication
KR20010005879A (ko) 리튬이온 전지의 제조방법

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): CN JP KR US

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE DK ES FI FR GB GR IE IT LU MC NL PT SE

121 Ep: the epo has been informed by wipo that ep was designated in this application
122 Ep: pct application non-entry in european phase