WO1998032902A1 - Procede de fabrication de particules cristallines sur un support ou sur un substrat - Google Patents

Procede de fabrication de particules cristallines sur un support ou sur un substrat Download PDF

Info

Publication number
WO1998032902A1
WO1998032902A1 PCT/EP1998/000392 EP9800392W WO9832902A1 WO 1998032902 A1 WO1998032902 A1 WO 1998032902A1 EP 9800392 W EP9800392 W EP 9800392W WO 9832902 A1 WO9832902 A1 WO 9832902A1
Authority
WO
WIPO (PCT)
Prior art keywords
cage
support
crystalline particles
crystal seeds
opened
Prior art date
Application number
PCT/EP1998/000392
Other languages
English (en)
Inventor
Guy R. Ester
Bernd Peter Ludwig Grimm
Erik Middelman
Original Assignee
Ester Guy R
Bernd Peter Ludwig Grimm
Erik Middelman
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ester Guy R, Bernd Peter Ludwig Grimm, Erik Middelman filed Critical Ester Guy R
Publication of WO1998032902A1 publication Critical patent/WO1998032902A1/fr

Abstract

L'invention porte sur un procédé de cristallisation de particules, dans lequel des germes de cristal sont nucléés dans un composé-cage. Ce procédé est caractérisé en ce que l'on forme des particules cristallines présentant une dimension supérieure à celle de la cavité de la cage, a) après avoir transféré les germes de cristal dans le composé-cage, placé ce composé-cage sur un support et ouvert le composé-cage, ou b) après avoir placé le composé-cage sur un support, ouvert le composé cage et transféré les germes de cristal pour les placer dans le composé-cage, ou c) après avoir placé le composé-cage sur un support, transféré les germes de cristal dans le composé-cage, puis ouvert celui-ci. On peut transférer sur un substrat les particules cristallines. On peut utiliser ce support ou substrat doté des particules cristallines, dans des dispositifs de stockage de données.
PCT/EP1998/000392 1997-01-22 1998-01-21 Procede de fabrication de particules cristallines sur un support ou sur un substrat WO1998032902A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP97200147.3 1997-01-22
EP97200147 1997-01-22

Publications (1)

Publication Number Publication Date
WO1998032902A1 true WO1998032902A1 (fr) 1998-07-30

Family

ID=8227941

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP1998/000392 WO1998032902A1 (fr) 1997-01-22 1998-01-21 Procede de fabrication de particules cristallines sur un support ou sur un substrat

Country Status (1)

Country Link
WO (1) WO1998032902A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2841794A1 (fr) * 2002-07-03 2004-01-09 Centre Nat Rech Scient Controle de la distribution spatiale de cristaux microscopiques dans des evidements realises sur un substrat

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3758387A (en) * 1971-05-10 1973-09-11 Philips Corp Ion displacement crystal growth
US4214893A (en) * 1977-11-07 1980-07-29 Nippon Columbia Kabushikikaisha Method of making a magnetic powder
JPH05139040A (ja) * 1991-11-18 1993-06-08 Nikon Corp Ｐｈｂ光記録媒体
US5277960A (en) * 1991-04-22 1994-01-11 Noboru Tsuya Substrate for magnetic recording medium and process of producing the same
US5358722A (en) * 1989-08-18 1994-10-25 Monsanto Company Ferritin analogs
DE4432045A1 (de) * 1994-09-09 1996-03-14 Franz Dietrich Oeste Ungefüllte und endohedral gefüllte Fullerene und Heterofullerene, Verfahren zu ihrer Herstellung und Anwendung derselben

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3758387A (en) * 1971-05-10 1973-09-11 Philips Corp Ion displacement crystal growth
US4214893A (en) * 1977-11-07 1980-07-29 Nippon Columbia Kabushikikaisha Method of making a magnetic powder
US5358722A (en) * 1989-08-18 1994-10-25 Monsanto Company Ferritin analogs
US5277960A (en) * 1991-04-22 1994-01-11 Noboru Tsuya Substrate for magnetic recording medium and process of producing the same
JPH05139040A (ja) * 1991-11-18 1993-06-08 Nikon Corp Ｐｈｂ光記録媒体
DE4432045A1 (de) * 1994-09-09 1996-03-14 Franz Dietrich Oeste Ungefüllte und endohedral gefüllte Fullerene und Heterofullerene, Verfahren zu ihrer Herstellung und Anwendung derselben

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
MELDRUM ET AL: "magnetoferritin: in vitro synthesis of a novel magnetic protein", SCIENCE, vol. 257, 24 July 1992 (1992-07-24), pages 522 - 523, XP000676756 *
PATENT ABSTRACTS OF JAPAN vol. 17, no. 524 (M - 1483) *

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2841794A1 (fr) * 2002-07-03 2004-01-09 Centre Nat Rech Scient Controle de la distribution spatiale de cristaux microscopiques dans des evidements realises sur un substrat
WO2004005590A2 (fr) * 2002-07-03 2004-01-15 Centre National De La Recherche Scientifique Controle de la distribution spatiale de cristaux microscopiques dans des evidements realises sur un substrat
WO2004005590A3 (fr) * 2002-07-03 2004-05-21 Centre Nat Rech Scient Controle de la distribution spatiale de cristaux microscopiques dans des evidements realises sur un substrat

Similar Documents

Publication Publication Date Title
US5652054A (en) Magnetic recording media having a magnetic thin film made of magnetic metals grains and nonmagnetic matrix
Terris et al. Patterning magnetic films by ion beam irradiation
US7282278B1 (en) Tilted recording media with L10 magnetic layer
JP4213076B2 (ja) 磁気記録媒体の製造方法
Sugita Co-Cr perpendicular magnetic recording tape by vacuum deposition
US20050260340A1 (en) Nanoparticle for magnetic recording medium, magnetic recording medium using the same, and process for manufacturing magnetic recording medium
US6896957B1 (en) Magnetizable device
US6713173B2 (en) Magnetizable device
KR100438802B1 (ko) 양자디스크및그제조방법
WO1998032902A1 (fr) Procede de fabrication de particules cristallines sur un support ou sur un substrat
JPS6150211A (ja) 垂直磁気記録媒体およびその製法
CN1279514C (zh) 多晶结构膜及其制造方法
US20070218282A1 (en) Hard-magnetic nanoparticles, manufacturing method therefor, magnetic fluid and magnetic recording medium
KR100280901B1 (ko) 기능성입자분산형 박막, 그래뉼형 자성박막 및 그 제조방법
KR20030095218A (ko) 수직 자기 기록 매체, 그 제조 방법 및 자기 기억 장치
JP2002170227A (ja) 高密度磁気記録媒体
Thiele et al. Grain size control in FePt thin films by Ar-ion etched Pt seed layers
US20050158883A1 (en) Multilayered structure film and method of making the same
Hirono et al. Cobalt-Carbon Nanogranular Magnetic Thin Films
JP4050643B2 (ja) 反強磁性微小粒子およびその製造方法
JPH0664738B2 (ja) 磁性体薄膜の製造方法
US7258893B2 (en) Method of fabricating a magnetic recording medium
EP1553565B1 (fr) Support d'enregistrement magnétique et procédé pour sa fabrication
WO2004074170A1 (fr) Materiau composite, corps structurel et son procede de fabrication film de structure polycristalline et procede de fabrication de particules
Maeda et al. Magnetic microstructures produced by compositional separation in Co-Cr based alloy thin films

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): JP US

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE DK ES FI FR GB GR IE IT LU MC NL PT SE

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
NENP Non-entry into the national phase

Ref country code: JP

Ref document number: 1998531604

Format of ref document f/p: F

122 Ep: pct application non-entry in european phase