WO1994025764A1 - Vis - Google Patents

Vis Download PDF

Info

Publication number
WO1994025764A1
WO1994025764A1 PCT/SE1994/000400 SE9400400W WO9425764A1 WO 1994025764 A1 WO1994025764 A1 WO 1994025764A1 SE 9400400 W SE9400400 W SE 9400400W WO 9425764 A1 WO9425764 A1 WO 9425764A1
Authority
WO
WIPO (PCT)
Prior art keywords
screw
layer
screw according
maximally
steel
Prior art date
Application number
PCT/SE1994/000400
Other languages
English (en)
Inventor
Tonny Westlund
Original Assignee
BERGHOLTZ, Göran
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from SE9301517A external-priority patent/SE9301517D0/xx
Priority claimed from SE9304267A external-priority patent/SE9304267D0/xx
Application filed by BERGHOLTZ, Göran filed Critical BERGHOLTZ, Göran
Priority to AU66617/94A priority Critical patent/AU6661794A/en
Priority to EP94915315A priority patent/EP0697072A1/fr
Priority to JP6524178A priority patent/JPH08509799A/ja
Publication of WO1994025764A1 publication Critical patent/WO1994025764A1/fr

Abstract

La présente invention concerne une vis, constituée d'acier inoxydable austénitique d'une dureté n'excédant pas 250 HV, lequel acier inoxydable austénitique présente une couche (3) ayant subi une trempe superficielle, réalisée par ionitruration, ladite couche possédant une épaisseur de 0,01-0,2 mm et une dureté d'au moins 900 HV.
PCT/SE1994/000400 1993-05-04 1994-05-03 Vis WO1994025764A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
AU66617/94A AU6661794A (en) 1993-05-04 1994-05-03 A screw
EP94915315A EP0697072A1 (fr) 1993-05-04 1994-05-03 Vis
JP6524178A JPH08509799A (ja) 1993-05-04 1994-05-03 ね じ

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
SE9301517A SE9301517D0 (sv) 1993-05-04 1993-05-04 Skruv
SE9301517-0 1993-12-23
SE9304267-9 1993-12-23
SE9304267A SE9304267D0 (sv) 1993-12-23 1993-12-23 Skruv

Publications (1)

Publication Number Publication Date
WO1994025764A1 true WO1994025764A1 (fr) 1994-11-10

Family

ID=26661728

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/SE1994/000400 WO1994025764A1 (fr) 1993-05-04 1994-05-03 Vis

Country Status (5)

Country Link
EP (1) EP0697072A1 (fr)
JP (1) JPH08509799A (fr)
AU (1) AU6661794A (fr)
CA (1) CA2160793A1 (fr)
WO (1) WO1994025764A1 (fr)

Cited By (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1996019675A1 (fr) * 1994-12-21 1996-06-27 Sfs Industrie Holding Ag Vis foreuse et taraudeuse et son procede d'enfoncement
WO1996019676A1 (fr) * 1994-12-21 1996-06-27 Sfs Industrie Holding Ag Vis foreuse et taraudeuse et son procede de vissage
GB2315079A (en) * 1996-07-08 1998-01-21 Rhp Bearings Ltd Ion nitriding surface treatment of rolling element bearing steels
DE102004053803A1 (de) * 2004-11-08 2006-05-24 Hilti Ag Gewindefurchende Schraube
EP1710455A1 (fr) * 2005-04-08 2006-10-11 Shinjo MFG. Co., Ltd. Vis auto foreuse à utiliser avec des tôles d'acier
EP2068012A2 (fr) * 2007-12-03 2009-06-10 BSH Bosch und Siemens Hausgeräte GmbH Vis à taraudage parciellement durci
EP2003348A3 (fr) * 2007-06-15 2010-02-10 Adolf Würth GmbH & Co. KG Vis et son utilisation
WO2012072209A1 (fr) * 2010-12-01 2012-06-07 Oerlikon Trading Ag, Trübbach Composant de façonnage de matières plastiques présentant une surface en acier
EP2468929B1 (fr) 2010-12-27 2015-04-08 Fontana Fasteners R.D. S.r.l. Procédé pour le revêtement de pièces métalliques filetées
WO2016023855A1 (fr) * 2014-08-14 2016-02-18 Sfs Intec Holding Ag Tarière

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5746832B2 (ja) * 2010-06-07 2015-07-08 株式会社田中 ステンレス鋼製ねじ

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE3235447A1 (de) * 1981-10-27 1983-05-11 Yugen Kaisha Shinjo Seisakusho, Osaka Bohrschraube
EP0523298A1 (fr) * 1991-07-18 1993-01-20 Daidousanso Co., Ltd. Vis en acier inoxydable austénitique dur

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE3235447A1 (de) * 1981-10-27 1983-05-11 Yugen Kaisha Shinjo Seisakusho, Osaka Bohrschraube
EP0523298A1 (fr) * 1991-07-18 1993-01-20 Daidousanso Co., Ltd. Vis en acier inoxydable austénitique dur

Cited By (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1996019676A1 (fr) * 1994-12-21 1996-06-27 Sfs Industrie Holding Ag Vis foreuse et taraudeuse et son procede de vissage
AU702314B2 (en) * 1994-12-21 1999-02-18 Sfs Industrie Holding Ag Hole-shaping and thread-forming screw and process for driving in the same
CN1058325C (zh) * 1994-12-21 2000-11-08 Sfs工业控股公司 自成孔和螺纹的螺钉以及螺钉拧入的方法
US6428258B1 (en) 1994-12-21 2002-08-06 Sfs Industrie Holding Ag Non cutting hole-shaping and thread-forming stainless screw and process with impact for driving in the same
WO1996019675A1 (fr) * 1994-12-21 1996-06-27 Sfs Industrie Holding Ag Vis foreuse et taraudeuse et son procede d'enfoncement
GB2315079A (en) * 1996-07-08 1998-01-21 Rhp Bearings Ltd Ion nitriding surface treatment of rolling element bearing steels
GB2315079B (en) * 1996-07-08 1999-03-24 Rhp Bearings Ltd Surface treatment of rolling element bearing steel
DE102004053803A1 (de) * 2004-11-08 2006-05-24 Hilti Ag Gewindefurchende Schraube
DE102004053803B4 (de) * 2004-11-08 2006-10-26 Hilti Ag Gewindefurchende Schraube
EP1710455A1 (fr) * 2005-04-08 2006-10-11 Shinjo MFG. Co., Ltd. Vis auto foreuse à utiliser avec des tôles d'acier
EP2003348A3 (fr) * 2007-06-15 2010-02-10 Adolf Würth GmbH & Co. KG Vis et son utilisation
EP2068012A2 (fr) * 2007-12-03 2009-06-10 BSH Bosch und Siemens Hausgeräte GmbH Vis à taraudage parciellement durci
EP2068012A3 (fr) * 2007-12-03 2011-11-23 BSH Bosch und Siemens Hausgeräte GmbH Vis à taraudage parciellement durci
WO2012072209A1 (fr) * 2010-12-01 2012-06-07 Oerlikon Trading Ag, Trübbach Composant de façonnage de matières plastiques présentant une surface en acier
EP2468929B1 (fr) 2010-12-27 2015-04-08 Fontana Fasteners R.D. S.r.l. Procédé pour le revêtement de pièces métalliques filetées
WO2016023855A1 (fr) * 2014-08-14 2016-02-18 Sfs Intec Holding Ag Tarière
CN106662137A (zh) * 2014-08-14 2017-05-10 Sfs因泰克控股股份公司 自攻螺钉
AU2015303305B2 (en) * 2014-08-14 2018-07-26 Sfs Intec Holding Ag Drilling screw
CN106662137B (zh) * 2014-08-14 2019-03-01 Sfs因泰克控股股份公司 自攻螺钉
US10221880B2 (en) 2014-08-14 2019-03-05 Sfs Intec Holding Ag Drilling screw
RU2683973C2 (ru) * 2014-08-14 2019-04-03 Сфс Интек Холдинг Аг Самонарезающий винт и применение самонарезающего винта

Also Published As

Publication number Publication date
CA2160793A1 (fr) 1994-11-10
JPH08509799A (ja) 1996-10-15
AU6661794A (en) 1994-11-21
EP0697072A1 (fr) 1996-02-21

Similar Documents

Publication Publication Date Title
TWI452170B (zh) 熱浸鍍鋅鋼板及其製造方法
US8021497B2 (en) Method for producing a hardened steel part
CA2123470C (fr) Acier ferritique inoxydable possedant une excellente resistance a la corrosion atmospherique et a celle des fissures
DE3901365C2 (fr)
EP2644737A1 (fr) TÔLE EN ACIER PLAQUÉE PAR IMMERSION À CHAUD À BASE D'Al-Zn
EP2644736A1 (fr) TÔLE EN ACIER PLAQUÉE PAR IMMERSION À CHAUD À BASE D'Al-Zn ET SON PROCÉDÉ DE FABRICATION
EP0697072A1 (fr) Vis
US6565931B1 (en) Corrosion protective coating for a metallic article and a method of applying a corrosion protective coating to a metallic article
CA1321906C (fr) Tole d'acier recouverte d'aluminium par immersion a chaud offrant une excellente resistance a la chaleur et a la corrosion
EP1347075B2 (fr) Procede de nitruration avec un bain de sel destine a la production d`elements en fer possedant une resistance a la corrosion amelioree et parties en fer
WO2022048990A1 (fr) Pièce en acier fabriquée par formage à chaud d'un produit plat en acier, produit plat en acier et procédé de fabrication d'une pièce en acier
DE102015212588A1 (de) Konturtreue Schutzschicht für Verdichterbauteile von Gasturbinen
EP0441216A1 (fr) Matériau pour toiture et façade
JP5151645B2 (ja) ドリリングタッピンねじ及びその製造方法
EP0852264A1 (fr) Alliages de zinc donnant des revêtements anticorrosifs sur matériaux ferreux
US7820099B2 (en) Hot rolled steel sheet excellent in chemical convertibility and method of production of the same
JP2004360056A (ja) 黒色化溶融Ｚｎ−Ａｌ−Ｍｇ系合金めっき鋼板及びその製造方法
CA2504470A1 (fr) Attache pour utilisation dans des conditions ambiantes difficiles
US11920624B2 (en) Zn-Ni as a coating layer on self-drilling screws of austenitic stainless steel
WO1996014514A1 (fr) Vis et procede de fabrication et de traitement de ladite vis
KR100319302B1 (ko) 내식성(耐食性)이 우수한 강재 및 이 강재를 이용한 구조물
KR102305748B1 (ko) 내부식성이 우수한 용융 합금도금 강재 및 그 제조방법
JP2002173753A (ja) 耐黒変性に優れた溶融Ｚｎ−Ａｌ合金めっき鋼板とその製造方法
US5389454A (en) Silicide coating having good resistance to molten metals
JP3383124B2 (ja) 塗装後耐食性に優れた建材用溶融アルミめっき鋼板およびその製造方法

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AT AU BB BG BR BY CA CH CN CZ DE DE DK DK ES FI GB GE HU JP KG KP KR KZ LK LU LV MD MG MN MW NL NO NZ PL PT RO RU SD SE SI SK TJ TT UA US UZ VN

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE DK ES FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN ML MR NE SN TD TG

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 1994915315

Country of ref document: EP

ENP Entry into the national phase

Ref document number: 1995 532655

Country of ref document: US

Date of ref document: 19951016

Kind code of ref document: A

WWE Wipo information: entry into national phase

Ref document number: 2160793

Country of ref document: CA

WWP Wipo information: published in national office

Ref document number: 1994915315

Country of ref document: EP

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

WWW Wipo information: withdrawn in national office

Ref document number: 1994915315

Country of ref document: EP