WO1993020164A1 - Compositions auto-adhesives d'acrylate durcissables par rayonnement ultraviolet - Google Patents

Compositions auto-adhesives d'acrylate durcissables par rayonnement ultraviolet Download PDF

Info

Publication number
WO1993020164A1
WO1993020164A1 PCT/US1993/002528 US9302528W WO9320164A1 WO 1993020164 A1 WO1993020164 A1 WO 1993020164A1 US 9302528 W US9302528 W US 9302528W WO 9320164 A1 WO9320164 A1 WO 9320164A1
Authority
WO
WIPO (PCT)
Prior art keywords
weight
polymer
parts
monomer
photoiniferter
Prior art date
Application number
PCT/US1993/002528
Other languages
English (en)
Inventor
Mahfuza B. Ali
Gaddam N. Babu
Patrick G. Zimmerman
Original Assignee
Minnesota Mining And Manufacturing Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Minnesota Mining And Manufacturing Company filed Critical Minnesota Mining And Manufacturing Company
Priority to EP93907594A priority Critical patent/EP0633918A1/fr
Priority to JP5517493A priority patent/JPH07505431A/ja
Publication of WO1993020164A1 publication Critical patent/WO1993020164A1/fr
Priority to KR1019940703387A priority patent/KR950700973A/ko

Abstract

L'invention se rapporte à des réticulations de (co)polymères de (méth)acrylate, et à un procédé de préparation de ces réticulations, selon lequel un homopolymère, un copolymère sans ordre ou un copolymère séquencé dérivé d'un initiateur/agent de transfert/élément de terminaison photochimique (photoiniferter) est dissous dans un mélange monomère compatible avec un articulateur et un photoinitiateur sensibles au rayonnement. Le mélange polymère-monomère est appliqué sur une bande appropriée et durcie par l'intermédiaire d'un rayonnement ultraviolet pour effectuer une réticulation produite par la polymérisation de monomères avec l'incorporation du polymère de photoiniferter actif. Ces réticulations présentent d'excellentes caractéristiques adhésives. Lorsque le polymère de photoiniferter est un homopolymère, un copolymère sans ordre ou un copolymer biséquencé du type AB, l'on obtient un adhésif autocollant lorsque le polymère de photoiniferter est un homopolymère ou un copolymère sans ordre, l'adhésif obtenu présente d'excellentes caractéristiques anti-vibration. Lorsque le polymère de photoiniferter est un copolymère triséquencé du type ABC, l'on obtient une colle d'assemblage.
PCT/US1993/002528 1992-03-31 1993-03-19 Compositions auto-adhesives d'acrylate durcissables par rayonnement ultraviolet WO1993020164A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
EP93907594A EP0633918A1 (fr) 1992-03-31 1993-03-19 Compositions auto-adhesives d'acrylate durcissables par rayonnement ultraviolet
JP5517493A JPH07505431A (ja) 1992-03-31 1993-03-19 紫外線硬化性アクリレート感圧接着剤組成物
KR1019940703387A KR950700973A (ko) 1992-03-31 1994-09-29 자외 방사선 경화가능한 감압성 아크릴레이트 접착제 조성물(ultraviolet radiation curable acrylate pressuresensitive adhesive compositions)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US86124292A 1992-03-31 1992-03-31
US07/861,242 1992-03-31

Publications (1)

Publication Number Publication Date
WO1993020164A1 true WO1993020164A1 (fr) 1993-10-14

Family

ID=25335262

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1993/002528 WO1993020164A1 (fr) 1992-03-31 1993-03-19 Compositions auto-adhesives d'acrylate durcissables par rayonnement ultraviolet

Country Status (4)

Country Link
EP (1) EP0633918A1 (fr)
JP (1) JPH07505431A (fr)
KR (1) KR950700973A (fr)
WO (1) WO1993020164A1 (fr)

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1996004346A1 (fr) * 1994-07-29 1996-02-15 Minnesota Mining And Manufacturing Company Sirop acrylique durcissable en materiau reticule viscoelastomere
FR2771747A1 (fr) * 1997-12-03 1999-06-04 Atochem Elf Sa Utilisation de copolymeres a blocs lineaires non-dieniques comme auto-adhesifs ou composants d'auto-adhesifs
EP1411098A1 (fr) * 2002-10-17 2004-04-21 tesa AG Les pièces adhésives formées
FR2884254A1 (fr) * 2005-04-08 2006-10-13 Arkema Sa Copolymere sequence a fonctions acides modulables et composition adhesive et thermoplastique le contenant
EP2380917A1 (fr) * 2009-01-22 2011-10-26 Nippon Paper Chemicals Co., Ltd. Composition de résine durcissable par faisceau d'énergie active
EP2492289A1 (fr) * 2009-10-23 2012-08-29 Kuraray Noritake Dental Inc. Composition polymérisable et matériau dentaire
WO2018118905A1 (fr) * 2016-12-22 2018-06-28 3M Innovative Properties Company Matériaux polymères réticulables et réticulés
CN109476774A (zh) * 2016-07-11 2019-03-15 3M创新有限公司 使用可控自由基引发剂的聚合物材料及制备方法
WO2019123182A1 (fr) * 2017-12-21 2019-06-27 3M Innovative Properties Company Compositions polymères préparées avec un initiateur radicalaire contrôlé

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
ES2277678T3 (es) * 1997-12-18 2007-07-16 E.I. Du Pont De Nemours And Company Proceso de polimerizacion con caracteristicas vivientes y polimeros obtenidos mediante este proceso.
JP4768103B2 (ja) * 2000-06-06 2011-09-07 日東電工株式会社 粘着剤組成物とその粘着シ―ト類およびこれらの製造方法
JP4768115B2 (ja) * 2000-12-01 2011-09-07 日東電工株式会社 紫外線架橋型粘着剤組成物とその製造方法ならびに粘着シ―トとその製造方法
FR2951187B1 (fr) * 2009-10-08 2012-10-19 Arkema France Composition thermoplastique a base de copolymeres a blocs acryliques et son utilisation dans l'encapsulation d'elements photovoltaiques
ES2494615T3 (es) * 2010-05-03 2014-09-15 Arkema France Encapsulante curable por UV
KR20150098296A (ko) * 2014-02-20 2015-08-28 (주)엘지하우시스 고무계 점착제 조성물 및 이를 이용한 자동차용 고무계 점착테이프

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0286376A2 (fr) * 1987-04-07 1988-10-12 Mitsubishi Petrochemical Co., Ltd. Copolymères séquencés du type ABA
EP0349270A2 (fr) * 1988-06-28 1990-01-03 Minnesota Mining And Manufacturing Company Adhésifs sensibles à la pression
EP0434334A1 (fr) * 1989-12-21 1991-06-26 Minnesota Mining And Manufacturing Company Compositions dentaires, procédé pour la préparation d'articles formés par une "polymérisation photoinifertée" de ces compositions dentaires et articles dentaires formés produits par ce procédé
EP0449619A2 (fr) * 1990-03-29 1991-10-02 Minnesota Mining And Manufacturing Company Adhésifs préparés au moyen de photoiniferte réticulable par radiation contrôlable pour attacher le matériel micro-électronique et méthode pour attacher le matériel microélectronique ensemble

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0286376A2 (fr) * 1987-04-07 1988-10-12 Mitsubishi Petrochemical Co., Ltd. Copolymères séquencés du type ABA
EP0349270A2 (fr) * 1988-06-28 1990-01-03 Minnesota Mining And Manufacturing Company Adhésifs sensibles à la pression
EP0434334A1 (fr) * 1989-12-21 1991-06-26 Minnesota Mining And Manufacturing Company Compositions dentaires, procédé pour la préparation d'articles formés par une "polymérisation photoinifertée" de ces compositions dentaires et articles dentaires formés produits par ce procédé
EP0449619A2 (fr) * 1990-03-29 1991-10-02 Minnesota Mining And Manufacturing Company Adhésifs préparés au moyen de photoiniferte réticulable par radiation contrôlable pour attacher le matériel micro-électronique et méthode pour attacher le matériel microélectronique ensemble

Cited By (25)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1996004346A1 (fr) * 1994-07-29 1996-02-15 Minnesota Mining And Manufacturing Company Sirop acrylique durcissable en materiau reticule viscoelastomere
JPH10503548A (ja) * 1994-07-29 1998-03-31 ミネソタ マイニング アンド マニュアファクチャリング カンパニー 架橋結合された粘弾性高分子材料に硬化可能なアクリル系シロップ
US5773485A (en) * 1994-07-29 1998-06-30 Minnesota Mining And Manufacturing Company Acrylic syrup curable to a crosslinked viscoelastomeric material
US5902836A (en) * 1994-07-29 1999-05-11 Minnesota Mining And Manufacturing Company Acrylic syrup curable to a crosslinked viscoelastomeric material
FR2771747A1 (fr) * 1997-12-03 1999-06-04 Atochem Elf Sa Utilisation de copolymeres a blocs lineaires non-dieniques comme auto-adhesifs ou composants d'auto-adhesifs
EP0921170A1 (fr) * 1997-12-03 1999-06-09 Elf Atochem S.A. Utilisation de copolymères à blocs linéaires non-diéniques comme auto-adhésifs ou composants d'auto-adhésifs
EP1411098A1 (fr) * 2002-10-17 2004-04-21 tesa AG Les pièces adhésives formées
FR2884254A1 (fr) * 2005-04-08 2006-10-13 Arkema Sa Copolymere sequence a fonctions acides modulables et composition adhesive et thermoplastique le contenant
WO2006106277A3 (fr) * 2005-04-08 2007-02-15 Arkema France Copolymere sequence a fonctions acides modulable et composition adhesive et thermoplastique le contenant
US8748507B2 (en) 2009-01-22 2014-06-10 Nippon Paper Chemicals Co., Ltd. Active energy ray curable resin composition
EP2380917A4 (fr) * 2009-01-22 2014-03-26 Nippon Paper Chemicals Co Ltd Composition de résine durcissable par faisceau d'énergie active
EP2380917A1 (fr) * 2009-01-22 2011-10-26 Nippon Paper Chemicals Co., Ltd. Composition de résine durcissable par faisceau d'énergie active
EP2492289A1 (fr) * 2009-10-23 2012-08-29 Kuraray Noritake Dental Inc. Composition polymérisable et matériau dentaire
EP2492289A4 (fr) * 2009-10-23 2014-10-29 Kuraray Noritake Dental Inc Composition polymérisable et matériau dentaire
US9333148B2 (en) 2009-10-23 2016-05-10 Kuraray Noritake Dental Inc. Polymerizable composition and dental material
CN109476774A (zh) * 2016-07-11 2019-03-15 3M创新有限公司 使用可控自由基引发剂的聚合物材料及制备方法
CN109476774B (zh) * 2016-07-11 2021-01-12 3M创新有限公司 使用可控自由基引发剂的聚合物材料及制备方法
WO2018118905A1 (fr) * 2016-12-22 2018-06-28 3M Innovative Properties Company Matériaux polymères réticulables et réticulés
CN110099938A (zh) * 2016-12-22 2019-08-06 3M创新有限公司 可交联聚合物材料和交联聚合物材料
US10640686B2 (en) 2016-12-22 2020-05-05 3M Innovative Properties Company Crosslinkable and crosslinked polymeric materials
CN110099938B (zh) * 2016-12-22 2021-01-15 3M创新有限公司 可交联聚合物材料和交联聚合物材料
WO2019123182A1 (fr) * 2017-12-21 2019-06-27 3M Innovative Properties Company Compositions polymères préparées avec un initiateur radicalaire contrôlé
CN111511861A (zh) * 2017-12-21 2020-08-07 3M创新有限公司 用受控自由基引发剂制备的聚合物组合物
US10913807B2 (en) 2017-12-21 2021-02-09 3M Innovative Properties Company Polymeric compositions prepared with a controlled radical initiator
CN111511861B (zh) * 2017-12-21 2021-06-18 3M创新有限公司 用受控自由基引发剂制备的聚合物组合物

Also Published As

Publication number Publication date
JPH07505431A (ja) 1995-06-15
KR950700973A (ko) 1995-02-20
EP0633918A1 (fr) 1995-01-18

Similar Documents

Publication Publication Date Title
US5869598A (en) Block polymer thermoplastic addition polymer and their production process and use
KR0128278B1 (ko) 점착화된 삼원 공중합체 접착제
EP0902816B1 (fr) Adhesifs autocollants thermomorphiques
CA1127592A (fr) Colle thermofusible tenant a la pression, curable par exposition a un rayon d'electron
US5416127A (en) Radiation curable hot melt pressure sensitive adhesives
US6232365B1 (en) Low temperature electron beam polymerization
EP0633918A1 (fr) Compositions auto-adhesives d'acrylate durcissables par rayonnement ultraviolet
JP2013514445A (ja) 低表面エネルギー基材用感圧性接着剤
CN104144953A (zh) 作为潜在离子交联剂用于丙烯酸类压敏粘合剂的光产碱剂
EP3904411A1 (fr) Composition de résine photodurcissable et procédé de fabrication d'un appareil d'affichage d'image
JPH0570752A (ja) アクリル系粘着剤組成物および粘着テープ、ラベルもしくはシート
EP0608891B1 (fr) Adhésifs thermofusibles sensibles à la pression durcissables par irradiation
JP2020516741A (ja) 感圧接着剤組成物
JP2686324B2 (ja) 感圧性接着剤組成物
TW201736554A (zh) 壓敏性黏著劑
JPH1112553A (ja) 接着剤組成物およびこれを利用した透明粘着フィルム
JPH08109356A (ja) アクリル系粘着テープ
JP2022515643A (ja) 接着剤組成物およびそれを形成する方法
JP3091783B2 (ja) 光重合性接着剤組成物とこれを用いた感圧性接着剤およびその接着シ―ト
JPH1025459A (ja) 粘着剤組成物
JPH0848944A (ja) 放射線硬化型粘着剤組成物および該組成物を用いてなる粘着テープもしくはシート
JP3444423B2 (ja) カルバメート官能性モノマーを含む紫外線硬化性アクリル系感圧接着剤組成物及びそれから調製された接着剤
JP2003027018A (ja) 粘着シートとその製造方法
JP2006225611A (ja) 粘着剤組成物、両面粘着テープおよび接着方法
EP0912647A1 (fr) Perles d'adhesif auto-collant a polymere acrylique modifie par styrile

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): JP KR

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE DK ES FR GB GR IE IT LU MC NL PT SE

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
WWE Wipo information: entry into national phase

Ref document number: 1993907594

Country of ref document: EP

WWP Wipo information: published in national office

Ref document number: 1993907594

Country of ref document: EP

WWR Wipo information: refused in national office

Ref document number: 1993907594

Country of ref document: EP

WWW Wipo information: withdrawn in national office

Ref document number: 1993907594

Country of ref document: EP