WO1993008974A1 - Articles faconnes et procedes de fabrication - Google Patents

Articles faconnes et procedes de fabrication Download PDF

Info

Publication number
WO1993008974A1
WO1993008974A1 PCT/GB1992/002068 GB9202068W WO9308974A1 WO 1993008974 A1 WO1993008974 A1 WO 1993008974A1 GB 9202068 W GB9202068 W GB 9202068W WO 9308974 A1 WO9308974 A1 WO 9308974A1
Authority
WO
WIPO (PCT)
Prior art keywords
filler
thermoplastic material
plastic
melted
particulate
Prior art date
Application number
PCT/GB1992/002068
Other languages
English (en)
Inventor
Alun Roy Williams
Original Assignee
Alun Roy Williams
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Alun Roy Williams filed Critical Alun Roy Williams
Publication of WO1993008974A1 publication Critical patent/WO1993008974A1/fr

Abstract

On décrit un procédé de fabrication d'un article façonné à partir d'un matériau thermoplastique et d'une charge particulaire, qui consiste à chauffer la charge à une température à laquelle le matériau thermoplastique fond et à mélanger la charge avec le plastique.
PCT/GB1992/002068 1991-11-08 1992-11-09 Articles faconnes et procedes de fabrication WO1993008974A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
GB9123817.0 1991-11-08
GB9123817A GB9123817D0 (en) 1991-11-08 1991-11-08 Shaped articles and methods for making them

Publications (1)

Publication Number Publication Date
WO1993008974A1 true WO1993008974A1 (fr) 1993-05-13

Family

ID=10704346

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/GB1992/002068 WO1993008974A1 (fr) 1991-11-08 1992-11-09 Articles faconnes et procedes de fabrication

Country Status (3)

Country Link
AU (1) AU2920092A (fr)
GB (1) GB9123817D0 (fr)
WO (1) WO1993008974A1 (fr)

Cited By (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1996017807A1 (fr) * 1994-11-28 1996-06-13 Vesa Keskisarja Procede de production d'une composition de remplissage a partir d'une matiere de remplissage chaude telle que des dechets et des matieres plastiques recyclables
DE4443988A1 (de) * 1994-12-12 1996-06-13 Hanichl Michelle Formteil, hergestellt aus Kunststoff enthaltenden Komponenten und Verfahren zu seiner Herstellung
FR2736579A1 (fr) * 1995-07-11 1997-01-17 Canuel Philippe Procede et installation pour la fabrication de produits composites et produits en resultant
WO2000061669A1 (fr) * 1999-04-08 2000-10-19 Donald Roy Crawley Transformation de matiere plastique en produit composite
WO2002016098A1 (fr) * 2000-08-25 2002-02-28 Pasell S.R.L. Procede de production d'articles et articles obtenus selon ce procede
WO2002000567A3 (fr) * 2000-06-30 2002-07-11 Michael Manes Materiau, de meme que procede et dispositif appropries pour le produire
WO2002090288A1 (fr) * 2001-05-08 2002-11-14 Shell Internationale Research Maatschappij B.V. Compositions contenant des particules solides et un liant
EP1354681A1 (fr) * 2002-04-15 2003-10-22 Bobo Holding B.V. Produit moulé comprenant un composant thermoplastique et une charge particulaire et son procédé de fabrication
EP2428351A2 (fr) 2010-09-09 2012-03-14 Siegfried Kreft Procédé et dispositifs de fabrication de pièces moulées et de granulés
US20150094412A1 (en) * 2013-09-27 2015-04-02 Victor Manuel García Alarcón Laterite and polymer construction brick and material and method of manufacturing same
CN108751796A (zh) * 2018-07-06 2018-11-06 四川建筑职业技术学院 一种利用城市污泥制备的复合建筑模板及其制备方法
CN110312612A (zh) * 2016-12-16 2019-10-08 创新石科技公司 板坯的制造方法

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE2226287A1 (de) * 1971-06-03 1972-12-14 Joto Chem Co Ltd Verfahren zum Herstellen geformter Produkte aus Gemischen von thermoplastischen Harzen und Füllstoffen
DE2311797A1 (de) * 1972-04-04 1973-10-18 Bunzl & Biach Ag Verfahren zur herstellung von festen gegenstaenden, belaegen, ueberzuegen od. dgl
NL8200730A (nl) * 1982-02-24 1983-09-16 Hubertus Zandbergen Bouwmateriaal uit kunststofafval.

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE2226287A1 (de) * 1971-06-03 1972-12-14 Joto Chem Co Ltd Verfahren zum Herstellen geformter Produkte aus Gemischen von thermoplastischen Harzen und Füllstoffen
DE2311797A1 (de) * 1972-04-04 1973-10-18 Bunzl & Biach Ag Verfahren zur herstellung von festen gegenstaenden, belaegen, ueberzuegen od. dgl
NL8200730A (nl) * 1982-02-24 1983-09-16 Hubertus Zandbergen Bouwmateriaal uit kunststofafval.

Cited By (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1996017807A1 (fr) * 1994-11-28 1996-06-13 Vesa Keskisarja Procede de production d'une composition de remplissage a partir d'une matiere de remplissage chaude telle que des dechets et des matieres plastiques recyclables
DE4443988A1 (de) * 1994-12-12 1996-06-13 Hanichl Michelle Formteil, hergestellt aus Kunststoff enthaltenden Komponenten und Verfahren zu seiner Herstellung
FR2736579A1 (fr) * 1995-07-11 1997-01-17 Canuel Philippe Procede et installation pour la fabrication de produits composites et produits en resultant
WO2000061669A1 (fr) * 1999-04-08 2000-10-19 Donald Roy Crawley Transformation de matiere plastique en produit composite
US7345107B2 (en) 2000-06-30 2008-03-18 Michael Manes Material and method and device for producing the same
WO2002000567A3 (fr) * 2000-06-30 2002-07-11 Michael Manes Materiau, de meme que procede et dispositif appropries pour le produire
WO2002016098A1 (fr) * 2000-08-25 2002-02-28 Pasell S.R.L. Procede de production d'articles et articles obtenus selon ce procede
WO2002090288A1 (fr) * 2001-05-08 2002-11-14 Shell Internationale Research Maatschappij B.V. Compositions contenant des particules solides et un liant
EP1354681A1 (fr) * 2002-04-15 2003-10-22 Bobo Holding B.V. Produit moulé comprenant un composant thermoplastique et une charge particulaire et son procédé de fabrication
EP2428351A2 (fr) 2010-09-09 2012-03-14 Siegfried Kreft Procédé et dispositifs de fabrication de pièces moulées et de granulés
DE102010037441A1 (de) 2010-09-09 2012-03-15 Horn Dietmar Verfahren und Vorrichtung zur Herstellung von Formteilen und Granulat
US20150094412A1 (en) * 2013-09-27 2015-04-02 Victor Manuel García Alarcón Laterite and polymer construction brick and material and method of manufacturing same
CN110312612A (zh) * 2016-12-16 2019-10-08 创新石科技公司 板坯的制造方法
CN110312612B (zh) * 2016-12-16 2021-08-03 创新石科技公司 板坯的制造方法
CN108751796A (zh) * 2018-07-06 2018-11-06 四川建筑职业技术学院 一种利用城市污泥制备的复合建筑模板及其制备方法

Also Published As

Publication number Publication date
GB9123817D0 (en) 1992-01-02
AU2920092A (en) 1993-06-07

Similar Documents

Publication Publication Date Title
WO1993008974A1 (fr) Articles faconnes et procedes de fabrication
US3574801A (en) Method for making panels of the artificial stone-type
AU5282290A (en) Acid resistant concrete articles, especially sulphur concrete pipes and a method of manufacturing them
US7345107B2 (en) Material and method and device for producing the same
US20120119414A1 (en) Process for manufacturing a shaped article from a composite material comprising a solid filler and a thermoplastic binder
WO1994027800A1 (fr) Procede de production d'un materiau de construction a partir d'un melange de dechets thermoplastiques et d'origine minerale cribles
GB2224283A (en) Process for obtaining artificial stone for flooring and stone facing
EA016011B1 (ru) Способ формования продукта из серного цемента
US5244850A (en) Building product comprising slate particles embedded in a fused glass binder
EP1638759B1 (fr) Procede de fabrication d'articles de type planche ou plaque bicouche et articles de type planche ou plaque pouvant etre obtenus par ledit procede
US4157907A (en) Method of producing a mouldable material having a high content of a crystallizable glass
WO1999005076A1 (fr) Materiau a base de ciment et de resine pour la refection des chaussees
CA2439626A1 (fr) Procede et appareil de creation de blocs de beton ayant l'apparence d'une pierre fossile naturelle
JPH04227095A (ja) 産業廃棄物の処理方法および樹脂コンクリート成形品
EP0989104B1 (fr) Matériau comprenant de l'argile cuite et procédé de son obtention
JPH05138652A (ja) 樹脂コンクリートの製造方法
KR960011322B1 (ko) 폐플라스틱콘크리트복합재료
BE898289A (fr) Procédé de fabrication d'un composite à microbilles de verres, d'objets décoratifs pour l'intérieur et l'extérieur ainsi que pour la décoration et la construction, à forte teneur en charge pour les produits obtenus
KR900005070B1 (ko) 조리기용 적외선 발열 브리켙의 성형방법
KR19990061709A (ko) 열경화성 불포화 폴리에스테르 수지조성물 및 이를 이용한 인조대리석의 제조방법
JP3076558B1 (ja) 有機廃材再利用品の成形装置、その製造方法
RU2304570C1 (ru) Композиция для изготовления декоративно-отделочных материалов
KR19990053897A (ko) 폐플라스틱을 이용한 바닥재 및 건축벽재용 성형물 및 그 제조방법
JP2007099572A (ja) レジンコンクリート成形品
KR100610657B1 (ko) 인조목재용 세라믹 조성물 및 그 인조목재용 세라믹조성물을 이용한 인조목재 판넬의 제조방법

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AT AU BB BG BR CA CH CS DE DK ES FI GB HU JP KP KR LK LU MG MN MW NL NO PL RO RU SD SE US

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE DK ES FR GB GR IE IT LU MC NL SE BF BJ CF CG CI CM GA GN ML MR SN TD TG

122 Ep: pct application non-entry in european phase
REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

NENP Non-entry into the national phase

Ref country code: CA