WO1993002821A1 - High-speed steel manufactured by powder metallurgy - Google Patents
High-speed steel manufactured by powder metallurgy Download PDFInfo
- Publication number
- WO1993002821A1 WO1993002821A1 PCT/SE1992/000538 SE9200538W WO9302821A1 WO 1993002821 A1 WO1993002821 A1 WO 1993002821A1 SE 9200538 W SE9200538 W SE 9200538W WO 9302821 A1 WO9302821 A1 WO 9302821A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- steel
- speed steel
- max
- carbides
- impurities
- Prior art date
Abstract
Description
Claims