WO1989005221A1 - A method for the production of wood products - Google Patents
A method for the production of wood products Download PDFInfo
- Publication number
- WO1989005221A1 WO1989005221A1 PCT/SE1988/000650 SE8800650W WO8905221A1 WO 1989005221 A1 WO1989005221 A1 WO 1989005221A1 SE 8800650 W SE8800650 W SE 8800650W WO 8905221 A1 WO8905221 A1 WO 8905221A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- adhesive
- hardener
- coated
- package
- veneer
- Prior art date
Links
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B27—WORKING OR PRESERVING WOOD OR SIMILAR MATERIAL; NAILING OR STAPLING MACHINES IN GENERAL
- B27D—WORKING VENEER OR PLYWOOD
- B27D1/00—Joining wood veneer with any material; Forming articles thereby; Preparatory processing of surfaces to be joined, e.g. scoring
- B27D1/04—Joining wood veneer with any material; Forming articles thereby; Preparatory processing of surfaces to be joined, e.g. scoring to produce plywood or articles made therefrom; Plywood sheets
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
- C09J5/00—Adhesive processes in general; Adhesive processes not provided for elsewhere, e.g. relating to primers
- C09J5/04—Adhesive processes in general; Adhesive processes not provided for elsewhere, e.g. relating to primers involving separate application of adhesive ingredients to the different surfaces to be joined
Definitions
- a method for the production of wood products relates to a method for the production of wood products such as plywood or similar products. More particularly the invention relates to an improved cold pressing technique at pre-pressing a package of veneer-
- glue is applied to veneers and a number of glue coated veneers are assembled to a package.
- This package is usually cold pressed before being hot pressed for the final curing.
- the number of veneers in the assembly is determined by the final thick ⁇ ness of the product.
- at least some of the veneers are placed with their grain directions perpendicular to the grain direction of the neighbour veneers. After glue application the veneers remain in the package for a longer or shorter time before this is further treated.
- the veneers hereby absorb moisture from the adhesive, they swell and become still more uneven than they were from the beginning.
- the veneer package becomes larger than the available press table opening of the hot press. To decrease the thickness of the package this must be pre-pressed cold.
- the pre- pressing shall also result in a holding together of the veneer layers at the further handling of the package.
- the cold tack of the adhesive composi- tion ie the bonding strength of the adhesive before this has been cured by heat
- the adhesives used in the manufacture of plywood are usually phenol resins (condensation products of phenol and formaldehyde) and amino resins (condensation products of formaldehyde and urea and/or melamine) .
- the amino resins do, however, give a high release of formaldehyde, both at pressing and from the finished products. If the molar ratio between formaldehyde (F) and comonomer (eg urea (U) ) in the adhesive is lowered, the formaldehyde emission will, however, be decreased. To fulfil the demands with regard to environment it has been necessary to reduce the molar ratio considerably.
- the adhesive has an inferior cold tack and long cold press times are. then required to obtain acceptable results. For reasons of * , economy it is thus desired to have short assembly times and- cold press times. - It is common to try to improve the cold tack of the-; adhesive by different additives. Among others, starch and', gluten are used. In DE A 3125823 it is suggested to add * , acrylate resin dispersions with free carboxylic groups to increase the cold tack of amino resins. The cold press properties of the adhesive are de ⁇ . pendent on several factors, among others on the moisture content of the veneers and the type of wood in these.
- the present invention is directed to an improved method at cold pressing of packages of veneers.
- one surface of a- veneer layer is coated with a curable adhesive in a known' manner.
- the veneer layer to be placed against the thus . adhesive- coated veneer is coated with a separate hardener in a zone along at least two of its edges. If only two edges are coated, those opposite each other are chosen.
- the veneer package is then assembled with every second surface -. coated with adhesive and every second coated with a sepa- . rate hardener.
- the veneer layers will be kept together by means of the cured adhesive along the edges.
- the requirement for sufficient cold tack of the adhesive has thus been eliminated.
- the time for the cold pressing can be kept short, since the separate hardener makes the adhesive cure rapidly.
- the cured adhesive along the edges gives as a result that also those veneers which before the cold pressing have undulating dented edges, due to moisture absorption, after the cold pressing will have straight edges which keep together well.
- the cold pressed veneer package is easy to handle and it is easy to introduce it into the often narrow space between the press platens in the hot press, where the final curing then takes place.
- the veneers can be coated along all four edges.
- the coating of different veneer layers with either adhesive or separate hardener can be carried out in arbitrary order.
- the middle veneer can thus, for example, be coated on both its surfaces with a hardener solution along the edges and the cover veneers can be coated with adhesive on one surface.
- the center veneer can be coated with adhesive on both surfaces and the cover veneers be coated with hardener on one surface, along the edges.
- the separate hardener can be applied in a zone along the edges of the veneer layer.
- a suitable size for this zone can be determined by the man skilled in the art by simple tests. For large veneers a suitable width can be from 10 to 100 mm, preferably from 30 to 60 mm.
- the zone to which the separate hardener has been applied does not have to be entirely coated. It can be sufficient that the zone is coated in strings or in dots along its surface, among other things dependent on the application equipment. 10 mm broad strings can thus for example be applied respectively 15 mm, 25 mm and 50 mm from the edge.
- the method according to the invention can be used with conventional formaldehyde based, curable adhesives which are used in plywood production.
- the applied adhesive contains, as conventional, a slow-reacting hardener for the final curing in the hot press.
- the applied amount of adhesive can vary within wide limits. As a suitable amount can, for example, be mentioned from 100 to 300 g/m .
- a rapid reacting hardener is meant a hardener which gives the adhesive such a gelling time that it cures during the cold press process.
- the hardener should give the adhesive a gelling time of less than 1 hour, preferably of from 5 to 20 minutes. It is not possible to use such a hardener as the sole hardener for the adhesive, since the adhesive would then get a much too short assembly time, which would result in a curing of the adhesive before the veneer package has reached the hot press. Using the present process the adhesive cures only along the edges at the cold pressing.
- the hardener can for example be an inorganic or organic acid, such as phosphoric acid, trichloroacetic acid, citric acid or maleic acid. Acid salts, such as for example aluminium sulphate and aluminium chloride, can also be used, when the adhesive is a phenol resin the edges of the veneer layers can be coated with a basic compound, * eg sodium carbonate.
- a basic compound * eg sodium carbonate.
- the amount of applied separate hardener can also -vary within wide limits.
- a suitable amount can be from 15 to 40 g/m 2 of a 20% aqueous hardener solution.
- the har ⁇ dener can be combined with for example tack giving substan ⁇ ces such as aqueous solutions or aqueous dispersions of poly inyl alcohol, polyvinyl acetate, polyacrylates.
- the press times required at cold pressing are of the same magnitude as for adhesives with good cold tack proper ⁇ ties, and thus in the range of from 5 to 20 minutes, preferably from 10 to 15 minutes.
- Example 1 The invention is further illustrated in the following examples wherein parts and per cent relate to parts by weight and per cent by weight, unless otherwise stated.
- Example 1
- the adhesive had a F:U ratio of 1.16 (as adhesive was used urea resin 1203 from Casco Nobel, 100 parts by weight with 20 parts by weight of hardener, hardener 2545 from Casco Nobel, based on ammonium chloride) .
- the amount of adhesive was 180 g/m 2 for a single adhesive joint.
- test a Two tests were made with variation of the assembly time (ie the time before cold pressing) and the time between cold pressing and hot pressing. Each test was made with separate hardener (test a) and without separate hardener (test b) .
- Example 1 was repeated but with 3 veneers of poplar having the dimensions 300x300x2 mm. The moisture content of these was about 5%.
Landscapes
- Engineering & Computer Science (AREA)
- Life Sciences & Earth Sciences (AREA)
- Manufacturing & Machinery (AREA)
- Mechanical Engineering (AREA)
- Wood Science & Technology (AREA)
- Forests & Forestry (AREA)
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Veneer Processing And Manufacture Of Plywood (AREA)
- Laminated Bodies (AREA)
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
FI902772A FI91501C (fi) | 1987-12-07 | 1990-06-04 | Menetelmä puutuotteiden valmistamiseksi |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SE8704891A SE463608B (sv) | 1987-12-07 | 1987-12-07 | Foerfarande foer framstaellning av traeprodukter |
SE8704891-4 | 1987-12-07 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO1989005221A1 true WO1989005221A1 (en) | 1989-06-15 |
Family
ID=20370530
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/SE1988/000650 WO1989005221A1 (en) | 1987-12-07 | 1988-11-25 | A method for the production of wood products |
Country Status (4)
Country | Link |
---|---|
EP (1) | EP0419477A1 (fi) |
FI (1) | FI91501C (fi) |
SE (1) | SE463608B (fi) |
WO (1) | WO1989005221A1 (fi) |
Cited By (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2002068178A2 (en) | 2001-02-26 | 2002-09-06 | Dynea Wood And Speciality Adhesives | Process of gluing |
WO2003062340A1 (en) * | 2002-01-25 | 2003-07-31 | Akzo Nobel N.V. | Method and apparatus for gluing |
WO2003066765A1 (en) * | 2002-02-07 | 2003-08-14 | Akzo Nobel Coatings International B.V. | Method of joining wood based materials |
RU2457230C1 (ru) * | 2011-03-09 | 2012-07-27 | Государственное образовательное учреждение высшего профессионального образования "Воронежская государственная лесотехническая академия" | Способ склеивания древесных материалов |
RU2459849C1 (ru) * | 2011-03-11 | 2012-08-27 | Государственное образовательное учреждение высшего профессионального образования "Воронежская государственная лесотехническая академия" | Способ склеивания древесных материалов |
WO2012131110A2 (en) | 2011-04-01 | 2012-10-04 | Dynea Oy | System for form pressing with high production efficiency |
US8410204B2 (en) | 2007-07-05 | 2013-04-02 | Akzo Nobel Coatings International B.V. | Hardener composition, adhesive system and method of gluing |
US20130131230A1 (en) * | 2010-08-03 | 2013-05-23 | Basf Se | Tackifiers For Composite Articles |
EP2731976B1 (en) | 2011-07-15 | 2017-03-22 | Akzo Nobel Coatings International B.V. | Adhesive system |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
SE331186B (fi) * | 1970-03-24 | 1970-12-14 | Casco Ab | |
SE368219B (fi) * | 1967-12-29 | 1974-06-24 | Roquette Freres | |
SE370546B (fi) * | 1971-11-22 | 1974-10-21 | Casco Ab | |
SE375317B (fi) * | 1972-04-11 | 1975-04-14 | Casco Ab | |
DE3518947A1 (de) * | 1985-05-25 | 1986-11-27 | Robert Bosch Gmbh, 7000 Stuttgart | Verfahren zum kleben von teilen und durch das verfahren hergestellte klebeverbindung |
-
1987
- 1987-12-07 SE SE8704891A patent/SE463608B/sv not_active IP Right Cessation
-
1988
- 1988-11-25 WO PCT/SE1988/000650 patent/WO1989005221A1/en active IP Right Grant
- 1988-11-25 EP EP19890900337 patent/EP0419477A1/en not_active Ceased
-
1990
- 1990-06-04 FI FI902772A patent/FI91501C/fi not_active IP Right Cessation
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
SE368219B (fi) * | 1967-12-29 | 1974-06-24 | Roquette Freres | |
SE331186B (fi) * | 1970-03-24 | 1970-12-14 | Casco Ab | |
SE370546B (fi) * | 1971-11-22 | 1974-10-21 | Casco Ab | |
SE375317B (fi) * | 1972-04-11 | 1975-04-14 | Casco Ab | |
DE3518947A1 (de) * | 1985-05-25 | 1986-11-27 | Robert Bosch Gmbh, 7000 Stuttgart | Verfahren zum kleben von teilen und durch das verfahren hergestellte klebeverbindung |
Cited By (12)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2002068178A2 (en) | 2001-02-26 | 2002-09-06 | Dynea Wood And Speciality Adhesives | Process of gluing |
WO2002068178A3 (en) * | 2001-02-26 | 2002-12-05 | Dynea Wood And Speciality Adhe | Process of gluing |
WO2003062340A1 (en) * | 2002-01-25 | 2003-07-31 | Akzo Nobel N.V. | Method and apparatus for gluing |
WO2003066765A1 (en) * | 2002-02-07 | 2003-08-14 | Akzo Nobel Coatings International B.V. | Method of joining wood based materials |
AU2003206319B2 (en) * | 2002-02-07 | 2006-03-09 | Akzo Nobel Coatings International B.V. | Method of joining wood based materials |
US8410204B2 (en) | 2007-07-05 | 2013-04-02 | Akzo Nobel Coatings International B.V. | Hardener composition, adhesive system and method of gluing |
US20130131230A1 (en) * | 2010-08-03 | 2013-05-23 | Basf Se | Tackifiers For Composite Articles |
RU2457230C1 (ru) * | 2011-03-09 | 2012-07-27 | Государственное образовательное учреждение высшего профессионального образования "Воронежская государственная лесотехническая академия" | Способ склеивания древесных материалов |
RU2459849C1 (ru) * | 2011-03-11 | 2012-08-27 | Государственное образовательное учреждение высшего профессионального образования "Воронежская государственная лесотехническая академия" | Способ склеивания древесных материалов |
WO2012131110A2 (en) | 2011-04-01 | 2012-10-04 | Dynea Oy | System for form pressing with high production efficiency |
WO2012131110A3 (en) * | 2011-04-01 | 2012-11-22 | Dynea Oy | Process for the manufacture of form- pressed or plywood products having at least three veneer layers and three component adhesive system |
EP2731976B1 (en) | 2011-07-15 | 2017-03-22 | Akzo Nobel Coatings International B.V. | Adhesive system |
Also Published As
Publication number | Publication date |
---|---|
SE463608B (sv) | 1990-12-17 |
FI91501B (fi) | 1994-03-31 |
SE8704891L (sv) | 1989-06-08 |
SE8704891D0 (sv) | 1987-12-07 |
FI91501C (fi) | 1994-07-11 |
FI902772A0 (fi) | 1990-06-04 |
EP0419477A1 (en) | 1991-04-03 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP2265684B1 (en) | Low formaldehyde emission adhesive system | |
US2414415A (en) | Production and utilization of cold setting polyhydric phenolic aldehyde resin adhesives | |
US5944938A (en) | wood bonding method | |
EP1372947B1 (en) | Process of gluing | |
WO1989005221A1 (en) | A method for the production of wood products | |
US6590013B1 (en) | Hardener for use in-urea-formaldehyde and urea-melamine-formaldehyde based adhesives, an adhesive composition comprising said hardener and its use | |
US3793113A (en) | Adhesive compositions and method of making plywood | |
US6569279B1 (en) | Method for bonding composite wood products | |
US4234658A (en) | Wood composites with foliage adhesive | |
US3701743A (en) | Modified urea-formaldehyde plywood adhesive | |
US5342880A (en) | Phenolic resol plywood resin, manufacture and use | |
JPH06330012A (ja) | レゾルシノール系樹脂接着剤組成物 | |
JP2895421B2 (ja) | 通気性被着体用接着剤 | |
US3681274A (en) | Ammonical fluorides for formaldehyde resin systems | |
JPS6227107A (ja) | パ−チクルボ−ド | |
CA2056700C (en) | Adhesive composition comprising isocyanate, phenol-formaldehide and tannin, useful for manufacturing plywoods for exterior application | |
AU2004242047B2 (en) | Method of joining surfaces | |
EP0066560B1 (en) | A method for bonding wood | |
Sontag et al. | Phenolic resin adhesive in the plywood industry | |
JPS61154901A (ja) | 合板の製造方法 | |
JPH02277601A (ja) | 難燃化木材の接着加工法 | |
SE442492B (sv) | Forfarande for framstellning av laminerade trekonstruktioner | |
JPS60238377A (ja) | 湿潤木材用接着剤 | |
Adams et al. | Water resistant plywood adhesive based on whole wheat flour | |
JPS59202801A (ja) | 突板化粧板 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): FI |
|
AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): AT BE CH DE FR GB IT LU NL SE |
|
WWE | Wipo information: entry into national phase |
Ref document number: 1989900337 Country of ref document: EP |
|
WWE | Wipo information: entry into national phase |
Ref document number: 902772 Country of ref document: FI |
|
WWP | Wipo information: published in national office |
Ref document number: 1989900337 Country of ref document: EP |
|
WWR | Wipo information: refused in national office |
Ref document number: 1989900337 Country of ref document: EP |
|
WWW | Wipo information: withdrawn in national office |
Ref document number: 1989900337 Country of ref document: EP |
|
WWG | Wipo information: grant in national office |
Ref document number: 902772 Country of ref document: FI |