WO1987001980A1 - Outil de coupe de finissage et procede de coupe de finissage pour l'acier - Google Patents
Outil de coupe de finissage et procede de coupe de finissage pour l'acier Download PDFInfo
- Publication number
- WO1987001980A1 WO1987001980A1 PCT/JP1986/000497 JP8600497W WO8701980A1 WO 1987001980 A1 WO1987001980 A1 WO 1987001980A1 JP 8600497 W JP8600497 W JP 8600497W WO 8701980 A1 WO8701980 A1 WO 8701980A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- finish cutting
- tool
- cutting
- finish
- oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Links
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23B—TURNING; BORING
- B23B27/00—Tools for turning or boring machines; Tools of a similar kind in general; Accessories therefor
- B23B27/14—Cutting tools of which the bits or tips or cutting inserts are of special material
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
- C04B35/48—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on zirconium or hafnium oxides, zirconates, zircon or hafnates
- C04B35/486—Fine ceramics
- C04B35/488—Composites
- C04B35/4885—Composites with aluminium oxide
Definitions
- the present invention relates to a finish cutting tool and a steel finish cutting method, and in particular, to obtain a cut surface having excellent properties by suppressing a component edge generated at a tool edge when finishing a sulfur cutting.
- the present invention relates to a cutting tool and a finish cutting method for a sulfur plant that can be obtained.
- Sulfur-containing ⁇ is widely accepted as having the advantage of low cutting heat and long tool life due to lower cutting resistance compared to ordinary ⁇ , while sulfur usually has a small part of the work material. Adhered to the tool and hardened by work and existed at a height of about 50 to 100 m on the tool edge. It is known. For example, in the report of the Ministry of International Trade and Industry's Machinery Laboratory, published on August 15, 1956, No. 43, page 57, 0.33% sulfur addition was added to high-speed steel tools (SKH3). Maximum cutting edge for cutting
- the cutting speed when finishing the sulfur at the factory is usually about 20 m / min to 100 mZmin, it is not effective to adjust the cutting speed as a countermeasure for the component edge.
- Is closed cutting tool of sulfur-containing ⁇ primarily high velocity ⁇ instrument Sa is the cemented carbide tool is used and sintered A 2 0 3 Se la Mi click scan, the TiC in N i - main Tsu May also be used.
- Each of these tools adheres to the work material ⁇ to form a component edge based on the cutting temperature and stress of the tool edge, so that the component edge transfers to the cut surface and the surface roughness increases. Is bad.
- the recently developed TiN coating tool has a small degree of adhesion to ⁇ and a small amount of generated cutting edge, so the surface finish is small, but the tool can be re-ground and reused. It has the drawback that it cannot be done, and is not widely used as a finishing tool containing sulfur.
- the continuous casting method has a higher cooling rate than the conventional ingot casting method, so that manganese sulfide in steel is easily refined and its machinability is easily deteriorated. Reported in 205453.
- the first cause of poor surface finish is the falling edge of the cutting edge generated on the rake face of the tool during cutting. Preventing the generation of a built-up edge is the most effective measure to improve the roughness of the cut surface.
- the continuous production method which is smaller than that of free-formed steel, usually about 10 to 120 ⁇ m / piece, requires water cooling, and the cooling rate is lower than that of ingot molding method.
- the growth of manganese sulfide, which precipitates during the solidification process cannot be expected much.
- New paper As a practical measure, increasing the average cross-sectional area of manganese sulfide is not an effective method.
- the present invention is hardly adhered to the surface, and as a result, is capable of forming an excellent cut surface by suppressing the formation of a built-up edge, and is industrially useful in that re-polishing is possible. It is intended to provide a cutting tool for sulfur-containing steel.
- the present invention provides a new cutting method for suppressing the generation of a component edge on a tool rake face and forming a clean finished surface when cutting a sulfur-containing steel in a normal finishing speed range. aimed to.
- the present inventors have found that elements having high chemical affinity with [S] of manganese sulfide interposed in steel are included in the tool, and manganese sulfide is present on the tool surface.
- the present inventors have found that a certain amount of sulfur When finishing with a tool that has an element (Zr) that has a strong chemical affinity with the [s] of the manganese sulfide, the temperature and pressure of the tool edge during the finish cutting are reduced.
- the rake face of the tool in contact with the swarf by the manganese sulfide in the rope being bound with the oxide of Zr in the tool regardless of the size of the manganese sulfide below A manganese sulfide film is formed on the manganese sulfide film, and it has been found that this manganese sulfide film has an effect of preventing adhesion between steel and a tool and suppressing formation of a built-up edge.
- the present inventors succeeded in developing a finish cutting method for sulfur-containing steel capable of obtaining an excellent finished surface and completed the present invention.
- the present invention relates to a ceramic tool for finish cutting of sulfur-containing steel, characterized by containing at least 50 mol%, preferably at least 90 mol% of zirconium oxide, and in terms of weight%. , M ⁇ ; 0.5 to 1.2%, S; 0.05% to 0.4% as a main component, a hot-rolled material containing 50% or more of zirconium oxide.
- a finish cutting method for steel which is characterized in that finish cutting is performed with a ramix tool.
- the term “sulfur-containing” refers to a manganese that contains 0.05% or more by weight of sulfur and is stoichiometrically fixed to sulfur as manganese sulfide. ⁇ which has a large amount of energy. This ⁇ may contain free-cutting elements such as Pb, Te, Se, P and N. When the upper limit of S exceeds 0.4%, the cold workability of ⁇ is reduced, so that 0.4% or less is preferable.
- Mn is preferably 0.5% or more to form manganese sulfide inclusions and to prevent FeS precipitation at the crystal grain boundary of ⁇ and cracking during hot rolling, but 1.2% is preferable. If it exceeds 0.1%, the steel cutting resistance is increased and tool wear is increased, so it is preferably 1.2% or less.Furthermore, chip disposability is improved, and the cutting edge temperature is suppressed by reducing the cutting resistance.
- Pb, 0.02 to 0.40%, Bi, 0.02 to 0.20%, and Te, 0.01 to 0.10%, known as free-cutting elements are required. It may be added immediately. Other components are C: 0.05 to 0.50%. Si: 0.001 to 0.35%, P: 0.005 to 0.10%, balance Fe and inevitable impurities.
- Iwo Sha Yu may be manufactured through an ingot-making process or through a continuous longevity process.
- a continuous ⁇ bloom size of the sulfur-containing free-cutting steel is produced through a process 400 x 600 2 order of 100 X 100 mm 2, the ratio amount of water is 1 kg * s tee 1 ⁇ 2 / kg.
- S tee i The average cross-sectional area of MnS in the steel after hot rolling is in the range of 10 to 120 nf.
- the average cross-sectional area of MnS was measured using an optical microscope with a magnification of 200 for manganese sulfide within 1 square M in the rolling direction of steel. At that time, fine manganese sulfides of 5 or less were excluded.
- the finishing cutting tool for the finishing tool is described.
- the lower limit of oxidizing zirconium Niu arm (ZrO 2) and 50% is to ensure Z r required to react with the manganese sulfide in the steel
- the ZrO. 2 of T. instrument substantially It can also be a target component.
- aluminum oxide two ⁇ beam ⁇ 2 0 3
- ⁇ of Mug Information & Technology arm MgO
- oxidized I tree Application Benefits U beam Y z 0 3
- neodymium oxide and cerium oxide (CeO) The upper limit of the content is 20 mol% for each component.
- a slab consisting of the components of the present invention is manufactured under continuous manufacturing or ingot manufacturing equipment under ordinary manufacturing conditions, and the slab is heated to a rolling temperature using a heating furnace, and hot-rolled. After manufacturing steel bars or by-line coils, move to the cutting process. In some cases, after rolling, the material may be transferred to the cutting process after annealing and drawing.
- Chip oxidized zirconium Niu-free tool is pressing (CIP) after forming the primary and Z r 0 2 Other powder, then calcined in air
- a tool is a tool whose constituent material forms a disposable blade tip called a throwaway tip, a tip with a bite with a blade, a tip with a finished byte, or at least an existing tool. It means that these substances are diffused, bonded, and sprayed on the cutting edge.
- New pig iron In the cutting process, rough cutting is performed using a high-speed tool or a cemented carbide tool, and finish cutting is performed with a ceramic tool containing Zr of the present invention at a cutting speed of about 100 m / min or less. As a result, it is possible to obtain an extremely smooth cut surface with a finished surface roughness of 4 to 7 im on average.
- Table 1 shows the effects of the tool of the present invention in comparison with comparative tools.
- A1S1 Commercial low-carbon sulfur-lead free cutting steel equivalent to 12L14 is applied to the rotating shaft using a parting-type tool with a tool edge shape, 20 ° rake angle, 6 ° clearance angle, and 5 ⁇ tool width.
- a turning test was performed at right angles to the direction. The cutting speed was 60 m / min, the feed was 0.05 rev, and the cutting cycle was 2 sec cutting and 5 sec non-cutting.
- the manganese sulfide film formed on the tool tip and the constituent cutting edges were observed with an optical microscope.
- the former was evaluated with the ratio of the manganese sulfide film area to the tool-chip contact area, and the latter was evaluated with or without formation. did.
- the value of the cut surface roughness is the value at the time of cutting cycle 800, expressed as R 2 (JIS).
- the manganese sulfide film occupies 89% to 95% of the tool-chip contact area, the component cutting edge is not formed, and the cut surface finish is rough. The size is small and the tool is better.
- 1 1 0 mol% of CeO. 2 is a 3 mole percent Y z 0 3
- 3 contains 1 0 mol% of MgO.
- Table 2 shows the effect of the cutting method of the present invention in comparison with the comparative cutting method.
- the tool is used after molding into a slurry-type chip and then sintering.
- the sample is a hot-rolled material manufactured through a series
- the cutting test method is as follows. Tool edge shape,
- a cutting test in the direction perpendicular to the shaft was performed using a tool.
- the front flank wear width (JIS display VB) was adopted.
- New paper Cutting Saprun 4 ⁇ Machining Surface roughness Rz is less than 7.4 ⁇ m.
- the finished surface roughness is poor.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Composite Materials (AREA)
- Ceramic Engineering (AREA)
- Manufacturing & Machinery (AREA)
- Materials Engineering (AREA)
- Structural Engineering (AREA)
- Organic Chemistry (AREA)
- Mechanical Engineering (AREA)
- Cutting Tools, Boring Holders, And Turrets (AREA)
- Turning (AREA)
Priority Applications (3)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| DE8686905922T DE3687837T2 (de) | 1985-09-27 | 1986-09-27 | Endbearbeitungsschneidwerkzeug und endbearbeitungsschneidverfahren fuer stahl. |
| JP61-505045A JPH0818164B2 (ja) | 1985-09-27 | 1986-09-27 | 鋼の仕上切削方法 |
| KR870700451A KR870700428A (ko) | 1985-09-27 | 1987-05-27 | 마무리 절삭공구 및 강의 마무리 절삭방법 |
Applications Claiming Priority (2)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| JP21269485 | 1985-09-27 | ||
| JP60/212694 | 1985-09-27 |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| WO1987001980A1 true WO1987001980A1 (fr) | 1987-04-09 |
Family
ID=16626880
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| PCT/JP1986/000497 Ceased WO1987001980A1 (fr) | 1985-09-27 | 1986-09-27 | Outil de coupe de finissage et procede de coupe de finissage pour l'acier |
Country Status (6)
| Country | Link |
|---|---|
| EP (1) | EP0250595B1 (enExample) |
| JP (1) | JPH0818164B2 (enExample) |
| KR (1) | KR870700428A (enExample) |
| AU (1) | AU586708B2 (enExample) |
| DE (1) | DE3687837T2 (enExample) |
| WO (1) | WO1987001980A1 (enExample) |
Cited By (2)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US5889603A (en) * | 1996-12-04 | 1999-03-30 | Ut Automotive Dearborn, Inc. | Optical drive away prevention security system |
| CN113524393A (zh) * | 2021-07-02 | 2021-10-22 | 红云红河烟草(集团)有限责任公司 | 一种切丝机专用陶瓷刀片及制造方法 |
Families Citing this family (1)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| DE102011008998B4 (de) | 2011-01-19 | 2024-07-25 | Mercedes-Benz Group AG | Verfahren zum spanenden Bearbeiten eines Werkstücks |
Citations (5)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| EP0013599A1 (en) * | 1979-01-04 | 1980-07-23 | Commonwealth Scientific And Industrial Research Organisation | Partially stabilized zirconia ceramics; method of making said ceramics, dies constructed of said ceramics, cutting tools with a cutting surface and tappet facings formed of said ceramics |
| JPS57205374A (en) * | 1981-06-09 | 1982-12-16 | Ngk Spark Plug Co | Sintered body for cutting tool and manufacture |
| JPS589784B2 (ja) * | 1979-04-13 | 1983-02-22 | 日本化学陶業株式会社 | ジルコニア質切削工具材 |
| JPS58185477A (ja) * | 1982-04-21 | 1983-10-29 | 三菱マテリアル株式会社 | 高速切削性能にすぐれた切削工具用セラミック材料の製造法 |
| JPS59162173A (ja) * | 1983-03-07 | 1984-09-13 | 東ソー株式会社 | ジルコニア焼結体 |
Family Cites Families (2)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| JPS6010377A (ja) * | 1983-06-30 | 1985-01-19 | Ricoh Co Ltd | メモリ・マルチアクセス制御方式 |
| JPH0280241A (ja) * | 1988-09-16 | 1990-03-20 | Sumitomo Electric Ind Ltd | フレキシブル配線基板 |
-
1986
- 1986-09-27 EP EP86905922A patent/EP0250595B1/en not_active Expired - Lifetime
- 1986-09-27 WO PCT/JP1986/000497 patent/WO1987001980A1/ja not_active Ceased
- 1986-09-27 AU AU64055/86A patent/AU586708B2/en not_active Ceased
- 1986-09-27 JP JP61-505045A patent/JPH0818164B2/ja not_active Expired - Lifetime
- 1986-09-27 DE DE8686905922T patent/DE3687837T2/de not_active Expired - Fee Related
-
1987
- 1987-05-27 KR KR870700451A patent/KR870700428A/ko not_active Ceased
Patent Citations (5)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| EP0013599A1 (en) * | 1979-01-04 | 1980-07-23 | Commonwealth Scientific And Industrial Research Organisation | Partially stabilized zirconia ceramics; method of making said ceramics, dies constructed of said ceramics, cutting tools with a cutting surface and tappet facings formed of said ceramics |
| JPS589784B2 (ja) * | 1979-04-13 | 1983-02-22 | 日本化学陶業株式会社 | ジルコニア質切削工具材 |
| JPS57205374A (en) * | 1981-06-09 | 1982-12-16 | Ngk Spark Plug Co | Sintered body for cutting tool and manufacture |
| JPS58185477A (ja) * | 1982-04-21 | 1983-10-29 | 三菱マテリアル株式会社 | 高速切削性能にすぐれた切削工具用セラミック材料の製造法 |
| JPS59162173A (ja) * | 1983-03-07 | 1984-09-13 | 東ソー株式会社 | ジルコニア焼結体 |
Non-Patent Citations (1)
| Title |
|---|
| See also references of EP0250595A4 * |
Cited By (3)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US5889603A (en) * | 1996-12-04 | 1999-03-30 | Ut Automotive Dearborn, Inc. | Optical drive away prevention security system |
| CN113524393A (zh) * | 2021-07-02 | 2021-10-22 | 红云红河烟草(集团)有限责任公司 | 一种切丝机专用陶瓷刀片及制造方法 |
| CN113524393B (zh) * | 2021-07-02 | 2022-11-15 | 红云红河烟草(集团)有限责任公司 | 一种切丝机专用陶瓷刀片及制造方法 |
Also Published As
| Publication number | Publication date |
|---|---|
| JPH0818164B2 (ja) | 1996-02-28 |
| EP0250595A1 (en) | 1988-01-07 |
| JPH0818164B1 (enExample) | 1996-02-28 |
| DE3687837D1 (de) | 1993-04-01 |
| EP0250595B1 (en) | 1993-02-24 |
| KR870700428A (ko) | 1987-12-29 |
| EP0250595A4 (en) | 1988-04-27 |
| AU586708B2 (en) | 1989-07-20 |
| AU6405586A (en) | 1987-04-24 |
| DE3687837T2 (de) | 1993-09-09 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| KR910002870B1 (ko) | 연속주조에 의해 제조된 저탄소-황 쾌삭강 | |
| EP0009859B1 (en) | Ceramic cutting tool composition, method of its manufacture and its use in machining cast iron | |
| US3846186A (en) | Stainless steel having improved machinability | |
| WO1987001980A1 (fr) | Outil de coupe de finissage et procede de coupe de finissage pour l'acier | |
| Thangaraj et al. | On the wear mechanisms and cutting performance of silicon carbide whisker-reinforced alumina | |
| JP6801541B2 (ja) | 機械構造用鋼およびその切削方法 | |
| Kankaanpää et al. | Machinability of calcium-treated steels using TiN-coated high-speed steel tools | |
| JP3901582B2 (ja) | 金型用快削鋼 | |
| JPH07173573A (ja) | 超硬工具による被削性と内部品質にすぐれる快削鋼 | |
| JPWO1987001980A1 (ja) | 鋼の仕上切削方法 | |
| JP2003049240A (ja) | 快削鋼 | |
| US3829312A (en) | Process for the manufacture of steel of good machinability | |
| JP4264175B2 (ja) | 被削性に優れた快削用棒鋼およびその製法 | |
| JP3698656B2 (ja) | 切削工具 | |
| CN113621892A (zh) | 一种抗冲击力强的硬质合金铣刀及其制备方法 | |
| JP3707675B2 (ja) | 工具摩耗抑制片状黒鉛鋳鉄 | |
| JPS63295104A (ja) | 硫黄含有鋼の仕上げ切削用工具および仕上げ切削方法 | |
| JP3581882B2 (ja) | 鉛フリー高強度快削鋼 | |
| JP2682945B2 (ja) | 工具寿命と仕上げ面粗さの優れた黒鉛快削鋼 | |
| JPH09291333A (ja) | 接種調製快削鋳鉄及びその切削方法 | |
| JPS62152604A (ja) | 硫黄含有鋼用切削工具 | |
| JPS61110754A (ja) | 低炭素硫黄−鉛快削鋼 | |
| JP2006255848A (ja) | 低炭快削鋼の切削工具及び切削方法 | |
| Tanaka et al. | Cutting performance of ceramic tools in turning of mild steel | |
| JP2002307201A (ja) | 機械構造用鋼の旋削方法 |
Legal Events
| Date | Code | Title | Description |
|---|---|---|---|
| AK | Designated states |
Kind code of ref document: A1 Designated state(s): AU JP KR US |
|
| AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): DE FR GB IT SE |
|
| WWE | Wipo information: entry into national phase |
Ref document number: 1986905922 Country of ref document: EP |
|
| WWP | Wipo information: published in national office |
Ref document number: 1986905922 Country of ref document: EP |
|
| WWG | Wipo information: grant in national office |
Ref document number: 1986905922 Country of ref document: EP |