US20240101870A1 - Void-containing layer, laminate, method for producing void-containing layer, optical member, and optical apparatus - Google Patents
Void-containing layer, laminate, method for producing void-containing layer, optical member, and optical apparatus Download PDFInfo
- Publication number
- US20240101870A1 US20240101870A1 US18/274,070 US202218274070A US2024101870A1 US 20240101870 A1 US20240101870 A1 US 20240101870A1 US 202218274070 A US202218274070 A US 202218274070A US 2024101870 A1 US2024101870 A1 US 2024101870A1
- Authority
- US
- United States
- Prior art keywords
- void
- group
- containing layer
- sensitive adhesive
- pressure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Links
- 239000011800 void material Substances 0.000 title claims abstract description 434
- 238000004519 manufacturing process Methods 0.000 title claims description 122
- 230000003287 optical effect Effects 0.000 title claims description 29
- 239000004820 Pressure-sensitive adhesive Substances 0.000 claims abstract description 290
- 239000002245 particle Substances 0.000 claims abstract description 124
- 239000000853 adhesive Substances 0.000 claims abstract description 107
- 230000001070 adhesive effect Effects 0.000 claims abstract description 107
- 125000000217 alkyl group Chemical group 0.000 claims abstract description 41
- 239000011203 carbon fibre reinforced carbon Substances 0.000 claims abstract description 16
- CREMABGTGYGIQB-UHFFFAOYSA-N carbon carbon Chemical compound C.C CREMABGTGYGIQB-UHFFFAOYSA-N 0.000 claims abstract description 12
- 125000000962 organic group Chemical group 0.000 claims abstract description 12
- 150000002484 inorganic compounds Chemical group 0.000 claims abstract description 8
- 229910010272 inorganic material Inorganic materials 0.000 claims abstract description 8
- 239000011246 composite particle Substances 0.000 claims abstract description 6
- 239000010410 layer Substances 0.000 claims description 468
- 238000000576 coating method Methods 0.000 claims description 176
- 239000011248 coating agent Substances 0.000 claims description 171
- 239000012790 adhesive layer Substances 0.000 claims description 130
- 239000011148 porous material Substances 0.000 claims description 99
- 239000000178 monomer Substances 0.000 claims description 89
- 239000000126 substance Substances 0.000 claims description 77
- 238000001035 drying Methods 0.000 claims description 73
- 238000000034 method Methods 0.000 claims description 73
- NIXOWILDQLNWCW-UHFFFAOYSA-M Acrylate Chemical compound [O-]C(=O)C=C NIXOWILDQLNWCW-UHFFFAOYSA-M 0.000 claims description 58
- 229920000058 polyacrylate Polymers 0.000 claims description 49
- 238000012360 testing method Methods 0.000 claims description 41
- NIXOWILDQLNWCW-UHFFFAOYSA-N acrylic acid group Chemical group C(C=C)(=O)O NIXOWILDQLNWCW-UHFFFAOYSA-N 0.000 claims description 40
- 239000003431 cross linking reagent Substances 0.000 claims description 35
- 239000012948 isocyanate Substances 0.000 claims description 27
- 125000004432 carbon atom Chemical group C* 0.000 claims description 25
- 150000002513 isocyanates Chemical class 0.000 claims description 23
- 239000007788 liquid Substances 0.000 claims description 20
- 125000000623 heterocyclic group Chemical group 0.000 claims description 19
- CERQOIWHTDAKMF-UHFFFAOYSA-N Methacrylic acid Chemical compound CC(=C)C(O)=O CERQOIWHTDAKMF-UHFFFAOYSA-N 0.000 claims description 16
- 125000004435 hydrogen atom Chemical group [H]* 0.000 claims description 16
- 239000006185 dispersion Substances 0.000 claims description 15
- 150000001451 organic peroxides Chemical class 0.000 claims description 14
- 125000002768 hydroxyalkyl group Chemical group 0.000 claims description 12
- SNVLJLYUUXKWOJ-UHFFFAOYSA-N methylidenecarbene Chemical compound C=[C] SNVLJLYUUXKWOJ-UHFFFAOYSA-N 0.000 claims description 8
- 229910052710 silicon Inorganic materials 0.000 claims description 8
- 238000003860 storage Methods 0.000 claims description 8
- 125000002947 alkylene group Chemical group 0.000 claims description 7
- 125000006365 alkylene oxy carbonyl group Chemical group 0.000 claims description 6
- 125000005740 oxycarbonyl group Chemical group [*:1]OC([*:2])=O 0.000 claims description 6
- 125000000325 methylidene group Chemical group [H]C([H])=* 0.000 claims description 5
- 125000004429 atom Chemical group 0.000 claims description 4
- 125000001033 ether group Chemical group 0.000 claims description 4
- 229910052749 magnesium Inorganic materials 0.000 claims description 4
- 229910052725 zinc Inorganic materials 0.000 claims description 4
- 229910052726 zirconium Inorganic materials 0.000 claims description 4
- 229910052782 aluminium Inorganic materials 0.000 claims description 3
- 230000000379 polymerizing effect Effects 0.000 claims description 3
- 229910052719 titanium Inorganic materials 0.000 claims description 2
- 239000000499 gel Substances 0.000 description 293
- 239000002904 solvent Substances 0.000 description 242
- 239000000243 solution Substances 0.000 description 202
- 239000000047 product Substances 0.000 description 190
- 239000010408 film Substances 0.000 description 115
- 150000003377 silicon compounds Chemical class 0.000 description 96
- 238000010298 pulverizing process Methods 0.000 description 95
- KFZMGEQAYNKOFK-UHFFFAOYSA-N Isopropanol Chemical compound CC(C)O KFZMGEQAYNKOFK-UHFFFAOYSA-N 0.000 description 90
- 239000003054 catalyst Substances 0.000 description 89
- 150000001875 compounds Chemical class 0.000 description 67
- -1 trimethylene oxycarbonyl group Chemical group 0.000 description 54
- ZXEKIIBDNHEJCQ-UHFFFAOYSA-N isobutanol Chemical compound CC(C)CO ZXEKIIBDNHEJCQ-UHFFFAOYSA-N 0.000 description 48
- 230000032683 aging Effects 0.000 description 47
- 239000000463 material Substances 0.000 description 44
- 239000002105 nanoparticle Substances 0.000 description 39
- LFQSCWFLJHTTHZ-UHFFFAOYSA-N Ethanol Chemical compound CCO LFQSCWFLJHTTHZ-UHFFFAOYSA-N 0.000 description 37
- IAZDPXIOMUYVGZ-UHFFFAOYSA-N Dimethylsulphoxide Chemical compound CS(C)=O IAZDPXIOMUYVGZ-UHFFFAOYSA-N 0.000 description 34
- 229920001296 polysiloxane Polymers 0.000 description 34
- 238000004132 cross linking Methods 0.000 description 33
- 238000010438 heat treatment Methods 0.000 description 31
- 230000008569 process Effects 0.000 description 30
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 description 28
- 235000019441 ethanol Nutrition 0.000 description 27
- 239000002243 precursor Substances 0.000 description 27
- 238000006243 chemical reaction Methods 0.000 description 26
- BFXIKLCIZHOAAZ-UHFFFAOYSA-N methyltrimethoxysilane Chemical compound CO[Si](C)(OC)OC BFXIKLCIZHOAAZ-UHFFFAOYSA-N 0.000 description 25
- 125000000524 functional group Chemical group 0.000 description 24
- 229940035429 isobutyl alcohol Drugs 0.000 description 24
- 238000001879 gelation Methods 0.000 description 22
- 230000035515 penetration Effects 0.000 description 22
- 229920005989 resin Polymers 0.000 description 22
- 239000011347 resin Substances 0.000 description 22
- BTANRVKWQNVYAZ-UHFFFAOYSA-N butan-2-ol Chemical compound CCC(C)O BTANRVKWQNVYAZ-UHFFFAOYSA-N 0.000 description 21
- 125000003709 fluoroalkyl group Chemical group 0.000 description 21
- LRHPLDYGYMQRHN-UHFFFAOYSA-N N-Butanol Chemical compound CCCCO LRHPLDYGYMQRHN-UHFFFAOYSA-N 0.000 description 19
- NKSJNEHGWDZZQF-UHFFFAOYSA-N ethenyl(trimethoxy)silane Chemical compound CO[Si](OC)(OC)C=C NKSJNEHGWDZZQF-UHFFFAOYSA-N 0.000 description 19
- ZMXDDKWLCZADIW-UHFFFAOYSA-N N,N-Dimethylformamide Chemical compound CN(C)C=O ZMXDDKWLCZADIW-UHFFFAOYSA-N 0.000 description 18
- MUBZPKHOEPUJKR-UHFFFAOYSA-N Oxalic acid Chemical compound OC(=O)C(O)=O MUBZPKHOEPUJKR-UHFFFAOYSA-N 0.000 description 18
- 125000005372 silanol group Chemical group 0.000 description 17
- BLRPTPMANUNPDV-UHFFFAOYSA-N Silane Chemical compound [SiH4] BLRPTPMANUNPDV-UHFFFAOYSA-N 0.000 description 16
- 230000018044 dehydration Effects 0.000 description 16
- 238000006297 dehydration reaction Methods 0.000 description 16
- 238000000691 measurement method Methods 0.000 description 16
- 229910000077 silane Inorganic materials 0.000 description 16
- OKKJLVBELUTLKV-UHFFFAOYSA-N Methanol Chemical compound OC OKKJLVBELUTLKV-UHFFFAOYSA-N 0.000 description 15
- 238000006482 condensation reaction Methods 0.000 description 15
- 125000002496 methyl group Chemical group [H]C([H])([H])* 0.000 description 15
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 description 14
- 230000015572 biosynthetic process Effects 0.000 description 14
- 239000000203 mixture Substances 0.000 description 14
- RTZKZFJDLAIYFH-UHFFFAOYSA-N ether Substances CCOCC RTZKZFJDLAIYFH-UHFFFAOYSA-N 0.000 description 13
- ZWEHNKRNPOVVGH-UHFFFAOYSA-N 2-Butanone Chemical compound CCC(C)=O ZWEHNKRNPOVVGH-UHFFFAOYSA-N 0.000 description 12
- XEKOWRVHYACXOJ-UHFFFAOYSA-N Ethyl acetate Chemical compound CCOC(C)=O XEKOWRVHYACXOJ-UHFFFAOYSA-N 0.000 description 12
- AMQJEAYHLZJPGS-UHFFFAOYSA-N N-Pentanol Chemical compound CCCCCO AMQJEAYHLZJPGS-UHFFFAOYSA-N 0.000 description 12
- 125000001931 aliphatic group Chemical group 0.000 description 12
- 238000009835 boiling Methods 0.000 description 12
- 238000009826 distribution Methods 0.000 description 12
- 238000005259 measurement Methods 0.000 description 12
- 238000002834 transmittance Methods 0.000 description 12
- 239000003795 chemical substances by application Substances 0.000 description 11
- 239000002121 nanofiber Substances 0.000 description 11
- 229920000642 polymer Polymers 0.000 description 11
- 230000000052 comparative effect Effects 0.000 description 10
- 238000002156 mixing Methods 0.000 description 10
- 229920000139 polyethylene terephthalate Polymers 0.000 description 10
- 239000005020 polyethylene terephthalate Substances 0.000 description 10
- 239000003505 polymerization initiator Substances 0.000 description 10
- QTBSBXVTEAMEQO-UHFFFAOYSA-N Acetic acid Chemical compound CC(O)=O QTBSBXVTEAMEQO-UHFFFAOYSA-N 0.000 description 9
- CSCPPACGZOOCGX-UHFFFAOYSA-N Acetone Chemical compound CC(C)=O CSCPPACGZOOCGX-UHFFFAOYSA-N 0.000 description 9
- HRPVXLWXLXDGHG-UHFFFAOYSA-N Acrylamide Chemical compound NC(=O)C=C HRPVXLWXLXDGHG-UHFFFAOYSA-N 0.000 description 9
- IJGRMHOSHXDMSA-UHFFFAOYSA-N Atomic nitrogen Chemical compound N#N IJGRMHOSHXDMSA-UHFFFAOYSA-N 0.000 description 9
- KWYUFKZDYYNOTN-UHFFFAOYSA-M Potassium hydroxide Chemical compound [OH-].[K+] KWYUFKZDYYNOTN-UHFFFAOYSA-M 0.000 description 9
- XUIMIQQOPSSXEZ-UHFFFAOYSA-N Silicon Chemical compound [Si] XUIMIQQOPSSXEZ-UHFFFAOYSA-N 0.000 description 9
- HEMHJVSKTPXQMS-UHFFFAOYSA-M Sodium hydroxide Chemical compound [OH-].[Na+] HEMHJVSKTPXQMS-UHFFFAOYSA-M 0.000 description 9
- YXFVVABEGXRONW-UHFFFAOYSA-N Toluene Chemical compound CC1=CC=CC=C1 YXFVVABEGXRONW-UHFFFAOYSA-N 0.000 description 9
- 239000003995 emulsifying agent Substances 0.000 description 9
- 125000001153 fluoro group Chemical group F* 0.000 description 9
- 230000007246 mechanism Effects 0.000 description 9
- VLKZOEOYAKHREP-UHFFFAOYSA-N n-Hexane Chemical compound CCCCCC VLKZOEOYAKHREP-UHFFFAOYSA-N 0.000 description 9
- 125000000391 vinyl group Chemical group [H]C([*])=C([H])[H] 0.000 description 9
- ARXJGSRGQADJSQ-UHFFFAOYSA-N 1-methoxypropan-2-ol Chemical compound COCC(C)O ARXJGSRGQADJSQ-UHFFFAOYSA-N 0.000 description 8
- NTIZESTWPVYFNL-UHFFFAOYSA-N Methyl isobutyl ketone Chemical compound CC(C)CC(C)=O NTIZESTWPVYFNL-UHFFFAOYSA-N 0.000 description 8
- UIHCLUNTQKBZGK-UHFFFAOYSA-N Methyl isobutyl ketone Natural products CCC(C)C(C)=O UIHCLUNTQKBZGK-UHFFFAOYSA-N 0.000 description 8
- WYURNTSHIVDZCO-UHFFFAOYSA-N Tetrahydrofuran Chemical compound C1CCOC1 WYURNTSHIVDZCO-UHFFFAOYSA-N 0.000 description 8
- 239000002390 adhesive tape Substances 0.000 description 8
- 239000002612 dispersion medium Substances 0.000 description 8
- 239000011521 glass Substances 0.000 description 8
- 239000001257 hydrogen Substances 0.000 description 8
- 229910052739 hydrogen Inorganic materials 0.000 description 8
- 230000014759 maintenance of location Effects 0.000 description 8
- 239000002994 raw material Substances 0.000 description 8
- 230000002829 reductive effect Effects 0.000 description 8
- 239000007787 solid Substances 0.000 description 8
- SMZOUWXMTYCWNB-UHFFFAOYSA-N 2-(2-methoxy-5-methylphenyl)ethanamine Chemical compound COC1=CC=C(C)C=C1CCN SMZOUWXMTYCWNB-UHFFFAOYSA-N 0.000 description 7
- ZNQVEEAIQZEUHB-UHFFFAOYSA-N 2-ethoxyethanol Chemical compound CCOCCO ZNQVEEAIQZEUHB-UHFFFAOYSA-N 0.000 description 7
- VEXZGXHMUGYJMC-UHFFFAOYSA-N Hydrochloric acid Chemical compound Cl VEXZGXHMUGYJMC-UHFFFAOYSA-N 0.000 description 7
- 229910052731 fluorine Inorganic materials 0.000 description 7
- 239000011737 fluorine Substances 0.000 description 7
- 239000000377 silicon dioxide Substances 0.000 description 7
- XLPJNCYCZORXHG-UHFFFAOYSA-N 1-morpholin-4-ylprop-2-en-1-one Chemical compound C=CC(=O)N1CCOCC1 XLPJNCYCZORXHG-UHFFFAOYSA-N 0.000 description 6
- OZAIFHULBGXAKX-UHFFFAOYSA-N 2-(2-cyanopropan-2-yldiazenyl)-2-methylpropanenitrile Chemical compound N#CC(C)(C)N=NC(C)(C)C#N OZAIFHULBGXAKX-UHFFFAOYSA-N 0.000 description 6
- OMPJBNCRMGITSC-UHFFFAOYSA-N Benzoylperoxide Chemical compound C=1C=CC=CC=1C(=O)OOC(=O)C1=CC=CC=C1 OMPJBNCRMGITSC-UHFFFAOYSA-N 0.000 description 6
- 229920008347 Cellulose acetate propionate Polymers 0.000 description 6
- 229920002284 Cellulose triacetate Polymers 0.000 description 6
- 229920000089 Cyclic olefin copolymer Polymers 0.000 description 6
- 239000004698 Polyethylene Substances 0.000 description 6
- 239000004743 Polypropylene Substances 0.000 description 6
- NNLVGZFZQQXQNW-ADJNRHBOSA-N [(2r,3r,4s,5r,6s)-4,5-diacetyloxy-3-[(2s,3r,4s,5r,6r)-3,4,5-triacetyloxy-6-(acetyloxymethyl)oxan-2-yl]oxy-6-[(2r,3r,4s,5r,6s)-4,5,6-triacetyloxy-2-(acetyloxymethyl)oxan-3-yl]oxyoxan-2-yl]methyl acetate Chemical compound O([C@@H]1O[C@@H]([C@H]([C@H](OC(C)=O)[C@H]1OC(C)=O)O[C@H]1[C@@H]([C@@H](OC(C)=O)[C@H](OC(C)=O)[C@@H](COC(C)=O)O1)OC(C)=O)COC(=O)C)[C@@H]1[C@@H](COC(C)=O)O[C@@H](OC(C)=O)[C@H](OC(C)=O)[C@H]1OC(C)=O NNLVGZFZQQXQNW-ADJNRHBOSA-N 0.000 description 6
- 235000019400 benzoyl peroxide Nutrition 0.000 description 6
- 230000008859 change Effects 0.000 description 6
- 230000007423 decrease Effects 0.000 description 6
- 238000000151 deposition Methods 0.000 description 6
- 230000008021 deposition Effects 0.000 description 6
- 238000005227 gel permeation chromatography Methods 0.000 description 6
- 125000002887 hydroxy group Chemical group [H]O* 0.000 description 6
- 238000005286 illumination Methods 0.000 description 6
- 238000007654 immersion Methods 0.000 description 6
- 235000006408 oxalic acid Nutrition 0.000 description 6
- 125000005010 perfluoroalkyl group Chemical group 0.000 description 6
- 229920000573 polyethylene Polymers 0.000 description 6
- 238000006116 polymerization reaction Methods 0.000 description 6
- 229920001155 polypropylene Polymers 0.000 description 6
- 229920006395 saturated elastomer Polymers 0.000 description 6
- 238000003756 stirring Methods 0.000 description 6
- 229920005992 thermoplastic resin Polymers 0.000 description 6
- 238000004804 winding Methods 0.000 description 6
- XNWFRZJHXBZDAG-UHFFFAOYSA-N 2-METHOXYETHANOL Chemical compound COCCO XNWFRZJHXBZDAG-UHFFFAOYSA-N 0.000 description 5
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 description 5
- 229920003171 Poly (ethylene oxide) Polymers 0.000 description 5
- 125000005396 acrylic acid ester group Chemical group 0.000 description 5
- 125000003647 acryloyl group Chemical group O=C([*])C([H])=C([H])[H] 0.000 description 5
- 239000012986 chain transfer agent Substances 0.000 description 5
- 230000000694 effects Effects 0.000 description 5
- 238000005401 electroluminescence Methods 0.000 description 5
- 238000006460 hydrolysis reaction Methods 0.000 description 5
- 238000010030 laminating Methods 0.000 description 5
- 239000003960 organic solvent Substances 0.000 description 5
- 239000004814 polyurethane Substances 0.000 description 5
- 229920002635 polyurethane Polymers 0.000 description 5
- 238000004626 scanning electron microscopy Methods 0.000 description 5
- 239000010703 silicon Substances 0.000 description 5
- WEVYAHXRMPXWCK-UHFFFAOYSA-N Acetonitrile Chemical compound CC#N WEVYAHXRMPXWCK-UHFFFAOYSA-N 0.000 description 4
- QGZKDVFQNNGYKY-UHFFFAOYSA-N Ammonia Chemical compound N QGZKDVFQNNGYKY-UHFFFAOYSA-N 0.000 description 4
- VHUUQVKOLVNVRT-UHFFFAOYSA-N Ammonium hydroxide Chemical compound [NH4+].[OH-] VHUUQVKOLVNVRT-UHFFFAOYSA-N 0.000 description 4
- 239000004342 Benzoyl peroxide Substances 0.000 description 4
- LYCAIKOWRPUZTN-UHFFFAOYSA-N Ethylene glycol Chemical compound OCCO LYCAIKOWRPUZTN-UHFFFAOYSA-N 0.000 description 4
- 239000005057 Hexamethylene diisocyanate Substances 0.000 description 4
- FXHOOIRPVKKKFG-UHFFFAOYSA-N N,N-Dimethylacetamide Chemical compound CN(C)C(C)=O FXHOOIRPVKKKFG-UHFFFAOYSA-N 0.000 description 4
- IMNFDUFMRHMDMM-UHFFFAOYSA-N N-Heptane Chemical compound CCCCCCC IMNFDUFMRHMDMM-UHFFFAOYSA-N 0.000 description 4
- SECXISVLQFMRJM-UHFFFAOYSA-N N-Methylpyrrolidone Chemical compound CN1CCCC1=O SECXISVLQFMRJM-UHFFFAOYSA-N 0.000 description 4
- PPBRXRYQALVLMV-UHFFFAOYSA-N Styrene Chemical compound C=CC1=CC=CC=C1 PPBRXRYQALVLMV-UHFFFAOYSA-N 0.000 description 4
- 125000003545 alkoxy group Chemical group 0.000 description 4
- 235000011114 ammonium hydroxide Nutrition 0.000 description 4
- 230000005540 biological transmission Effects 0.000 description 4
- 125000003178 carboxy group Chemical group [H]OC(*)=O 0.000 description 4
- 238000009833 condensation Methods 0.000 description 4
- 230000005494 condensation Effects 0.000 description 4
- 238000010528 free radical solution polymerization reaction Methods 0.000 description 4
- 238000007756 gravure coating Methods 0.000 description 4
- RRAMGCGOFNQTLD-UHFFFAOYSA-N hexamethylene diisocyanate Chemical compound O=C=NCCCCCCN=C=O RRAMGCGOFNQTLD-UHFFFAOYSA-N 0.000 description 4
- 230000007062 hydrolysis Effects 0.000 description 4
- 230000002401 inhibitory effect Effects 0.000 description 4
- 150000002576 ketones Chemical class 0.000 description 4
- 239000002609 medium Substances 0.000 description 4
- 229910052751 metal Inorganic materials 0.000 description 4
- 239000002184 metal Substances 0.000 description 4
- 125000005397 methacrylic acid ester group Chemical group 0.000 description 4
- VNWKTOKETHGBQD-UHFFFAOYSA-N methane Chemical compound C VNWKTOKETHGBQD-UHFFFAOYSA-N 0.000 description 4
- 239000005543 nano-size silicon particle Substances 0.000 description 4
- 229910052757 nitrogen Inorganic materials 0.000 description 4
- 239000012788 optical film Substances 0.000 description 4
- JYVLIDXNZAXMDK-UHFFFAOYSA-N pentan-2-ol Chemical compound CCCC(C)O JYVLIDXNZAXMDK-UHFFFAOYSA-N 0.000 description 4
- 239000011941 photocatalyst Substances 0.000 description 4
- 229920003023 plastic Polymers 0.000 description 4
- 239000004033 plastic Substances 0.000 description 4
- 239000005056 polyisocyanate Substances 0.000 description 4
- 229920001228 polyisocyanate Polymers 0.000 description 4
- 238000002360 preparation method Methods 0.000 description 4
- 239000011164 primary particle Substances 0.000 description 4
- 238000012545 processing Methods 0.000 description 4
- 239000011369 resultant mixture Substances 0.000 description 4
- 230000035882 stress Effects 0.000 description 4
- YLQBMQCUIZJEEH-UHFFFAOYSA-N tetrahydrofuran Natural products C=1C=COC=1 YLQBMQCUIZJEEH-UHFFFAOYSA-N 0.000 description 4
- CWERGRDVMFNCDR-UHFFFAOYSA-N thioglycolic acid Chemical compound OC(=O)CS CWERGRDVMFNCDR-UHFFFAOYSA-N 0.000 description 4
- CPUDPFPXCZDNGI-UHFFFAOYSA-N triethoxy(methyl)silane Chemical compound CCO[Si](C)(OCC)OCC CPUDPFPXCZDNGI-UHFFFAOYSA-N 0.000 description 4
- XDQWJFXZTAWJST-UHFFFAOYSA-N 3-triethoxysilylpropyl prop-2-enoate Chemical compound CCO[Si](OCC)(OCC)CCCOC(=O)C=C XDQWJFXZTAWJST-UHFFFAOYSA-N 0.000 description 3
- KBQVDAIIQCXKPI-UHFFFAOYSA-N 3-trimethoxysilylpropyl prop-2-enoate Chemical compound CO[Si](OC)(OC)CCCOC(=O)C=C KBQVDAIIQCXKPI-UHFFFAOYSA-N 0.000 description 3
- 239000004925 Acrylic resin Substances 0.000 description 3
- 229920000178 Acrylic resin Polymers 0.000 description 3
- UHOVQNZJYSORNB-UHFFFAOYSA-N Benzene Chemical compound C1=CC=CC=C1 UHOVQNZJYSORNB-UHFFFAOYSA-N 0.000 description 3
- 229920000049 Carbon (fiber) Polymers 0.000 description 3
- ZJCCRDAZUWHFQH-UHFFFAOYSA-N Trimethylolpropane Chemical compound CCC(CO)(CO)CO ZJCCRDAZUWHFQH-UHFFFAOYSA-N 0.000 description 3
- 238000005299 abrasion Methods 0.000 description 3
- 239000003377 acid catalyst Substances 0.000 description 3
- 150000001298 alcohols Chemical class 0.000 description 3
- 150000001338 aliphatic hydrocarbons Chemical class 0.000 description 3
- 239000000908 ammonium hydroxide Substances 0.000 description 3
- DKPFZGUDAPQIHT-UHFFFAOYSA-N butyl acetate Chemical compound CCCCOC(C)=O DKPFZGUDAPQIHT-UHFFFAOYSA-N 0.000 description 3
- 239000004917 carbon fiber Substances 0.000 description 3
- 239000002041 carbon nanotube Substances 0.000 description 3
- 229910021393 carbon nanotube Inorganic materials 0.000 description 3
- HKQOBOMRSSHSTC-UHFFFAOYSA-N cellulose acetate Chemical compound OC1C(O)C(O)C(CO)OC1OC1C(CO)OC(O)C(O)C1O.CC(=O)OCC1OC(OC(C)=O)C(OC(C)=O)C(OC(C)=O)C1OC1C(OC(C)=O)C(OC(C)=O)C(OC(C)=O)C(COC(C)=O)O1.CCC(=O)OCC1OC(OC(=O)CC)C(OC(=O)CC)C(OC(=O)CC)C1OC1C(OC(=O)CC)C(OC(=O)CC)C(OC(=O)CC)C(COC(=O)CC)O1 HKQOBOMRSSHSTC-UHFFFAOYSA-N 0.000 description 3
- 229910001873 dinitrogen Inorganic materials 0.000 description 3
- 238000002296 dynamic light scattering Methods 0.000 description 3
- FWDBOZPQNFPOLF-UHFFFAOYSA-N ethenyl(triethoxy)silane Chemical compound CCO[Si](OCC)(OCC)C=C FWDBOZPQNFPOLF-UHFFFAOYSA-N 0.000 description 3
- 125000001495 ethyl group Chemical group [H]C([H])([H])C([H])([H])* 0.000 description 3
- 238000011156 evaluation Methods 0.000 description 3
- 239000003999 initiator Substances 0.000 description 3
- 150000007529 inorganic bases Chemical class 0.000 description 3
- PHTQWCKDNZKARW-UHFFFAOYSA-N isoamylol Chemical compound CC(C)CCO PHTQWCKDNZKARW-UHFFFAOYSA-N 0.000 description 3
- 239000004973 liquid crystal related substance Substances 0.000 description 3
- 125000001570 methylene group Chemical group [H]C([H])([*:1])[*:2] 0.000 description 3
- 150000002894 organic compounds Chemical group 0.000 description 3
- 150000002978 peroxides Chemical class 0.000 description 3
- 239000011112 polyethylene naphthalate Substances 0.000 description 3
- YKYONYBAUNKHLG-UHFFFAOYSA-N propyl acetate Chemical compound CCCOC(C)=O YKYONYBAUNKHLG-UHFFFAOYSA-N 0.000 description 3
- 230000001681 protective effect Effects 0.000 description 3
- 230000009467 reduction Effects 0.000 description 3
- 238000004062 sedimentation Methods 0.000 description 3
- 239000004065 semiconductor Substances 0.000 description 3
- HBGXFGADFJLHST-UHFFFAOYSA-N silylmethanetriol Chemical compound OC(O)(O)[SiH3] HBGXFGADFJLHST-UHFFFAOYSA-N 0.000 description 3
- 238000000371 solid-state nuclear magnetic resonance spectroscopy Methods 0.000 description 3
- 238000001179 sorption measurement Methods 0.000 description 3
- 238000005507 spraying Methods 0.000 description 3
- 239000004094 surface-active agent Substances 0.000 description 3
- 229920001187 thermosetting polymer Polymers 0.000 description 3
- UMFJXASDGBJDEB-UHFFFAOYSA-N triethoxy(prop-2-enyl)silane Chemical compound CCO[Si](CC=C)(OCC)OCC UMFJXASDGBJDEB-UHFFFAOYSA-N 0.000 description 3
- 229920002554 vinyl polymer Polymers 0.000 description 3
- 239000008096 xylene Substances 0.000 description 3
- AGKBXKFWMQLFGZ-UHFFFAOYSA-N (4-methylbenzoyl) 4-methylbenzenecarboperoxoate Chemical compound C1=CC(C)=CC=C1C(=O)OOC(=O)C1=CC=C(C)C=C1 AGKBXKFWMQLFGZ-UHFFFAOYSA-N 0.000 description 2
- NOBYOEQUFMGXBP-UHFFFAOYSA-N (4-tert-butylcyclohexyl) (4-tert-butylcyclohexyl)oxycarbonyloxy carbonate Chemical compound C1CC(C(C)(C)C)CCC1OC(=O)OOC(=O)OC1CCC(C(C)(C)C)CC1 NOBYOEQUFMGXBP-UHFFFAOYSA-N 0.000 description 2
- QPFMBZIOSGYJDE-UHFFFAOYSA-N 1,1,2,2-tetrachloroethane Chemical compound ClC(Cl)C(Cl)Cl QPFMBZIOSGYJDE-UHFFFAOYSA-N 0.000 description 2
- VBQCFYPTKHCPGI-UHFFFAOYSA-N 1,1-bis(2-methylpentan-2-ylperoxy)cyclohexane Chemical compound CCCC(C)(C)OOC1(OOC(C)(C)CCC)CCCCC1 VBQCFYPTKHCPGI-UHFFFAOYSA-N 0.000 description 2
- AYMDJPGTQFHDSA-UHFFFAOYSA-N 1-(2-ethenoxyethoxy)-2-ethoxyethane Chemical compound CCOCCOCCOC=C AYMDJPGTQFHDSA-UHFFFAOYSA-N 0.000 description 2
- DPGYCJUCJYUHTM-UHFFFAOYSA-N 2,4,4-trimethylpentan-2-yloxy 2-ethylhexaneperoxoate Chemical compound CCCCC(CC)C(=O)OOOC(C)(C)CC(C)(C)C DPGYCJUCJYUHTM-UHFFFAOYSA-N 0.000 description 2
- QQZOPKMRPOGIEB-UHFFFAOYSA-N 2-Oxohexane Chemical compound CCCCC(C)=O QQZOPKMRPOGIEB-UHFFFAOYSA-N 0.000 description 2
- KANZWHBYRHQMKZ-UHFFFAOYSA-N 2-ethenylpyrazine Chemical compound C=CC1=CN=CC=N1 KANZWHBYRHQMKZ-UHFFFAOYSA-N 0.000 description 2
- ZACVGCNKGYYQHA-UHFFFAOYSA-N 2-ethylhexoxycarbonyloxy 2-ethylhexyl carbonate Chemical compound CCCCC(CC)COC(=O)OOC(=O)OCC(CC)CCCC ZACVGCNKGYYQHA-UHFFFAOYSA-N 0.000 description 2
- 125000000954 2-hydroxyethyl group Chemical group [H]C([*])([H])C([H])([H])O[H] 0.000 description 2
- RTEZVHMDMFEURJ-UHFFFAOYSA-N 2-methylpentan-2-yl 2,2-dimethylpropaneperoxoate Chemical compound CCCC(C)(C)OOC(=O)C(C)(C)C RTEZVHMDMFEURJ-UHFFFAOYSA-N 0.000 description 2
- NMZSJIQGMAGSSO-UHFFFAOYSA-N 3-[[1-amino-2-[[1-amino-1-(2-carboxyethylimino)-2-methylpropan-2-yl]diazenyl]-2-methylpropylidene]amino]propanoic acid Chemical compound OC(=O)CCNC(=N)C(C)(C)N=NC(C)(C)C(=N)NCCC(O)=O NMZSJIQGMAGSSO-UHFFFAOYSA-N 0.000 description 2
- 229920002799 BoPET Polymers 0.000 description 2
- 102000004190 Enzymes Human genes 0.000 description 2
- 108090000790 Enzymes Proteins 0.000 description 2
- 101000720524 Gordonia sp. (strain TY-5) Acetone monooxygenase (methyl acetate-forming) Proteins 0.000 description 2
- MHAJPDPJQMAIIY-UHFFFAOYSA-N Hydrogen peroxide Chemical compound OO MHAJPDPJQMAIIY-UHFFFAOYSA-N 0.000 description 2
- 239000005058 Isophorone diisocyanate Substances 0.000 description 2
- YIVJZNGAASQVEM-UHFFFAOYSA-N Lauroyl peroxide Chemical compound CCCCCCCCCCCC(=O)OOC(=O)CCCCCCCCCCC YIVJZNGAASQVEM-UHFFFAOYSA-N 0.000 description 2
- BAPJBEWLBFYGME-UHFFFAOYSA-N Methyl acrylate Chemical compound COC(=O)C=C BAPJBEWLBFYGME-UHFFFAOYSA-N 0.000 description 2
- 238000005481 NMR spectroscopy Methods 0.000 description 2
- CTQNGGLPUBDAKN-UHFFFAOYSA-N O-Xylene Chemical compound CC1=CC=CC=C1C CTQNGGLPUBDAKN-UHFFFAOYSA-N 0.000 description 2
- 239000004793 Polystyrene Substances 0.000 description 2
- ATUOYWHBWRKTHZ-UHFFFAOYSA-N Propane Chemical compound CCC ATUOYWHBWRKTHZ-UHFFFAOYSA-N 0.000 description 2
- QAOWNCQODCNURD-UHFFFAOYSA-N Sulfuric acid Chemical compound OS(O)(=O)=O QAOWNCQODCNURD-UHFFFAOYSA-N 0.000 description 2
- 238000010521 absorption reaction Methods 0.000 description 2
- 230000001133 acceleration Effects 0.000 description 2
- 239000002253 acid Substances 0.000 description 2
- 239000000654 additive Substances 0.000 description 2
- 125000005370 alkoxysilyl group Chemical group 0.000 description 2
- 125000005037 alkyl phenyl group Chemical group 0.000 description 2
- PNEYBMLMFCGWSK-UHFFFAOYSA-N aluminium oxide Inorganic materials [O-2].[O-2].[O-2].[Al+3].[Al+3] PNEYBMLMFCGWSK-UHFFFAOYSA-N 0.000 description 2
- 229910021529 ammonia Inorganic materials 0.000 description 2
- RDOXTESZEPMUJZ-UHFFFAOYSA-N anisole Chemical compound COC1=CC=CC=C1 RDOXTESZEPMUJZ-UHFFFAOYSA-N 0.000 description 2
- 239000007864 aqueous solution Substances 0.000 description 2
- 239000003849 aromatic solvent Substances 0.000 description 2
- 239000007853 buffer solution Substances 0.000 description 2
- NSGQRLUGQNBHLD-UHFFFAOYSA-N butan-2-yl butan-2-yloxycarbonyloxy carbonate Chemical compound CCC(C)OC(=O)OOC(=O)OC(C)CC NSGQRLUGQNBHLD-UHFFFAOYSA-N 0.000 description 2
- 229910052799 carbon Inorganic materials 0.000 description 2
- 230000003197 catalytic effect Effects 0.000 description 2
- 229920002678 cellulose Polymers 0.000 description 2
- 239000001913 cellulose Substances 0.000 description 2
- 239000013522 chelant Substances 0.000 description 2
- MVPPADPHJFYWMZ-UHFFFAOYSA-N chlorobenzene Chemical compound ClC1=CC=CC=C1 MVPPADPHJFYWMZ-UHFFFAOYSA-N 0.000 description 2
- 238000007766 curtain coating Methods 0.000 description 2
- 238000005520 cutting process Methods 0.000 description 2
- 125000004122 cyclic group Chemical group 0.000 description 2
- JHIVVAPYMSGYDF-UHFFFAOYSA-N cyclohexanone Chemical compound O=C1CCCCC1 JHIVVAPYMSGYDF-UHFFFAOYSA-N 0.000 description 2
- 230000003247 decreasing effect Effects 0.000 description 2
- 230000007547 defect Effects 0.000 description 2
- 125000005442 diisocyanate group Chemical class 0.000 description 2
- 238000007720 emulsion polymerization reaction Methods 0.000 description 2
- 230000003628 erosive effect Effects 0.000 description 2
- MBGQQKKTDDNCSG-UHFFFAOYSA-N ethenyl-diethoxy-methylsilane Chemical compound CCO[Si](C)(C=C)OCC MBGQQKKTDDNCSG-UHFFFAOYSA-N 0.000 description 2
- JBTWLSYIZRCDFO-UHFFFAOYSA-N ethyl methyl carbonate Chemical compound CCOC(=O)OC JBTWLSYIZRCDFO-UHFFFAOYSA-N 0.000 description 2
- 238000007765 extrusion coating Methods 0.000 description 2
- 238000011049 filling Methods 0.000 description 2
- 230000012447 hatching Effects 0.000 description 2
- 230000003301 hydrolyzing effect Effects 0.000 description 2
- WGCNASOHLSPBMP-UHFFFAOYSA-N hydroxyacetaldehyde Natural products OCC=O WGCNASOHLSPBMP-UHFFFAOYSA-N 0.000 description 2
- 239000010954 inorganic particle Substances 0.000 description 2
- MLFHJEHSLIIPHL-UHFFFAOYSA-N isoamyl acetate Chemical compound CC(C)CCOC(C)=O MLFHJEHSLIIPHL-UHFFFAOYSA-N 0.000 description 2
- IQPQWNKOIGAROB-UHFFFAOYSA-N isocyanate group Chemical group [N-]=C=O IQPQWNKOIGAROB-UHFFFAOYSA-N 0.000 description 2
- 125000001261 isocyanato group Chemical group *N=C=O 0.000 description 2
- ZFSLODLOARCGLH-UHFFFAOYSA-N isocyanuric acid Chemical group OC1=NC(O)=NC(O)=N1 ZFSLODLOARCGLH-UHFFFAOYSA-N 0.000 description 2
- NIMLQBUJDJZYEJ-UHFFFAOYSA-N isophorone diisocyanate Chemical compound CC1(C)CC(N=C=O)CC(C)(CN=C=O)C1 NIMLQBUJDJZYEJ-UHFFFAOYSA-N 0.000 description 2
- JMMWKPVZQRWMSS-UHFFFAOYSA-N isopropanol acetate Natural products CC(C)OC(C)=O JMMWKPVZQRWMSS-UHFFFAOYSA-N 0.000 description 2
- 229940011051 isopropyl acetate Drugs 0.000 description 2
- 125000001449 isopropyl group Chemical group [H]C([H])([H])C([H])(*)C([H])([H])[H] 0.000 description 2
- GWYFCOCPABKNJV-UHFFFAOYSA-M isovalerate Chemical compound CC(C)CC([O-])=O GWYFCOCPABKNJV-UHFFFAOYSA-M 0.000 description 2
- 238000003475 lamination Methods 0.000 description 2
- 125000005395 methacrylic acid group Chemical group 0.000 description 2
- GNARHXWTMJZNTP-UHFFFAOYSA-N methoxy-[3-(oxiran-2-ylmethoxy)propyl]silane Chemical compound CO[SiH2]CCCOCC1CO1 GNARHXWTMJZNTP-UHFFFAOYSA-N 0.000 description 2
- 239000012046 mixed solvent Substances 0.000 description 2
- 238000006011 modification reaction Methods 0.000 description 2
- QYZFTMMPKCOTAN-UHFFFAOYSA-N n-[2-(2-hydroxyethylamino)ethyl]-2-[[1-[2-(2-hydroxyethylamino)ethylamino]-2-methyl-1-oxopropan-2-yl]diazenyl]-2-methylpropanamide Chemical compound OCCNCCNC(=O)C(C)(C)N=NC(C)(C)C(=O)NCCNCCO QYZFTMMPKCOTAN-UHFFFAOYSA-N 0.000 description 2
- 125000004108 n-butyl group Chemical group [H]C([H])([H])C([H])([H])C([H])([H])C([H])([H])* 0.000 description 2
- TVMXDCGIABBOFY-UHFFFAOYSA-N octane Chemical compound CCCCCCCC TVMXDCGIABBOFY-UHFFFAOYSA-N 0.000 description 2
- SRSFOMHQIATOFV-UHFFFAOYSA-N octanoyl octaneperoxoate Chemical compound CCCCCCCC(=O)OOC(=O)CCCCCCC SRSFOMHQIATOFV-UHFFFAOYSA-N 0.000 description 2
- PGMYKACGEOXYJE-UHFFFAOYSA-N pentyl acetate Chemical compound CCCCCOC(C)=O PGMYKACGEOXYJE-UHFFFAOYSA-N 0.000 description 2
- 229960004624 perflexane Drugs 0.000 description 2
- ZJIJAJXFLBMLCK-UHFFFAOYSA-N perfluorohexane Chemical compound FC(F)(F)C(F)(F)C(F)(F)C(F)(F)C(F)(F)C(F)(F)F ZJIJAJXFLBMLCK-UHFFFAOYSA-N 0.000 description 2
- JRKICGRDRMAZLK-UHFFFAOYSA-L persulfate group Chemical group S(=O)(=O)([O-])OOS(=O)(=O)[O-] JRKICGRDRMAZLK-UHFFFAOYSA-L 0.000 description 2
- 229920006267 polyester film Polymers 0.000 description 2
- 229920000098 polyolefin Polymers 0.000 description 2
- 229920002223 polystyrene Polymers 0.000 description 2
- 239000000843 powder Substances 0.000 description 2
- 230000001737 promoting effect Effects 0.000 description 2
- BDERNNFJNOPAEC-UHFFFAOYSA-N propan-1-ol Chemical compound CCCO BDERNNFJNOPAEC-UHFFFAOYSA-N 0.000 description 2
- 125000001436 propyl group Chemical group [H]C([*])([H])C([H])([H])C([H])([H])[H] 0.000 description 2
- 238000010526 radical polymerization reaction Methods 0.000 description 2
- 230000002441 reversible effect Effects 0.000 description 2
- 238000007761 roller coating Methods 0.000 description 2
- 238000001878 scanning electron micrograph Methods 0.000 description 2
- 229910052708 sodium Inorganic materials 0.000 description 2
- 239000011734 sodium Substances 0.000 description 2
- KZNICNPSHKQLFF-UHFFFAOYSA-N succinimide Chemical compound O=C1CCC(=O)N1 KZNICNPSHKQLFF-UHFFFAOYSA-N 0.000 description 2
- 239000000725 suspension Substances 0.000 description 2
- 238000003786 synthesis reaction Methods 0.000 description 2
- 238000009864 tensile test Methods 0.000 description 2
- OPQYOFWUFGEMRZ-UHFFFAOYSA-N tert-butyl 2,2-dimethylpropaneperoxoate Chemical compound CC(C)(C)OOC(=O)C(C)(C)C OPQYOFWUFGEMRZ-UHFFFAOYSA-N 0.000 description 2
- NMOALOSNPWTWRH-UHFFFAOYSA-N tert-butyl 7,7-dimethyloctaneperoxoate Chemical compound CC(C)(C)CCCCCC(=O)OOC(C)(C)C NMOALOSNPWTWRH-UHFFFAOYSA-N 0.000 description 2
- CIHOLLKRGTVIJN-UHFFFAOYSA-N tert‐butyl hydroperoxide Chemical compound CC(C)(C)OO CIHOLLKRGTVIJN-UHFFFAOYSA-N 0.000 description 2
- VZGDMQKNWNREIO-UHFFFAOYSA-N tetrachloromethane Chemical compound ClC(Cl)(Cl)Cl VZGDMQKNWNREIO-UHFFFAOYSA-N 0.000 description 2
- 239000010936 titanium Substances 0.000 description 2
- DVKJHBMWWAPEIU-UHFFFAOYSA-N toluene 2,4-diisocyanate Chemical compound CC1=CC=C(N=C=O)C=C1N=C=O DVKJHBMWWAPEIU-UHFFFAOYSA-N 0.000 description 2
- 239000013638 trimer Substances 0.000 description 2
- IJROHELDTBDTPH-UHFFFAOYSA-N trimethoxy(3,3,4,4,5,5,6,6,6-nonafluorohexyl)silane Chemical compound CO[Si](OC)(OC)CCC(F)(F)C(F)(F)C(F)(F)C(F)(F)F IJROHELDTBDTPH-UHFFFAOYSA-N 0.000 description 2
- LFRDHGNFBLIJIY-UHFFFAOYSA-N trimethoxy(prop-2-enyl)silane Chemical compound CO[Si](OC)(OC)CC=C LFRDHGNFBLIJIY-UHFFFAOYSA-N 0.000 description 2
- BPSIOYPQMFLKFR-UHFFFAOYSA-N trimethoxy-[3-(oxiran-2-ylmethoxy)propyl]silane Chemical compound CO[Si](OC)(OC)CCCOCC1CO1 BPSIOYPQMFLKFR-UHFFFAOYSA-N 0.000 description 2
- 239000003021 water soluble solvent Substances 0.000 description 2
- 239000011240 wet gel Substances 0.000 description 2
- DGVVWUTYPXICAM-UHFFFAOYSA-N β‐Mercaptoethanol Chemical compound OCCS DGVVWUTYPXICAM-UHFFFAOYSA-N 0.000 description 2
- HFROTQKOFJESPY-CMDGGOBGSA-N (e)-3-(2-hydroxyphenyl)-1-piperidin-1-ylprop-2-en-1-one Chemical compound OC1=CC=CC=C1\C=C\C(=O)N1CCCCC1 HFROTQKOFJESPY-CMDGGOBGSA-N 0.000 description 1
- UOCLXMDMGBRAIB-UHFFFAOYSA-N 1,1,1-trichloroethane Chemical compound CC(Cl)(Cl)Cl UOCLXMDMGBRAIB-UHFFFAOYSA-N 0.000 description 1
- WSLDOOZREJYCGB-UHFFFAOYSA-N 1,2-Dichloroethane Chemical compound ClCCCl WSLDOOZREJYCGB-UHFFFAOYSA-N 0.000 description 1
- FKTHNVSLHLHISI-UHFFFAOYSA-N 1,2-bis(isocyanatomethyl)benzene Chemical class O=C=NCC1=CC=CC=C1CN=C=O FKTHNVSLHLHISI-UHFFFAOYSA-N 0.000 description 1
- QWOVEJBDMKHZQK-UHFFFAOYSA-N 1,3,5-tris(3-trimethoxysilylpropyl)-1,3,5-triazinane-2,4,6-trione Chemical compound CO[Si](OC)(OC)CCCN1C(=O)N(CCC[Si](OC)(OC)OC)C(=O)N(CCC[Si](OC)(OC)OC)C1=O QWOVEJBDMKHZQK-UHFFFAOYSA-N 0.000 description 1
- RYHBNJHYFVUHQT-UHFFFAOYSA-N 1,4-Dioxane Chemical compound C1COCCO1 RYHBNJHYFVUHQT-UHFFFAOYSA-N 0.000 description 1
- OVBFMUAFNIIQAL-UHFFFAOYSA-N 1,4-diisocyanatobutane Chemical compound O=C=NCCCCN=C=O OVBFMUAFNIIQAL-UHFFFAOYSA-N 0.000 description 1
- GEWWCWZGHNIUBW-UHFFFAOYSA-N 1-(4-nitrophenyl)propan-2-one Chemical compound CC(=O)CC1=CC=C([N+]([O-])=O)C=C1 GEWWCWZGHNIUBW-UHFFFAOYSA-N 0.000 description 1
- UYBGGSUXZMAIBV-UHFFFAOYSA-N 1-(9,10-dioxoanthracen-2-yl)ethyl 1h-imidazole-2-carboxylate Chemical compound C=1C=C2C(=O)C3=CC=CC=C3C(=O)C2=CC=1C(C)OC(=O)C1=NC=CN1 UYBGGSUXZMAIBV-UHFFFAOYSA-N 0.000 description 1
- IAUGBVWVWDTCJV-UHFFFAOYSA-N 1-(prop-2-enoylamino)propane-1-sulfonic acid Chemical compound CCC(S(O)(=O)=O)NC(=O)C=C IAUGBVWVWDTCJV-UHFFFAOYSA-N 0.000 description 1
- BQTPKSBXMONSJI-UHFFFAOYSA-N 1-cyclohexylpyrrole-2,5-dione Chemical compound O=C1C=CC(=O)N1C1CCCCC1 BQTPKSBXMONSJI-UHFFFAOYSA-N 0.000 description 1
- JWYVGKFDLWWQJX-UHFFFAOYSA-N 1-ethenylazepan-2-one Chemical compound C=CN1CCCCCC1=O JWYVGKFDLWWQJX-UHFFFAOYSA-N 0.000 description 1
- OSSNTDFYBPYIEC-UHFFFAOYSA-N 1-ethenylimidazole Chemical compound C=CN1C=CN=C1 OSSNTDFYBPYIEC-UHFFFAOYSA-N 0.000 description 1
- DCRYNQTXGUTACA-UHFFFAOYSA-N 1-ethenylpiperazine Chemical compound C=CN1CCNCC1 DCRYNQTXGUTACA-UHFFFAOYSA-N 0.000 description 1
- PBGPBHYPCGDFEZ-UHFFFAOYSA-N 1-ethenylpiperidin-2-one Chemical compound C=CN1CCCCC1=O PBGPBHYPCGDFEZ-UHFFFAOYSA-N 0.000 description 1
- CSCSROFYRUZJJH-UHFFFAOYSA-N 1-methoxyethane-1,2-diol Chemical compound COC(O)CO CSCSROFYRUZJJH-UHFFFAOYSA-N 0.000 description 1
- HIDBROSJWZYGSZ-UHFFFAOYSA-N 1-phenylpyrrole-2,5-dione Chemical compound O=C1C=CC(=O)N1C1=CC=CC=C1 HIDBROSJWZYGSZ-UHFFFAOYSA-N 0.000 description 1
- RESPXSHDJQUNTN-UHFFFAOYSA-N 1-piperidin-1-ylprop-2-en-1-one Chemical compound C=CC(=O)N1CCCCC1 RESPXSHDJQUNTN-UHFFFAOYSA-N 0.000 description 1
- BFYSJBXFEVRVII-UHFFFAOYSA-N 1-prop-1-enylpyrrolidin-2-one Chemical compound CC=CN1CCCC1=O BFYSJBXFEVRVII-UHFFFAOYSA-N 0.000 description 1
- WLPAQAXAZQUXBG-UHFFFAOYSA-N 1-pyrrolidin-1-ylprop-2-en-1-one Chemical compound C=CC(=O)N1CCCC1 WLPAQAXAZQUXBG-UHFFFAOYSA-N 0.000 description 1
- VIUDSFQSAFAVGV-UHFFFAOYSA-N 10-triethoxysilyldecyl 2-methylprop-2-enoate Chemical compound CCO[Si](OCC)(OCC)CCCCCCCCCCOC(=O)C(C)=C VIUDSFQSAFAVGV-UHFFFAOYSA-N 0.000 description 1
- ZZXDHSIJYPCDOM-UHFFFAOYSA-N 10-triethoxysilyldecyl prop-2-enoate Chemical compound CCO[Si](OCC)(OCC)CCCCCCCCCCOC(=O)C=C ZZXDHSIJYPCDOM-UHFFFAOYSA-N 0.000 description 1
- BXBOUPUNKULVKB-UHFFFAOYSA-N 10-trimethoxysilyldecyl 2-methylprop-2-enoate Chemical compound CO[Si](OC)(OC)CCCCCCCCCCOC(=O)C(C)=C BXBOUPUNKULVKB-UHFFFAOYSA-N 0.000 description 1
- CCQJKEYNLSZZNO-UHFFFAOYSA-N 10-trimethoxysilyldecyl prop-2-enoate Chemical compound CO[Si](OC)(OC)CCCCCCCCCCOC(=O)C=C CCQJKEYNLSZZNO-UHFFFAOYSA-N 0.000 description 1
- 238000005160 1H NMR spectroscopy Methods 0.000 description 1
- CCTFAOUOYLVUFG-UHFFFAOYSA-N 2-(1-amino-1-imino-2-methylpropan-2-yl)azo-2-methylpropanimidamide Chemical compound NC(=N)C(C)(C)N=NC(C)(C)C(N)=N CCTFAOUOYLVUFG-UHFFFAOYSA-N 0.000 description 1
- UGIJCMNGQCUTPI-UHFFFAOYSA-N 2-aminoethyl prop-2-enoate Chemical compound NCCOC(=O)C=C UGIJCMNGQCUTPI-UHFFFAOYSA-N 0.000 description 1
- POAOYUHQDCAZBD-UHFFFAOYSA-N 2-butoxyethanol Chemical compound CCCCOCCO POAOYUHQDCAZBD-UHFFFAOYSA-N 0.000 description 1
- PGMMQIGGQSIEGH-UHFFFAOYSA-N 2-ethenyl-1,3-oxazole Chemical compound C=CC1=NC=CO1 PGMMQIGGQSIEGH-UHFFFAOYSA-N 0.000 description 1
- MZNSQRLUUXWLSB-UHFFFAOYSA-N 2-ethenyl-1h-pyrrole Chemical compound C=CC1=CC=CN1 MZNSQRLUUXWLSB-UHFFFAOYSA-N 0.000 description 1
- ZDHWTWWXCXEGIC-UHFFFAOYSA-N 2-ethenylpyrimidine Chemical compound C=CC1=NC=CC=N1 ZDHWTWWXCXEGIC-UHFFFAOYSA-N 0.000 description 1
- SVONRAPFKPVNKG-UHFFFAOYSA-N 2-ethoxyethyl acetate Chemical compound CCOCCOC(C)=O SVONRAPFKPVNKG-UHFFFAOYSA-N 0.000 description 1
- OWHSTLLOZWTNTQ-UHFFFAOYSA-N 2-ethylhexyl 2-sulfanylacetate Chemical compound CCCCC(CC)COC(=O)CS OWHSTLLOZWTNTQ-UHFFFAOYSA-N 0.000 description 1
- NJRHMGPRPPEGQL-UHFFFAOYSA-N 2-hydroxybutyl prop-2-enoate Chemical compound CCC(O)COC(=O)C=C NJRHMGPRPPEGQL-UHFFFAOYSA-N 0.000 description 1
- WGRZHLPEQDVPET-UHFFFAOYSA-N 2-methoxyethoxysilane Chemical compound COCCO[SiH3] WGRZHLPEQDVPET-UHFFFAOYSA-N 0.000 description 1
- HFCUBKYHMMPGBY-UHFFFAOYSA-N 2-methoxyethyl prop-2-enoate Chemical compound COCCOC(=O)C=C HFCUBKYHMMPGBY-UHFFFAOYSA-N 0.000 description 1
- QENRKQYUEGJNNZ-UHFFFAOYSA-N 2-methyl-1-(prop-2-enoylamino)propane-1-sulfonic acid Chemical compound CC(C)C(S(O)(=O)=O)NC(=O)C=C QENRKQYUEGJNNZ-UHFFFAOYSA-N 0.000 description 1
- RASDUGQQSMMINZ-UHFFFAOYSA-N 2-methyl-1-piperidin-1-ylprop-2-en-1-one Chemical compound CC(=C)C(=O)N1CCCCC1 RASDUGQQSMMINZ-UHFFFAOYSA-N 0.000 description 1
- QTWJRLJHJPIABL-UHFFFAOYSA-N 2-methylphenol;3-methylphenol;4-methylphenol Chemical compound CC1=CC=C(O)C=C1.CC1=CC=CC(O)=C1.CC1=CC=CC=C1O QTWJRLJHJPIABL-UHFFFAOYSA-N 0.000 description 1
- NDAJNMAAXXIADY-UHFFFAOYSA-N 2-methylpropanimidamide Chemical compound CC(C)C(N)=N NDAJNMAAXXIADY-UHFFFAOYSA-N 0.000 description 1
- AGBXYHCHUYARJY-UHFFFAOYSA-N 2-phenylethenesulfonic acid Chemical compound OS(=O)(=O)C=CC1=CC=CC=C1 AGBXYHCHUYARJY-UHFFFAOYSA-N 0.000 description 1
- 125000003903 2-propenyl group Chemical group [H]C([*])([H])C([H])=C([H])[H] 0.000 description 1
- KGIGUEBEKRSTEW-UHFFFAOYSA-N 2-vinylpyridine Chemical compound C=CC1=CC=CC=N1 KGIGUEBEKRSTEW-UHFFFAOYSA-N 0.000 description 1
- HJIMAFKWSKZMBK-UHFFFAOYSA-N 3,3,4,4,5,5,6,6,7,7,8,8,9,9,10,10,10-heptadecafluorodecyl(trimethoxy)silane Chemical compound CO[Si](OC)(OC)CCC(F)(F)C(F)(F)C(F)(F)C(F)(F)C(F)(F)C(F)(F)C(F)(F)C(F)(F)F HJIMAFKWSKZMBK-UHFFFAOYSA-N 0.000 description 1
- NHCZYSDZAMNWGB-UHFFFAOYSA-N 3,4,6,7,8,9-hexahydro-2h-pyrimido[1,2-a]pyrimidine;2-(9-oxoxanthen-2-yl)propanoic acid Chemical compound C1CCN2CCCNC2=N1.C1=CC=C2C(=O)C3=CC(C(C(O)=O)C)=CC=C3OC2=C1 NHCZYSDZAMNWGB-UHFFFAOYSA-N 0.000 description 1
- MCDBEBOBROAQSH-UHFFFAOYSA-N 3-[dimethoxy(methyl)silyl]propyl prop-2-enoate Chemical compound CO[Si](C)(OC)CCCOC(=O)C=C MCDBEBOBROAQSH-UHFFFAOYSA-N 0.000 description 1
- ZCRUJAKCJLCJCP-UHFFFAOYSA-N 3-[methoxy(dimethyl)silyl]propyl prop-2-enoate Chemical compound CO[Si](C)(C)CCCOC(=O)C=C ZCRUJAKCJLCJCP-UHFFFAOYSA-N 0.000 description 1
- QOXOZONBQWIKDA-UHFFFAOYSA-N 3-hydroxypropyl Chemical group [CH2]CCO QOXOZONBQWIKDA-UHFFFAOYSA-N 0.000 description 1
- OFNISBHGPNMTMS-UHFFFAOYSA-N 3-methylideneoxolane-2,5-dione Chemical compound C=C1CC(=O)OC1=O OFNISBHGPNMTMS-UHFFFAOYSA-N 0.000 description 1
- ATVJXMYDOSMEPO-UHFFFAOYSA-N 3-prop-2-enoxyprop-1-ene Chemical group C=CCOCC=C ATVJXMYDOSMEPO-UHFFFAOYSA-N 0.000 description 1
- URDOJQUSEUXVRP-UHFFFAOYSA-N 3-triethoxysilylpropyl 2-methylprop-2-enoate Chemical compound CCO[Si](OCC)(OCC)CCCOC(=O)C(C)=C URDOJQUSEUXVRP-UHFFFAOYSA-N 0.000 description 1
- XDLMVUHYZWKMMD-UHFFFAOYSA-N 3-trimethoxysilylpropyl 2-methylprop-2-enoate Chemical compound CO[Si](OC)(OC)CCCOC(=O)C(C)=C XDLMVUHYZWKMMD-UHFFFAOYSA-N 0.000 description 1
- CFZDMXAOSDDDRT-UHFFFAOYSA-N 4-ethenylmorpholine Chemical compound C=CN1CCOCC1 CFZDMXAOSDDDRT-UHFFFAOYSA-N 0.000 description 1
- SXIFAEWFOJETOA-UHFFFAOYSA-N 4-hydroxy-butyl Chemical group [CH2]CCCO SXIFAEWFOJETOA-UHFFFAOYSA-N 0.000 description 1
- MQWCXKGKQLNYQG-UHFFFAOYSA-N 4-methylcyclohexan-1-ol Chemical compound CC1CCC(O)CC1 MQWCXKGKQLNYQG-UHFFFAOYSA-N 0.000 description 1
- VGVHNLRUAMRIEW-UHFFFAOYSA-N 4-methylcyclohexan-1-one Chemical compound CC1CCC(=O)CC1 VGVHNLRUAMRIEW-UHFFFAOYSA-N 0.000 description 1
- NLHHRLWOUZZQLW-UHFFFAOYSA-N Acrylonitrile Chemical compound C=CC#N NLHHRLWOUZZQLW-UHFFFAOYSA-N 0.000 description 1
- QGZKDVFQNNGYKY-UHFFFAOYSA-O Ammonium Chemical compound [NH4+] QGZKDVFQNNGYKY-UHFFFAOYSA-O 0.000 description 1
- CBFAZWAGKJUAAD-UHFFFAOYSA-N C(C)O[Si](OCC)(OCC)C(CC)(CC)[Si](OCC)(OCC)OCC Chemical compound C(C)O[Si](OCC)(OCC)C(CC)(CC)[Si](OCC)(OCC)OCC CBFAZWAGKJUAAD-UHFFFAOYSA-N 0.000 description 1
- CBMHHCNDXPVVKT-UHFFFAOYSA-N CO[Si](OC)(OC)C(CN)(N(CCC)CCCC)[Si](OC)(OC)OC Chemical compound CO[Si](OC)(OC)C(CN)(N(CCC)CCCC)[Si](OC)(OC)OC CBMHHCNDXPVVKT-UHFFFAOYSA-N 0.000 description 1
- ABMORCBKJDAAFO-UHFFFAOYSA-N C[Si](C)(C)OC([SiH3])=C(O[Si](C)(C)C)O[Si](C)(C)C Chemical compound C[Si](C)(C)OC([SiH3])=C(O[Si](C)(C)C)O[Si](C)(C)C ABMORCBKJDAAFO-UHFFFAOYSA-N 0.000 description 1
- GXGJIOMUZAGVEH-UHFFFAOYSA-N Chamazulene Chemical group CCC1=CC=C(C)C2=CC=C(C)C2=C1 GXGJIOMUZAGVEH-UHFFFAOYSA-N 0.000 description 1
- 229920002101 Chitin Polymers 0.000 description 1
- 229920001661 Chitosan Polymers 0.000 description 1
- 241001146209 Curio rowleyanus Species 0.000 description 1
- 229920001651 Cyanoacrylate Polymers 0.000 description 1
- XDTMQSROBMDMFD-UHFFFAOYSA-N Cyclohexane Chemical compound C1CCCCC1 XDTMQSROBMDMFD-UHFFFAOYSA-N 0.000 description 1
- 239000004593 Epoxy Substances 0.000 description 1
- OTMSDBZUPAUEDD-UHFFFAOYSA-N Ethane Chemical compound CC OTMSDBZUPAUEDD-UHFFFAOYSA-N 0.000 description 1
- PXGOKWXKJXAPGV-UHFFFAOYSA-N Fluorine Chemical compound FF PXGOKWXKJXAPGV-UHFFFAOYSA-N 0.000 description 1
- DGAQECJNVWCQMB-PUAWFVPOSA-M Ilexoside XXIX Chemical compound C[C@@H]1CC[C@@]2(CC[C@@]3(C(=CC[C@H]4[C@]3(CC[C@@H]5[C@@]4(CC[C@@H](C5(C)C)OS(=O)(=O)[O-])C)C)[C@@H]2[C@]1(C)O)C)C(=O)O[C@H]6[C@@H]([C@H]([C@@H]([C@H](O6)CO)O)O)O.[Na+] DGAQECJNVWCQMB-PUAWFVPOSA-M 0.000 description 1
- PEEHTFAAVSWFBL-UHFFFAOYSA-N Maleimide Chemical compound O=C1NC(=O)C=C1 PEEHTFAAVSWFBL-UHFFFAOYSA-N 0.000 description 1
- CERQOIWHTDAKMF-UHFFFAOYSA-M Methacrylate Chemical compound CC(=C)C([O-])=O CERQOIWHTDAKMF-UHFFFAOYSA-M 0.000 description 1
- MWCLLHOVUTZFKS-UHFFFAOYSA-N Methyl cyanoacrylate Chemical compound COC(=O)C(=C)C#N MWCLLHOVUTZFKS-UHFFFAOYSA-N 0.000 description 1
- VVQNEPGJFQJSBK-UHFFFAOYSA-N Methyl methacrylate Chemical compound COC(=O)C(C)=C VVQNEPGJFQJSBK-UHFFFAOYSA-N 0.000 description 1
- GYCMBHHDWRMZGG-UHFFFAOYSA-N Methylacrylonitrile Chemical compound CC(=C)C#N GYCMBHHDWRMZGG-UHFFFAOYSA-N 0.000 description 1
- YNAVUWVOSKDBBP-UHFFFAOYSA-N Morpholine Chemical group C1COCCN1 YNAVUWVOSKDBBP-UHFFFAOYSA-N 0.000 description 1
- WHNWPMSKXPGLAX-UHFFFAOYSA-N N-Vinyl-2-pyrrolidone Chemical compound C=CN1CCCC1=O WHNWPMSKXPGLAX-UHFFFAOYSA-N 0.000 description 1
- CYTYCFOTNPOANT-UHFFFAOYSA-N Perchloroethylene Chemical group ClC(Cl)=C(Cl)Cl CYTYCFOTNPOANT-UHFFFAOYSA-N 0.000 description 1
- 229920000538 Poly[(phenyl isocyanate)-co-formaldehyde] Chemical class 0.000 description 1
- 239000002202 Polyethylene glycol Substances 0.000 description 1
- 239000004721 Polyphenylene oxide Substances 0.000 description 1
- DWAQJAXMDSEUJJ-UHFFFAOYSA-M Sodium bisulfite Chemical compound [Na+].OS([O-])=O DWAQJAXMDSEUJJ-UHFFFAOYSA-M 0.000 description 1
- DBMJMQXJHONAFJ-UHFFFAOYSA-M Sodium laurylsulphate Chemical compound [Na+].CCCCCCCCCCCCOS([O-])(=O)=O DBMJMQXJHONAFJ-UHFFFAOYSA-M 0.000 description 1
- GWEVSGVZZGPLCZ-UHFFFAOYSA-N Titan oxide Chemical compound O=[Ti]=O GWEVSGVZZGPLCZ-UHFFFAOYSA-N 0.000 description 1
- XSTXAVWGXDQKEL-UHFFFAOYSA-N Trichloroethylene Chemical group ClC=C(Cl)Cl XSTXAVWGXDQKEL-UHFFFAOYSA-N 0.000 description 1
- XTXRWKRVRITETP-UHFFFAOYSA-N Vinyl acetate Chemical compound CC(=O)OC=C XTXRWKRVRITETP-UHFFFAOYSA-N 0.000 description 1
- QYKIQEUNHZKYBP-UHFFFAOYSA-N Vinyl ether Chemical group C=COC=C QYKIQEUNHZKYBP-UHFFFAOYSA-N 0.000 description 1
- YBUIRAZOPRQNDE-UHFFFAOYSA-N [dimethoxy(methyl)silyl]methyl 2-methylprop-2-enoate Chemical compound CO[Si](C)(OC)COC(=O)C(C)=C YBUIRAZOPRQNDE-UHFFFAOYSA-N 0.000 description 1
- 239000011358 absorbing material Substances 0.000 description 1
- 125000004018 acid anhydride group Chemical group 0.000 description 1
- 230000002378 acidificating effect Effects 0.000 description 1
- 150000007513 acids Chemical class 0.000 description 1
- 150000001252 acrylic acid derivatives Chemical class 0.000 description 1
- 238000004220 aggregation Methods 0.000 description 1
- 230000002776 aggregation Effects 0.000 description 1
- 125000003158 alcohol group Chemical group 0.000 description 1
- 125000004183 alkoxy alkyl group Chemical group 0.000 description 1
- 125000000278 alkyl amino alkyl group Chemical group 0.000 description 1
- 125000005907 alkyl ester group Chemical group 0.000 description 1
- 150000005215 alkyl ethers Chemical class 0.000 description 1
- XYLMUPLGERFSHI-UHFFFAOYSA-N alpha-Methylstyrene Chemical compound CC(=C)C1=CC=CC=C1 XYLMUPLGERFSHI-UHFFFAOYSA-N 0.000 description 1
- ZIXLDMFVRPABBX-UHFFFAOYSA-N alpha-methylcyclopentanone Natural products CC1CCCC1=O ZIXLDMFVRPABBX-UHFFFAOYSA-N 0.000 description 1
- BTBJBAZGXNKLQC-UHFFFAOYSA-N ammonium lauryl sulfate Chemical compound [NH4+].CCCCCCCCCCCCOS([O-])(=O)=O BTBJBAZGXNKLQC-UHFFFAOYSA-N 0.000 description 1
- 229940063953 ammonium lauryl sulfate Drugs 0.000 description 1
- ROOXNKNUYICQNP-UHFFFAOYSA-N ammonium peroxydisulfate Substances [NH4+].[NH4+].[O-]S(=O)(=O)OOS([O-])(=O)=O ROOXNKNUYICQNP-UHFFFAOYSA-N 0.000 description 1
- VAZSKTXWXKYQJF-UHFFFAOYSA-N ammonium persulfate Chemical compound [NH4+].[NH4+].[O-]S(=O)OOS([O-])=O VAZSKTXWXKYQJF-UHFFFAOYSA-N 0.000 description 1
- 229910001870 ammonium persulfate Inorganic materials 0.000 description 1
- 125000000129 anionic group Chemical group 0.000 description 1
- ZWDNVDDEDBXBMD-UHFFFAOYSA-N anthracen-9-ylmethyl n,n-diethylcarbamate Chemical compound C1=CC=C2C(COC(=O)N(CC)CC)=C(C=CC=C3)C3=CC2=C1 ZWDNVDDEDBXBMD-UHFFFAOYSA-N 0.000 description 1
- 238000013459 approach Methods 0.000 description 1
- 238000007611 bar coating method Methods 0.000 description 1
- 229920005601 base polymer Polymers 0.000 description 1
- 239000011324 bead Substances 0.000 description 1
- 238000010009 beating Methods 0.000 description 1
- 239000000440 bentonite Substances 0.000 description 1
- 229910000278 bentonite Inorganic materials 0.000 description 1
- SVPXDRXYRYOSEX-UHFFFAOYSA-N bentoquatam Chemical compound O.O=[Si]=O.O=[Al]O[Al]=O SVPXDRXYRYOSEX-UHFFFAOYSA-N 0.000 description 1
- 239000011942 biocatalyst Substances 0.000 description 1
- 229920001400 block copolymer Polymers 0.000 description 1
- 238000012662 bulk polymerization Methods 0.000 description 1
- CQEYYJKEWSMYFG-UHFFFAOYSA-N butyl acrylate Chemical compound CCCCOC(=O)C=C CQEYYJKEWSMYFG-UHFFFAOYSA-N 0.000 description 1
- 125000000484 butyl group Chemical group [H]C([*])([H])C([H])([H])C([H])([H])C([H])([H])[H] 0.000 description 1
- 229910052791 calcium Inorganic materials 0.000 description 1
- 239000002134 carbon nanofiber Substances 0.000 description 1
- 230000015556 catabolic process Effects 0.000 description 1
- 239000003638 chemical reducing agent Substances 0.000 description 1
- 229910052804 chromium Inorganic materials 0.000 description 1
- 239000011247 coating layer Substances 0.000 description 1
- 239000007859 condensation product Substances 0.000 description 1
- 239000000470 constituent Substances 0.000 description 1
- 238000010924 continuous production Methods 0.000 description 1
- 229920001577 copolymer Polymers 0.000 description 1
- 229910052802 copper Inorganic materials 0.000 description 1
- 229930003836 cresol Natural products 0.000 description 1
- HPXRVTGHNJAIIH-UHFFFAOYSA-N cyclohexanol Chemical compound OC1CCCCC1 HPXRVTGHNJAIIH-UHFFFAOYSA-N 0.000 description 1
- BGTOWKSIORTVQH-UHFFFAOYSA-N cyclopentanone Chemical compound O=C1CCCC1 BGTOWKSIORTVQH-UHFFFAOYSA-N 0.000 description 1
- LLBJHMHFNBRQBD-UHFFFAOYSA-N dec-9-enyl(triethoxy)silane Chemical compound CCO[Si](OCC)(OCC)CCCCCCCCC=C LLBJHMHFNBRQBD-UHFFFAOYSA-N 0.000 description 1
- IIMISJTWARSKOJ-UHFFFAOYSA-N dec-9-enyl(trimethoxy)silane Chemical compound CO[Si](OC)(OC)CCCCCCCCC=C IIMISJTWARSKOJ-UHFFFAOYSA-N 0.000 description 1
- 238000006731 degradation reaction Methods 0.000 description 1
- 238000006356 dehydrogenation reaction Methods 0.000 description 1
- 230000006866 deterioration Effects 0.000 description 1
- 235000014113 dietary fatty acids Nutrition 0.000 description 1
- WQABCVAJNWAXTE-UHFFFAOYSA-N dimercaprol Chemical compound OCC(S)CS WQABCVAJNWAXTE-UHFFFAOYSA-N 0.000 description 1
- PKTOVQRKCNPVKY-UHFFFAOYSA-N dimethoxy(methyl)silicon Chemical group CO[Si](C)OC PKTOVQRKCNPVKY-UHFFFAOYSA-N 0.000 description 1
- 125000002147 dimethylamino group Chemical group [H]C([H])([H])N(*)C([H])([H])[H] 0.000 description 1
- 238000003618 dip coating Methods 0.000 description 1
- VFNGKCDDZUSWLR-UHFFFAOYSA-L disulfate(2-) Chemical compound [O-]S(=O)(=O)OS([O-])(=O)=O VFNGKCDDZUSWLR-UHFFFAOYSA-L 0.000 description 1
- WNAHIZMDSQCWRP-UHFFFAOYSA-N dodecane-1-thiol Chemical compound CCCCCCCCCCCCS WNAHIZMDSQCWRP-UHFFFAOYSA-N 0.000 description 1
- GVGUFUZHNYFZLC-UHFFFAOYSA-N dodecyl benzenesulfonate;sodium Chemical compound [Na].CCCCCCCCCCCCOS(=O)(=O)C1=CC=CC=C1 GVGUFUZHNYFZLC-UHFFFAOYSA-N 0.000 description 1
- 125000003438 dodecyl group Chemical group [H]C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])* 0.000 description 1
- 239000003480 eluent Substances 0.000 description 1
- 238000004945 emulsification Methods 0.000 description 1
- 125000003700 epoxy group Chemical group 0.000 description 1
- UIWXSTHGICQLQT-UHFFFAOYSA-N ethenyl propanoate Chemical compound CCC(=O)OC=C UIWXSTHGICQLQT-UHFFFAOYSA-N 0.000 description 1
- JEWCZPTVOYXPGG-UHFFFAOYSA-N ethenyl-ethoxy-dimethylsilane Chemical compound CCO[Si](C)(C)C=C JEWCZPTVOYXPGG-UHFFFAOYSA-N 0.000 description 1
- MABAWBWRUSBLKQ-UHFFFAOYSA-N ethenyl-tri(propan-2-yloxy)silane Chemical compound CC(C)O[Si](OC(C)C)(OC(C)C)C=C MABAWBWRUSBLKQ-UHFFFAOYSA-N 0.000 description 1
- 125000005448 ethoxyethyl group Chemical group [H]C([H])([H])C([H])([H])OC([H])([H])C([H])([H])* 0.000 description 1
- SBRXLTRZCJVAPH-UHFFFAOYSA-N ethyl(trimethoxy)silane Chemical compound CC[Si](OC)(OC)OC SBRXLTRZCJVAPH-UHFFFAOYSA-N 0.000 description 1
- 125000000816 ethylene group Chemical group [H]C([H])([*:1])C([H])([H])[*:2] 0.000 description 1
- 238000001704 evaporation Methods 0.000 description 1
- 239000000194 fatty acid Substances 0.000 description 1
- 229930195729 fatty acid Natural products 0.000 description 1
- 239000000945 filler Substances 0.000 description 1
- 239000000706 filtrate Substances 0.000 description 1
- 239000010419 fine particle Substances 0.000 description 1
- 238000007647 flexography Methods 0.000 description 1
- 239000007789 gas Substances 0.000 description 1
- 239000003365 glass fiber Substances 0.000 description 1
- 230000009477 glass transition Effects 0.000 description 1
- 125000003055 glycidyl group Chemical group C(C1CO1)* 0.000 description 1
- 238000010559 graft polymerization reaction Methods 0.000 description 1
- CGQIJXYITMTOBI-UHFFFAOYSA-N hex-5-enyl(trimethoxy)silane Chemical compound CO[Si](OC)(OC)CCCCC=C CGQIJXYITMTOBI-UHFFFAOYSA-N 0.000 description 1
- 125000004836 hexamethylene group Chemical group [H]C([H])([*:2])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])[*:1] 0.000 description 1
- FUZZWVXGSFPDMH-UHFFFAOYSA-N hexanoic acid Chemical compound CCCCCC(O)=O FUZZWVXGSFPDMH-UHFFFAOYSA-N 0.000 description 1
- 125000004051 hexyl group Chemical group [H]C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])C([H])([H])* 0.000 description 1
- 239000000413 hydrolysate Substances 0.000 description 1
- 230000002209 hydrophobic effect Effects 0.000 description 1
- 150000002466 imines Chemical class 0.000 description 1
- 230000001771 impaired effect Effects 0.000 description 1
- 229910052738 indium Inorganic materials 0.000 description 1
- 239000011261 inert gas Substances 0.000 description 1
- 238000002347 injection Methods 0.000 description 1
- 239000007924 injection Substances 0.000 description 1
- 239000011810 insulating material Substances 0.000 description 1
- 230000003993 interaction Effects 0.000 description 1
- 229910052742 iron Inorganic materials 0.000 description 1
- GJRQTCIYDGXPES-UHFFFAOYSA-N iso-butyl acetate Natural products CC(C)COC(C)=O GJRQTCIYDGXPES-UHFFFAOYSA-N 0.000 description 1
- 125000000959 isobutyl group Chemical group [H]C([H])([H])C([H])(C([H])([H])[H])C([H])([H])* 0.000 description 1
- FGKJLKRYENPLQH-UHFFFAOYSA-M isocaproate Chemical compound CC(C)CCC([O-])=O FGKJLKRYENPLQH-UHFFFAOYSA-M 0.000 description 1
- OQAGVSWESNCJJT-UHFFFAOYSA-N isovaleric acid methyl ester Natural products COC(=O)CC(C)C OQAGVSWESNCJJT-UHFFFAOYSA-N 0.000 description 1
- DKYWVDODHFEZIM-UHFFFAOYSA-N ketoprofen Chemical compound OC(=O)C(C)C1=CC=CC(C(=O)C=2C=CC=CC=2)=C1 DKYWVDODHFEZIM-UHFFFAOYSA-N 0.000 description 1
- 230000031700 light absorption Effects 0.000 description 1
- 230000007774 longterm Effects 0.000 description 1
- FPYJFEHAWHCUMM-UHFFFAOYSA-N maleic anhydride Chemical compound O=C1OC(=O)C=C1 FPYJFEHAWHCUMM-UHFFFAOYSA-N 0.000 description 1
- 229910052748 manganese Inorganic materials 0.000 description 1
- 239000012528 membrane Substances 0.000 description 1
- 125000000956 methoxy group Chemical group [H]C([H])([H])O* 0.000 description 1
- UZKWTJUDCOPSNM-UHFFFAOYSA-N methoxybenzene Substances CCCCOC=C UZKWTJUDCOPSNM-UHFFFAOYSA-N 0.000 description 1
- 238000013508 migration Methods 0.000 description 1
- 230000005012 migration Effects 0.000 description 1
- 230000004048 modification Effects 0.000 description 1
- 238000012986 modification Methods 0.000 description 1
- ZQXSMRAEXCEDJD-UHFFFAOYSA-N n-ethenylformamide Chemical class C=CNC=O ZQXSMRAEXCEDJD-UHFFFAOYSA-N 0.000 description 1
- 125000004123 n-propyl group Chemical group [H]C([H])([H])C([H])([H])C([H])([H])* 0.000 description 1
- 239000012802 nanoclay Substances 0.000 description 1
- 239000002086 nanomaterial Substances 0.000 description 1
- 229910052759 nickel Inorganic materials 0.000 description 1
- JFNLZVQOOSMTJK-KNVOCYPGSA-N norbornene Chemical compound C1[C@@H]2CC[C@H]1C=C2 JFNLZVQOOSMTJK-KNVOCYPGSA-N 0.000 description 1
- REJKHFKLPFJGAQ-UHFFFAOYSA-N oxiran-2-ylmethanethiol Chemical compound SCC1CO1 REJKHFKLPFJGAQ-UHFFFAOYSA-N 0.000 description 1
- 125000004430 oxygen atom Chemical group O* 0.000 description 1
- 125000004817 pentamethylene group Chemical group [H]C([H])([*:2])C([H])([H])C([H])([H])C([H])([H])C([H])([H])[*:1] 0.000 description 1
- 125000001147 pentyl group Chemical group C(CCCC)* 0.000 description 1
- 125000002467 phosphate group Chemical group [H]OP(=O)(O[H])O[*] 0.000 description 1
- 125000004193 piperazinyl group Chemical group 0.000 description 1
- XBXHCBLBYQEYTI-UHFFFAOYSA-N piperidin-4-ylmethanol Chemical compound OCC1CCNCC1 XBXHCBLBYQEYTI-UHFFFAOYSA-N 0.000 description 1
- 125000003386 piperidinyl group Chemical group 0.000 description 1
- 239000004014 plasticizer Substances 0.000 description 1
- 229920000728 polyester Polymers 0.000 description 1
- 229920000570 polyether Polymers 0.000 description 1
- 229920001223 polyethylene glycol Polymers 0.000 description 1
- 229920005862 polyol Polymers 0.000 description 1
- 150000003077 polyols Chemical class 0.000 description 1
- 229920002503 polyoxyethylene-polyoxypropylene Polymers 0.000 description 1
- 229920001451 polypropylene glycol Polymers 0.000 description 1
- USHAGKDGDHPEEY-UHFFFAOYSA-L potassium persulfate Chemical compound [K+].[K+].[O-]S(=O)(=O)OOS([O-])(=O)=O USHAGKDGDHPEEY-UHFFFAOYSA-L 0.000 description 1
- UIIIBRHUICCMAI-UHFFFAOYSA-N prop-2-ene-1-sulfonic acid Chemical compound OS(=O)(=O)CC=C UIIIBRHUICCMAI-UHFFFAOYSA-N 0.000 description 1
- 239000001294 propane Substances 0.000 description 1
- 125000004368 propenyl group Chemical group C(=CC)* 0.000 description 1
- 229940090181 propyl acetate Drugs 0.000 description 1
- 125000000719 pyrrolidinyl group Chemical group 0.000 description 1
- 229920005604 random copolymer Polymers 0.000 description 1
- 239000000376 reactant Substances 0.000 description 1
- 230000035484 reaction time Effects 0.000 description 1
- 239000012966 redox initiator Substances 0.000 description 1
- 238000011160 research Methods 0.000 description 1
- 239000013557 residual solvent Substances 0.000 description 1
- 125000002914 sec-butyl group Chemical group [H]C([H])([H])C([H])([H])C([H])(*)C([H])([H])[H] 0.000 description 1
- SCPYDCQAZCOKTP-UHFFFAOYSA-N silanol Chemical compound [SiH3]O SCPYDCQAZCOKTP-UHFFFAOYSA-N 0.000 description 1
- RMAQACBXLXPBSY-UHFFFAOYSA-N silicic acid Chemical compound O[Si](O)(O)O RMAQACBXLXPBSY-UHFFFAOYSA-N 0.000 description 1
- 239000002356 single layer Substances 0.000 description 1
- 238000005245 sintering Methods 0.000 description 1
- 238000007764 slot die coating Methods 0.000 description 1
- 235000010378 sodium ascorbate Nutrition 0.000 description 1
- PPASLZSBLFJQEF-RKJRWTFHSA-M sodium ascorbate Substances [Na+].OC[C@@H](O)[C@H]1OC(=O)C(O)=C1[O-] PPASLZSBLFJQEF-RKJRWTFHSA-M 0.000 description 1
- 229960005055 sodium ascorbate Drugs 0.000 description 1
- 229940080264 sodium dodecylbenzenesulfonate Drugs 0.000 description 1
- 235000010267 sodium hydrogen sulphite Nutrition 0.000 description 1
- 235000019333 sodium laurylsulphate Nutrition 0.000 description 1
- PPASLZSBLFJQEF-RXSVEWSESA-M sodium-L-ascorbate Chemical compound [Na+].OC[C@H](O)[C@H]1OC(=O)C(O)=C1[O-] PPASLZSBLFJQEF-RXSVEWSESA-M 0.000 description 1
- 125000006850 spacer group Chemical group 0.000 description 1
- 238000004528 spin coating Methods 0.000 description 1
- 238000010561 standard procedure Methods 0.000 description 1
- 229960002317 succinimide Drugs 0.000 description 1
- 125000000542 sulfonic acid group Chemical group 0.000 description 1
- 239000002344 surface layer Substances 0.000 description 1
- 125000000999 tert-butyl group Chemical group [H]C([H])([H])C(*)(C([H])([H])[H])C([H])([H])[H] 0.000 description 1
- 229950011008 tetrachloroethylene Drugs 0.000 description 1
- 125000000383 tetramethylene group Chemical group [H]C([H])([*:1])C([H])([H])C([H])([H])C([H])([H])[*:2] 0.000 description 1
- OGIDPMRJRNCKJF-UHFFFAOYSA-N titanium oxide Inorganic materials [Ti]=O OGIDPMRJRNCKJF-UHFFFAOYSA-N 0.000 description 1
- 238000012546 transfer Methods 0.000 description 1
- 125000005409 triarylsulfonium group Chemical group 0.000 description 1
- UBOXGVDOUJQMTN-UHFFFAOYSA-N trichloroethylene Natural products ClCC(Cl)Cl UBOXGVDOUJQMTN-UHFFFAOYSA-N 0.000 description 1
- FOQJQXVUMYLJSU-UHFFFAOYSA-N triethoxy(1-triethoxysilylethyl)silane Chemical compound CCO[Si](OCC)(OCC)C(C)[Si](OCC)(OCC)OCC FOQJQXVUMYLJSU-UHFFFAOYSA-N 0.000 description 1
- PGVSPORIGRCPMG-UHFFFAOYSA-N triethoxy(1-triethoxysilylhexyl)silane Chemical compound CCCCCC([Si](OCC)(OCC)OCC)[Si](OCC)(OCC)OCC PGVSPORIGRCPMG-UHFFFAOYSA-N 0.000 description 1
- LMEKMHPYJBYBEV-UHFFFAOYSA-N triethoxy(2-triethoxysilylpropan-2-yl)silane Chemical compound CCO[Si](OCC)(OCC)C(C)(C)[Si](OCC)(OCC)OCC LMEKMHPYJBYBEV-UHFFFAOYSA-N 0.000 description 1
- IDGYYGWFOFXISD-UHFFFAOYSA-N triethoxy(3-triethoxysilylbutan-2-yl)silane Chemical compound C(C)O[Si](OCC)(OCC)C(C)C(C)[Si](OCC)(OCC)OCC IDGYYGWFOFXISD-UHFFFAOYSA-N 0.000 description 1
- DENFJSAFJTVPJR-UHFFFAOYSA-N triethoxy(ethyl)silane Chemical compound CCO[Si](CC)(OCC)OCC DENFJSAFJTVPJR-UHFFFAOYSA-N 0.000 description 1
- RKYSDIOEHLMYRS-UHFFFAOYSA-N triethoxy(hex-5-enyl)silane Chemical compound CCO[Si](OCC)(OCC)CCCCC=C RKYSDIOEHLMYRS-UHFFFAOYSA-N 0.000 description 1
- NBXZNTLFQLUFES-UHFFFAOYSA-N triethoxy(propyl)silane Chemical compound CCC[Si](OCC)(OCC)OCC NBXZNTLFQLUFES-UHFFFAOYSA-N 0.000 description 1
- NIINUVYELHEORX-UHFFFAOYSA-N triethoxy(triethoxysilylmethyl)silane Chemical compound CCO[Si](OCC)(OCC)C[Si](OCC)(OCC)OCC NIINUVYELHEORX-UHFFFAOYSA-N 0.000 description 1
- JVAFDQZZUMUFSM-UHFFFAOYSA-N triethoxy-[5,5,6,6,7,7,7-heptafluoro-4,4-bis(trifluoromethyl)heptyl]silane Chemical compound CCO[Si](OCC)(OCC)CCCC(C(F)(F)F)(C(F)(F)F)C(F)(F)C(F)(F)C(F)(F)F JVAFDQZZUMUFSM-UHFFFAOYSA-N 0.000 description 1
- UZIAQVMNAXPCJQ-UHFFFAOYSA-N triethoxysilylmethyl 2-methylprop-2-enoate Chemical compound CCO[Si](OCC)(OCC)COC(=O)C(C)=C UZIAQVMNAXPCJQ-UHFFFAOYSA-N 0.000 description 1
- JBYXACURRYATNJ-UHFFFAOYSA-N trimethoxy(1-trimethoxysilylhexyl)silane Chemical compound CCCCCC([Si](OC)(OC)OC)[Si](OC)(OC)OC JBYXACURRYATNJ-UHFFFAOYSA-N 0.000 description 1
- WGUISIBZFQKBPC-UHFFFAOYSA-N trimethoxy(1-trimethoxysilylpropyl)silane Chemical compound CO[Si](OC)(OC)C(CC)[Si](OC)(OC)OC WGUISIBZFQKBPC-UHFFFAOYSA-N 0.000 description 1
- JCGDCINCKDQXDX-UHFFFAOYSA-N trimethoxy(2-trimethoxysilylethyl)silane Chemical compound CO[Si](OC)(OC)CC[Si](OC)(OC)OC JCGDCINCKDQXDX-UHFFFAOYSA-N 0.000 description 1
- QRTOPPGMVFGMNI-UHFFFAOYSA-N trimethoxy(3-trimethoxysilylbutan-2-yl)silane Chemical compound CO[Si](OC)(OC)C(C(C)[Si](OC)(OC)OC)C QRTOPPGMVFGMNI-UHFFFAOYSA-N 0.000 description 1
- BQXJQTRISSSESR-UHFFFAOYSA-N trimethoxy(3-trimethoxysilylpentan-3-yl)silane Chemical compound CO[Si](OC)(OC)C(CC)(CC)[Si](OC)(OC)OC BQXJQTRISSSESR-UHFFFAOYSA-N 0.000 description 1
- RKLXSINPXIQKIB-UHFFFAOYSA-N trimethoxy(oct-7-enyl)silane Chemical compound CO[Si](OC)(OC)CCCCCCC=C RKLXSINPXIQKIB-UHFFFAOYSA-N 0.000 description 1
- LGROXJWYRXANBB-UHFFFAOYSA-N trimethoxy(propan-2-yl)silane Chemical compound CO[Si](OC)(OC)C(C)C LGROXJWYRXANBB-UHFFFAOYSA-N 0.000 description 1
- HQYALQRYBUJWDH-UHFFFAOYSA-N trimethoxy(propyl)silane Chemical compound CCC[Si](OC)(OC)OC HQYALQRYBUJWDH-UHFFFAOYSA-N 0.000 description 1
- DJYGUVIGOGFJOF-UHFFFAOYSA-N trimethoxy(trimethoxysilylmethyl)silane Chemical compound CO[Si](OC)(OC)C[Si](OC)(OC)OC DJYGUVIGOGFJOF-UHFFFAOYSA-N 0.000 description 1
- 125000003258 trimethylene group Chemical group [H]C([H])([*:2])C([H])([H])C([H])([H])[*:1] 0.000 description 1
- 238000009281 ultraviolet germicidal irradiation Methods 0.000 description 1
- NQPDZGIKBAWPEJ-UHFFFAOYSA-N valeric acid Chemical compound CCCCC(O)=O NQPDZGIKBAWPEJ-UHFFFAOYSA-N 0.000 description 1
- 229910052720 vanadium Inorganic materials 0.000 description 1
- 239000003643 water by type Substances 0.000 description 1
- 230000037303 wrinkles Effects 0.000 description 1
- PAPBSGBWRJIAAV-UHFFFAOYSA-N ε-Caprolactone Chemical compound O=C1CCCCCO1 PAPBSGBWRJIAAV-UHFFFAOYSA-N 0.000 description 1
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
- C08J9/009—Use of pretreated compounding ingredients
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
- C09J7/00—Adhesives in the form of films or foils
- C09J7/20—Adhesives in the form of films or foils characterised by their carriers
- C09J7/22—Plastics; Metallised plastics
- C09J7/26—Porous or cellular plastics
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
- C09J4/00—Adhesives based on organic non-macromolecular compounds having at least one polymerisable carbon-to-carbon unsaturated bond ; adhesives, based on monomers of macromolecular compounds of groups C09J183/00 - C09J183/16
- C09J4/06—Organic non-macromolecular compounds having at least one polymerisable carbon-to-carbon unsaturated bond in combination with a macromolecular compound other than an unsaturated polymer of groups C09J159/00 - C09J187/00
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B27/00—Layered products comprising a layer of synthetic resin
- B32B27/28—Layered products comprising a layer of synthetic resin comprising synthetic resins not wholly covered by any one of the sub-groups B32B27/30 - B32B27/42
- B32B27/283—Layered products comprising a layer of synthetic resin comprising synthetic resins not wholly covered by any one of the sub-groups B32B27/30 - B32B27/42 comprising polysiloxanes
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B3/00—Layered products comprising a layer with external or internal discontinuities or unevennesses, or a layer of non-planar form; Layered products having particular features of form
- B32B3/26—Layered products comprising a layer with external or internal discontinuities or unevennesses, or a layer of non-planar form; Layered products having particular features of form characterised by a particular shape of the outline of the cross-section of a continuous layer; characterised by a layer with cavities or internal voids ; characterised by an apertured layer
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B7/00—Layered products characterised by the relation between layers; Layered products characterised by the relative orientation of features between layers, or by the relative values of a measurable parameter between layers, i.e. products comprising layers having different physical, chemical or physicochemical properties; Layered products characterised by the interconnection of layers
- B32B7/02—Physical, chemical or physicochemical properties
- B32B7/023—Optical properties
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B7/00—Layered products characterised by the relation between layers; Layered products characterised by the relative orientation of features between layers, or by the relative values of a measurable parameter between layers, i.e. products comprising layers having different physical, chemical or physicochemical properties; Layered products characterised by the interconnection of layers
- B32B7/04—Interconnection of layers
- B32B7/12—Interconnection of layers using interposed adhesives or interposed materials with bonding properties
- B32B7/14—Interconnection of layers using interposed adhesives or interposed materials with bonding properties applied in spaced arrangements, e.g. in stripes
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F265/00—Macromolecular compounds obtained by polymerising monomers on to polymers of unsaturated monocarboxylic acids or derivatives thereof as defined in group C08F20/00
- C08F265/04—Macromolecular compounds obtained by polymerising monomers on to polymers of unsaturated monocarboxylic acids or derivatives thereof as defined in group C08F20/00 on to polymers of esters
- C08F265/06—Polymerisation of acrylate or methacrylate esters on to polymers thereof
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G18/00—Polymeric products of isocyanates or isothiocyanates
- C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
- C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
- C08G18/40—High-molecular-weight compounds
- C08G18/62—Polymers of compounds having carbon-to-carbon double bonds
- C08G18/6283—Polymers of nitrogen containing compounds having carbon-to-carbon double bonds
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G18/00—Polymeric products of isocyanates or isothiocyanates
- C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
- C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
- C08G18/72—Polyisocyanates or polyisothiocyanates
- C08G18/80—Masked polyisocyanates
- C08G18/8003—Masked polyisocyanates masked with compounds having at least two groups containing active hydrogen
- C08G18/8006—Masked polyisocyanates masked with compounds having at least two groups containing active hydrogen with compounds of C08G18/32
- C08G18/8009—Masked polyisocyanates masked with compounds having at least two groups containing active hydrogen with compounds of C08G18/32 with compounds of C08G18/3203
- C08G18/8022—Masked polyisocyanates masked with compounds having at least two groups containing active hydrogen with compounds of C08G18/32 with compounds of C08G18/3203 with polyols having at least three hydroxy groups
- C08G18/8029—Masked aromatic polyisocyanates
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K9/00—Use of pretreated ingredients
- C08K9/04—Ingredients treated with organic substances
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
- C09J133/00—Adhesives based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Adhesives based on derivatives of such polymers
- C09J133/04—Homopolymers or copolymers of esters
- C09J133/06—Homopolymers or copolymers of esters of esters containing only carbon, hydrogen and oxygen, the oxygen atom being present only as part of the carboxyl radical
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
- C09J133/00—Adhesives based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Adhesives based on derivatives of such polymers
- C09J133/04—Homopolymers or copolymers of esters
- C09J133/06—Homopolymers or copolymers of esters of esters containing only carbon, hydrogen and oxygen, the oxygen atom being present only as part of the carboxyl radical
- C09J133/10—Homopolymers or copolymers of methacrylic acid esters
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
- C09J133/00—Adhesives based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Adhesives based on derivatives of such polymers
- C09J133/04—Homopolymers or copolymers of esters
- C09J133/14—Homopolymers or copolymers of esters of esters containing halogen, nitrogen, sulfur or oxygen atoms in addition to the carboxy oxygen
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
- C09J151/00—Adhesives based on graft polymers in which the grafted component is obtained by reactions only involving carbon-to-carbon unsaturated bonds; Adhesives based on derivatives of such polymers
- C09J151/003—Adhesives based on graft polymers in which the grafted component is obtained by reactions only involving carbon-to-carbon unsaturated bonds; Adhesives based on derivatives of such polymers grafted on to macromolecular compounds obtained by reactions only involving unsaturated carbon-to-carbon bonds
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
- C09J175/00—Adhesives based on polyureas or polyurethanes; Adhesives based on derivatives of such polymers
- C09J175/04—Polyurethanes
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
- C09J4/00—Adhesives based on organic non-macromolecular compounds having at least one polymerisable carbon-to-carbon unsaturated bond ; adhesives, based on monomers of macromolecular compounds of groups C09J183/00 - C09J183/16
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
- C09J7/00—Adhesives in the form of films or foils
- C09J7/30—Adhesives in the form of films or foils characterised by the adhesive composition
- C09J7/38—Pressure-sensitive adhesives [PSA]
- C09J7/381—Pressure-sensitive adhesives [PSA] based on macromolecular compounds obtained by reactions involving only carbon-to-carbon unsaturated bonds
- C09J7/385—Acrylic polymers
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F220/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride ester, amide, imide or nitrile thereof
- C08F220/02—Monocarboxylic acids having less than ten carbon atoms; Derivatives thereof
- C08F220/10—Esters
- C08F220/12—Esters of monohydric alcohols or phenols
- C08F220/16—Esters of monohydric alcohols or phenols of phenols or of alcohols containing two or more carbon atoms
- C08F220/18—Esters of monohydric alcohols or phenols of phenols or of alcohols containing two or more carbon atoms with acrylic or methacrylic acids
- C08F220/1804—C4-(meth)acrylate, e.g. butyl (meth)acrylate, isobutyl (meth)acrylate or tert-butyl (meth)acrylate
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G2170/00—Compositions for adhesives
- C08G2170/40—Compositions for pressure-sensitive adhesives
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J2383/00—Characterised by the use of macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing silicon with or without sulfur, nitrogen, oxygen, or carbon only; Derivatives of such polymers
- C08J2383/04—Polysiloxanes
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
- C09J2301/00—Additional features of adhesives in the form of films or foils
- C09J2301/10—Additional features of adhesives in the form of films or foils characterized by the structural features of the adhesive tape or sheet
- C09J2301/12—Additional features of adhesives in the form of films or foils characterized by the structural features of the adhesive tape or sheet by the arrangement of layers
- C09J2301/124—Additional features of adhesives in the form of films or foils characterized by the structural features of the adhesive tape or sheet by the arrangement of layers the adhesive layer being present on both sides of the carrier, e.g. double-sided adhesive tape
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
- C09J2301/00—Additional features of adhesives in the form of films or foils
- C09J2301/30—Additional features of adhesives in the form of films or foils characterized by the chemical, physicochemical or physical properties of the adhesive or the carrier
- C09J2301/302—Additional features of adhesives in the form of films or foils characterized by the chemical, physicochemical or physical properties of the adhesive or the carrier the adhesive being pressure-sensitive, i.e. tacky at temperatures inferior to 30°C
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
- C09J2301/00—Additional features of adhesives in the form of films or foils
- C09J2301/30—Additional features of adhesives in the form of films or foils characterized by the chemical, physicochemical or physical properties of the adhesive or the carrier
- C09J2301/312—Additional features of adhesives in the form of films or foils characterized by the chemical, physicochemical or physical properties of the adhesive or the carrier parameters being the characterizing feature
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
- C09J2301/00—Additional features of adhesives in the form of films or foils
- C09J2301/50—Additional features of adhesives in the form of films or foils characterized by process specific features
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
- C09J2400/00—Presence of inorganic and organic materials
- C09J2400/20—Presence of organic materials
- C09J2400/24—Presence of a foam
- C09J2400/243—Presence of a foam in the substrate
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
- C09J2433/00—Presence of (meth)acrylic polymer
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
- C09J2483/00—Presence of polysiloxane
- C09J2483/006—Presence of polysiloxane in the substrate
-
- G—PHYSICS
- G02—OPTICS
- G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
- G02B1/00—Optical elements characterised by the material of which they are made; Optical coatings for optical elements
- G02B1/10—Optical coatings produced by application to, or surface treatment of, optical elements
- G02B1/11—Anti-reflection coatings
- G02B1/111—Anti-reflection coatings using layers comprising organic materials
Definitions
- the present invention relates to a void-containing layer, a laminate, a method for producing a void-containing layer, an optical member, and an optical apparatus.
- an air layer having a low refractive index is used as a total reflection layer.
- optical film members e.g., a light guide plate and a reflector
- a liquid crystal device are laminated with an air layer interposed therebetween.
- the respective members are separated from each other by an air layer, particularly in a case where the members are large in size, problems such as distortion of the members may arise.
- the respective members are integrated by a pressure-sensitive adhesive/adhesive without an air layer interposed therebetween (Patent Literature 1).
- Patent Literature 1 if there is no air layer serving as a total reflection layer, optical characteristics may become poor, which causes light leakage.
- Patent Literature 2 describes a structure in which a light guide plate and a reflector are laminated with a layer having a lower refractive index than that of the light guide plate interposed therebetween.
- the low refractive index layer for example, a void-containing layer having voids is used in order to make the refractive index low as close as possible to air.
- Patent Literature 3 Furthermore, in order to introduce a void-containing layer into a device, an integrated configuration with a pressure-sensitive adhesive/adhesive layer has also been proposed (Patent Literature 3).
- the void-containing layer is laminated on another layer with a pressure-sensitive adhesive/adhesive layer interposed therebetween to use.
- the pressure-sensitive adhesive or adhesive constituting the pressure-sensitive adhesive/adhesive layer may penetrate into the voids of the void-containing layer to fill the voids, which lowers the void fraction of the void-containing layer and increases the refractive index. The higher the void fraction of the void-containing layer, the more likely the pressure-sensitive adhesive or adhesive will penetrate.
- the pressure-sensitive adhesive or adhesive In a high-temperature environment, the pressure-sensitive adhesive or adhesive is prone to penetrate into the voids due to the molecular motion (decrease in elastic modulus) of the pressure-sensitive adhesive or adhesive. In a high humidity environment, the pressure-sensitive adhesive or adhesive is prone to penetrate into the voids due to water absorption of the pressure-sensitive adhesive or adhesive.
- the pressure-sensitive adhesive or the adhesive having an elastic modulus as high as possible may be used. However, if the elastic modulus of the pressure-sensitive adhesive or adhesive is high (hard), the pressure-sensitive adhesive force or the adhesive force may be lowered. Conversely, if the elastic modulus of the pressure-sensitive adhesive or adhesive is low (soft), although a high pressure-sensitive adhesive force or an adhesive force is readily obtained, the pressure-sensitive adhesive or adhesive may be prone to penetrate into the voids.
- a layer that can suppress the penetration of the pressure-sensitive adhesive or the adhesive on the void-containing layer by using a substance other than the pressure-sensitive adhesive or the adhesive.
- forming the penetration suppressing layer is required separately from forming the void-containing layer, which increases the number of manufacturing processes.
- a void-containing layer in which a pressure-sensitive adhesive or an adhesive is less liable to penetrate into voids.
- the present invention provides a void-containing layer, including: particles chemically bonding to each other, wherein the void-containing layer has a void fraction of 35 vol % or more, the particle is an inorganic-organic composite particle in which an organic group is bonded to an inorganic compound, the organic group includes a R 1 group which is a linear or branched alkyl group and a R 2 group which is a group containing a carbon-carbon unsaturated bond, and a molar ratio of the R 2 group relative to a sum of the R 1 group and the R 2 group is from 1 to 30 mol %.
- the present invention also provides a laminate including: the void-containing layer according to the present invention; and a pressure-sensitive adhesive/adhesive layer directly laminated on one or both sides of the void-containing layer.
- the present invention also provides a method for producing the void-containing layer according to the present invention, including: coating a dispersion liquid including the particles; and drying the coated dispersion liquid.
- the present invention also provides an optical member including: the laminate according to the present invention.
- the present invention also provides an optical apparatus including: the optical member according to the present invention.
- the present invention can provide a void-containing layer in which a pressure-sensitive adhesive or an adhesive is less liable to penetrate into voids, a laminate including the void-containing layer, a method for producing the void-containing layer, and an optical member and an optical apparatus including the void-containing layer.
- FIG. 1 is a cross-sectional view schematically illustrating an example of a method for forming a laminate of the present invention in which a void-containing layer 21 , an intermediate layer 22 , and a pressure-sensitive adhesive/adhesive layer 30 are laminated on a resin base 10 .
- FIG. 2 is a schematic view showing an example of some processes in a method for producing a laminated film in the form of a roll (“laminated film roll”) and an apparatus used in the method.
- FIG. 3 is a schematic view showing another example of some processes in a method for producing a laminated film roll and an apparatus used for the method.
- the R 1 group may be a linear or branched alkyl group having 1 to 6 carbon atoms.
- one or more carbon-carbon unsaturated bonds may be present per R 2 group, for example.
- the carbon-carbon unsaturated bond may be, for example, a carbon-carbon double bond or a carbon-carbon triple bond.
- the carbon-carbon unsaturated bond may be, for example, one or both of a carbon-carbon double bond and a carbon-carbon triple bond.
- the R 2 group may be a group represented by the following chemical formula (R 2 ):
- R 21 , R 22 and R 23 are each a hydrogen atom or a linear or branched alkyl group, and may be the same or different from one another, and R 24 is a linear or branched alkylene group, an oxycarbonyl group, an ether group, or a linear or branched alkylene oxycarbonyl group, or is not present.
- R 24 is a linear or branched alkylene group, an oxycarbonyl group, an ether group, or a linear or branched alkylene oxycarbonyl group, or is not present.
- the “oxycarbonyl group” refers to “—COO—” which is an atomic group in which a hydrogen atom of a carboxy group “—COOH” is replaced with a bond (single bond).
- R 21 is a hydrogen atom
- R 22 is a methyl group
- R 23 is a hydrogen atom
- R 24 is an oxycarbonyl group
- R 2 is “CH 2 ⁇ C(CH 3 )—COO—”.
- the “linear or branched alkylene oxycarbonyl group” refers to a “—COO-L-” (L is a linear or branched alkylene group) which is an atomic group in which a hydrogen atom of the carboxy group “—COOH” is replaced with a linear or branched alkylene group.
- R 21 is a hydrogen atom
- R 1 is a methyl group
- R 1 is a hydrogen atom
- R 24 is a trimethylene oxycarbonyl group (a kind of linear or branched alkylene oxycarbonyl group)
- R 2 is “CH 2 ⁇ C(CH 3 )—COO—(CH 2 ) 3 —”.
- the void-containing layer of the present invention may be, for example a void-containing layer, wherein in the chemical formulae (R 2 ).
- R 21 , R 22 and R 23 are each a hydrogen atom or a linear or branched alkyl group having 1 to 6 carbon atoms, and may be the same or different from one another, and R 24 is a linear or branched alkylene group having 1 to 6 carbon atoms, an oxycarbonyl group, an ether group, or a linear or branched alkylene oxycarbonyl group having 1 to 7 carbon atoms, or is not present.
- the R 2 group may be CH 2 ⁇ CH—, CH 2 ⁇ CH—(CH 2 ) 1-6 —, CH 2 ⁇ C(CH 3 )—COO—(CH 2 ⁇ CH—O—, CH 2 ⁇ C(CH 3 )—COO—(CH 2 ) 1-6 —, or CH 2 ⁇ C(CH 3 )—CH 2 —.
- —(CH 2 ) 1-6 — represents a linear alkylene group having any of 1 to 6 methylene groups, that is, a methylene group, an ethylene group (dimethylene group), a trimethylene group, a tetramethylene group, a pentamethylene group, or a hexamethylene group.
- the inorganic compound in the particle contains at least one skeletal atom selected from the group consisting of Si, Mg, Al, Ti, Zn and Zr.
- the void-containing layer may be, for example, a silicone-porous material.
- silicone porous material refers to a polymer porous material containing siloxane bonds, and includes, for example, a porous material containing silsesquioxane as a structural unit.
- the void-containing layer of the present invention may have a refractive index of 1.25 or less, for example.
- the laminate of the present invention may include, for example, an intermediate layer between the void-containing layer and the pressure-sensitive adhesive/adhesive layer, wherein the intermediate layer is a layer formed by uniting the void-containing layer and the pressure-sensitive adhesive/adhesive layer.
- the pressure-sensitive adhesive/adhesive layer is formed from a pressure-sensitive adhesive/adhesive coating solution containing a (meth)acrylic polymer, and a weight average molecular weight of the (meth)acrylic polymer obtained by polymerizing 3 to 10 wt % of a heterocycle-containing acrylic monomer, 0.5 to 5 wt % of (meth)acrylic acid, 0.05 to 2 wt % of hydroxyalkyl (meth)acrylate, and 83 to 96.45 wt % of alkyl (meth)acrylate, as monomer components, is 1.5 million to 2.8 million.
- the (meth)acrylic polymer may include a (meth)acrylic polymer crosslinked with a crosslinking agent.
- the pressure-sensitive adhesive/adhesive layer may be formed by a method including: preparing a pressure-sensitive adhesive/adhesive coating solution including a (meth)acrylic polymer, a monomer having one or two reactive double bonds per molecule, an isocyanate-based crosslinking agent, and an organic peroxide; coating the pressure-sensitive adhesive/adhesive coating solution onto a base; and heat-drying the base coated with the pressure-sensitive adhesive/adhesive coating solution.
- the monomer having one or two reactive double bonds is heterocycle-containing acrylate.
- the pressure-sensitive adhesive/adhesive layer may have a storage elastic modulus of 1.0 ⁇ 10 5 or more at 23° C.
- the laminate of the present invention may have, for example, a refractive index of 1.25 or less after a heat/humidification durability test of maintaining a temperature at 60° C. and a relative humidity at 90% for 1000 hours.
- the laminate of the present invention can suppress obvious penetration of the pressure-sensitive adhesive/adhesive layer into the void-containing layer even under a particularly long-term heat/humidification durability test, for example.
- the reason (mechanism) for achieving both of the pressure-sensitive adhesive force or the adhesive force and the resistance to penetration of the pressure-sensitive adhesive or the adhesive into the voids is conceivable as follows, for example.
- the particles in the void-containing layer contain R 2 groups (for example, vinyl groups) which are groups containing carbon-carbon unsaturated bonds
- the R 2 groups are sterically hindered and electrostatically repulsed. Due to the steric hindrance and the electrostatic repulsion between the R 2 groups, when the particles are gelled by incorporating synthetic solvents of the void-containing layer (when skeleton is formed), the particles form a gel structure with a wider intermolecular distance. Therefore, the diameter of the void of the void-containing layer after removing the synthetic solvents from the skeleton of the void-containing layer increases.
- the electrostatic repulsion also acts when the particles are deposited to form a void-containing layer, which increases the volume of air contained in the void-containing layer, resulting in a decrease in the initial refractive index.
- the increase in the refractive index of the void-containing layer due to the absorption of the pressure-sensitive adhesive/adhesive layer under heat/humidification conditions and the penetration of the pressure-sensitive adhesive/adhesive layer into the voids due to the apparent decrease in the elastic modulus at high temperatures is caused by the penetration of the sol components from the pressure-sensitive adhesive/adhesive layer into the voids of the void-containing layer.
- the amount of the penetration component contained in the pressure-sensitive adhesive/adhesive layer is a constant amount when the thickness of the pressure-sensitive adhesive/adhesive layer is fixed. Therefore, if the void fraction of the void-containing layer is increased, the proportion of the voids filled with the pressure-sensitive adhesive in the entire void-containing layer after the heat/humidification durability test inevitably decreases. As a result, an increase in the refractive index after the heat/humidification durability test is suppressed. It is to be noted, however, that these mechanisms merely are examples and do not limit the present invention by any means.
- the content of the R 2 group is preferably not too large and not too small.
- the reason why the content of the R 2 group is preferably not too large is conceivable as follows, for example. First, when the R 2 group, which is a group containing a carbon-carbon unsaturated bond, is present, the diameter of the void of the void-containing layer tends to increase due to the steric hindrance and electrostatic repulsion.
- the content of the R 2 group be not too large.
- the content of the R 2 group be not too large in order to prevent the void diameter per void from becoming too large.
- a target Mw weight average molecular weight
- a target Mw weight average molecular weight range having a molecular size appropriate for the void diameter in the pressure-sensitive adhesive/adhesive layer will expand, resulting in increased sol components that can be penetrated into the void.
- the content of the R 2 group it is preferable that the content of the R 2 group be not too large.
- the void of the void-containing layer of the present invention may include nanoparticles, surfaces of which being modified with a compound having a surface orientation.
- the compound having the surface orientation may be an alkoxysilane derivative, and the alkoxysilane derivative may contain a fluoroalkyl group having 5 to 17 or 5 to 10 fluorine atoms.
- the fluoroalkyl group may be an alkyl group in which only a part of hydrogen is substituted with fluorine, or may be an alkyl group (perfluoroalkyl group) in which all hydrogen is substituted with fluorine.
- the void-containing layer of the present invention may contain, for example, 10 to 50 mass % of the nanoparticles relative to a skeleton component of the void-containing layer.
- a layer composed of the nanoparticles may be formed inside the void-containing layer while forming the void-containing layer.
- the pressure-sensitive adhesive/adhesive layer is less liable to penetrate into the void-containing layer.
- the reason (mechanism) is conceivable as follows, for example. First, the surface orientation (migration to an air interface) of a compound having a surface orientation (e.g., a compound having perfluoroalkyl) is utilized to impart the surface orientation to nanoparticles themselves, the surfaces of which have been modified with the compound.
- the compound having the surface orientation alone can perform the surface modification of the void-containing layer but is not enough to suppress the macroscopic penetration of the pressure-sensitive adhesive.
- the voids on the outermost surface of the void-containing layer are filled with the nanoparticles and the penetration of the pressure-sensitive adhesive or the adhesive is physically suppressed.
- nanoparticles, surfaces of which being not modified have no surface orientation, they are just present in the void-containing layer and are not oriented on the surface of the void-containing layer, which does not bring about a penetration suppressing effect.
- the nanoparticles By modifying the nanoparticles with a compound having a surface orientation, the nanoparticles have surface orientation to the void-containing layer.
- the voids on the outermost surface of the void-containing layer are filled with the nanoparticles modified with a compound having a surface orientation, thereby forming a layer for suppressing penetration of the pressure-sensitive adhesive or the adhesive on the outermost surface (surface layer).
- a penetration suppressing layer is unnecessary, and an increase in the number of manufacturing processes due to forming the penetration suppressing layer can be avoided.
- these mechanisms merely are examples and do not limit the present invention by any means.
- nanoparticles modified with a compound having a surface-orientation may be added to a coating solution for forming a void-containing layer.
- the void-containing layer of the present invention is a void-containing layer formed by chemically bonding particles to each other, wherein the void-containing layer has a void fraction of 35 vol % or more, the particle is an inorganic-organic composite particle in which an organic group is bonded to an inorganic compound, the organic group includes a R group which is a linear or branched alkyl group and a R 2 group which is a group containing a carbon-carbon unsaturated bond, and a molar ratio of the R 2 group relative to the sum of the R 1 group and the R 2 group is from 1 to 30 mol %.
- the laminate of the present invention is characterized in that it includes the void-containing layer of the present invention and a pressure-sensitive adhesive % adhesive layer directly laminated on one or both sides of the void-containing layer.
- the pressure-sensitive adhesive/adhesive layer is ‘directly laminated on’ the void-containing layer” may mean either the pressure-sensitive adhesive/adhesive layer is in direct contact with the void-containing layer or the pressure-sensitive adhesive/adhesive layer is laminated on the void-containing layer with an intermediate layer interposed therebetween.
- the void retention rate of the void-containing layer may be, for example, 70 vol % or more, 80 vol % or more, or 83 vol % or more relative to the voids before the heat/humidification durability test, and the upper limit of the void retention rate is not particularly limited, and is ideally 100 vol %, and may be 99 vol % or less, 98 vol % or less, or 95 vol % or less.
- the increasing rate of the thickness of the intermediate layer may be 500% or less relative to the thickness of the intermediate layer before the heat/humidification durability test with the thickness of the intermediate layer before the heat/humidification durability test being considered as 100%.
- the increasing rate of the thickness of the intermediate layer after the heat/humidification durability test may be, for example, 500% or less, 400% or less, or 300%/o or less, and for example, 110% or more, 120% or more, 130% or more, or 150% or more, relative to the thickness of the intermediate layer before the heat/humidification durability test with the thickness of the intermediate layer before the heat/humidification durability test being considered as 100%.
- the void retention rate of the void-containing layer after the heat/humidification durability test may be, for example, 80% or more, 85% or more, or 88% or more, and may be 99% or less, 98% or less, or 97% or less of the void retention rate in the case where only the void-containing layer has been subjected to the heat/humidification durability test.
- the light transmittance of the void-containing layer of the present invention or the laminate of the present invention may be 80% or more.
- the haze of the void-containing layer of the present invention or the laminate of the present invention may be 3% or less.
- the light transmittance may be, for example, 82% or more, 84% or more, 86% or more, or 88% or more, and the upper limit is not particularly limited, and is ideally 100%, and may be, for example, 95% or less, 92% or less, 91% or less, or 90% or less.
- the haze of the void-containing layer of the present invention or the laminate of the present invention can be measured, for example, by the haze measurement method described below.
- the light transmittance is a transmittance of light at a wavelength of 550 nm, and can be measured by, for example, the following measurement method.
- a spectrophotometer U-4100 (product name, manufactured by Hitachi, Ltd.) is used, and the laminate is used as a sample to be measured.
- the total light transmittance (light transmittance) of the sample is measured with the total light transmittance of air being considered as 100%.
- the value of the total light transmittance (light transmittance) is a value measured at a wavelength of 550 nm.
- the pressure-sensitive adhesive/adhesive layer may have a pressure-sensitive adhesive force or an adhesive force of 0.7N/25 mm or more, 0.8N/25 mm or more, 1.0N/25 mm or more, or 1.5N/25 mm or more, and 50N/25 mm or less, 30N/25 mm or less, 10N/25 mm or less, 5N/25 mm or less, or 3N/25 mm or less. From the viewpoint of risks of peeling off during handling when the laminate is attached to another layer, it is preferable that the pressure-sensitive adhesive force or the adhesive force of the pressure-sensitive adhesive/adhesive layer be not too low.
- the pressure-sensitive adhesive force or the adhesive force of the pressure-sensitive adhesive/adhesive layer be not too high.
- the pressure-sensitive adhesive force or the adhesive force of the pressure-sensitive adhesive/adhesive layer can be measured, for example, as follows.
- the laminated film of the present invention film in which the laminate of the present invention is formed on a resin film base
- a rectangular strip-shaped piece with a size of 50 mm ⁇ 140 mm is obtained as a sample, and the sample is fixed to a stainless plate with a double-sided tape.
- An acrylic pressure-sensitive adhesive layer (thickness: 20 ⁇ m) is attached to a PET film (T100: manufactured by Mitsubishi Plastics, Inc.), and the thus-obtained pressure-sensitive adhesive tape is cut into a piece with a size of 25 mm ⁇ 100 mm.
- the thus-obtained cut piece is attached to the laminated film of the present invention on the side opposite to the resin film to form a laminate of the PET film and the laminated film.
- the sample is chucked in an autograft tensile testing machine (AG-Xplus, manufactured by Shimadzu Corporation) with a distance between chucks being 100 mum, and the tensile test is performed at a tensile speed of 0.3 m/min.
- the mean value of the peel test data for 50 mm is set as the peel adhesion force, i.e., pressure-sensitive adhesive force.
- the adhesive force can also be measured by the same measurement method. In the present invention, there is no clear distinction between the “pressure-sensitive adhesive force” and the “adhesive force”.
- the laminate of the present invention may be formed on a base such as, for example, a film.
- the film may be, for example, a resin film.
- the “film” and the “sheet” generally, the one having a relatively small thickness is called a “film” and the one having a relatively large thickness is called a “sheet” in some cases, however, in the present invention, there is no particular distinction between the “film” and the “sheet”.
- the base is not limited to particular bases, and for example, a base made of a thermoplastic resin, a base made of glass, an inorganic base plate typified by silicon, a plastic formed of a thermosetting resin, an element such as a semiconductor, or a carbon fiber-based material typified by carbon nanotube can be favorably used.
- the base is by no means limited thereto.
- Examples of the form of the base include a film and a plate.
- the thermoplastic resin include polyethylene terephthalate (PET), acrylic resins, cellulose acetate propionate (CAP), cycloolefin polymer (COP), triacetylcellulose (TAC), polyethylene naphthalate (PEN), polyethylene (PE), and polypropylene (PP).
- the optical member of the present invention is not particularly limited, and may be, for example, an optical film including the laminate of the present invention.
- the optical apparatus (optical device) of the present invention is not particularly limited, and may be, for example, an image display device, an illumination device, or the like.
- the image display device include a liquid crystal display, an organic electro luminescence (EL) display, and a micro light emitting diode (LED) display.
- the illumination device may be, for example, an organic EL illumination, or the like.
- the void-containing layer in the laminate of the present invention (hereinafter also referred to as the “void-containing layer of the present invention”) will be described below with reference to examples. It is to be noted, however, that the void-containing layer of the present invention is not limited thereto.
- the void-containing layer of the present invention may have, for example, a void fraction of 35 vol % or more and a peak pore diameter of 50 nm or less.
- a void fraction of 35 vol % or more and a peak pore diameter of 50 nm or less may have, for example, a void fraction of 35 vol % or more and a peak pore diameter of 50 nm or less.
- the void fraction may be, for example, 35 vol % or more, 38 vol % or more, or 40 vol % or more, and 90 vol % or less, 80 vol % or less, or 75 vol % or less.
- the void-containing layer of the present invention may be, for example, a highly void-containing layer having a void fraction of 60 vol % or more.
- the void fraction can be measured, for example, by the following measurement method.
- the ratio (volume ratio) between the component of the layer and the air can be calculated by a standard method (for example, weight and volume are measured to calculate the density), whereby the void fraction (vol %) can be calculated.
- the void fraction can be calculated from the value of the refractive index as a layer, for example. Specifically, the void fraction is calculated according to the Lorentz-Lorenz's formula from the value of the refractive index measured by an ellipsometer.
- the void-containing layer of the present invention can be produced, for example, by chemical bonding of gel pulverized products (microporous particles) as will be described below.
- the voids of the void-containing layer can be divided into three types (1) to (3) below for convenience.
- the voids (2) are voids formed during pulverization, which are different from the voids (1) that can be formed in each block when each particle group generated by pulverizing a gel is regarded as one mass (block) regardless of the size or the like of the gel pulverized product (microporous particle).
- the voids (3) are voids created because of irregularity in the sizes or the like of the gel pulverized products (microporous particles) in pulverization (e.g., media-less pulverization).
- the void-containing layer of the present invention contains the voids (1) to (3), whereby an appropriate void fraction and peak pore diameter can be achieved, for example.
- the peak pore diameter may be, for example, 5 nm or more, 10 nm or more, or 20 nm or more, and 50 nm or less, 40 nm or less, or 30 nm or less.
- the lower limit value of the peak pore diameter of the void-containing layer is not particularly limited, but it is preferable that the peak pore diameter be not too small because it is difficult to increase the void fraction if the peak pore diameter is too small.
- the peak pore diameter can be measured, for example, by the following method.
- the peak pore diameter is calculated from the results of the BJH plot and the BET plot by nitrogen adsorption and the isothermal adsorption line using a pore distribution/specific surface area analyzer (product name: BELLSORP MINI, MicrotracBEL Corp.).
- the void-containing layer is a void-containing layer formed by chemically bonding particles to each other.
- the particle is an inorganic-organic composite particle in which an organic group is bonded to an inorganic compound, the organic group includes a R 1 group which is a linear or branched alkyl group and a R 2 group which is a group containing a carbon-carbon unsaturated bond, and the molar ratio of the R 2 group relative to the sum of the R 1 group and the R 2 group is from 1 to 30 mol %.
- the method for causing the particles to contain the R 23 group and the R 2 group will be described in detail below.
- the void-containing layer of the present invention may include nanoparticles, surfaces of which being modified with a compound having a surface orientation, as described above.
- the nanoparticles will be described in detail below.
- the void-containing layer of the present invention may include, for example, 10 to 50 mass %, 15 to 40 mass %, or 20 to 30 mass % of the nanoparticles relative to a skeleton component of the void-containing layer.
- the “skeleton component” means a component having the largest mass among components forming the void-containing layer of the present invention other than air.
- the “skeleton component” in the void-containing layer of the present invention is a condensation product of monoalkyl(trimethoxy)silane, for example.
- the thickness of the void-containing layer of the present invention is not particularly limited, and may be, for example, 100 nm or more, 200 nm or more, or 300 nm or more, and 10000 nm or less, 5000 nm or less, or 2000 nm or less.
- the void-containing layer of the present invention uses pulverized products of the porous gel material, for example. Tis, the three-dimensional structure of the porous gel material is destroyed, whereby a new three-dimensional structure different from that of the porous gel material is formed. As will be described below, the void-containing layer of the present invention becomes a layer having a new pore structure (new void-containing structure) that cannot be obtained in a layer formed using the porous gel material. That is, a nano-scale void-containing layer having a high void fraction can be formed.
- the void-containing layer of the present invention is a silicone porous material
- the pulverized products in the void-containing layer are chemically bonded to each other while adjusting the number of functional groups having siloxane bonds of the silicon compound gel, for example.
- a new three-dimensional structure is formed as a void-containing layer precursor, and pulverized products are thereafter bonded chemically (e.g., crosslinked) to each other in bonding.
- the void-containing layer of the present invention is a functional porous material
- the void-containing layer has a structure with void spaces while maintaining sufficient strength and sufficient flexibility. Therefore, according to the present invention, the void-containing layer can be easily and simply applied to various objects.
- the void-containing layer of the present invention includes pulverized products of a porous gel material as will be described below, and the pulverized products are chemically bonded to each other.
- the form of the chemical bonding (chemical bonds) between the pulverized products is not limited to particular forms. Specifically, the chemical bonds may be crosslinking bonds, for example.
- the method for chemically bonding the pulverized products to each other is as will be described in detail in, for example, the method for producing the void-containing layer to be described below.
- the crosslinking bonds are siloxane bonds, for example.
- examples of the siloxane bonds include T2, T3, and T4 bonds shown below.
- the silicone porous material of the present invention may have any one of the T2, T3, and T4 bonds, any two of them, or all three of them, for example.
- the proportions of T2 and T3 among the siloxane bonds become higher, the silicone porous material becomes more flexible, so that it is expected that the silicone porous material exhibits characteristics intrinsic to the gel.
- the film strength of the silicone porous material is deteriorated.
- silicon atoms contained in the void-containing layer of the present invention be bonded to each other through siloxane bonds, for example.
- the proportion of unbonded silicon atoms (i.e., residual silanol) among all the silicon atoms contained in the silicone porous material is less than 50%, 30% or less, or 15% or less, for example.
- the void-containing layer of the present invention has a pore structure.
- the size of each void space in the pore structure indicates, out of the diameter of the long axis and the diameter of the short axis of the void space (pore), the diameter of the long axis.
- the void space size (pore) is from 5 nm to 50 m, for example.
- the lower limit of the size is, for example, 5 nm or more, 10 nm or more, or 20 nm or more.
- the upper limit of the size is, for example, 50 nm or less, 40 nm or less, or 30 nm or less.
- the range of the size is, for example, from 5 nm to 50 nm or from 10 nm to 40 nm.
- a preferable void space size is determined depending on the use of the void-containing structure. Thus, it is necessary to adjust the void space size to a desired size according to the intended use, for example.
- the void space size can
- the void-containing layer can be observed and analyzed using a scanning electron microscopy (SEM).
- SEM scanning electron microscopy
- the void-containing layer is subjected to FIB processing (acceleration voltage: 30 kV) while being cooled, and the cross-sectional electronic image of the obtained cross-sectional sample can be obtained by FIB-SEM (product name: Helios NanoLab 600 , manufactured by FEI Company, acceleration voltage: 1 kV) at an observing magnification of 100,000 ⁇ .
- the void space size can be quantified according to the BET test. Specifically, 0.1 g of a sample (the void-containing layer of the present invention) is set in a capillary of a pore distribution/surface area measurement apparatus (product name: BELLSORP MIN, manufactured by MicrotracBEL Corp.), and dried under reduced pressure at room temperature for 24 hours to remove gas in the void-containing structure. Then, a BET plot, a BJH plot, and an adsorption isotherm are created by causing the sample to adsorb nitrogen gas, whereby the pore distribution is determined. On the basis of the thus-determined pore distribution, the void space size can be evaluated.
- a pore distribution/surface area measurement apparatus product name: BELLSORP MIN, manufactured by MicrotracBEL Corp.
- the void-containing layer of the present invention may have, for example, a pore structure (porous structure) as mentioned above, and the pore structure may be an open-cell structure in which pores are interconnected with each other, for example.
- the open-cell structure means that, for example, pores three-dimensionally communicate with each other in the void-containing layer.
- the open-cell structure means the state where void spaces inside the pore structure are interconnected with each other.
- this structure allows the bulk body to have a higher void fraction.
- closed-cell particles such as hollow silica particles are used, an open-cell structure cannot be formed.
- an open-cell structure can be formed easily for the following reason.
- Sol particles pulverized products of a porous gel material for forming a sol
- each have a dendritic structure so that the open-cell structure is formed as a result of sedimentation and deposition of the dendritic particles in a coating film (a coating film formed of a sol containing pulverized products of the porous gel material).
- the void-containing layer of the present invention form a monolith structure, which is an open-cell structure including two or more types of micropore distributions.
- the monolith structure refers to a layered structure including a structure in which nano-sized minute void spaces are present and an open-cell structure formed by aggregation of the nano-sized void spaces, for example.
- the film strength is imparted by the minute void spaces whereas a high void fraction is achieved by the presence of the void spaces forming a bulky open-cell structure.
- both film strength and a high void fraction can be attained.
- the monolith structure can be formed by, for example, controlling, at the time of pulverizing the porous gel material, the particle sizes of the pulverized products so that a desired particle size distribution can be obtained.
- the haze value indicating the transparency is not particularly limited, and the lower limit thereof is, for example, 0.1% or more, 0.2% or more, or 0.3% or more, the upper limit thereof is, for example, 10% or less, 5% or less, or 3% or less, and the range thereof is, for example, from 0.1% to 10%, from 0.2% to 5%, or from 0.3% to 3%.
- the haze value can be measured in the following manner, for example.
- a void-containing layer (the void-containing layer of the present invention) is cut into a piece with a size of 50 mm ⁇ 50 mm, and the thus-obtained cut piece is set in a haze meter (HM-150, manufactured by Murakami Color Research Laboratory) to measure the haze value.
- the haze value is calculated by the following equation.
- Haze value (%) [diffuse transmittance (%)/total light transmittance (%)] ⁇ 100(%)
- the “refractive index” of a given medium generally refers to the ratio of transmission speed of the wavefront of light in vacuum to the phase velocity of the light in the medium.
- the refractive index of the void-containing layer of the present invention is not particularly limited, and the upper limit thereof is, for example, 1.3 or less, less than 1.3, 1.25 or less, 1.2 or less, or 1.15 or less, the lower limit thereof is, for example, 1.05 or more, 1.06 or more, or 1.07 or more, and the range thereof is, for example, 1.05 or more and 1.3 or less, 1.05 or more and less than 1.3, 1.05 or more and 1.25 or less, 1.06 or more and less than 1.2, or 1.07 or more and 1.15 or less.
- the refractive index refers to the one measured at a wavelength of 550 nm, unless otherwise stated.
- the method for measuring the refractive index is not particularly limited.
- the refractive index can be measured in the following manner.
- a void-containing layer (the void-containing layer of the present invention) is formed on an acrylic film, and the obtained laminate is then cut into a piece with a size of 50 mm ⁇ 50 mm.
- the thus-obtained cut piece is attached to a surface of a glass plate (thickness: 3 mm) with a pressure-sensitive adhesive layer.
- the central portion (diameter: about 20 mm) of the back surface of the glass plate is painted entirely with black ink, thereby preparing a sample that allows no reflection at the back surface of the glass plate.
- the sample is set in an ellipsometer (VASE, manufactured by J. A. Woollam Japan), and the refractive index is measured at a wavelength of 500 nm and at an incidence angle of 50° to 80°.
- the mean value of the thus-obtained measured values is set as the refractive index.
- the thickness of the void-containing layer of the present invention is not particularly limited, and the lower limit thereof is, for example, 0.05 am or more or 0.1 ⁇ m or more, and the upper limit thereof is, for example, 1000 ⁇ m or less or 100 ⁇ m or less, and the range thereof is, for example, from 0.05 to 1000 ⁇ m or 0.1 to 100 ⁇ m.
- the form of the void-containing layer of the present invention is not particularly limited, and may be, for example, in the form of a film, a block, or the like.
- the method for producing the void-containing layer of the present invention is not particularly limited, and can be produced by, for example, the method as will be described below.
- the void-containing layer is a void-containing layer formed by chemically bonding particles to each other.
- the particle is an inorganic-organic composite particle in which an organic group is bonded to an inorganic compound, the organic group includes a R 1 group which is a linear or branched alkyl group and a R 2 group which is a group containing a carbon-carbon unsaturated bond, and the molar ratio of the R 2 group relative to the sum of the R 1 group and the R 2 group is from 1 to 30 mol %.
- the molar ratio of the R 2 group relative to the stun of the R 1 group and the R 2 group may be, for example, 30 mol % or less, 25 mol % or less, or 10 mol % or less, and may be, for example, 1 mol % or more, 1.5 mol % or more, 1.8 mol % or more, 2 mol % or more, or 2.5 mol % or more.
- the molar ratio can be obtained by comparing the intensity of the proton peak from the R 23 group and the intensity of the proton peak from the R 2 group using a solid-state NMR ( 1 H-NMR).
- the R 1 group is not particularly limited, and examples thereof include a methyl group, an ethyl group, a n-propyl group, an isopropyl group, a n-butyl group, a sec-butyl group, and a tert-butyl group.
- the R 2 group is also not particularly limited, and examples thereof include those as described above.
- a compound containing the R 1 group and the R 2 group may be used as a part or the whole of a raw material in producing the particles. Further, for example, a compound containing the R group and a compound containing the R 2 group may be used, as part or the whole of the raw material, in addition to or in place of the compound containing the R 1 group and the R 2 group.
- the compound containing the R 1 group and the R 2 group is not particularly limited, and may be, for example, a combination of methyltrimethoxysilane and vinyltrimethoxysilane.
- Methyltrimethoxysilane is a compound having a methyl group as the R 1 group and vinyltrimethoxysilane is a compound having a vinyl group as the R 2 group.
- examples of the combination of the compounds having the R group and the R 2 group include a combination of methyltrimethoxysilane and allyl trimethoxysilane, a combination of methyltrimethoxysilane and 3-(acryloxy)propyltrimethoxysilane, a combination of methyltriethoxysilane and allyltrimethoxysilane, a combination of methyltriethoxysilane and 3-(acryloxy)propyltrimethoxysilane, a combination of methyltriethoxysilane and vinyltrimethoxysilane, a combination of methyltrimethoxysilane and allyl triethoxysilane, a combination of methyltrimethoxysilane and 3-(acryloxy)propyltrieth
- the compound containing the R 1 group is not particularly limited, and examples thereof include methyltrimethoxysilane, methyltriethoxysilane, ethyltrimethoxysilane, ethyltriethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, isopropyltrimethoxysilane, and isopropyltiethoxysilane.
- the compound containing the R 2 group is not particularly limited, and examples thereof include vinyltrimethoxysilane, vinyltriethoxysilane, allyltriethoxysilane, allyltriethoxysilane, 3-(acryloxy)propyltrimethoxysilane, 3-(acryloxy)propyltriethoxysilane, methylvinyldiethoxysilane, methylvinyldiethoxysilane, vinyltriisopropoxysilane, vinyhris(2-methoxyethoxy)silane, tris(trimethylsiloxy)vinylsilane, dimethylethoxyvinylsilane, trimethoxy(7-octene-1-yl)silane, 3-[dimethoxy(methyl)silyl]propyhnethacrylate, 3-(methoxydimethylsilyl)propyl acrylate, 3-(trimethoxysilyl)propyl methacrylate, 3-(triethoxysily
- the content of the compound containing the R 1 group and the R 2 group, the compound containing the R 1 group, and the compound containing the R 2 group in the raw material is not particularly limited, and may be appropriately set so that the content of the R group and the R 2 group in the particles is suitable, for example.
- the content of the compound containing the R 2 group in the raw material is not particularly limited, and may be, for example, 30 mass % or less, 20 mass % or less, or 10 mass % or less, and may be, for example, 1 mass % or more, 1.5 mass % or more, 1.8 mass % or more, or 2 mass % or more, relative to the total mass of the compound containing the R 1 group and the R 2 group.
- a compound other than the compound containing the R 1 group and the R 2 group may be included.
- Nanoparticles, Surfaces of which being Modified with a Compound Having a Surface Orientation [4. Nanoparticles, Surfaces of which being Modified with a Compound Having a Surface Orientation]
- the void-containing layer of the present invention may include a compound having a surface orientation, as described above.
- the compound having the surface orientation may contain, for example, a fluoroalkyl group having 5 to 17 or 5 to 10 fluorine atoms.
- the fluoroalkyl group may be an alkyl group in which only a part of hydrogen is substituted with fluorine, or may be an alkyl group (perfluoroalkyl group) in which all hydrogen is substituted with fluorine.
- the fluoroalkyl group may be, for example, a fluoroalkyl group including a perfluoroalkyl group in a part of its structure.
- the alkyl group in the fluoroalkyl group is not particularly limited, and, may be a linear or branched alkyl group having 2 to 10 carbon atoms, for example.
- the compound having the surface orientation is an alkoxysilane derivative
- the alkoxysilane derivative may contain a fluoroalkyl group having to 17 or 5 to 10 fluorine atoms.
- the fluoroalkyl group may be an alkyl group in which only a part of hydrogen is substituted with fluorine, or may be an alkyl group (perfluoroalkyl group) in which all hydrogen is substituted with fluorine.
- the fluoroalkyl group may be, for example, a fluoroalkyl group including a perfluoroalkyl group in a part of its structure.
- the alkyl group in the fluoroalkyl group is not particularly limited, and, may be a linear or branched alkyl group having 2 to 10 carbon atoms, for example, as described above.
- the alkoxysilane derivative may be, for example, a monoalkoxysilane, a dialkoxysilane, a trialkoxysilane, or a tetraalkoxysilane derivative. More specifically, the alkoxysilane derivative may be a derivative in which one or more alkyl groups among the alkoxy groups per molecule of the alkoxysilane is substituted with the fluoroalkyl group.
- the alkyl group in the fluoroalkyl group is, for example, as described above.
- the alkoxy group in which the alkyl group is not substituted with the fluoroalkyl group is not particularly limited, and is, for example, a linear or branched alkyl group having 1 to 4 carbon atoms, and may be, for example, a methoxy group or the like.
- alkoxysilane derivative examples include trimethoxy(1H,1H,2H,2H-nonafluorohexyl)silane, trimethoxy(1H,1H,2H,2H-heptadecafluorodecyl)silane, and triethoxy[5,5,6,6,7,7,7-heptafluoro-4,4-bis(trifluoromethyl)heptyl]silane.
- only one type of the alkoxysilane derivative may be used alone or two or more of the alkoxysilane derivatives may be used in combination.
- a surfactant having a perfluoro group and further having a hydrophilic site such as a hydroxyl group or a sodium sulfonate group and a hydrophobic site in one structure at a terminal thereof can be given.
- the nanoparticle is not particularly limited, and may be, for example, a silica particle, and more specifically, for example, a pulverized product of a silicon compound gel as described below, or the like.
- the particle diameter of the nanoparticle is not particularly limited, and, for example, the volume average particle diameter may be 1 nm or more, 2 nm or more, 3 nm or more, or 5 nm or more, and 1000 nm or less, 500 nm or less, 200 nm or less, or 50 nm or less.
- the volume average particle diameter can be measured using a particle size distribution analyzer based on dynamic light scattering, laser diffraction, or the like, or using an electron microscope such as a scanning electron microscope (SEM) or a transmission electron microscope (TEM), for example.
- SEM scanning electron microscope
- TEM transmission electron microscope
- the method of modifying the nanoparticles with the compound having the surface orientation is not particularly limited, and, for example, a known method or the like can be appropriately used. More specifically, for example, the nanoparticles and the compound having the surface orientation may be heated and reacted in a liquid.
- the medium (dispersion medium) in the liquid is not particularly limited, and may be, for example, water and alcohol, and only one type of the medium may be used alone or two or more types of the media may be used in combination.
- the alcohol examples include IPA (isopropyl alcohol), IBA (isobutyl alcohol), ethanol, and methanol, and may include solvents other than the above-described alcohols such as MIBK (methyl isobutyl ketone) and MEK (methyl ethyl ketone).
- the reaction temperature and the reaction time of the reaction are not particularly limited, and can be appropriately set.
- the pressure-sensitive adhesive/adhesive layer is not particularly limited, and can be formed using, for example, a pressure-sensitive adhesive/adhesive coating solution (hereinafter sometimes referred to as the “pressure-sensitive adhesive/adhesive coating solution of the present invention”) containing a (meth)acrylic polymer, a monomer having one or two reactive double bonds per molecule, an isocyanate-based crosslinking agent, and an organic peroxide, as described above.
- a pressure-sensitive adhesive/adhesive coating solution hereinafter sometimes referred to as the “pressure-sensitive adhesive/adhesive coating solution of the present invention” containing a (meth)acrylic polymer, a monomer having one or two reactive double bonds per molecule, an isocyanate-based crosslinking agent, and an organic peroxide, as described above.
- the pressure-sensitive adhesive/adhesive coating solution of the present invention can be produced, for example, by a production method including mixing the (meth)acrylic polymer, a monomer having one or two reactive double bonds per molecule, the isocyanate-based crosslinking agent, and the organic peroxide.
- the “pressure-sensitive adhesive” and the “adhesive” are not always clearly distinguishable from each other as described below.
- the “pressure-sensitive adhesive/adhesive” shall include both of the “pressure-sensitive adhesive” and the “adhesive”, unless otherwise stated.
- the pressure-sensitive adhesive/adhesive coating solution of the present invention includes a (meth)acrylic polymer, a monomer having one or two reactive double bonds per molecule, an isocyanate-based crosslinking agent, and an organic peroxide.
- the pressure-sensitive adhesive/adhesive coating solution of the present invention is not particularly limited, and is exemplified as follows, for example.
- the (meth)acrylic polymer includes, as a monomer component, 3 to 10 wt % of a heterocycle-containing acrylic monomer and a polymerizable functional group, and includes 0.5 to 5 wt % of (meth)acrylic acid, 0.05 to 2 wt % of hydroxyalkyl (meth)acrylate, and 83 to 96.45 wt % of alkyl (meth)acrylate, and this (meth)acrylic polymer is used as a base polymer.
- heterocycle-containing acrylic monomer for example, one having a polymerizable functional group and having a heterocyclic ring can be used without any particular limitation.
- the polymerizable functional group include a (meth)acryloyl group and a vinyl ether group. Of these, the (meth)acryloyl group is preferred.
- heterocycle include morpholine rings, piperidine rings, pyrrolidine rings, and piperazine rings.
- the heterocycle-containing acrylic monomer include N-acryloylmorpholine, N-acryloylpiperidine, N-methacryloylpiperidine, and N-acryloylpyrrolidine. Among these, N-acryloylmorpholine is preferable.
- the heterocycle-containing acrylic monomer can improve the durability of any of heat resistance and moisture resistance in the case of thinning the pressure-sensitive adhesive layer. In the following description, N-acryloylmorpholine is sometimes referred to as “ACMO”.
- the heterocycle-containing acrylic monomer is preferable from the viewpoint of improving the pressure-sensitive adhesive force of the pressure-sensitive adhesive layer to the optical film.
- the heterocycle-containing acrylic monomer is used, for example, in a proportion of 3 to 10 wt % relative to the total amount of monomer components forming the (meth)acrylic polymer.
- the proportion of the heterocycle-containing acrylic monomer may be, for example, 4 to 9.5 wt % or 6 to 9 wt %.
- the proportion of the heterocycle-containing acrylic monomer is preferably not less than the above range from the viewpoints of the heat resistance and the moisture resistance in the case of thinning the pressure-sensitive adhesive layer.
- the proportion of the heterocycle-containing acrylic monomer is preferably not more than the above range from the viewpoint of the moisture resistance in the case of thinning the pressure-sensitive adhesive layer.
- the proportion of the heterocycle-containing acrylic monomer is preferably not more than the above range from the viewpoint of improving the attaching property of the pressure-sensitive adhesive layer. In addition, the proportion of the heterocycle-containing acrylic monomer is preferably not more than the above range from the viewpoint of the pressure-sensitive adhesive force.
- the (Meth)Acrylic Acid is Preferably Acrylic Acid.
- the (meth)acrylic acid is used, for example, in a proportion of 0.5 to 5 wt % relative to the total amount of monomer components forming the (meth)acrylic polymer.
- the proportion of the (meth)acrylic acid may be, for example, 1 to 4.5 wt % or 1.5 to 4 wt %.
- the proportion of the (meth)acrylic acid is preferably not less than the above range from the viewpoint of heat resistance in the case of thinning the pressure-sensitive adhesive layer (pressure-sensitive adhesive/adhesive layer).
- the proportion of the (meth)acrylic acid is preferably not more than the above range from the viewpoints of the heat resistance and the moisture resistance in the case of thinning the pressure-sensitive adhesive layer.
- the proportion of the (meth)acrylic acid is preferably not more than the above range from the viewpoint of the pressure-sensitive adhesive force.
- hydroxyalkyl(meth)acrylate for example, one having a polymerizable functional group and having a hydroxyl group can be used without any particular limitation.
- the hydroxyalkyl (meth)acrylate include hydroxyalkyl(meth)acrylates such as 2-hydroxyethyl (meth)acrylate, 2-hydroxybutyl (meth)acrylate, 3-hydroxypropyl (meth)acrylate, 4-hydroxybutyl (meth)acrylate, 6-hydroxyhexyl (meth)acrylate, 8-hydroxyoctyl (meth)acrylate, 10-hydroxydecyl (meth)acrylate, and 12-hydroxylauryl (meth)acrylate.
- hydroxyalkyl(meth)acrylates such as 2-hydroxyethyl (meth)acrylate, 2-hydroxybutyl (meth)acrylate, 3-hydroxypropyl (meth)acrylate, 4-hydroxybutyl (meth)acrylate, 6-hydroxyhexyl (meth)acrylate, 8-hydroxyoct
- the hydroxyalkyl (meth)acrylate is used, for example, in proportion of 0.05 to 2 wt % relative to the total amount of monomer components forming the (meth)acrylic polymer.
- the proportion of the hydroxyalkyl (meth)acrylate may be, for example, 0.075 to 1.5 wt % or 0.1 to 1 wt %.
- the proportion of the hydroxyalkyl (meth)acrylate is preferably not less than the above range from the viewpoint of the heat resistance in the case of thinning the pressure-sensitive adhesive layer (pressure-sensitive adhesive/adhesive layer).
- the proportion of the hydroxyalkyl (meth)acrylate is preferably not more than the above range from the viewpoints of the heat resistance and the moisture resistance in the case of thinning the pressure-sensitive adhesive layer. In addition, the proportion of the hydroxyalkyl (meth)acrylate is preferably not more than the above range from the viewpoint of the pressure-sensitive adhesive force.
- the alkyl group of the alkyl (meth)acrylate may have an average carbon number of about 1 to 12.
- (meth)acrylate refers to acrylate and/or methacrylate, and has the same meaning as (meth) of the present invention.
- alkyl (meth)acrylate examples include methyl (meth)acrylate, ethyl (meth)acrylate, n-butyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, isooctyl (meth)acrylate, isononyl (meth)acrylate, and lauryl (meth)acrylate, and one of them may be used alone or two or more of them may be used in combination.
- alkyl (meth)acrylate having 1 to 9 carbon atoms in the alkyl group is preferable.
- the alkyl (meth)acrylate is used, for example, in a proportion of 83 to 96.45 wt % relative to the total amount of the monomer components forming the (meth)acrylic polymer.
- the alkyl (meth)acrylate is usually the remainder other than the heterocycle-containing acrylic monomer, (meth)acrylic acid, and hydroxyalkyl (meth)acrylate.
- any monomer other than those mentioned above may be used in a range of 10% or less of the total amount of the monomers, as long as the object of the present invention is not impaired.
- Examples of such a monomer include acid anhydride group-containing monomers such as maleic anhydride and itaconic anhydride: a caprolactone adduct of acrylic acid, sulfonic acid group-containing monomers such as styrenesulfonic acid, allylsulfonic acid, 2-(meth)acrylamido-2-methylpropanesulfonic acid, (meth)acrylamidopropanesulfonic acid, sulfopropyl (meth)acrylate, and (meth)acryloyloxynaphthalenesulfonic acid; and a phosphate group-containing monomer such as 2-hydroxyethyl acryloylylphosphate.
- acid anhydride group-containing monomers such as maleic anhydride and itaconic anhydride: a caprolactone adduct of acrylic acid, sulfonic acid group-containing monomers such as styrenesulfonic acid, allylsulfonic acid,
- nitrogen-containing vinyl monomers can be used, and examples thereof include maleimide, N-cyclohexylmaleimide, N-phenylmaleimide; (N-substituted) amide monomers such as (meth)acrylamide, N,N-dimethyl (meth)acrylamide, N,N-diethyl (meth)acrylamide, N-hexyl (meth)acrylamide, N-methyl (meth)acrylamide, N-butyl (meth)acrylamide,N-butyl (meth)acrylamide, N-methylol (meth)acrylamide, and N-methylolpropane (meth)acrylamide; alkylaminoalkyl (meth)acrylate monomers such as (meth)aminoethyl acrylate, aminopropyl (meth)acrylate, N,N-dimethylaminoethyl (meth)acrylate, t-butylaminoethyl (meth)acrylate, and 3-(
- Vinyl monomers such as vinyl acetate, vinyl propionate, N-vinylpyrrolidone, methylvinylpyrrolidone, vinylpyridine, vinylpiperidone, vinylpyrimidine, vinylpiperazine, vinylpyrazine, vinylpyrrole, vinylimidazole, vinyloxazole, vinylmorpholine, N-vinylcarboxylic acid amides, styrene, ⁇ -methylstyrene, and N-vinylcaprolactam; cyanoacrylate monomers such as acrylonitrile and methacrylonitrile: epoxy group-containing acrylic monomers such as glycidyl (meth)acrylate: glycol-based acrylic ester monomers such as polyethylene glycol (meth)acrylate, polypropylene glycol (meth)acrylate, methoxyethylene glycol (meth)acrylate, and methoxypolypropylene glycol (meth)acrylate; and acrylic acid ester monomers such as tetrahydrofurfury
- examples of the copolymerizable monomer other than the above include silane-based monomers containing silicon atoms.
- examples of the silane-based monomer include 3-acryloxypropyltriethoxysilane, vinyltrimethoxysilane, vinyltriethoxysilane, 4-vinylbutyltrimethoxysilane, 4-vinylbutyltriethoxysilane, 8-vinyloctyltrimethoxysilane, 8-vinyloctyltriethoxysilane, 10-methacryloyloxydecyltrimethoxysilane, 10-acryloyloxydecyltrimethoxysilane, 10-methacryloyloxydecyltriethoxysilane, and 10-acryloyloxydecyltriethoxysilane.
- the (meth)acrylic polymer used in the present invention may have, for example, a weight average molecular weight of 1.5 million to 2.8 million.
- the weight average molecular weight may be, for example, 1.7 million to 2.7 million or 2 million to 2.5 million.
- the weight average molecular weight is preferably not smaller than the above range from the viewpoints of the heat resistance and the moisture resistance in the case of thinning the pressure-sensitive adhesive layer.
- the weight average molecular weight is preferably not larger than the above range from the viewpoints of the durability, the attaching property, and the pressure-sensitive adhesive force in the case of thinning the pressure-sensitive adhesive layer.
- the weight average molecular weight is, for example, a value measured by gel permeation chromatography (GPC) and calculated in terms of polystyrene.
- the method for producing such a (meth)acrylic polymer is not particularly limited, and known production methods such as solution polymerization, bulk polymerization, emulsion polymerization, and various radical polymerization can be appropriately selected. Further, the (meth)acrylic polymer obtained may be any of a random copolymer, a block copolymer, a grafl copolymer, or the like.
- solution polymerization for example, ethyl acetate or toluene is used as a polymerization solvent.
- the reaction is carried out under an inert gas stream such as nitrogen by adding a polymerization initiator, for example, at about 50 to 70° C. for about 5 to 30 hours.
- the polymerization initiator, the chain transfer agent, the emulsifier, and the like used in the radical polymerization are not particularly limited, and can be appropriately selected and used.
- the weight average molecular weight of the (meth)acrylic polymer can be controlled according to the amount of the polymerization initiator, the chain transfer agent, or the like, and the reaction conditions, and the amount of the (meth)acrylic polymer to be used is appropriately adjusted according to the types of the polymerization initiator, the chain transfer agent, and reaction conditions.
- polymerization initiator examples include, but not limited to, azo-based initiators such as 2,2′-azobisisobutyronitrile, 2,2′-azobis(2-amidinopropane)dihydrochloride, 2,2′-azobis[2-(5-methyl-2-imidazolne-2-yl)propane] dihydrochloride, 22′-azobis(2-methylpropionamidine)disulfate, 2,2′-azobis(N,N′-dimethyleneisobutylamidine), and 2,2′-azobis[N-(2-carboxyethyl)-2-methylpropionamidine]hydrate (VA-057, manufactured by Wako Pure Chemical Industries, Ltd.); persulfates such as potassium persulfate and ammonium persulfate; peroxide-based initiators such as di(2-ethylhexyl)peroxydicarbonate, di(4-t-butylcyclohexyl)peroxydicarbon
- One of the polymerization initiators may be used alone or two or more of them may be mixed to use.
- the total content of the polymerization initiator may be, for example, about 0.005 to 1 parts by weight or about 0.02 to 0.5 parts by weight relative to 100 parts by weight of the monomer.
- the amount of the polymerization initiator used may be, for example, about 0.06 to 0.2 parts by weight or about 0.08 to 0.175 parts by weight relative to 100 parts by weight of the total amount of the monomer components.
- chain transfer agent examples include lauryl mercaptan, glycidyl mercaptan, mercaptoacetic acid, 2-mercaptoethanol, thioglycolic acid, 2-ethylhexyl thioglycolate, and 2,3-dimercapto-1-propanol.
- One of the chain transfer agents may be used alone or two or more of them may be mixed to use.
- the total content of the chain transfer agent is, for example, about 0.1 parts by weight or less relative to 100 parts by weight of the total amount of the monomer components.
- Examples of the emulsifier used in the emulsion polymerization include anionic emulsifiers such as sodium lauryl sulfate, ammonium lauryl sulfate, sodium dodecylbenzene sulfonate, ammonium polyoxyethylene alkyl ether sulfate, and sodium polyoxyethylene alkyl phenyl ether sulfate; and nonionic emulsifiers such as polyoxyethylene alkyl ether, polyoxyethylene alkyl phenyl ether, polyoxyethylene fatty acid ester, and polyoxyethylene-polyoxypropylene block polymer.
- anionic emulsifiers such as sodium lauryl sulfate, ammonium lauryl sulfate, sodium dodecylbenzene sulfonate, ammonium polyoxyethylene alkyl ether sulfate, and sodium polyoxyethylene alkyl phenyl ether sulfate
- a radically polymerizable functional group such as a propenyl group or an allyl ether group
- a reactive emulsifier examples include Akuaron HS- 10 , HS- 20 , KH- 10 , BC- 05 , BC- 10 , and BC- 20 (all of which are manufactured by DKS Co., Ltd.) and ADEKA REASOAP SE10N (manufactured by ADEKA CORPORATION). Since the reactive emulsifier is incorporated into the polymer chain after the polymerization, the water resistance is improved, which is preferable.
- the amount of the emulsifier to be used is preferably 0.3 to 5 parts by weight relative to 100 parts by weight of the total amount of the monomer components, and more preferably 0.5 to 1 parts by weight relative to 100 parts by weight of the total amount of the monomer components from the viewpoints of the polymerization stability and the mechanical stability.
- the content of the (meth)acrylic polymer in the pressure-sensitive adhesive/adhesive coating solution of the present invention is not particularly limited, and may be, for example, 3 mass % or more or 5 mass % or more, and may be, for example, 30 mass % or less, 20 mass % or less, or 10 mass % or less, relative to the total mass of the pressure-sensitive adhesive/adhesive coating solution of the present invention.
- the pressure-sensitive adhesive/adhesive coating solution of the present invention includes a monomer having one or two reactive double bonds per molecule.
- the monomer having one or two reactive double bonds per molecule is not particularly limited, and examples thereof include acrylic monomers, methacrylic monomers, vinyl-based monomers, and allyl-based monomers, and acrylic monomers are more preferable from the viewpoint of the reaction rate of the graft reaction.
- the acrylic monomer is not particularly limited, and may be, for example, the same as the monomer exemplified as the monomer component of the (meth)acrylic polymer.
- the structure of the side chain is not particularly limited, and a heterocycle-containing monomer is preferable from the viewpoint of achieving a high elastic modulus within a proper range and a reduction in a semi-polymer amount at the same time.
- the content of the monomer having one or two reactive double bonds per molecule in the pressure-sensitive adhesive/adhesive coating solution of the present invention is not particularly limited, and may be, for example, 0.1 mass % or more, 0.5 mass % or more, or 1 mass % or more, and may be, for example, 30 mass % or less, 20 mass % or less, or 10 mass % or less relative to the total mass of the (meth)acrylic polymer.
- the pressure-sensitive adhesive/adhesive coating solution includes an isocyanate-based crosslinking agent.
- the isocyanate-based crosslinking agent is not particularly limited, and examples thereof include aromatic isocyanates such as tolylene diisocyanate and xylene diisocyanate; alicyclic isocyanates such as isophorone diisocyanate: and aliphatic isocyanates such as hexamethylene diisocyanate.
- isocyanate-based crosslinking agent examples include lower aliphatic polyisocyanates such as butylenediisocyanate and hexamethylene diisocyanate; alicyclic isocyanates such as cyclopentylene diisocyanate, cyclohexylene diisocyanate, and isophorone diisocyanate; aromatic diisocyanates such as 2,4-tolylene diisocyanate.
- lower aliphatic polyisocyanates such as butylenediisocyanate and hexamethylene diisocyanate
- alicyclic isocyanates such as cyclopentylene diisocyanate, cyclohexylene diisocyanate, and isophorone diisocyanate
- aromatic diisocyanates such as 2,4-tolylene diisocyanate.
- isocyanate adducts such as a trimethylolpropaneltolylene diisocyanate trimer adduct (product name: Coronate@ L, manufactured by Nippon Polyurethane Industry Co., Ltd.), a trimethylolpropane/hexamethylene diisocyanate trimer adduct (product name: Coronate@ HL, manufactured by Nippon Polyurethane Industry Co., Ltd.), and isocyanurate form of hexamethylene diisocyanate (product name: Coronate@ HX, manufactured by Nippon Polyurethane Industry Co., Ltd.); polyether polyisocyanate: polyester polyisocyanate; and adducts of these with various polyols, and polyisocyanates multifunctionalized with isocyanurate bonds, biuret bonds, allophanate;
- the total content of the isocyanate-based crosslinking agent may be, for example, 0.02 to 2 parts by mass, 0.04 to 1.5 parts by mass, or 0.05 to 1 part by mass relative to 100 parts by mass of the (meth)acrylic polymer.
- the content of the isocyanate-based crosslinking agent is preferably 0.02 parts by mass or more from the viewpoint of cohesive force, while it is preferably 2 parts by mass or less from the viewpoint of suppressing or preventing a decrease in adhesive force due to excessive crosslinking formation.
- the pressure-sensitive adhesive/adhesive coating solution of the present invention may or may not further contain a crosslinking agent other than the isocyanate-based crosslinking agent.
- a crosslinking agent include an organic crosslinking agent and a polyfunctional metal chelate.
- the organic crosslinking agent include an epoxy-based crosslinking agent and an imine-based crosslinking agent.
- the organic crosslinking agent is preferably an isocyanate-based crosslinking agent.
- a polyfunctional metal chelate is one in which a polyvalent metal is covalently or coordinately bonded to an organic compound.
- the polyvalent metallic atom include Al, Cr, Zr, Co, Cu, Fe, Ni. V, Zn, In, Ca, Mg, Mn.
- the atom in the organic compound to be covalently or coordinately bonded may be, for example, an oxygen atom, and examples of the organic compound include an alkyl ester, an alcohol compound, a carboxylic acid compound, an ether compound, and a ketone compound.
- the pressure-sensitive adhesive/adhesive coating solution includes an organic peroxide.
- the organic peroxide is not particularly limited, and examples thereof include di(2-ethylhexyl)peroxydicarbonate, di(4-t-butylcyclohexyl)peroxydicarbonate, di-sec-butyl peroxydicarbonate, t-butyl peroxyneodecanoate, t-hexyl peroxypivalate, t-butyl peroxypivalate, dilauroyl peroxide, di-n-octanoyl peroxide, 1,1,3,3-tetramethylbutyl peroxy-2-ethylhexanoate, di(4-methylbenzoyl)peroxide, dibenzoyl peroxide, t-butyl peroxyisobutyrate, 1,1-di(t-hexylperoxy)cyclohexane, and t-butyl hydroperoxid
- the content of the organic peroxide in the pressure-sensitive adhesive/adhesive coating solution of the present invention is not particularly limited, and may be, for example, 0.1 mass % or more, 0.5 mass % or more, 1 mass % or more, 2 mass % or more, or 2.5 mass % or more, and may be, for example, 20 mass % or less, 10 mass % or less, 8 mass % or less, or 6 mass % or less relative to the total mass of the (meth)acrylic polymer.
- the pressure-sensitive adhesive/adhesive coating solution of the present invention may further contain a solvent or the like.
- the solvent is not particularly limited, and for example, a polymerization solvent used in solution polymerization in the production of the (meth)acrylic polymer may be used as it is.
- the pressure-sensitive adhesive/adhesive coating solution of the present invention a tackifier, a plasticizer, a filler containing glass fibers, glass beads, metal powders, other inorganic powders, and the like may be used as appropriate, and various additives may be used as appropriate without departing from the scope of the present invention.
- the pressure-sensitive adhesive layer may contain fine particles and exhibit light diffusibility.
- the pressure-sensitive adhesive coating solution of the present invention when used, it is easy to achieve both the pressure-sensitive adhesive force or the adhesive force and the resistance to penetration of the pressure-sensitive adhesive or the adhesive into the voids.
- the reason (mechanism) is conceivable as follows, for example. For example, by using a particular pressure-sensitive adhesive/adhesive to form a pressure-sensitive adhesive/adhesive layer, both the pressure-sensitive adhesive force or the adhesive force and the resistance to penetration of the pressure-sensitive adhesive or the adhesive into the voids can be achieved.
- an intermediate layer is formed by uniting a part of the void-containing layer and a part of the pressure-sensitive adhesive/adhesive layer.
- the intermediate layer serves as a stopper, which makes it possible to suppress a reduction in the void fraction caused by filling the voids of the void-containing layer with the pressure-sensitive adhesive.
- a (meth)acrylic polymer which is a main component, can be crosslinked with an isocyanate-based crosslinking agent by being heated.
- the pressure-sensitive adhesive/adhesive coating solution of the present invention it is preferable that one or two reactive double bonds be present per molecule for efficiently crosslinking the main chains during the grafting reaction.
- (meth)acrylic means at least one of acrylic and methacrylic.
- (meth)acrylic acid means at least one of acrylic acid and methacrylic acid.
- (meth)acrylic acid ester means at least one of an acrylic acid ester and a methacrylic acid ester, and “methyl(meth)acrylate” means at least one of methyl acrylate and methyl methacrylate.
- (meth)acrylic polymer refers to a polymer having a structure obtained by polymerizing a component containing at least one element selected from the group consisting of acrylic acid, methacrylic acid, acrylic acid ester, methacrylic acid ester, monomer having an acryloyl group, and monomer having a methacryloyl group, for example.
- the component may or may not contain at least one substance other than at least one element selected from the group consisting of acrylic acid, methacrylic acid, acrylic acid ester, methacrylic acid ester, monomer having an acryloyl group, and monomer having a methacryloyl group.
- acrylic monomer refers to a monomer including at least one element selected from the group consisting of acrylic acid, methacrylic acid, acrylic acid ester, methacrylic acid ester, a monomer having an acryloyl group, and a monomer having a methacryloyl group.
- the “isocyanate-based crosslinking agent” refers to, for example, a crosslinking agent having an isocyanate group (isocyanato group) in a molecule.
- the number of isocyanate groups (isocyanato groups) per molecule of the isocyanate-based crosslinking agent is not particularly limited, and is preferably 2 or more, and, for example, 2 or 3 or 4, and the upper limit value is not particularly limited, and is, for example, or less.
- the void-containing layer production method and laminate production method of the present invention are not particularly limited, and can be performed by, for example, the production method described below. The following description, however, is illustrative and does not limit the invention in any way. In the following description, the void-containing layer production method of the present invention may be referred to as a “void-containing layer production method of the present invention”.
- the void-containing layer production method of the present invention is described below with reference to examples.
- the void-containing layer production method of the present invention is not limited in any way by the following description.
- the void-containing layer of the present invention may be formed, for example, of a silicon compound.
- the void-containing layer of the present invention may be, for example, a void-containing layer formed by chemically bonding microporous particles.
- the microporous particles may be gel pulverized products.
- the void-containing layer of the present invention may have, for example, the R 1 group and the R 2 group in addition to the skeleton formed by chemical bonding among the microporous particles.
- a part or the whole of the silicon compound may be a compound containing the R 1 group and the R 2 group.
- a compound containing the R 1 group and a compound containing the R 2 group may be used as a part or the whole of the silicon compound in addition to or in place of the compound containing the R 1 group and the R 2 group.
- the compound containing the R 1 group and the R 2 group, the compound containing the R 1 group, and the compound containing the R 2 group are not particularly limited, and are, for example, as described above.
- the content of the compound containing the R group and the R 2 group, the compound containing the R 1 group, and the compound containing the R group in the silicon compound is not particularly limited, and may be appropriately set so that the content of the R 1 group and the R 2 group in the particles is suitable, for example.
- the silicon compound may have 3 to 20 mass % of vinyltrimethoxysilane as the compound containing the R 2 group.
- the remainder of the silicon compound (other than vinyltrimethoxysilane) is not particularly limited, and may be, for example, methyltrimethoxysilane (MTMS).
- the content of the compound containing the R 1 group in the silicon compound is not particularly limited, and may be, for example, 99 mass % or less, 98.5 mass % or less, or 98 mass % or less, and may be, for example, 50 mass % or more, 60 mass % or more, or 70 mass % or more relative to the total mass of the silicon compound.
- the content of the compound containing the R 2 group in the silicon compound is not particularly limited, and may be, for example, 50 mass % or less, 40 mass % or less, or 30 mass % or less, and may be, for example, 1 mass % or more, 1.5 mass % or more, 1.8 mass % or more, or 2 mass % or more relative to the total mass of the silicon compound.
- the void-containing layer of the present invention may include, in addition to a skeleton formed by chemical bonding between the microporous particles, nanoparticles, surfaces of which being modified with the compound having the surface orientation, for example.
- pulverizing a gel of pulverizing the porous gel material may be performed by one stage, however, is preferably performed by multiple stages.
- the number of the pulverization stages is not limited to particular numbers and may be, for example, two, three, or more.
- the shape of the “particle” is not limited to particular shapes and may be, for example, a spherical shape or non-spherical shape.
- the particle of the gel pulverized product may be, for example, a sol-gel beaded particle, a nanoparticle (hollow nanosilica/nanoballoon particle), or a nanofiber.
- the gel is preferably a porous gel
- the gel pulverized product is preferably a porous gel pulverized product.
- the present invention is by no means limited thereto.
- the gel pulverized product may be in at least one form selected from the group consisting of particulate forms, fibrous forms, and plate-like forms, for example.
- the particulate structural unit and the plate-like structural unit may be made of an inorganic substance, for example.
- the constituent element(s) of the particulate structural units includes at least one element selected from the group consisting of Si, Mg, Al Ti, Zn, and Zr, for example.
- the particulate structure (structural unit) may be a solid particle or a hollow particle, and specific examples thereof include silicone particles, silicone particles having micropores, silica hollow nanoparticles, and silica hollow nanoballoons.
- the fibrous structural unit may be, for example, a nanofiber with a nano-sized diameter, and specific examples thereof include cellulose nanofibers and alumina nanofibers.
- the plate-like structural unit may be, for example, nanoclay, and specific examples thereof include nano-sized bentonite (e.g., Kunipia F (product name)).
- the fibrous structural unit is not particularly limited, and may be, for example, at least one fibrous substance selected from the group consisting of carbon nanofibers, cellulose nanofibers, alumina nanofibers, chitin nanofibers, chitosan nanofibers, polymer nanofibers, glass nanofibers, and silica nanofibers.
- the pulverizing a gel (e.g., multiple pulverization stages including the first pulverization stage and the second pulverization stage) may be performed in “another solvent”, for example.
- another solvent is described in detail below.
- the “solvent” e.g., a gel production solvent, a void-containing layer production solvent, a replacement solvent
- the “solvent” may not dissolve a gel or pulverized products thereof, and the gel or the pulverized products thereof may be dispersed or precipitated in the solvent.
- the volume average particle diameter of the gel after the first pulverization stage may be, for example, from 0.5 to 100 ⁇ m, from 1 to 100 ⁇ m, from 1 to 50 ⁇ m, from 2 to 20 ⁇ m, or from 3 to 10 ⁇ m.
- the volume average particle diameter of the gel after the second pulverization stage may be, for example, from 10 to 1000 nm, from 100 to 500 nm, or from 200 to 300 nm.
- the volume average particle diameter indicates a variation in particle size of the pulverized products in the solution containing the gel (gel-containing solution).
- the volume average particle diameter can be measured using a particle size distribution analyzer based on dynamic light scattering, laser diffraction, or the like, or using an electron microscope such as a scanning electron microscope (SEM) or a transmission electron microscope (TEM), for example.
- SEM scanning electron microscope
- TEM transmission electron microscope
- the void-containing layer production method of the present invention further includes, for example, gelling a massive porous material in a solvent to obtain a gel.
- the gel obtained by the gelling may be used in the first pulverization stage among the pulverization stages (e.g., the first pulverization stage), for example.
- the void-containing layer production method of the present invention further includes, for example, aging the gel in a solvent.
- the gel after the aging may be used in the first pulverization stage among the pulverization stages (e.g., the first pulverization stage), for example.
- the void-containing layer production method of the present invention further includes replacing the solvent with “another solvent” after the gelling, for example.
- the gel in “another solvent” may be used in the first pulverization stage among the pulverization stages (e.g., the first pulverization stage), for example.
- the pulverization of the porous material is controlled while measuring the shear viscosity of the solution in at least one of the pulverization stages among multiple stages (e.g., at least one of the first pulverization stage and the second pulverization stage) in the void-containing layer production method of the present invention.
- At least one of the pulverization stages among multiple stages (e.g., at least one of the first pulverization stage and the second pulverization stage) in the void-containing layer production method of the present invention is performed by, for example, high pressure media-less pulverization.
- the gel is, for example, a gel of a silicon compound at least containing three or less functional groups having saturated bonds.
- the gel pulverized product-containing solution obtained by processes including the pulverizing a gel may be referred to as the “gel pulverized product-containing solution of the present invention”.
- the void-containing layer of the present invention as a functional porous material can be formed by forming a coating film of the solution and chemically bonding the pulverized products in the coating film.
- the void-containing layer of the present invention can be applied to various objects. Therefore, the gel pulverized product-containing solution of the present invention and the production method of the same are useful, for example, in the production of the void-containing layer of the present invention.
- the gel pulverized product-containing solution of the present invention has, for example, significantly excellent uniformity, for example, when the void-containing layer of the present invention is applied to an optical member, the appearance of the member can be improved.
- the gel pulverized product-containing solution may be, for example, a gel pulverized product-containing solution for obtaining a layer (void-containing layer) having a high void fraction by applying (coating) the gel pulverized product-containing solution onto a base and then drying the coated gel pulverized product-containing solution.
- the gel pulverized product-containing solution of the present invention may be, for example, a gel pulverized product-containing solution for obtaining a porous material (a bulk body having a large thickness or a massive bulk body) having a high void fraction.
- the bulk body can be obtained, for example, by performing bulk film formation using the gel pulverized product-containing solution.
- the void-containing layer of the present invention having a high void fraction can be produced by a production method including producing the gel pulverized product-containing solution of the present invention, adding nanoparticles, surfaces of which being modified with the compound having the surface orientation, to the gel pulverized product-containing solution, coating the gel pulverized product-containing solution onto a base to form a coating film, and drying the coating film.
- a laminated film in the form of a roll can be produced by a production method including the producing the gel pulverized product-containing solution of the present invention, feeding the rolled resin film, coating the gel pulverized product-containing solution onto the fed resin film to form a coating film, drying the coating film, and, after the drying, winding up the laminated film in which the void-containing layer of the present invention is formed on the resin film.
- the gel pulverized product-containing solution of the present invention contains, for example, gel pulverized products pulverized by the pulverizing a gel (e.g., the first pulverization stage and the second pulverization stage) and the other solvent(s).
- the void-containing layer production method of the present invention may include, for example, as described above, multiple pulverization stages of the pulverizing a gel (e.g., porous gel material), which may include, for example, the first pulverization stage and the second pulverization stage.
- a gel e.g., porous gel material
- the present invention will be described below with reference to examples in which the gel pulverized product-containing solution production method of the present invention includes the first pulverization stage and the second pulverization stage.
- the following description is made mainly for the case where the gel is a porous material (porous gel material).
- the present invention is by no means limited thereto, and the description of the case where the gel is a porous material (porous gel material) can be applied in an analogical manner to other cases.
- the multiple pulverization stages (e.g., the first pulverization stage and the second pulverization stage) in the void-containing layer production method of the present invention may be collectively also referred to as the “pulverizing a gel”.
- the gel pulverized product-containing solution of the present invention can be used in the production of a functional porous material that exhibits the same function as an air layer (e.g., a low refractive index) as described below.
- the functional porous material may be, for example, the void-containing layer of the present invention.
- the gel pulverized product-containing solution obtained by the production method of the present invention contains pulverized products of the porous gel material, the three-dimensional structure of the non-pulverized porous gel material in the pulverized products is destroyed, whereby a new three-dimensional structure different from that of the non-pulverized porous gel material can be formed in the pulverized products.
- a coating film (functional porous material precursor) formed using the gel pulverized product-containing solution becomes a layer having a new pore structure (new void-containing structure) that cannot be obtained in a layer formed using the non-pulverized porous gel material.
- the layer having a new pore structure can exhibit the same function (have, for example, a low refractive index) as the air layer.
- the pulverized products of the gel pulverized product-containing solution of the present invention have residual silanol groups, after forming a new three-dimensional structure as the coating film (functional porous material precursor), the pulverized products can be bonded chemically to each other.
- the functional porous material to be formed has a structure with void spaces, it can maintain sufficient strength and sufficient flexibility. Therefore, according to the present invention, the functional porous material can be easily and simply applied to various objects.
- the gel pulverized product-containing solution obtained by the production method of the present invention is very useful, for example, in the production of the porous structure which can be a substitute for an air layer.
- the functional porous material formed by using the gel pulverized product-containing solution of the present invention can exhibit the same function as the air layer by simply disposing it on an intended site. Therefore, as described above, the present invention can allow various objects to exhibit the same function as that of an air layer easily and simply as compared with the case of forming the air layer.
- the gel pulverized product-containing solution of the present invention also can be referred to as, for example, a solution for forming the functional porous material or a solution for forming a void-containing layer or a low refractive index layer.
- the porous material is the pulverized product.
- the range of the volume average particle diameter of the pulverized products (particles of porous gel material) in the gel pulverized product-containing solution of the present invention is, for example, from 10 to 1000 nm, from 100 to 500 nm, or from 200 to 300 nm.
- the volume average particle diameter indicates a variation in particle size of the pulverized products in the gel pulverized product-containing solution according to the present invention.
- the volume average particle diameter can be measured using a particle size distribution analyzer based on dynamic light scattering, laser diffraction, or the like, or using an electron microscope such as a scanning electron microscope (SEM) or a transmission electron microscope (TEM), as described above, for example.
- the concentration of the gel pulverized products in the gel pulverized product-containing solution of the present invention is not limited to particular concentrations and is, for example, from 2.5 to 4.5 wt %, from 2.7 to 4.0 wt %, or from 2.8 to 3.2 wt % as particles with a particle diameter from 10 to 1000 nm.
- the gel (e.g., porous gel material) in the gel pulverized product-containing solution of the present invention is not limited to particular gels and can be, for example, a silicon compound.
- the silicon compound is not limited to particular compounds and can be, for example, a silicon compound at least containing three or less functional groups having saturated bonds. “Containing three or less functional groups having saturated bonds” means that the silicon compound contains three or less functional groups and these functional groups have saturated bonds with silicon (Si).
- the silicon compound is, for example, a compound represented by the following chemical formula (2).
- R 1 and R 2 are each a linear or branched alkyl group, R 1 and R 2 may be the same or different from each other, R 1 may be the same or different from each other when X is 2, and R 2 may be the same or different from each other.
- R 1 are the same as those in the chemical formula (1) to be described below, for example.
- R 2 reference can be made to the description as to the examples of R 1 in the chemical formula (1), for example.
- a compound containing the R 1 group and the R 2 group may be used in addition to or in place of the silicon compound represented by the formula (2). Further, for example, as described above, a compound containing the R 1 group and a compound containing the R 2 group may be used in addition to or in place of the compound containing the R 1 group and the R 2 group.
- a specific example of the silicon compound represented by the chemical formula (2) is the one in which X is 3, which is a compound represented by the following chemical formula (2′).
- R 1 and R 2 are the same as those in the chemical formula (2).
- the silicon compound is trimethoxy(methyl)silane (also referred to as “MTMS” hereinafter).
- the solvent can be, for example, a dispersion medium.
- the dispersion medium (hereinafter, also referred to as “coating solvent”) is not limited to particular media and can be, for example, a gelation solvent or a pulverization solvent and is preferably the pulverization solvent.
- the coating solvent contains an organic solvent having a boiling point of 70° C. or higher and less than 180° C. and a saturation vapor pressure of 15 kPa or less at 20° C.
- organic solvent examples include carbon tetrachloride, 1,2-dichloroethane, 1,1,2,2-tetrachloroethane, trichloroethylene, isopropyl alcohol, isopropyl alcohol, isopentyl alcohol, 1-pentyl alcohol (pentanol), ethyl alcohol (ethanol), ethylene glycol monoethyl ether, ethylene glycol monoethyl ether acetate, ethylene glycol mono-n-butyl ether, ethylene glycol monomethyl ether, xylene, cresol, chlorobenzene, isobutyl acetate, isopropyl acetate, isopentyl acetate, ethyl acetate, n-butyl acetate, n-propyl acetate, n-pentyl acetate, cyclohexanol, cyclohexanone, 1,4-dioxane, N,N-dimethylform
- the gel pulverized product-containing solution can be, for example, a sol particle solution obtained by dispersing the pulverized products in the dispersion medium.
- a sol particle solution obtained by dispersing the pulverized products in the dispersion medium.
- sol refers to a state where, by pulverizing a three-dimensional structure of a gel, pulverized products (i.e., particles of porous sol material each having a three-dimensional nanostructure holding part of the void-containing structure) are dispersed in a solvent and exhibit fluidity.
- pulverized products i.e., particles of porous sol material each having a three-dimensional nanostructure holding part of the void-containing structure
- a catalyst for chemically bonding the pulverized products of the gel to each other can be added to the gel pulverized product-containing solution of the present invention, for example.
- the content of the catalyst is not particularly limited, and is, for example, from 0.01 to 20 wt %, from 0.05 to 10 wt %, or from 0.1 to 5 wt %, relative to the weight of the gel pulverized products.
- the gel pulverized product-containing solution of the present invention may contain a crosslinking assisting agent for indirectly bonding the pulverized products of the gel, for example.
- the content of the crosslinking assisting agent is not particularly limited, and is, for example, from 0.01 to 20 wt %/o, from 0.05 to 15 wt %, or from 0.1 to 10 wt % relative to the weight of the gel pulverized product.
- the proportion of functional groups that are not involved in a crosslinked structure inside the gel among functional groups of structural unit monomers of the gel in the pulverized product-containing solution of the present invention may be, for example, 30 mol % or less, 25 mol % or less, 20 mol % or less, or 15 mol % or less, and may be, for example, 1 mol % or more, 2 mol % or more, 3 mol % or more, or 4 mol % or more.
- the proportion of functional groups that are not involved in the crosslinked structure inside the gel can be measured as follows, for example.
- the gel after drying is subjected to a solid state NMR (Si-NMR), and the proportion of residual silanol groups that are not involved in the crosslinked structure (functional groups that are not involved in the crosslinked structure inside the gel) is calculated from the peak ratio obtained by the NMR. Further, when the functional group is other than the silanol group, the proportion of functional groups that are not involved in the crosslinked structure inside the gel can be calculated from the peak ratio obtained by the NMR according to this method.
- Mixing particles (pulverized products) of the porous gel material and the solvent is optional in the gel pulverized product-containing solution production method of the present invention, and may or may not be included.
- a specific example of the mixing includes, for example, mixing a dispersion medium and pulverized products of a gelled silicon compound (silicon compound gel) obtained from a silicon compound at least containing three or less functional groups having saturated bonds.
- the pulverized products of the porous gel material can be obtained from the porous gel material by the pulverizing a gel to be described below, for example.
- the pulverized products of the porous gel material can be obtained from the porous gel material that is obtained after an aging treatment in the aging to be described below, for example.
- the gelling is, for example, gelling a massive porous material in a solvent to generate a porous gel material.
- a specific example of the gelling can be, for example, gelling a silicon compound at least containing three or less functional groups having saturated bonds in a solvent to generate a silicon compound gel.
- the gelling will be described below with reference to the case where the porous material is a silicon compound as an example.
- the gelling is, for example, gelling the monomer silicon compound by a dehydration condensation reaction in the presence of a dehydration condensation catalyst, and by the gelling, a silicon compound gel is obtained.
- the silicon compound gel contains, for example, a residual silanol group, and the residual silanol group is preferably adjusted, as appropriate, according to the chemical bonding among pulverized products of the silicon compound gel to be described below.
- the silicon compound is only required to be gelled by a dehydration condensation reaction and is not limited to particular compounds.
- the silicon compounds are bonded by the dehydration condensation reaction. Bonding between the silicon compounds is, for example, hydrogen bond or intermolecular force bond.
- the silicon compound can be, for example, a silicon compound represented by the chemical formula (1).
- the silicon compound represented by the chemical formula (1) contains hydroxyl groups.
- silicon compounds of the chemical formula (1) can be bonded to each other by hydrogen bond or intermolecular force bond via their hydroxyl groups, for example.
- X is 2, 3, or 4, and R 1 is a linear or a branched alkyl group, for example.
- the number of carbon atoms in R 1 is 1 to 6, 1 to 4, or 1 to 2, for example.
- the linear alkyl group is a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, or a hexyl group, for example.
- the branched alkyl group is an isopropyl group or an isobutyl group, for example.
- the X is 3 or 4, for example.
- a specific example of the silicon compound represented by the chemical formula (1) is the one in which X is 3, which is a compound represented by the following chemical formula (1′).
- R 1 is the same as that in the chemical formula (1), and is, for example, a methyl group.
- the silicon compound is tris(hydroxy)methylsilane.
- X is 3, the silicon compound is a trifunctional silane having three functional groups, for example.
- silicon compound represented by the chemical formula (1) is the one in which X is 4.
- the silicon compound is a tetrafunctional silane having four functional groups, for example.
- the silicon compound may be a precursor for forming a silicon compound represented by the chemical formula (1) by hydrolysis, for example.
- the precursor is not limited as long as it can generate the silicon compound when it is hydrolyzed, for example.
- a specific example of the silicon compound precursor is a compound represented by the chemical formula (2).
- the production method of the present invention may further include hydrolyzing the precursor prior to the gelling, for example.
- the method for the hydrolysis of the precursor is not limited to particular methods, and the precursor can be hydrolyzed through a chemical reaction in the presence of a catalyst, for example.
- the catalyst include acids such as an oxalic acid and an acetic acid.
- the hydrolysis reaction can be caused by, for example, adding an aqueous oxalic acid solution dropwise slowly to a solution of the silicon compound precursor in dimethylsulfoxide at room temperature and then stirring the resultant mixture for about 30 minutes.
- hydrolysis of the silicon compound precursor for example, by hydrolyzing the alkoxy group of the silicon compound precursor completely, it is possible to more efficiently achieve gelation and aging to be performed subsequently and heating and immobilization to be performed after the formation of a void-containing structure.
- the silicon compound can be, for example, a hydrolysate of trimethoxy(methyl)silane.
- the monomer silicon compound is not limited to particular compounds and can be selected, as appropriate, according to the intended use of the functional porous material to be produced, for example.
- the silicon compound preferably is the trifunctional silane in terms of its excellent properties to achieve a low refractive index when a premium is placed on the low refractive index, for example.
- the silicon compound preferably is the tetrafunctional silane from the viewpoint of imparting high abrasion resistance when a premium is placed on strength (e.g., abrasion resistance), for example.
- As the silicon compound as a raw material of the silicon compound gel only one type of the silicon compound may be used, or two or more types of the silicon compounds may be used in combination, for example.
- the silicon compound may be made up of the trifunctional silane only, the tetrafunctional silane only, or both the trifunctional silane and the tetrafunctional silane, for example.
- the silicon compounds may further include a silicon compound(s) other than the trifunctional silane and the tetrafunctional silane, for example.
- the ratio thereof is not limited to particular ratios and can be set as appropriate.
- the gelation of the porous material such as the silicon compound can be achieved by a dehydration condensation reaction of the porous bodies, for example.
- the dehydration condensation reaction preferably is performed in the presence of a catalyst, for example.
- the catalyst include dehydration condensation catalysts such as: acid catalysts including a hydrochloric acid, an oxalic acid, and a sulfuric acid: and base catalysts including ammonia, potassium hydroxide, sodium hydroxide, and ammonium hydroxide.
- the dehydration condensation catalyst particularly preferably is a base catalyst.
- the amount of the catalyst to be added relative to the porous material is not limited to particular materials, and is, for example, from 0.01 to 10 mol, from 0.05 to 7 mol, or from 0.1 to mol per mole of the porous material.
- the gelation of the porous material such as the silicon compound preferably is performed in a solvent, for example.
- the proportion of the porous material in the solvent is not limited to particular proportions.
- the solvent include dimethylsulfoxide (DMSO), N-methylpyrrolidone (NMP), N,N-dimethylacetamide (DMAc), dimethylformamide (DMF), ⁇ -butyrolactone (GBL), acetonitrile (MeCN), and ethylene glycol ethyl ether (EGEE).
- DMSO dimethylsulfoxide
- NMP N-methylpyrrolidone
- DMAc N,N-dimethylacetamide
- DMF dimethylformamide
- GBL ⁇ -butyrolactone
- MeCN acetonitrile
- EGEE ethylene glycol ethyl ether
- One type of the solvent may be used alone or two or more types of the solvents may be used in combination, for example.
- the conditions for the gelation are not limited to particular conditions.
- the treatment temperature for treating the solvent containing the porous material is, for example, from 20° C. to 30′C, from 22′C to 28° C., or from 24° C. to 26° C., and the treatment time for treating the same is, for example, from 1 to 60 minutes, from 5 to 40 minutes, or from 10 to 30 minutes.
- the treatment conditions are not limited to particular conditions, and the treatment conditions given above as examples also apply to the dehydration condensation reaction.
- the porous material is a silicon compound, siloxane bonds are grown and silica primary particles are formed by the gelation, for example. As the reaction further proceeds, the primary particles are connected in the form of a string of beads, whereby a gel having a three-dimensional structure is generated.
- the form of the gel obtained from the porous material in the gelling is not limited to particular forms.
- the term “gel” generally refers to a solidified state of a solute where particles of the solute have lost their independent mobility owing to interaction and form an aggregate.
- a “wet gel” generally refers to a gel containing a dispersion medium in which particles of a solute build a uniform structure
- a “xerogel” generally refers to a gel from which a solvent is removed and in which particles of a solute form a network structure with void spaces.
- a wet gel is preferably used as the silicon compound gel.
- the porous gel material is a silicon compound gel
- the amount of a residual silanol group in the silicon compound gel is not limited to particular amounts and can be, for example, in the same range to be described below.
- the porous gel material per se obtained by the gelation may be subjected to the replacing a solvent and the first pulverization stage or may be subjected to an aging treatment in the aging prior to the first pulverization stage, for example.
- the gelled porous material (porous gel material) is aged in a solvent.
- the conditions for the aging treatment in the aging are not limited to particular conditions, and for example, the porous gel material may be incubated in a solvent at a predetermined temperature. For example, by further growing the primary particles of the porous gel material having a three-dimensional strmcture obtained by the gelation through the aging treatment, it is possible to increase the size of the particles themselves.
- the contact area at the neck portion where the particles are in contact with each other increases so that the contact state can be changed from point contact to surface contact.
- the above-described aging treatment of the porous gel material improves the strength of the gel itself, for example, whereby the strength of the three-dimensional basic structures of the pulverized products after pulverization can be improved.
- pores in the void-containing structure formed by deposition of the three-dimensional basic structures may become smaller as the solvent in the coating film volatilizes during the drying, for example.
- the lower limit thereof is, for example, 30° C. or higher, 35° C. or higher, or 40° C. or higher
- the upper limit thereof is, for example, 80° C. or lower, 75° C. or lower, or 70° C. or lower
- the range thereof is, for example, from 30° C. to 80° C., from 35° C. to 75° C., or from 40° C. to 70° C.
- the predetermined time is not limited particularly, and the lower limit thereof is, for example, 5 hours or more, 10 hours or more, or 15 hours or more, the upper limit thereof is, for example, 50 hours or less, 40 hours or less, or 30 hours or less, and the range thereof is, for example, from 5 to 50 hours, from 10 to 40 hours, or from 15 to 30 hours.
- Optimal aging conditions are, for example, as described above, conditions set to increase the size of the primary particles and to increase the contact area at the neck portion in the porous gel material. Furthermore, it is preferable to take the boiling point of the solvent used into consideration for the temperature in the aging treatment in the aging, for example.
- the solvent may volatilize excessively to cause defectiveness such that the pores in the three-dimensional void-containing structure are closed due to the condensation of the concentration of the coating solution.
- the aging temperature is too high in the aging treatment, the solvent may volatilize excessively to cause defectiveness such that the pores in the three-dimensional void-containing structure are closed due to the condensation of the concentration of the coating solution.
- the aging temperature is too low in the aging treatment, the effect of the aging cannot be obtained sufficiently.
- variation in temperature over time in a mass production process increases, which may result in products with poor quality.
- the same solvent as in the gelling can be used, for example.
- a reactant obtained after the gelation treatment i.e., the solvent containing the porous gel material
- the amount of residual silanol groups contained in the silicon compound gel having been subjected to the gelation and the subsequent aging treatment by mole indicates, for example, the proportion of the residual silanol groups, assuming that the amount of the alkoxy groups in the raw material used in the gelation (e.g., the silicon compound or the precursor thereof) by mole is 100.
- the lower limit thereof is, for example, 50% or more, 40% or more, or 30% or more
- the upper limit thereof is, for example, 1% or less, 3% or less, or 5% or less
- the range thereof is, for example, from 1% to 50%, from 3% to 40%, or from 5% to 30%.
- the amount of the residual silanol groups by mole be smaller, for example.
- the amount of the residual silanol groups by mole is too large, there is a possibility that the void-containing structure cannot be maintained until the crosslinking of the functional porous material precursor is completed in formation of the functional porous material, for example.
- the functional porous material precursor cannot be crosslinked, so that a sufficient film strength cannot be imparted, for example.
- the above description is directed to an example where residual silanol groups are used.
- the silicon compounds that have been modified with various reactive functional groups are used as raw materials of the silicon compound gel, for example, the same phenomenon can be applied to each of the reactive functional groups.
- the porous gel material per se obtained by the gelation is subjected to, for example, an aging treatment in the aging, then the replacing a solvent, and thereafter the pulverizing a gel.
- the solvent is replaced with another solvent.
- the pulverizing a gel is, as described above, pulverizing the porous gel material.
- the porous gel material after the gelling may be subjected to the pulverization, and the porous gel material having been subjected to the aging treatment may further be subjected to the pulverization, for example.
- controlling a gel form of controlling the shape and the size of the gel may be performed prior to the replacing a solvent (e.g., after the aging).
- the shape and the size of the gel to be controlled in the controlling a gel form is not limited to particular shapes and sizes and are, for example, as described above.
- the controlling a gel form may be performed by dividing the gel into solids (3D solid) in an appropriate size and shape, for example.
- the pulverizing a gel is performed after subjecting the gel to the replacing a solvent.
- the solvent is replaced with another solvent.
- the following problem may arise.
- the catalyst and solvent used in the gelling remain after the aging to cause gelation of the solution over time and affect the pot life of the gel pulverized product-containing solution to be obtained finally, and the drying efficiency at the time when the coating film formed using the gel pulverized product-containing solution is dried is reduced.
- such a solvent in the pulverizing a gel is also referred to as a “pulverization solvent”.
- the pulverization solvent is not limited to particular solvents, and may be, for example, an organic solvent.
- the organic solvent may be, for example, the one having a boiling point of 140° C. or lower, 130° C. or lower, 100° C. or lower, or 85° C. or lower. Specific examples thereof include isopropyl alcohol (IPA), ethanol, methanol, butanol, n-butanol, 2-butanol, isobutyl alcohol, pentyl alcohol, propylene glycol monomethyl ether (PGME), methyl cellosolve, and acetone.
- One type of the pulverization solvent may be used, or two or more types of the pulverization solvents may be used in combination, for example.
- the replacing a solvent is performed by multiple solvent replacement stages, and in the solvent replacement stages, the hydrophilicity of such a solvent may be caused to be lower in a subsequent stage than that in a prior stage.
- solvent replacement efficiency can be improved, and the residual amount of a gel production solvent in the gel (e.g., DMSO) can be significantly reduced.
- the replacing a solvent is performed by three solvent replacement stages, and DMSO in a gel may be first replaced with water in the first solvent replacement stage, the water in the gel may then be replaced with IPA in the second solvent replacement stage, and the IPA in the gel may thereafter be replaced with isobutyl alcohol in the third solvent replacement stage.
- the combination of the gelation solvent and the pulverization solvent is not limited to particular combinations, and examples thereof include the combinations of: DMSO and IPA; DMSO and ethanol: DMSO and isobutyl alcohol: and DMSO and n-butanol.
- the replacing a solvent is not particularly limited and can be performed as follows, for example. That is, first, the gel (e.g., gel after the aging treatment) produced in producing a gel is immersed in or brought into contact with another solvent to dissolve a gel production catalyst in the gel and an alcohol component and water generated by the condensation reaction in the solvent. The solvent in which the gel is immersed or with which the gel is brought into contact is drained, and the gel is again immersed or brought into contact with a new solvent. This is repeatedly performed until the residual amount of the gel production solvent in the gel becomes a desired amount. Each immersion time is, for example, 0.5 hours or more, 1 hour or more, or 1.5 hours or more. The upper limit thereof is not limited to particular times and is, for example, 10 hours or less.
- the immersion in the solvent may be performed by continuous contact of the solvent with the gel.
- the temperature during the immersion is not limited to particular temperatures and is, for example, from 20° C. to 70° C., from 25° C. to 65° C., or from 30° C. to 60° C.
- the solvent is replaced promptly, and the amount of the solvent required for replacement can be reduced.
- the solvent may be simply replaced at room temperature.
- each of the solvent replacement stages may be performed in the manner described above.
- another solvent replacement solvent
- the hydrophilicity of “another solvent” is caused to be lower in a subsequent stage than that in a prior stage
- such a solvent replacement solvent
- “another solvent” replacement solvent
- the void-containing layer production solvent include a solvent having a boiling point of 140° C. or lower.
- the void-containing layer production solvent include alcohol, ether, ketone, an ester solvent, an aliphatic hydrocarbon solvent, and an aromatic solvent. Specific examples of the alcohol having a boiling point of 140° C.
- IPA isopropyl alcohol
- ether having a boiling point of 140° C. or lower
- ether having a boiling point of 140° C. or lower
- PGME propylene glycol monomethyl ether
- ketone having a boiling point of 140° C. or lower
- ester solvent having a boiling point of 140° C.
- the void-containing layer production solvent is preferably alcohol, ether, or an aliphatic hydrocarbon solvent.
- One type of the pulverization solvent may be used, or two or more types of the pulverization solvents may be used in combination.
- IPA isopropyl alcohol
- ethanol n-butanol
- 2-butanol isobutyl alcohol
- IBA pentyl alcohol
- PGME propylene glycol monomethyl ether
- methyl cellosolve heptane
- octane is preferred.
- the saturation vapor pressure (volatility) of the void-containing layer production solvent be not too high.
- the one containing an aliphatic group having three or four or more carbon atoms is preferable, and the one containing an aliphatic group having four or more carbon atoms is more preferable.
- the solvent containing an aliphatic group having three or four or more carbon atoms may be, for example, alcohol.
- IPA isopropyl alcohol
- IBA isobutyl alcohol
- n-butanol, 2-butanol, 1-pentanol, and 2-pentanol are preferable and isobutyl alcohol (IBA) is particularly preferable.
- Another solvent (replacement solvent) in a stage other than the last solvent replacement stage is not particularly limited, and examples thereof include alcohol, ether, and ketone.
- alcohol include isopropyl alcohol (IPA), ethanol, methanol, n-butanol, 2-butanol, isobutyl alcohol (IBA), and pentyl alcohol.
- ether include propylene glycol monomethyl ether (PGME), methyl cellosolve, and ethyl cellosolve.
- ketone is acetone.
- Another solvent (replacement solvent) is not limited as long as it can replace the gel production solvent or “another solvent” (replacement solvent) in a previous stage.
- another solvent (replacement solvent) in a stage other than the last solvent replacement stage is preferably a solvent which does not finally remain in the gel or which hardly erodes the base (e.g., resin film) during coating even if it remains in the gel.
- another solvent replacement solvent
- “another solvent” (replacement solvent) in a stage other than the last solvent replacement stage is preferably alcohol.
- another solvent is preferably alcohol.
- another solvent may be, for example, water or a mixed solvent containing water in freely-selected proportion.
- Water or a mixed solvent containing water is highly compatible with a gel production solvent (e.g., DMSO) having a high hydrophilicity, so that the gel production solvent can be easily replaced and is preferable in terms of costs.
- a gel production solvent e.g., DMSO
- the multiple solvent replacement stages may include a stage in which “another solvent” is water, then a stage in which “another solvent” is the one containing an aliphatic group having three or less carbon atoms, and thereafter a stage in which “another solvent” is the one containing an aliphatic group having four or more carbon atoms.
- At least one of the solvent containing an aliphatic group having three or less carbon atoms and the solvent containing an aliphatic group having four or more carbon atoms may be an alcohol.
- the alcohol having an aliphatic group having three or less carbon atoms is not particularly limited, and examples thereof include isopropyl alcohol (IPA), ethanol, methanol, and n-propyl alcohol.
- the alcohol having an aliphatic group having four or more carbon atoms is not particularly limited, and examples thereof include n-butanol, 2-butanol, isobutyl alcohol (IBA), and pentyl alcohol.
- the solvent containing an aliphatic group having three or less carbon atoms may be isopropyl alcohol, and the solvent containing an aliphatic group having four or more carbon atoms may be isobutyl alcohol.
- the inventors of the present invention have found that it is very important to focus on the residual amount of the gel production solvent in order to form a void-containing layer having film strength under a relatively mild condition such as at 200° C. or lower, for example. This finding, which has been found independently by the inventors of the present invention, is not described in the prior arts including the patent literature and the non-patent literature.
- the gel production solvent is preferably a high-boiling-point solvent (e.g., DMSO) or the like for the progress of gelation reactions.
- a high-boiling-point solvent e.g., DMSO
- the “solvent” e.g., a gel production solvent, a void-containing layer production solvent, a replacement solvent
- the “solvent” may not dissolve a gel or pulverized products thereof, and the gel or the pulverized products thereof may be dispersed or precipitated in the solvent.
- the gel production solvent may have a boiling point of 140° C. or higher, for example.
- the gel production solvent is, for example, a water-soluble solvent.
- the “water-soluble solvent” refers to a solvent that can be mixed with water in a freely-selected ratio.
- each of the solvent replacement stages can be performed, for example, as follows. That is, first, the gel is immersed in or brought into contact with “another solvent” to dissolve a gel production catalyst in the gel, an alcohol component generated by the condensation reaction, and water in “another solvent”. Thereafter, the solvent in which the gel has been immersed or with which the gel has been brought into contact is drained, and the gel is again immersed or brought into contact with a new solvent. This is repeatedly performed until the residual amount of the gel production solvent in the gel becomes a desired amount. Each immersion time is, for example, 0.5 hours or more, 1 hour or more, or 1.5 hours or more.
- the upper limit thereof is not limited to particular times and is, for example, 10 hours or less.
- the immersion in the solvent may be performed by continuous contact of the solvent with the gel.
- the temperature during the immersion is not limited to particular temperatures and is, for example, from 20° C. to 70° C., from 25° C. to 65° C., or from 30° C. to 60° C.
- By heating the solvent is replaced promptly, and the amount of the solvent required for replacement can be reduced.
- the solvent may be simply replaced at room temperature.
- This solvent replacement stage is performed a plurality of times by gradually changing “another solvent” (replacement solvent) from the one having a high hydrophilicity to the one having a low hydrophilicity (a high hydrophobicity).
- a highly hydrophilic gel production solvent e.g., DMSO
- water e.g., water
- isobutyl alcohol coating solvent
- the solvent replacement can be efficiently performed by once replacing with isopropyl alcohol and then with isobutyl alcohol, which is a coating solvent.
- another solvent replacement solvent is not particularly limited.
- the solvent replacement stage may be performed a plurality of times by gradually changing “another solvent” (replacement solvent) from the one having a high hydrophilicity to the one having a low hydrophilicity (having a high hydrophobicity).
- replacement solvent replacement solvent
- This can significantly reduce the residual amount of the gel production solvent in the gel as described above.
- it is possible to significantly reduce the amount of the solvent to be used and to reduce the cost, as compared with a case of performing the solvent replacement by one stage using only the coating solvent.
- pulverizing a gel in the pulverization solvent is performed after the replacing a solvent. Furthermore, for example, as described above, the concentration of the gel may be measured, if necessary, after the replacing a solvent and prior to the pulverizing a gel, and adjusting a gel concentration may be performed thereafter if necessary.
- the concentration of the gel after the replacing a solvent and prior to the pulverizing a gel can be measured as follows, for example. That is, first, a gel is taken out from “another solvent” (pulverization solvent) after the replacing a solvent. This gel is controlled to be masses in appropriate shapes and sizes (e.g., blocks) by the controlling a gel form, for example.
- a solvent attached to the periphery of each mass of the gel is then removed, and the concentration of the solid content in one mass of the gel is measured by weight dry method.
- the concentration of the solid content in each of a plurality of randomly sampled masses e.g., 6 masses
- variations of the measured concentrations from the mean value thereof are calculated, to determine reproducibility of the measured concentrations.
- the concentration of the gel in the gel-containing solution may be decreased by adding “another solvent” (pulverization solvent).
- the concentration of the gel in the gel-containing solution may be increased by evaporating “another solvent” (pulverization solvent).
- the pulverizing a gel may be performed by one stage but is preferably performed by multiple stages. Specifically, for example, the first pulverization stage and the second pulverization stage may be performed. In addition to the first pulverization stage and the second pulverization stage, a further pulverization stage may be performed as the pulverizing a gel. That is, in the gel pulverized product-containing solution production method of the present invention, the number of pulverization stages included in the pulverizing a gel is not limited to two and may be three or more.
- a solution e.g., a suspension
- a catalyst for chemically bonding the microporous particles after or during the preparation of the solution containing the microporous particles, it is possible to prepare a solution containing the microporous particles and the catalyst.
- the amount of the catalyst to be added is not particularly limited, and is, for example 0.01 to 20 wt %, 0.05 to 10 wt %, or 0.1 to 5 wt % relative to the weight of the pulverized products of the silicon compound.
- the catalyst may be, for example, a catalyst that promotes crosslinking of the microporous particles.
- the chemical reaction for chemically bonding the microporous particles to each other preferably is a reaction utilizing a dehydration condensation reaction of residual silanol groups contained in silica sol molecules.
- the catalyst may be a photoactive catalyst or a thermoactive catalyst, for example. With the use of the photoactive catalyst, in forming a void-containing layer, the microporous particles can be bonded (e.g., crosslinked) to each other without heating, for example.
- a substance that generates a catalyst may be used.
- a substance that generates a catalyst when subjected to light irradiation photocatalyst generator
- thermoactive catalyst a substance that generates a catalyst when heated
- the photocatalyst generator is not particularly limited, and may be, for example, a photobase generator (a substance that generates a basic catalyst when subjected to light irradiation) or a photoacid generator (a substance that generates an acidic catalyst when subjected to light irradiation). Among them, the photobase generator is preferable.
- Examples of the photobase generator include 9-anthrylmethyl N,N-diethylcarbamate (product name: WPBG-018), (E)-1-[3-(2-hydroxyphenyl)-2-propenoyl]piperidine (product name: WPBG-027), 1-(anthraquinon-2-yl)ethyl imidazolecarboxylate (product name: WPBG-140), 2-nitrophenyhnethyl 4-methacryloyloxypiperidine-1-carboxylate (product name: WPBG-165), 1,2-diisopropyl-3-[bis(dimethylamino) methylene]guanidium 2-(3-benzoylphenyl)propionate (product name: WPBG-266), 1,2-dicyclohexyl-4,4,5,5-tetramethylbiguamidium n-butyltriphenylborate (product name: WPBG-300), 2-(9-oxoxanthen-2-yl)
- the photoacid generator examples include aromatic sulfonium salt (product name: SP-170, manufactured by ADEKA), triarylsulfonium salt (product name: CPI101A, manufactured by San-Apro Ltd.), and aromatic iodonium salt (product name: Irgacure 250, manufactured by Ciba Japan).
- the catalyst for chemically bonding the microporous particles to each other is not limited to the photoactive catalyst and the photocatalyst generator, and may be a thermoactive catalyst or a thermal catalyst generator, for example.
- Examples of the catalyst for chemically bonding the microporous particles to each other include: base catalysts such as potassium hydroxide, sodium hydroxide, and ammonium hydroxide: and acid catalysts such as a hydrochloric acid, an acetic acid, and an oxalic acid. Among them, the base catalysts are preferable.
- the catalyst or the catalyst generator for chemically bonding the microporous particles to each other can be used by adding it to a sol particle solution (e.g., suspension) containing the pulverized products (microporous particles) immediately before coating the sol particle solution, or can be used in the form of a mixture with a solvent, for example.
- the mixture may be, for example, a coating solution obtained by adding the catalyst directly to and dissolving the catalyst in the sol particle solution, a solution obtained by dissolving the catalyst or the catalyst generator in a solvent, or a dispersion liquid obtained by dispersing the catalyst or the catalyst generator in a solvent.
- the solvent is not particularly limited, and examples thereof include various organic solvents, water, and buffer solutions.
- the appearance of the film in film formation by coating can be improved.
- the amount of the high-boiling-point solvent is not particularly limited, and is, for example, 0.05 to 0.8 times, 0.1 to 0.5 times, and particularly 0.15 to 0.4 times relative to the solid content of the solution containing the microporous particles.
- the high-boiling-point solvent is not particularly limited and examples thereof include dimethyl sulfoxide (DMSO), N,N-dimethylformamide (DMF), N,N-dimethylacetamide (DMAc), N-methylpyrrolidone (NMP), ⁇ -butyl lactone (GBL), and ethylene glycol ethyl ether (EGEE).
- DMSO dimethyl sulfoxide
- DMF N,N-dimethylformamide
- DMAc N,N-dimethylacetamide
- NMP N-methylpyrrolidone
- GBL ⁇ -butyl lactone
- EGEE ethylene glycol ethyl ether
- a solvent having a boiling point of 110° C. or higher is preferable, and the present invention is not limited to the specific examples described above. It is considered that the high-boiling-point solvent serves as a leveling agent in film forming in which particles are aligned.
- the above-described high-boiling-point solvent also in the gel synthesis. It is to be noted, although details are unknown, the high-boiling-point solvent effectively acts when the high-boiling-point solvent is newly added to the solution containing the microporous particles produced after the solvent used in the synthesis has been completely removed. It is to be noted, however, that the above-described mechanisms merely are examples and do not limit the present invention by any means.
- nanoparticles surfaces of which being modified with the compound having the surface orientation, are added to the produced gel pulverized product-containing solution, and the resultant gel pulverized product-containing solution can be used for producing the void-containing layer of the present invention.
- the nanoparticles may be added at a proportion of; for example, 10 to 50 mass %, 15 to 40 mass %, or to 30 mass % relative to a skeleton component of the void-containing layer.
- the laminate production method of the present invention is described together with the methods of producing the void-containing layer and pressure-sensitive adhesive/adhesive layer that configure the laminate, with reference to examples.
- the methods will be described below mainly with reference to a case in which the void-containing layer of the present invention is a silicone porous material formed of a silicon compound.
- the void-containing layer of the present invention is not limited only to a silicone porous material.
- the void-containing layer is other than a silicone-porous material, reference can be made to the following description unless otherwise stated.
- the gel pulverized product-containing solution used for producing the void-containing layer of the present invention contains nanoparticles, surfaces of which being modified with the compound having the surface orientation, unless otherwise stated.
- the nanoparticles, surfaces of which being modified with the compound having the surface orientation can be added to the gel pulverized product-containing solution after being produced, for example.
- the void-containing layer production method of the present invention includes, for example, forming a void-containing layer precursor using the gel pulverized product-containing solution of the present invention, and chemically bonding the pulverized products of the gel pulverized product-containing solution contained in the precursor.
- the precursor may be referred to as a coating film, for example.
- a porous structure having the same function as an air layer is formed.
- the reason for this is speculated as follows, for example.
- the present invention is not limited by this speculation. The reason will be described below with reference to a case in which the void-containing layer is a silicone porous material.
- the gel pulverized product-containing solution used in the method for producing the silicone porous material contains pulverized products of the silicon compound gel.
- the three-dimensional structure of the gelled silica compound is dispersed in three-dimensional basic structures of the pulverized products.
- the precursor e.g., coating film
- the three-dimensional basic structures are deposited, and the void-containing structure based on the three-dimensional basic structures are formed, for example. That is, according to the method for producing a silicone porous material, a new porous structure different from that of the silicon compound gel is formed of the pulverized products having the three-dimensional basic structures.
- the pulverized products are further chemically bonded to each other, whereby the new three-dimensional structure is immobilized.
- the void-containing layer e.g., silicone porous material
- the void-containing layer obtained by the present invention can be used as a member utilizing voids in a wide range of products such as heat insulating materials, sound absorbing materials, optical members, and ink-receiving layers, for example.
- a laminated film having various functions imparted therein can be produced using the void-containing layer.
- the gel pulverized product-containing solution of the present invention is coated on the base, for example.
- the gel pulverized product-containing solution of the present invention onto, for example, a base, drying the coating film, and thereafter chemically bonding (e.g., crosslinking) pulverized products in the bonding, for example, a void-containing layer having film strength at or above a certain level can be formed continuously.
- the amount of the gel pulverized product-containing solution to be coated onto the base is not particularly limited, and can be set as appropriate depending on, for example, a desired thickness of the void-containing layer of the present invention.
- the amount of the pulverized products to be coated onto the base is, for example, in the range from 0.01 to 60000 ⁇ g, 0.1 to 5000 ⁇ g, or 1 to 50 ⁇ g per square meter of the base. It is difficult to uniquely define a preferable amount of the gel pulverized product-containing solution to be coated, because it may be affected by the concentration of the solution, the coating method, etc., for example.
- a coating layer as thin as possible.
- the coating amount is too large, for example, it is likely that the solvent may be dried in a drying oven before it volatilizes. If the solvent is dried before the void-containing structure is formed by the sedimentation and deposition of nano-sized pulverized sol particles in the solvent, formation of void spaces may be inhibited to lower the void fraction considerably.
- the coating amount is too small, the risk of cissing due to unevenness, variation in hydrophilicity and hydrophobicity, etc. on the surface of the base may increase.
- the porous material precursor may be subjected to a drying treatment.
- the purpose of the drying treatment is not only to remove the solvent in the porous material precursor (the solvent contained in the gel pulverized product-containing solution) but also to allow the sedimentation and deposition of the sol particles to occur to form a void-containing structure during the drying treatment, for example.
- the temperature of the drying treatment is from 50° C. to 250° C., from 60° C. to 150° C., or from 70° C. to 130° C., for example, and the time of the drying treatment is from 0.1 to 30 minutes, from 0.2 to 10 minutes, or from 0.3 to 3 minutes, for example.
- the temperature and the time of the drying treatment it is preferable to set the temperature and the time of the drying treatment lower and shorter, respectively, for example.
- the following problem may arise, for example. That is, when the base is a resin film, for example, the base may extend in a drying oven as the temperature approaches the glass-transition temperature of the base, so that a void-containing structure formed immediately after the coating may have defects such as cracks.
- the conditions are too mild, the following problem may arise, for example. That is, the film may contain a residual solvent when it comes out of the drying oven, so that, if the film rubs against a roller in a subsequent process, defects in appearance such as scratches may be caused.
- the drying treatment may be natural drying, heat-drying, or drying under reduced pressure, for example.
- the drying method is not particularly limited, and a commonly used heater can be used, for example.
- the heater include a hot air fan, a heating roller, and a far-infrared heater.
- heat-drying is preferable.
- a solvent having a low surface tension for the purpose of inhibiting the shrinkage stress that may occur as the solvent volatizes during the drying process and inhibiting a crack phenomenon in the void-containing layer (the silicone porous material) caused by the shrinkage stress.
- the solvent include, but are not limited to, lower alcohols (typically, isopropyl alcohol [IPA]), hexane, and perfluorohexane.
- the base is not limited to particular bases, and for example, a base made of a thermoplastic resin, a base made of glass, an inorganic base plate typified by silicon, a plastic formed of a thermosetting resin, an element such as a semiconductor, or a carbon fiber-based material typified by carbon nanotube can be favorably used.
- the base is by no means limited thereto.
- Examples of the form of the base include a film and a plate.
- the thermoplastic resin include polyethylene terephthalate (PET), acrylic resins, cellulose acetate propionate (CAP), cycloolefin polymer (COP), triacetylcellulose (TAC), polyethylene naphthalate (PEN), polyethylene (PE), and polypropylene (PP).
- the bonding is chemically bonding the pulverized products contained in the porous material precursor (coating film).
- the three-dimensional structures of the pulverized products in the porous material precursor are immobilized, for example.
- a treatment at a high temperature of at least 200° C. is performed to induce the dehydration condensation reaction of silanol groups and the formation of siloxane bonds.
- various additives that catalyze the above-described dehydration condensation reaction are caused to react with each other.
- the method for achieving the above-described chemical bonding is not particularly limited, and can be determined as appropriate depending on the type of the gel (e.g. silicon compound gel), for example.
- the chemical bonding can be achieved by chemically crosslinking the pulverized products.
- inorganic particles such as titanium oxide particles
- the inorganic particles and the pulverized products may be chemically bonded by crosslinking.
- a site of the catalyst other than the catalytic site may be chemically crosslinked with the pulverized products.
- the present invention is not only applicable to a void-containing layer formed by sol particles bonded to each other, but the applicable range of the present invention can be expanded to an organic-inorganic hybrid void-containing layer and a host-guest void-containing layer, for example. It is to be noted, however, that the applicable range of the present invention is not limited thereto.
- the bonding can be carried out by causing a chemical reaction in the presence of a catalyst, for example.
- the chemical reaction in the present invention preferably is a reaction utilizing a dehydration condensation reaction of residual silanol groups contained in the pulverized products of the silicon compound gel.
- the catalyst examples include, but are not limited to, base catalysts such as potassium hydroxide, sodium hydroxide, and ammonium hydroxide and acid catalysts such as a hydrochloric acid, an acetic acid, and an oxalic acid.
- base catalyst is particularly preferable.
- catalysts that exhibit catalytic activity when irradiated with light e.g., ultraviolet rays
- photoacid generation catalysts and photobase generation catalysts can be used preferably.
- the photoacid generation catalysts and photobase generation catalysts are not particularly limited, and are as described above, for example.
- the catalyst it is preferable to add the catalyst to a sol particle solution containing the pulverized products immediately before coating the sol particle solution as described above, or to use the catalyst in the form of a mixture with a solvent, for example.
- the mixture may be, for example, a coating solution obtained by adding the catalyst directly to and dissolving the catalyst in the sol particle solution, a solution obtained by dissolving the catalyst in a solvent, or a dispersion liquid obtained by dispersing the catalyst in a solvent.
- the solvent is not particularly limited, and examples thereof include water and buffer solutions, as described above.
- a crosslinking assisting agent for indirectly bonding the pulverized products of the gel may be further added to the gel-containing solution of the present invention.
- This crosslinking assisting agent enters the spaces between the respective particles (the pulverized products), where it interacts with or bonds to the particles. This allows the particles somewhat apart from each other to bond to each other. As a result, it becomes possible to efficiently improve the strength.
- the crosslinking assisting agent preferably is a multi-crosslinking silane monomer.
- the multi-crosslinking silane monomer may have at least two and at most three alkoxysilyl groups, the chain length between the alkoxysilyl groups may be at least one and at most ten carbon atoms, and the multi-crosslinking silane monomer may contain an element other than carbon, for example.
- crosslinking assisting agent examples include bis(trimethoxysilyl)ethane, bis(triethoxysilyl)ethane, bis(trimethoxysilyl)methane, bis(triethoxysilyl)methane, bis(triethoxysilyl)propane, bis(trimethoxysilyl)propane, bis(triethoxysilyl)butane, bis(trimethoxysilyl)butane, bis(triethoxysilyl)pentane, bis(trimethoxysilyl)pentane, bis(triethoxysilyl)hexane, bis(trimethoxysilyl)hexane, bis(trimethoxysilyl)-N-butyl-N-propyl-ethane-1,2-diamine, tris-(3-trimethoxysilylpropyl) isocyanurate, and tris-(3-triethoxysilylpropyl)
- the amount of the crosslinking assisting agent to be added is not particularly limited, and is, for example, in the range from 0.01 wt % to 20 wt %, from 0.05 wt % to 15 wt %, or from 0.1 wt % to 10 wt % relative to the weight of the pulverized products of the silicon compound.
- the chemical reaction in the presence of the catalyst can be caused by, for example: subjecting the coating film containing the catalyst or the catalyst generator previously added to the gel pulverized product-containing solution to light irradiation or beating; subjecting the coating film to light irradiation or heating after spraying the catalyst over the coating film; or subjecting the coating film to light irradiation or heating while spraying the catalyst or the catalyst generator over the coating film.
- the catalyst is a photoactive catalyst
- the silicone porous material can be formed by chemically bonding the microporous particles to each other by light irradiation.
- the silicone porous material can be formed by chemically bonding the microporous particles to each other by heating.
- the irradiation dose (energy) in the above irradiation is not limited to particular amounts and is, for example, from 200 to 800 mJ/cm 2 , from 250 to 600 mJ/cm 2 , or from 300 to 400 mJ/cm 2 in terms of light at a wavelength of 360 nm.
- the accumulated amount of light preferably is 200 mJ/cm 2 or more, from the viewpoint of preventing the problem in that, owing to insufficient irradiation dose, degradation of the catalyst generator by light absorption may not proceed sufficiently, so that the catalyst generator cannot exhibit its effect sufficiently.
- the accumulated amount of light preferably is 800 mJ/cm or less, from the viewpoint of preventing damage to the base disposed under the void-containing layer so as to prevent the formation of heat wrinkles.
- the wavelength of light in the irradiation is not limited to particular wavelengths and is, for example, from 200 to 500 nm or from 300 to 450 nm.
- the irradiation time in the irradiation is not limited to particular times and is, for example, from 0.1 to 30 minutes, from 0.2 to 10 minutes, or from 0.3 to 3 minutes.
- the conditions for the heat treatment are not limited to particular conditions.
- the heating temperature is from 50° C. to 250° C., from 60° C. to 150° C. or from 70° C. to 130° C.
- the heating time is from 0.1 to 30 minutes, from 0.2 to 10 minutes, or from 0.3 to 3 minutes, for example.
- a solvent having a low surface tension for the purpose of inhibiting the shrinkage stress that may occur as the solvent volatizes during the drying process and inhibiting a crack phenomenon in the void-containing layer caused by the shrinkage stress.
- the solvent include, but are not limited to, lower alcohols typically, isopropyl alcohol (IPA), hexane, and perfluorohexane.
- the void-containing layer (e.g., silicone porous material) of the present invention can be produced in the above-described manner.
- the void-containing layer production method of the present invention is not limited thereto.
- the void-containing layer of the present invention which is a silicone porous material, may be referred to as a “silicone porous material of the present invention” in the description below.
- the laminate production method of the present invention includes, for example, producing the pressure-sensitive adhesive/adhesive layer of the present invention by the pressure-sensitive adhesive/adhesive layer production method of the present invention; and attaching the pressure-sensitive adhesive/adhesive layer to the void-containing layer.
- the pressure-sensitive adhesive/adhesive layer production method of the present invention includes, for example, coating the pressure-sensitive adhesive/adhesive coating solution of the present invention onto a base, and heat-drying the base coated with the pressure-sensitive adhesive/adhesive coating solution.
- the pressure-sensitive adhesive/adhesive layer may be formed on the void-containing layer of the present invention by attaching, e.g., an adhesive tape including a base and the pressure-sensitive adhesive/adhesive layer of the present invention laminated on the base to the void-containing layer with the pressure-sensitive adhesive/adhesive layer side of the adhesive tape facing the void-containing layer.
- the base of the adhesive tape may be left on or peeled off from the pressure-sensitive adhesive/adhesive layer.
- the thickness of the sheet can be significantly reduced and the increase in the thickness of the device or the like can be prevented.
- the terms “pressure-sensitive adhesive” and “pressure-sensitive adhesive layer” respectively refer to an agent and a layer that adhere a substance in a peelable manner, for example.
- the terms “adhesive” and “adhesive layer” respectively refer to an agent and a layer that adhere a substance in a non-peelable manner, for example.
- the “pressure-sensitive adhesive” and the “adhesive” are not always clearly distinguishable from each other, and also, the “pressure-sensitive adhesive layer” and the “adhesive layer” are not always clearly distinguishable from each other.
- the pressure-sensitive adhesive/adhesive layer of the present invention can be produced using the pressure-sensitive adhesive/adhesive coating solution of the present invention as described above.
- the pressure-sensitive adhesive/adhesive coating solution of the present invention can be produced by the method for producing the pressure-sensitive adhesive/adhesive coating solution of the present invention including mixing a (meth)acrylic polymer, a monomer having one or two reactive double bonds per molecule, an isocyanate-based crosslinking agent, and an organic peroxide.
- the producing the pressure-sensitive adhesive/adhesive layer can be performed, for example, as follows.
- the pressure-sensitive adhesive/adhesive coating solution of the present invention is produced by the mixing a (meth)acrylic polymer, a monomer having one or two reactive double bonds per molecule, an isocyanate-based crosslinking agent, and an organic peroxide.
- the pressure-sensitive adhesive/adhesive coating solution includes a component(s) other than the (meth)acrylic polymer, a monomer having one or two reactive double bonds per molecule, the isocyanate-based crosslinking agent, and the organic peroxide, such a component(s) may be mixed together.
- the polymerization solvent at the time of producing the (meth)acrylic polymer may not be removed and mixed as a component of the pressure-sensitive adhesive/adhesive coating solution of the present invention.
- the method for producing the pressure-sensitive adhesive/adhesive coating solution of the present invention may or may not include a process other than the mixing, and may simply mix all the components of the pressure-sensitive adhesive/adhesive coating solution of the present invention in the mixing.
- the base is not particularly limited, and may be, for example, a base such as a film.
- the base is not limited to particular bases, and for example, a base made of a thermoplastic resin, a base made of glass, an inorganic base plate typified by silicon, a plastic formed of a thermosetting resin, an element such as a semiconductor, or a carbon fiber-based material typified by carbon nanotube can be favorably used.
- the base is by no means limited thereto. Examples of the form of the base include a film and a plate.
- thermoplastic resin examples include polyethylene terephthalate (PET), acrylic resins, cellulose acetate propionate (CAP), cycloolefin polymer (COP), triacetylcellulose (TAC), polyethylene naphthalate (PEN), polyethylene (PE), and polypropylene (PP).
- PET polyethylene terephthalate
- CAP cellulose acetate propionate
- COP cycloolefin polymer
- TAC triacetylcellulose
- PEN polyethylene naphthalate
- PE polyethylene
- PP polypropylene
- the coating thickness of the pressure-sensitive adhesive/adhesive coating solution is not particularly limited, but may be appropriately adjusted so that, for example, the thickness of the dried pressure-sensitive adhesive/adhesive layer becomes a predetermined thickness.
- the thickness of the dried pressure-sensitive adhesive/adhesive layer is not particularly limited, and is, for example, as described below.
- the base coated with the pressure-sensitive adhesive/adhesive coating solution is heated and dried (heat-drying).
- the temperature is not particularly limited, and may be, for example, 50° C. or higher, 80° C. or higher, 100° C. or higher, or 155° C. or higher, and may be, for example, 200° C. or lower, 180° C. or lower, or 160° C. or lower.
- the time of heat-drying may be, for example, 1 minute or longer, 2 minutes or longer, or 3 minutes or longer, and for example, 60 minutes or shorter, 30 minutes or shorter, 20 minutes or shorter, or 10 minutes or shorter.
- a crosslinking reaction and a graft polymerization occur among the (meth)acrylic polymer, a monomer having one or two reactive double bonds per molecule, and the isocyanate-based crosslinking agent.
- the amount of the semi-polymer present in the pressure-sensitive adhesive/adhesive coating solution is reduced, and the pressure-sensitive adhesive/adhesive layer is less liable to penetrate into the voids of the void-containing layer.
- the pressure-sensitive adhesive/adhesive layer of the present invention can be produced.
- the pressure-sensitive adhesive/adhesive layer is attached to the void-containing layer (attaching).
- the pressure-sensitive adhesive/adhesive layer may be formed on the void-containing layer of the present invention by attaching. e.g., an adhesive tape including a base and the pressure-sensitive adhesive/adhesive layer of the present invention laminated on the base to the void-containing layer with the pressure-sensitive adhesive/adhesive layer side of the adhesive tape facing the void-containing layer.
- the laminate production method of the present invention may further include, for example, heating the pressure-sensitive adhesive/adhesive layer and the void-containing layer after the attaching.
- the heating may be referred to as “aging”.
- the heating temperature is not particularly limited, and may be, for example, 40° C. or higher, 45° C. or higher, or 50° C. or higher, and may be, for example, 80° C. or lower, 70° C. or lower, 60° C. or lower, or 55° C. or lower.
- the heating time may be, for example, 1 minute or longer, 10 minutes or longer, 60 minutes or longer, or 1800 minutes or longer, and may be, for example, 3000 minutes or shorter, 2800 minutes or shorter, 2500 minutes or shorter, or 2000 minutes or shorter.
- the intermediate layer is formed by uniting the void-containing layer and the pressure-sensitive adhesive/adhesive layer. Then, for example, as described above, the intermediate layer serves as a stopper, which makes it possible to suppress a reduction in the void fraction caused by filling the voids of the void-containing layer with the pressure-sensitive adhesive.
- the void-containing layer can be protected from physical damage (particularly abrasion) by the pressure-sensitive adhesive/adhesive layer. It is preferable that the pressure-sensitive adhesive/adhesive layer have excellent pressure resistance so that the void-containing layer does not collapse even when used as a (baseless) void-containing layer-containing pressure-sensitive adhesive/adhesive sheet having no base, however, is not limited thereto.
- the thickness of the pressure-sensitive adhesive/adhesive layer is not particularly limited, and is, for example, from 0.1 to 100 ⁇ m, from 5 to 50 ⁇ m, from 10 to 30 ⁇ m, or from 12 to 25 ⁇ m.
- the void-containing layer of the present invention obtained in this manner may be further laminated on another film (layer) to form a laminated structure including the porous structure, for example.
- the respective components of the laminated structure may be laminated through the pressure-sensitive adhesive/adhesive layer (pressure-sensitive adhesive or adhesive), for example.
- the respective components may be laminated by continuous processing using a long film (e.g., the so-called “roll-to-roll” process) in terms of efficiency, for example.
- a long film e.g., the so-called “roll-to-roll” process
- the components that have been subjected to batch processing may be laminated on the base.
- FIG. 2 shows, after the film formation of the void-containing layer (silicone porous material), a protective film is attached to the thus-formed film and the thus-obtained laminate is wound up.
- the void-containing layer is laminated on another functional film, this may be achieved in the above-described manner, or alternatively, in the following manner: after performing coating and drying for forming the functional film, the void-containing layer formed into a film is attached to the functional film immediately before being wound-up.
- the film forming processes shown in FIGS. 1 to 3 are merely illustrative and do not limit the present invention by any means.
- the base may be the resin film described above.
- the void-containing layer of the present invention is obtained by forming the void-containing layer on the base.
- the void-containing layer of the present invention also is obtained by forming the void-containing layer on the base and then laminating the void-containing layer on the resin film described above in connection with the void-containing layer of the present invention.
- FIG. 1 schematically shows an example of a process of the laminate production method of the present invention in which the void-containing layer, the intermediate layer, and the pressure-sensitive adhesive/adhesive layer are laminated in this order on the base (resin film).
- the method for forming the void-containing layer includes coating (1) of coating a sol particle solution 20 ′′ of pulverized products of a gelled compound onto a base (resin film) 10 to form a coating film, drying (2) of drying the sol particle solution 20 ′′ to form a dried coating film 20 ′, chemical treating (for example, crosslinking) (3) of subjecting the coating film 20 ′ to a chemical treatment (for example, crosslinking treatment) to form a void-containing layer 20 , attaching (4) of attaching a pressure-sensitive adhesive/adhesive layer 30 to the void-containing layer 20 , and forming an intermediate layer (5) of reacting the void-containing layer 20 with the pressure-sensitive adhesive/adhesive layer 30 to form an intermediate layer 22 .
- the laminate production method of the present invention includes, as described above, producing the pressure-sensitive adhesive/adhesive layer by the pressure-sensitive adhesive/adhesive layer production method of the present invention, and attaching the pressure-sensitive adhesive/adhesive layer to the void-containing layer.
- the pressure-sensitive adhesive/adhesive layer production method of the present invention includes coating the pressure-sensitive adhesive/adhesive coating solution of the present invention onto a base, and heat-drying the base coated with the pressure-sensitive adhesive/adhesive coating solution.
- the chemical treating (crosslinking) (3) corresponds to the “forming a void-containing layer” of forming a void-containing layer in the laminate of the present invention, and the forming an intermediate layer (5) corresponds to the above-described heating (aging).
- the forming an intermediate layer (5) (hereinafter sometimes referred to as “aging”) also serves as improving the strength of the void-containing layer 20 (crosslinking-reacting for causing a crosslinking reaction inside the void-containing layer 20 ), and after the forming an intermediate layer (5), the void-containing layer 20 is changed to a void-containing layer 21 having improved strength.
- the attaching (4) may be attaching of an adhesive tape having a pressure-sensitive adhesive/adhesive layer to a base.
- the base coated with the pressure-sensitive adhesive/adhesive coating solution (the base on which the pressure-sensitive adhesive/adhesive layer is formed) is not shown, the base may be peeled off from or left on the pressure-sensitive adhesive/adhesive layer 30 .
- a laminated film in which the void-containing layer 21 , the intermediate layer 22 , and the pressure-sensitive adhesive/adhesive layer 30 are laminated in this order on the resin film 10 can be produced.
- the laminate production method of the present invention may or may not appropriately include processes other than those described with reference to FIG. 1 .
- the method for coating the sol particle solution 20 ′′ is not particularly limited, and a commonly used coating method can be employed.
- the coating method include a slot die method, a reverse gravure coating method, a micro-gravure method (micro-gravure coating method), a dip method (dip coating method), a spin coating method, a brush coating method, a roller coating method, a flexography, a wire-bar coating method, a spray coating method, an extrusion coating method, a curtain coating method, and a reverse coating method.
- the extrusion coating method, the curtain coating method, the roller coating method, and the micro-gravure coating method are preferable.
- the coating amount of the sol particle solution 20 ′′ is not particularly limited, and can be set as appropriate so that the void-containing layer 20 having a suitable thickness is obtained, for example.
- the thickness of the void-containing layer 21 is not particularly limited, and is as described above, for example.
- the sol particle solution 20 ′′ is dried (i.e., a dispersion medium contained in the sol particle solution 20 ′′ is removed) to form the coating film after drying (void-containing layer precursor) 20 ′.
- the conditions for the drying treatment are not particularly limited, and may be as described above.
- the coating film 20 ′ containing a catalyst or the catalyst generator e.g., a photoactive catalyst, a photocatalyst generator, a thermoactive catalyst, or a thermal catalyst generator
- a catalyst or the catalyst generator e.g., a photoactive catalyst, a photocatalyst generator, a thermoactive catalyst, or a thermal catalyst generator
- the pulverized products in the coating film 20 ′ are chemically bonded (e.g., crosslinked) to each other.
- the void-containing layer 20 is formed.
- the conditions for the light irradiation and heating in the chemical treating (3) are not particularly limited, and may be as described above.
- the pressure-sensitive adhesive/adhesive layer of the present invention is separately produced by the producing the pressure-sensitive adhesive/adhesive layer.
- the producing the pressure-sensitive adhesive/adhesive layer (the pressure-sensitive adhesive/adhesive layer production method of the present invention) is as described above, for example.
- the attaching (4) and forming an intermediate layer (5) are performed.
- the forming an intermediate layer (5) is heating the pressure-sensitive adhesive/adhesive layer 30 and the void-containing layer 20 after the attaching (4).
- the pressure-sensitive adhesive is a pressure-sensitive adhesive composition containing a polymer (for example, a (meth)acrylic polymer) and a crosslinking agent
- the polymer may be crosslinked by the crosslinking agent by the heating.
- the heating may also serve, for example, as drying the pressure-sensitive adhesive.
- the heating may also serve as the forming an intermediate layer (5).
- the temperature in the heating is not particularly limited, and is, for example, 70 to 160° C., 80 to 155° C. or 90 to 150° C.
- the time of the heating is not particularly limited, and is, for example, 1 to 10 minutes, 1 to 7 minutes, or 2 to 5 minutes.
- FIG. 2 schematically shows an example of a slot die coating apparatus and the method for forming a void-containing layer using the same. While FIG. 2 is a sectional view, hatching is omitted for the sake of clarity.
- the respective processes in the method using this apparatus are performed while conveying a base 10 in one direction by rollers.
- the conveyance speed is not particularly limited, and is, for example, from 1 to 100 nm/min, from 3 to 50 m/min, or from 5 to n/min.
- drying (2) is performed in an oven zone 110 .
- a pre-drying is performed after the coating (1) and prior to the drying (2).
- the pre-drying can be performed at room temperature without heating.
- heaters 111 are used.
- the heater 111 a hot air fan, a heating roll, a far-infrared heater, or the like can be used as appropriate, as described above.
- the drying (2) may be divided into two or more processes, and the drying temperatures in the respective processes may be set so that the drying temperature increases as it proceeds to the later process.
- chemical treating (3) is performed in a chemical treatment zone 120 .
- a coating film 20 ′ after being dried contains a photoactive catalyst, for example, the coating film 20 ′ is irradiated with light emitted from lamps (light irradiators) 121 disposed above and below the base 10 .
- the coating film 20 ′ after being dried contains a thermoactive catalyst, for example, hot air fans (heaters) are used instead of the lamps (light irradiators) 121 , and the base 10 is heated using the hot air fans 121 disposed above and below the base 10 .
- the timing at which chemical bonding of the pulverized products is caused in the production method of the present invention is not particularly limited, as described above.
- the drying (2) may also serve as the chemical treating (3).
- the chemical treating (3) further may be performed to make the chemical bonds between the pulverized products still stronger.
- the chemical bonding of the pulverized products may occur in the processes (e.g., the pre-drying, the coating (1), and preparing the coating solution) prior to the drying (2).
- attaching (4) of attaching a pressure-sensitive adhesive/adhesive layer 30 to the void-containing layer 20 is performed in a pressure-sensitive adhesive/adhesive layer coating zone 130 a by an attacher 131 a .
- the attaching (4) may be, for example, attaching (adhering) of an adhesive tape including a base and the pressure-sensitive adhesive/adhesive layer 30 to the base as described above.
- the base may be peeled off from or left on the pressure-sensitive adhesive/adhesive layer 30 , for example, as described above.
- an intermediate layer (aging) (5) is performed in an intermediate layer forming zone (aging zone) 130 to form an intermediate layer 22 by reacting the void-containing layer 20 with the pressure-sensitive adhesive/adhesive layer 30 .
- the void-containing layer 20 undergoes an internal crosslinking reaction and turns into a void-containing layer 21 with improved strength, as described above.
- the forming an intermediate layer (aging) (5) may be performed, for example, by heating the void-containing layer 20 and the pressure-sensitive adhesive/adhesive layer 30 using hot air fans (heaters) 131 disposed above and below the base 10 .
- the heating temperature, time, and the like are not particularly limited, and are, for example, as described above.
- a laminate obtained by forming the void-containing layer 21 on the base 10 is wound up by the winding roller 105 .
- the void-containing layer 21 in the laminate is protected by being covered with a protective sheet fed by a roller 106 .
- a protective sheet instead of the protective sheet, another layer formed of a long film may be laminated on the void-containing layer 21 .
- FIG. 3 schematically shows an example of a coating apparatus for a micro-gravure method (micro-gravure coating method) and the method for forming a void-containing layer using the same. While FIG. 3 is a sectional view, hatching is omitted for the sake of clarity.
- the respective processes in the method using this apparatus are performed while conveying a base 10 in one direction by rollers, as in the example shown in FIG. 2 .
- the conveyance speed is not particularly limited, and is, for example, from 1 to 100 m/min, from 3 to 50 m/min, or from 5 to 30 m/min.
- the sol particle solution 20 ′′ is coated using a solution reservoir 202 , a doctor (doctor knife) 203 , and a micro-gravure coater 204 .
- the sol particle solution 20 ′′ in the solution reservoir 202 is caused to be carried on the surface of the micro-gravure coater 204 , and is then coated on the surface of the base 10 with the micro-gravure coater 204 while controlling the thickness of the coating film of the sol particle solution 20 ′′ to a predetermined thickness with the doctor 203 .
- the micro-gravure coater 204 merely is an example of a coater. The coater is not limited to the micro-gravure coater 204 , and any coater may be employed.
- drying (2) is performed. Specifically, as shown in FIG. 3 , the base 10 having the sol particle solution 20 ′′ coated thereon is conveyed to an oven zone 210 .
- the sol particle solution 20 ′′ is dried by being heated with heaters 211 disposed in the oven zone 210 .
- the heaters 211 may be the same as those in FIG. 2 , for example.
- the drying (2) may be divided into two or more processes by dividing the oven zone 210 into two or more sections, for example.
- the drying temperatures in the respective processes may be set so that the drying temperature increases as it proceeds to the later process.
- chemical treating (3) is performed in a chemical treatment zone 220 .
- a coating film 20 ′ after being dried contains a photoactive catalyst
- the coating film 20 ′ is irradiated with light emitted from lamps (light irradiators) 221 disposed above and below the base 10 .
- the coating film 20 ′ after being dried contains a thermoactive catalyst, for example, hot air fans (heaters) are used instead of the lamps (light irradiators) 221 , and the base is heated using the hot air fans 221 disposed below the base 10 .
- thermoactive catalyst for example, hot air fans (heaters) are used instead of the lamps (light irradiators) 221 , and the base is heated using the hot air fans 221 disposed below the base 10 .
- attaching (4) of attaching the pressure-sensitive adhesive/adhesive layer 30 to the void-containing layer 20 in a pressure-sensitive adhesive/adhesive layer coating zone 230 a by an attacher 231 a may be, for example, attaching (adhering) of an adhesive tape including a base and the pressure-sensitive adhesive/adhesive layer 30 on the base as described above.
- the base may be peeled off from or left on the pressure-sensitive adhesive/adhesive layer 30 , for example, as described above.
- an intermediate layer (aging) (5) is performed in an intermediate layer forming zone (aging zone) 230 to form an intermediate layer 22 by reacting the void-containing layer 20 with the pressure-sensitive adhesive/adhesive layer 30 .
- the void-containing layer 20 turns into a void-containing layer 21 with improved strength, as described above.
- the forming an intermediate layer (aging) (5) may be performed, for example, by heating the void-containing layer 20 and the pressure-sensitive adhesive/adhesive layer 30 using hot air fans (heaters) 231 disposed above and below the base 10 .
- the heating temperature, time, and the like are not particularly limited, and are, for example, as described above.
- a laminated film obtained by forming the void-containing layer 21 on the base 10 is wound up by a winding roller 251 .
- another layer may be laminated on the laminated film, for example.
- another layer may be laminated on the laminated film, for example.
- the storage elastic modulus of the pressure-sensitive adhesive/adhesive layer at 23° C. was measured by the following measuring methods.
- the storage elastic modulus of the pressure-sensitive adhesive/adhesive layer at 23° C. was measured by the following methods using a viscoelasticity measurement device ARES (product of TA Instruments). That is, first, a sheet (layer) that is the same as the pressure-sensitive adhesive/adhesive layer in the following Reference Examples, Examples, and Comparative Examples except that the sheet has a thickness of 2 mm was formed. The sheet was stamped into the shapes corresponding to the parallel plates having a diameter of 25 mm, thereby obtaining measurement samples. The measurement sample was mounted on a chuck of the viscoelasticity measurement device ARES. Then, the temperature was increased from ⁇ 70° C. to 150° C. at a heating rate of 5° C./min while applying strain in the cycle of 1 Hz. and the storage elastic modulus at 23° C. was measured.
- ARES product of TA Instruments
- a base sample with a low refractive index layer was set in an ellipsometer (VASE, manufactured by J. A. Woollam Japan), and the refractive index was measured at a wavelength of 500 nm and at an incidence angle of 50° to 80°. The mean value of the thus-obtained measured values was set as the refractive index.
- a prism of the device was brought into close contact with a base side of a laminate obtained by laminating a pressure-sensitive adhesive on an ultra-low flexural layer, the total reflection critical angle was measured using a laser, and the refractive index was calculated from the critical angle.
- the void fraction was calculated according to the Lorentz-Lorenz's formula from the refractive index measured as described above.
- the thicknesses of the pressure-sensitive adhesive layer at five points were measured using a dial gauge.
- the mean value of the thus-obtained measured values was set as the thickness of the pressure-sensitive adhesive layer.
- a thick part with different contrast present between the pressure-sensitive adhesive layer and the low-refractive-index layer in an SEM image was considered as an intermediate layer and the thicknesses of the intermediate layer at two points in the SEM image was read.
- the mean value of the thus-obtained values was set as the thickness of the intermediate layer.
- the weight average molecular weight of the sol content and the proportion (weight percentage) of the low molecular weight component having a molecular weight of 10,000 or less were calculated.
- a measurement sample prepared in the same manner as the pressure-sensitive adhesive/adhesive layer in the following Reference Examples, Examples, and Comparative Examples (respective pressure-sensitive adhesive compositions were subjected to coating and then heat-drying) was prepared, 10 ml of tetrahydrofuran (THF) was added to 200 mg of the measurement sample, and the resultant was left to stand for 20 hours and filtered with a 0.45- ⁇ m membrane filter.
- THF tetrahydrofuran
- the obtained filtrate was subjected to GPC measurement using the following measurement device under the following measurement conditions. Then, in the same manner as described above, the weight average molecular weight of the sol content and the proportion (weight percentage) of the low molecular weight component having a molecular weight of 10,000 or less were calculated from the molecular weight distribution curve.
- the refractive index at the wavelength 500 nm was measured by the above-described method.
- gelation of silicon compound (the following process (1)) and aging (the following process (2)) were performed to produce a gel (silicone porous material) having a porous structure.
- controlling a gel form (3) replacing a solvent (4), pulverizing a gel (5), modifying nanoparticles with fluoroalkyl groups (6), and mixing a fluoroalkyl group-modified nanoparticle dispersion liquid (7) described below were further performed to obtain a coating solution for forming a void-containing layer (gel pulverized product-containing solution).
- the controlling a gel form (3) was performed as a different process from the process (1) as described below.
- the present invention is not limited thereto, and, for example, the controlling a gel form (3) may be performed during the process (1)
- the gelled silicon compound obtained by the above gelation treatment was subjected to an aging treatment by incubating it at 40° C. for 20 hours. Thus, a cuboid gel mass was obtained.
- the gel (gelled silicon compound) obtained after the replacing a solvent (4) was subjected to a total of two stages of pulverization including a first pulverization stage by continuous emulsification dispersion (Milder MDN304, manufactured by Pacific Machinery & Engineering Co., Ltd.) and a second pulverization stage by high pressure media-less pulverization (Star Burst HJP-25005, manufactured by Sugino Machine Limited).
- This pulverization treatment was performed in the following manner. First, 43.4 kg of the gel containing a gelled silicon compound having been subjected to solvent replacement was prepared, 26.2 kg of isobuyl alcohol was added to this gel, and the mixture was then weighed.
- methyl isobutyl ketone having 1.5% WPBG-266 product name, manufactured by Wako Pure Chemical Industries, Ltd.
- 67.2 g of methyl isobutyl ketone having 5% bis(trimethoxylyl)ethane manufactured by Tokyo Chemical Industry Co., Ltd.
- 31.8 g of N,N-dimethylformamide was added and mixed, thereby obtaining a gel pulverized product-containing liquid.
- IPA isopropyl alcohol
- MIBK-ST product name of Nissan Chemical Corporation: Si nanoparticle MIBK [methyl isobutyl ketone] dispersion liquid
- trimethoxy(1H,1H,2H,2H-nonafluorohexyl)silane was added.
- the mixture thus obtained was heated and stirred at 60° C. for 1 hour to perform the modification reaction of the Si nanoparticles, thereby obtaining a fluoroalkyl group-modified Si nanoparticle dispersion liquid (modified nanoparticle dispersion liquid).
- a coating solution for forming void-containing layer was prepared in the same manner as in Reference Example 1 except that 94 mass % of MTMS and 6 mass % of vinyltrimethoxysilane (manufactured by Tokyo Chemical Industry Co., Ltd. (TCI)) were used instead of the total mass (100 mass %) of MTMS of Reference Example 1 (that is, 6 mass % of MTMS was replaced with vinyltrimethoxysilane).
- a pressure-sensitive adhesive/adhesive coating solution was prepared as follows. In addition, the pressure-sensitive adhesive/adhesive coating solution was used to produce a pressure-sensitive adhesive/adhesive layer.
- an isocyanate-based crosslinking agent product name: “Coronate L” manufactured by Nippon Polyurethane Industry Co., Ltd., an adduct of trimethylolpropane with trilene diisocyanate
- benzoyl peroxide product name: “NYPER BMT” manufactured by NOF CORPORATION
- ⁇ -glycidoxypropylmethoxysilane product name: “KBM-403” manufactured by Shin-Etsu Chemical Co., Ltd.
- 8 parts of N-acryloylmorpholine were added, thereby preparing an acrylic pressure-sensitive adhesive solution.
- N-acryloyhnorpholine corresponds to “a monomer having one or two reactive double bonds per molecule”.
- N-acryloyhnorpholine is a monomer having one reactive double bond per molecule.
- the acrylic pressure-sensitive adhesive solution prepared as described above was coated onto one side of a silicone-treated polyethylene terephthalate (PET) film (manufactured by Mitsubishi Chemical Polyester Film Corporation, thickness: 38 ⁇ m) so that the thickness of the pressure-sensitive adhesive layer after being dried achieves 10 ⁇ m, and the coated acrylic pressure-sensitive adhesive composition was dried at 150° C. for 3 minutes, thereby producing a pressure-sensitive adhesive/adhesive layer of the present Reference Example.
- PET polyethylene terephthalate
- the storage elastic modulus G′ of the pressure-sensitive adhesive/adhesive layer at 23° C. was 1.3 ⁇ 10.
- a pressure-sensitive adhesive/adhesive coating solution was prepared as follows. In addition, the pressure-sensitive adhesive/adhesive coating solution was used to produce a pressure-sensitive adhesive/adhesive layer.
- the acrylic polymer solution the same as Reference Example 3 was prepared in the same manner as in Reference Example 3, “Production of Acrylic Polymer”.
- an isocyanate-based crosslinking agent product name: “Coronate L” manufactured by Nippon Polyurethane Industry Co., Ltd., an adduct of trimethylolpropane with trilene diisocyanate
- benzoyl peroxide product name: “NYPER BMT” manufactured by NOF CORPORATION
- ⁇ -glycidoxypropylmethoxysilane product name: “KBM-403” manufactured by Shin-Etsu Chemical Co., Ltd.
- an acrylic pressure-sensitive adhesive solution was prepared in the same manner as in “Preparation of pressure-sensitive adhesive/adhesive coating solution” of Reference Example 3 except that no N-acryloylmorpholine was added and the quantity of benzoyl peroxide was changed.
- the acrylic pressure-sensitive adhesive solution prepared as described above was coated onto one side of a silicone-treated polyethylene terephthalate (PET) film (manufactured by Mitsubishi Chemical Polyester Film Corporation, thickness: 38 ⁇ m) so that the thickness of the pressure-sensitive adhesive layer after being dried achieves 10 ⁇ m, and the coated acrylic pressure-sensitive adhesive composition was dried at 150° C. for 3 minutes, thereby producing a pressure-sensitive adhesive/adhesive layer of the present Reference Example.
- PET polyethylene terephthalate
- the pressure-sensitive adhesive/adhesive layer of the present Reference Example was produced in the same manner as “Production of pressure-sensitive adhesive/adhesive layer” of Reference Example 3 except that the acrylic pressure-sensitive adhesive solution of the present Reference Example (Reference Example 4) was used instead of the acrylic pressure-sensitive adhesive solution of the Reference Example 3.
- the storage elastic modulus G′ of the pressure-sensitive adhesive/adhesive layer at 23° C. was 1.3 ⁇ 10 3 .
- the coating solution for forming void-containing layer prepared in Reference Example 1 was coated onto an acrylic base and then dried to form a high void fraction layer (void fraction: 59 vol %) having a thickness of about 850 nm.
- void fraction void fraction: 59 vol %
- UV irradiation 450 mJ/cm 2
- the pressure-sensitive adhesive/adhesive layer having a thickness of 10 nm obtained in Reference Example 3 was attached to the high void fraction layer surface, and aging was performed at 50° C. for 30 hours to produce a laminate of the present invention in which a pressure-sensitive adhesive/adhesive layer was directly laminated on one side of a void-containing layer.
- the produced laminate of the present invention was subjected to a heat/humidification durability test for 1000 hours in an oven at 60° C. and at 90% RH.
- the amounts of the refractive index change before and after the heat/humidification durability test were measured and compared. The results are shown in Table 1.
- a laminate in which a pressure-sensitive adhesive/adhesive layer was directly laminated on one side of a void-containing layer was produced in the same manner as in Example 1 except that the pressure-sensitive adhesive/adhesive layer of Reference Example 4 was used instead of the pressure-sensitive adhesive/adhesive layer of Reference Example 3. Further, in the same manner as described in Example 1, the produced laminate was subjected to a heat/humidification durability test for 1000 hours in an oven at 60° C. and 90% RH. The refractive index change amounts before and after the heat/humidification durability test were measured and compared. The results are shown in Table 1.
- a laminate in which a pressure-sensitive adhesive/adhesive layer was directly laminated on one side of a void-containing layer was produced in the same manner as in Example 1 except that the ratio of MTMS and vinyl trimethoxysilane in the coating solution for forming void-containing layer of Reference Example 2 was changed to 97 mass % of MTMS and 3 mass % of vinyl trimethoxysilane. Further, in the same manner as described in Example 1, the produced laminate was subjected to a heat/humidification durability test for 1000 hours in an oven at 60° C. and 90% RH. The refractive index change amounts before and after the heat/humidification durability test were measured and compared. The results are shown in Table 1.
- a laminate in which a pressure-sensitive adhesive/adhesive layer was directly laminated on one side of a void-containing layer was produced in the same manner as in Example 1 except that the ratio of MTMS and vinyl trimethoxysilane in the coating solution for forming void-containing layer of Reference Example 2 was changed to 90 mass % of MTMS and 10 mass % of vinyl trimethoxysilane. Further, in the same manner as described in Example 1, the produced laminate was subjected to a heat/humidification durability test for 1000 hours in an oven at 60° C. and 90% RH. The refractive index change amounts before and after the heat/humidification durability test were measured and compared. The results are shown in Table 1.
- a laminate in which a pressure-sensitive adhesive/adhesive layer was directly laminated on one side of a void-containing layer was produced in the same manner as in Example 2 except that the coating solution for forming void-containing layer of Reference Example 1 was used instead of the coating solution for forming void-containing layer of Reference Example 2. Further, in the same manner as described in Example 1, the produced laminate was subjected to a heat/humidification durability test for 1000 hours in an oven at 60° C. and 90% RH. The refractive index change amounts before and after the heat/humidification durability test were measured and compared. The results are shown in Table 1.
- a laminate in which a pressure-sensitive adhesive/adhesive layer was directly laminated on one side of a void-containing layer was produced in the same manner as in Example 1 except that the ratio of MTMS and vinyl trimethoxysilane in the coating solution for forming void-containing layer was changed to 50 mass % of MTMS and 50 mass % of vinyl trimethoxysilane. Further, in the same manner as described in Example 1, the produced laminate was subjected to a heat/humidification durability test for 1000 hours in an oven at 60° C. and 90% RH. The refractive index change amounts before and after the heat/humidification durability test were measured and compared. The results are shown in Table 1.
- the “void retention rate before and after durability test” represents a numerical value obtained by dividing the void fraction (vol %) of the void-containing layer after the heat/humidification durability test by the void fraction (vol %) of the void-containing layer before the heat/humidification durability test.
- the “introduced double bond” represents the content (mass %) of vinyltrimethoxysilane relative to the sum of the total mass of MTMS and vinyltrimethoxysilane in the coating solution for forming void-containing layer.
- the void fraction of the void-containing layer was as high as 52 vol % or more in all the laminates of Examples and Comparative Examples, and consequently, the refractive index of the void-containing layer was as low as 1.20 or less.
- the void retention rate of the void-containing layer was high in all the laminates of the Examples, and consequently, the refractive index of the void-containing layer was maintained as low as 1.21 or less.
- the present invention can provide avoid-containing layer in which a pressure-sensitive adhesive or an adhesive is less liable to penetrate into voids, a laminate including the void-containing layer, a method for producing the void-containing layer, and an optical member and an optical apparatus including the void-containing layer.
- the application of the present invention is not particularly limited.
- the optical apparatus of the present invention is not particularly limited, and may be an image display device, an illumination device, or the like. Examples of the image display device include a liquid crystal display, an organic EL display, and a micro LED display.
- the illumination device may be, for example, an organic EL illumination, or the like.
- the application of the void-containing layer and the laminate of the present invention is not limited to the optical member and the optical apparatus of the present invention, and can be used in a wide range of applications.
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2021011080 | 2021-01-27 | ||
JP2021-011080 | 2021-01-27 | ||
PCT/JP2022/002704 WO2022163655A1 (ja) | 2021-01-27 | 2022-01-25 | 空隙層、積層体、空隙層の製造方法、光学部材および光学装置 |
Publications (1)
Publication Number | Publication Date |
---|---|
US20240101870A1 true US20240101870A1 (en) | 2024-03-28 |
Family
ID=82654664
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US18/274,070 Pending US20240101870A1 (en) | 2021-01-27 | 2022-01-25 | Void-containing layer, laminate, method for producing void-containing layer, optical member, and optical apparatus |
Country Status (7)
Country | Link |
---|---|
US (1) | US20240101870A1 (ja) |
EP (1) | EP4276499A1 (ja) |
JP (1) | JPWO2022163655A1 (ja) |
KR (1) | KR20230138461A (ja) |
CN (1) | CN116745656A (ja) |
TW (1) | TW202243866A (ja) |
WO (1) | WO2022163655A1 (ja) |
Family Cites Families (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH1062626A (ja) | 1996-06-12 | 1998-03-06 | Nissha Printing Co Ltd | 面発光装置とその製造方法 |
JP2008256747A (ja) * | 2007-03-30 | 2008-10-23 | Fujifilm Corp | 偏光板用保護フィルム、及びその製造方法、偏光板、並びに液晶表示装置 |
JP5411477B2 (ja) * | 2008-09-30 | 2014-02-12 | 積水化学工業株式会社 | 中空有機−無機ハイブリッド微粒子、反射防止性樹脂組成物、反射防止フィルム用コーティング剤、反射防止積層体及び反射防止フィルム |
JP2012156082A (ja) | 2011-01-28 | 2012-08-16 | Furukawa Electric Co Ltd:The | バックライトパネル、導光板、反射板、および接着シート |
US20130337161A1 (en) * | 2011-02-21 | 2013-12-19 | Asahi Kasei Chemicals Corporation | Coating Material Containing Organic/Inorganic Composite, Organic/Inorganic Composite Film and Antireflection Member |
JP5907839B2 (ja) | 2012-08-30 | 2016-04-26 | 旭化成ケミカルズ株式会社 | 積層体、偏光板、光学材料、表示装置及びタッチパネル |
JP6573445B2 (ja) * | 2014-10-22 | 2019-09-11 | 旭化成株式会社 | 光学塗膜、光学塗膜の製造方法、及び反射防止膜 |
JP6713871B2 (ja) * | 2015-07-31 | 2020-06-24 | 日東電工株式会社 | 光学積層体、光学積層体の製造方法、光学部材、画像表示装置、光学部材の製造方法および画像表示装置の製造方法 |
WO2019065999A1 (ja) * | 2017-09-29 | 2019-04-04 | 日東電工株式会社 | 積層体、光学部材および光学装置 |
JP2020152873A (ja) * | 2019-03-22 | 2020-09-24 | 株式会社カネカ | 硬化物、硬化物の製造方法、硬化性樹脂組成物および硬化物の利用 |
JP6738107B1 (ja) | 2019-07-08 | 2020-08-12 | 株式会社Tbm | 印刷用シート及び印刷用シートの製造方法 |
-
2022
- 2022-01-25 WO PCT/JP2022/002704 patent/WO2022163655A1/ja active Application Filing
- 2022-01-25 KR KR1020237025018A patent/KR20230138461A/ko unknown
- 2022-01-25 EP EP22745875.9A patent/EP4276499A1/en active Pending
- 2022-01-25 JP JP2022578412A patent/JPWO2022163655A1/ja active Pending
- 2022-01-25 CN CN202280011761.XA patent/CN116745656A/zh active Pending
- 2022-01-25 US US18/274,070 patent/US20240101870A1/en active Pending
- 2022-01-26 TW TW111103387A patent/TW202243866A/zh unknown
Also Published As
Publication number | Publication date |
---|---|
EP4276499A1 (en) | 2023-11-15 |
JPWO2022163655A1 (ja) | 2022-08-04 |
TW202243866A (zh) | 2022-11-16 |
CN116745656A (zh) | 2023-09-12 |
KR20230138461A (ko) | 2023-10-05 |
WO2022163655A1 (ja) | 2022-08-04 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US11420413B2 (en) | Laminate, optical member, and optical apparatus | |
US11396614B2 (en) | Void-containing layer, laminate, method for producing void-containing layer, optical member, and optical apparatus | |
JP7182358B2 (ja) | 低屈折率層含有粘接着シート、低屈折率層含有粘接着シートの製造方法、および光学デバイス | |
JP2024001067A (ja) | 積層体、光学部材および光学装置 | |
US11402569B2 (en) | Optical sheet for light guide plate type liquid crystal display, backlight unit for light guide plate type liquid crystal display, and light guide plate type liquid crystal display | |
WO2018142813A1 (ja) | 低屈折率層含有粘接着シート、低屈折率層含有粘接着シートの製造方法、および光学デバイス | |
US20240101870A1 (en) | Void-containing layer, laminate, method for producing void-containing layer, optical member, and optical apparatus | |
WO2023053913A1 (ja) | 積層体、積層体の製造方法、光学部材、光学装置、光学部材の製造方法、及び光学装置の製造方法 | |
JP2022114690A (ja) | 積層体、粘接着剤塗工液の製造方法、粘接着剤塗工液、粘接着剤層の製造方法、積層体の製造方法、光学部材、光学装置、光学部材の製造方法、および光学装置の製造方法 | |
WO2023190103A1 (ja) | 積層体、光学部材、及び光学装置 | |
WO2023053912A1 (ja) | 積層体、光学部材、及び光学装置 | |
JP2023051690A (ja) | 積層体、光学部材、及び光学装置 | |
CN118043195A (en) | Laminate, method for producing laminate, optical member, optical device, method for producing optical member, and method for producing optical device |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
STPP | Information on status: patent application and granting procedure in general |
Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION |