US20220274836A1 - Carbon nanotube production device and production method - Google Patents

Carbon nanotube production device and production method Download PDF

Info

Publication number
US20220274836A1
US20220274836A1 US17/632,730 US202017632730A US2022274836A1 US 20220274836 A1 US20220274836 A1 US 20220274836A1 US 202017632730 A US202017632730 A US 202017632730A US 2022274836 A1 US2022274836 A1 US 2022274836A1
Authority
US
United States
Prior art keywords
raw material
catalyst raw
temperature
catalyst
material supplying
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
US17/632,730
Other languages
English (en)
Inventor
Suguru Noda
Katsuya NAMIKI
Zihao Zhang
Toshio Osawa
Hisashi Sugime
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Waseda University
Meijo Nano Carbon Co Ltd
Original Assignee
Waseda University
Meijo Nano Carbon Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Waseda University, Meijo Nano Carbon Co Ltd filed Critical Waseda University
Assigned to MEIJO NANO CARBON CO., LTD., WASEDA UNIVERSITY reassignment MEIJO NANO CARBON CO., LTD. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: NAMIKI, Katsuya, ZHANG, ZIHAO, OSAWA, TOSHIO, NODA, SUGURU, SUGIME, HISASHI
Publication of US20220274836A1 publication Critical patent/US20220274836A1/en
Pending legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
    • C01B32/00—Carbon; Compounds thereof
    • C01B32/15—Nano-sized carbon materials
    • C01B32/158—Carbon nanotubes
    • C01B32/159—Carbon nanotubes single-walled
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J19/00—Chemical, physical or physico-chemical processes in general; Their relevant apparatus
    • B01J19/26—Nozzle-type reactors, i.e. the distribution of the initial reactants within the reactor is effected by their introduction or injection through nozzles
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J4/00—Feed or outlet devices; Feed or outlet control devices
    • B01J4/001—Feed or outlet devices as such, e.g. feeding tubes
    • B01J4/002—Nozzle-type elements
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J4/00—Feed or outlet devices; Feed or outlet control devices
    • B01J4/008—Feed or outlet control devices
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J6/00—Heat treatments such as Calcining; Fusing ; Pyrolysis
    • B01J6/008—Pyrolysis reactions
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
    • C01B32/00—Carbon; Compounds thereof
    • C01B32/15—Nano-sized carbon materials
    • C01B32/158—Carbon nanotubes
    • C01B32/16—Preparation
    • C01B32/162—Preparation characterised by catalysts
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J2204/00—Aspects relating to feed or outlet devices; Regulating devices for feed or outlet devices
    • B01J2204/002—Aspects relating to feed or outlet devices; Regulating devices for feed or outlet devices the feeding side being of particular interest
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J2219/00—Chemical, physical or physico-chemical processes in general; Their relevant apparatus
    • B01J2219/00049—Controlling or regulating processes
    • B01J2219/00051—Controlling the temperature
    • B01J2219/00074—Controlling the temperature by indirect heating or cooling employing heat exchange fluids
    • B01J2219/00119—Heat exchange inside a feeding nozzle or nozzle reactor
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J2219/00—Chemical, physical or physico-chemical processes in general; Their relevant apparatus
    • B01J2219/00049—Controlling or regulating processes
    • B01J2219/00051—Controlling the temperature
    • B01J2219/00132—Controlling the temperature using electric heating or cooling elements
    • B01J2219/00135—Electric resistance heaters
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B82—NANOTECHNOLOGY
    • B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
    • B82Y30/00—Nanotechnology for materials or surface science, e.g. nanocomposites
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B82—NANOTECHNOLOGY
    • B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
    • B82Y40/00—Manufacture or treatment of nanostructures
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
    • C01B2202/00—Structure or properties of carbon nanotubes
    • C01B2202/20—Nanotubes characterized by their properties
    • C01B2202/30—Purity
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
    • C01B2202/00—Structure or properties of carbon nanotubes
    • C01B2202/20—Nanotubes characterized by their properties
    • C01B2202/36—Diameter

Definitions

  • the present invention relates to a device and method for producing carbon nanotubes.
  • FCCVD floating catalyst chemical vapor deposition
  • the object of this method is to generate, at a high density, catalyst metal particles with a small diameter in a space by decomposing the organic metal compound in a short period of time, and attempts were also made in this method to improve the quality of CNTs synthesized and increase the yield thereof (e.g. Non-patent document 1).
  • a catalyst metal vapor is to be generated by decomposing a catalyst raw material with a premixed flame, followed by generating catalyst metal nanoparticles by mixing the catalyst metal vapor with a carrier gas and a carbon raw material gas so as to continuously synthesizing single-walled CNTs (e.g. Patent document 1).
  • the problem with the CNT synthesis method disclosed in the non-patent document 1 is as follows. That is, since heating is performed from outside the catalyst raw material supplying nozzle with the tungsten wire, while the temperature of an inner portion of the alumina-made catalyst raw material supplying nozzle can be raised to a temperature of the same level as the temperature of a reaction field of the synthesis furnace, it is difficult to set the temperature of the inner portion higher than the temperature of the reaction field, which makes it impossible to heat the catalyst raw material flowing through the catalyst raw material supplying nozzle to a sufficiently high temperature. Further, since the alumina-made catalyst raw material supplying nozzle is to be heated to a high temperature, there is also a problem that the alumina component of the catalyst raw material supplying nozzle will mix into the CNTs synthesized.
  • the problem with the CNT synthesis method disclosed in the patent document 1 is that it is difficult to improve a productivity, because an excessive amount of oxygen (O 2 ), water vapor (H 2 O) and carbon dioxide (CO 2 ) will mix into a raw material for synthesizing CNTs, and the number of the catalyst metal nanoparticles by which CNTs do not grow will thus increase.
  • O 2 oxygen
  • H 2 O water vapor
  • CO 2 carbon dioxide
  • the present invention was made in view of these circumstances, and provides a carbon nanotube production device and production method capable of improving the quality and yield of CNTs synthesized by a reaction of catalyst metal particles and a carbon raw material, where a catalyst raw material is to be thermally decomposed by raising the temperature of the catalyst raw material in a catalyst raw material supplying nozzle to a high temperature, the thermally decomposed catalyst raw material is then supplied to a synthesis furnace to be rapidly cooled to a chemical vapor deposition (CVD) temperature as a CNT growth temperature band so as to generate microscopic catalyst metal particles, and an agglutination caused by the collision between these microscopic catalyst metal particles is inhibited.
  • CVD chemical vapor deposition
  • the present invention provides a carbon nanotube production device including:
  • a catalyst raw material supplying nozzle for supplying a catalyst raw material used to synthesize the carbon nanotubes to the synthesis furnace
  • a nozzle temperature adjusting unit capable of setting a temperature of an inner portion of the catalyst raw material supplying nozzle higher than a temperature of a reaction field of the synthesis furnace.
  • the production device may be such that the temperature of the inner portion of the catalyst raw material supplying nozzle is a temperature at which the catalyst raw material thermally decomposes to generate a catalyst metal vapor; the temperature of the reaction field of the synthesis furnace is a temperature at which catalyst metal particles are generated, and CNTs are generated.
  • the nozzle temperature adjusting unit may be provided inside the catalyst raw material supplying nozzle.
  • the nozzle temperature adjusting unit may be a heater.
  • the heater may be composed of carbon, and may be electrically heated to adjust the temperature of the inner portion of the catalyst raw material supplying nozzle.
  • the production device of the present invention there may be provided a plurality of the catalyst raw material supplying nozzles.
  • a carbon raw material flow passage for flowing a carbon raw material therethrough may be provided outside an outer circumferential portion of the catalyst raw material supplying nozzle.
  • the present invention provides a carbon nanotube production method wherein a catalyst raw material is heated by setting a temperature of an inner portion of a catalyst raw material supplying nozzle for supplying the catalyst raw material used to synthesize carbon nanotubes to a synthesis furnace higher than a temperature of a reaction field of the synthesis furnace for synthesizing the carbon nanotubes.
  • the temperature of the inner portion of the catalyst raw material supplying nozzle may be adjusted by a nozzle temperature adjusting unit provided inside the catalyst raw material supplying nozzle.
  • the present invention can provide a carbon nanotube production device and production method capable of improving the quality and yield of CNTs synthesized, by setting the temperature of the inner portion of the catalyst raw material supplying nozzle higher than the temperature of the reaction field of the synthesis furnace.
  • FIG. 1 is a schematic view showing a carbon nanotube production device of an embodiment of the present invention.
  • FIG. 2 is a schematic view partially showing an example of a configuration of a carbon nanotube production device of a working example 1 of the present invention.
  • FIG. 3 is a schematic view showing a nozzle temperature adjusting unit of the working example 1 of the present invention.
  • FIG. 4 is a schematic view showing a catalyst raw material supplying nozzle of a comparative example 1.
  • FIG. 5 is a schematic view showing a catalyst raw material supplying nozzle and a coil for electric heating of a comparative example 2.
  • FIG. 6 is a graph showing a temperature distribution in a depth direction of an inner portion of the catalyst raw material supplying nozzle of the working example 1 and the comparative example 2 of the present invention.
  • FIG. 7 is a photograph of CNTs produced in the working example 1 of the present invention.
  • FIG. 8 is a graph showing a CNT productivity and EDS quantitative analysis results of residues obtained after thermogravimetry differential thermal analysis in the working example 1, comparative example 1 and comparative example 2 of the present invention.
  • FIG. 9 is a diagram showing a Raman spectrum of CNTs produced in the working example 1, comparative example 1 and comparative example 2 of the present invention.
  • FIG. 10 is a set of diagrams showing thermogravimetry differential thermal analysis results of the CNTs produced in the working example 1, comparative example 1 and comparative example 2 of the present invention.
  • FIG. 11 is a set of images including a SEM image ( FIG. 11A ) and TEM image ( FIG. 11B ) of the CNTs produced in the working example 1 of the present invention.
  • FIG. 12 is a diagram showing a Raman spectrum of CNTs produced in a working example 2a of the present invention.
  • FIG. 13 is a SEM image of the CNTs produced in the working example 2a of the present invention.
  • FIG. 14 is a diagram showing a Raman spectrum of CNTs produced in a working example 2b of the present invention.
  • FIG. 15 is a SEM image of the CNTs produced in the working example 2b of the present invention.
  • FIG. 16 is a diagram showing a Raman spectrum of CNTs produced in a working example 2c of the present invention.
  • FIG. 17 is a SEM image of the CNTs produced in the working example 2c of the present invention.
  • FIG. 18 is a diagram showing a Raman spectrum of CNTs produced in a working example 2d of the present invention.
  • FIG. 19 is a SEM image of the CNTs produced in the working example 2d of the present invention.
  • FIG. 20 is a diagram showing a Raman spectrum of CNTs produced in a working example 2e of the present invention.
  • FIG. 21 is a SEM image of the CNTs produced in the working example 2e of the present invention.
  • FIG. 22 is a diagram showing a thermogravimetry differential thermal analysis result of the CNTs produced in the working example 2e of the present invention.
  • FIG. 23 is a diagram showing a Raman spectrum of CNTs produced in a working example 2f of the present invention.
  • FIG. 24 is a SEM image of the CNTs produced in the working example 2f of the present invention.
  • FIG. 25 is a diagram showing a thermogravimetry differential thermal analysis result of the CNTs produced in the working example 2f of the present invention.
  • FIG. 26 is a diagram showing a Raman spectrum of CNTs produced in a working example 2g of the present invention.
  • FIG. 27 is a SEM image of the CNTs produced in the working example 2g of the present invention.
  • FIG. 28 is a diagram showing a Raman spectrum of CNTs produced in a working example 2h of the present invention.
  • FIG. 29 is a SEM image of the CNTs produced in the working example 2h of the present invention.
  • FIG. 30 is a diagram showing a thermogravimetry differential thermal analysis result of the CNTs produced in the working example 2h of the present invention.
  • FIG. 31 is a schematic view partially showing an example of a configuration of a carbon nanotube production device of a working example 3 of the present invention.
  • FIG. 32 is a side cross-sectional view partially showing an example of the CNT production device of the working example 3 of the present invention that is configured to have a plurality of catalyst raw material supplying nozzles.
  • FIG. 33 is a top cross-sectional view of the production device, showing an example of the configuration of the working example 3 of the present invention that has a plurality of the catalyst raw material supplying nozzles, where the catalyst raw material supplying nozzles are integrally formed by boring a plurality of holes in a heat insulation material.
  • FIG. 34 is a top cross-sectional view of the production device, showing an example of the configuration of the working example 3 of the present invention that has a plurality of the catalyst raw material supplying nozzles, where the catalyst raw material supplying nozzles are separately formed using individual heat insulation materials.
  • FIG. 1 is a schematic view showing a carbon nanotube production device 1 of the present embodiment.
  • This production device 1 includes a synthesis furnace 2 for synthesizing carbon nanotubes; a catalyst raw material supplying nozzle 3 for supplying a catalyst raw material used to synthesize carbon nanotubes to the synthesis furnace 2 ; and a nozzle temperature adjusting unit 6 capable of setting a temperature of an inner portion 4 of the catalyst raw material supplying nozzle 3 higher than a temperature of a reaction field 5 of the synthesis furnace 2 .
  • a catalyst raw material supplying portion 11 for supplying the catalyst raw material and a cocatalyst if necessary is connected to the catalyst raw material supplying nozzle 3 through a catalyst raw material supplying tube 14 .
  • a carbon raw material supplying portion 12 for supplying a carbon raw material is connected to a carbon raw material supplying tube 15 .
  • an inert gas supplying tube 16 is connected to an inert gas supplying portion 13 for supplying, if necessary, an inert gas such as argon (Ar) used for purging.
  • the synthesis furnace 2 is formed of a cylindrical container made of, for example, quartz glass, ceramics or stainless steel.
  • the reaction field 5 of the synthesis furnace 2 is a region where CNTs grow.
  • the catalyst raw material and cocatalyst are to be supplied from the catalyst raw material supplying portion 11 to the catalyst raw material supplying nozzle 3 through the catalyst raw material supplying tube 14 , in the form of a vapor after being sublimated, and using argon (Ar) or the like as a carrier gas. Since the temperature of the inner portion 4 of the catalyst raw material supplying nozzle 3 is set in such a manner that heating therein shall take place at a temperature higher than the temperature of the reaction field 5 of the synthesis furnace 2 , the catalyst raw material will be subjected to a rapid temperature rise and thermally decomposed inside the catalyst raw material supplying nozzle 3 . The thermally decomposed catalyst raw material will then be rapidly cooled to a CVD temperature at the synthesis furnace 2 to form catalyst metal particles; carbon nanotubes will then be produced by having these catalyst metal particles react with the carbon raw material.
  • the catalyst raw material is heated to a temperature (e.g. 1,400° C. or higher as the temperature of the inner portion 4 of the catalyst raw material supplying nozzle 3 ) higher than the temperature of the reaction field 5 of the synthesis furnace 2 in a short period of time (e.g. 10 msec or shorter), thereby allowing the catalyst raw material to be supplied to the synthesis furnace while decomposing the same and inhibiting the generation of the catalyst metal particles.
  • a temperature e.g. 1,400° C. or higher as the temperature of the inner portion 4 of the catalyst raw material supplying nozzle 3
  • a short period of time e.g. 10 msec or shorter
  • a catalyst metal vapor will be cooled to the CVD temperature (e.g. 1,200° C. or lower) as the temperature of the reaction field 5 of the synthesis furnace 2 such that nuclei of metal particles will be generated, and that microscopic catalyst metal particles will then be generated at a high density in the space of the reaction field 5 of the synthesis furnace 2 , thus allowing CNTs with a small diameter to be vapor-grown at a high density without permitting time for the catalyst metal particles to agglutinate.
  • the CVD temperature e.g. 1,200° C. or lower
  • the catalyst raw material there can be used a material containing, as a catalyst component(s), at least one metal element selected from iron (Fe), cobalt (Co), nickel (Ni), molybdenum (Mo), yttrium (Y) and copper (Cu).
  • iron (Fe) is particularly preferred;
  • ferrocene (Fe(C 5 H 5 ) 2 ) is particularly preferred as the catalyst raw material.
  • S is preferred as the cocatalyst.
  • a sulfur source there may be used, for example, sulfur, thiophene and hydrogen sulfide. Sulfur is expected to bring about an effect of stably forming small catalyst metal particles, and promoting carbon precipitation from the iron catalyst metal particles.
  • the cocatalyst is not an essential component.
  • the carbon raw material is to be supplied from the carbon raw material supplying portion 12 to the synthesis furnace 2 through the carbon raw material supplying tube 15 , as a carbon source gas.
  • the carbon raw material include methane (CH 4 ), acetylene (C 2 H 2 ), ethylene (C 2 H 4 ), toluene (C 6 H 5 CH 3 ) and ethanol (C 2 H 5 OH); in the present invention, methane (CH 4 ) and ethylene (C 2 H 4 ) are particularly preferred as they are capable of inhibiting the occurrence of impurities such as tar.
  • the carbon raw material can, for example, be supplied to the synthesis furnace 2 together with a carrier gas such as argon (Ar) and hydrogen (H 2 ).
  • the carbon raw material flows from top down in the carbon raw material supplying tube 15 provided at an upper outer circumferential portion of the synthesis furnace 2 , and is then horizontally supplied to the synthesis furnace 2 from a carbon raw material flow outlet 19 provided at a side portion of the synthesis furnace 2 .
  • a method for supplying the carbon raw material so long as the method allows the carbon raw material and the decomposed catalyst raw material supplied from the catalyst raw material supplying nozzle 3 to be mixed in the reaction field 5 of the synthesis furnace 2 .
  • a carbon raw material flow passage 17 for flowing the carbon raw material therethrough may be provided outside an outer circumferential portion of the catalyst raw material supplying nozzle 3 .
  • the carbon raw material is preheated utilizing the heat discharged from the nozzle temperature adjusting unit 6 , and then supplied to the synthesis furnace 2 after the rise in temperature, thereby allowing the reaction field 5 to maintain a high temperature.
  • the thermally decomposed catalyst raw material and the preheated carbon raw material can be swiftly mixed together.
  • the CNT production device 1 may also be configured in a manner where there are provided a plurality of the catalyst raw material supplying nozzles 3 .
  • the CNT production device 1 can be scaled up to a large device such as those used in a plant so that productivity can be improved as a mass production facility.
  • a specific configuration example of the CNT production device 1 having a plurality of the catalyst raw material supplying nozzles 3 is described later.
  • the nozzle temperature adjusting unit 6 there may be employed, for example, a unit for heating the inner portion 4 of the catalyst raw material supplying nozzle 3 from within the catalyst raw material supplying nozzle 3 . Further, there are no particular restrictions on the unit as the nozzle temperature adjusting unit 6 for heating the inner portion 4 of the catalyst raw material supplying nozzle 3 so long as the temperature of the inner portion 4 of the catalyst raw material supplying nozzle 3 can be set to a temperature that is sufficiently higher than the temperature of the reaction field 5 of the synthesis furnace 2 ; for example, the inner portion 4 of the catalyst raw material supplying nozzle 3 may be heated from outside the catalyst raw material supplying nozzle 3 .
  • the nozzle temperature adjusting unit 6 as a unit for performing heating from within the catalyst raw material supplying nozzle 3 , the nozzle temperature adjusting unit 6 can be provided inside the catalyst raw material supplying nozzle 3 . In such case, since the catalyst raw material flowing through the catalyst raw material supplying nozzle 3 can be directly heated by the nozzle temperature adjusting unit 6 , the catalyst raw material can be decomposed in a short period of time. Further, the catalyst raw material supplying nozzle 3 can be prevented from being damaged by the heat generated from the nozzle temperature adjusting unit 6 .
  • this unit may also be used in combination with a unit for performing heating from within the catalyst raw material supplying nozzle 3 .
  • a ceramic heat transfer rod (see FIG. 2 and FIG. 3 ), for example, may be installed inside the catalyst raw material supplying nozzle 3 such that the heat transfer rod will be heated by a radiation from within the catalyst raw material supplying nozzle 3 .
  • the catalyst raw material supplying nozzle 3 Since the inner portion 4 of the catalyst raw material supplying nozzle 3 will be evenly heated both from within the catalyst raw material supplying nozzle 3 and by the surface of the heat transfer rod, the catalyst raw material can be thermally decomposed in a short period of time, and then by cooling such catalyst raw material to the CVD temperature at the reaction field 5 of the synthesis furnace 2 , the catalyst metal particles can be generated at a high density in the space.
  • the nozzle temperature adjusting unit 6 may also be a heater 7 (see FIG. 31 ).
  • the heater 7 is composed of carbon, and is electrically heated so as to raise the temperature of the inner portion 4 of the catalyst raw material supplying nozzle 3 , where the temperature of the inner portion 4 of the catalyst raw material supplying nozzle 3 is adjusted by changing the amount of electricity conducted.
  • the temperature of the catalyst raw material can be raised to a high temperature at which the catalyst metal will not yet be condensed, and while reliably inhibiting the generation of the catalyst metal particles at the nozzle inner portion 4 of the catalyst raw material supplying nozzle 3 , by cooling the catalyst metal vapor to the CVD temperature at the reaction field 5 of the synthesis furnace 2 , the catalyst metal particles can be generated at a high density in the space.
  • a heat retention unit 8 for controlling the temperature of the reaction field 5 of the synthesis furnace 2 be provided, for example, outside an outer circumferential portion of the synthesis furnace 2 .
  • the heat retention unit 8 may, for example, be a heating furnace such as an electric furnace performing heating by passing an electric current through nichrome wires, a ceramic heat generating body or the like; or a heat insulation material provided to cover the outer circumferential portion of the synthesis furnace 2 .
  • the temperature of the reaction field 5 of the synthesis furnace 2 is preferably retained in a range of 800 to 1,300° C., more preferably 1,000 to 1,200° C., in order to, for example, suit the growth of carbon nanotubes.
  • the heat retention unit 8 serves to manage the temperature of the reaction field 5 of the synthesis furnace 2 so as to maintain a growth temperature of CNT and achieve a longer growth time thereof.
  • the inventors of the present invention have confirmed that high-quality single-walled carbon nanotubes (SWCNT) can be synthesized by mixing the heated catalyst raw material and the carbon raw material with the temperature of the heat retention unit 8 being 1,150 to 1,200° C.
  • the temperature of the inner portion 4 of the catalyst raw material supplying nozzle 3 for supplying the catalyst raw material to the synthesis furnace 2 may be set higher than the temperature of the reaction field 5 of the synthesis furnace 2 .
  • the temperature of the inner portion 4 of the catalyst raw material supplying nozzle 3 is a temperature at which the catalyst raw material thermally decomposes; particularly, it may be a temperature at which the catalyst raw material thermally decomposes to generate the catalyst metal vapor.
  • the temperature of the reaction field 5 of the synthesis furnace 2 may be a temperature at which the catalyst metal particles are generated, and CNTs are generated.
  • the temperature of the inner portion 4 of the catalyst raw material supplying nozzle 3 be a temperature at which the catalyst metal vapor will not be condensed.
  • a temperature at which the catalyst metal vapor will not be condensed For example, when supplying an argon (Ar) gas containing 0.4 Pa of ferrocene (Fe(C 5 H 5 ) 2 ), if the temperature of the inner portion 4 of the catalyst raw material supplying nozzle 3 is about 1,400° C. or higher, a vapor of iron (Fe) as the catalyst metal can be inhibited from being condensed and generating iron particles.
  • the catalyst raw material is to be heated and decomposed by setting the temperature of the inner portion 4 of the catalyst raw material supplying nozzle 3 for supplying the catalyst raw material used to synthesize carbon nanotubes to the synthesis furnace 2 higher than the temperature of the reaction field 5 of the synthesis furnace 2 for synthesizing carbon nanotubes.
  • the temperature of the inner portion 4 of the catalyst raw material supplying nozzle 3 can be adjusted by the nozzle temperature adjusting unit 6 provided inside the catalyst raw material supplying nozzle 3 .
  • the synthesis furnace 2 in FIG. 1 is formed into a vertical shape elongated in a vertical direction of the drawing; the synthesis furnace 2 may also be formed into a transverse shape elongated in a left and right direction of the drawing.
  • the catalyst raw material and the carbon raw material are to be supplied from top down in the drawing.
  • one or both of the catalyst raw material and the carbon raw material may be supplied from bottom up in the drawing, or from the transverse direction of the drawing. This also applies when the synthesis furnace 2 is of a transverse shape.
  • single-walled carbon nanotubes SWCNT
  • MWCNT multi-walled carbon nanotubes
  • the crystallizability of CNTs can, for example, be analyzed via laser micro-Raman spectroscopic analysis.
  • a peak observed near 1,590 cm ⁇ 1 is called G-band, and is derived from the in-plane stretching vibrations of carbon atoms composing a six-membered ring structure.
  • a peak observed near 1,350 cm ⁇ 1 is called D-band, and is likely to be observed when the six-membered ring structure is defective.
  • a relative crystallizability of CNTs can be evaluated by a peak intensity ratio I G /I D (G/D ratio) of G-band to D-band.
  • a peak observed near 200 cm ⁇ 1 is unique to single-walled carbon nanotubes (SWCNT) called RBM (Radial Breathing Mode) which is a mode where vibrations occur in the diametrical direction of the tubes.
  • SWCNT single-walled carbon nanotubes
  • RBM Ring Breathing Mode
  • thermogravimetry differential thermal analysis for analyzing a carbon material
  • the temperature of the material is to be raised to about 1,000° C. at about 5° C./min so as to then analyze a peak temperature of burning and a residue thereof, thereby making it possible to evaluate the constituent elements and quality of the carbon material.
  • a product in FCCVD is a mixture of: a metal contained in the catalyst raw material, such as iron (Fe); CNTs; amorphous carbon (a-C); and graphitic carbon (g-C).
  • a-C burns at about 350 to 450° C.; CNTs and g-C start to burn at about 400° C., and completely burns out at about 700° C.
  • a thermal analysis device model number: TG8120 by Rigaku Corporation was used to perform thermogravimetry differential thermal analysis under air flow and at a temperature rise rate of 5° C./min.
  • thermogravimetry differential thermal analysis is an oxidized metal(s)
  • quantitative analysis of the residue was conducted using a scanning electron microscope (SEM) (model number: S-4800 by Hitachi High-Tech Corporation) and an energy dispersive X-ray analysis (EDX) device (model number: EDAX Genesis by AMETEK. Inc.).
  • SEM scanning electron microscope
  • EDX energy dispersive X-ray analysis
  • FIG. 2 and FIG. 3 are schematic views partially showing an example of a configuration of a CNT production device 1 of a working example 1 of the present invention.
  • the catalyst raw material supplying nozzle 3 is connected to the catalyst raw material supplying portion 11 for supplying the catalyst raw material and, if necessary, the cocatalyst through the catalyst raw material supplying tube 14 .
  • the carbon raw material supplying tube 15 is connected to the carbon raw material supplying portion 12 for supplying the carbon raw material.
  • the inert gas supplying tube 16 is connected to the inert gas supplying portion 13 for supplying, if necessary, an inert gas such as argon (Ar) used for purging.
  • a coil 21 is provided outside the outer circumferential portion of the catalyst raw material supplying nozzle 3 , and a heat transfer rod 22 is provided inside the catalyst raw material supplying nozzle 3 .
  • the inner portion 4 can be heated from outside the catalyst raw material supplying nozzle 3 by energizing the coil 21 , and also from within the catalyst raw material supplying nozzle 3 by the heat transfer rod 22 that has been heated by the radiation from within the catalyst raw material supplying nozzle 3 , thereby allowing the temperature of the inner portion 4 of the catalyst raw material supplying nozzle 3 to be easily set high.
  • the temperature of the inner portion 4 of the catalyst raw material supplying nozzle 3 was adjusted by the amount of electricity conducted to the coil 21 .
  • the temperature of the inner portion 4 of the catalyst raw material supplying nozzle 3 was set higher than the temperature of the reaction field 5 of the synthesis furnace 2 .
  • the temperature of the catalyst raw material supplied from the catalyst raw material supplying portion 11 through the catalyst raw material supplying tube 14 and flowing through the catalyst raw material supplying nozzle 3 was raised to a high temperature in a short contact time. Due to the heat transfer rod 22 , in the inner portion 4 of the catalyst raw material supplying nozzle 3 , since a region where the catalyst raw material would decompose was evenly heated, the catalyst raw material was able to be decomposed in a short contact time.
  • the catalyst raw material supplying nozzle 3 and the heat transfer rod 22 were made of alumina (Al 2 O 3 ); an inner diameter of the catalyst raw material supplying nozzle 3 was set to 4 mm, and a diameter of the heat transfer rod was set to 2 mm.
  • the coil 21 provided outside the outer circumferential portion of the catalyst raw material supplying nozzle 3 was made of tungsten (W).
  • a numerical symbol “ 23 ” denotes a heat insulation material for keeping the inner portion 4 of the catalyst raw material supplying nozzle 3 at a high temperature.
  • FIG. 4 shows a catalyst raw material supplying nozzle 3 used in a CNT production device of a comparative example 1.
  • a catalyst raw material supplying nozzle 3 identical to that used in the present working example; there were not employed the heat transfer rod 22 and the coil 21 provided outside the outer circumferential portion of the catalyst raw material supplying nozzle 3 , and the catalyst raw material was supplied to the reaction field 5 of the synthesis furnace 2 without being heated.
  • the rest of the configurations were identical to those of the working example 1.
  • FIG. 5 shows a CNT production device of a comparative example 2 that includes the catalyst raw material supplying nozzle 3 and the coil 21 provided outside the outer circumferential portion of the catalyst raw material supplying nozzle 3 .
  • the coil 21 was electrically heated such that the inner portion 4 of the catalyst raw material supplying nozzle 3 was heated only via the heating unit provided outside the catalyst raw material supplying nozzle 3 .
  • the rest of the configurations were similar to those of the working example 1.
  • FIG. 6 is a graph showing a change in temperature in a depth direction of the inner portion 4 when flowing a total of 2 SLM of a gas through the catalyst raw material supplying nozzle 3 .
  • the temperature was measured using a thermocouple (not shown) provided in the center of the catalyst raw material supplying nozzle 3 .
  • a temperature in a central portion of the catalyst raw material supplying nozzle 3 was calculated via fluid analysis using a general-purpose numerical value fluid analyzing software (ANSYS Fluent).
  • the set temperature of the heat retention unit 8 (Furnace) was 1,150° C.
  • the temperature rose toward a flow outlet of the catalyst raw material supplying nozzle 3 , the temperature only rose to a temperature lower than 1,150° C.
  • the temperature reached 1,150° C. at 50 to 55 mm of the catalyst raw material supplying nozzle 3 in a depth direction thereof where the coil is already gradually wound therearound, and a temperature of the inner portion 4 of the catalyst raw material supplying nozzle 3 from such location to the flow outlet became higher than the set temperature (1,150° C.) of the heat retention unit 8 .
  • a maximum value of the temperature of the inner portion 4 was about 1,400° C.
  • the gas of the flow rate of 2 SLM passes through a gap of a cross-sectional area of 0.0942 cm 2 between the catalyst raw material supplying nozzle 3 having the inner diameter of 4 mm and the heat transfer rod having the diameter of 2 mm.
  • the flow rate of the gas was 33.3 cm 3 /s at 0° C., and became 204 cm 3 /s when heated to 1,400° C.
  • the gas passed through the gap of the cross-sectional area of 0.0942 cm 2 at 2,170 cm/s on average, and a time spent in passing by 2 cm of the heated portion of the catalyst raw material supplying nozzle 3 was 0.9 ms on average.
  • the temperature of the reaction field 5 of the synthesis furnace 2 was either at the same level of or lower than the set temperature (1,150° C.) of the heat retention unit 8 .
  • comparative example 1 and comparative example 2 there were used an identical catalyst raw material, an identical carbon raw material, an identical gaseous species of the purge gas and carrier gas, an identical gas flow rate, an identical gas temperature and an identical set temperature of the heat retention unit 8 .
  • an argon (Ar) gas as a carrier gas was supplied to the catalyst raw material supplying tube 14 at 120° C. and 0.5 SLM.
  • An argon (Ar) gas was supplied from the inert gas supplying portion 13 to the inert gas supplying tube 16 at 1.0 SLM.
  • Ethylene (C 2 H 4 ) as the carbon raw material was supplied from the carbon raw material supplying portion 12 to the carbon raw material supplying tube 15 at 0.05 SLM.
  • a hydrogen (H 2 ) gas was supplied to the carbon raw material supplying tube 15 at 0.5 SLM, and an argon (Ar) gas as a carrier gas was supplied to the carbon raw material supplying tube 15 at 1.5 SLM.
  • an electric furnace was provided outside the outer circumferential portion of the synthesis furnace 2 , and the temperature of the electric furnace was set to 1,150° C.
  • CNTs were produced as an aggregate 31 .
  • the length of the aggregate taken out from the reaction tube was about 10 cm.
  • Various evaluations of the CNTs produced in the working example 1, comparative example 1 and comparative example 2 are collectively shown in Table 1. Described hereunder are details of each evaluation result.
  • the productivity was calculated as a yield per unit time based on the yield of CNTs and a synthesis time.
  • the productivity in the working example 1 was 5.73 mg/min which was higher than 2.80 mg/min in the comparative example 1 and 3.81 mg/min in the comparative example 2.
  • thermogravimetry differential thermal analysis was performed on a residue obtained after performing a later-described thermogravimetry differential thermal analysis (TG-DTA).
  • TG-DTA thermogravimetry differential thermal analysis
  • the ratio in the working example 1 was 84.9 wt % which was higher than 80.6 wt % in the comparative example 1 and 71.7 wt % in the comparative example 2.
  • the working example 1 provides a CNT production device and method having a high productivity, and that CNTs with a high purity can be produced thereby.
  • FIG. 9 is a Raman spectrum of the CNTs produced.
  • I G /I D G/D ratio
  • thermogravimetric analysis (TG) result of the CNTs produced a lower graph in FIG. 10 is a graph showing a differential thermal analysis result (DTA).
  • Table 2 shows the evaluation results of thermogravimetry differential thermal analysis.
  • TG thermogravimetric analysis
  • the mass increased in the beginning due to the oxidation of iron (Fe) as the catalyst (( 1 ) in the graph).
  • a peak of mass increase in the working example 1 was smaller than those in the comparative examples 1 and 2. Burning started at about 350° C. Based on a peak change in DTA, it can be concluded that a range of about 350° C. to about 420° C.
  • the burning of amorphous carbon (a-C) took place (( 2 ) in FIG. 10 ), and that a range of about 420° C. to about 650° C. was where the burning of CNTs took place (( 3 ) in the graph).
  • the amount of the ashes of the residue was 22 wt % as compared to before burning, which was smaller than 30 wt % in the comparative example 1 and 43 wt % in the comparative example 2.
  • the utilization efficiency of the catalyst was able to be improved.
  • FIG. 11 includes a SEM image ( FIG. 11A ) of the CNTs produced in the working example 1; and a TEM image thereof ( FIG. 11B ). As shown in the SEM image, it was indicated that the number of the particles was small. That is, it was indicated that the number of the catalyst metal particles that were not used for synthesizing CNTs was small, whereas the number of the catalyst metal particles that were effective in growing the CNTs had increased.
  • the TEM image indicates that SWCNT 32 was produced. There, the diameter of the CNTs and the distribution thereof were observed by TEM.
  • the diameter of the CNTs produced in the working example 1 was 1.55 nm on average which was smaller than 2.22 nm in the comparative example 1 and 1.69 nm in the comparative example 2. In this way, it was indicated that in the working example 1, CNTs with a small diameter were able to be produced by thermally decomposing the catalyst raw material, mixing the decomposed catalyst metal raw material with the carbon source gas to then rapidly perform cooling to the CVD temperature so as to generate the microscopic catalyst metal particles and immediately generate CNTs.
  • a standard deviation ⁇ of the diameter of the CNTs produced in the working example 1 was 0.43 which was smaller than 0.90 in the comparative example 1 and 0.63 in the comparative example 2. In this way, it was indicated that by using the heat transfer rod 22 , the temperature distribution in the inner portion 4 of the catalyst raw material supplying nozzle 3 will be even such that the thermal decomposition of the catalyst raw material shall spatially evenly take place, and that as a result, the catalyst metal particles are able to be spatially evenly generated.
  • Carbon nanotubes were synthesized in a manner such that a device identical to that used in the working example 1 was used, a catalyst raw material-containing argon (Ar) gas was passed through the catalyst raw material supplying tube 14 from the catalyst raw material supplying portion 11 under a condition identical to that of the working example 1, and as the carbon source, methane (CH 4 ) was used instead of ethylene (C 2 H 4 ).
  • Other synthesis conditions for working examples 2a to 2h are as shown in Table 3; experiments were conducted by changing the temperature of the synthesis furnace 2 in a range of 1,150 to 1,200° C.
  • the temperature of the inner portion of the catalyst raw material supplying nozzle is as shown in FIG. 6 ; and a region having a temperature higher than that of the synthesis furnace 2 was set to be about 20 mm.
  • FIGS. 12, 14, 16, 18, 20, 23, 26 and 28 are all Raman spectra of the CNTs produced in the working examples 2a to 2h; I G /I D (G/D ratio) in each working example was calculated.
  • FIGS. 13, 15, 17, 19, 21, 24, 27 and 29 are all SEM images of the CNTs produced in the working examples 2a to 2h.
  • thermogravimetry differential thermal analysis (TG-DTA) was performed ( FIGS. 22, 25 and 30 ).
  • Table 3 the amount of the ashes of the residue was not larger than 23.1 wt % as compared to before burning, which was smaller than those in the comparative examples 1 and 2.
  • EDS quantitative analysis was performed on a residue obtained after performing thermogravimetry differential thermal analysis (TG-DTA).
  • the ratio of the carbon (C) derived from CNTs to the iron (Fe) derived from ferrocene (Fe(C 5 H 5 ) 2 ) as the catalyst raw material and the aluminum (Al) derived from alumina (Al 2 O 3 ) of the catalyst raw material supplying nozzle 3 was 92.7 wt % which was higher than those in the comparative examples 1 and 2.
  • FIG. 31 is a schematic view partially showing an example of a configuration of a CNT production device 1 of a working example 3 of the present invention.
  • the nozzle temperature adjusting unit 6 is provided inside the catalyst raw material supplying nozzle 3 .
  • This configuration allows the temperature of the inner portion 4 of the catalyst raw material supplying nozzle 3 to be easily set high, and even higher than the temperature of the reaction field 5 of the synthesis furnace 2 . Further, the temperature of the catalyst raw material supplied from the catalyst raw material supplying portion 11 through the catalyst raw material supplying tube 14 and flowing through the catalyst raw material supplying nozzle 3 , can be raised to a high temperature in a short period of time.
  • the temperature of the catalyst raw material supplying nozzle can be maintained lower than that of the nozzle temperature adjusting unit 6 , when the temperature of the nozzle temperature adjusting unit 6 is set to an especially high temperature, the catalyst raw material whose temperature has been raised will be thermally decomposed at a high temperature and in a short period of time to generate a catalyst metal vapor, and the catalyst metal vapor thus generated will then be supplied to the reaction field 5 of the synthesis furnace 2 without being condensed.
  • a thermal damage of the catalyst raw material supplying nozzle 3 can be inhibited as compared to when performing heating from outside by installing a coil outside the outer circumferential portion of the catalyst raw material supplying nozzle 3 .
  • the nozzle temperature adjusting unit 6 is the heater 7 .
  • This heater 7 is composed of carbon, and is electrically heated so as to then adjust the temperature of the inner portion 4 of the catalyst raw material supplying nozzle 3 by changing the amount of electricity conducted.
  • the catalyst raw material supplying nozzle 3 can be made of a heat-resistant ceramics material; for example, it may be a cylinder made of zirconia (ZrO 2 ).
  • the heater 7 may, for example, be formed into an inverted U shape with a slit 18 being provided in a C/C composite (carbon fiber-reinforced carbon composite material) sheet, and be arranged inside the catalyst raw material supplying nozzle 3 .
  • a Ni-made electrode 9 may, for example, be connected to the heater 7 so as to electrically conduct the heater 7 through such electrode 9 . Since the heater 7 will heat the catalyst raw material to a temperature higher than the temperature of the reaction field 5 of the synthesis furnace 2 , the nucleation of the metal particles from the catalyst raw material can be inhibited from occurring in the catalyst raw material supplying nozzle 3 . The heated catalyst raw material will then be supplied to the reaction field 5 of the synthesis furnace 2 as the catalyst metal vapor.
  • a numerical symbol “ 17 ” denotes the carbon raw material flow passage that is provided outside the outer circumferential portion of the catalyst raw material supplying nozzle 3 , and allows the carbon raw material to flow therethrough.
  • the carbon raw material is supplied from the carbon raw material supplying portion 12 to the carbon raw material flow passage 17 through the carbon raw material supplying tube 15 .
  • the carbon raw material flows outside the outer circumferential portion of the catalyst raw material supplying nozzle 3 whose inner portion 4 has been heated to a temperature higher than the temperature of the reaction field 5 of the synthesis furnace 2 , since a heat-insulating catalyst raw material supplying nozzle 3 is used, the carbon raw material can be efficiently preheated to the extent that it will not decompose.
  • FIG. 32 is a side cross-sectional view of a CNT production device 1 configured to have a plurality of the catalyst raw material supplying nozzles 3 , as opposed to the CNT production device 1 of FIG. 31 that has only one catalyst raw material supplying nozzle 3 .
  • FIG. 33 is a top view corresponding to FIG. 32 . Except for the configuration of employing a plurality of the catalyst raw material supplying nozzles 3 , this production device 1 can be configured in a similar manner as FIG. 31 .
  • the plurality of the catalyst raw material supplying nozzles 3 are formed by boring in a cylindrical heat insulation material a plurality of holes 41 penetrating such heat insulation material from the upper surface thereof to the lower surface thereof.
  • the heater 7 is provided in each of the plurality of holes 41 , and the catalyst raw material supplying tube 14 is connected to the upper portion of each hole.
  • FIG. 34 shows an example different from FIG. 33 .
  • each of the plurality of the catalyst raw material supplying nozzles 3 is individually made of a cylindrical heat insulation material.
  • the heater 7 is provided inside each cylindrical heat insulation material, and the catalyst raw material supplying tube 14 is connected to the upper portion of each heat insulation material.
  • the carbon nanotube production method of the present invention can be performed using the production device(s) shown in FIGS. 1 to 3 and FIGS. 31 to 34 , whereby carbon nanotubes can be produced at a high density, high purity, high quality and high yield.
  • the present invention may be variously modified before exploitation.
  • sizes such as the diameter and length of the catalyst raw material supplying nozzle 3 , the width and length of the heater 7 provided inside the catalyst raw material supplying nozzle 3 and the width of the slit 18 , are not limited to those shown in FIG. 31 , but may be appropriately configured.
  • shape of the heater 7 There are also no particular restrictions on the shape of the heater 7 ; for example, even if it is to be formed into an inverted U shape, a production method thereof shall not be limited to the method described above. Other than electric heating, induction heating or the like may also be employed for heating the heater 7 .
  • the production device may also be a device where the carbon raw material is to be supplied to the synthesis furnace 2 at a low temperature without being preheated, and then rapidly heated at the synthesis furnace 2 .
  • the working example 3 is described as a specific configuration employing a plurality of the catalyst raw material supplying nozzles 3 ; as is the case with the working example 3, the working examples 1 and 2 may also have a configuration employing a plurality of the catalyst raw material supplying nozzles 3 .

Landscapes

  • Chemical & Material Sciences (AREA)
  • Organic Chemistry (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Nanotechnology (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Inorganic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Carbon And Carbon Compounds (AREA)
US17/632,730 2019-08-09 2020-07-27 Carbon nanotube production device and production method Pending US20220274836A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2019-147941 2019-08-09
JP2019147941A JP7158646B2 (ja) 2019-08-09 2019-08-09 カーボンナノチューブの製造装置および製造方法
PCT/JP2020/028754 WO2021029212A1 (ja) 2019-08-09 2020-07-27 カーボンナノチューブの製造装置および製造方法

Publications (1)

Publication Number Publication Date
US20220274836A1 true US20220274836A1 (en) 2022-09-01

Family

ID=74569423

Family Applications (1)

Application Number Title Priority Date Filing Date
US17/632,730 Pending US20220274836A1 (en) 2019-08-09 2020-07-27 Carbon nanotube production device and production method

Country Status (5)

Country Link
US (1) US20220274836A1 (ko)
JP (1) JP7158646B2 (ko)
KR (1) KR102541963B1 (ko)
CN (1) CN114174220B (ko)
WO (1) WO2021029212A1 (ko)

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FI130805B1 (fi) * 2022-03-24 2024-03-27 Canatu Oy Laitteisto ja menetelmä katalyyttihiukkasten tuottamiseksi

Family Cites Families (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA2350099C (en) * 1998-11-03 2008-05-20 William Marsh Rice University Gas-phase nucleation and growth of single-wall carbon nanotubes from high pressure co
FI121334B (fi) 2004-03-09 2010-10-15 Canatu Oy Menetelmä ja laitteisto hiilinanoputkien valmistamiseksi
KR100646221B1 (ko) * 2004-05-13 2006-11-23 재단법인서울대학교산학협력재단 열플라즈마 토치를 이용한 탄소나노튜브 제조방법 및 장치
CN101018737A (zh) * 2004-07-16 2007-08-15 独立行政法人科学技术振兴机构 催化剂粒径控制式碳纳米结构物的制造方法、制造装置以及碳纳米结构物
EP2298699A4 (en) * 2008-07-16 2011-11-30 Hodogaya Chemical Co Ltd CARBON FIBER MASS, MANUFACTURING METHOD THEREFOR, AND COMPOSITE MATERIAL CONTAINING SAME
JPWO2012015044A1 (ja) * 2010-07-30 2013-09-12 保土谷化学工業株式会社 気相成長炭素繊維集合体
WO2016068599A1 (ko) * 2014-10-28 2016-05-06 주식회사 엘지화학 탄소나노튜브섬유의 제조장치 및 이를 이용한 탄소나노튜브섬유 제조방법
GB201421664D0 (en) * 2014-12-05 2015-01-21 Q Flo Ltd Method
CN204455392U (zh) * 2015-02-12 2015-07-08 新永裕应用科技材料股份有限公司 气相成长石墨纤维组成物的生产系统
RU2018101886A (ru) 2015-07-16 2019-08-16 Торэй Индастриз, Инк. Способ получения содержащей углеродные нанотрубки композиции
KR102672047B1 (ko) * 2015-10-01 2024-06-05 가부시키가이샤 메이조 나노 카본 카본 나노 튜브의 제조 장치 및 제조 방법
CN109607513B (zh) * 2018-11-29 2022-05-31 中国科学院金属研究所 一种生长促进剂可控制备不含硫杂质的单壁碳纳米管方法

Also Published As

Publication number Publication date
KR20220062492A (ko) 2022-05-17
JP2021028284A (ja) 2021-02-25
WO2021029212A1 (ja) 2021-02-18
CN114174220B (zh) 2023-06-30
JP7158646B2 (ja) 2022-10-24
CN114174220A (zh) 2022-03-11
KR102541963B1 (ko) 2023-06-14

Similar Documents

Publication Publication Date Title
US7824649B2 (en) Apparatus and method for synthesizing a single-wall carbon nanotube array
JP5550833B2 (ja) 高品質単層カーボンナノチューブ成長の方法および装置
US20170001865A1 (en) Carbon nanotubes functionalized with fullerenes
Hoyos-Palacio et al. Catalytic effect of Fe, Ni, Co and Mo on the CNTs production
Kibria et al. Synthesis of narrow-diameter carbon nanotubes from acetylene decomposition over an iron–nickel catalyst supported on alumina
Arcaro et al. MWCNTs produced by electrolysis of molten carbonate: Characteristics of the cathodic products grown on galvanized steel and nickel chrome electrodes
AU2005302978A1 (en) Carbon nanotube aggregate and process for producing the same
US7052667B2 (en) RF plasma method for production of single walled carbon nanotubes
JP6492598B2 (ja) カーボンナノチューブの製造方法
US20220274836A1 (en) Carbon nanotube production device and production method
Yamagiwa et al. Liquid-phase synthesis of highly aligned carbon nanotubes on preheated stainless steel substrates
Kanai et al. High-yield synthesis of single-walled carbon nanotubes by gravity-free arc discharge
JP5672008B2 (ja) ナノカーボン複合体の製造方法および製造装置
US7955663B2 (en) Process for the simultaneous and selective preparation of single-walled and multi-walled carbon nanotubes
Saravanan et al. Techno-economics of carbon nanotubes produced by open air arc discharge method
JP4604342B2 (ja) カーボンナノ構造体の合成用のアーク電極
JP2006290698A (ja) カーボンナノ繊維の製造方法
JP6455988B2 (ja) カーボンナノチューブの製造装置および製造方法
Hosseini et al. Large diameter MWNTs growth on iron-sprayed catalyst by CCVD method under atmospheric pressure
He et al. Growth of single-walled carbon nanotubes with large chiral angles on rhodium nanoparticles
JP3952479B2 (ja) カーボンナノチューブの製造方法
Dikio et al. A comparative study of the effect of MgO and CaCO3 as support materials in the synthesis of carbon nanotubes with Fe/Co as catalyst
Shajahan et al. Low cost growth route for single-walled carbon nanotubes from decomposition of acetylene over magnesia supported Fe-Mo catalyst
Kim et al. Carbon nanotube growth on Invar alloy using coal tar pitch
Dikio A comparative study of carbon nanotubes synthesized from Co/Zn/Al and Fe/Ni/Al catalyst

Legal Events

Date Code Title Description
AS Assignment

Owner name: MEIJO NANO CARBON CO., LTD., JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:NODA, SUGURU;NAMIKI, KATSUYA;ZHANG, ZIHAO;AND OTHERS;SIGNING DATES FROM 20211218 TO 20211227;REEL/FRAME:058881/0802

Owner name: WASEDA UNIVERSITY, JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:NODA, SUGURU;NAMIKI, KATSUYA;ZHANG, ZIHAO;AND OTHERS;SIGNING DATES FROM 20211218 TO 20211227;REEL/FRAME:058881/0802

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION