US20200269522A1 - Composite moulding materials - Google Patents

Composite moulding materials Download PDF

Info

Publication number
US20200269522A1
US20200269522A1 US16/611,021 US201816611021A US2020269522A1 US 20200269522 A1 US20200269522 A1 US 20200269522A1 US 201816611021 A US201816611021 A US 201816611021A US 2020269522 A1 US2020269522 A1 US 2020269522A1
Authority
US
United States
Prior art keywords
graphene
resin
layers
graphitic
nanoplates
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US16/611,021
Other languages
English (en)
Inventor
Nigel Ashley BLATHERWICK
Matthew David SHARP
Kevin Andrew Yeomans
William Weaver
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Universal Matter GBR Ltd
Original Assignee
Applied Graphene Materials UK Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Applied Graphene Materials UK Ltd filed Critical Applied Graphene Materials UK Ltd
Publication of US20200269522A1 publication Critical patent/US20200269522A1/en
Assigned to UNIVERSAL MATTER GBR LTD reassignment UNIVERSAL MATTER GBR LTD CHANGE OF NAME (SEE DOCUMENT FOR DETAILS). Assignors: APPLIED GRAPHENE MATERIALS UK LIMITED
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
    • C08J5/04—Reinforcing macromolecular compounds with loose or coherent fibrous material
    • C08J5/10—Reinforcing macromolecular compounds with loose or coherent fibrous material characterised by the additives used in the polymer mixture
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29B—PREPARATION OR PRETREATMENT OF THE MATERIAL TO BE SHAPED; MAKING GRANULES OR PREFORMS; RECOVERY OF PLASTICS OR OTHER CONSTITUENTS OF WASTE MATERIAL CONTAINING PLASTICS
    • B29B11/00—Making preforms
    • B29B11/14—Making preforms characterised by structure or composition
    • B29B11/16—Making preforms characterised by structure or composition comprising fillers or reinforcement
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C70/00—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts
    • B29C70/02—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts comprising combinations of reinforcements, e.g. non-specified reinforcements, fibrous reinforcing inserts and fillers, e.g. particulate fillers, incorporated in matrix material, forming one or more layers and with or without non-reinforced or non-filled layers
    • B29C70/021—Combinations of fibrous reinforcement and non-fibrous material
    • B29C70/025—Combinations of fibrous reinforcement and non-fibrous material with particular filler
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C70/00—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts
    • B29C70/02—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts comprising combinations of reinforcements, e.g. non-specified reinforcements, fibrous reinforcing inserts and fillers, e.g. particulate fillers, incorporated in matrix material, forming one or more layers and with or without non-reinforced or non-filled layers
    • B29C70/028—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts comprising combinations of reinforcements, e.g. non-specified reinforcements, fibrous reinforcing inserts and fillers, e.g. particulate fillers, incorporated in matrix material, forming one or more layers and with or without non-reinforced or non-filled layers and with one or more layers of non-plastics material or non-specified material, e.g. supports
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C70/00—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts
    • B29C70/04—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts comprising reinforcements only, e.g. self-reinforcing plastics
    • B29C70/06—Fibrous reinforcements only
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C70/00—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts
    • B29C70/04—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts comprising reinforcements only, e.g. self-reinforcing plastics
    • B29C70/28—Shaping operations therefor
    • B29C70/54—Component parts, details or accessories; Auxiliary operations, e.g. feeding or storage of prepregs or SMC after impregnation or during ageing
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C70/00—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts
    • B29C70/88—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts characterised primarily by possessing specific properties, e.g. electrically conductive or locally reinforced
    • B29C70/887—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts characterised primarily by possessing specific properties, e.g. electrically conductive or locally reinforced locally reinforced, e.g. by fillers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B5/00—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts
    • B32B5/22—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by the presence of two or more layers which are next to each other and are fibrous, filamentary, formed of particles or foamed
    • B32B5/24—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by the presence of two or more layers which are next to each other and are fibrous, filamentary, formed of particles or foamed one layer being a fibrous or filamentary layer
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B82—NANOTECHNOLOGY
    • B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
    • B82Y30/00—Nanotechnology for materials or surface science, e.g. nanocomposites
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
    • C08J5/005—Reinforced macromolecular compounds with nanosized materials, e.g. nanoparticles, nanofibres, nanotubes, nanowires, nanorods or nanolayered materials
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
    • C08J5/04—Reinforcing macromolecular compounds with loose or coherent fibrous material
    • C08J5/06—Reinforcing macromolecular compounds with loose or coherent fibrous material using pretreated fibrous materials
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K3/00—Use of inorganic substances as compounding ingredients
    • C08K3/02—Elements
    • C08K3/04—Carbon
    • C08K3/042—Graphene or derivatives, e.g. graphene oxides
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2101/00—Use of unspecified macromolecular compounds as moulding material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2307/00—Use of elements other than metals as reinforcement
    • B29K2307/04—Carbon
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2255/00—Coating on the layer surface
    • B32B2255/02—Coating on the layer surface on fibrous or filamentary layer
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2255/00—Coating on the layer surface
    • B32B2255/20—Inorganic coating
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2264/00—Composition or properties of particles which form a particulate layer or are present as additives
    • B32B2264/10—Inorganic particles
    • B32B2264/107—Ceramic
    • B32B2264/108—Carbon, e.g. graphite particles
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2305/00—Condition, form or state of the layers or laminate
    • B32B2305/08—Reinforcements
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/50—Properties of the layers or laminate having particular mechanical properties
    • B32B2307/514—Oriented
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/70—Other properties
    • B32B2307/72—Density
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B41—PRINTING; LINING MACHINES; TYPEWRITERS; STAMPS
    • B41J—TYPEWRITERS; SELECTIVE PRINTING MECHANISMS, i.e. MECHANISMS PRINTING OTHERWISE THAN FROM A FORME; CORRECTION OF TYPOGRAPHICAL ERRORS
    • B41J2202/00—Embodiments of or processes related to ink-jet or thermal heads
    • B41J2202/01—Embodiments of or processes related to ink-jet heads
    • B41J2202/05—Heads having a valve
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2300/00—Characterised by the use of unspecified polymers
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K2201/00—Specific properties of additives
    • C08K2201/011—Nanostructured additives

Definitions

  • the present invention relates to composite moulding materials and in particular fibre reinforced composite moulding materials comprising graphene and or graphite and composite components made therefrom.
  • Fibre reinforced composites are widely used in many areas of manufacture, especially in the manufacture of high strength/lightweight structures, due to their relative light weight and high in-plane specific strength and stiffness characteristics.
  • FRC's typically have a laminate structure made up of a plurality of fibre reinforcement layers consolidated within a matrix resin. It is within the planes of the fibre reinforcement layers where the in-plane strength and stiffness is found.
  • their out-of-plane (through-thickness) properties represent weakness, presenting vulnerability to delamination either from edges or as a result of external loads or damage and subsequent propagation, imperilling serviceability, overall integrity and potentially leading to catastrophic failure.
  • a composite moulding material comprising a fibrous layer and a graphene/graphitic material applied to the fibrous layer at one or more localised regions over a surface of the fibrous layer in which the graphene/graphitic material is comprised of graphene nanoplates, graphene oxide nanoplates, reduced graphene oxide nanoplates, bilayer graphene nanoplates, bilayer graphene oxide nanoplates, bilayer reduced graphene oxide nanoplates, few-layer graphene nanoplates, few-layer graphene oxide nanoplates, few-layer reduced graphene oxide nanoplates, graphene/graphite nanoplates of 6 to 14 layers of carbon atoms, graphite flakes with nanoscale dimensions and 40 or less layers of carbon atoms, graphite flakes with nanoscale dimensions and 25 to 30 layers of carbon atoms, graphite flakes with nanoscale dimensions and 25 to 35 layers of carbon atoms, graphite flakes with nanoscale dimensions and 20 to 35 layers of
  • graphene nanoplates graphene oxide nanoplates, reduced graphene oxide nanoplates, bilayer graphene nanoplates, bilayer graphene oxide nanoplates, bilayer reduced graphene oxide nanoplates, few-layer graphene nanoplates, few-layer graphene oxide nanoplates, few-layer reduced graphene oxide nanoplates, graphene/graphite nanoplates of 6 to 14 layers of carbon atoms, graphite flakes with nanoscale dimensions and 40 or less layers of carbon atoms, graphite flakes with nanoscale dimensions and 25 to 30 layers of carbon atoms, graphite flakes with nanoscale dimensions and 20 to 35 layers of carbon atoms, graphite flakes with nanoscale dimensions and 25 to 35 layers of carbon atoms, or graphite flakes with nanoscale dimensions and 20 to 40 layers of carbon atoms are hereafter collectively referred to as “graphene/graphitic platelets”.
  • Graphene, graphene oxide, and/or reduced graphene oxide nanoplates typically have a thickness of 1 to 10 layers of carbon atoms, typically between 0.3 nm and 3 nm, and lateral dimensions ranging from around 100 nm to 100 ⁇ m.
  • the graphene/graphitic material may be selectively located at at least one and preferably a plurality of predetermined regions over a surface of the fibrous layer.
  • the regions may be spaced and discrete.
  • the or each region may cover a surface area on the fibrous layer of between 0.001 mm 2 and 0.01 mm 2 , 0.002 mm 2 and 0.01 mm 2 , 0.01 mm 2 and 1.5 mm 2 , between 0.01 mm 2 and 1.0 mm 2 , between 0.5 mm 2 and 1.5 mm 2 , and greater than 0.003 mm 2 , greater than 0.5 mm 2 or greater than 1 mm 2 .
  • the graphene/graphitic material at the, each or at least one of the region(s) may comprise a single body of material or may comprise a plurality of discrete bodies within the region(s).
  • the graphene/graphitic material may form one or more islands on the surface of the fibrous layer, the or each island preferably being surrounded by one or more areas of fibrous material deficient in graphene/graphitic material. That is where there is no graphene/graphitic material.
  • Each body may be one such island.
  • the graphene/graphitic material may be located at or in an array or pattern of regions over a surface of the fibrous layer.
  • the array or pattern may be regular, such as a regular array of bands, stripes, circles, spots, squares, blocks, columns, rows, or an array aligned along the nominal vertices of polyhedral shapes, for example hexagons, pentagons or other tessellating shapes.
  • the array may be irregular or may be regular in part and irregular in other part.
  • Bodies of graphene/graphitic material at the or at least one of the region(s) may comprise an array or pattern of graphene/graphitic material over a surface of the fibrous layer.
  • the array or pattern may be regular, such as a regular array of bands, stripes, circles, spots, squares, blocks, columns, rows, or an array aligned along the nominal vertices of polyhedral shapes, for example hexagons, pentagons or other tessellating shapes.
  • the array may be irregular or may be regular in part and irregular in other part.
  • the graphene/graphitic material may be located at one or more regions where the properties of the graphene/graphitic material will be beneficial to a composite component moulded from the composite moulding material.
  • the graphene/graphitic material may be a dispersion comprising graphene/graphite platelets dispersed in a carrier medium.
  • the graphene/graphitic platelets may comprise platelets comprising a plurality of layers of graphene/graphite and may have an average thickness of between 0.8 and 12 nanometres, may be between 1.3 and 9.4 nanometres and may be between 2.5 and 6 nanometres.
  • the graphene/graphitic platelets may comprise up to 25 or up to 35 layers of graphene, may be between 5 and 25 or 5 and 35 layers of graphene, and may be between 5 and 15 or 25 to 35 layers of graphene.
  • the graphene/graphitic platelets may comprise one or more of graphene, graphene oxide, reduced graphene oxide, graphite, graphite oxide, or reduced graphite oxide with a general plate-like (platelet) planar conformation.
  • the graphene/graphitic platelets may have a carbon content of between 40 wt % and 99 wt % and may be between 97 wt % and 99 wt % for platelets of graphene or graphite, may be between 80 wt % and 99 wt % for platelets of reduced graphene oxide or reduced graphite oxide, and may be between 40 wt % and 60 wt % by weight for platelets of graphene oxide or graphite oxide.
  • the graphene/graphitic platelets may have an sp2 content of between 40 wt % and 98 wt % and may be between 95 wt % and 98 wt % for platelets of graphene or graphite, may be between 60 wt % and 95 wt % for platelets of reduced graphene oxide or reduced graphite oxide and may be between 40 wt % and 60 wt % for graphene oxide or graphite oxide.
  • the graphene/graphitic platelets may comprise between 1 wt % and 50 wt % oxygen, may be between 1 wt % and 3 wt % oxygen for platelets of graphene or graphite, may be between 5 wt % and 10 wt % for platelets of reduced graphene oxide or reduced graphite oxide, and may be between 20 wt % and 50 wt % for platelets of graphene oxide or graphite oxide.
  • the graphene/graphitic platelets may have an average platelet size (planar dimension) of up to 40 ⁇ m, a d90 size of between 5 ⁇ m and 25 ⁇ m, a d90 size of between 1 ⁇ m and 40 ⁇ m, a d50 size of between 5 ⁇ m and 12 ⁇ m, and or a d50 size of between 1 ⁇ m and 30 ⁇ m.
  • the particle sizes being measured using a Mastersizer 3000.
  • the graphene/graphitic platelets may comprise a plurality of layers of graphene, graphene oxide and/or reduced graphene oxide embedded in graphitic carbon.
  • the carrier medium may comprise resin, such as thermoset resin which may comprise one or more of epoxy, polyester (unsaturated), phenolic, vinyl ester, polyurethane, silicone, polyamide, polyamideimide, bismaleimide, cyanate ester, benzoxazine.
  • resin such as thermoset resin which may comprise one or more of epoxy, polyester (unsaturated), phenolic, vinyl ester, polyurethane, silicone, polyamide, polyamideimide, bismaleimide, cyanate ester, benzoxazine.
  • the carrier medium may comprise thermoplastic resin which may comprise one or more of polyethylene (PE), polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polycarbonate (PC), acrylonitrile butadiene styrene (ABS), polyamide (PA or nylon) and polypropylene (PP).
  • thermoplastic resins polyetheretherketone (PEEK), polyetherketone (PEK), polyamide-imide (PAI), polyarylsulfone (PAS), polyetherimide (PEI), polyethersulfone (PES), polyphenylene sulphide (PPS).
  • the carrier medium may comprise biobased resins which may comprise one or more of starch, starch caprolactone blends, polyesters—polyalkylene succinates, polyesteramides, polyhydroxy alkanoates—polyvinyl butyral—polyvinyl valeate, polyhydroxy acids—polylacticacid—polyglycolic acid, cellulose acetate, furfural alcohol/furan resins, oil modified polyesters—vegetable oil modification—cashew nut oil modification.
  • biobased resins which may comprise one or more of starch, starch caprolactone blends, polyesters—polyalkylene succinates, polyesteramides, polyhydroxy alkanoates—polyvinyl butyral—polyvinyl valeate, polyhydroxy acids—polylacticacid—polyglycolic acid, cellulose acetate, furfural alcohol/furan resins, oil modified polyesters—vegetable oil modification—cashew nut oil modification.
  • the carrier medium may comprise deionised water and/or solvent, which may comprise one or more of hexane, benzene, toluene, xylene, diethylether, 1,4-dioxane, ethyl acetate, nbutyl acetate, t-butyl acetate, ethyl ethoxy propionate, propyleneglycol monomethyl ether acetate, methyl acetate, dimethylcarbonate, tetrahydrofuran, dichloromethane, acetone, methyl ethyl ketone, methyl isobutyl ketone, methyl propyl ketone, methyl isoamyl ketone, acetonitrile, dimethlyformamide, dimethylsluphoxide, n-butanol, methanol, ethanol, n-propanol, isopropanol, butanol, glycols-
  • solvent may comprise
  • the carrier medium may be the same as or otherwise compatible with resin in the fibrous layer.
  • the dispersion may have a graphene/graphitic material content in the range 0.001 wt % to 10 wt %, 0.001 wt % to 1 wt %, 0.01 wt % to 0.5 wt %, 0.01 wt % to 5 wt %.
  • the area density of graphene/graphitic material applied to the fibrous layer may be in the range 1 mg/m 2 to 35000 mg/m 2 , 1 mg/m 2 to 2000 mg/m 2 , 10 mg/m 2 to 100 mg/m 2 , 1000 mg/m 2 to 20000 mg/m 2 , 1000 mg/m 2 to 10000 mg/m 2 , or 10 mg/m 2 to 20 mg/m 2 .
  • the dispersion may have a viscosity in the range 1 to 75 centipoise, 1 to 50 centipoise, 10 to 50 centipoise, approximately 20 centipoise, or approximately 15 centipoise as measured at 10 ⁇ (s ⁇ 1)@23° C.
  • the graphene/graphite material is preferably applied to the fibrous layer by a selective application process such as ink jet printing, including one or more of thermal drop on demand and a piezo drop on demand ink jet printing, valve jet printing, contact printing, non-contact printing, by spray techniques or by use of a mask and spray methods.
  • a selective application process such as ink jet printing, including one or more of thermal drop on demand and a piezo drop on demand ink jet printing, valve jet printing, contact printing, non-contact printing, by spray techniques or by use of a mask and spray methods.
  • the graphene/graphitic material may be applied in droplets and the inter-droplet spacing may be between 0.01 mm and 0.5 mm or between 0.3 mm and 2 mm.
  • the graphene/graphitic material may be applied in any manner that enables selective application for the accurate location of the graphene/graphitic material at one or more selected regions across the surface of the fibrous layer, the said region(s) may be preselected as being at or anticipated to lie at stressed or potentially stressed locations within a composite component moulded from the composite moulding material.
  • the fibrous layer may comprise fibrous material partially or fully impregnated with curable matrix resin and may be in the form of one or more of a prepreg, a partially cured prepreg, an uncured fibrous preform, a partially cured fibrous preform.
  • the fibrous layer may comprise one or more plies of fibrous material.
  • the fibrous layer may comprise, at least in part, dry fibrous material.
  • the fibrous material may comprise one or more forms of fibrous reinforcing materials for fibre reinforced composites, including one or more of woven mat, unwoven mat, continuous fabric, unidirectional fabric, braided fabric, knitted fabric, woven fabric, discontinuous mat, chopped fibres, 3D woven materials, single fibre tow, unidirectional prepreg, slit tape prepreg, tow prepreg.
  • the fibrous material may comprise one or more of carbon fibres, glass fibres, aramid fibres, plastic fibres, nylon fibres, terylene fibres, hemp fibres, wood fibres and/or other organic fibres or inorganic fibres.
  • the curable matrix resin of the fibrous layer may comprise resin, such as thermoset resin which may comprise one or more of epoxy, polyester (unsaturated), phenolic, vinyl ester, polyurethane, silicone, polyamide, polyamideimide, bismaleimide, cyanate ester, benzoxazine.
  • resin such as thermoset resin which may comprise one or more of epoxy, polyester (unsaturated), phenolic, vinyl ester, polyurethane, silicone, polyamide, polyamideimide, bismaleimide, cyanate ester, benzoxazine.
  • the curable matrix resin of the fibrous layer comprises thermoplastic resin which may comprise one or more of polyethylene (PE), polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polycarbonate (PC), acrylonitrile butadiene styrene (ABS), polyamide (PA or nylon) and polypropylene (PP).
  • thermoplastic resin which may comprise one or more of polyethylene (PE), polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polycarbonate (PC), acrylonitrile butadiene styrene (ABS), polyamide (PA or nylon) and polypropylene (PP).
  • the curable matrix resin of the fibrous layer may comprise biobased resins which may comprise one or more of starch, starch caprolactone blends, polyesters—polyalkylene succinates, polyesteramides, polyhydroxy alkanoates—polyvinyl butyral-polyvinyl valeate, polyhydroxy acids—polylacticacid—polyglycolic acid, cellulose acetate, furfuralalcohol/furan resins, oil modified polyesters—vegetable oil modification—cashew nut oil modification.
  • biobased resins which may comprise one or more of starch, starch caprolactone blends, polyesters—polyalkylene succinates, polyesteramides, polyhydroxy alkanoates—polyvinyl butyral-polyvinyl valeate, polyhydroxy acids—polylacticacid—polyglycolic acid, cellulose acetate, furfuralalcohol/furan resins, oil modified polyesters—vegetable oil modification—cashew nut oil modification.
  • the carrier may be the same resin as, substantially the same as, or otherwise compatible with the curable matrix resin.
  • the fibrous layer may comprise a laminate structure, which may comprise a plurality of plies of fibrous material, in which the fibrous material and/or the curable matrix resin may be the same or may differ between the plies.
  • the composite moulding material may comprise one or more outer layers that may cover any otherwise externally exposed graphene/graphitic material in the composite moulding material.
  • the outer layer(s) may comprise a fibrous layer.
  • a moulding laminate comprising a plurality of layers of composite moulding material as described in any of the preceding paragraphs.
  • the composite moulding material may be the same in some and preferably all of the layers.
  • the composite moulding material may differ between layers and each layer may be different to all other layers within the moulding laminate.
  • the layers of composite moulding material may be laminated, one on top of the other.
  • the layers may be laminated so that graphene/graphitic material on at least one or some of the layers is aligned or substantially aligned with graphene/graphitic material on at least one other layer within the moulding material in the out-of-plane direction.
  • the out of plane direction being a direction approximately perpendicular to the plane of the layer or layers at the position of the graphene/graphitic material being considered.
  • the layers may be laminated so that some or all of the graphene/graphitic material on adjacent layers or on at least two adjacent layers is superimposed or substantially superimposed in the out-of-plane direction.
  • layers may be laminated so that graphene/graphitic material on adjacent layers is misaligned or substantially misaligned or at least some of the graphene/graphitic material on adjacent layers is misaligned or substantially misaligned between those layers.
  • the moulding laminate may comprise one or more outer laminate layers that may cover any otherwise externally exposed graphene/graphitic material in the moulding laminate.
  • the outer laminate layer(s) may be the same or substantially the same as a fibrous layer of composite moulding material in the moulding laminate.
  • a fibre reinforced composite component comprising a plurality of fibrous layers held within a cured matrix resin and graphene/graphitic material at one or more localised regions between at least two of the fibrous layers to provide interlaminar fracture toughness at said region(s).
  • a method of manufacturing a composite moulding material comprising providing a fibrous layer and applying a graphene/graphitic dispersion at one or more localised regions over a surface of the fibrous layer in which the graphene/graphitic dispersion comprises graphene nanoplates, graphene oxide nanoplates, reduced graphene oxide nanoplates, bilayer graphene nanoplates, bilayer graphene oxide nanoplates, bilayer reduced graphene oxide nanoplates, few-layer graphene nanoplates, few-layer graphene oxide nanoplates, few-layer reduced graphene oxide nanoplates, graphene/graphite nanoplates of 6 to 14 layers of carbon atoms, graphite flakes with nanoscale dimensions and 40 or less layers of carbon atoms, graphite flakes with nanoscale dimensions and 25 to 30 layers of carbon atoms, graphite flakes with nanoscale dimensions and 25 to 35 layers of carbon atoms, graphite flakes with nano
  • the graphene/graphitic dispersion is a liquid that can be applied to a fibrous layer. Once applied the dispersion may become solid or at least a liquid of higher viscosity so forming the graphene/graphitic material.
  • the process by which the dispersion becomes the material is dependent on the nature of the dispersion and may include, but not be limited to, evaporation of a solvent, chemical reaction, or thermo-chemical reaction.
  • the graphene/graphitic dispersion may be selectively applied to at least one and preferably a plurality of predetermined regions over a surface of the fibrous layer.
  • the graphene/graphitic dispersion may be selectively applied to spaced and discrete regions.
  • the graphene/graphitic dispersion may be selectively applied so that the or each region may cover a surface area on the fibrous layer of between 0.01 and 1.5 mm 2 , between 0.01 mm 2 and 1.0 mm 2 , between 0.5 mm 2 and 1.5 mm 2 , and typically of greater than 0.5 mm 2 or greater than 1 mm 2 .
  • the graphene/graphitic dispersion may be selectively applied so that the graphene/graphitic dispersion at the, each or at least one of the region(s) may comprise a single body of material or may comprise a plurality of discrete bodies within the region(s).
  • the graphene/graphitic dispersion may be selectively applied so that the graphene/graphitic dispersion may form one or more islands on the surface of the fibrous layer, the or each island preferably being surrounded by one or more areas of fibrous material deficient in graphene/graphite.
  • the graphene/graphitic dispersion may be applied at or in an array or pattern of localised regions over a surface of the fibrous layer.
  • the graphene/graphitic dispersion may be applied as a regular array or pattern, such as a regular array of bands, stripes, circles, spots, squares, blocks, columns, rows, or an array aligned along the nominal vertices of polyhedral shapes, for example hexagons, pentagons or other tessellating shapes.
  • the graphene/graphitic dispersion may be applied as an irregular array or pattern, or as an array or pattern regular in part and irregular in other part.
  • Bodies of graphene/graphitic dispersion at the or at least one of the region(s) may be applied as an array or pattern of graphene/graphitic dispersion over a surface of the fibrous layer.
  • the array or pattern may be regular, such as a regular array of bands, stripes, circles, spots, squares, blocks, columns, rows, or an array aligned along the nominal vertices of polyhedral shapes, for example hexagons, pentagons or other tessellating shapes.
  • the array may be irregular or may be regular in part and irregular in other part.
  • the graphene/graphitic dispersion may be applied at one or more regions where the properties of the graphene/graphitic material will be beneficial to a composite component moulded from the composite moulding material.
  • the graphene/graphitic dispersion may comprise graphene/graphitic platelets dispersed in a carrier medium.
  • the graphene/graphitic platelets may comprise platelets comprising a plurality of layers of graphene and may have an average thickness of between 0.8 and 12 nanometres, between 1.3 and 9.4 nanometres and may be between 2.5 and 6 nanometres.
  • the graphene/graphitic platelets may comprise up to 25 or up to 35 layers of graphene, may be between 5 and 25 or 5 and 35 layers of graphene, and may be between 5 and 15 or 25 to 35 layers of graphene.
  • the graphene/graphitic platelets may comprise one or more of graphene, graphene oxide, reduced graphene oxide, graphite, graphite oxide, reduced graphite oxide with a generally plate-like (platelet) conformation.
  • the graphene/graphitic platelets may have a carbon content of between 40 wt % and 99 wt % and may be between 97 wt % and 99 wt % for platelets of graphene or graphite, may be between 80 wt % and 99 wt % for platelets of reduced graphene oxide or reduced graphite oxide, and may be between 40 wt % and 60 wt % by weight for platelets of graphene oxide or graphite oxide.
  • the graphene/graphitic platelets may have an sp2 content of between 40 wt % and 98 wt % and may be between 95 wt % and 98 wt % for platelets of graphene or graphite, may be between 60 wt % and 95 wt % for platelets of reduced graphene oxide or reduced graphite oxide and may be between 40 wt % and 60 wt % for graphene oxide or graphite oxide.
  • the graphene/graphitic platelets may comprise between 1 wt % and 50 wt % oxygen, may be between 1 wt % and 3 wt % oxygen for platelets of graphene or graphite, may be between 5 wt % and 10 wt % for platelets of reduced graphene oxide or reduced graphite oxide, and may be between 20 wt % and 50 wt % for platelets of graphene oxide or graphite oxide.
  • the graphene/graphitic platelets may have an average platelet size (planar dimension) of up to 40 ⁇ m, a d90 size of between 5 ⁇ m and 25 ⁇ m, a d90 size of between 1 ⁇ m and 40 ⁇ m, a d50 size of between 5 ⁇ m and 12 ⁇ m, and or a d50 size of between 1 ⁇ m and 30 ⁇ m.
  • the particle sizes being measured using a Mastersizer 3000.
  • the graphene platelets may comprise a plurality of layers of graphene, graphene oxide and/or reduced graphene oxide embedded in graphitic carbon.
  • the carrier medium used may comprise resin, such as thermoset resin which may comprise one or more of epoxy, polyester (unsaturated), phenolic, vinyl ester, polyurethane, silicone, polyamide, polyamideimide, bismaleimide, cyanate ester, benzoxazine.
  • resin such as thermoset resin which may comprise one or more of epoxy, polyester (unsaturated), phenolic, vinyl ester, polyurethane, silicone, polyamide, polyamideimide, bismaleimide, cyanate ester, benzoxazine.
  • the carrier medium may comprise thermoplastic resin which may comprise one or more of polyethylene (PE), polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polycarbonate (PC), acrylonitrile butadiene styrene (ABS), polyamide (PA or nylon) and polypropylene (PP).
  • thermoplastic resins polyetheretherketone (PEEK), polyetherketone (PEK), polyamide-imide (PAI), polyarylsulfone (PAS), polyetherimide (PEI), polyethersulfone (PES), polyphenylene sulphide (PPS).
  • the carrier medium may comprise biobased resins which may comprise one or more of starch, starch caprolactone blends, polyesters—polyalkylene succinates, polyesteramides, polyhydroxy alkanoates polyvinyl butyral—polyvinyl valeate, polyhydroxy acids—polylacticacid—polyglycolic acid, cellulose acetate, furfuralalcohol/furan resins, oil modified polyesters—vegetable oil modification—cashew nut oil modification
  • the carrier medium may comprise deionised water and/or solvent, such as one or more of hexane, benzene, toluene, xylene, diethylether, 1,4-Dioxane, ethyl acetate, nbutyl acetate, t-butyl acetate, ethyl ethoxy propionate, propyleneglycol monomethyl ether acetate, methyl acetate, Dimethylcarbonate, tetrahydrofuran, Dichloromethane, acetone, methyl ethyl ketone, methyl isobutyl ketone, methyl propyl ketone, methyl isoamyl ketone, Acetonitrile, Dimethlyformamide, dimethylsluphoxide, n-butanol, methanol, ethanol, n-propanol, isopropanol, butanol, glycols-ethylene glycol, ethylene glyco
  • the carrier medium used may be the same as or otherwise compatible with resin in the fibrous layer.
  • the dispersion may have a graphene/graphitic platelet content in the range 0.001 wt % to 10 wt %, 0.001 wt % to 1 wt %, 0.01 wt % to 0.5 wt %, 0.01 wt % to 5 wt %.
  • the area density of graphene/graphitic dispersion applied to the fibrous layer may be in the range 1 mg/m 2 to 35000 mg/m 2 , 1 mg/m 2 to 2000 mg/m 2 , 10 mg/m 2 to 100 mg/m 2 , 1000 mg/m 2 to 20000 mg/m 2 , 1000 mg/m 2 to 10000 mg/m 2 , or 10 mg/m 2 to 20 mg/m 2 .
  • the dispersion may have a viscosity in the range 1 to 75 centipoise, 1 to 50 centipoise, 10 to 50 centipoise, approximately 20 centipoise, or approximately 15 centipoise as measured at 10 ⁇ (s ⁇ 1)@23° C.
  • the graphene/graphitic dispersion is preferably applied to the fibrous layer by a selective application process such as ink jet printing, including one or more of thermal drop on demand and a piezo drop on demand ink jet printing, valvejet printing, contact printing, non-contact printing, by spray techniques or by use of a mask and spray methods.
  • a selective application process such as ink jet printing, including one or more of thermal drop on demand and a piezo drop on demand ink jet printing, valvejet printing, contact printing, non-contact printing, by spray techniques or by use of a mask and spray methods.
  • the graphene/graphitic dispersion may be applied in droplets and the inter-droplet spacing may be between 0.01 mm and 0.5 mm or between 0.3 mm and 2 mm.
  • the graphene/graphitic dispersion may be applied in any manner that enables selective application for the accurate location of the graphene/graphitic material at one or more selected regions across the surface of the fibrous layer, the said region(s) may be preselected as being or anticipated to lie at stressed or potentially stressed locations within a composite component moulded from the composite moulding material.
  • the fibrous layer provided may comprise fibrous material partially or fully impregnated with curable matrix resin and may be in the form of one or more of a prepreg, a partially cured prepreg, an uncured fibrous preform, a partially cured fibrous preform.
  • the fibrous layer provided may comprise one or more plies of fibrous material.
  • the fibrous layer provided may comprise, at least in part, dry fibrous material.
  • the fibrous material used may comprise one or more forms of fibrous reinforcing materials for fibre-reinforced composites, including one or more of woven mat, unwoven mat, continuous fabric, unidirectional fabric, braided fabric, knitted fabric, woven fabric, discontinuous mat, chopped fibres, 3D woven materials, single fibre tow, unidirectional prepreg, slit tape prepreg, tow prepreg.
  • the fibrous material used may comprise one or more of carbon fibres, glass fibres, aramid fibres, plastic fibres, nylon fibres, terylene fibres, hemp fibres, wood fibres and/or other organic fibres or inorganic fibres.
  • the curable matrix resin of the fibrous layer may comprise resin, such as thermoset resin which may comprise one or more of epoxy, polyester (unsaturated), phenolic, vinyl ester, polyurethane, silicone, polyamide, polyamideimide, bismaleimide, cyanate ester, benzoxazine.
  • resin such as thermoset resin which may comprise one or more of epoxy, polyester (unsaturated), phenolic, vinyl ester, polyurethane, silicone, polyamide, polyamideimide, bismaleimide, cyanate ester, benzoxazine.
  • the curable matrix resin of the fibrous layer comprises thermoplastic resin which may comprise one or more of polyethylene (PE), polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polycarbonate (PC), acrylonitrile butadiene styrene (ABS), polyamide (PA or nylon) and polypropylene (PP).
  • thermoplastic resin which may comprise one or more of polyethylene (PE), polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polycarbonate (PC), acrylonitrile butadiene styrene (ABS), polyamide (PA or nylon) and polypropylene (PP).
  • the curable matrix resin of the fibrous layer may comprise biobased resins which may comprise one or more of starch, starch caprolactone blends, polyesters—polyalkylene succinates, polyesteramides, polyhydroxy alkanoates—polyvinyl butyral-polyvinyl valeate, polyhydroxy acids—polylacticacid—polyglycolic acid, cellulose acetate, furfuralalcohol/furan resins, oil modified polyesters—vegetable oil modification—cashew nut oil modification
  • the carrier used may be the same resin as, substantially the same as, or otherwise compatible with the curable matrix resin.
  • the fibrous layer provided may comprise a laminate structure, which may have a plurality of plies of fibres, in which the fibrous material and/or the curable matrix resin may be the same or may differ between the plies.
  • One or more outer layers may be provided to cover any otherwise externally exposed graphene/graphite material in the composite moulding material.
  • the outer layer(s) provided may comprise a fibrous layer.
  • a method of manufacturing a moulding laminate comprising laminating a plurality of composite moulding materials as described above.
  • the composite moulding material used may be the same in some and preferably all of the layers.
  • the composite moulding material used may differ between layers and each layer may be different to all other layers within the moulding laminate.
  • the layers of composite moulding material may be laminated one on top of the other.
  • the layers may be laminated so that graphene/graphitic material on at least some of the layers is aligned or substantially aligned with graphene/graphitic material on at least one other layer within the moulding material.
  • the layers may be laminated so that some or all of the graphene/graphitic material on adjacent layers is superimposed or substantially superimposed in the out-of-plane direction.
  • layers may be laminated so that graphene/graphitic material on adjacent layers is misaligned or substantially misaligned or at least some of the graphene/graphitic material on adjacent layers is misaligned or substantially misaligned between those layers.
  • One or more outer laminate layers may be provided that may cover any otherwise externally exposed graphene/graphitic material in the moulding laminate.
  • the outer laminate layer(s) used may be the same or substantially the same as a fibrous layer of composite moulding material in the moulding laminate.
  • a method of manufacturing a fibre reinforced composite component comprising providing a plurality of fibrous layers, a curable matrix resin to consolidate the fibrous layers and applying a graphene/graphitic dispersion at one or more localised regions over a surface of at least one of the fibrous layers, positioning the fibrous layers so that the graphene/graphitic material is located between two adjacent fibrous layers and subjecting the component to conditions to cure the matrix resin around the fibrous material.
  • An ink for use in an inkjet printer was prepared as follows:
  • Graphene/graphitic material A-GNP10 is commercially available from Applied Graphene Materials UK Limited, UK and comprises graphite platelets of between 25 and 35 layers of atoms thick).
  • Graphene/graphitic material A-GNP30 is commercially available from Applied Graphene Materials UK Limited, UK and comprises graphite platelets of between 3 and 6 layers of atoms thick).
  • Graphene/graphitic material A-GNP35(T) is commercially available from Applied Graphene Materials UK Limited, UK and comprises graphite platelets of between 6 and 12 layers of atoms thick).
  • the sample was then pressure cured with a cure temperature profile which includes a ramp rate of 1° C./min to 120° C., followed by a 1 hour dwell at 120° C., and at a pressure of 600 kPa (6 Bar).
  • FIG. 1 is a diagrammatic perspective of a composite material according to the present invention
  • FIG. 2 is a diagrammatic perspective of a composite material according to another embodiment of the present invention.
  • FIG. 3 is a diagrammatic perspective of a composite material according to a further embodiment of the present invention.
  • FIG. 4 is a diagrammatic perspective of a composite material according to another embodiment of the present invention.
  • FIG. 5 is a diagrammatic perspective of a composite material according to a further embodiment of the present invention.
  • FIG. 6 is a diagrammatic perspective of a composite material according to another embodiment of the present invention.
  • FIG. 7 is a diagrammatic perspective of a composite material according to a further embodiment of the present invention.
  • FIG. 8 is a diagrammatic cross-sectional view of a composite moulding material according to a still further embodiment of the present invention.
  • FIG. 9 a is a diagrammatic perspective view of a moulding laminate according to the present invention.
  • FIG. 9 b is a diagrammatic cross-section along the line IXb of FIG. 9 a;
  • FIG. 10 a is a diagrammatic perspective view of a moulding laminate according to a further embodiment of the present invention.
  • FIG. 10 b is a diagrammatic cross-section of the moulding laminate of FIG. 10 a along the line X 13 ,
  • FIG. 11 is a diagrammatic cross-section of a further moulding laminate according to a further embodiment of the present invention.
  • FIG. 12 is a diagrammatic cross-section of a fibre reinforced composite component according to the present invention.
  • FIG. 13 is a diagrammatic cross-section of two fibre reinforced composite components according to the present invention, secured by a fastener F;
  • FIG. 14 is a diagrammatic cross-section of the moulding laminate of FIG. 10 a , being moulded.
  • the invention provides a composite moulding material comprising a fibrous layer and a graphene/graphitic material applied to the fibrous layer at one or more localised regions on a surface of the fibrous layer.
  • FIG. 1 illustrates one embodiment of a composite moulding material 10 which has a fibrous layer 12 and a graphene/graphitic material 14 applied to the fibrous layer 12 at four localised regions R 1 , R 2 , R 3 , R 4 over the surface 16 of the fibrous layer 12 .
  • the graphene/graphitic material 14 has been selectively applied at each of the predetermined regions R 1 , R 2 , R 3 , R 4 on the surface 16 of the fibrous layer 12 .
  • each of the four predetermined regions R 1 , R 2 , R 3 , R 4 is located generally in a respective corner of the surface 16 of the fibrous layer 12 .
  • the regions R 1 , R 2 , R 3 , R 4 are spaced from each other to provide discrete bodies of graphene/graphitic material 14 .
  • a single body of graphene/graphitic material 14 is provided in each region R 1 , R 2 , R 3 , R 4 .
  • the amount of graphene/graphitic material applied to the fibrous layer in a given region is determined according to a number of factors, including the nature of the graphene/graphitic material itself, the nature of the fibrous layer, the nature of any moulding laminate to be produced using the composite moulding material, the desired properties and characteristics, in particular interlaminar toughness and strength characteristics, required or sought for composite components to be formed using the composite moulding material.
  • the graphene/graphitic material 14 in each region R 1 , R 2 , R 3 , R 4 may cover a surface on the fibrous layer of between 0.01 and 1.5 mm 2 in certain embodiments, between 0.5 mm 2 and 1.5 mm 2 in other embodiments, between 0.01 mm 2 and 1.0 mm 2 in other embodiments, greater than 0.5 mm 2 , or greater than 1 mm 2 .
  • the area covered may be considerably greater than 1 mm 2 if appropriate/required.
  • Each body of graphene/graphitic material 14 in the embodiment of FIG. 1 forms an island of graphene/graphitic material on the surface of the fibrous layer 12 and each island is surrounded by fibrous material deficient in graphene/graphite.
  • the graphene/graphitic material 14 is located in a regular array or pattern of regions with R 1 , R 2 , R 3 , R 4 being aligned along the nominal vertices of a quadrilateral.
  • FIG. 2 illustrates a composite moulding material according to a further embodiment, where features that are the same or equivalent to features in embodiment of FIG. 1 have the same reference numeral but prefixed with a ‘1’. In relation to other embodiments described herein that have the same or equivalent features, these are referenced with the same numeral but with a respective prefix number.
  • the graphene/graphitic material 114 has been applied in two localised regions R 1 , R 2 , which are generally in the form of a simple pattern of two bands or stripes that extend across the surface 116 and generally parallel both mutually and to the sides of the fibrous layer 112 of the composite moulding material 210 .
  • the graphene/graphitic material can be applied in any number of regions or configuration of regions and those regions may form a regular array or pattern over the surface of the fibrous layer, such as regular arrays or patterns of bands, strips, circles, spots, squares, blocks, columns, rows, and/or any array or pattern aligned along the nominal vertices of polyhedral shapes, for example hexagons, pentagons or other tessellating shapes.
  • the graphene/graphitic material is provided at localised, preselected and predetermined regions that between them define an irregular pattern or array.
  • FIG. 3 illustrates one such exemplary embodiment, where graphene/graphitic material 214 is provided as an irregular pattern or array of regions R 1 , R 2 , R 3 , R 4 , R 5 on the surface 216 of the fibrous layer 212 of the composite moulding material 310 .
  • the graphene/graphitic material is applied to the surface of the fibrous layer in an array or pattern that in part is regular and in other part is irregular.
  • FIG. 4 An illustrated example of such embodiments is shown in FIG. 4 , where the regions R 1 , R 2 , R 3 , R 4 provide a regular part of the array or pattern and R 5 , R 6 , R 7 represent an irregular part.
  • the graphene/graphitic material can be applied at any configuration of localised regions on the surface of the fibrous layer and an advantage of the present invention is that it allows materials to be engineered that provide for the advantageous characteristics and properties of the graphene/graphitic material, and in particular the graphene/graphitic within the material to be realised in a selective and predetermined manner, which in turn enables a number of related advantages to be realised, as will be discussed.
  • the present invention provides for the selective application of graphene/graphitic material at predetermined localised regions within composite moulding materials that can be used to produce such composite components to allow composite components to be engineered such that graphene/graphitic material is present in those areas or zones, thus affording the composites the improved interlaminar fracture toughness and strength characteristics that the graphene/graphite material provides, precisely where needed and not elsewhere, where not needed.
  • the precision placement of the graphene/graphitic material into the interlaminar boundary will enhance fracture toughness through crack bridging and deflection mechanisms. It is expected that this will result in a reduction in crack growth and an improvement in composite designs under fatigue.
  • the improved fracture toughness at the interlaminar boundary enhances the performance of composite and enables a change in composite design methodologies.
  • the use of such graphene/graphite platelet modified materials should enable composite structures to be developed to the same safety design considerations of today but with a smaller number of composite layers resulting in significant benefits in materials used and weight of the composite component.
  • bodies of graphene/graphitic material are provided within a region and the bodies comprise an array or pattern of graphene/graphitic material on a surface of the fibrous layer, within a zone.
  • FIG. 5 illustrates one such embodiment in a composite moulding material 410 , where three discrete bodies B 1 , B 2 , B 3 of graphene/graphitic material 414 are provided in each region R 1 , R 2 , R 3 , R 4 .
  • the regions R 1 , R 2 , R 3 , R 4 are in a mutually regular pattern and the bodies B 1 , B 2 , B 3 within each region are likewise in a mutually regular pattern.
  • the bodies B 1 , B 2 , B 3 are each a strip that run mutually parallel within the respective region R 1 , R 2 , R 3 , R 4 .
  • the pattern or array of bodies of graphene/graphitic material within the region or one or more of the regions are otherwise regular, such as regular arrays or patterns of bands, circles, spots, squares, blocks, columns, rows, or any array aligned along the nominal vertices of polyhedral shapes, for example hexagons, pentagons or other tessellating shapes.
  • the bodies within a region are applied in an array or pattern that is irregular, as illustrated by the bodies B 1 , B 2 , B 3 in the composite moulding material 510 embodied in FIG. 6 .
  • one or more of the regions are regular and the bodies within the other or at least one of the other regions are irregular.
  • FIG. 7 An illustrative example of a moulding material 610 according to such an embodiment is shown in FIG. 7 , where the bodies B 1 , B 2 , B 3 of graphene/graphitic material 614 in region R 1 are in an irregular pattern or array and the bodies B 1 , B 2 , B 3 of graphene/graphitic material 614 in region R 2 are in a regular array of three mutually parallel strips or lines on the surface 612 .
  • the graphene/graphitic material comprises a dispersion of graphene/graphite platelets dispersed in a carrier medium.
  • the graphene/graphite platelets comprise plate-like particles or platelets that comprise a plurality of layers of graphene (monolayer), each platelet having a general thickness (measured through the thickness of the platelets, generally perpendicularly across the plane of the platelet) of between 0.8 and 12 nanometres in certain embodiments, of between 1.3 and 9.4 nanometres in other embodiments, and of between 2.5 and 6.0 nanometres in still further embodiments.
  • Graphene/graphite platelets that have been found to have particular utility in the present invention comprise up to 25 layers or up to 35 layers of graphene/graphite.
  • the graphene/graphite platelets have between 5 and 25 or 5 and 35 layers of graphene/graphite and in other embodiments between 5 and 15 or 25 and 35 layers of graphene/graphite.
  • the graphene/graphite platelets have a carbon content of between 40% and 99% by weight, although the chemical content will vary according to the composition of the platelets.
  • graphene/graphite platelets with an sp2 content of between 60% and 98% have particular utility in the present invention, although again the sp2 content will vary according to the composition of the platelets.
  • the oxygen content of the graphene/graphite platelets is between 1% and 50%, varying according to the composition of the platelets.
  • the table 5 shows the typical percentage carbon content, sp2 content and percentage oxygen, by weight, of platelets of graphene, reduced graphene oxide and graphene oxide.
  • the graphene/graphitic platelets may have an average platelet size (planar dimension) of up to 40 ⁇ m, a d90 size of between 5 ⁇ m and 25 ⁇ m, a d90 size of between 1 ⁇ m and 40 ⁇ m, a d50 size of between 5 ⁇ m and 12 ⁇ m, and or a d50 size of between 1 ⁇ m and 30 ⁇ m.
  • the particle sizes being measured using a Mastersizer 3000.
  • the graphene platelets may comprise one or more of graphene, graphene oxide and reduced graphene oxide, which is typically embedded in graphitic carbon.
  • the carrier medium comprises thermoset resin which comprises one or more of epoxy, polyester (unsaturated), phenolic, vinyl ester, polyurethane, silicone, polyamide, polyamideimide, bismaleimide, cyanate ester, benzoxazine.
  • the carrier medium comprises thermoplastic resin, which in certain embodiments is selected from one or more of polyethylene (PE), polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polycarbonate (PC), acrylonitrile butadiene styrene (ABS), polyamide (PA or nylon) and polypropylene (PP).
  • thermoplastic resins polyetheretherketone (PEEK), polyetherketone (PEK), polyamide-imide (PAI), polyarylsulfone (PAS), polyetherimide (PEI), polyethersulfone (PES), polyphenylene sulphide (PPS).
  • the carrier medium comprises biobased resins which can comprise one or more of starch, starch caprolactone blends, polyesters—polyalkylene succinates, polyesteramides, polyhydroxy alkanoates—polyvinyl butyral-polyvinyl valeate, polyhydroxy acids—polylacticacid—polyglycolic acid, cellulose acetate, furfuralalcohol/furan resins, oil modified polyesters—vegetable oil modification—cashew nut oil modification
  • the carrier medium can comprise deionised water and/or solvent, such as one or more of hexane, benzene, toluene, xylene, diethylether, 1,4-Dioxane, ethyl acetate, nbutyl acetate, t-butyl acetate, ethyl ethoxy propionate, propyleneglycol monomethyl ether acetate, methyl acetate, Dimethylcarbonate, tetrahydrofuran, Dichloromethane, acetone, methyl ethyl ketone, methyl isobutyl ketone, methyl propyl ketone, methyl isoamyl ketone, Acetonitrile, Dimethlyformamide, dimethylsluphoxide, n-butanol, methanol, ethanol, n-propanol, isopropanol, butanol, glycols-ethylene glycol, propylene
  • the carrier medium comprises one or more of thermoset resin, thermoplastic resin, bio-based resin, solvent and water.
  • the carrier medium is compatible with the resin in the fibrous layer and in certain embodiments the carrier medium is the same as resin in the fibrous layer.
  • the dispersion has a graphene/graphite platelet content in the range of 0.001 wt % to 10 wt %, 0.001 wt % to 1 wt %, by weight, may be in the range 0.01 wt % to 0.5 wt %, 0.01 wt % to 5 wt % by weight.
  • the area density of graphene/graphitic material applied to the fibrous layer is in the range 1 mg/m 2 to 35000 mg/m 2 , 1 mg/m 2 to 2000 mg/m 2 , 10 mg/m 2 to 100 mg/m 2 , 1000 mg/m 2 to 20000 mg/m 2 , 1000 mg/m 2 to 10000 mg/m 2 , or 10 mg/m 2 to 20 mg/m 2 .
  • the dispersion particularly at the time of application, has a viscosity in the range 1 to 75 centipoise, 1 to 50 centipoise, 10 to 50 centipoise, approximately 20 centipoise, or approximately 15 centipoise
  • the dispersion typically comprises approximately 20% by weight of resin, with solvent, such as xylene or any of the other solvent carriers described herein.
  • the viscosity of the dispersion is in the range 0.9 to 50 centipoise, and in such embodiments the dispersion is typically resin free or substantially resin free, with the graphene/graphite platelets dispersed in a non-resinous carrier medium such as solvent, one being xylene, or any of the others described herein.
  • a non-resinous carrier medium such as solvent, one being xylene, or any of the others described herein.
  • Viscosities discussed in connection with the present invention are as measured on a Malvern Kinexus rheometer at 10 ⁇ (s ⁇ 1)@23° C.
  • the graphene/graphitic material is of a viscosity that enables it to be applied to the fibrous layer by a selective application process such as ink jet printing, including one or more of thermal drop on demand and piezo drop on demand ink jet printing, valvejet printing, contact printing, non-contact printing, by any other suitably selective and accurate spray technique or by use of a mask and spray method.
  • a selective application process such as ink jet printing, including one or more of thermal drop on demand and piezo drop on demand ink jet printing, valvejet printing, contact printing, non-contact printing, by any other suitably selective and accurate spray technique or by use of a mask and spray method.
  • a particularly favoured application process for the present invention is ink jet printing, as this enables selective application for the accurate location of the graphene/graphitic material at the predetermined localised region or regions on the surface of the fibrous layer.
  • the graphene/graphitic material can be applied in a single stage of printing, or in a multiple stage printing process.
  • the fibrous layer of the composite moulding material comprises fibrous material partially or fully impregnated with curable matrix resin.
  • the fibrous layer comprises an uncured prepreg, a partially cured prepreg, an uncured fibrous preform or a partially cured fibrous preform.
  • the fibrous layer comprises one ply of fibrous material and in other embodiments comprises a plurality of plies of fibrous material.
  • the fibrous layer comprises dry fibrous material (without any associated resin) and in other embodiments comprises one or more plies of dry fibrous material and one or more plies of fibrous material preimpregnated with resin.
  • the fibrous material of the composite moulding materials of the present invention can be known formats of fibre reinforcement typically used for fibre reinforced composites, including one or more of woven mat, unwoven mat, continuous fabric, unidirectional fabric, braided fabric, knitted fabric, woven fabric, discontinuous mat, chopped fibres, single fibre tow, impregnated slit tape, 3D woven materials, unidirectional prepreg, slit tape prepreg, tow prepreg.
  • the fibrous material can comprise any suitable organic and/or inorganic fibre and in certain embodiments can comprise one or more of carbon fibres, glass fibres, aramid fibres, plastic fibres, nylon fibres, terylene fibres, hemp fibres, wood fibres.
  • the curable matrix resin of the fibrous layer comprises thermoset resin, which can be selected from one or more of epoxy, polyester (unsaturated), phenolic, vinyl ester, polyurethane, silicone, polyamide, polyamideimide, bismaleimide, cyanate ester, benzoxazine.
  • the curable matrix resin of the fibrous layer comprises thermoplastic resin, which can be selected from one or more of polyethylene (PE), polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polycarbonate (PC), acrylonitrile butadiene styrene (ABS), polyamide (PA or nylon) and polypropylene (PP).
  • thermoplastic resin which can be selected from one or more of polyethylene (PE), polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polycarbonate (PC), acrylonitrile butadiene styrene (ABS), polyamide (PA or nylon) and polypropylene (PP).
  • the curable matrix resin of the fibrous layer can comprise biobased resins such as one or more of starch, starch caprolactone blends, polyesters—polyalkylene succinates, polyesteramides, polyhydroxy alkanoates—polyvinyl butyral-polyvinyl valeate, polyhydroxy acids—polylacticacid—polyglycolic acid, cellulose acetate, furfural alcohol/furan resins, oil modified polyesters—vegetable oil modification—cashew nut oil modification
  • the curable matrix resin is the same, substantially the same or otherwise compatible with the carrier medium of the graphene material.
  • the fibrous layer comprises a laminate structure, which comprises a plurality of plies of fibrous material.
  • the fibrous material is the same between laminates and in other embodiments the fibrous material can be different between laminates.
  • FIG. 8 is a diagrammatic cross-section of one exemplary embodiment of a composite moulding material 710 that has a laminate structure made up of three plies P 1 , P 2 , P 3 of fibrous materials impregnated with an uncured resinous material that holds the plies together.
  • Graphene/graphitic material 714 is shown on the surface 716 of the fibrous layer 712 at two localised regions R 1 , R 2 .
  • an outer layer (not shown) is provided over the surface 716 to cover and typically to protect the graphene/graphitic material 714 applied to the surface 716 .
  • the outer layer is typically removed prior to cure, although in certain embodiments it remains during the cure process and can become part of the cured composite component.
  • the invention also provides moulding laminates comprising a plurality of layered composite moulding materials as described above.
  • FIGS. 9 a and 9 b illustrate one embodiment of a moulding laminate 18 comprising three laminated layers of composite moulding material 810 A, 810 B, 810 C.
  • the composite moulding materials 810 A, 810 B, 810 C are the same and the layers are laminated directly one on top of the other so that bodies of the graphene/graphitic material 814 A, 814 B, 814 C in the respective layers are aligned on top of each other in the direction through generally (perpendicular to) the plane of the layers.
  • the composite moulding materials differ between layers, and in certain embodiments each layer is different to all other layers within the moulding laminate.
  • the location of the graphene/graphitic material can still be at the same region on the respective layers, such that when laminated the graphene/graphitic material can be in alignment, generally as illustrated in FIGS. 9 a and 9 b , despite the differences between in particular the fibrous layer in each composite moulding material.
  • the same or differing layers may be laminated so that the bodies of graphene/graphitic material on at least some of the layers are not in alignment.
  • FIGS. 10 a and 10 b illustrate a moulding laminate 118 that comprises three layers of composite material 910 A, 910 B, 910 C, wherein composite moulding materials 910 A and 910 C are the same and the bodies of graphene/graphitic material 914 A, 914 C are generally aligned in the direction generally perpendicular to (through) the plane of the layers, and the intermediate layer 910 B has a differing or offset pattern or array of graphene/graphitic material 910 B to those on composite moulding materials 910 A, 910 C.
  • Such embodiments provide differing locations of graphene/graphitic material, and thus locations of toughening and strengthening through the thickness of the laminate.
  • an outer laminate layer is provided to cover graphene/graphitic material that would otherwise be exposed on the outer surface of the stack of layers.
  • FIG. 11 shows the composite moulding materials of FIGS. 10 a and 10 b with such an outer laminate layer 20 .
  • the outer laminate layer 20 is the same as the fibrous layer of one or all of the composite moulding materials of the moulding laminate.
  • the outer laminate layer is of a different material, such as a protective or release sheet or film.
  • the fibrous material of the composite moulding materials of the present invention can be of many known forms and almost unlimited shapes and sizes, the primary limitations being that the materials are of a handleable and processable size and present a surface on which graphene/graphitic material can be applied to the fibrous layer at one or more localised regions over that surface. So for example, the material can be in the form of a sheet or ply, a 3D preform, a tape, a tow.
  • the invention also provides a fibre reinforced composite component comprising a plurality of fibrous layers held within a cured matrix resin and graphene/graphitic material at one or more localised regions between at least two of the fibrous layers to provide interlaminar fracture toughness of said region(s).
  • FIG. 12 illustrates one embodiment of a fibre reinforced composite component 22 that comprises four fibrous layers 1012 A, 1012 B, 1012 C, 1012 D, consolidated within a matrix resin with graphene/graphitic material 1014 A, 1014 B, 1014 C located between each of the four fibrous layers 1012 A, 1012 B, 1012 C, 1012 D at a generally central region within the component.
  • the presence of the graphene/graphitic material 1014 A, 1014 B, 1014 C provides for interlaminar fracture toughness where it is located and in the embodiment shown in FIG. 12 the alignment of graphene/graphitic material 1014 A, 1014 B, 1014 C in the direction through the thickness of the component 22 provides a central region of improved toughness extending through the thickness of the component 22 .
  • This through-thickness interlaminar toughness provides precise, localised beneficial physical characteristics to the component 22 .
  • FIG. 13 is a diagrammatic illustration of a mechanical fastening F, such as a rivet, bolt or similar, that passes through the illustrated central region of two fibre reinforced composite components 22 , to fasten them together.
  • a mechanical fastening F such as a rivet, bolt or similar
  • the provision of the graphene/graphitic material in accordance with the present invention provides for improved interlaminar fracture toughness and resistance to such interlaminar delamination and crack propagation and thus provides components with improved, yet localised toughness and resistance to delamination.
  • the composite moulding materials, the moulding laminates and the fibre reinforced composite components can be engineered through the selective, predetermined and precise localised provision of graphene/graphitic material at the locations where the fasteners are to be used, provides improved interlaminar toughness and strength in a specific, precise, cost effective and otherwise advantageous manner.
  • the present invention also provides a method of manufacturing a fibre reinforced composite component, the method comprising providing a plurality of fibrous layers, a curable matrix resin to consolidate the fibrous layers and applying a graphene/graphitic dispersion at one or more localised regions over a surface of at least one of the fibrous layers, positioning the fibrous layers so that the graphene/graphitic material is located between two adjacent fibrous layers and subjecting to conditions to cure the matrix resin around the fibrous material.
  • Known techniques and processes for forming fibre reinforced components can be used as part of the manufacturing method of the present invention. For example, manual and automated lay-up of plies of fibrous layers, vacuum moulding, autoclave moulding, fibre placement, pultrusion, tape laying, etc can be used.
  • FIG. 14 is a diagrammatic illustration of a simple vacuum moulding process used to form a composite component from the moulding laminate 118 of FIG. 10 b .
  • the laminate 118 is sealed on the surface of a mould M, beneath an impermeable membrane IM. Air from beneath the membrane IM is drawn out, shown diagrammatically by the arrow A, as heat is applied to the laminate to consolidate the laminate and cure the matrix resin.
  • Processes such as filament winding, tape laying and pultrusion can be used for moulding composite moulding materials of the present invention in the form of tows or tapes and can be used to mould composite moulding materials according to the present invention.
  • the graphene/graphitic material can be applied to a fibrous layer that is preimpregnated with resin, or to a dry fibrous layer (not preimpregnated with resin) or, within certain embodiments, of composite laminate according to the present invention, to both.
  • moulding laminates can be provided according to the present invention by layering any number of the same or different combinations of composite moulding materials falling within the scope of this invention, either in partial, total or non-alignment, and the nature of alignment may vary between respective layers in multilayer laminates.
  • the composite moulding material with a moulding laminate may be layered so that the orientation of respective composite moulding materials may be varied, such as alternated between successive layers, so that the respective surface carrying the graphene/graphitic material alternate through the structure, enabling graphene/graphite material on adjacent layers to contact when aligned.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Composite Materials (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Manufacturing & Machinery (AREA)
  • Nanotechnology (AREA)
  • Physics & Mathematics (AREA)
  • Condensed Matter Physics & Semiconductors (AREA)
  • General Physics & Mathematics (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Laminated Bodies (AREA)
  • Reinforced Plastic Materials (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
  • Carbon And Carbon Compounds (AREA)
  • Moulding By Coating Moulds (AREA)
US16/611,021 2017-05-09 2018-05-09 Composite moulding materials Abandoned US20200269522A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
GB1707428.7 2017-05-09
GBGB1707428.7A GB201707428D0 (en) 2017-05-09 2017-05-09 Composite moulding materials
PCT/GB2018/051237 WO2018206939A1 (en) 2017-05-09 2018-05-09 Composite moulding materials

Publications (1)

Publication Number Publication Date
US20200269522A1 true US20200269522A1 (en) 2020-08-27

Family

ID=59065497

Family Applications (2)

Application Number Title Priority Date Filing Date
US16/611,017 Active US11820872B2 (en) 2017-05-09 2018-05-09 Composite moulding materials
US16/611,021 Abandoned US20200269522A1 (en) 2017-05-09 2018-05-09 Composite moulding materials

Family Applications Before (1)

Application Number Title Priority Date Filing Date
US16/611,017 Active US11820872B2 (en) 2017-05-09 2018-05-09 Composite moulding materials

Country Status (8)

Country Link
US (2) US11820872B2 (ko)
EP (2) EP3609951A1 (ko)
JP (3) JP2020519500A (ko)
KR (2) KR102196307B1 (ko)
CN (2) CN111051396A (ko)
GB (3) GB201707428D0 (ko)
SG (1) SG10202112162SA (ko)
WO (2) WO2018206939A1 (ko)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20230141859A1 (en) * 2021-11-10 2023-05-11 Rolls-Royce Plc Composite laminate and a method of manufacturing a composite laminate
US11820872B2 (en) 2017-05-09 2023-11-21 Applied Graphene Materials Uk Limited Composite moulding materials
US11912007B2 (en) 2020-12-21 2024-02-27 Horton World Solutions, Llc Composite structured laminate and method of manufacture

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110713611B (zh) * 2019-07-25 2022-04-15 北京汽车集团有限公司 纤维增强复合材料的层间改性方法及纤维增强复合材料
WO2021067895A1 (en) * 2019-10-04 2021-04-08 Kana Holdings, LLC System for providing three-dimensional features on large format print products
US20230115588A1 (en) * 2021-10-13 2023-04-13 Nanoxplore Inc. Sheet molding compound reinforced with graphene flakes, and methods of producing the same

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20090306276A1 (en) * 2006-05-18 2009-12-10 Arkema France Use of composite materials based on carbon nanotubes as thickening agents for aqueous solutions
US20130175182A1 (en) * 2010-09-14 2013-07-11 Council Of Scientific & Industrial Research Electrochemical process for synthesis of graphene

Family Cites Families (48)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE2966731D1 (en) 1978-12-05 1984-04-05 Osaka City Valve nozzle for an injection molding machine
US5591382A (en) 1993-03-31 1997-01-07 Hyperion Catalysis International Inc. High strength conductive polymers
US6265333B1 (en) * 1998-06-02 2001-07-24 Board Of Regents, University Of Nebraska-Lincoln Delamination resistant composites prepared by small diameter fiber reinforcement at ply interfaces
US6846548B2 (en) * 1999-02-19 2005-01-25 Honeywell International Inc. Flexible fabric from fibrous web and discontinuous domain matrix
AU2003217548A1 (en) 2002-02-19 2003-09-09 Photon-X, Inc. Athermal polymer nanocomposites
US20060249705A1 (en) 2003-04-08 2006-11-09 Xingwu Wang Novel composition
US20050216075A1 (en) 2003-04-08 2005-09-29 Xingwu Wang Materials and devices of enhanced electromagnetic transparency
US20060102871A1 (en) 2003-04-08 2006-05-18 Xingwu Wang Novel composition
US7077334B2 (en) * 2003-04-10 2006-07-18 Massachusetts Institute Of Technology Positive pressure drop-on-demand printing
GB0505894D0 (en) 2005-03-22 2005-04-27 Ten Cate Advanced Textiles Bv Composition for dot on demand finishing of a textile article
KR100543176B1 (ko) * 2003-11-06 2006-01-20 한국기계연구원 나노 패터닝용 프린팅헤드 장치
US7605188B2 (en) 2004-12-31 2009-10-20 Owens Corning Intellectual Capital, Llc Polymer foams containing multi-functional layered nano-graphite
US20060062983A1 (en) 2004-09-17 2006-03-23 Irvin Glen C Jr Coatable conductive polyethylenedioxythiophene with carbon nanotubes
US8652391B2 (en) 2005-02-03 2014-02-18 Entegris, Inc. Method of forming substrate carriers and articles from compositions comprising carbon nanotubes
US8148276B2 (en) 2005-11-28 2012-04-03 University Of Hawaii Three-dimensionally reinforced multifunctional nanocomposites
CN1923506B (zh) * 2006-07-19 2010-08-04 中国航空工业第一集团公司北京航空材料研究院 一种增韧的复合材料层合板及其制备方法
US20080292887A1 (en) 2006-09-22 2008-11-27 Hyonny Kim Conductive Multiwalled Carbon Nanotube/Polyethylene Oxide (PEO) Composite Films and Methods of Use
US8017188B2 (en) 2007-04-17 2011-09-13 General Electric Company Methods of making articles having toughened and untoughened regions
US20090110919A1 (en) * 2007-10-24 2009-04-30 Dattatreya Panse Burn protective materials
US8693079B2 (en) 2008-01-31 2014-04-08 Ajjer, Llc Sealants and conductive busbars for chromogenic devices
US20110134617A1 (en) 2008-08-08 2011-06-09 Pp-Mid Gmbh Polymer molded bodies and printed circuit board arrangement and method for the production thereof
US20110204296A1 (en) 2008-08-20 2011-08-25 Bayer Materialscience Ag Method for producing composite materials having reduced resistance and comprising carbon nanotubes
US7981501B2 (en) * 2008-12-02 2011-07-19 GM Global Technology Operations LLC Laminated composites and methods of making the same
US20110014466A1 (en) 2009-07-17 2011-01-20 Xerox Corporation Composite materials comprising core-shell nano-fibrils
US20110143107A1 (en) 2009-12-14 2011-06-16 Basf Se Production of metallized surfaces, metallized surface and use thereof
US9475034B2 (en) 2010-04-22 2016-10-25 3M Innovative Properties Company Nonwoven fibrous webs containing chemically active particulates and methods of making and using same
WO2011133394A1 (en) 2010-04-22 2011-10-27 3M Innovative Properties Company Nonwoven nanofiber webs containing chemically active particulates and methods of making and using same
CN102254582B (zh) 2010-05-18 2013-05-15 国家纳米科学中心 一种石墨烯基导电材料及其制备方法
US8679621B2 (en) 2010-06-18 2014-03-25 Board Of Trustees Of The University Of Illinois Materials and methods for autonomous restoration of electrical conductivity
JP6054865B2 (ja) 2010-07-07 2016-12-27 スリーエム イノベイティブ プロパティズ カンパニー パターン付きエアレイド不織布繊維ウェブ、並びにこれらの製造及び使用方法
KR20130091734A (ko) 2010-07-07 2013-08-19 쓰리엠 이노베이티브 프로퍼티즈 컴파니 패턴화된 에어 레이드 부직포 일렉트릿 섬유질 웨브 및 그 제조 및 사용 방법
EP2629962B1 (en) 2010-10-18 2019-06-12 Short Brothers Plc Method of forming a composite material with added nanoparticles
US20120277360A1 (en) * 2010-10-28 2012-11-01 Vorbeck Materials Corp. Graphene Compositions
TWI517774B (zh) 2011-02-09 2016-01-11 創業發展聯盟技術有限公司 製造多層石墨烯被覆基板之方法
ES2540462T3 (es) 2011-02-16 2015-07-09 Grupo Antolín-Ingeniería, S.A. Proceso para obtener nanoplaquetas de óxido de grafeno y nanoplaquetas de grafeno
KR20130010285A (ko) * 2011-07-18 2013-01-28 정호순 탄소나노소재가 코팅된 전자파차폐용 복합재 및 그 제조방법
KR101251216B1 (ko) * 2011-09-26 2013-04-08 서울대학교산학협력단 잉크젯 프린팅을 이용한 그래핀 전극 제조 방법
WO2014210584A1 (en) * 2013-06-28 2014-12-31 Graphene 3D Lab Inc. Dispersions for nanoplatelets of graphene-like materials
US20150207254A1 (en) * 2014-01-22 2015-07-23 Apple Inc. Molded Plastic Structures With Graphene Signal Paths
CN107107537B (zh) 2014-09-22 2020-03-10 塞特工业公司 具有高的z方向电导率的复合材料
US9845556B2 (en) 2014-09-23 2017-12-19 The Boeing Company Printing patterns onto composite laminates
US10472472B2 (en) 2014-09-23 2019-11-12 The Boeing Company Placement of modifier material in resin-rich pockets to mitigate microcracking in a composite structure
EP3000602B1 (en) 2014-09-26 2020-07-22 Agfa Nv High viscosity jetting method
EP3034311B1 (en) 2014-12-18 2017-10-11 Agfa Graphics Nv Inkjet printing of pearlescent and metallic colours
FR3032362B1 (fr) * 2015-02-06 2020-05-29 Thales Procede de depot de nanoparticules et de microparticules carbonees oxydees
US10710113B2 (en) 2015-09-08 2020-07-14 Grafoid, Inc. Process for coating a substrate with a carbon-based material
US10427378B2 (en) 2015-10-29 2019-10-01 King Abdulaziz University Composite epoxy material with embedded silicon carbide and alumina nanoparticles
GB201707428D0 (en) 2017-05-09 2017-06-21 Applied Graphene Mat Plc ] Composite moulding materials

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20090306276A1 (en) * 2006-05-18 2009-12-10 Arkema France Use of composite materials based on carbon nanotubes as thickening agents for aqueous solutions
US20130175182A1 (en) * 2010-09-14 2013-07-11 Council Of Scientific & Industrial Research Electrochemical process for synthesis of graphene

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
Kim et al., Graphite Nanoplatelets Interlayered Carbon/Epoxy Composites, Nov. 2009, AIAA Journal, Vol. 47, No. 11, Technical notes, pp. 2779-2784 (Year: 2009) *

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11820872B2 (en) 2017-05-09 2023-11-21 Applied Graphene Materials Uk Limited Composite moulding materials
US11912007B2 (en) 2020-12-21 2024-02-27 Horton World Solutions, Llc Composite structured laminate and method of manufacture
US20230141859A1 (en) * 2021-11-10 2023-05-11 Rolls-Royce Plc Composite laminate and a method of manufacturing a composite laminate

Also Published As

Publication number Publication date
KR20200005615A (ko) 2020-01-15
EP3609951A1 (en) 2020-02-19
GB201906694D0 (en) 2019-06-26
GB201707428D0 (en) 2017-06-21
SG10202112162SA (en) 2021-12-30
GB2564525A (en) 2019-01-16
KR102196307B1 (ko) 2020-12-30
WO2018206939A9 (en) 2019-12-05
GB2572270B (en) 2020-07-29
JP6789415B2 (ja) 2020-11-25
EP3609950A1 (en) 2020-02-19
CN111051396A (zh) 2020-04-21
US11820872B2 (en) 2023-11-21
CN111051395A (zh) 2020-04-21
GB2572270A (en) 2019-09-25
US20200123331A1 (en) 2020-04-23
GB201807535D0 (en) 2018-06-20
EP3609950B1 (en) 2024-03-27
KR102535369B1 (ko) 2023-05-22
GB2564525B (en) 2020-03-25
EP3609950C0 (en) 2024-03-27
JP2023067882A (ja) 2023-05-16
WO2018206939A1 (en) 2018-11-15
JP2020519500A (ja) 2020-07-02
WO2018206938A9 (en) 2019-11-28
WO2018206938A1 (en) 2018-11-15
JP2020519503A (ja) 2020-07-02
KR20200005612A (ko) 2020-01-15

Similar Documents

Publication Publication Date Title
US20200269522A1 (en) Composite moulding materials
EP3000593B1 (en) Nonwoven decorative laminates and methods of making the same
US9511571B2 (en) Composite laminate having a damping interlayer and method of making the same
EP2067592B1 (en) Process for producing composite prepreg base, layered base, and fiber-reinforced plastic
JP2016064648A (ja) 複合構造体における微小亀裂生成を軽減するための、樹脂リッチポケット内への改質材料の載置
GB2498711A (en) Prepreg with powder coating, for FRP
US20040142143A1 (en) Moulding materials
US7267868B2 (en) Composite products and molded articles obtained from said products
JP2020519500A5 (ko)
KR101923381B1 (ko) 보강 복합재 및 이를 포함하는 물품
US10717109B2 (en) Nanotube enhancement of interlaminar performance for a composite component
JP5239350B2 (ja) プリプレグ及び繊維補強複合材料
US20220388274A1 (en) Moulding material
US20230241873A1 (en) Surface film for composite laminates
TWM642530U (zh) 回收碳纖維與回收塑膠纖維之複合材結構
KR20110079033A (ko) 열가소성 프리프레그의 제조방법 및 그에 의하여 제조된 열가소성 프리프레그

Legal Events

Date Code Title Description
STPP Information on status: patent application and granting procedure in general

Free format text: APPLICATION DISPATCHED FROM PREEXAM, NOT YET DOCKETED

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STCV Information on status: appeal procedure

Free format text: NOTICE OF APPEAL FILED

STCV Information on status: appeal procedure

Free format text: NOTICE OF APPEAL FILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: ADVISORY ACTION MAILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION

AS Assignment

Owner name: UNIVERSAL MATTER GBR LTD, ENGLAND

Free format text: CHANGE OF NAME;ASSIGNOR:APPLIED GRAPHENE MATERIALS UK LIMITED;REEL/FRAME:065737/0080

Effective date: 20230328