US20200165759A1 - Tempered Melt-Blown Nonwoven Having a High Compression Hardness - Google Patents

Tempered Melt-Blown Nonwoven Having a High Compression Hardness Download PDF

Info

Publication number
US20200165759A1
US20200165759A1 US16/633,065 US201816633065A US2020165759A1 US 20200165759 A1 US20200165759 A1 US 20200165759A1 US 201816633065 A US201816633065 A US 201816633065A US 2020165759 A1 US2020165759 A1 US 2020165759A1
Authority
US
United States
Prior art keywords
nonwoven fabric
meltblown nonwoven
annealed
meltblown
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US16/633,065
Other languages
English (en)
Inventor
Axel Nickel
Norbert Jording
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Publication of US20200165759A1 publication Critical patent/US20200165759A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
    • D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
    • D04H1/54—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties by welding together the fibres, e.g. by partially melting or dissolving
    • D04H1/56—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties by welding together the fibres, e.g. by partially melting or dissolving in association with fibre formation, e.g. immediately following extrusion of staple fibres
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
    • D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
    • D04H1/42—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties characterised by the use of certain kinds of fibres insofar as this use has no preponderant influence on the consolidation of the fleece
    • D04H1/4282—Addition polymers
    • D04H1/4291—Olefin series
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H3/00—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length
    • D04H3/005—Synthetic yarns or filaments
    • D04H3/007—Addition polymers
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H3/00—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length
    • D04H3/08—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length characterised by the method of strengthening or consolidating
    • D04H3/16—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length characterised by the method of strengthening or consolidating with bonds between thermoplastic filaments produced in association with filament formation, e.g. immediately following extrusion
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2321/00—Fibres made from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • D10B2321/02—Fibres made from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds polyolefins
    • D10B2321/022—Fibres made from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds polyolefins polypropylene

Definitions

  • the present invention relates to an annealed meltblown nonwoven with a high compression hardness and particularly to an annealed voluminous meltblown nonwoven with a high compression hardness.
  • the present invention further relates to a method for manufacturing such an annealed meltblown nonwoven fabric.
  • Felts and nonwoven fabrics are usually manufactured from staple fibers and/or continuous filaments using known mechanical or aerodynamic methods.
  • One known aerodynamic process is the meltblown method based on the Exxon principle as described in U.S. Pat. No. 3,755,527, for example. In that method, a low-viscosity polymer is extruded through capillaries located at a nozzle tip. The polymer droplets that form are then acted upon from two sides with a high-temperature, high-speed air flow that is referred to as blast air, whereby the polymer droplets are drawn into a free polymer jet in the form of fine filaments.
  • blast air high-temperature, high-speed air flow
  • the filaments obtained after deposition of the filaments on a carrier and after cooling can have a diameter and a fineness of a few micrometers in the single-digit range or even less.
  • the meltblown nonwoven fabrics or meltblown nonwovens manufactured in this manner are used for a variety of applications, such as barrier functions in the hygiene sector, for example. For these applications, the filaments are deposited on the carrier as a flat, two-dimensional nonwoven fabric.
  • Voluminous, three-dimensional meltblown nonwoven fabrics can also be manufactured by depositing the filaments formed between two suction drums or double drums, as described in DE 17 85 712 C3 and in U.S. Pat. No. 4,375,446, for example.
  • These voluminous meltblown nonwovens can be used, for example, as oil absorbers or as acoustic damping materials.
  • these voluminous meltblown nonwoven fabrics have the disadvantage that they are highly ductile and characterized by poor relaxation, which results in a loss of volume following a compressive load.
  • meltblown nonwoven fabrics are known from U.S. Pat. No. 4,118,531 which, in addition to the meltblown filaments, contain staple fibers incorporated therein that are composed of polyethylene terephthalate. These nonwoven fabrics are characterized by increased rebound elasticity, which is why the nonwoven has better relaxation. However, these nonwoven fabrics are composed of two polymers that are mutually incompatible, which precludes recycling and thus results in a sizable cost disadvantage.
  • the nonwoven fabrics must be voluminous—i.e., have a large internal void volume.
  • One major drawback of the known voluminous meltblown nonwovens is their comparatively low stiffness and resulting low compression hardness, particularly under greater loads. Furthermore, these materials are usually limp, which means that they deform under their own weight but do not retain any particular shape. For these reasons, it is only with difficulty that a predetermined shape can be imparted permanently to these known meltblown nonwoven fabrics, particularly to these known voluminous meltblown nonwoven fabrics. Deformation also generally results in a compression of these nonwoven fabrics.
  • this object is achieved by an annealed meltblown nonwoven fabric that can be obtained by means of a method in which at least a portion of the meltblown nonwoven fabric is subsequently annealed at a temperature between the glass transition temperature and 0.1° C. below the current melting temperature of the filaments of the meltblown nonwoven fabric ( 15 ), the meltblown nonwoven fabric having a weight per unit area of from 100 to 600 g/m 2 , a density of from 5 to 50 kg/m 3 , and preferably a compression hardness at 60% compression of at least 2 kPa as measured according to DIN EN ISO 3386.
  • a voluminous meltblown nonwoven fabric that is subsequently annealed at a temperature between the glass transition temperature and 0.1° C. below the melting temperature of the filaments of the meltblown nonwoven fabric, namely one with a weight per unit area of from 100 to 600 g/m 2 and with a density of from 5 to 50 kg/m 3 , has a significantly increased stiffness compared to the corresponding unannealed meltblown nonwoven fabric.
  • the voluminous meltblown nonwoven fabric according to the invention is characterized by a significantly increased compression hardness above all under greater loads such as at 40% or 60% compression, for example, namely by a compression hardness at 60% compression of at least 2 kPa.
  • the voluminous meltblown nonwoven fabric according to the invention can be easily shaped into a desired shape during annealing.
  • these benefits are at least partly due to the fact that the degree of crystallinity of the nonwoven filaments, which are predominantly amorphous beforehand, is significantly increased during the annealing that is subsequently performed according to the invention. This is supposed because the inventors have observed that, depending on the conditions during annealing, the melting temperature of the filaments of the meltblown nonwoven fabric can be increased by about 10 to 20° C. as a result of the annealing.
  • the experiments conducted by the inventors appear to show that, due to the very high pay-off speeds during the manufacture of the filaments to very thin finenesses of the filaments, the polymer melt cools rapidly despite the hot air blast, whereby the amorphous molecular structure of the melt is “frozen in place,” as it were.
  • the degree of crystallinity of the amorphous nonwoven filaments is increased by the annealing according to the invention.
  • the filament fineness and the nonwoven structure are not altered or only insignificantly at most by the annealing, so that the voluminous nonwoven fabric retains its other characteristics after annealing, namely its thickness-specific acoustic characteristics such as its absorption coefficient.
  • meltblown nonwoven fabric is understood to be a nonwoven fabric that is manufactured using one of the known meltblown methods, independently of whether it is a flat 2-dimensional nonwoven fabric or a voluminous nonwoven fabric. Methods for manufacturing such meltblown nonwoven fabrics are described in U.S. Pat. No. 4,118,531, in U.S. Pat. No. 4,375,446, in U.S. Pat. No. 4,380,570, and in DE 17 85 712 C3, for example.
  • annealing is generally understood as a heat treatment, i.e., the heating of the meltblown nonwoven fabric at the abovementioned temperature for a defined period of time.
  • the meltblown nonwoven fabric is subsequently annealed, namely at a temperature between the glass transition temperature and 0.1° C. below the melting temperature of the filaments of the meltblown nonwoven fabric.
  • both the glass transition temperature and the melting temperature of the filaments of the meltblown nonwoven fabric refer to the corresponding temperatures of the meltblown nonwoven fabric at that point in time.
  • the inventors have observed that, depending on the conditions during annealing, the melting temperature of the filaments of the meltblown nonwoven fabric can be increased by about 10 to 20° C. as a result of the annealing. The temperature can thus be increased during annealing.
  • the annealing can be carried out in such a way, for example, that the meltblown nonwoven fabric is initially annealed at a temperature of 150° C., the temperature is increased to 155° C. (which is 2° C. below the melting temperature that the filaments of the meltblown nonwoven fabric have at this point in time) after a defined period of time of 10 minutes, for example, before the temperature is increased to 165° C. (2° C. below the melting temperature that the filaments of the meltblown nonwoven fabric have at this point in time) after another defined period of time of 10 minutes, for example.
  • meltblown nonwoven fabric is partially or fully annealed in the process. A certain portion of the meltblown nonwoven fabric or multiple portions of the meltblown nonwoven fabric be annealed, whereas the rest of the meltblown nonwoven fabric remains unannealed. It is also possible and, according to the present invention, also especially preferred for the entire meltblown nonwoven fabric to be annealed.
  • the meltblown nonwoven fabric or the subregion(s) thereof to be annealed are annealed at a temperature that lies between 20° C. below the melting temperature and 0.1° C. below the melting temperature of the filaments of the meltblown nonwoven fabric.
  • the annealing is performed at a temperature that lies between 15° C. below the melting temperature and 1° C. below the melting temperature, more preferably between 10° C. below the melting temperature and 0.1° C. below the melting temperature, very especially preferably between 5° C. below the melting temperature and 0.1° C. below the melting temperature, such as for example about 5° C.
  • the melting temperature i.e., between 8° C. below the melting temperature and 2° C. below the melting temperature, for example
  • the duration of the annealing depends on the temperature to which the meltblown nonwoven is heated during the annealing, with a lower annealing temperature tending to require a longer annealing time.
  • an annealing period of from 1 minute to 10 days and particularly from 2 minutes to 24 hours has proven to be suitable.
  • the period of annealing is preferably from 2 minutes to 2 hours, especially preferably from 2 to 60 minutes, and most preferably from 2 to 10 minutes.
  • the meltblown nonwoven fabric is annealed for 2 minutes to 2 hours at a temperature that lies between 20° C. below the melting temperature and 1° C. below the melting temperature of the filaments of the meltblown nonwoven fabric.
  • the annealing of the meltblown nonwoven fabric is performed for 2 to 60 minutes at a temperature that lies between 15° C. below the melting temperature and 2° C. below the melting temperature of the filaments of the meltblown nonwoven fabric, and very especially preferably, the annealing of the meltblown nonwoven fabric is performed for 2 to 10 minutes at a temperature that lies about 5° C., i.e., between 8° C. below the melting temperature and 2° C. below the melting temperature of the filaments of the meltblown nonwoven fabric.
  • the melting point of the meltblown nonwoven fabric can increase during annealing due to the increase in the degree of crystallinity.
  • the interval between the annealing temperature and the melting point of the meltblown nonwoven fabric would increase more and more during annealing in this case, so the required annealing time would be relatively long. Therefore, it is proposed according to an alternative embodiment of the present invention that the temperature be increased during annealing in order to always keep the tempering temperature just below (e.g., about 2° C. or 5° C. below) the melting point of the meltblown nonwoven fabric, which increases during annealing. For example, if the melting temperature of the filaments of the meltblown nonwoven fabric is 152° C.
  • the annealing can, as explained above, be carried out in such a way, for example, that the meltblown nonwoven fabric is initially annealed at a temperature of 150° C., the temperature is increased to 155° C. (which is 2° C. below the melting temperature that the filaments of the meltblown nonwoven fabric have at this point in time) after a defined period of time of 10 minutes, for example, before the temperature is increased to 165° C. (2° C. below the melting temperature that the filaments of the meltblown nonwoven fabric have at this point in time) after another defined period of time of 10 minutes, for example.
  • the present invention is not restricted in terms of the manner in which the meltblown nonwoven fabric is annealed.
  • annealing in which the meltblown nonwoven fabric is exposed to hot air and/or with superheated steam has been found to be not only simple, but also especially effective.
  • the hot air or superheated steam has a temperature that corresponds to the temperature to which the meltblown nonwoven fabric is to be heated during annealing.
  • the meltblown nonwoven fabric is preferably exposed to hot air or superheated steam by having the hot air or superheated steam flow around or, more preferably, flow through the meltblown nonwoven fabric.
  • the meltblown nonwoven fabric is preferably annealed in a furnace having at least one blast box that is arranged such that the hot air or the superheated steam can be blown into the meltblown nonwoven fabric.
  • the blast box is to be designed such that the hot air or superheated steam is blown only into the portion(s) of the meltblown nonwoven fabric that are to be annealed.
  • the meltblown nonwoven fabric be annealed in a furnace having at least one suction box that is arranged such that air or superheated steam flowing through the meltblown nonwoven fabric can be extracted in order to ensure a reliable flow.
  • the application of a vacuum on both sides ensures that the hot air or the superheated steam flows reliably through the nonwoven fabric and that the nonwoven fabric does not collapse but maintains its volume.
  • the meltblown nonwoven fabric is annealed in a furnace that has at least one blast box and at least one suction box, with the at least one blast box being arranged such that the hot air or the superheated steam can be blown into the meltblown nonwoven fabric, and with the at least one suction box being arranged such that the air or superheated steam flowing through the meltblown fabric can be extracted.
  • the furnace especially preferably has two blast boxes and one or two suction boxes; in the case of one suction box, the suction box is arranged downstream from the first or second blast box, and in the case of two suction boxes, both suction boxes are arranged downstream from the first and the second blast box.
  • the meltblown nonwoven fabric has a weight per unit area of from 100 to 600 g/m 2 .
  • the weight per unit area of the meltblown nonwoven is from 150 to 400 g/m 2 , particularly preferably 200 to 400 g/m 2 , and very especially preferably 250 to 350 g/m 2 , e.g., about 350 g/m 2 .
  • meltblown nonwoven fabric be a voluminous meltblown nonwoven fabric with a density of from 7 to 40 kg/m 3 , more preferably 8 to 25 kg/m 3 , and especially preferably 10 to 20 kg/m 3 .
  • the filaments of the meltblown nonwoven fabric can be composed of any polymer having a melting point that is suitable for extrusion and a sufficiently low viscosity in the molten state for the meltblown process, such as polyolefins, polyamides, polyesters, polyphenylene sulfides, polytetrafluoroethylenes, or a polyether ether ketone, for example.
  • polyolefins polyamides
  • polyesters polyphenylene sulfides
  • polytetrafluoroethylenes polytetrafluoroethylenes
  • polyether ether ketone a polyether ether ketone
  • polyesters are polyethylene terephthalate and polybutylene terephthalate. Filaments made of polyolefin and especially preferably of polypropylene and/or polyethylene have proven to be especially suitable.
  • the filaments of the meltblown nonwoven fabric are very especially preferably composed of isotactic polypropylene, since it has been found that the degree of crystallinity is increased especially well during annealing in the case of filaments of isotactic polypropylene.
  • the thickness of the meltblown nonwoven fabric is preferably 6 to 50 mm, more preferably 8 to 40 mm, very especially preferably 10 to 30 mm, and most preferably 15 to 25 mm, such as particularly about 20 mm.
  • the meltblown nonwoven fabric be annealed in a mold body in order to also impart a predefined shape to the meltblown nonwoven fabric during annealing.
  • This can be achieved, for example, by having the mold in which the meltblown nonwoven fabric is annealed be embodied at least partially as a screen, so that the meltblown nonwoven fabric can be flowed through and/or flowed around by hot air or with superheated steam during annealing.
  • meltblown nonwoven fabric be placed into a mold body after heating but before cooling and thereby transformed into a predefined shape, with the meltblown nonwoven fabric being cooled in the mold in order to conclude the annealing process.
  • meltblown nonwoven fabric is shaped by the annealing as a stamped part into a specific shape, such as a hemisphere, for example.
  • the meltblown nonwoven fabric that is annealed and shaped in this way has substantially greater dimensional stability than the starting material and retains its shape to the greatest possible extent.
  • the meltblown nonwoven fabric can therefore take on strengths after annealing that enable additional stiffening structural elements in the meltblown nonwoven to be dispensed with after molding.
  • a provision is made that at least one spacer is arranged in the meltblown nonwoven fabric in the thickness direction of the meltblown nonwoven fabric that has a length that is greater than the thickness of the meltblown nonwoven fabric. This is advantageous, for example, if the meltblown nonwoven fabric is to be used as an acoustic absorber.
  • an inherently stiff molded part is obtained in which—if it is mounted as an acoustic absorber in front of a reflective plane, such as the sheet-metal wall of an automobile—a not insignificant air gap is formed between the absorber and the reflective plane due to the spacer or spacers, the additional air volume that is created in this way acting as an integral part of the structure of the absorber.
  • the volume of air between the absorber and wall described above can also be created by a structure of the wall in the case of a flat absorber or a structure of the wall and of the absorber, the inherent stiffness of the absorber being necessary for the permanent formation of the volume of air.
  • meltblown nonwoven fabric to be subjected to annealing can be manufactured by means of any of the known meltblown processes, such as those described in U.S. Pat. Nos. 4,118,531, 4,375,446, 4,380,570, or DE 17 85 712 C3, for example.
  • nonwoven fabric is manufactured using a meltblown process by applying flowing air to the outside of a polymer melt that is extruded through a die and drawing said polymer melt before the filaments that are formed in this way are placed onto a carrier and cooled.
  • the carrier is preferably a double suction drum.
  • the degree of crystallinity of the meltblown nonwoven fabric is increased by the annealing.
  • the filaments of the annealed meltblown nonwoven fabric have a degree of crystallinity at least in portions and preferably over the entire surface of from 20 to 80%, more preferably from 30 to 75%, especially preferably from 40 to 75%, and most preferably from 50 to 70%.
  • the annealed regions of the annealed meltblown nonwoven fabric preferably have a degree of crystallinity of from 20 to 80%, more preferably from 30 to 75%, especially preferably from 40 to 75%, and most preferably from 50 to 70%.
  • the meltblown nonwoven fabric has, at least in portions and preferably over its entire surface, a compression hardness (compressive stress) at 60% compression of at least 2 kPa as measured according to DIN EN ISO 3386.
  • the meltblown nonwoven fabric has a compression hardness (compressive stress) at least in portions and preferably over its entire surface at 60% compression of at least 4 kPa, more preferably of at least 8 kPa, even more preferably of at least 10 kPa, even more especially preferably of at least 12 kPa, yet more especially preferably of at least 15 kPa, very especially preferably of at least 20 kPa, and most preferably of at least 30 kPa as measured according to DIN EN ISO 3386.
  • the compression hardness at 60% compression is to be understood as the required compressive stress under which a material sample undergoes a change in thickness by 60% of its initial thickness. Furthermore, the preload for determining the initial thickness of the material is reduced to 0.014 kPa in order to take the very low compression hardness of the unannealed material into account. In case of degrees of compression or other test conditions that deviate therefrom, deviating compressive stresses with nonlinear correlations to the cited values can arise.
  • the annealing temperature be increased in a continuous or stepwise manner during annealing, preferably even beyond the melting temperature of the unannealed filaments of the meltblown nonwoven fabric, but on the proviso that the annealing temperature be always at least 0.1° C. below the current melting temperature of the filaments of the meltblown nonwoven fabric existing at this point in time.
  • the present invention makes it possible to increase the degree of crystallinity of the filaments of meltblown nonwoven fabrics in portions or over their entire surface and thus the stiffness of meltblown nonwoven fabrics in portions or over their entire surface.
  • the present invention can be used to anneal the entire surface of the meltblown nonwoven and thus to increase the degree of crystallinity over the entire surface of the meltblown nonwoven fabric.
  • This enables rigid, pressure-stable two-dimensional components to be produced.
  • the shaped meltblown nonwoven fabric can also be annealed only in portions, thereby increasing the degree of crystallinity in the meltblown nonwoven fabric only over a portion of its surface, for example in order to increase the stiffness only in component-specific regions or in the continuous grid of the component.
  • the edge regions of the component made of the meltblown nonwoven fabric can be annealed in order to make the edge regions of the component stiffer, for example in order to increase the stackability of the component made of the meltblown nonwoven fabric.
  • the annealing of the meltblown nonwoven fabric enables a component to be shaped and the degree of crystallinity therein increased over its entire surface in order to manufacture inherently rigid three-dimensional components.
  • locally compressed or consolidated regions can expand the functionality, particularly in order to form contact surfaces at attachment points, for example.
  • Another object of the present invention is an annealed meltblown nonwoven fabric whose filaments have a degree of crystallinity at least in portions and preferably over their entire surface of from 20 to 80%, preferably from 30 to 75%, especially preferably from 40 to 75%, and most preferably from 50 to 70%.
  • the present invention further relates to a meltblown nonwoven fabric that has, at least in portions and preferably over its entire surface, a compression hardness at 60% compression of at least 2 kPa as measured according to DIN EN ISO 3386.
  • the meltblown nonwoven fabric has a compression hardness at 60% compression of at least 4 kPa, especially preferably of at least 6 kPa, more preferably of at least 8 kPa, even more preferably of at least 10 kPa, even more preferably of at least 12 kPa, yet more preferably of at least 15 kPa, very especially preferably of at least 20 kPa, and most preferably of at least 30 kPa.
  • Another object of the object of the present invention is a method for manufacturing an annealed meltblown nonwoven fabric with a weight per unit area of from 100 to 600 g/m 2 and with a density of from 5 to 50 kg/m 3 , comprising the following steps:
  • the meltblown nonwoven fabric is especially preferably annealed in step b) for 2 minutes to 2 hours at a temperature that lies between 20° C. below the melting temperature and 1° C. below the melting temperature of the filaments of the meltblown nonwoven fabric.
  • FIG. 1 shows a schematic of a furnace for manufacturing an annealed meltblown nonwoven fabric according to one exemplary embodiment of the present invention.
  • FIG. 2 shows a schematic of a mold for the simultaneous shaping and annealing of a meltblown nonwoven fabric according to another exemplary embodiment of the present invention.
  • FIG. 3 shows a comparison of the compression hardness of an annealed meltblown nonwoven fabric according to another exemplary embodiment of the present invention to the compression hardness of an unannealed meltblown nonwoven fabric according to the prior art.
  • FIG. 4 shows the results of the measurement of sound absorption of annealed meltblown nonwoven fabric prepared in example 1 according to the present invention (curve A) in comparison to the unannealed meltblown nonwoven fabric manufactured in the comparative example (curve B).
  • FIG. 5 shows the results of the measurement of the absorption coefficient of the annealed meltblown nonwoven fabric prepared in example 1 mounted directly against a body panel (curve A), mounted on a body panel at a distance of 10 mm (curve B), and mounted on a body panel at a distance of 40 mm (curve C).
  • FIG. 1 shows a schematic of a belt furnace 10 for manufacturing an annealed meltblown nonwoven fabric according to one exemplary embodiment of the present invention.
  • the furnace 10 comprises air-permeable belts 14 , 14 ′ that are guided and driven on rollers 12 over which the meltblown nonwoven fabric 15 is guided into and through the furnace 10 .
  • a first blast box 16 , a suction box 18 , and a second blast box 16 ′ are arranged in the furnace 10 above and below the two belts 14 , 14 ′ in this sequence as seen from right to left in the direction of conveyance.
  • the meltblown nonwoven fabric 15 is fed from right to left on the lower belt 14 through the furnace 10 .
  • meltblown nonwoven fabric 15 passes through the blast boxes 16 , 16 ′, hot air is flowed into and through it in order to elevate the filaments of the meltblown nonwoven fabric 15 to the desired annealing temperature. Air flowing through the meltblown nonwoven fabric 15 is extracted in the vicinity of the suction box 18 in order to ensure that the meltblown nonwoven fabric 15 is reliably flowed through by the hot air and the meltblown nonwoven fabric 15 also does not collapse but rather retains its volume.
  • FIG. 2 shows a schematic of a mold 20 for the simultaneous shaping and annealing of a meltblown nonwoven fabric 15 according to another exemplary embodiment of the present invention.
  • the meltblown nonwoven fabric 15 is maintained in the desired shape from both sides by appropriately shaped screens 22 , 22 ′ of which the mold 20 is composed and heated to the desired temperature for annealing through passage of air around or through.
  • the nonwoven mat manufactured in this way retains the impressed shape and is dimensionally stable.
  • FIG. 3 shows the compression hardness of an annealed meltblown nonwoven fabric at 60% compression with a weight per unit area of about 300 g/m2 and a density of about 15 kg/m3 according to another exemplary embodiment of the present invention (upper curve) and the compression hardness of an unannealed meltblown nonwoven fabric with the same weight per unit area and the same density according to the prior art (lower curve) in a comparison.
  • the compression hardness is shown as compression in % versus the compressive stress in kPa. As can be seen from FIG.
  • a meltblown nonwoven fabric with a weight per unit area of 300 g/m2 and with a density of 15 kg/m3 was manufactured from filaments composed of isotactic polypropylene with a mean filament fineness of 5 ⁇ m using the meltblown process described in U.S. Pat. No. 4,375,446.
  • This meltblown nonwoven fabric was then annealed in a circulating-air furnace for 10 minutes at 158° C. As a result of the placement of the cold nonwoven fabric and the opening of the furnace door, the initial temperature was below the melting point of the filaments of the unannealed nonwoven fabric.
  • the sound absorption coefficient of the annealed meltblown nonwoven fabric was measured according to DIN EN ISO 10534 as a function of the thickness-normalized frequency.
  • the results are shown in FIG. 4 in curve A in comparison to the values that were achieved with the unannealed meltblown nonwoven fabric that was manufactured in the comparative example (curve B).
  • the unit of the abscissa is the measurement frequency ⁇ absorber thickness/15 mm.
  • the comparison of the results shows that the annealing according to the invention has no negative influences on the sound absorption characteristics of the nonwoven fabric.
  • a portion of the annealed meltblown nonwoven fabric was mounted directly against a vehicle body panel, whereas another portion of the annealed meltblown nonwoven fabric was mounted on a vehicle body panel at a distance of 10 mm and another portion of the annealed meltblown nonwoven fabric was mounted on a vehicle body panel at a distance of 40 mm.
  • the absorption coefficient was then determined for the three constructions as a function of frequency. The results are shown in FIG.
  • curve A shows the values for the meltblown nonwoven fabric that was mounted directly against the vehicle body panel
  • curve B shows the values for the meltblown nonwoven fabric that was mounted on the vehicle body panel at a distance of 10 mm
  • curve C howl the values for the meltblown nonwoven fabric that was mounted on the vehicle body panel at a distance of 40 mm.
  • An annealed meltblown nonwoven fabric was manufactured according to the procedure described in example 1, except that the annealing was carried out at 155° C. for 10 minutes.
  • An annealed meltblown nonwoven fabric was manufactured according to the procedure described in example 1, except that the annealing was carried out at 155° C. for 25 minutes.
  • An unannealed meltblown nonwoven fabric was manufactured according to the procedure described in example 1, except that the annealing described in example 1 was not carried out.

Landscapes

  • Engineering & Computer Science (AREA)
  • Textile Engineering (AREA)
  • Nonwoven Fabrics (AREA)
US16/633,065 2017-05-22 2018-05-22 Tempered Melt-Blown Nonwoven Having a High Compression Hardness Abandoned US20200165759A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
EP17172180.6A EP3406780B1 (de) 2017-05-22 2017-05-22 Getemperter meltblown-vliesstoff mit hoher stauchhärte
EP17172180.6 2017-05-22
PCT/EP2018/063287 WO2018215402A1 (de) 2017-05-22 2018-05-22 Getemperter meltblown-vliesstoff mit hoher stauchhärte

Publications (1)

Publication Number Publication Date
US20200165759A1 true US20200165759A1 (en) 2020-05-28

Family

ID=58772401

Family Applications (1)

Application Number Title Priority Date Filing Date
US16/633,065 Abandoned US20200165759A1 (en) 2017-05-22 2018-05-22 Tempered Melt-Blown Nonwoven Having a High Compression Hardness

Country Status (4)

Country Link
US (1) US20200165759A1 (zh)
EP (1) EP3406780B1 (zh)
CN (1) CN111226001B (zh)
WO (1) WO2018215402A1 (zh)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11192327B2 (en) * 2017-07-03 2021-12-07 Axel Nickel Voluminous meltblown nonwoven fabric with improved stackability and storability

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5702652A (en) * 1990-05-31 1997-12-30 Crain Industries, Inc. Controlled cooling of porous materials
US6214094B1 (en) * 1997-10-01 2001-04-10 3M Innovative Properties Company Electret filters that exhibit increased oily mist resistance
US20080011303A1 (en) * 2006-07-17 2008-01-17 3M Innovative Properties Company Flat-fold respirator with monocomponent filtration/stiffening monolayer

Family Cites Families (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE1785712C3 (de) 1967-09-29 1979-01-11 Celanese Corp., New York, N.Y. (V.St.A.) Fülliger Vliesstoff und seine Verwendung
US3755527A (en) 1969-10-09 1973-08-28 Exxon Research Engineering Co Process for producing melt blown nonwoven synthetic polymer mat having high tear resistance
CA1073648A (en) 1976-08-02 1980-03-18 Edward R. Hauser Web of blended microfibers and crimped bulking fibers
JPS6056825B2 (ja) 1978-05-01 1985-12-12 東亜燃料工業株式会社 不織布の製造法
US4380570A (en) 1980-04-08 1983-04-19 Schwarz Eckhard C A Apparatus and process for melt-blowing a fiberforming thermoplastic polymer and product produced thereby
CA2101833A1 (en) * 1992-12-14 1994-06-15 Kimberly-Clark Worldwide, Inc. Stretchable meltblown fabric with barrier properties
US5690873A (en) * 1995-12-11 1997-11-25 Pall Corporation Polyarylene sulfide melt blowing methods and products
US6213122B1 (en) * 1997-10-01 2001-04-10 3M Innovative Properties Company Electret fibers and filter webs having a low level of extractable hydrocarbons
US6068799A (en) * 1997-10-01 2000-05-30 3M Innovative Properties Company Method of making electret articles and filters with increased oily mist resistance
US5958322A (en) * 1998-03-24 1999-09-28 3M Innovation Properties Company Method for making dimensionally stable nonwoven fibrous webs
US7476632B2 (en) * 2002-11-15 2009-01-13 3M Innovative Properties Company Fibrous nonwoven web
US8802002B2 (en) * 2006-12-28 2014-08-12 3M Innovative Properties Company Dimensionally stable bonded nonwoven fibrous webs
US10161063B2 (en) * 2008-09-30 2018-12-25 Exxonmobil Chemical Patents Inc. Polyolefin-based elastic meltblown fabrics
JP5477123B2 (ja) * 2010-04-02 2014-04-23 Ｊｎｃ株式会社 熱風処理不織布加工装置および加工方法
KR102251716B1 (ko) * 2013-11-26 2021-05-13 쓰리엠 이노베이티브 프로퍼티즈 캄파니 치수 안정적인 용융-취입된 부직 섬유질 구조체, 및 이를 제조하기 위한 방법 및 장치

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5702652A (en) * 1990-05-31 1997-12-30 Crain Industries, Inc. Controlled cooling of porous materials
US6214094B1 (en) * 1997-10-01 2001-04-10 3M Innovative Properties Company Electret filters that exhibit increased oily mist resistance
US20080011303A1 (en) * 2006-07-17 2008-01-17 3M Innovative Properties Company Flat-fold respirator with monocomponent filtration/stiffening monolayer

Non-Patent Citations (3)

* Cited by examiner, † Cited by third party
Title
Higashitani, Ko Makino, Hisao Matsusaka, Shuji. (2020). Powder Technology Handbook (4th Edition). Taylor & Francis. Retrieved from https://app.knovel.com/hotlink/toc/id:kpPTHE0026/powder-technology-handbook/powder-technology-handbook *
Meaning of Compression, Cambridge Dictionary, https://dictionary.cambridge.org/us/dictionary/english/compression, retrieved 8 June 2023. *
Meaning of Stiffness, Cambridge Dictionary, https://dictionary.cambridge.org/us/dictionary/english/stiffness, retrieved 8 June 2023. *

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11192327B2 (en) * 2017-07-03 2021-12-07 Axel Nickel Voluminous meltblown nonwoven fabric with improved stackability and storability

Also Published As

Publication number Publication date
CN111226001B (zh) 2022-12-30
CN111226001A (zh) 2020-06-02
EP3406780A1 (de) 2018-11-28
WO2018215402A1 (de) 2018-11-29
EP3406780B1 (de) 2020-01-08

Similar Documents

Publication Publication Date Title
US11440289B2 (en) Melt blown nonwoven fabric, laminate using same, melt blown nonwoven fabric production method and melt blowing apparatus
US6656400B2 (en) Method for producing a pleatable filter material from a nonwoven fabric
US4496508A (en) Method for manufacturing polypropylene spun-bonded fabrics with low draping coefficient
US10655256B2 (en) Nonwoven fabric structure and method for producing the same
KR101836623B1 (ko) 자동차 외장용 부직포 보드 및 이의 제조방법
KR102302375B1 (ko) 멜트 블로 부직포 및 그 제조 방법
JP6362400B2 (ja) 不織布ウェブ
US20200165759A1 (en) Tempered Melt-Blown Nonwoven Having a High Compression Hardness
KR102036663B1 (ko) 우수한 공기 투과도와 개선된 보풀 및 박리강도를 갖는 에어 필터 지지체용 부직포의 제조방법
CN112074632A (zh) 卷曲复合纤维的不织布及其层压制品、与包含该层压制品的物品
CN104988660A (zh) 一种立体热风无纺布生产方法
KR102351767B1 (ko) 자동차 장비재용 반제품의 제조 방법
KR101651943B1 (ko) 이형단면 중공섬유를 포함하는 섬유 집합체
US20050014673A1 (en) Fabric softener dryer sheet substrate
EP3611296A2 (en) Non-woven fabric improved in weight reduction and sound absorption and method for manufacturing same
JP2001011768A (ja) 伸縮性不織布およびその製造方法
KR100715203B1 (ko) 공기필터용 폴리에스테르 스펀본드 부직포 및 그 제조방법
KR20090092437A (ko) 흡음재와 표피재가 결합된 섬유기재 및 이것의 제조방법
JP3219800B2 (ja) 電池用セパレータの製造方法
KR102620314B1 (ko) 폴리젖산 에어 스루 본딩 부직포의 제조방법
AU2006101041B4 (en) A thermoformable acoustic sheet
KR20210068221A (ko) 성형체 및 이의 제조방법
JP2002242066A (ja) 吸音材の製造方法
US20190186061A1 (en) Method of non-woven fabric for base cloth of carpet
KR20020004705A (ko) 합성섬유 스펀본드 부직포

Legal Events

Date Code Title Description
STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: ADVISORY ACTION MAILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION