US20180244020A1 - Interlayer film for laminated glass, and laminated glass - Google Patents

Interlayer film for laminated glass, and laminated glass Download PDF

Info

Publication number
US20180244020A1
US20180244020A1 US15/757,962 US201615757962A US2018244020A1 US 20180244020 A1 US20180244020 A1 US 20180244020A1 US 201615757962 A US201615757962 A US 201615757962A US 2018244020 A1 US2018244020 A1 US 2018244020A1
Authority
US
United States
Prior art keywords
layer
interlayer film
laminated glass
mole
less
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US15/757,962
Other languages
English (en)
Inventor
Tatsuya Iwamoto
Nami Minakuchi
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sekisui Chemical Co Ltd
Original Assignee
Sekisui Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sekisui Chemical Co Ltd filed Critical Sekisui Chemical Co Ltd
Assigned to SEKISUI CHEMICAL CO., LTD. reassignment SEKISUI CHEMICAL CO., LTD. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: MINAKUCHI, Nami, IWAMOTO, TATSUYA
Publication of US20180244020A1 publication Critical patent/US20180244020A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/1055—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
    • B32B17/10761—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer containing vinyl acetal
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/10009—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the number, the constitution or treatment of glass sheets
    • B32B17/10036—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the number, the constitution or treatment of glass sheets comprising two outer glass sheets
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/1055—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
    • B32B17/10614—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer comprising particles for purposes other than dyeing
    • B32B17/10633—Infrared radiation absorbing or reflecting agents
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/1055—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
    • B32B17/10678—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer comprising UV absorbers or stabilizers, e.g. antioxidants
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/1055—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
    • B32B17/10688—Adjustment of the adherence to the glass layers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/1055—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
    • B32B17/1077—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer containing polyurethane
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/1055—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
    • B32B17/10788—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer containing ethylene vinylacetate
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/10807—Making laminated safety glass or glazing; Apparatus therefor
    • B32B17/10816—Making laminated safety glass or glazing; Apparatus therefor by pressing
    • B32B17/10825—Isostatic pressing, i.e. using non rigid pressure-exerting members against rigid parts
    • B32B17/10834—Isostatic pressing, i.e. using non rigid pressure-exerting members against rigid parts using a fluid
    • B32B17/10844—Isostatic pressing, i.e. using non rigid pressure-exerting members against rigid parts using a fluid using a membrane between the layered product and the fluid
    • B32B17/10853—Isostatic pressing, i.e. using non rigid pressure-exerting members against rigid parts using a fluid using a membrane between the layered product and the fluid the membrane being bag-shaped
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/06—Layered products comprising a layer of synthetic resin as the main or only constituent of a layer, which is next to another layer of the same or of a different material
    • B32B27/08—Layered products comprising a layer of synthetic resin as the main or only constituent of a layer, which is next to another layer of the same or of a different material of synthetic resin
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/18—Layered products comprising a layer of synthetic resin characterised by the use of special additives
    • B32B27/22—Layered products comprising a layer of synthetic resin characterised by the use of special additives using plasticisers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/30—Layered products comprising a layer of synthetic resin comprising vinyl (co)polymers; comprising acrylic (co)polymers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/30—Layered products comprising a layer of synthetic resin comprising vinyl (co)polymers; comprising acrylic (co)polymers
    • B32B27/306—Layered products comprising a layer of synthetic resin comprising vinyl (co)polymers; comprising acrylic (co)polymers comprising vinyl acetate or vinyl alcohol (co)polymers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B7/00—Layered products characterised by the relation between layers; Layered products characterised by the relative orientation of features between layers, or by the relative values of a measurable parameter between layers, i.e. products comprising layers having different physical, chemical or physicochemical properties; Layered products characterised by the interconnection of layers
    • B32B7/02—Physical, chemical or physicochemical properties
    • B32B7/027—Thermal properties
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B60—VEHICLES IN GENERAL
    • B60J—WINDOWS, WINDSCREENS, NON-FIXED ROOFS, DOORS, OR SIMILAR DEVICES FOR VEHICLES; REMOVABLE EXTERNAL PROTECTIVE COVERINGS SPECIALLY ADAPTED FOR VEHICLES
    • B60J1/00—Windows; Windscreens; Accessories therefor
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C27/00—Joining pieces of glass to pieces of other inorganic material; Joining glass to glass other than by fusing
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2250/00—Layers arrangement
    • B32B2250/03—3 layers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/10—Properties of the layers or laminate having particular acoustical properties
    • B32B2307/102—Insulating
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2329/00—Polyvinylalcohols, polyvinylethers, polyvinylaldehydes, polyvinylketones or polyvinylketals
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2329/00—Polyvinylalcohols, polyvinylethers, polyvinylaldehydes, polyvinylketones or polyvinylketals
    • B32B2329/06—PVB, i.e. polyinylbutyral
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2605/00—Vehicles
    • B32B2605/08—Cars
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/24—Structurally defined web or sheet [e.g., overall dimension, etc.]
    • Y10T428/24942—Structurally defined web or sheet [e.g., overall dimension, etc.] including components having same physical characteristic in differing degree
    • Y10T428/2495—Thickness [relative or absolute]

Definitions

  • the present invention relates to an interlayer film for laminated glass which is used for obtaining laminated glass. Moreover, the present invention relates to laminated glass prepared with the interlayer film for laminated glass.
  • laminated glass Since laminated glass generates only a small amount of scattering glass fragments even when subjected to external impact and broken, laminated glass is excellent in safety. As such, the laminated glass is widely used for automobiles, railway vehicles, aircraft, ships, buildings, and the like.
  • the laminated glass is produced by sandwiching an interlayer film for laminated glass between two glass plates.
  • Examples of the interlayer film for laminated glass include a single-layered interlayer film having a one-layer structure and a multi-layered interlayer film having a two or more-layer structure.
  • Patent Document 1 discloses a sound insulating layer including 100 parts by weight of a polyvinyl acetal resin with an acetalization degree of 60 to 85% by mole, 0.001 to 1.0 part by weight of at least one kind of metal salt among an alkali metal salt and an alkaline earth metal salt, and a plasticizer in an amount more than 30 parts by weight.
  • This sound insulating layer can be used alone as a single-layered interlayer film.
  • Patent Document 1 also describes a multi-layered interlayer film in which the sound insulating layer and another layer are layered.
  • Another layer to be layered with the sound insulating layer includes 100 parts by weight of a polyvinyl acetal resin with an acetalization degree of 60 to 85% by mole, 0.001 to 1.0 part by weight of at least one kind of metal salt among an alkali metal salt and an alkaline earth metal salt, and a plasticizer in an amount of 30 parts by weight or less.
  • Patent Document 2 discloses an interlayer film which is constituted of a polymer layer having a glass transition temperature of 33° C. or more.
  • the sound insulating properties in a high frequency area of 1000 Hz or more of the laminated glass are not sufficient. Moreover, it is difficult to sufficiently heighten the sound insulating properties in a high frequency area of 2000 Hz or more of the laminated glass and it is further difficult to sufficiently heighten the sound insulating properties in a high frequency area of about 4000 Hz of the laminated glass.
  • An object of the present invention is to provide an interlayer film for laminated glass with which the sound insulating properties in a high frequency area of 2000 Hz or more can be effectively enhanced. Moreover, the present invention is also aimed at providing laminated glass prepared with the interlayer film for laminated glass.
  • an interlayer film for laminated glass having a three or more-layer structure and being provided with a first layer containing a thermoplastic resin, a second layer containing a thermoplastic resin, and a third layer containing a thermoplastic resin, the second layer being arranged on a first surface side of the first layer, the third layer being arranged on a second surface side opposite to the first surface of the first layer, the glass transition temperature of the first layer being lower than the glass transition temperature of the second layer, the glass transition temperature of the first layer being lower than the glass transition temperature of the third layer, the ratio of the thickness of the first layer to the total thickness of the second layer and the third layer being 0.25 or more, and the thickness of the interlayer film being more than 600 ⁇ m.
  • the thermoplastic resin in the first layer is a polyvinyl acetal resin and the content of the hydroxyl group of the polyvinyl acetal resin in the first layer is 30% by mole or less.
  • the interlayer film is provided with the second layer as a surface layer and is provided with the third layer as a surface layer.
  • thermoplastic resin in the first layer be a polyvinyl acetal resin. It is preferred that the thermoplastic resin in the second layer be a polyvinyl acetal resin. It is preferred that the thermoplastic resin in the third layer be a polyvinyl acetal resin. It is preferred that the first layer contain a plasticizer. It is preferred that the second layer contain a plasticizer. It is preferred that the third layer contain a plasticizer.
  • laminated glass including a first lamination glass member, a second lamination glass member, and the above-described interlayer film for laminated glass, the interlayer film for laminated glass being arranged between the first lamination glass member and the second lamination glass member.
  • the interlayer film for laminated glass according to the present invention has a three or more-layer structure and is provided with a first layer containing a thermoplastic resin, a second layer containing a thermoplastic resin, and a third layer containing a thermoplastic resin, the second layer is arranged on a first surface side of the first layer, the third layer is arranged on a second surface side opposite to the first surface of the first layer, the glass transition temperature of the first layer is lower than the glass transition temperature of the second layer, the glass transition temperature of the first layer is lower than the glass transition temperature of the third layer, the ratio of the thickness of the first layer to the total thickness of the second layer and the third layer is 0.25 or more, and the thickness of the interlayer film is more than 600 ⁇ m, the sound insulating properties in a high frequency area of 2000 Hz or more can be effectively enhanced.
  • FIG. 1 is a sectional view schematically showing an interlayer film for laminated glass in accordance with a first embodiment of the present invention.
  • FIG. 2 is a sectional view schematically showing an example of laminated glass prepared with the interlayer film for laminated glass shown in FIG. 1 .
  • the interlayer film for laminated glass (hereinafter, sometimes abbreviated as “the interlayer film”) according to the present invention has a three or more-layer structure.
  • the interlayer film according to the present invention may have a three-layer structure and may have a three or more-layer structure.
  • the interlayer film according to the present invention is provided with a first layer containing a thermoplastic resin, a second layer containing a thermoplastic resin, and a third layer containing a thermoplastic resin.
  • the second layer is arranged on a first surface side of the first layer.
  • the third layer is arranged on a second surface side opposite to the first surface of the first layer.
  • the glass transition temperature (Tg) of the first layer is lower than the glass transition temperature (Tg) of the second layer.
  • the glass transition temperature (Tg) of the first layer is lower than the glass transition temperature (Tg) of the third layer.
  • a ratio (T1/(T2+T3)) of the thickness of the first layer (T1) to the total thickness of the second layer and the third layer (T2+T3) is 0.25 or more.
  • the thickness of the interlayer film according to the present invention is more than 600 ⁇ m.
  • the interlayer film according to the present invention is provided with the above-mentioned configuration, the sound insulating properties in a high frequency area of 1000 Hz or more, particularly 2000 Hz or more, can be effectively enhanced. Furthermore, in the interlayer film according to the present invention, the sound insulating properties in a high frequency area of 2000 Hz or more can be further effectively enhanced, and furthermore, the sound insulating properties in a high frequency area of about 4000 Hz, which have hitherto been difficult to be enhanced, can also be enhanced.
  • the present inventors have found out that, by combining the constitution in which the glass transition temperature (Tg) of the first layer is lower than the glass transition temperature (Tg) of each of the second layer and the third layer, the constitution in which the ratio (T1/(T2+T3)) is 0.25 or more, and the constitution in which the thickness of the interlayer film is more than 600 ⁇ m, the sound insulating properties in a high frequency area can be effectively enhanced to the extent hardly attainable by the conventional technique.
  • the penetration resistance of laminated glass can also be enhanced.
  • both high sound insulating properties and high penetration resistance can be achieved at the same time.
  • the high penetration resistance is brought about not only by being relatively thick in thickness of the interlayer film but also by the limited constituent features other than the thicknesses of the first layer, the second layer, and the third layer.
  • Tg of the first layer is lower than Tg of the second layer.
  • the absolute value of a difference between Tg of the first layer and Tg of the second layer is preferably 32° C. or more, more preferably 34° C. or more, and preferably 55° C. or less, and more preferably 50° C. or less.
  • Tg of the first layer is lower than Tg of the third layer.
  • the absolute value of a difference between Tg of the first layer and Tg of the third layer is preferably 32° C. or more, more preferably 34° C. or more, and preferably 55° C. or less, and more preferably 50° C. or less.
  • Tg of the second layer is preferably 32° C. or more, more preferably 33° C. or more, further preferably 34° C. or more, and preferably 45° C. or less, and more preferably 44° C. or less.
  • Tg of the third layer is preferably 32° C. or more, more preferably 33° C. or more, further preferably 34° C. or more, and preferably 45° C. or less, and more preferably 44° C. or less.
  • Examples of a method of measuring the glass transition temperature include a method of measuring the viscoelasticity of an interlayer film with the use of a dynamic viscoelasticity measuring apparatus “DMA+1000” available from 01 dB-Metravib immediately after the interlayer film obtained is stored for 12 hours under an environment of a room temperature of 23 ⁇ 2° C. and a humidity of 25 ⁇ 5%. It is preferred that the interlayer film or each layer be cut into a size of 8 mm in longitudinal width by 5 mm in lateral width and be measured, using the shear mode, for the glass transition temperature under the condition in which the temperature is increased from ⁇ 30° C. to 100° C. at a temperature increasing rate of 5° C./minute and under the condition of a frequency of 1 Hz and a strain of 0.08%.
  • DMA+1000 available from 01 dB-Metravib immediately after the interlayer film obtained is stored for 12 hours under an environment of a room temperature of 23 ⁇ 2° C. and a humidity of 25 ⁇ 5%. It is preferred that the interlayer film
  • the ratio (T1/(T2+T3)) is 0.25 or more. From the viewpoint of effectively enhancing the sound insulating properties in a high frequency area, the ratio (T1/(T2+T3)) is preferably 0.25 or more, more preferably 0.3 or more, and preferably 0.65 or less, and more preferably 0.6 or less.
  • the thickness of the interlayer film is more than 600 ⁇ m. From the viewpoints of effectively enhancing the sound insulating properties in a high frequency area and attaining reduced weight of laminated glass, the thickness of the interlayer film is preferably 610 ⁇ m or more, more preferably 700 ⁇ m or more, further preferably 800 ⁇ m or more, and preferably 2000 ⁇ m or less, and more preferably 1800 ⁇ m or less. Moreover, when the thickness of the interlayer film is the above lower limit or more, the penetration resistance of laminated glass is further enhanced. When the thickness of the interlayer film is the above upper limit or less, the transparency of the interlayer film is further improved. The thickness of the interlayer film may be 950 ⁇ m or less and may be 787 ⁇ m or less.
  • the interlayer film is provided with the first layer as a layer other than a surface layer (a layer which is not a surface layer) and is provided with the first layer as an intermediate layer.
  • the first layer is not used so as to be brought into contact with a lamination glass member.
  • the interlayer film be provided with the second layer as a surface layer.
  • the interlayer film be provided with the third layer as a surface layer.
  • FIG. 1 shows an interlayer film for laminated glass in accordance with a first embodiment of the present invention schematically represented as a sectional view.
  • An interlayer film 11 shown in FIG. 1 is a multi-layered interlayer film having a three or more-layer structure.
  • the interlayer film 11 is used for obtaining laminated glass.
  • the interlayer film 11 is an interlayer film for laminated glass.
  • the interlayer film 11 is provided with a first layer 1 , a second layer 2 , and a third layer 3 .
  • the second layer 2 is arranged on a first surface 1 a of the first layer 1 to be layered thereon.
  • the third layer 3 is arranged on a second surface 1 b opposite to the first surface 1 a of the first layer 1 to be layered thereon.
  • the first layer 1 is an intermediate layer.
  • Each of the second layer 2 and the third layer 3 is a protective layer and is a surface layer in the present embodiment.
  • the first layer 1 is arranged between the second layer 2 and the third layer 3 to be sandwiched therebetween. Accordingly, the interlayer film 11 has a multilayer structure (a second layer 2 /a first layer 1 /a third layer 3 ) in which the second layer 2 , the first layer 1 , and the third layer 3 are layered in this order.
  • additional layers may be arranged between the second layer 2 and the first layer 1 and between the first layer 1 and the third layer 3 , respectively. It is preferred that each of the second layer 2 and the third layer 3 be directly layered on the first layer 1 .
  • the additional layer include a layer containing polyethylene terephthalate and the like.
  • the interlayer film be provided with the second layer as a surface layer of the interlayer film. It is preferred that the interlayer film be provided with the third layer as a surface layer of the interlayer film.
  • the first layer contains a thermoplastic resin (hereinafter, sometimes described as a thermoplastic resin (1)), and it is preferred that the first layer contain a polyvinyl acetal resin (hereinafter, sometimes described as a polyvinyl acetal resin (1)) as the thermoplastic resin (1).
  • the second layer contains a thermoplastic resin (hereinafter, sometimes described as a thermoplastic resin (2)), and it is preferred that the second layer contain a polyvinyl acetal resin (hereinafter, sometimes described as a polyvinyl acetal resin (2)) as the thermoplastic resin (2).
  • the third layer contain a thermoplastic resin (hereinafter, sometimes described as a thermoplastic resin (3)), and it is preferred that the third layer contain a polyvinyl acetal resin (hereinafter, sometimes described as a polyvinyl acetal resin (3)) as the thermoplastic resin (3).
  • a thermoplastic resin hereinafter, sometimes described as a thermoplastic resin (3)
  • a polyvinyl acetal resin hereinafter, sometimes described as a polyvinyl acetal resin (3)
  • One kind of each of the thermoplastic resin (1), the thermoplastic resin (2), and the thermoplastic resin (3) may be used alone and two or more kinds thereof may be used in combination.
  • the thermoplastic resin (1), the thermoplastic resin (2), and the thermoplastic resin (3) may be the same as or different from one another.
  • thermoplastic resin examples include a polyvinyl acetal resin, an ethylene-vinyl acetate copolymer resin, an ethylene-acrylic acid copolymer resin, a polyurethane resin, a polyvinyl alcohol resin, and the like. Thermoplastic resins other than these may be used.
  • the polyvinyl acetal resin can be obtained by acetalizing polyvinyl alcohol (PVA) with an aldehyde. It is preferred that the polyvinyl acetal resin be an acetalized product of polyvinyl alcohol.
  • the polyvinyl alcohol can be obtained by saponifying polyvinyl acetate. The saponification degree of the polyvinyl alcohol generally falls within the range of 70 to 99.9% by mole.
  • the average polymerization degree of the polyvinyl alcohol (PVA) is preferably 200 or more, more preferably 500 or more, even more preferably 1500 or more, further preferably 1600 or more, especially preferably 2600 or more, most preferably 2700 or more, and preferably 5000 or less, more preferably 4000 or less and further preferably 3500 or less.
  • PVA polyvinyl alcohol
  • the average polymerization degree of the polyvinyl alcohol is determined by a method in accordance with JIS K6726 “Testing methods for polyvinyl alcohol”.
  • the number of carbon atoms of the acetal group in the polyvinyl acetal resin lie within the range of 3 to 5, and it is preferred that the number of carbon atoms of the acetal group be 4 or 5.
  • aldehyde an aldehyde with 1 to 10 carbon atoms is suitably used.
  • aldehyde with 1 to 10 carbon atoms include formaldehyde, acetaldehyde, propionaldehyde, n-butyraldehyde, isobutyraldehyde, n-valeraldehyde, 2-ethylbutyraldehyde, n-hexylaldehyde, n-octylaldehyde, n-nonylaldehyde, n-decylaldehyde, benzaldehyde, and the like.
  • Acetaldehyde, propionaldehyde, n-butyraldehyde, isobutyraldehyde, n-hexylaldehyde, or n-valeraldehyde is preferred, acetaldehyde, propionaldehyde, n-butyraldehyde, isobutyraldehyde, or n-valeraldehyde is more preferred, and n-butyraldehyde or n-valeraldehyde is further preferred.
  • One kind of the aldehyde may be used alone and two or more kinds thereof may be used in combination.
  • the content of the hydroxyl group (the amount of hydroxyl groups) of the polyvinyl acetal resin (1) is preferably 17% by mole or more, more preferably 20% by mole or more, further preferably 22% by mole or more, and preferably 30% by mole or less, more preferably 28% by mole or less, even more preferably 27% by mole or less, further preferably 25% by mole or less, especially preferably less than 25% by mole, and most preferably 24% by mole or less.
  • the content of the hydroxyl group is the above lower limit or more, the mechanical strength of the interlayer film is further enhanced.
  • the content of the hydroxyl group of the polyvinyl acetal resin (1) is 20% by mole or more, the resin is high in reaction efficiency and is excellent in productivity, moreover, when being 30% by mole or less, the sound insulating properties of laminated glass are further enhanced, and when being 28% by mole or less, the sound insulating properties are still further enhanced.
  • the content of the hydroxyl group is the above upper limit or less, the flexibility of the interlayer film is enhanced and the handling of the interlayer film is facilitated.
  • the content of the hydroxyl group of each of the polyvinyl acetal resin (2) and the polyvinyl acetal resin (3) is preferably 25% by mole or more, more preferably 28% by mole or more, more preferably 30% by mole or more, even more preferably more than 31% by mole, further preferably 31.5% by mole or more, still further preferably 32% by mole or more, especially preferably 33% by mole or more, and preferably 37% by mole or less, more preferably 36.5% by mole or less, and further preferably 36% by mole or less.
  • the content of the hydroxyl group is the above lower limit or more, the adhesive force of the interlayer film is further enhanced.
  • the flexibility of the interlayer film is enhanced and the handling of the interlayer film is facilitated.
  • the content of the hydroxyl group of the polyvinyl acetal resin (1) be lower than the content of the hydroxyl group of the polyvinyl acetal resin (2) and it is preferred that the content of the hydroxyl group of the polyvinyl acetal resin (1) be lower than the content of the hydroxyl group of the polyvinyl acetal resin (3).
  • each of the absolute value of the difference between the content of the hydroxyl group of the polyvinyl acetal resin (1) and the content of the hydroxyl group of the polyvinyl acetal resin (2) and the absolute value of the difference between the content of the hydroxyl group of the polyvinyl acetal resin (1) and the content of the hydroxyl group of the polyvinyl acetal resin (3) is preferably 1% by mole or more, more preferably 5% by mole or more, further preferably 9% by mole or more, especially preferably 10% by mole or more, and most preferably 12% by mole or more.
  • Each of the absolute value of the difference between the content of the hydroxyl group of the polyvinyl acetal resin (1) and the content of the hydroxyl group of the polyvinyl acetal resin (2) and the absolute value of the difference between the content of the hydroxyl group of the polyvinyl acetal resin (1) and the content of the hydroxyl group of the polyvinyl acetal resin (3) is preferably 20% by mole or less.
  • the content of the hydroxyl group of the polyvinyl acetal resin is a mole fraction, represented in percentage, obtained by dividing the amount of ethylene groups to which the hydroxyl group is bonded by the total amount of ethylene groups in the main chain.
  • the amount of ethylene groups to which the hydroxyl group is bonded can be measured in accordance with JIS K6728 “Testing methods for polyvinyl butyral”.
  • the acetylation degree (the amount of acetyl groups) of the polyvinyl acetal resin (1) is preferably 0.01% by mole or more, more preferably 0.1% by mole or more, even more preferably 7% by mole or more, further preferably 9% by mole or more, and preferably 30% by mole or less, more preferably 25% by mole or less, further preferably 24% by mole or less, and especially preferably 20% by mole or less.
  • the acetylation degree is the above lower limit or more, the compatibility between the polyvinyl acetal resin and a plasticizer is enhanced.
  • the acetylation degree is the above upper limit or less, with regard to the interlayer film and laminated glass, the moisture resistance thereof is enhanced.
  • the acetylation degree of the polyvinyl acetal resin (1) is 0.1% by mole or more and 25% by mole or less, the resulting laminated glass is further excellent in penetration resistance.
  • the acetylation degree of each of the polyvinyl acetal resin (2) and the polyvinyl acetal resin (3) is preferably 0.01% by mole or more, more preferably 0.5% by mole or more, and preferably 10% by mole or less, and more preferably 2% by mole or less.
  • the acetylation degree is the above lower limit or more, the compatibility between the polyvinyl acetal resin and a plasticizer is enhanced.
  • the acetylation degree is the above upper limit or less, with regard to the interlayer film and laminated glass, the moisture resistance thereof is enhanced.
  • the acetylation degree is a mole fraction, represented in percentage, obtained by dividing the amount of ethylene groups to which the acetyl group is bonded by the total amount of ethylene groups in the main chain.
  • the amount of ethylene groups to which the acetyl group is bonded can be measured in accordance with JIS K6728 “Testing methods for polyvinyl butyral”.
  • the acetalization degree of the polyvinyl acetal resin (1) is preferably 47% by mole or more, more preferably 60% by mole or more, and preferably 85% by mole or less, more preferably 80% by mole or less and further preferably 75% by mole or less.
  • the acetalization degree is the above lower limit or more, the compatibility between the polyvinyl acetal resin and a plasticizer is enhanced.
  • the acetalization degree is the above upper limit or less, the reaction time required for producing the polyvinyl acetal resin is shortened.
  • the acetalization degree of each of the polyvinyl acetal resin (2) and the polyvinyl acetal resin (3) is preferably 55% by mole or more, more preferably 60% by mole or more, and preferably 75% by mole or less and more preferably 71% by mole or less.
  • the acetalization degree is the above lower limit or more, the compatibility between the polyvinyl acetal resin and a plasticizer is enhanced.
  • the acetalization degree is the above upper limit or less, the reaction time required for producing the polyvinyl acetal resin is shortened.
  • the acetalization degree is a mole fraction, represented in percentage, obtained by dividing a value obtained by subtracting the amount of ethylene groups to which the hydroxyl group is bonded and the amount of ethylene groups to which the acetyl group is bonded from the total amount of ethylene groups in the main chain by the total amount of ethylene groups in the main chain.
  • the content of the hydroxyl group (the amount of hydroxyl groups), the acetalization degree (the butyralization degree) and the acetylation degree be calculated from the results measured by a method in accordance with JIS K6728 “Testing methods for polyvinyl butyral”.
  • a method in accordance with ASTM D1396-92 may be used.
  • the content of the hydroxyl group (the amount of hydroxyl groups), the acetalization degree (the butyralization degree) and the acetylation degree can be calculated from the results measured by a method in accordance with JIS K6728 “Testing methods for polyvinyl butyral”.
  • the polyvinyl acetal resin (1) be a polyvinyl acetal resin (A) with an acetylation degree (a) of less than 8% by mole and an acetalization degree (a) of 65% by mole or more or a polyvinyl acetal resin (B) with an acetylation degree (b) of 8% by mole or more.
  • Each of the polyvinyl acetal resin (2) and the polyvinyl acetal resin (3) may be the polyvinyl acetal resin (A) and may be the polyvinyl acetal resin (B).
  • the acetylation degree (a) of the polyvinyl acetal resin (A) is less than 8% by mole, preferably 7.9% by mole or less, more preferably 7.8% by mole or less, further preferably 6.5% by mole or less, especially preferably 6% by mole or less, and preferably 0.1% by mole or more, more preferably 0.5% by mole or more, further preferably 5% by mole or more, and especially preferably 5.5% by mole or more.
  • the acetylation degree (a) is 0.1% by mole or more and less than 8% by mole, the transfer of a plasticizer can be easily controlled and the sound insulating properties of laminated glass are further enhanced.
  • the acetalization degree (a) of the polyvinyl acetal resin (A) is 65% by mole or more, preferably 66% by mole or more, more preferably 67% by mole or more, further preferably 67.5% by mole or more, especially preferably 75% by mole or more, and preferably 85% by mole or less, more preferably 84% by mole or less, further preferably 83% by mole or less and especially preferably 82% by mole or less.
  • the acetalization degree (a) is the above lower limit or more, the sound insulating properties of laminated glass are further enhanced.
  • the acetalization degree (a) is the above upper limit or less, the reaction time required for producing the polyvinyl acetal resin (A) can be shortened.
  • the content (a) of the hydroxyl group of the polyvinyl acetal resin (A) is preferably 18% by mole or more, more preferably 19% by mole or more, further preferably 20% by mole or more, especially preferably 21% by mole or more, most preferably 23% by mole or more, and preferably 31% by mole or less, more preferably 30% by mole or less, further preferably 29% by mole or less, and especially preferably 28% by mole or less.
  • the content (a) of the hydroxyl group is the above lower limit or more, the adhesive force of the second layer or the third layer to the first layer is further enhanced when the second layer or the third layer is directly layered on the first layer.
  • the content (a) of the hydroxyl group is the above upper limit or less, the sound insulating properties of laminated glass are further enhanced.
  • the acetylation degree (b) of the polyvinyl acetal resin (B) is 8% by mole or more, preferably 9% by mole or more, more preferably 9.5% by mole or more, further preferably 10% by mole or more, especially preferably 10.5% by mole or more, and preferably 30% by mole or less, more preferably 28% by mole or less, further preferably 26% by mole or less and especially preferably 24% by mole or less.
  • the acetylation degree (b) is the above lower limit or more, the sound insulating properties of laminated glass are further enhanced.
  • the reaction time required for producing the polyvinyl acetal resin (B) can be shortened.
  • the acetalization degree (b) of the polyvinyl acetal resin (B) is preferably 50% by mole or more, more preferably 53% by mole or more, further preferably 55% by mole or more, especially preferably 60% by mole or more, and preferably 78% by mole or less, more preferably 75% by mole or less, further preferably 72% by mole or less and especially preferably 70% by mole or less.
  • the acetalization degree (b) is the above lower limit or more, the sound insulating properties of laminated glass are further enhanced.
  • the reaction time required for producing the polyvinyl acetal resin (B) can be shortened.
  • the content (b) of the hydroxyl group of the polyvinyl acetal resin (B) is preferably 18% by mole or more, more preferably 19% by mole or more, further preferably 20% by mole or more, especially preferably 21% by mole or more, most preferably 23% by mole or more, and preferably 31% by mole or less, more preferably 30% by mole or less, further preferably 29% by mole or less, and especially preferably 28% by mole or less.
  • the content (b) of the hydroxyl group is the above lower limit or more, the adhesive force of the second layer or the third layer to the first layer is further enhanced when the second layer or the third layer is directly layered on the first layer.
  • the content (b) of the hydroxyl group is the above upper limit or less, the sound insulating properties of laminated glass are further enhanced.
  • each of the polyvinyl acetal resin (A) and the polyvinyl acetal resin (B) be a polyvinyl butyral resin.
  • the first layer contain a plasticizer (hereinafter, sometimes described as a plasticizer (1)). It is preferred that the second layer contain a plasticizer (hereinafter, sometimes described as a plasticizer (2)). It is preferred that the third layer contain a plasticizer (hereinafter, sometimes described as a plasticizer (3)).
  • a plasticizer hereinafter, sometimes described as a plasticizer (1).
  • the plasticizer (2), and the plasticizer (3) may be the same as or different from one another.
  • One kind of each of the plasticizer (1), the plasticizer (2), and the plasticizer (3) may be used alone and two or more kinds thereof may be used in combination.
  • plasticizer examples include organic ester plasticizers such as a monobasic organic acid ester and a polybasic organic acid ester, organic phosphate plasticizers such as an organic phosphate plasticizer and an organic phosphite plasticizer, and the like: Organic ester plasticizers are preferred. It is preferred that the plasticizer be a liquid plasticizer.
  • Examples of the monobasic organic acid ester include a glycol ester obtained by the reaction of a glycol with a monobasic organic acid, and the like.
  • Examples of the glycol include triethylene glycol, tetraethylene glycol, tripropylene glycol, and the like.
  • Examples of the monobasic organic acid include butyric acid, isobutyric acid, caproic acid, 2-ethylbutyric acid, heptanoic acid, n-octylic acid, 2-ethylhexanoic acid, n-nonylic acid, decanoic acid, and the like.
  • polybasic organic acid ester examples include an ester compound of a polybasic organic acid and an alcohol having a linear or branched structure of 4 to 8 carbon atoms.
  • polybasic organic acid examples include adipic acid, sebacic acid, azelaic acid, and the like.
  • organic ester plasticizer examples include triethylene glycol di-2-ethylpropanoate, triethylene glycol di-2-ethylbutyrate, triethylene glycol di-2-ethylhexanoate, triethylene glycol dicaprylate, triethylene glycol di-n-octanoate, triethylene glycol di-n-heptanoate, tetraethylene glycol di-n-heptanoate, dibutyl sebacate, dioctyl azelate, dibutyl carbitol adipate, ethylene glycol di-2-ethylbutyrate, 1,3-propylene glycol di-2-ethylbutyrate, 1,4-butylene glycol di-2-ethylbutyrate, diethylene glycol di-2-ethylbutyrate, diethylene glycol di-2-ethylhexanoate, dipropylene glycol di-2-ethylbutyrate, triethylene glycol di-2-ethy
  • organic phosphate plasticizer examples include tributoxyethyl phosphate, isodecyl phenyl phosphate, triisopropyl phosphate, and the like.
  • the plasticizer be a diester plasticizer represented by the following formula (1).
  • R1 and R2 each represent an organic group with 2 to 10 carbon atoms
  • R3 represents an ethylene group, an isopropylene group or an n-propylene group
  • p represents an integer of 3 to 10. It is preferred that R1 and R2 in the foregoing formula (1) each be an organic group with 5 to 10 carbon atoms, and it is more preferred that R1 and R2 each be an organic group with 6 to 10 carbon atoms.
  • the plasticizer include triethylene glycol di-2-ethylhexanoate (3GO), triethylene glycol di-2-ethylbutyrate (3GH), or triethylene glycol di-2-ethylpropanoate, it is more preferred that the plasticizer include triethylene glycol di-2-ethylhexanoate or triethylene glycol di-2-ethylbutyrate, and it is further preferred that the plasticizer include triethylene glycol di-2-ethylhexanoate.
  • 3GO triethylene glycol di-2-ethylhexanoate
  • 3GH triethylene glycol di-2-ethylbutyrate
  • the plasticizer include triethylene glycol di-2-ethylhexanoate.
  • each of the content of the plasticizer (2) (hereinafter, sometimes described as the content (2)) relative to 100 parts by weight of the thermoplastic resin (2) (100 parts by weight a polyvinyl acetal resin (2) when the thermoplastic resin (2) is the polyvinyl acetal resin (2)) and the content of the plasticizer (3) (hereinafter, sometimes described as the content (3)) relative to 100 parts by weight of the thermoplastic resin (3) (100 parts by weight a polyvinyl acetal resin (3) when the thermoplastic resin (3) is the polyvinyl acetal resin (3)) is preferably 10 parts by weight or more, more preferably parts by weight or more, and preferably 40 parts by weight or less, more preferably 39 parts by weight or less, further preferably 35 parts by weight or less, still further preferably 32 parts by weight or less, and especially preferably 30 parts by weight or less.
  • the content (2) and the content (3) are the above lower limit or more, the flexibility of the interlayer film is enhanced and the handling of the interlayer film is facilitated.
  • the content (2) and the content (3) are the above
  • the content of the plasticizer (1) (hereinafter, sometimes described as the content (1)) relative to 100 parts by weight of the polyvinyl acetal resin (1) is preferably 50 parts by weight or more, more preferably 55 parts by weight or more, further preferably 60 parts by weight or more, and preferably 100 parts by weight or less, more preferably 90 parts by weight or less, further preferably 85 parts by weight or less, and especially preferably 80 parts by weight or less.
  • the content (1) is the above lower limit or more, the flexibility of the interlayer film is enhanced and the handling of the interlayer film is facilitated.
  • the content (1) is the above upper limit or less, the penetration resistance of laminated glass is further enhanced.
  • the content (1) be larger than the content (2) and it is preferred that the content (1) be larger than the content (3).
  • each of the absolute value of the difference between the content (2) and the content (1) and the absolute value of the difference between the content (3) and the content (1) is preferably 10 parts by weight or more, more preferably 15 parts by weight or more, and further preferably 20 parts by weight or more.
  • Each of the absolute value of the difference between the content (2) and the content (1) and the absolute value of the difference between the content (3) and the content (1) is preferably 80 parts by weight or less, more preferably 75 parts by weight or less, and further preferably 70 parts by weight or less.
  • the interlayer film include a heat shielding compound. It is preferred that the first layer contain a heat shielding compound. It is preferred that the second layer contain a heat shielding compound. It is preferred that the third layer contain a heat shielding compound.
  • One kind of the heat shielding compound may be used alone, and two or more kinds thereof may be used in combination.
  • the interlayer film include at least one kind of Ingredient X among a phthalocyanine compound, a naphthalocyanine compound and an anthracyanine compound. It is preferred that the first layer contain the Ingredient X. It is preferred that the second layer contain the Ingredient X. It is preferred that the third layer contain the Ingredient X.
  • the Ingredient X is a heat shielding compound. One kind of the Ingredient X may be used alone, and two or more kinds thereof may be used in combination.
  • the Ingredient X is not particularly limited.
  • As the Ingredient X conventionally known phthalocyanine compound, naphthalocyanine compound and anthracyanine compound can be used.
  • the Ingredient X be at least one kind selected from the group consisting of phthalocyanine, a derivative of phthalocyanine, naphthalocyanine and a derivative of naphthalocyanine, and it is more preferred that the Ingredient X be at least one kind among phthalocyanine and a derivative of phthalocyanine.
  • the Ingredient X contain vanadium atoms or copper atoms. It is preferred that the Ingredient X contain vanadium atoms and it is also preferred that the Ingredient X contain copper atoms. It is more preferred that the Ingredient X be at least one kind among phthalocyanine containing vanadium atoms or copper atoms and a derivative of phthalocyanine containing vanadium atoms or copper atoms. With regard to the interlayer film and laminated glass, from the viewpoint of still further enhancing the heat shielding properties thereof, it is preferred that the Ingredient X have a structural unit in which an oxygen atom is bonded to a vanadium atom.
  • the content of the Ingredient X is preferably 0.001% by weight or more, more preferably 0.005% by weight or more, further preferably 0.01% by weight or more, especially preferably 0.02% by weight or more, and preferably 0.2% by weight or less, more preferably 0.1% by weight or less, further preferably 0.05% by weight or less and especially preferably 0.04% by weight or less.
  • the content of the Ingredient X is the above lower limit or more and the above upper limit or less, the heat shielding properties are sufficiently enhanced and the visible light transmittance is sufficiently enhanced. For example, it is possible to make the visible light transmittance 70% or more.
  • the interlayer film include heat shielding particles. It is preferred that the first layer contain the heat shielding particles. It is preferred that the second layer contain the heat shielding particles. It is preferred that the third layer contain the heat shielding particles.
  • the heat shielding particle is of a heat shielding compound. By the use of heat shielding particles, infrared rays (heat rays) can be effectively cut off. One kind of the heat shielding particles may be used alone, and two or more kinds thereof may be used in combination.
  • the heat shielding particles be metal oxide particles. It is preferred that the heat shielding particle be a particle (a metal oxide particle) formed from an oxide of a metal.
  • the energy amount of an infrared ray with a wavelength of 780 nm or longer which is longer than that of visible light is small as compared with an ultraviolet ray.
  • the thermal action of infrared rays is large, and when infrared rays are absorbed into a substance, heat is released from the substance.
  • infrared rays are generally called heat rays.
  • the heat shielding particle means a particle capable of absorbing infrared rays.
  • the heat shielding particles include metal oxide particles such as aluminum-doped tin oxide particles, indium-doped tin oxide particles, antimony-doped tin oxide particles (ATO particles), gallium-doped zinc oxide particles (GZO particles), indium-doped zinc oxide particles (IZO particles), aluminum-doped zinc oxide particles (AZO particles), niobium-doped titanium oxide particles, sodium-doped tungsten oxide particles, cesium-doped tungsten oxide particles, thallium-doped tungsten oxide particles, rubidium-doped tungsten oxide particles, tin-doped indium oxide particles (ITO particles), tin-doped zinc oxide particles and silicon-doped zinc oxide particles, lanthanum hexaboride (LaB 6 ) particles, and the like.
  • metal oxide particles such as aluminum-doped tin oxide particles, indium-doped tin oxide particles, antimony-doped tin oxide particles
  • Heat shielding particles other than these may be used. Since the heat ray shielding function is high, preferred are metal oxide particles, more preferred are ATO particles, GZO particles, IZO particles, ITO particles or tungsten oxide particles, and especially preferred are ITO particles or tungsten oxide particles. In particular, since the heat ray shielding function is high and the particles are readily available, preferred are tin-doped indium oxide particles (ITO particles), and also preferred are tungsten oxide particles.
  • ITO particles tin-doped indium oxide particles
  • the tungsten oxide particles be metal-doped tungsten oxide particles.
  • the “tungsten oxide particles” include metal-doped tungsten oxide particles.
  • the metal-doped tungsten oxide particles include sodium-doped tungsten oxide particles, cesium-doped tungsten oxide particles, thallium-doped tungsten oxide particles, rubidium-doped tungsten oxide particles, and the like.
  • the interlayer film and laminated glass from the viewpoint of further enhancing the heat shielding properties thereof, cesium-doped tungsten oxide particles are especially preferred.
  • the cesium-doped tungsten oxide particles be tungsten oxide particles represented by the formula: Cs 0.33 WO 3 .
  • the average particle diameter of the heat shielding particles is preferably 0.01 ⁇ m or more, more preferably 0.02 ⁇ m or more, and preferably 0.1 ⁇ m or less and more preferably 0.05 ⁇ m or less.
  • the average particle diameter is the above lower limit or more, the heat ray shielding properties are sufficiently enhanced.
  • the average particle diameter is the above upper limit or less, the dispersibility of heat shielding particles is enhanced.
  • the “average particle diameter” refers to the volume average particle diameter.
  • the average particle diameter can be measured using a particle size distribution measuring apparatus (“UPA-EX150” available from NIKKISO CO., LTD.), or the like.
  • each content of the heat shielding particles is preferably 0.01% by weight or more, more preferably 0.1% by weight or more, further preferably 1% by weight or more, especially preferably 3.5% by weight or more, and preferably 6% by weight or less, more preferably 5.5% by weight or less, further preferably 4% by weight or less, especially preferably 3.5% by weight or less and most preferably 3% by weight or less.
  • the content of the heat shielding particles is the above lower limit or more and the above upper limit or less, the heat shielding properties are sufficiently enhanced and the visible light transmittance is sufficiently enhanced.
  • the interlayer film include at least one kind of metal salt (hereinafter, sometimes described as Metal salt M) among an alkali metal salt, an alkaline earth metal salt, and an Mg salt.
  • Metal salt M metal salt among an alkali metal salt, an alkaline earth metal salt, and an Mg salt.
  • the first layer contain the Metal salt M.
  • the second layer contain the Metal salt M.
  • the surface layer contain the Metal salt M.
  • the Metal salt M contain at least one kind of metal selected from the group consisting of Li, Na, K, Rb, Cs, Mg, Ca, Sr, and Ba. It is preferred that the metal salt contained in the interlayer film contain at least one kind of metal between K and Mg.
  • the Metal salt M be an alkali metal salt of an organic acid with 2 to 16 carbon atoms, an alkaline earth metal salt of an organic acid with 2 to 16 carbon atoms, and an Mg salt of an organic acid with 2 to 16 carbon atoms, and it is further preferred that the Metal salt M be a magnesium carboxylate with 2 to 16 carbon atoms or a potassium carboxylate with 2 to 16 carbon atoms.
  • magnesium carboxylate with 2 to 16 carbon atoms and the potassium carboxylate with 2 to 16 carbon atoms are not particularly limited, examples thereof include magnesium acetate, potassium acetate, magnesium propionate, potassium propionate, magnesium 2-ethylbutyrate, potassium 2-ethylbutanoate, magnesium 2-ethylhexanoate, potassium 2-ethylhexanoate, and the like.
  • the total of the contents of Mg and K in a layer containing the Metal salt M is preferably 5 ppm or more, more preferably 10 ppm or more, further preferably 20 ppm or more, and preferably 300 ppm or less, more preferably 250 ppm or less, and further preferably 200 ppm or less.
  • the adhesivity between the interlayer film and a lamination glass member or the adhesivity between respective layers in the interlayer film can be further well controlled.
  • the interlayer film include an ultraviolet ray screening agent. It is preferred that the first layer contain an ultraviolet ray screening agent. It is preferred that the second layer contain an ultraviolet ray screening agent. It is preferred that the third layer contain an ultraviolet ray screening agent.
  • an ultraviolet ray screening agent By the use of an ultraviolet ray screening agent, even when the interlayer film and the laminated glass are used for a long period of time, the visible light transmittance becomes further difficult to be lowered.
  • One kind of the ultraviolet ray screening agent may be used alone, and two or more kinds thereof may be used in combination.
  • Examples of the ultraviolet ray screening agent include an ultraviolet ray absorber. It is preferred that the ultraviolet ray screening agent be an ultraviolet ray absorber.
  • Examples of the ultraviolet ray screening agent include an ultraviolet ray screening agent containing a metal atom, an ultraviolet ray screening agent containing a metal oxide, an ultraviolet ray screening agent having a benzotriazole structure, an ultraviolet ray screening agent having a benzophenone structure, an ultraviolet ray screening agent having a triazine structure, an ultraviolet ray screening agent having a malonic acid ester structure, an ultraviolet ray screening agent having an oxanilide structure, an ultraviolet ray screening agent having a benzoate structure, and the like.
  • Examples of the ultraviolet ray screening agent containing a metal atom include platinum particles, particles in which the surface of platinum particles is coated with silica, palladium particles, particles in which the surface of palladium particles is coated with silica, and the like. It is preferred that the ultraviolet ray screening agent not be heat shielding particles.
  • the ultraviolet ray screening agent is preferably an ultraviolet ray screening agent having a benzotriazole structure, an ultraviolet ray screening agent having a benzophenone structure, an ultraviolet ray screening agent having a triazine structure or an ultraviolet ray screening agent having a benzoate structure, more preferably an ultraviolet ray screening agent having a benzotriazole structure or an ultraviolet ray screening agent having a benzophenone structure, and further preferably an ultraviolet ray screening agent having a benzotriazole structure.
  • Examples of the ultraviolet ray screening agent containing a metal oxide include zinc oxide, titanium oxide, cerium oxide, and the like. Furthermore, with regard to the ultraviolet ray screening agent containing a metal oxide, the surface thereof may be coated with any material. Examples of the coating material for the surface of the ultraviolet ray screening agent containing a metal oxide include an insulating metal oxide, a hydrolyzable organosilicon compound, a silicone compound, and the like.
  • Examples of the ultraviolet ray screening agent having a benzotriazole structure include ultraviolet ray screening agents having a benzotriazole structure such as 2-(2′-hydroxy-5′-methylphenyl)benzotriazole (“Tinuvin P” available from BASF Japan Ltd.), 2-(2′-hydroxy-3′,5′-di-t-butylphenyl)benzotriazole (“Tinuvin 320” available from BASF Japan Ltd.), 2-(2′-hydroxy-3′-t-butyl-5-methylphenyl)-5-chlorobenzotriazole (“Tinuvin 326” available from BASF Japan Ltd.) and 2-(2′-hydroxy-3′,5′-di-amylphenyl)benzotriazole (“Tinuvin 328” available from BASF Japan Ltd.).
  • ultraviolet ray screening agents having a benzotriazole structure such as 2-(2′-hydroxy-5′-methylphenyl)benzotriazole (“Tinuvin P” available from BASF Japan Ltd
  • the ultraviolet ray screening agent be an ultraviolet ray screening agent having a benzotriazole structure containing a halogen atom, and it is more preferred that the ultraviolet ray screening agent be an ultraviolet ray screening agent having a benzotriazole structure containing a chlorine atom, because those are excellent in ultraviolet ray absorbing performance.
  • Examples of the ultraviolet ray screening agent having a benzophenone structure include octabenzone (“Chimassorb 81” available from BASF Japan Ltd.), and the like.
  • Examples of the ultraviolet ray screening agent having a triazine structure include “LA-F70” available from ADEKA CORPORATION, 2-(4,6-diphenyl-1,3,5-triazine-2-yl)-5-[(hexyl)oxy]-phenol (“Tinuvin 1577FF” available from BASF Japan Ltd.), and the like.
  • Examples of the ultraviolet ray screening agent having a malonic acid ester structure include dimethyl 2-(p-methoxybenzylidene)malonate, tetraethyl-2,2-(1,4-phenylenedimethylidene)bismalonate, 2-(p-methoxybenzylidene)-bis(1,2,2,6,6-pentamethyl-4-piperidinyl)malonate, and the like.
  • Examples of a commercial product of the ultraviolet ray screening agent having a malonic acid ester structure include Hostavin B-CAP, Hostavin PR-25 and Hostavin PR-31 (any of these is available from Clariant Japan K.K.).
  • Examples of the ultraviolet ray screening agent having an oxanilide structure include a kind of oxalic acid diamide having a substituted aryl group and the like on the nitrogen atom such as N-(2-ethylphenyl)-N′-(2-ethoxy-5-t-butylphenyl)oxalic acid diamide, N-(2-ethylphenyl)-N′-(2-ethoxy-phenyl)oxalic acid diamide and 2-ethyl-2′-ethoxy-oxanilide (“Sanduvor VSU” available from Clariant Japan K.K.).
  • Examples of the ultraviolet ray screening agent having a benzoate structure include 2,4-d-tert-butylphenyl-3,5-di-tert-butyl-4-hydroxybenzoate (“Tinuvin 120” available from BASF Japan Ltd.), and the like.
  • the content of the ultraviolet ray screening agent is preferably 0.1% by weight or more, more preferably 0.2% by weight or more, further preferably 0.3% by weight or more, especially preferably 0.5% by weight or more, and preferably 2.5% by weight or less, more preferably 2% by weight or less, further preferably 1% by weight or less and especially preferably 0.8% by weight or less.
  • the content of the ultraviolet ray screening agent to be 0.2% by weight or more in 100% by weight of a layer containing the ultraviolet ray screening agent, with regard to the interlayer film and laminated glass, the lowering in visible light transmittance thereof after the lapse of a certain period of time can be significantly suppressed.
  • the interlayer film include an oxidation inhibitor. It is preferred that the first layer contain an oxidation inhibitor. It is preferred that the second layer contain an oxidation inhibitor. It is preferred that the third layer contain an oxidation inhibitor. One kind of the oxidation inhibitor may be used alone, and two or more kinds thereof may be used in combination.
  • the oxidation inhibitor examples include a phenol-based oxidation inhibitor, a sulfur-based oxidation inhibitor, a phosphorus-based oxidation inhibitor, and the like.
  • the phenol-based oxidation inhibitor is an oxidation inhibitor having a phenol skeleton.
  • the sulfur-based oxidation inhibitor is an oxidation inhibitor containing a sulfur atom.
  • the phosphorus-based oxidation inhibitor is an oxidation inhibitor containing a phosphorus atom.
  • the oxidation inhibitor be a phenol-based oxidation inhibitor or a phosphorus-based oxidation inhibitor.
  • phenol-based oxidation inhibitor examples include 2,6-di-t-butyl-p-cresol (BHT), butyl hydroxyanisole (BHA), 2,6-di-t-butyl-4-ethylphenol, stearyl butyl-4-hydroxyphenyl)propionate, 2,2′-methylenebis-(4-methyl-6-butylphenol), 2,2′-methylenebis-(4-ethyl-6-t-butylphenol), 4,4′-butylidene-bis-(3-methyl-6-t-butylphenol), 1,1,3-tris-(2-methyl-hydroxy-5-t-butylphenyl)butane, tetrakis[methylene-3-(3′,5′-butyl-4-hydroxyphenyl)propionate]methane, 1,3,3-tris-(2-methyl-4-hydroxy-5-t-butylphenol)butane, 1,3,5-trimethyl-2,4,6-tris(3,5-d
  • Examples of the phosphorus-based oxidation inhibitor include tridecyl phosphite, tris(tridecyl) phosphite, triphenyl phosphite, trinonylphenyl phosphite, bis(tridecyl)pentaerithritol diphosphite, bis(decyl)pentaerithritol diphosphite, tris(2,4-di-t-butylphenyl) phosphite, bis(2,4-di-t-butyl-6-methylphenyl)ethyl ester phosphorous acid, tris(2,4-di-t-butylphenyl) phosphite, 2,2′-methylenebis(4,6-di-t-butyl-1-phenyloxy)(2-ethylhexyloxy)phosphorus, and the like.
  • One kind or two or more kinds among these oxidation inhibitors
  • Examples of a commercial product of the oxidation inhibitor include “IRGANOX 245” available from BASF Japan Ltd., “IRGAFOS 168” available from BASF Japan Ltd., “IRGAFOS 38” available from BASF Japan Ltd., “Sumilizer BHT” available from Sumitomo Chemical Co., Ltd., “IRGANOX 1010” available from BASF Japan Ltd., and the like.
  • the content of the oxidation inhibitor be 0.1% by weight or more in 100% by weight of the interlayer film or in 100% by weight of the layer containing the oxidation inhibitor (a first layer, a second layer or a third layer). Moreover, since an effect commensurate with the addition of an oxidation inhibitor is not attained, it is preferred that the content of the oxidation inhibitor be 2% by weight or less in 100% by weight of the interlayer film or in 100% by weight of the layer containing the oxidation inhibitor.
  • Each of the first layer, the second layer, and the third layer may contain additives such as a coupling agent containing silicon, aluminum, or titanium, a dispersing agent, a surfactant, a flame retardant, an antistatic agent, a pigment, a dye, a moisture-resistance improving agent, a fluorescent brightening agent, and an infrared ray absorber, as necessary.
  • additives such as a coupling agent containing silicon, aluminum, or titanium, a dispersing agent, a surfactant, a flame retardant, an antistatic agent, a pigment, a dye, a moisture-resistance improving agent, a fluorescent brightening agent, and an infrared ray absorber, as necessary.
  • additives such as a coupling agent containing silicon, aluminum, or titanium, a dispersing agent, a surfactant, a flame retardant, an antistatic agent, a pigment, a dye, a moisture-resistance improving agent, a fluorescent brightening agent
  • Examples of the production method of the interlayer film according to the present invention include a method of separately forming respective resin compositions used for constituting respective layers into respective layers, and then, for example, layering the respective obtained layers, a method of coextruding respective resin compositions used for constituting respective layers with an extruder and layering the respective layers, and the like.
  • a production method of extrusion-molding is preferred because the method is suitable for continuous production.
  • respective polyvinyl acetal resins contained in the second layer and the third layer be the same as each other, it is more preferred that respective polyvinyl acetal resins contained in the second layer and the third layer be the same as each other and respective plasticizers contained therein be the same as each other, and it is further preferred that the second layer and the third layer be formed from the same resin composition as each other.
  • the interlayer film has a recess/protrusion shape. It is more preferred that surfaces of both sides of the interlayer film have a recess/protrusion shape.
  • the method for forming the recess/protrusion shape is not particularly limited, and examples thereof include a lip emboss method, an embossing roll method, a calender roll method, a profile extrusion method, and the like. Since it is possible to quantitatively form many embosses with a recess/protrusion shape constituting a constant uneven pattern, the embossing roll method is preferred.
  • FIG. 2 is a sectional view schematically showing an example of laminated glass prepared with the interlayer film for laminated glass shown in FIG. 1 .
  • the laminated glass 31 shown in FIG. 2 is provided with a first lamination glass member 21 , a second lamination glass member 22 , and an interlayer film 11 .
  • the interlayer film 11 is arranged between the first lamination glass member 21 and the second lamination glass member 22 to be sandwiched therebetween.
  • the first lamination glass member 21 is layered on a first surface 11 a of the interlayer film 11 .
  • the second lamination glass member 22 is layered on a second surface 11 b opposite to the first surface 11 a of the interlayer film 11 .
  • the first lamination glass member 21 is layered on an outer surface 2 a of a second layer 2 .
  • the second lamination glass member 22 is layered on an outer surface 3 a of a third layer 3 .
  • the laminated glass according to the present invention is provided with a first lamination glass member, a second lamination glass member, and an interlayer film and the interlayer film is the interlayer film for laminated glass according to the present invention.
  • the above-mentioned interlayer film is arranged between the first lamination glass member and the second lamination glass member.
  • the lamination glass member examples include a glass plate, a PET (polyethylene terephthalate) film, and the like.
  • laminated glass laminated glass in which an interlayer film is sandwiched between a glass plate and a PET film or the like, as well as laminated glass in which an interlayer film is sandwiched between two glass plates, is included.
  • the laminated glass is a laminate provided with a glass plate, and it is preferred that at least one glass plate be used. It is preferred that each of the first lamination glass member and the second lamination glass member be a glass plate or a PET film, and the laminated glass be provided with a glass plate as at least one among the first lamination glass member and the second lamination glass member.
  • the glass plate examples include a sheet of inorganic glass and a sheet of organic glass.
  • the inorganic glass examples include float plate glass, heat ray-absorbing plate glass, heat ray-reflecting plate glass, polished plate glass, figured glass, wired plate glass, and the like.
  • the organic glass is synthetic resin glass substituted for inorganic glass.
  • the organic glass examples include a polycarbonate plate, a poly(meth)acrylic resin plate, and the like.
  • the poly(meth)acrylic resin plate examples include a polymethyl (meth)acrylate plate, and the like.
  • the thickness of the lamination glass member is preferably 1 mm or more, and preferably 5 mm or less, and more preferably 3 mm or less. Moreover, when the lamination glass member is a glass plate, the thickness of the glass plate is preferably 0.5 mm or more, more preferably 0.7 mm or more, and preferably 5 mm or less, and more preferably 3 mm or less. When the lamination glass member is a PET film, the thickness of the PET film is preferably 0.03 mm or more and preferably 0.5 mm or less.
  • the penetration resistance of laminated glass can be maintained high even when the thickness of the laminated glass is thinned.
  • the thickness of the glass plate is preferably 2 mm or less, more preferably 1.8 mm or less, even more preferably 1.5 mm or less, further preferably 1 mm or less, still further preferably 0.8 mm or less, and especially preferably 0.7 mm or less.
  • the thickness of the laminated glass may be 6 mm or less, may be 4 mm or less, and may be 3.5 mm or less.
  • the method for producing the laminated glass is not particularly limited.
  • the interlayer film is sandwiched between the first lamination glass member and the second lamination glass member, and then, passed through pressure rolls or subjected to decompression suction in a rubber bag, so that the air remaining between the first lamination glass member and the interlayer film and between the second lamination glass member and the interlayer film is removed, and thus, a laminate is obtained.
  • the members are preliminarily bonded together at about 70 to 110° C. to obtain a preliminarily bonded body.
  • the members are press-bonded together at about 120 to 150° C. and under a pressure of 1 to 1.5 MPa. In this way, laminated glass can be obtained.
  • a first layer, a second layer, and a third layer may be layered.
  • each of the interlayer film and the laminated glass can be used for automobiles, railway vehicles, aircraft, ships, buildings and the like. Each of the interlayer film and the laminated glass can also be used for applications other than these applications. It is preferred that the interlayer film and the laminated glass be an interlayer film and laminated glass for vehicles or for building respectively, and it is more preferred that the interlayer film and the laminated glass be an interlayer film and laminated glass for vehicles respectively. Each of the interlayer film and the laminated glass can be used for a windshield, side glass, rear glass or roof glass of an automobile, and the like. The interlayer film and the laminated glass are suitably used for automobiles. The interlayer film is suitably used for obtaining laminated glass of an automobile.
  • the visible light transmittance of laminated glass is preferably 65% or more and more preferably 70% or more.
  • the visible light transmittance of laminated glass can be measured in accordance with JIS R3211 (1998). It is preferred that the visible light transmittance of laminated glass obtained by sandwiching the interlayer film for laminated glass according to the present invention between two sheets of green glass (heat ray-absorbing plate glass) with a thickness of 2 mm in accordance with JIS R3208 be 70% or more.
  • the visible light transmittance is more preferably 75% or more.
  • Polyvinyl acetal resins shown in the following Table 2 were appropriately used. In all polyvinyl acetal resins used, n-butyraldehyde which has 4 carbon atoms is used for the acetalization.
  • the acetalization degree (the butyralization degree), the acetylation degree, and the content of the hydroxyl group were measured by a method in accordance with JIS K6728 “Testing methods for polyvinyl butyral”.
  • JIS K6728 “Testing methods for polyvinyl butyral”.
  • Tinuvin 326 (2-(2′-hydroxy-3′-t-butyl-5-methylphenyl)-5-chlorobenzotriazole, “Tinuvin 326” available from BASF Japan Ltd.)
  • a plasticizer 3GO
  • an ultraviolet ray screening agent Tinuvin 326
  • BHT oxidation inhibitor
  • a plasticizer 3GO
  • an ultraviolet ray screening agent Tinuvin 326
  • BHT oxidation inhibitor
  • composition for forming a first layer and the composition for forming a second layer and a third layer were coextruded with a coextruder to prepare an interlayer film (1170 ⁇ m in thickness) having a layered structure with a stack of a second layer (435 ⁇ m in thickness)/a first layer (300 ⁇ m in thickness)/a third layer (435 ⁇ m in thickness).
  • the obtained interlayer film was cut into a size of 55 cm in longitudinal length ⁇ 55 cm in transversal length.
  • a sheet of clear float glass 50 cm in longitudinal length ⁇ 50 cm in transversal length ⁇ 2 mm in thickness
  • a sheet of clear float glass 50 cm in longitudinal length ⁇ 50 cm in transversal length ⁇ 1.6 mm in thickness
  • the laminate was put into a rubber bag and the inside thereof was degassed for 20 minutes at a degree of vacuum of 2.6 kPa, after which the laminate was transferred into an oven while keeping the laminate degassed, and furthermore, held in place for 30 minutes at 90° C. and pressed under vacuum to subject the laminate to preliminary press-bonding.
  • the preliminarily press-bonded laminate was subjected to press-bonding for 20 minutes under conditions of 135° C. and a pressure of 1.2 MPa in an autoclave to obtain a sheet of Laminated glass A.
  • the obtained interlayer film was cut out into a piece of 100 cm in longitudinal length ⁇ 100 cm in transversal length.
  • the interlayer film was sandwiched between two sheets of clear glass (30 cm in longitudinal length ⁇ 30 cm in transversal length ⁇ 2.5 mm in thickness) and held in place and pressed under vacuum at 90° C. for 30 minutes with a vacuum laminator to obtain a laminate.
  • interlayer film portions protruded from the sheet of glass were cut away to obtain a sheet of Laminated glass B.
  • An interlayer film and a sheet of laminated glass were obtained in the same manner as that in Example 1 except that the kind and blending amount of each of the polyvinyl acetal resin and the plasticizer which are used for compositions for forming a first layer, a second layer, and a third layer were set to those listed in the following Table 2 and the thicknesses of the first layer, the second layer, and the third layer were set to those listed in the following Table 2.
  • the interlayer film obtained was stored for 2 months at a temperature of 23° C. and a humidity of 30%, after which each of the surface layers (the second layer and the third layer) was peeled off to isolate an object to be measured and the objects to be measured was press-molded with a press molding machine.
  • the measurement was performed using the “ARES-G2” available from TA Instruments Japan Inc. A parallel plate with a diameter of 8 mm was used as a jig, and the measurement was performed under the condition in which the temperature is decreased from 100° C. to ⁇ 10° C. at a temperature decreasing rate of 3° C./minute and under the condition of a frequency of 1 Hz and a strain of 1%.
  • the peak temperature of the loss tangent was defined as the glass transition temperature Tg (° C.).
  • the sound insulating properties of a sheet of Laminated glass A were evaluated with sound transmission losses.
  • the sheet was measured for the sound transmission loss at 20° C. on the basis of JIS A1441-1. Specifically, the sheet was measured in the following way. In an opening between a sound generating room and a sound receiving room, the sheet of Laminated glass A prepared was installed. With the use of an acoustic intensity probe “SI-34” available from RION Co., Ltd., by being scanned at a position apart from the sample installed in the niche opening at the sound receiving room side by 13 cm, the sheet was measured for the average acoustic intensity level. The scanning time was set to 25 to 40 seconds, the scanning rate was set to 0.15 to 0.2 m/second, and an average value was calculated from two kinds of scan pattern measured values.
  • the sheet of laminated glass obtained was stored for 16 hours at a temperature of ⁇ 18° C. ⁇ 0.6° C. so that the sheet temperature was adjusted to the temperature.
  • the center part (the part of 150 mm in longitudinal length ⁇ 150 mm in transversal length) of this sheet of laminated glass was struck by a hammer with a head of 0.45 kg until the glass was broken into pieces having a particle diameter of 6 mm or less and the glass was partially peeled off, after which the degree of exposure of a film portion from which glass pieces were peeled off was measured to determine the pummel value according to the following Table 1.
  • the pummel value is a value with which the adhesive force between an interlayer film for laminated glass and a glass plate is evaluated
  • the pummel value is a value specified by the degree of exposure (% by area) of a film portion from which glass pieces are peeled off when a sheet of laminated glass is stored for 16 hours at a temperature of ⁇ 18° C. ⁇ 0.6° C.
  • the center part (the part of 150 mm in longitudinal length ⁇ 150 mm in transversal length) of this sheet of laminated glass is struck by a hammer with a head of 0.45 kg until the glass is broken into pieces having a particle diameter of 6 mm or less, and the glass is partially peeled off, and the pummel value is defined in Table 1. That is, the higher the pummel value is, the higher the adhesive force between the interlayer film and the glass is, and this means that the laminated glass is excellent in anti-scattering properties of glass fragments.
  • the surface temperature of the sheet of laminated glass (30 cm in longitudinal length ⁇ 30 cm in transversal length) obtained was adjusted to 23° C. Then, in accordance with JIS R3212: 1998, a hard sphere with a mass of 2260 g and a diameter of 82 mm was dropped at the center part of each of six sheets of laminated glass from a height of 4 m.
  • the laminated glass is acceptable: ⁇ .
  • sheets of laminated glass through each of which the hard sphere does not penetrate within 5 seconds after the hard sphere has collided therewith are three or less sheets, the laminated glass is not acceptable: x.
  • sheets of laminated glass through each of which the hard sphere does not penetrate are four sheets, separately, six sheets of laminated glass are evaluated for the penetration resistance.
  • sheets of laminated glass through each of which the hard sphere does not penetrate are five sheets, separately, one sheet of laminated glass is additionally tested.
  • the laminated glass is acceptable: ⁇ .
  • a hard sphere with a mass of 2260 g and a diameter of 82 mm was dropped at the center part of each of six sheets of laminated glass from a height of 4.0 m, 4.5 m, 5.0 m, 5.5 m, 6.0 m, 6.5 m, or 7.0 m to evaluate the penetration resistance of laminated glass.
  • Example 1 Example 2
  • Example 3 Example 4
  • Example 5 Example 6
  • Composition Thickness ⁇ m 300 400 200 300 400 200 for forming Polyvinyl Average polymerization 3000 3000 3000 3000 3000 first layer acetal degree of PVA resin Content of hydroxyl % by mole 23.8 23.8 23.8 23.8 23.8 24.4 group Acetylation degree % by mole 12.1 12.1 12.1 12.1 12 Acetalization degree % by mole 64.1 64.1 64.1 64.1 63.6 Content Parts by 100 100 100 100 100 100 100 100 100 100 100 100 weight Plasticizer Kind 3GO 3GO 3GO 3GO 3GO 3GO 3GO 3GO Content Parts by 60 60 60 60 60 60 60 weight Glass transition temperature ° C.
  • plural sheets of laminated glass of the respective Examples 1 to 11 were prepared. That is, plural sheets of laminated glass were prepared per one example. The surface temperature of a sheet of laminated glass was adjusted to 23° C. Then, in accordance with JIS R3212: 1998, a hard sphere with a mass of 2260 g and a diameter of 82 mm was dropped at the center part of each of the plural sheets of laminated glass of the respective examples from a height of 6.0 m. In this test, any one of probabilities of permitting the hard sphere to penetrate through the sheet of laminated glass within 5 seconds after the hard sphere has collided therewith in Examples 1 to 11 was determined to be 30% or less.
  • any one of probabilities of permitting the hard sphere to penetrate through the sheet of laminated glass within 5 seconds after the hard sphere has collided therewith in Examples 3 and 6 to 10 was determined to be higher than any one of probabilities of permitting the hard sphere to penetrate through the sheet of laminated glass within 5 seconds after the hard sphere has collided therewith in Examples 1, 2, 4, and 5.
  • the plural sheets of laminated glass of the respective Examples 1, 2, 4, and 5 were determined to be further stably excellent in penetration resistance.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Engineering & Computer Science (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Thermal Sciences (AREA)
  • Biochemistry (AREA)
  • Mechanical Engineering (AREA)
  • General Chemical & Material Sciences (AREA)
  • Geochemistry & Mineralogy (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Ceramic Engineering (AREA)
  • Joining Of Glass To Other Materials (AREA)
  • Laminated Bodies (AREA)
  • Adhesives Or Adhesive Processes (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
  • Adhesive Tapes (AREA)
US15/757,962 2015-09-11 2016-09-09 Interlayer film for laminated glass, and laminated glass Abandoned US20180244020A1 (en)

Applications Claiming Priority (9)

Application Number Priority Date Filing Date Title
JP2015180215 2015-09-11
JP2015-180216 2015-09-11
JP2015180216 2015-09-11
JP2015-180215 2015-09-11
JP2015-180217 2015-09-11
JP2015180217 2015-09-11
JP2016-021340 2016-02-05
JP2016021340 2016-02-05
PCT/JP2016/076598 WO2017043625A1 (fr) 2015-09-11 2016-09-09 Film intercouches pour verre feuilleté, et verre feuilleté

Publications (1)

Publication Number Publication Date
US20180244020A1 true US20180244020A1 (en) 2018-08-30

Family

ID=58239890

Family Applications (2)

Application Number Title Priority Date Filing Date
US15/757,962 Abandoned US20180244020A1 (en) 2015-09-11 2016-09-09 Interlayer film for laminated glass, and laminated glass
US15/757,944 Active 2036-12-26 US10987905B2 (en) 2015-09-11 2016-09-09 Interlayer film for laminated glass, and laminated glass

Family Applications After (1)

Application Number Title Priority Date Filing Date
US15/757,944 Active 2036-12-26 US10987905B2 (en) 2015-09-11 2016-09-09 Interlayer film for laminated glass, and laminated glass

Country Status (11)

Country Link
US (2) US20180244020A1 (fr)
EP (2) EP3348532A4 (fr)
JP (2) JP6725427B2 (fr)
KR (2) KR102604616B1 (fr)
CN (2) CN108025967A (fr)
AU (1) AU2016319585A1 (fr)
MX (1) MX2018002765A (fr)
RU (1) RU2713000C2 (fr)
TW (2) TWI719048B (fr)
WO (2) WO2017043625A1 (fr)
ZA (1) ZA201801831B (fr)

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113739556B (zh) * 2021-07-21 2023-01-10 广东申菱环境系统股份有限公司 一种热泵烘干机组及其控制方法

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20100028642A1 (en) * 2008-08-01 2010-02-04 Kuraray Europe Gmbh Multilayer Films Or Plasticizer-Containing Polyvinyl Acetal With Sound-Absorbing Properties
US20130323516A1 (en) * 2011-02-10 2013-12-05 Michio Shimamoto Laminated glass intermediate film and laminated glass
US20160159039A1 (en) * 2014-12-08 2016-06-09 Solutia Inc. Polymer interlayers having improved sound insulation properties

Family Cites Families (27)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3341399A (en) * 1966-11-16 1967-09-12 Brockway Glass Co Inc Glass to glass adhesives
JP3050967B2 (ja) * 1991-10-16 2000-06-12 積水化学工業株式会社 遮音性中間膜
US5340654A (en) * 1992-04-23 1994-08-23 Sekisui Kagaku Kogyo Kabushiki Kaisha Interlayer film for laminated glass
JPH05330864A (ja) * 1992-05-27 1993-12-14 Sekisui Chem Co Ltd 合わせガラス用中間膜
JP3204890B2 (ja) * 1995-12-12 2001-09-04 積水化学工業株式会社 遮音性合わせガラス用中間膜及び遮音性合わせガラス
US20010046595A1 (en) 1999-12-14 2001-11-29 Moran James R. Intrusion resistant glass laminates
US6903152B2 (en) 2000-03-02 2005-06-07 Sekisui Chemical Co., Ltd. Interlayer film for laminated glass and laminated glass
DE60131668T2 (de) * 2000-09-28 2008-10-30 Solutia Inc. Einbruchbeständiges verbundglas
US6825255B2 (en) * 2003-05-01 2004-11-30 Solutia Incorporated Polyvinyl butyral sheet having antiblocking characteristics
US7846532B2 (en) * 2005-03-17 2010-12-07 Solutia Incorporated Sound reducing wedge shaped polymer interlayers
US7510771B2 (en) 2005-03-17 2009-03-31 Solutia Incorporated Sound reducing polymer interlayers
US20060216485A1 (en) * 2005-03-24 2006-09-28 Solutia, Inc. Polymer interlayers comprising skin layers
JP2007070200A (ja) 2005-09-09 2007-03-22 Asahi Glass Co Ltd 合わせガラス
JP5715565B2 (ja) * 2009-08-07 2015-05-07 株式会社クラレ ポリビニルアセタール組成物、積層体、およびその用途
JP5489960B2 (ja) * 2009-11-30 2014-05-14 日本合成化学工業株式会社 合わせガラス
JP4789025B2 (ja) 2009-12-25 2011-10-05 積水化学工業株式会社 合わせガラス用中間膜及び合わせガラス
EP2610226B1 (fr) 2010-08-24 2015-09-30 Sekisui Chemical Co., Ltd. Film intermédiaire pour verre feuilleté, et verre feuilleté
EP3299349A1 (fr) * 2010-09-30 2018-03-28 Sekisui Chemical Co., Ltd. Film intermédiaire pour verre feuilleté et verre feuilleté
JP2013010671A (ja) 2011-06-29 2013-01-17 Sekisui Chem Co Ltd 合わせガラス用中間膜及び合わせガラス
US9833976B2 (en) 2012-03-09 2017-12-05 Solutia Inc. Defect resisting acoustic polymer interlayers
US10173396B2 (en) 2012-03-09 2019-01-08 Solutia Inc. High rigidity interlayers and light weight laminated multiple layer panels
US9254625B2 (en) * 2013-06-10 2016-02-09 Solutia Inc. Polymer interlayers having improved optical properties
RU2663009C2 (ru) 2014-01-15 2018-08-01 Секисуй Кемикал Ко., Лтд. Межслойная пленка для многослойного стекла и многослойное стекло
EP3095767B1 (fr) 2014-01-15 2019-04-24 Sekisui Chemical Co., Ltd. Film intercouches destiné à un verre feuilleté, et verre feuilleté
US20170100918A1 (en) 2015-10-09 2017-04-13 Solutia Inc. High rigidity interlayers and light weight laminated multiple layer panels
US20170100919A1 (en) 2015-10-09 2017-04-13 Solutia Inc. High rigidity interlayers and light weight laminated multiple layer panels
US20190105880A1 (en) * 2017-10-10 2019-04-11 Solutia Inc. Poly(vinyl acetal) resin compositions, layers, and interlayers having enhanced properties

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20100028642A1 (en) * 2008-08-01 2010-02-04 Kuraray Europe Gmbh Multilayer Films Or Plasticizer-Containing Polyvinyl Acetal With Sound-Absorbing Properties
US20130323516A1 (en) * 2011-02-10 2013-12-05 Michio Shimamoto Laminated glass intermediate film and laminated glass
US20160159039A1 (en) * 2014-12-08 2016-06-09 Solutia Inc. Polymer interlayers having improved sound insulation properties

Also Published As

Publication number Publication date
EP3348532A4 (fr) 2019-07-24
WO2017043624A1 (fr) 2017-03-16
EP3348533A1 (fr) 2018-07-18
TW201718734A (zh) 2017-06-01
US20180339495A1 (en) 2018-11-29
EP3348533A4 (fr) 2019-06-12
JPWO2017043625A1 (ja) 2018-06-21
CN108025966A (zh) 2018-05-11
KR20180050324A (ko) 2018-05-14
TWI719048B (zh) 2021-02-21
KR20180050323A (ko) 2018-05-14
US10987905B2 (en) 2021-04-27
CN108025967A (zh) 2018-05-11
RU2713000C2 (ru) 2020-02-03
JPWO2017043624A1 (ja) 2018-06-21
EP3348532A1 (fr) 2018-07-18
AU2016319585A1 (en) 2018-02-01
ZA201801831B (en) 2019-07-31
JP6725429B2 (ja) 2020-07-15
KR102604616B1 (ko) 2023-11-22
TW201718431A (zh) 2017-06-01
TWI757247B (zh) 2022-03-11
KR102616635B1 (ko) 2023-12-26
MX2018002765A (es) 2018-04-13
RU2018112647A (ru) 2019-10-11
WO2017043625A1 (fr) 2017-03-16
JP6725427B2 (ja) 2020-07-15
RU2018112647A3 (fr) 2019-11-19

Similar Documents

Publication Publication Date Title
US11135811B2 (en) Interlayer for laminated glass, and laminated glass
US11554574B2 (en) Interlayer film for laminated glass and laminated glass
US20180001598A1 (en) Intermediate film for laminated glass, and laminated glass
US20180001600A1 (en) Interlayer for laminated glass and laminated glass
US20170266928A1 (en) Intermediate film for laminated glass, and laminated glass
US10611127B2 (en) Interlayer film for laminated glass, and laminated glass
US20210070020A1 (en) Interlayer film for laminated glass, and laminated glass
US10683694B2 (en) Interlayer for laminated glass, and laminated glass
US10814592B2 (en) Interlayer for laminated glass and laminated glass
US11267231B2 (en) Intermediate film for laminated glass, rolled body, and laminated glass
US10987905B2 (en) Interlayer film for laminated glass, and laminated glass
US10981361B2 (en) Interlayer for laminated glass, and laminated glass

Legal Events

Date Code Title Description
AS Assignment

Owner name: SEKISUI CHEMICAL CO., LTD., JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:IWAMOTO, TATSUYA;MINAKUCHI, NAMI;SIGNING DATES FROM 20180215 TO 20180225;REEL/FRAME:045125/0965

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION